Crystallization of amorphous Co2MnSi thin film

Amorphous Co₂MnSi thin film was deposited using radio-frequency sputtering. The amorphous film crystallized into a single-phased L2₁ structure at 500 °C, which was highly disordered. The structure was meta-stable as the crystallized film decomposed upon further heating. Increasing the annealing temperature to 600 °C precipitated fcc Co together with Co₂MnSi. Magnetic measurements showed that the as-deposited amorphous film was paramagnetic, exhibiting a spin glass state below 44 K. The phase transition at 500 °C produced a ferromagnetic Co₂MnSi thin film whose saturation magnetic moment was considerably lower than reported values due to the disordered structure of the crystallized film.     

Enhanced antiferromagnetic coupling in dual-synthetic antiferromagnet with Co2FeAl electrodes

We study dual-synthetic antiferromagnets (DSyAFs) using Co₂FeAl (CFA) Heusler electrodes with a stack structure of Ta/CFA/Ru/CFA/Ru/CFA/Ta. When the thicknesses of the two Ru layers are 0.45 nm, 0.65 nm or 0.45 nm, 1.00 nm, the CFA-based DSyAF has a strong antiferromagnetic coupling between adjacent CFA layers at room temperature with a saturation magnetic field of ∼11,000 Oe, a saturation magnetization of ∼710 emu/cm³ and a coercivity of ∼2.0 Oe. Moreover, the DSyAF has a good thermal stability up to 400 °C, at which CFA films show B2-ordered structure. Therefore, the CFA-based DSyAFs are favorable for applications in future spintronic devices.     

Influence of deposition temperature on the structural and morphological properties of Be3N2 thin films grown by reactive laser ablation

Be₃N₂ thin films have been grown on Si(1 1 1) substrates using the pulsed laser deposition method at different substrate temperatures: room temperature (RT), 200 °C, 400 °C, 600 °C and 700 °C. Additionally, two samples were deposited at RT and were annealed after deposition in situ at 600 °C and 700 °C. In order to obtain the stoichiometry of the samples, they have been characterized in situ by X-ray photoelectron (XPS) and reflection electron energy loss spectroscopy (REELS). The influence of the substrate temperature on the morphological and structural properties of the films was investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM) and X-ray diffraction (XRD). The results show that all prepared films presented the Be₃N₂ stoichiometry. Formation of whiskers with diameters of 100-200 nm appears at the surface of the films prepared with a substrate temperature of 600 °C or 700 °C. However, the samples grown at RT and annealed at 600 °C or 700 °C do not show whiskers on the surface. The average root mean square (RMS) roughness and the average grain size of the samples grown with respect the substrate temperature is presented. The films grown with a substrate temperature between the room temperature to 400 °C, and the sample annealed in situ at 600 °C were amorphous; while the αBe₃N₂ phase was presented on the samples with a substrate temperature of 600 °C, 700 °C and that deposited with the substrate at RT and annealed in situ at 700 °C.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

On the thermal stability of Co2Z hexagonal ferrites for low-temperature ceramic cofiring technologies

Co₂Z hexaferrite Ba₃Co₂Fe₂₄O₄₁ was prepared by a mixed oxalate co-precipitation route and the standard ceramic technology. XRD studies show that at T<1300 °C different ferrite phases coexist with the M-type hexaferrite as majority phase between 1000 and 1100 °C and the Y-type ferrite at 1230 °C. The Z-type material has its stability interval between 1300 and 1350 °C. Both synthesis routes result in almost single-phase Z-type ferrites after calcination at 1330 °C, intermediate grinding and sintering at 1330 °C. The permeability of Co₂Z-type ferrite of about μ=20 is stable up to several 100 MHz, with maximum losses μ′′ around 700 MHz. Addition of 3 wt% Bi₂O₃ as sintering aid shifts the temperature of maximum shrinkage down to 950 °C and enables sintering of Z-type ferrite powders at 950 °C. However, the permeability is reduced to μ=3. It is shown here for the first time that Co₂Z ferrite is not stable under these conditions; partial thermal decomposition into other hexagonal ferrites is found by XRD studies. This is accompanied by a significant decrease of permeability. This shows that Co₂Z hexagonal ferrite is not suitable for the fabrication of multilayer inductors for high-frequency applications via the low-temperature ceramic cofiring technology since the material is not compatible with the typical process cofiring temperature of 950 °C.     

Effect of Li2O and CoO-doping of CuO/Fe2O3 system on its surface and catalytic properties

Physicochemical, surface and catalytic properties of pure and doped CuO/Fe₂O₃ system were investigated using X-ray diffraction (XRD), energy dispersive X-ray analysis (EDX), nitrogen adsorption at −196 °C and CO-oxidation by O₂ at 80-220 °C using a static method. The dopants were Li₂O (2.5 mol%) and CoO (2.5 and 5 mol%). The results revealed that the increase in precalcination temperature from 400 to 600 °C and Li₂O-doping of CuO/Fe₂O₃ system enhanced CuFe₂O₄ formation. However, heating both pure and doped solids at 600 °C did not lead to complete conversion of reacting oxides into CuFe₂O₄. The promotion effect of Li₂O dopant was attributed to dissolution of some of dopant ions in the lattices of CuO and Fe₂O₃ with subsequent increase in the mobility of reacting cations. CoO-doping led also to the formation of mixed ferrite Co_xCu_1−xFe₂O₄. The doping process of the system investigated decreased to a large extent the crystallite size of unreacted portion of Fe₂O₃ in mixed solids calcined at 600 °C. This process led to a significant increase in the S_BET of the treated solids. Doping CuO/Fe₂O₃ system with either Li₂O or CoO, followed by calcination at 400 and 600 °C decreased its catalytic activity in CO-oxidation by O₂. However, the activation energy of the catalyzed reaction was not much affected by doping.     

Synthesis and surface modified hard magnetic properties in Co0.5Pt0.5 nanocrystallites from a rheological liquid precursor

Small crystallites of a metastable phase Co_0.5Pt_0.5 are precipitated by heating a rheological liquid precursor of cobalt–hydrazine complex and platinum chloride H₂PtCl₆·xH₂O in polymer molecules of poly(vinylpyrrolidone) (PVP) in ethylene glycol. The hydrazine co-reduces nascent atoms from the Co²⁺ and Pt⁴⁺ that recombine and grow as Co_0.5Pt_0.5. The PVP molecules cap a growing Co_0.5Pt_0.5 as it achieves a critical size so that it stops growing further in given conditions. X-ray diffraction pattern of a recovered powder reveals a crystalline Co_0.5Pt_0.5 phase (average crystallite size D∼8 nm) of a well-known Fm3m-fcc crystal structure with the lattice parameter a=0.3916 nm (density ρ=14.09 g/cm³). A more ordered L1₀ phase (ρ=15.91 g/cm³) transforms (D≥25 nm) upon annealing the powder at temperature lesser than 700 °C (in vacuum). At room temperature, the virgin crystallites bear only a small saturation magnetization M_s=5.54 emu/g (D=8 nm) of a soft magnet and it hardly grows on bigger sizes (D≤31 nm) in a canted ferromagnetic structure. A rectangular hysteresis loop is markedly expanded on an optimally annealed L1₀ phase at 800 °C for 60 min, showing a surface modified coercivity H_c=7.781 kOe with remnant ratio M_r/M_s=0.5564, and M_s=39.75 emu/g. Crystallites self-assembled in an acicular shape tailor large H_c from ideal single domains and high magnetocrystalline anisotropy of a hard magnet L1₀ phase.     

Characterization of AgInS2 thin films prepared by vacuum evaporation

We characterized AgInS₂ thin films prepared by vacuum evaporation. In the case of thin films annealed at 400 °C, diffraction peaks were observed only for the chalcopyrite AgInS₂ phase. The chemical composition of the thin films annealed at 400 °C was 26.5 at% Ag, 23.8 at% In, and 49.7 at% S. PL spectra of the AgInS₂ thin films at 10.7 K showed peaks at 1.70, 1.80, and 1.83 eV. The PL peak at1.80 eV was attributed to sulfur deficiency.     

Effects of Nb substitution for Zr on the phases,microstructure and magnetic properties of Co80Zr18−xNbxB2 melt-spun ribbons

The phases, microstructure, and magnetic properties of Co₈₀Zr_18−xNb_xB₂ (x=1, 2, 3, and 4) melt-spun ribbons were investigated. The small substitution of Nb for Zr in the Co–Zr–B melt-spun ribbons resulted in the improvement of magnetic properties, especially the coercivity. The main effect of added Nb on the coercovity of Co–Zr–Nb–B melt-spun ribbons, originated from modification of the grain size of Co₁₁Zr₂ phase. The coercivity of the Co–Zr–Nb–B melt-spun ribbons depends on the annealing temperature. The optimal magnetic properties of H_c=5.1 kOe, and (BH)_max=3.4 MGOe were obtained in the Co₈₀Zr₁₅Nb₃B₂ melt-spun ribbons annealed at 600 °C for 3 min.     

Influence of substrate temperature on structures and dielectric properties of pyrochlore Bi1.5Zn1.0Nb1.5O7 thin films prepared by pulsed laser deposition

The influence of substrate temperature on structural and dielectric properties of cubic pyrochlore Bi_1.5Zn_1.0Nb_1.5O₇ (BZN) thin films prepared by pulsed laser deposition process has been investigated. BZN thin films were deposited on Pt/Ti/SiO₂/Si(1 0 0) substrate and in situ annealed at 700 °C. The results indicate that the substrate temperature has a significant effect on the structural and dielectric properties of BZN thin films. The films exhibit a cubic pyrochlore structure in the substrate temperature range from 550 °C to 700 °C and at the annealing temperature of 700 °C. With further increase of substrate temperature to 750 °C, the phases of Bi₂O₃, BiNbO₄ and Bi₅Nb₃O₁₅ can be detected in the XRD pattern due to the Zn loss. The dielectric constant and loss tangent of the films deposited at 650 °C are 192 and 6 × 10⁻⁴ at 10 kHz, respectively. The tunability is 10% at a dc bias field of 0.9 MV/cm.     

High-temperature oxidation resistance and magnetic properties of Si-doped Sm2Co17-type magnets at 500 °C

The high-temperature oxidation resistance and magnetic properties of Si-doped Sm₂Co₁₇-type magnets at 500 °C were systematically investigated. The Sm(Co_0.76, Fe_0.1, Cu_0.1, Zr_0.04)₇Si_x (x=0–0.6) magnets were prepared by the conventional powder metallurgical technique. It is found that the addition of silicon in the Sm₂Co₁₇-type magnet can remarkably improve its oxidation resistance. Moreover, a small amount of silicon addition can also increase its high-temperature intrinsic coercivity. A maximum intrinsic coercivity of 6.7 kOe at 500 °C was obtained for the Sm₂Co₁₇-type magnet with Si content x=0.4, whose high-temperature maximum energy product loss was about 2.5 times smaller than pure Sm₂Co₁₇-type magnet after oxidation at 500 °C for 100 h, indicating the enhanced oxidation resistance. Its corresponding Curie temperature and saturation magnetization are about 723.9 °C and 7.4 kG, respectively.     

Magnetic,structural and electrical properties of ordered and disordered Co50Fe50 films

Co₅₀Fe₅₀ films with thickness varying from 100 to 500 Å were deposited on a glass substrate by sputtering process, respectively. Two kinds of CoFe films were studied: one was the as-deposited film, and the other the annealed film. The annealing procedure was to keep the films at 400 °C for 5 h in a vacuum of 5×10⁻⁶ mbar. From the X-ray study, we find that the as-deposited film prefers the CoFe(1 1 0) orientation. Moreover, the body-centered cubic (bcc) CoFe(1 1 0) line is split into two peaks: one corresponding to the ordered body-centered tetragonal (bct) phase, and the other, the disordered bcc phase. After annealing, the peak intensity of the ordered bct phase becomes much stronger, while that of the disordered bcc phase disappears. The annealing has also caused the ordered CoFe(2 0 0) line to appear. When the amount of the ordered bct phase in Co₅₀Fe₅₀ is increased, the saturation magnetization (M_s) and coercivity (H_c) become larger, but the electrical resistivity (ρ) decreases. From the temperature coefficient of resistance (TCR) measurement, we learn that the bct grains in the CoFe film start to grow at temperature 82 °C.     

Thermoluminescent and stuctural properties of BaAl2O4:Eu,Nd,Gdphosphors prepared by combustion method

BaAl₂O₄:Eu²⁺,Nd³⁺,Gd³⁺ phosphors were prepared by a combustion method at different initiating temperatures (400–1200 °C), using urea as a comburent. The powders were annealed at different temperatures in the range of 400–1100 °C for 3 h. X-ray diffraction data show that the crystallinity of the BaAl₂O₄ structure greatly improved with increasing annealing temperature. Blue-green photoluminescence, with persistent/long afterglow, was observed at 498 nm. This emission was attributed to the 4f⁶5d¹–4f⁷ transitions of Eu²⁺ ions. The phosphorescence decay curves were obtained by irradiating the samples with a 365 nm UV light. The glow curves of the as-prepared and the annealed samples were investigated in this study. The thermoluminescent (TL) glow peaks of the samples prepared at 600 °C and 1200 °C were both stable at ∼72 °C suggesting that the traps responsible for the bands were fixed at this position irrespective of annealing temperature. These bands are at a similar position, which suggests that the traps responsible for these bands are similar. The rate of decay of the sample annealed at 600 °C was faster than that of the sample prepared at 1200 °C.     

Nuclear resonant time spectra for Sn in Co2TiSn Heusler alloy films

Co₂TiSn Heusler alloy films were grown on MgO substrates at the substrate temperature between 200 and 600 °C using atomically controlled alternate deposition and magnetic hyperfine field at the Sn nuclei was measured by the Mössbauer spectroscopy and the nuclear resonant scattering method. The relation between the hyperfine field and the structural disorder estimated by X-ray diffraction measurements was also examined. The results showed that the sample prepared at higher substrate temperature has higher degree of L2₁ order and larger hyperfine field. For the Co₂TiSn film grown at 600 °C, the hyperfine field estimated from the oscillatory pattern of the nuclear resonant time spectra was 6.1 T at room temperature and increased with a decrease of temperature to 7.5, 8.1, and 8.3 T at 200, 100, and 5 K, respectively, which shows that the film prepared by this method and condition has almost the same magnetization value and Curie temperature as bulk samples.     

Effect of annealing on magnetoimpedance of Co68Fe4Zr10Cu2B16 ribbons

Magnetoimpedance (MI) in Co₆₈Fe₄Zr₁₀Cu₂B₁₆ alloy has been investigated in the frequency range 500 kHz–5 MHz and with the application of external steady magnetic field in the longitudinal direction, up to 100 Oe. MI measurements were carried out on as-cast ribbons and also on conventionally annealed and Joule-annealed ribbons. In as cast ribbons, the maximum MI observed is 13% at a frequency of 500 kHz and it decreases to 5% and 4% with conventional annealing at 100 °C and 150 °C, respectively. On the other hand, MI decreases to 8% and 6% with Joule annealing employing currents of 100 mA and 200 mA, respectively. However, Joule annealing with the application of a magnetic field of 5–10 Oe in the transverse direction causes the MI to decrease to 12% and 11% for currents of 100 mA and 200 mA, respectively. In the as-cast ribbons, double peak behavior is observed in all the frequencies whereas, in the annealed ribbons, double peak behavior in general is observed only at high frequencies.     

Ferromagnetism at 300 K in spin-coated films of Co doped anatase and rutile-TiO2

Thin films of Ti_1−xCo_xO₂ (x=0 and 0.03) have been prepared on sapphire substrates by spin-on technique starting from metalorganic precursors. When heat treated in air at 550 and 700 °C, respectively, these films present pure anatase and rutile structures as shown both by X-ray diffraction and Raman spectroscopy. Optical absorption indicate a high degree of transparency in the visible region. Such films show a very small magnetic moment at 300 K. However, when the anatase and the rutile films are annealed in a vacuum of 1×10⁻⁵ Torr at 500 and 600 °C, respectively, the magnetic moment, at 300 K, is strongly enhanced reaching 0.36μ_B/Co for the anatase sample and 0.68μ_B/Co for the rutile one. The ferromagnetic Curie temperature of these samples is above 350 K.     

Spin polarization measurements of Co2Mn (Ga0.5Sn0.5) thin films

Co₂MnGa_0.5Sn_0.5 (CMGS) thin films were epitaxially grown on MgO (0 0 1) substrates by magnetron sputtering and the current spin polarizations of the films with different post annealing conditions were measured by the point contact Andreev reflection method. The film deposited at a substrate temperature of 150 °C had a B2 structure and its spin polarization was estimated to be 59%. The film was ordered to the L2₁ structure by annealing at 600 °C, and the spin polarization was enhanced to 66%. The spin polarization and the intensity of the L2₁ diffraction showed clear correlation, suggesting L2₁ ordering is essential to achieve higher spin polarization of this quaternary Heusler alloy.     

Microstructures and magnetic properties of CoPt-TiO2 nanocomposite films prepared by annealing CoPt/TiO2 multilayers

CoPt-TiO₂ nanocomposite films were synthesized by rapid thermal annealing of CoPt/TiO₂ multilayers. The effects of annealing temperature, annealing time, Ag addition and TiO₂ volume fraction on the microstructures and magnetic properties of the CoPt-TiO₂ nanocomposite films were studied. Results showed that the ordering degree of CoPt and coercivity of CoPt-TiO₂ nanocomposites increased with annealing temperature. Increasing annealing time and Ag addition were able to increase the ordering degree and coercivity of CoPt. However, complete L1₀-ordering of CoPt at 550 °C annealing was not realized by increasing annealing time up to 30 min and Ag addition up to 30 vol.%. Increasing TiO₂ volume fraction at 700 °C annealing did not lead to the change of ordering of CoPt. However, the grain structure of the films changed slightly when TiO₂ volume fraction was larger than 56%. The coercivity of the film decreased slightly with the addition of TiO₂.     

Stabilization of a very high-k crystalline ZrO2 phase by post deposition annealing of atomic layer deposited ZrO2/La2O3 dielectrics on germanium

The impact of the ZrO₂/La₂O₃ film thickness ratio and the post deposition annealing in the temperature range between 400 °C and 600 °C on the electrical properties of ultrathin ZrO₂/La₂O₃ high-k dielectrics grown by atomic layer deposition on (1 0 0) germanium is investigated. As-deposited stacks have a relative dielectric constant of 24 which is increased to a value of 35 after annealing at 500 °C due to the stabilization of tetragonal/cubic ZrO₂ phases. This effect depends on the absolute thickness of ZrO₂ within the dielectric stack and is limited due to possible interfacial reactions at the oxide/Ge interface. We show that adequate processing leads to very high-k dielectrics with EOT values below 1 nm, leakage current densities in the range of 0.01 A/cm², and interface trap densities in the range of 2-5 × 10¹² eV⁻¹ cm⁻².     

Charge-discharge characteristics of nanocrystalline Co3O4 powders via aerosol flame synthesis

Nanocrystalline Co₃O₄ powders were synthesized by aerosol flame synthesis (AFS) method for the anode of lithium ion batteries and the basic electrochemical properties were investigated. The effects of synthesis conditions and heat-treatment temperature on the morphology, crystallite size and electrochemical properties were investigated. As-prepared soot contained Co₃O₄, CoO and Co(OH)₂, which were eventually converted into cubic spinel Co₃O₄ by post heat treatment. The as-prepared particle size was in the range of 10-30 nm and grew to 50-85 nm by the heat treatment. With growing particle size and improved crystallinity, charge-discharge capacity and cycle performance were improved and the discharge capacity of the powder heat-treated at 700 °C was 571 mAh/g after 30 cycles, which was better than Co₃O₄ powder reported in the previous literature.