钠离子电池正极材料Na2MnPO4F的23Na MAS NMR谱研究

Na₂MnPO₄F材料是一种很有发展前景的钠离子电池正极材料,本文通过非原位XRD和固体核磁共振技术研究该材料充放电结构变化（晶体结构与局域Na位）. 非原位XRD测试发现,充电过程在2θ为31^o和36^o左右出现新的衍射峰,表明钠脱出后电极上有中间相物质生成. ²³Na MAS NMR谱图的-209 ppm、-258 ppm和-295 ppm三个谱峰分别对应于该材料结构中Na1 + Na2位、Na3位和Na4位. 非原位²³Na MAS NMR谱研究发现,充电过程中-209 ppm处信号峰面积比例减小,表明Na1和Na2位的Na比Na3和Na4位先脱出. 充电至4.2 V,-132 ppm和-330 ppm处出现中间相物质的信号峰;而放电过程则相反.     

Sodium ion-conducting solid electrolytes in the system Na3PO4Na2SO4

In the system Na₃PO₄Na₂SO₄, the high-temperature, cubic γ form of Na₃PO₄ forms an extensive range of solid solutions: Na_3−x(P_1−xS_x)O₄, 0 < x < (0.57 to 0.70, depending on temperature). For compositions in the range x = ca. 0.33 to 0.57, these γ solid solutions are thermodynamically stable at all temperatures. The conductivity of the γ solid solutions increases with increasing x and reaches a maximum at x = 0.5 to 0.6, with values of 2 × 10⁻⁵ ohm⁻¹ cm⁻¹ at 100°C, rising to 1.3 × 10⁻² ohm⁻¹ cm⁻¹ by 300°C; this conductivity increase with x is attributed to an increase in the sodium ion vacancy concentration, associated with the solid solution mechanism Na + PS. The phase diagram for the system Na₃PO₄Na₂SO₄ is given together with lattice parameters of the γ solid solutions.     

复盐K3Na(SO4)2的热化学研究

钾芒硝是一种成因复杂的复盐[1～ 3 ] ,并且由于钾芒硝Ｋ3 Ｎａ(ＳＯ4 ) 2 与硫酸钾石 [Ｋ3 Ｎａ(ＳＯ4 ) 2 或Ｎａ2 ＳＯ4 ·3Ｋ2 ＳＯ4 ]的化学组成相同 ,未能确定二者是否属于同一种复盐[4 ,5] 。我们合成了复盐Ｋ3 Ｎａ(ＳＯ4 )2[3 ] ,用溶解量热法测定了Ｋ3 Ｎａ(ＳＯ4 )2 和反应物 [Ｎａ2 ＳＯ4 (ｓ) +Ｋ2 ＳＯ4 (ｓ) ]的溶解焓 ,通过设计热化学循环计算出复盐的标准生成焓 ,为我们了解钾芒硝和硫酸钾石是否为同一复盐 ,并为进一步研究其成因和组成提供参考。1　实验部分1 1　试剂与仪器Ｋ2 ＳＯ4 (ｓ)和Ｎａ2 ＳＯ4 (ｓ)为Ａ .Ｒ .…     

25 oC下Na2CO3/Na2SO4/NaCl混合盐的溶解动力学研究

研究了25℃时,搅拌速度,加样量及氯化钠的量等不同实验条件下,Na2CO3, Na2SO4, NaCl混合盐的溶解过程,对不同时刻液相的化学组成进行分析并鉴定其平衡时的固相,结果表明：混合盐溶解前期搅拌速度占主导因素,当溶液中三种盐达到一定浓度后,同离子效应占主导因素,随着加样量的增加,碳酸钠和硫酸钠浓度达到一定程度之后反应生成碳钠矾。结合动力学模型计算得到体系中NaCl的溶解动力学方程,得出在25℃条件下溶解符合Stumm模型,溶解过程属于扩散过程控制,同时还伴随着界面反应和化学反应。     

三元体系Na2SO4-CuSO4-H2O 25 ℃活度系数的研究

用自制的Hg-Hg_2SO_4电极和Na离子选择性电极, 在25 ℃和离子强度分别为1.0和2.0的条件下, 测定了Na_2SO_4在Na_2SO_4和CuSO_4混合水溶液中的平均活度系数。对所使用的电极组的热力学响应、重现性等性能进行了检验。根据文献提供的Pitzer方程, 推导了计算Na_2SO_-CuSO_4-H_2O体系中Na_2SO_4和CuSO_4平均活度系数的表达式, 求出了Pitzer混合参数和Harned方程系数, 计算了CuSO_4在该体系中的平均活度系数。     

An investigation of the polythermal diagram of the H2ONa2HPO4Na2SO4 system

The polythermal diagram of the ternary system H₂ONa₂HPO₄Na₂SO₄ has been established, setting up nine isotherms obtained between 0 and 25°C by conductimetric analysis. The solubility domains of the various solid phases have been determined. One eutectic, three stable and one metastable transitional transformations have been observed. Temperature and composition of the eutectic point have been obtained by thermal analysis at constant flow.     

Na2S溶液吸收低浓度SO2的动力学研究

近几年来我国城市空气质量虽有所改善,但改善幅度不大.2004年我国SO2排放量达2254.9万吨,出现酸雨的城市比上年增加了2.1个百分点[1].     

碱性水溶液中4Na2SO4·2H2O2·NaCl的分解动力学

以低浓度(30(wt)%)的双氧水制备了硫酸钠-过氧化氢-氯化钠加合物,各组分的含量均接近于理论值,其纯度为99.3%;在323K和333K下,研究了4Na2SO4*2H2O2*NaCl于碱性水溶液中的分解动力学.结果表明,在不同条件下,其分解均为一级反应;随着温度和pH的增加,其分解速率加快.置信水平为95%时k和C0的联合置信域均为椭圆形且面积较小,求得的参数精确度较高;优化出的模型能较准确地描述4Na2SO4*2H2O2*NaCl于碱性水溶液中的分解过程.     

Phase equilibria of the Na,K,Mg,Ca//SO4,Cl-H2O system at 50°C in the crystallization range of glaserite 3K2SO4·Na2SO4

Phase equilibria of the Na,K,Mg,Na,K,Mg,Ca//SO₄,Cl-H₂O system are studied at 50°C via translation in the crystallization range of glaserite (3K₂SO₄ · Na₂SO₄). It is found that glaserite as the equilibrium phase of the investigated system at 50°C participates in the formation of 21 invariant points, 21 monovariant curves, and 34 divariant fields. A fragment of the phase equilibria diagram of the investigated system is constructed in the crystallization range of glaserite.     

多核NMR在相图研究中的应用——NaCl-NH4Cl-H2O体系的23Na、14N NMR研究

In the present paper, preliminary application of NMR to phase diagram study was reported. A multinuclear NMR quantitative method was developed. NaCl- NH_4Cl-H_2O system was studied by ~(23)Na and ~(14)N NMR. It has been shown that the multinuclear NMR quantitative method has its advantages when studying systems of multi-components.     

Chemical effects induced by γ-irradiated Na2SO4 in aqueous ammonium nitrate

It is well known that paramagnetic centers are formed when Na₂SO₄ crystals are exposed to -radiation. The dissolution of such crystals in aqueous ammonium nitrate results in reduction of nitrate to nitrite. Various factors which influence the yield of nitrite are investigated. The yield of nitrite is found to vary with the amount of irradiated Na₂SO₄ added, the dose absorbed by Na₂SO₄ crystals, the storing period of the irradiated salt, photoannealing time, concentration of aqueous ammonium nitrate and particle size of the Na₂SO₄ crystals. The G(NO ₂ ^– ) value under optimum conditions of the conversion of nitrate to nitrite by irradiated Na₂SO₄ in aqueous ammonium nitrate is 0.009. The efficiency of energy transfer is 1.5%. The mechanism of reduction is based on the reactions of paramagnetic centers with nitrate ions.     

KPS—CuSO4—Na2SO3参与的无皂液聚合

研究了MMA-St在氧化还原引发剂KPS-CuSO_4-Na_2SO_3存在下的快速无皂乳液聚合.当[MMA]=0.51mol/L、[St]=0.49 mol/L、70℃对,在[KPS]=2.77×10~(-3)mol/L、[CuSO_4]=1.50×10~(-5)mol/L、[Na_2SO_3]=2.77×10~(-3) mol/L条件下反应100min,转化率大于90％;讨论了胶乳的分子量及其分布;求出了聚合反应活化能E_a=81.6 kJ/mol和聚合反应速率常数k_p=321.9 L/mol·s.     

Na2O2和SO2反应原理的实验探索

高中化学(必修)第一册分别简单介绍了有关Na2O2和SO2的一些知识，但没有涉及Na2O2与SO2之间如何反应的问题。为此，已有一些同志作了实验研究，文章认为Na2O2和SO2反应生成Na2O2，但在实验设计过程中没有验证是否产生O2，没有检验生成物中是否存在SO3^2-。     

Experimental Study on Phase Equilibria in Na2B4O7–Na2SO4–H2O and Li2B4O7–Na2B4O7–H2O Aqueous Ternary Systems at 273 K

Russian Journal of Physical Chemistry A - The solubility data for ternary systems Na2SO4–Na2B4O7–H2O and Li2B4O7–Na2B4O7–H2O at 273 K were obtained experimentally by the...     

银电极在Na2SO4溶液中氧化还原过程的原位拉曼光谱研究

采用原位拉曼光谱结合循环伏安法研究银电极在０．１ｍｏｌ／Ｌ的Ｎａ２ＳＯ４溶液中不同电位下的氧化还原过程，在电位扫描过程中，实时记录的拉曼光谱表明，电极表面在０．２Ｖ开始生成吸附原子氧物种，当电位正于０．４Ｖ，部分吸附的原子氧扩散进入电极的亚表面区，而另一些则通过强的化学吸附与银表面成键；同时部分银氧化为＋１价，各谱带的产生和消失与氧化还原电流峰有很好的对应关系，表明电化学原位拉曼光谱能在分子水平上     

掺杂NASICON系统的23Na NMR研究

化合物Na3Zr2Si2PO12。是由ZrO6八面体与SiO4或PO4四面体共角构成的开放三维骨架结构，Na 位于骨架间隙，称之为NASICON（NaSuperIoaicConductor），具有和Na－Al2O3相似的离子电导率（在300℃时，σ＝0．2Ω－1·cm-1［1］但是由于该化合物在100－2000℃间存在单斜一、立方的可逆相变，使其应用受到限制．为了抑制这种相变，已进行了骨架掺杂的研究工作，制备出了多种化学掺杂的NASICON系统［2］．在Na3Zr2Si2PO12化合物中，三个Na十分别位于结构中两个不同的位置，然而掺杂以后，骨架结构发生变化，这时Na十位置，将关系…     

Thermodynamic properties and molecular dynamics of (NH4)2Zn(SO4)2·6H2O studied by single-crystal NMR and MAS NMR

The thermodynamic properties and molecular dynamics of (NH₄)₂Zn(SO₄)₂·6H₂O were investigated using thermogravimetric analysis, differential scanning calorimetry, and nuclear magnetic resonance observations. The first mass loss occurs near 350 K (= T _d) and is interpreted as the onset of partial thermal decomposition. The temperature dependences of the spin–lattice relaxation time in laboratory frame T ₁ and in rotating frame T _1ρ for H nuclei were studied near T _d and T _C1. The increase in T ₁ near T _d seems to be related to the ammonium protons, and the abrupt decrease in T _1ρ near T _d can be explained due to the loss of H₂O.     

BeSO4-Al2(SO4)3-Na2SO4三元熔盐体系相图的研究

热分析法研究了BeSO₄-Al₂(SO₄)3-Na₂SO₄三元熔盐体系的状态图。体系中存在三元转熔(包晶)点P,温度490℃,组成为BeSO₄18.8Wt%,Al₂(SO₄)₃15.0%,Na₂SO₄66.2%;三元低共熔(共晶)点E₁,温度为476℃,组成为BeSO₄20.0%,Al₂(SO₄)₃11.2,%,Na₂SO₄68.8%。另一低共熔点E₂温度为595℃,组成未能确定。体系中无三元化合物生成。