The effect of different temperature annealing on phase relation of LaFe11.5Si1.5 and the magnetocaloric effects of La0.8Ce0.2Fe11.5−xCoxSi1.5 alloys

The phase relation of LaFe_11.5Si_1.5 alloys annealed at different high-temperature from 1223 K (5 h) to 1673 K (0.5 h) has been studied. The powder X-ray diffraction (XRD) patterns show that large amount of 1:13 phase begins to form in the matrix alloy consisting of α-Fe and LaFeSi phases when the annealing temperature is 1423 K. In the temperature range from 1423  to 1523 K, α-Fe and LaFeSi phases rapidly decrease to form 1:13 phase, and LaFeSi phase is rarely observed in the XRD pattern of LaFe_11.5Si_1.5 alloy annealed at 1523 K. With annealing temperature increasing from 1573  to 1673 K, the LaFeSi phase is detected again in the LaFe_11.5Si_1.5 alloy, and there is La₅Si₃ phase when the annealing temperature reaches 1673 K. There almost is no change in the XRD patterns of LaFe_11.5Si_1.5 alloys annealed at 1523 K for 3-5 h. According to this result, the La_0.8Ce_0.2Fe_11.5−xCo_xSi_1.5 (0≤×≤0.7) alloys are annealed at 1523 K (3 h). The analysis of XRD patterns shows that La_0.8Ce_0.2Fe_11.5xCo_xSi_1.5 alloys consist of the NaZn₁₃-type main phase and α-Fe impurity phase. With the increase of Co content from x=0 to 0.7, the Curie temperature T_C increases from 180 to 266 K. Because the increase of Co content can weaken the itinerant electron metamagnetic transition, the order of the magnetic transition at T_C changes from first to second-order between x=0.3 and 0.5. Although the magnetic entropy change decreases from 34.9 to 6.8 J/kg K with increasing Co concentration at a low magnetic field of 0-2 T, the thermal and magnetic hysteresis loss reduces remarkably, which is very important for the magnetic refrigerant near room temperature.     

Structure and magnetic properties of LaFe11.5−xCoxSi1.5C0.2 compounds for magnetic refrigeration near room temperature

The influence of cobalt on the microstructural, magnetic and magnetocaloric properties of LaFe_11.5−xCo_xSi_1.5C_0.2 (x=0.50–0.85) compounds was investigated. The ingots were prepared by using a vacuum induction melting furnace. Before annealing, a large amount of 1:13 phase was distinctly observed. Nearly single 1:13 phase was obtained after annealing at 1353 K for only 3 days. The easy formation of 1:13 phase in the annealing process could be attributed to carbon doping. The Curie temperature (T_C) increases linearly with increasing the cobalt content. Although the maximum magnetic entropy changes of the compounds decrease rapidly when T_C rises from 275 to 298 K, and it decreases mildly when T_C continues to rise. Two composite refrigerants based on the compounds are proposed. Their entropy changes remains approximately constant over the temperature range from 266 to 292 K and 289 to 309 K.     

Large magnetic entropy change near room temperature in the LaFe11.5Si1.5H1.3 interstitial compound

The LaFe_11.5Si_1.5H_1.3 interstitial compound has been prepared. Its Curie temperature T_C (288 K) has been adjusted to around room temperature, and the maximal magnetic entropy change (|ΔS|～17.0 J·kg^-1·K^-1 at T_C) is larger than that of Gd (|ΔS|～9.8 J·kg^-1·K^-1 at T_C=293 K) by ～73.5% under a magnetic change from 0 to 5 T. The origin of the large magnetic entropy change is attributed to the first-order field-induced itinerant-electron metamagnetic transition. Moreover, the magnetic hysteresis of LaFe_11.5Si_1.5H_1.3 under the increase and decrease of the field is very small, which is favourable to magnetic refrigeration application. The present study suggests that the LaFe_11.5Si_1.5H_1.3 compound is a promising candidate as a room-temperature magnetic refrigerant.     

Simultaneous enhancements of Curie temperature and magnetocaloric effects in the La1−xCexFe11.5Si1.5Cy compounds

The effects of introducing Ce and C atoms on the Curie temperature (T_C), the magnetic entropy change (ΔS_M) and the hysteresis loss have been investigated in the NaZn₁₃-type LaFe_11.5Si_1.5 compound. Partial replacement of La with Ce leads to a decrease in T_C and an increase in ΔS_M; however, the introduction of interstitial C atoms can adjust T_C to high temperature. The itinerant-electron metamagnetic transition is weakened after carbonization, which results in a reduction of both the hysteresis loss and magnetocaloric effect (MCE). The maximum value of ΔS_M for La_0.8Ce_0.2Fe_11.5Si_1.5C_0.2 is found to be −28 J/kg K at T_C=207 K with an effective refrigeration capacity of 420 J/kg for a field change from 0 to 5 T. Our study reveals that the enhancements of both T_C and MCEs can be achieved simultaneously in the La_1−xCe_xFe_11.5Si_1.5C_y compounds by adjusting the concentrations of Ce and C atoms appropriately.     

Magnetic and electrical properties of new magnetic phase in Si1−xMnx crystals

We have investigated the magnetic and electrical transport properties of Si_1−xMn_x single crystals grown by the vertical Bridgman method. The alloys with Mn concentrations up to x=0.64 have weak ferromagnetic ordering around T_C∼30 K. However, Si_0.25Mn_0.75 alloys show weak ferromagnetic ordering at 70 K and antiferromagnetic ordering at 104 K, which is confirmed by magnetization and electrical transport studies.     

The study of phase,microstructure, and magnetocaloric properties in LaFe11.6*xSi1.4B0.1 alloys

The effect of Fe on the phase and magnetocaloric property of LaFe_11.6*xSi_1.4B_0.1 alloys with x = 1.0–1.4 have been studied. The results show that the excess of Fe will make the α-Fe phases increase, but the easy corrosion LaFeSi phase reduces in LaFe_11.6*xSi_1.4B_0.1 alloys. All LaFe_11.6*xSi_1.4B_0.1 alloys keep the first-order magnetic phase transition. The saturation magnetizations of LaFe_11.6*xSi_1.4B_0.1 alloys with x > 1 are much higher than LaFe_11.6Si_1.4B_0.1 alloy under 2T magnetic field. This results in the maximum isothermal magnetic entropy changes, and the relative cooling power of LaFe_11.6*xSi_1.4B_0.1 alloys is bigger than for LaFe_11.6Si_1.4B_0.1 alloys.     

Near room temperature magnetocaloric properties of melt-spun Gd100−xBx (x=0, 5, 10, 15, and 20 at%) alloys

The magnetocaloric properties of melt-spun Gd-B alloys were examined with the aim to explore their potential application as magnetic refrigerants near room temperature. A series of Gd_100−xB_x (x=0, 5, 10, 15, and 20 at%) alloys were prepared by melt spinning. With the decrease in Gd/B ratio, Curie temperature (T_C) remains constant at ∼293 K, and saturation magnetization, at 275 K, decreases from ∼100 to ∼78 emu/g. Negligible magnetic hysteresis was observed in these alloys. The peak value of magnetic entropy change, (−ΔS_M)_max, decreased from ∼9.9 J/kg K (0-5 T) and ∼5.5 J/kg K (0-2 T) for melt-spun Gd to ∼7.7 J/kg K (0-5 T) and ∼4.0 J/kg K (0-2 T), respectively for melt-spun Gd₈₅B₁₅ and Gd₈₀B₂₀ alloys. Similarly, the refrigeration capacity (q) decreased monotonously from ∼430 J/kg (0-5 T) for melt-spun Gd to ∼330 J/kg (0-5 T) for melt-spun Gd₈₀B₂₀ alloy. The near room temperature magnetocaloric properties of melt-spun Gd_100−xB_x (0≤x≤20) alloys were found to be comparable to few first-order transition based magnetic refrigerants.     

Influence of boron on the giant magnetocaloric effect of La(Fe0.9Si0.1)13

The influences of boron addition on the phase formation, Curie temperature and magnetic entropy change of the NaZn₁₃-type La(Fe_0.9Si_0.1)₁₃ compound have been investigated. Eight boron containing La(Fe_0.9Si_0.1)₁₃B_x samples were prepared with x=0, 0.03, 0.06, 0.1, 0.2, 0.3, 0.5 and 0.6, respectively. Experimental results show that a small amount of B addition in La(Fe_0.9Si_0.1)₁₃ forms the solid solution NaZn₁₃-type structure phase by substituting B for Si or doping B into interstitial position of the lattice, preserves its giant magnetocaloric effects due to their first-order structural/magnetic transition, as well as increase its Curie temperature T_c slightly. The maximum magnetic entropy changes in the magnetic field change of 0–1.6 T are around 20 J kg^–1 K^–1 for the samples with Boron addition less than 0.3, while improving the Curie temperatures by 2 K.     

Magnetic transitions in LaFe13−x−yCoySix compounds

The magnetic properties of a set of LaFe_13?x?yCo_ySi_x compounds (x = 1.6 ? 2.6; y = 0, y = 1.0) have been investigated using magnetic measurements, thermal expansion, ⁵⁷Fe Mössbauer spectroscopy and high resolution neutron powder diffraction methods over the temperature range 10–300 K. The natures of the magnetic transitions in these LaFe_13?x?yCo_ySi_x compounds have been determined. The Curie temperatures of LaFe_13?xSi_x were found to increase with Si content from T_C = 219(5) K for Si content x = 1.6 to T_C = 250(5) K for x = 2.6. Substitution of Co for Fe in LaFe_10.4Si_2.6 resulted in a further enhancement of the magnetic ordering temperature to T_C = 281(5) K for the LaFe_9.4CoSi_2.6 compound. The nature of the magnetic transition at the Curie temperature changes from first order for LaFe_11.4Si_1.6 to second order for LaFe_10.4Si_2.6 and LaFe_9.4CoSi_2.6. The temperature dependences of the mean magnetic hyperfine field values lead to T_C values in good agreement with analyses of the magnetic measurements. The magnetic entropy change, ?ΔS_M, has been determined from the magnetization curves as functions of temperature and magnetic field (ΔB = 0 ? 5 T) by applying the standard Maxwell relation. In the case of LaFe_12.4Si_1.6 for example, the magnetic entropy change around T_C is determined to be -ΔS_M ～ 14.5 J kg^?1 K^?1 for a magnetic field change Δ B = 0 ? 5 T.     

High Bs nanocrystalline Fe84−x−yCuxNbySi4B12 alloys (x=0.0-1.4, y=0.0-2.5)

In this study, Cu and Nb content dependences of magnetic properties for annealed Fe_84−x−yCu_xNb_ySi₄B₁₂ alloy ribbons fabricated by melt spinning were investigated. In Fe_83−xCu_xNb₁Si₄B₁₂ alloy systems, the coercivity H_c markedly decreases with increasing x and exhibits a minimum at around x=1.0-1.2, while the saturation magnetic flux density B_s shows a slight variation. In Fe_83−yCu₁Nb_ySi₄B₁₂ alloy systems, H_c markedly decreases at around y=0.5, while B_s shows a monotonic decrease. Fe₈₂Cu₁Nb₁Si₄B₁₂ nanocrystalline alloy ribbons exhibit a high B_s of 1.78 T and a low H_c of 3.2 A/m. The core losses of the present alloys at 1.0 T at 400 Hz, P_10/400, and at 1.0 T at 1 kHz, P_10/1k, are 1.3 and 4.4 W/kg, respectively.     

Magnetic ordering above room temperature in the sigma-phase of Fe66V34

Magnetic properties of four sigma-phase Fe_100−xV_x samples with 34.4?x?55.1 were investigated by Mössbauer spectroscopy and magnetic measurements in the temperature interval 4.2-300 K. Four magnetic quantities, viz. hyperfine field, Curie temperature, magnetic moment and susceptibility, were determined. The sample containing 34.4 at% V was revealed to exhibit the largest values found up to now for the sigma-phase for average hyperfine field, 〈B〉=12.1 T, average magnetic moment per Fe atom, 〈μ〉=0.89 μ_B, and Curie temperature, T_C=315.3 K. The quantities were shown to be strongly correlated with each other. In particular, T_C is linearly correlated with 〈μ〉 with a slope of 406.5 K/μ_B, as well as 〈B〉 is so correlated with 〈μ〉, yielding 14.3 T/μ_B for the hyperfine coupling constant.     

Spin-glass-like behaviour and magnetic order in Mn[Cr0.5Ga1.5]S4 spinels

Magnetization and susceptibility were investigated as a function of temperature and magnetic field in polycrystalline Mn[Cr_0.5Ga_1.5]S₄ spinel. The dc susceptibility measurements at 919 Oe showed a disordered ferrimagnetic behaviour with a Curie-Weiss temperature θ_CW=−55 K and an effective magnetic moment of 5.96 μ_B close to the spin-only value of 6.52 μ_B for Cr³⁺ and Mn²⁺ ions in the 3d³ and 3d⁵ configurations, respectively. The magnetization measured at 100 Oe revealed the multiple magnetic transitions with a sharp maximum at the Néel temperature T_N=3.9 K, a minimum at the Yafet-Kittel temperature T_YK=5 K, a broad maximum at the freezing temperature T_f=7.9 K, and an inflection point at the Curie temperature T_C=48 K indicating a transition to paramagnetic phase. A large splitting between the zero-field-cooled (ZFC) and field-cooled (FC) magnetizations at a temperature smaller than T_C suggests the presence of spin-glass-like behaviour. This behaviour is considered in a framework of competing interactions between the antiferromagnetic ordering of the A(Mn) sublattice and the ferromagnetic ordering of the B(Cr) sublattice.     

Magnetic domain structure in Fe78.8−xCoxCu0.6Nb2.6Si9B9 nanocrystalline alloys studied by Lorentz microscopy

The magnetic domain structures of Fe_78.8−xCo_xCu_0.6Nb_2.6Si₉B₉ (x=0, 20, 40, 60) alloys are investigated by Lorentz microscopy coupled with the focused ion beam method. The specimen prepared using the FIB method is found to have a considerably more uniform thickness compared to that prepared using the ion-milling method. In Fe_38.8Co₄₀Cu_0.6Nb_2.6Si₉B₉ and Fe_18.8Co₆₀Cu_0.6Nb_2.6Si₉B₉ alloys, 180° domain walls extending in the direction of the induced magnetic anisotropy are observed. Analysis with Lorentz microscopy reveals that the width of the magnetic domains decreases with an increase in the cobalt content or the induced magnetic anisotropy K_u, that is, the domain width d is proportional to the induced magnetic anisotropy (K_u)^−1/4. On the other hand, in the in situ Lorentz microscopy observation as a function of temperature, magnetic ripple structures are found to appear in a localized area due to the fluctuation of magnetization vectors from 423 K. It is observed that the induced magnetic anisotropy caused by the applied magnetic field at 803 K is not suppressed by the magnetic ripple structures observed at 423–443 K.     

Electron transport properties of Co71−xFexCr7Si8B14 (x=0, 2, 3.2, 4, 6,8 and 12 at%) amorphous alloys during devitrification

The investigation addresses the electron transport properties of Co_71−xFe_xCr₇Si₈B₁₄ (x=0, 2, 3.2, 4, 6, 8 and 12 at%) amorphous alloys. The variation in electrical resistivity of as-cast amorphous materials with thermal scanning from room temperature to 1000 K was measured. The CoFe-based alloys revealed an initial decrease in temperature coefficient of resistivity (TCR), a characteristic of spin-wave phenomena in glassy metallic systems. This behaviour in the present alloys was in a sharp contrast to the Co-based amorphous materials that indicate the drop in resistivity much below room temperature. In the studied alloys, the variation in initial TCR values and the full-width at half-maxima determined from X-ray diffraction of as-quenched materials exhibited a similar trend with increasing Fe content, indicating the compositional effect of near neighbouring atoms. After the initial decrease in resistivity, all the alloys indicated a subsequent increase at T_min. The Curie temperature (T_C), which was measured from thermal variation of ac susceptibility showed non-monotonic change with Fe content. In the temperature range between T_min and T_C the relative scattering by electron-magnon and electron-phonon resulted in the non-monotonic change in Curie temperature. At crystallization onset (T_X1) all the alloys except there with X=6, showed a sharp decrease in electrical resistivity which was attributed to ordering phenomena. In contrast to this resistivity decrease, X=6 alloy exhibited a drastic increase in resistivity around T_X1 observed during amorphous to nanocrystalline transformation. Such nanocrystalline state was observed by Transmission electron microscopy.     

Magnetic properties of NdAu2Ge2

Physical properties of NdAu₂Ge₂, crystallising with the tetragonal ThCr₂Si₂-type crystal structure, were investigated by means of magnetic, calorimetric and electrical transport measurements as well as by neutron diffraction. The compound exhibits antiferromagnetic ordering below T_N=4.5 K with a collinear magnetic structure of the AFI-type. The neodymium magnetic moments are parallel to the c-axis and amount to 1.04(4) μ_B at 1.5 K. The observed magnetic behaviour is strongly influenced by crystalline electric field effect.     

Reduction of hysteresis loss in LaFe11.7Si1.3Hx hydrides with significant magnetocaloric effects

Magnetic properties and magnetocaloric effects (MCEs) have been investigated in hydrogenated LaFe_11.7 Si_1.3H _x (x=0,1.37, and 2.07) compounds. It is found that the Curie temperature, T _C, can be tuned from 192 to 338 K by adjusting the hydrogen content from 0 to 2.07. It is attractive that both thermal and magnetic hysteresis are remarkably reduced because of the weakness of the itinerant-electron metamagnetic transition after hydrogenation. The maximal hysteresis loss at T _C decreases from 33.4 to 8.8 J/kg as x increases from 0 to 2.07. For the samples with x=0,1.37, and 2.07, the maximal values of the isothermal magnetic entropy change, ΔS _M, are 20.9, 15.1, and 15.83 J/kg K for the increasing field and 20.76 J/kg K, 14.53 J/kg K and 15.61 J/kg K for the decreasing field at T _C, with efficient refrigeration capacities of 439, 330, and 304 J/kg for a field change of 0–5 T, respectively. Large reversible MCE and small hysteresis with considerable refrigeration capacity indicate the potential of LaFe_11.7Si_1.3H _x hydride as a candidate magnetic refrigerant around room temperature.     

The structural and magnetic properties of Ni2Mn1−xBxGa Heusler alloys

The influence of the substitution of manganese by boron on the crystal structure and magnetic properties of Ni₂Mn_1−xB_xGa Heusler alloys with 0?x?0.5 has been investigated using X-ray diffraction, thermal expansion, resistivity, and magnetization measurements. The samples with concentrations x<0.25 were found to be of single phase and belonged to the cubic L2₁ crystal structure at room temperature. Crystal cell parameters of the alloys decreased from 5.830 to 5.825 Å with increasing boron concentration (x) from 0 to 0.25. The alloys were ferromagnetically ordered at 5 K and the saturation magnetization decreased with increasing boron concentration. The ferromagnetic ordering and structural transition temperatures for 0?x?0.3 have been observed and the phase (x−T) diagram of the Ni₂Mn_1−xB_xGa system was constructed. The phase (x−T) diagram indicates that the ground state of Ni₂Mn_1−xB_xGa alloys belongs to ferromagnetic martensitic, premartensitic, and austenitic phases in x?0.12, 0.12<x?0.18, and 0.18<x?0.3, respectively. The relative influence of cell parameters and electron concentrations on the phase diagram is discussed.     

The magnetic entropy change in La0.8Ce0.2Fe11.4Si1.6Bx compounds prepared by copper-mold casting

The magnetocaloric effect (MCE) of La_0.8Ce_0.2Fe_11.4Si_1.6B_x (x=0.0-0.5) compounds, prepared by a copper-mold casting (CMC) method, has been investigated. Comparing with the conventional arc-melting (CAM) method, the relatively homogenous composition and microstructure were achieved in the precursor alloys prepared by the CMC method. As a result, the annealing time is dramatically shortened from several weeks for CAM alloys to 2 h for CMC alloys, suggesting that CMC method is a time-saving and energy-saving method for fabrication of MCE alloys. On the other hand, it is revealed that B addition gives rise to an enhancement of Curie temperature (T_C), a reduction of thermal lag and magnetic hysteresis and a broadening of working temperature span as well. Although the peak value of magnetic entropy change decreases with B content, various B-contained compounds hold close refrigerant capacities. Comprehensively considering magnetocaloric properties of the B-contained La_0.8Ce_0.2Fe_11.4Si_1.6B_x compounds, it can be concluded that the B-contained compounds prepared by CMC method are promising candidates of magnetocaloric materials in practical application.     

Effect of interstitial nitrogen on magnetism and entropy change of LaFe11.7Si1.3 compound

Crystal structure, magnetism and magnetocaloric properties of LaFe_11.7Si_1.3N_y (y=0, 1.3) compounds have been studied by X-ray diffraction and magnetic measurements. The LaFe_11.7Si_1.3N_y compounds present a cubic NaZn₁₃-type structure. Insertion of 1.3 nitrogen atoms per LaFe_11.7Si_1.3 formula increases the lattice parameter and Curie temperature from 11.467 to 11.733 Å and from 190 to ∼230 K, respectively. Besides, the absorption of nitrogen drives drastically the magnetic transition from first to second order and accordingly strongly decreases the magnetocaloric effect compared to the parent alloy. Under an external field change of 5 T, the value of isothermal entropy change −ΔS is about 28 and 3.5 J/kg K for LaFe_11.7Si_1.3 and LaFe_11.7Si_1.3N_1.3, respectively, close to their Curie temperature. However, the relative cooling power RCP(S) of the nitride is about half that of the parent alloy.     

Thermal annealing effects on the magnetic behavior of Ce2NiSi3

We have investigated the crystallographic, magnetic and thermodynamic properties of the as-cast and annealed Ce₂NiSi₃ alloys, crystallizing in the AlB₂-type hexagonal structure. The DC-magnetic susceptibility data show that the as-cast sample exhibits an antiferromagnetic (AFM) ordering below T_N= 3.8 K, whereas the annealed sample shows, at 4.2 K, a magnetic transition of AFM nature and, around 2.5 K, an additional anomaly. The specific heat shows a peak with at 3.8 K for the as cast sample, which shifts to lower temperatures when the magnetic field increases, consistent with the antiferromagnetic nature of the transition. On the other hand, in the annealed alloy, the maximum of the specific heat peak reaches at 4.2 K, and no additional anomalies were observed. The different magnetic behavior between the as-cast and annealed samples is attributed to thermal effects on the structural disorder of nickel and silicon atoms, as already observed in other isotypic R₂TSi₃ alloys, where R=U or Ce, and T= transition metal.