Green synthesis of soya bean sprouts-mediated superparamagnetic Fe3O4 nanoparticles

Superparamagnetic Fe₃O₄ nanoparticles were first synthesized via soya bean sprouts (SBS) templates under ambient temperature and normal atmosphere. The reaction process was simple, eco-friendly, and convenient to handle. The morphology and crystalline phase of the nanoparticles were determined from scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED), and X-ray diffraction (XRD) spectra. The effect of SBS template on the formation of Fe₃O₄ nanoparticles was investigated using X-ray photoemission spectroscopy (XPS) and Fourier-transform infrared spectroscopy (FT-IR). The results indicate that spherical Fe₃O₄ nanoparticles with an average diameter of 8 nm simultaneously formed on the epidermal surface and the interior stem wall of SBS. The SBS are responsible for size and morphology control during the whole formation of Fe₃O₄ nanoparticles. In addition, the superconducting quantum interference device (SQUID) results indicate the products are superparamagnetic at room temperature, with blocking temperature (T_B) of 150 K and saturation magnetization of 37.1 emu/g.     

Exchange coupling behavior in bimagnetic CoFe2O4/CoFe2 nanocomposite

In this work we report a study of the magnetic behavior of ferrimagnetic oxide CoFe₂O₄ and ferrimagnetic oxide/ferromagnetic metal CoFe₂O₄/CoFe₂ nanocomposite. The latter compound is a good system to study hard ferrimagnet/soft ferromagnet exchange coupled. Two steps were followed to synthesize the bimagnetic CoFe₂O₄/CoFe₂ nanocomposite: (i) first, preparation of CoFe₂O₄ nanoparticles using a simple hydrothermal method, and (ii) second, reduction reaction of cobalt ferrite nanoparticles using activated charcoal in inert atmosphere and high temperature. The phase structures, particle sizes, morphology, and magnetic properties of CoFe₂O₄ nanoparticles were investigated by X-Ray diffraction (XRD), Mossbauer spectroscopy (MS), transmission electron microscopy (TEM), and vibrating sample magnetometer (VSM) with applied field up to 3.0 kOe at room temperature and 50 K. The mean diameter of CoFe₂O₄ particles is about 16 nm. Mossbauer spectra revealed two sites for Fe³⁺. One site is related to Fe in an octahedral coordination and the other one to the Fe³⁺ in a tetrahedral coordination, as expected for a spinel crystal structure of CoFe₂O₄. TEM measurements of nanocomposite showed the formation of a thin shell of CoFe₂ on the cobalt ferrite and indicate that the nanoparticles increase to about 100 nm. The magnetization of the nanocomposite showed a hysteresis loop that is characteristic of exchange coupled systems. A maximum energy product (BH)_max of 1.22 MGOe was achieved at room temperature for CoFe₂O₄/CoFe₂ nanocomposites, which is about 115% higher than the value obtained for CoFe₂O₄ precursor. The exchange coupling interaction and the enhancement of product (BH)_max in nanocomposite CoFe₂O₄/CoFe₂ are discussed.     

An easy and novel approach for the decoration of graphene oxide by Fe3O4 nanoparticles

A new and relatively general route was developed to fabricate graphene oxide (GO)-Fe₃O₄ hybrid. X-ray diffraction, transmission electron morphology, X-ray photoelectron spectroscopy (XPS) and energy-dispersive spectrum were used to demonstrate the successful attachment of iron oxide nanoparticles to GO sheets. Transmission electron microscopy observation indicates that the size of the Fe₃O₄ nanoparticles was about 2.7 nm with narrow size distribution. Moreover, this hybrid shows superparamagnetic property and allows the rapid separation under an external-magnetic field. In addition, the method could be extended to further development of graphene-based nanoelectronics.     

Microwave synthesis of magnetic Fe3O4 nanoparticles used as a precursor of nanocomposites and ferrofluids

Methods to synthesize magnetic Fe₃O₄ nanoparticles and to modify the surface of particles are presented in the present investigation. Fe₃O₄ magnetic nanoparticles were prepared by the co-precipitation of Fe³⁺ and Fe²⁺, NH₃·H₂O was used as the precipitating agent to adjust the pH value, and the aging of Fe₃O₄ magnetic nanoparticles was accelerated by microwave (MW) irradiation. The obtained Fe₃O₄ magnetic nanoparticles were characterized by Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), X-ray powder diffraction (XRD) and vibrating sample magnetometer (VSM). The average size of Fe₃O₄ crystallites was found to be around 8–9 nm. Thereafter, the surface of Fe₃O₄ magnetic nanoparticles was modified by stearic acid. The resultant sample was characterized by FT-IR, scanning electron microscopy (SEM), XRD, lipophilic degree (LD) and sedimentation test. The FT-IR results indicated that a covalent bond was formed by chemical reaction between the hydroxyl groups on the surface of Fe₃O₄ nanoparticles and carboxyl groups of stearic acid, which changed the polarity of Fe₃O₄ nanoparticles. The dispersion of Fe₃O₄ in organic solvent was greatly improved. Effects of reaction time, reaction temperature and concentration of stearic acid on particle surface modification were investigated. In addition, Fe₃O₄/polystyrene (PS) nanocomposite was synthesized by adding surface modified Fe₃O₄ magnetic nanoparticles into styrene monomer, followed by the radical polymerization. The obtained nanocomposite was tested by thermogravimetry (TG), differential scanning calorimetry (DSC) and XRD. Results revealed that the thermal stability of PS was not significantly changed after adding Fe₃O₄ nanoparticles. The Fe₃O₄ magnetic fluid was characterized using UV–vis spectrophotometer, Gouy magnetic balance and laser particle-size analyzer. The testing results showed that the magnetic fluid had excellent stability, and had susceptibility of 4.46×10⁻⁸ and saturated magnetization of 6.56 emu/g. In addition, the mean size d (0.99) of magnetic Fe₃O₄ nanoparticles in the fluid was 36.19 nm.     

Low-temperature synthesis and growth of superparamagnetic Zn0.5Ni0.5Fe2O4 nanosized particles

Mono-disperse spinel Ni_0.5Zn_0.5Fe₂O₄ nanosized particles have been synthesized via a hydrothermal method at low temperature. X-ray diffraction (XRD), transmission electron microscope (TEM) and high-resolution transmission electron microscope (HRTEM) analysis indicated that the synthesized nanocrystals were of pure cubic spinel structure with the size about 6-20 nm. The activation energy of grain growth is 35.06 kJ/mol experimented by the Arrhenius equation. A primary experimental model was put forward to shed light on the growth mechanism of crystallined spinel Ni-Zn ferrite nanosized particles under hydrothermal conditions. The magnetic measurements shows that the prepared Ni_0.5Zn_0.5Fe₂O₄ nanoparticle possess good superparamagnetic behavior.     

Chemical synthesis of spinel nickel ferrite (NiFe2O4) nano-sheets

The present investigation is related to the deposition of single-phase nano-sheets spinel nickel ferrite (NiFe₂O₄) thin films onto glass substrates using a chemical method. Nano-sheets nickel ferrite films were deposited from an alkaline bath containing Ni²⁺ and Fe²⁺ ions. The films were characterized for their structural, surface morphological and electrical properties by means of X-ray diffraction (XRD), transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and two-point probe electrical resistivity techniques. The X-ray diffraction pattern showed that NiFe₂O₄ nano-sheets are oriented along (3 1 1) plane. The FT-IR spectra of NiFe₂O₄ films showed strong absorption peaks around 600 and 400 cm⁻¹ which are typical for cubic spinel crystal structure. Microstructural study of NiFe₂O₄ film revealed nano-sheet like morphology with average sheet thickness of 30 nm. The room temperature electrical resistivity of the NiFe₂O₄ nano-sheets was 10⁷ Ω cm.     

Effect of grain size on the magnetic properties of superparamagnetic Ni0.5Zn0.5Fe2O4 nanoparticles by co-precipitation process

Ni_0.5Zn_0.5Fe₂O₄ (NZFO) spinel-type nanoparticles were directly fabricated by the chemical co-precipitation process using metal nitrate and acetate as precursors since nitrogen and carbon would be taken away in the forms of oxynitride and oxycarbide, respectively, after the precursors were annealed and then investigated in detail by employing X-ray diffraction (XRD), magnetic measurement and Raman spectroscopy. XRD analysis indicates that the as-prepared nanocrystals are all of a pure cubic spinel structure with their sizes ranging from 20.8 to 53.3 nm, as well as peaks of some samples shifting to lower angles due to lattice expansion. Calculations from the derived XRD data indicate that the activation energy is 30.83 kJ/mol. The magnetic measurements show that these samples are superparamagnetic. The saturation magnetization increases with annealing temperature, which may be explained by super-exchange interactions of Fe ions occurring at A- and B-sites. The variation of coercivity with particle size is interpreted on the basis of domain structure and crystal anisotropy. Furthermore, these nanoparticles exhibit a redshift phenomenon at lower temperatures seen in the Raman spectra, which could be related to ionic substitution.     

Synthesis and magnetic characterization of Zn0.7Ni0.3Fe2O4 nanoparticles via microwave-assisted combustion route

We report on the synthesis of Zn_0.7Ni_0.3Fe₂O₄ nanoparticles via microwave assisted combustion route by using urea as fuel. XRD and FT-IR analyses confirm the composition and structure as spinel ferrite. The crystallite size estimated from XRD (16.4 nm) and the magnetic core size (15.04 nm) estimated from VSM agree well, while a slightly smaller magnetic diameter reflects a very thin magnetically dead layer on the surface of the nanoparticles. Morphological investigation of the products was done by TEM which revealed the existence of irregular shapes such spherical, spherodial and polygon. Magnetization measurements performed on Zn_0.7Ni_0.3Fe₂O₄ nanoparticles showed that saturation was not attained at even in the high magnetic field. The sample shows superparamagnetic behavior at around the room temperature and ferromagnetic behavior below the blocking temperature which is measured as 284 K.     

Microwave dielectric and magnetic properties of superparamagnetic 8-nm Fe3O4 nanoparticles

The superparamagnetic 8-nm Fe₃O₄ nanoparticles were successfully prepared by chemical oxidation process. For the complex permittivity, the dual dielectric relaxation processes have been proved by two overlapped Cole–Cole semicircles, and the natural resonance frequency is 3.03 GHz for the complex permeability. The maximum reflection loss value reaches −55.5 dB at 6.11 GHz with 3.85 mm in the thickness of the absorbers for the superparamagnetic 8-nm Fe₃O₄ nanoparticles which is better than that of 150 nm and 30 nm Fe₃O₄ nanoparticles. It is believed that the superparamagnetic 8-nm Fe₃O₄ nanoparticles can be used as a kind of candidate for microwave absorber.     

Biosynthesis and magnetic properties of mesoporous Fe3O4 composites

Magnetic Fe₃O₄ materials with mesoporous structure are synthesized by co-precipitation method using yeast cells as a template. The X-ray diffraction (XRD) pattern indicates that the as-synthesized mesoporous hybrid Fe₃O₄ is well crystallized. The Barrett-Joyner-Halenda (BJH) models reveal the existence of mesostructure in the dried sample which has a specific surface area of 96.31 m²/g and a pore size distribution of 8-14 nm. Transmission electron microscopy (TEM) measurements confirm the wormhole-like structure of the resulting samples. The composition and chemical bonds of the Fe₃O₄/cells composites are studied by Fourier transform infrared (FT-IR) spectroscopy. Preliminary magnetic properties of the mesoporous hybrid Fe₃O₄ are characterized by a vibrating sample magnetometer (VSM). The magnetic Fe₃O₄/cells composites with mesoporous structure have potential applications in biomedical areas, such as drug delivery.     

High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

Nano-sized magnetic Y₃Fe₅O₁₂ ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y₃Fe₅O₁₂ ferrites. The highest heat ability in the AC magnetic field was for the fine Y₃Fe₅O₁₂ powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mm? beads). The heat generation ability of the excessively milled Y₃Fe₅O₁₂ samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mm? beads, the heat generation ability (W g⁻¹) was estimated using a 3.58×10⁻⁴ fH² frequency (f/kHz) and the magnetic field (H/kA m⁻¹), which is the highest reported value of superparamagnetic materials.     

Microwave synthesis, characterization, and electrochemical properties of α-Fe2O3 nanoparticles

Ultrafine α-Fe₂O₃ nanoparticles with an extremely narrow distribution were synthesized by microwave heating. Transmission electron microscopy (TEM) images showed that most primary particles have ellipsoid shapes, and the average diameter of the primary particles was less than 10 nm. The electron diffraction pattern and fringes in some particles in TEM images showed that these nanoparticles were single crystals. The BET surface area of the freeze-dried product was 217 m²/g. The initial discharge capacity of the α-Fe₂O₃ nanoparticles exceeded 1007 mA/g (cut-off voltage: 0.5 V). This large capacity corresponds to that calculated by assuming the reduction of Fe³⁺ to Fe⁰. The α-Fe₂O₃ nanoparticles also work as a rechargeable electrode material. The charge-discharge test between 4 V and 1.5 V gave a good rechargeable capacity of about 150 mAh/g.     

The structure and magnetic properties of Zn1−xNixFe2O4 ferrite nanoparticles prepared by sol–gel auto-combustion

Zn_1−xNi_xFe₂O₄ ferrite nanoparticles were prepared by sol–gel auto-combustion and then annealed at 700 °C for 4 h. The results of differential thermal analysis indicate that the thermal decomposition temperature is about 210 °C and Ni–Zn ferrite nanoparticles could be synthesized in the self-propagating combustion process. The microstructure and magnetic properties were investigated by means of X-ray diffraction, scanning electron microscope, and Vibrating sample magnetometer. It is observed that all the spherical nanoparticles with an average grain size of about 35 nm are of pure spinel cubic structure. The crystal lattice constant declines gradually with increasing x from 0.8435 nm (x=0.20) to 0.8352 nm (x=1.00). Different from the composition of Zn_0.5Ni_0.5Fe₂O₄ for the bulk, the maximum M_s is found in the composition of Zn_0.3Ni_0.7Fe₂O₄ for nanoparticles. The H_c of samples is much larger than the bulk ferrites and increases with the enlarging x. The results of Zn_0.3Ni_0.7Fe₂O₄ annealed at different temperatures indicate that the maximum M_s (83.2 emu/g) appears in the sample annealed at 900 °C. The H_c of Zn_0.3Ni_0.7Fe₂O₄ firstly increases slightly as the grain size increases, and presents a maximum value of 115 Oe when the grains grow up to about 30 nm, and then declines rapidly with the grains further growing. The critical diameter (under the critical diameter, the grain is of single domain) of Zn_0.3Ni_0.7Fe₂O₄ nanoparticles is found to be about 30 nm.     

Synthesis and characterization of TiO2/Fe2O3 core-shell nanocomposition film and their photoelectrochemical property

TiO₂/Fe₂O₃ core-shell nanocomposition film has been fabricated via two-step method. TiO₂ nanorod arrays are synthesized by a facile hydrothermal method, and followed by Fe₂O₃ nanoparticles deposited on TiO₂ nanorod arrays through an ordinary chemical bath deposition. The phase structures, morphologies, particle size, chemical compositions of the composites have been characterized by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and ultraviolet-visible (UV-vis) spectrophotometer. The results confirm that Fe₂O₃ nanoparticles of mean size ca. 10 nm coated on the surface of TiO2 NRs. After depositing Fe₂O₃, UV-vis absorption property is induces the shift to the visible-light range, the annealing temperature of 600 °C is the best condition for UV-vis absorption property of TiO₂/Fe₂O₃ nanocomposite film, and increasing Fe content, optical activity are enhanced one by one. The photoelectrochemical (PEC) performances of the as-prepared composite nanorods are determined by measuring the photo-generated currents under illumination of UV-vis light. The TiO₂ NRs modified by Fe₂O₃ show the photocurrent value of 1.36 mA/cm² at 0 V vs Ag/AgCl, which is higher than those of unmodified TiO₂ NRs.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

Ag-deposited silica-coated Fe3O4 magnetic nanoparticles catalyzed reduction of p-nitrophenol

In this paper, a novel approach was successfully developed for advanced catalyst Ag-deposited silica-coated Fe₃O₄ magnetic nanoparticles, which possess a silica coated magnetic core and growth active silver nanoparticles on the outer shell using n-butylamine as the reductant of AgNO₃ in ethanol. The as-synthesized nanoparticles have been characterized by X-ray powder diffraction (XRD), transmission electron microscopy (TEM), energy dispersive X-ray analysis (EDX), Fourier transform infrared spectra (FT-IR), vibration sample magnetometer (VSM), and have been exploited as a solid phase catalyst for the reduction of p-nitrophenol in the presence of NaBH₄ by UV-vis spectrophotometry. The obtained products exhibited monodisperse and bifunctional with high magnetization and excellent catalytic activity towards p-nitrophenol reduction. As a result, the as-obtained nanoparticles showed high performance in catalytic reduction of p-nitrophenol to p-aminophenol with conversion of 95% within 14 min in the presence of an excess amount of NaBH₄, convenient magnetic separability, as well as remained activity after recycled more than 6 times. The Fe₃O₄@SiO₂-Ag functional nanostructure could hold great promise for various catalytic reactions.     

Synthesis of nanocrystalline Zn0.5Mn0.5Fe2O4 via in situ polymerization technique

Nanocrystalline Zn_0.5Mn_0.5Fe₂O₄ was synthesized through the pyrolysis of polyacrylate salt precursors prepared via in situ polymerization of the metal salts and acrylic acid. The pyrolysis behavior of the polymeric precursors was studied by use of thermal analysis. The as-obtained product was characterized by powder X-ray diffraction (XRD), transmission electron microscope (TEM), electron diffraction (ED) pattern, scanning electron microscopy (SEM) and electron dispersive X-ray (EDX) analysis. The results revealed that the particle size is in the range of 15–25 nm for Zn-Mn ferrites with good crystallinity. Magnetic properties of the sample at 300 K were measured using a vibrating sample magnetometer, which showed that the sample exhibited characteristics of superparamagnetism.     

Fabrication, characterization and measurement of thermal conductivity of Fe3O4 nanofluids

Magnetite Fe₃O₄ nanoparticles were synthesized by a co-precipitation method at different pH values. The products were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, and transmission electronic microscopy. Their magnetic properties were evaluated on a vibrating sample magnetometer. The results show that the shape of the particles is cubic and they are superparamagnetic at room temperature. Magnetic nanofluids were prepared by dispersing the Fe₃O₄ nanoparticles in water as a base fluid in the presence of tetramethyl ammonium hydroxide as a dispersant. The thermal conductivity of the nanofluids was measured as a function of volume fraction and temperature. The results show that the thermal conductivity ratio of the nanofluids increases with increase in temperature and volume fraction. The highest enhancement of thermal conductivity was 11.5% in the nanofluid of 3 vol% of nanoparticles at 40 °C. The experimental results were also compared with the theoretical models.     

Novel approach to preparation of LiMn2O4 core/LiNixMn2−xO4 shell composite

Combining two methods, coating and doping, to modify spinel LiMn₂O₄, is a novel approach we used to synthesize active material. First we coated the LiMn₂O₄ particles with the nickel oxide particles by means of homogenous precipitation, and then the nickel oxide-coated LiMn₂O₄ was calcined at 750 °C to form a LiNi_xMn_2−xO₄ shell on the surface of spinel LiMn₂O₄ particles. Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), cyclic voltammetry (CV) and charge-discharge test were performed to characterize the spinel LiMn₂O₄ before and after modification. The experimental results indicated that a spinel LiMn₂O₄ core is surrounded by a LiNi_xMn_2−xO₄ shell. The resulting composite showed excellent electrochemical cycling performance with an average fading rate of 0.014% per cycle. This improved cycle stability is greatly attributed to the suppression of Jahn-Teller distortion on the surface of spinel LiMn₂O₄ particles during cycling.     

High temperature ferromagnetism of the vacuum-annealed (In1−xFex)2O3 powders

(In_1−xFe_x)₂O₃ (x = 0.02, 0.05, 0.2) powders were prepared by a solid state reaction method and a vacuum annealing process. A systematic study was done on the structural and magnetic properties of (In_1−xFe_x)₂O₃ powders as a function of Fe concentration and annealing temperature. The X-ray diffraction and high-resolution transmission electron microscopy results confirmed that there were not any Fe or Fe oxide secondary phases in vacuum-annealed (In_1−xFe_x)₂O₃ samples and the Fe element was incorporated into the indium oxide lattice by substituting the position of indium atoms. The X-ray photoelectron spectroscopy revealed that both Fe²⁺ and Fe³⁺ ions existed in the samples. Magnetic measurements indicated that all samples were ferromagnetic with the magnetic moment of 0.49-1.73 μ_B/Fe and the Curie temperature around 783 K. The appearance of ferromagnetism was attributed to the ferromagnetic coupling of Fe²⁺ and Fe³⁺ ions via an electron trapped in a bridging oxygen vacancy.