Effects of thermal annealing on the structural and optical properties of Mg(x)Zn(1-x)O nanocrystals

Mg(x)Zn(1-x)O ternary alloy nanocrystals with hexagonal wurtzite structures were fabricated by using the sol-gel method. X-ray diffraction patterns, UV-vis absorption spectra, and photoluminescence spectra were used to characterize the structural and optical properties of the nanocrystals. For as-prepared nanocrystals, the band gap increases with increasing Mg content. Weak excitonic emission with strong deep-level emission related to oxygen vacancy and interface defects is observed in the photoluminescence spectra at room temperature. Thermal annealing in oxygen was used to decrease the number of defects and to improve the quality of the nanocrystals. In terms of XRD results, the grain sizes of nanocrystals increase with increasing annealing temperature and the lattice constants of alloy are smaller than those of pure ZnO. The band gap becomes narrower with increasing annealing temperature. For Mg(x)Zn(1-x)O nanocrystals (x=0.03-0.15) annealed at temperatures ranging from 500 to 1000 degrees C, intense near-band-edge (NBE) emissions and weak deep-level (DL) emissions are observed. Consequently, the quality of Mg(x)Zn(1-x)O nanocrystals can be improved by thermal annealing.     

Ce-doped ZnO (Ce(x)Zn(1-x)O) becomes an efficient visible-light-sensitive photocatalyst by co-catalyst (Cu2+) grafting

We have fabricated an efficient visible-light-sensitive Cu(2+)-grafted Ce-doped ZnO photocatalyst (Cu(2+)-Ce(x)Zn(1-x)O) by adopting a metal ion doping and co-catalyst modification. Impurity states were formed below the conduction band (CB) edge in Ce(x)Zn(1-x)O, and these impurity states induce the visible-light absorption. Ce(x)Zn(1-x)O without a Cu(2+)-co-catalyst showed negligible visible-light activity due to the low reduction power of electrons in impurity levels. Surprisingly, Cu(2+)-modification over Ce(x)Zn(1-x)O drastically increased its visible-light activity. Excited electrons in impurity states can transfer to the Cu(2+)-ions on the surface and form Cu(2+)/Cu(+) redox couples, which cause the efficient oxygen reduction through a multi-electron reduction process. One of the striking features of the present study is that the metal doped semiconductors which were inactive due to their impurity states become efficient visible-light photocatalysts upon co-catalyst modification. The successful strategy used here for designing a highly active visible-light photocatalyst would provide numerous opportunities to develop an efficient metal-ion based visible-light photocatalyst.     

Local structural distortion of BaZr(x)Ti(1-x)O3 nanocrystals synthesized at room temperature

Single crystalline, sub-15 nm BaZr(x)Ti(1-x)O(3) (0 ≤x≤ 1) nanocrystals were synthesized at room temperature via the vapor diffusion sol-gel method. As-prepared nanocrystals exhibit noncentrosymmetric regions whose volume fraction increases significantly upon substitution of small amounts of Zr(4+) for Ti(4+) and reaches a maximum for substitution levels ranging from 10 to 20 mol%.     

Ferromagnetism in colloidal Mn2+ -doped ZnO nanocrystals

High-temperature hydrolysis of Zn(II) and Mn(II) alkoxides in a high boiling point solvent in the presence of surfactants was used to prepare surfactant-coated Zn(1-x)Mn(x)O nanocrystals with average size of 5.5 nm and x = 0.04 +/- 0.03. The magnetic properties of the nanocrystals were measured both for isolated particles diluted in a hydrocarbon matrix and for a nanocrystal powder. Nanocrystals of manganese oxide and ZnO coated with manganese oxide were prepared for comparison to the Zn(1-x)Mn(x)O nanocrystals. We find that the manganese ions primarily substitute zinc ions in the hexagonal ZnO lattice, and part of them are ferromagnetically coupled up to room temperature even in isolated noninteracting nanocrystals. The rest of the ions are magnetically disordered or uncoupled. Surprisingly, these small Zn(1-x)Mn(x)O nanocrystals poses relatively large low-temperature magnetic coercivity and relatively high blocking temperature in the isolated form, which indicate large magnetic anisotropy. In the nanocrystal powder the coercive field decreased significantly. This study highlights the advantages of working with noninteracting single domain particles of these intriguing materials.     

Magnetic and high rate adsorption properties of porous Mn(1-x)Zn(x)Fe2O4 (0 ≤ x ≤ 0.8) adsorbents

Porous spinel ferrites Mn(1-x)Zn(x)Fe(2)O(4) (0 ≤ x ≤ 0.8) are synthesized by a simple sol-gel method with egg white. All samples exhibit porous morphologies and large BET surface area (S(BET)). The substitution of Zn(2+) affects the magnetic properties of ferrites and the adsorption properties of methylene blue (MB) on ferrites, obviously. The saturation magnetization (Ms) of Mn(1-x)Zn(x)Fe(2)O(4) increases before x=0.4, and decreases with further increase of Zn(2+) substitution. This can be ascribed to the changes of the cationic distribution and the variation of spin arrangement in A-site and B-site of spinel structure. All samples show high adsorption capacity and the removal efficiencies of MB reach up to >90% within 3 h. The Zn(2+) substitution accelerates the adsorption rate and capacity of MB on Mn(1-x)Zn(x)Fe(2)O(4). The quickest adsorption occurred at x=0.2 and the largest adsorption capacity occurred at x=0.8.     

Optical properties of cation-substituted zinc oxide

Zinc oxide (ZnO)-based optoelectronics has emerged as a frontier area in semiconductor research in recent years. In the design of ZnO-based optoelectronic devices, cation-substituted ZnO serves as essential components for the desired device functions. Band-gap engineering by cation substitution enables the facile preparation of barrier layers and quantum wells in device structures. Wurtzite solid solutions Zn 1- x Mg x O, Zn 1- x Cd x O, and Zn 1- x Be x O have been reported as examples where band gaps are gradually modulated as functions of x. In this contribution, we present an overview of composition-dependent band-gap variations of Zn 1- x M x O solid solutions. In addition, we describe the optical properties and microstructural evolution in polycrystalline Zn 1- x Mg x O (0 相似文献   

Highly mixed phases in ball-milled Cu/ZnO catalysts: an EXAFS and XANES study

New highly mixed phases have been identified in Cu/ZnO systems by EXAFS and XANES at both the Cu and Zn K-edge. The phases were generated by ball-milling Cu(2)O/ZnO mixtures under three different atmospheres of synthetic air (SA), SA + CO(2) and CO(2). The system milled in CO(2) shows disproportionation of Cu(2)O into Cu(0), Cu(1+) (cuprite Cu(2)O-type phase) and Cu(2+) (tenorite CuO-type phase), while most of the Zn(2+) is transformed into a nanocrystalline/amorphous ZnO-type zincite that forms a superficial mixture of oxide and carbonate phases. When synthetic air is added to the CO(2) atmosphere, ball milling results in the oxidation of nearly half the Cu(1+) into Cu(2+) with no Cu metal formed. The copper phase in this material is almost entirely amorphous. In SA, a significant amount of Cu(2+)- and Zn(2+)-based phases appears to react to form a nanocrystalline/amorphous Cu(1-x)Zn(x)O (x approximately 0.3) solid solution. This distorted rock saltlike solid solution, in which Zn and Cu feature different octahedral environments, was never reported before. It is thought to be formed by incorporation of Zn(2+) in the Cu fcc sublattice of the cuprite Cu(2)O matrix and the concomitant oxidation of Cu(1+) into Cu(2+). The formation of such a highly mixed Cu(1-x)Zn(x)O phase indicates strong Cu/Zn interaction in the Cu/ZnO system, which also suggests the presence of highly mixed phases in conventionally prepared activated catalysts.     

Design of energy band alignment at the Zn(1-x)Mg(x)O/Cu(In,Ga)Se2 interface for Cd-free Cu(In,Ga)Se2 solar cells

The electronic band structure at the Zn(1-x)Mg(x)O/Cu(In(0.7)Ga(0.3))Se(2) interface was investigated for its potential application in Cd-free Cu(In,Ga)Se(2) thin film solar cells. Zn(1-x)Mg(x)O thin films with various Mg contents were grown by atomic layer deposition on Cu(In(0.7)Ga(0.3))Se(2) absorbers, which were deposited by the co-evaporation of Cu, In, Ga, and Se elemental sources. The electron emissions from the valence band and core levels were measured by a depth profile technique using X-ray and ultraviolet photoelectron spectroscopy. The valence band maximum positions are around 3.17 eV for both Zn(0.9)Mg(0.1)O and Zn(0.8)Mg(0.2)O films, while the valence band maximum value for CIGS is 0.48 eV. As a result, the valence band offset value between the bulk Zn(1-x)Mg(x)O (x = 0.1 and x = 0.2) region and the bulk CIGS region was 2.69 eV. The valence band offset value at the Zn(1-x)Mg(x)O/CIGS interface was found to be 2.55 eV after considering a small band bending in the interface region. The bandgap energy of Zn(1-x)Mg(x)O films increased from 3.25 to 3.76 eV as the Mg content increased from 0% to 25%. The combination of the valence band offset values and the bandgap energy of Zn(1-x)Mg(x)O films results in the flat (0 eV) and cliff (-0.23 eV) conduction band alignments at the Zn(0.8)Mg(0.2)O/Cu(In(0.7)Ga(0.3))Se(2) and Zn(0.9)Mg(0.1)O/Cu(In(0.7)Ga(0.3))Se(2) interfaces, respectively. The experimental results suggest that the bandgap energy of Zn(1-x)Mg(x)O films is the main factor that determines the conduction band offset at the Zn(1-x)Mg(x)O/Cu(In(0.7)Ga(0.3))Se(2) interface. Based on these results, we conclude that a Zn(1-x)Mg(x)O film with a relatively high bandgap energy is necessary to create a suitable conduction band offset at the Zn(1-x)Mg(x)O/CIGS interface to obtain a robust heterojunction. Also, ALD Zn(1-x)Mg(x)O films can be considered as a promising alternative buffer material to replace the toxic CdS for environmental safety.     

Effects of Mg concentration on solubility and chemical state of N in N-doped MgZnO alloy

Solubility and chemical state of N in an N-doped Mg(x)Zn(1-x)O film were studied by using Raman and x-ray photoelectron spectroscopy. Three anomalous Raman peaks are observed at 272, 580, and 642 cm(-1), respectively, and are demonstrated to be only related to substitution of N for O site (N(O)) but not to substitution of N(2) for O site (N(2))(O). The solubility of the N(O) is dominated by Mg concentration and chemical potentials of N and O in growth condition. The chemical state of the N can change from coexistence of (N(2))(O) and N(O) to single (N(2))(O) with increasing Mg concentration.     

Overall water splitting on (Ga(1-x)Zn(x))(N(1-x)O(x)) solid solution photocatalyst: relationship between physical properties and photocatalytic activity

The physical and photocatalytic properties of a novel solid solution between GaN and ZnO, (Ga(1-x)Zn(x))(N(1-x)O(x)), are investigated. Nitridation of a mixture of Ga(2)O(3) and ZnO at 1123 K for 5-30 h under NH(3) flow results in the formation of a (Ga(1-x)Zn(x))(N(1-x)O(x)) solid solution with x = 0.05-0.22. With increasing nitridation time, the zinc and oxygen concentrations decrease due to reduction of ZnO and volatilization of zinc, and the crystallinity and band gap energy of the product increase. The highest activity for overall water splitting is obtained for (Ga(1-x)Zn(x))(N(1-x)O(x)) with x = 0.12 after nitridation for 15 h. The crystallinity of the catalyst is also found to increase with increasing the ratio of ZnO to Ga(2)O(3) in the starting material, resulting in an increase in activity.     

Structural, optical, and magnetic properties of Mn-doped ZnO thin film

The Zn(1-x)Mn(x)O (x = 0, 0.16, and 0.25) thin films were grown on fused quartz substrates by reactive magnetron cosputtering. X-ray-diffraction measurement revealed that all the films were single phase and had wurtzite structure with c-axis orientation. As Mn concentration increased in the Zn(1-x)Mn(x)O films, the c-axis lattice constant and band-gap energy increased gradually. In Raman-scattering studies, an additional Mn-related vibration mode appeared at 520 cm(-1). E(2H) phonon line of Zn(1-x)Mn(x)O alloy was broadened asymmetrically and redshifted as a result of microscopic structural disorder induced by Mn(2+) random substitution. The Zn(0.84)Mn(0.16)O film exhibited a ferromagnetic characteristic with a Curie temperature of approximately 62 K. However, with increasing Mn concentration to 25 at. %, ferromagnetism disappeared due to the enhanced antiferromagnetic superexchange interactions between neighboring Mn(2+) ions.     

Effect of explicit cationic size and valence constraints on the phase stability of 1:2 B-site-ordered perovskite ruthenates

The related parameters of cation size and valence that control the crystallization of Sr(3)CaRu(2)O(9) into a 1:2 B-site-ordered perovskite structure were explored by cationic substitution at the strontium and calcium sites and by the application of high pressure. At ambient pressures, Sr(3)MRu(2)O(9) stoichiometries yield multiphasic mixtures for M = Ni(2+), Mg(2+), and Y(3+), whereas pseudocubic perovskites result for M = Cu(2+) and Zn(2+). For A-site substitutions, an ordered perovskite structure results for Sr(3-x)Ca(x)CaRu(2)O(9), with 0 相似文献   

Large scale synthesis of stable tricolor Zn(1-x)Cd(x)Se core/multishell nanocrystals via a facile phosphine-free colloidal method

Here we report a new "green" method to synthesize Zn(1-x)Cd(x)Se (x = 0-1) and stable red-green-blue tricolor Zn(1-x)Cd(x)Se core/shell nanocrystals using only low cost, phosphine-free and environmentally friendly reagents. The first excitonic absorption peak and photoluminescence (PL) position of the Zn(1-x)Cd(x)Se nanocrystals (the value of x is in the range 0.005-0.2) can be fixed to any position in the range 456-540 nm. There is no red or blue shift in the entire reaction process. Three similar sizes of alloyed Zn(1-x)Cd(x)Se nanocrystals with blue, green, and yellow emissions were successfully selected as cores to synthesize high quality blue, green, and red core/shell nanocrystal emitters. For the synthesis of core/shell nanocrystals with a high quantum yield (QY) and stability, the selection of shell materials has been proven to be very important. Therefore, alternative protocols have been used to optimize thick shell growth. ZnSe/ZnSe(x)S(1-x) and CdS/Zn(1-x)Cd(x)S have been found as an excellent middle multishell to overcoat between the alloyed Zn(1-x)Cd(x)Se core and ZnS outshell. The QYs of the as-synthesized core/shell alloyed Zn(1-x)Cd(x)Se nanocrystals can reach 40-75%. The Cd content is reduced to less than 0.1% for Zn(1 -x)Cd(x)Se core/shell nanocrystals with emissions in the range 456-540 nm. More than 15 g of high quality Zn(1-x)Cd(x)Se core/shell nanocrystals were prepared successfully in a large scale, one-pot reaction. Importantly, the emissions of such thick multishell nanocrystals are not susceptible to ligand loss and stability in various physiological conditions.     

Thermal activated energy transfer between luminescent states of Mn2+-doped ZnTe nanoparticles embedded in a glass matrix

Zn(1-x)Mn(x)Te nanocrystals (NCs), at various concentrations x, were successfully grown in a host glass matrix by the fusion method after appropriate annealing. Growth of these NCs was evidenced by optical absorption (OA), X-Ray Diffraction (XRD), magnetic force microscopy (MFM) and photoluminescence (PL) measurements. From the room temperature OA spectra, it was possible to observe the formation of two well defined, different sized groups of NCs, one attributed to quantum dots (QDs) and the other to bulk-like nanocrystals (NCs). XRD results have confirmed that the cubic zincblend structure of nanoparticles is not altered by the substitutional incorporation of Mn(2+) ions into the ZnTe NCs. MFM images supported the OA spectra results and thus provided additional confirmation of the formation of Zn(1-x)Mn(x)Te magnetic nanoparticles in the host glass matrix. The two groups of NCs were also observed in the PL spectra as well as deep defects attributed to the presence of oxygen centers in the electronic structure of the Zn(1-x)Mn(x)Te NCs. Strong agreement between the fitting model, based on rate equation, and experimental PL intensity data at different temperatures demonstrates that this model adequately describes the energy transfer processes between the NCs and the defects of the Zn(1-x)Mn(x)Te system at different temperatures.     

Growth kinetic on the optical properties of the Pb(1-x)Mn(x)Se nanocrystals embedded in a glass matrix: thermal annealing and Mn2+ concentration

Semimagnetic Pb(1-x)Mn(x)Se nanocrystals were synthesized by a fusion method in a glass matrix and characterized by optical absorption (OA), atomic/magnetic force microscopy (AFM/MFM), and photoluminescence techniques. MFM images strongly indicated the formation of Pb(1-x)Mn(x)Se magnetic phases in the glass system. Quantum dot size was manipulated by tuning annealing time. It was shown that Mn(2+) impurity affects nucleation, where Mn(2+)-doped samples present a redshift of the OA peak after a short annealing time and a blueshift after long annealing time compared to undoped PbSe NCs. This behavior was linked to the dependence of band-gap energy and the absorption selection rule on Mn(2+) concentration. Photoluminescence in the Pb(1-x)Mn(x)Se nanocrystals increases as the temperature rises up to a point and then decreases at higher temperatures. Anomalous increases in emission efficiency were analyzed by considering temperature induced carrier-transfer in semimagnetic Pb(1-x)Mn(x)Se quantum dots nanocrystals of different sizes.     

Soft X-ray characterization of Zn(1-x)Sn(x)O(y) electronic structure for thin film photovoltaics

Zinc tin oxide (Zn(1-x)Sn(x)O(y)) has been proposed as an alternative buffer layer material to the toxic, and light narrow-bandgap CdS layer in CuIn(1-x),Ga(x)Se(2) thin film solar cell modules. In this present study, synchrotron-based soft X-ray absorption and emission spectroscopies have been employed to probe the densities of states of intrinsic ZnO, Zn(1-x)Sn(x)O(y) and SnO(x) thin films grown by atomic layer deposition. A distinct variation in the bandgap is observed with increasing Sn concentration, which has been confirmed independently by combined ellipsometry-reflectometry measurements. These data correlate directly to the open circuit potentials of corresponding solar cells, indicating that the buffer layer composition is associated with a modification of the band discontinuity at the CIGS interface. Resonantly excited emission spectra, which express the admixture of unoccupied O 2p with Zn 3d, 4s, and 4p states, reveal a strong suppression in the hybridization between the O 2p conduction band and the Zn 3d valence band with increasing Sn concentration.     

Cd(1-x)Zn(x)O [0.05 ≤x≤ 0.26] synthesized by vapor-diffusion induced hydrolysis and co-nucleation from aqueous metal salt solutions

Nanoparticulate Cd(1-x)Zn(x)O (x = 0, 0.05-0.26, 1) is synthesized in a simple two-step synthesis approach. Vapor-diffusion induced catalytic hydrolysis of two molecular precursors at low temperature induces co-nucleation and polycondensation to produce bimetallic layered hydroxide salts (M = Cd, Zn) as precursor materials which are subsequently converted to Cd(1-x)Zn(x)O at 400 °C. Unlike ternary materials prepared by standard co-precipitation procedures, all products presented here containing < 30 mol% Zn(2+) ions are homogeneous in elemental composition on the micrometre scale. This measured compositional homogeneity within the samples, as determined by energy dispersive spectroscopy and inductively coupled plasma spectroscopy, is a testimony to the kinetic control achieved by employing slow hydrolysis conditions. In agreement with this observation, the optical properties of the materials obey Vegard's Law for a homogeneous solid solution of Cd(1-x)Zn(x)O, where x corresponds to the values determined by inductively coupled plasma analysis, even though powder X-ray diffraction shows phase separation into a cubic mixed metal oxide phase and a hexagonal ZnO phase at all doping levels.     

One-pot noninjection synthesis of Cu-doped Zn(x)Cd(1-x)S nanocrystals with emission color tunable over entire visible spectrum

Unlike Mn doped quantum dots (d-dots), the emission color of Cu dopant in Cu d-dots is dependent on the nature, size, and composition of host nanocrystals (NCs). The tunable Cu dopant emission has been achieved via tuning the particle size of host NCs in previous reports. In this paper, for the first time we doped Cu impurity in Zn(x)Cd(1-x)S alloyed NCs and tuned the dopant emission in the whole visible spectrum via variation of the stoichiometric ratio of Zn/Cd precursors in the host Zn(x)Cd(1-x)S alloyed NCs. A facile noninjection and low cost approach for the synthesis of Cu:Zn(x)Cd(1-x)S d-dots was reported. The optical properties and structure of the obtained Cu:Zn(x)Cd(1-x)S d-dots have been characterized by UV-vis spectroscopy, photoluminescence (PL) spectroscopy, transmission electron microscopy (TEM), and X-ray diffraction (XRD). The influences of various experimental variables, including Zn/Cd ratio, reaction temperature, and Cu dopant concentration, on the optical properties of Cu dopant emission have been systematically investigated. The as-prepared Cu:Zn(x)Cd(1-x)S d-dots did show PL emission but with quite low quantum yield (QY) (typically below 6%). With the deposition of ZnS shell around the Cu:Zn(x)Cd(1-x)S core NCs, the PL QY increased substantially with a maximum value of 65%. More importantly, the high PL QY can be preserved when the initial oil-soluble d-dots were transferred into aqueous media via ligand replacement by mercaptoundeconic acid. In addition, these d-dots have thermal stability up to 250 °C.     

Synthesis of colloidal Mn2+:ZnO quantum dots and high-TC ferromagnetic nanocrystalline thin films

We report the synthesis of colloidal Mn(2+)-doped ZnO (Mn(2+):ZnO) quantum dots and the preparation of room-temperature ferromagnetic nanocrystalline thin films. Mn(2+):ZnO nanocrystals were prepared by a hydrolysis and condensation reaction in DMSO under atmospheric conditions. Synthesis was monitored by electronic absorption and electron paramagnetic resonance (EPR) spectroscopies. Zn(OAc)(2) was found to strongly inhibit oxidation of Mn(2+) by O(2), allowing the synthesis of Mn(2+):ZnO to be performed aerobically. Mn(2+) ions were removed from the surfaces of as-prepared nanocrystals using dodecylamine to yield high-quality internally doped Mn(2+):ZnO colloids of nearly spherical shape and uniform diameter (6.1 +/- 0.7 nm). Simulations of the highly resolved X- and Q-band nanocrystal EPR spectra, combined with quantitative analysis of magnetic susceptibilities, confirmed that the manganese is substitutionally incorporated into the ZnO nanocrystals as Mn(2+) with very homogeneous speciation, differing from bulk Mn(2+):ZnO only in the magnitude of D-strain. Robust ferromagnetism was observed in spin-coated thin films of the nanocrystals, with 300 K saturation moments as large as 1.35 micro(B)/Mn(2+) and T(C) > 350 K. A distinct ferromagnetic resonance signal was observed in the EPR spectra of the ferromagnetic films. The occurrence of ferromagnetism in Mn(2+):ZnO and its dependence on synthetic variables are discussed in the context of these and previous theoretical and experimental results.     

Fabrication and photoluminescent properties of heteroepitaxial ZnO/Zn0.8Mg0.2O coaxial nanorod heterostructures

ZnO/Zn0.8Mg0.2O coaxial nanorod heterostructures were prepared by employing catalyst-free metal-organic vapor-phase epitaxy, and their structural and photoluminescent (PL) properties were investigated using transmission electron microscopy (TEM) and temperature-dependent PL spectroscopy. TEM images show that ZnO/Zn0.8Mg0.2O layers were epitaxially grown on the entire surfaces of the ZnO nanorods and the ZnO nanorod diameters as a core material were as small as 9 +/- 2 nm. A dominant PL peak was observed at 3.316 eV, from room-temperature PL spectra of ZnO/Zn0.8Mg0.2O coaxial nanorod heterostructures with ZnO core diameters of 9 nm, indicating a PL blue shift of 30 meV, which resulted from a quantum confinement effect along the radial direction in ZnO nanorods. Furthermore, temperature-dependent PL properties of the coaxial nanorod heterostructures were investigated, showing much higher PL intensity for the coaxial nanorod heterostructures than that of bare ZnO nanorods at room temperature. The origin of the enhanced PL intensity and reduced thermal quenching for the coaxial nanorod heterostructures is also discussed.