Synthesis and characterization of biodegradable poly(L-aspartic acid-co-PEG)

The melt polycondensation reaction of the prepolymer prepared from N-(benzyloxycarbonyl)-L -aspartic acid anhydride (N-CBz-L -aspartic acid anhydride) and low molecular weight poly(ethylene glycol) (PEG) using titanium isopropoxide (TIP) as a catalyst produced the new biodegradable poly(L -aspartic acid-co-PEG). This new copolymer had pendant amine functional groups along the polymer backbone chain. The optimal reaction conditions for the preparation of the prepolymer were obtained by using a 0.12 mol % of p-toluenesulfonic acid with PEG 200 for 48 h. The weight-average molecular weight of the prepolymer increased from 1,290 to 31,700 upon melt polycondensation for 6 h at 130°C under vacuum using 0.5 wt % TIP as a catalyst. The synthesized monomer, prepolymer, and copolymer were characterized by FTIR, ¹H- and ¹³C-NMR, and UV spectrophotometers. Thermal properties of the prepolymer and the protected copolymer were measured by DSC. The glass transition temperature (T_g) of the prepolymer shifted to a significantly higher temperature with increasing molecular weight via melt polycondensation reaction, and no melting temperature was observed. The in vitro hydrolytic degradation of these poly(L -aspartic acid-co-PEG) was measured in terms of molecular weight loss at different times and pHs at 37°C. This pH-dependent molecular weight loss was due to a simple hydrolysis of the backbone ester linkages and was characterized by more rapid rates of hydrolysis at an alkaline pH. These new biodegradable poly(L -aspartic acid-co-PEG)s may have potential applications in the biomedical field. © 1998 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 36: 2949–2959, 1998     

Synthesis and characterization of phthalazinone containing poly(arylene ether)s via a novel N–C coupling reaction

High‐molecular‐weight poly(phthalazinone)s with very high glass‐transition temperatures (T_g's) were synthesized via a novel N–C coupling reaction. New bisphthalazinone monomers ( 7a–e ) were synthesized from 2‐(4‐chlorobenzoyl) phthalic acid in two steps. Poly(phthalazinone)s, having inherent viscosities in the range of 0.34–0.91 dL/g, were prepared by the reaction of the bis(phthalazinone) monomers with an activated aryl halide in a dipolar aprotic solvent in the presence of potassium carbonate. The poly(phthalazinone)s exhibited T_g's greater than 230 °C. polymer 8b synthesized from diphenyl biphenol and bis(4‐flurophenyl) sulfone demonstrated the highest T_g of 297 °C. Thermal stabilities of the poly(phthalazinone)s were determined by thermogravimetric analysis. All the poly(phthalazinone)s showed a similar pattern of decomposition with no weight loss below 450 °C in nitrogen. The temperatures of 5% weight loss were observed to be about 500 °C. The poly(phthalazinone)s containing 4,4′‐isopropylidenediphenol and 4,4′‐(hexafluoroisopropylidene) diphenol and diphenyl ether linkage were soluble in chlorinated solvents such as chloroform. Other poly‐(phthalazinone)s were soluble in dipolar aprotic solvents such as N,N′‐dimethylacetamide. The soluble poly(phthalazinone)s can be cast as flexible films from solution. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2481–2490, 2003     

Parameters affecting transition temperatures of poly(lactic acid‐co‐polydiols) copolymer‐based polyester urethanes and their shape memory behavior

A series of polyester urethanes (PEUs) comprising poly(lactic acid‐co‐polydiol) copolymers as a soft segment, 4,4′‐diphenylmethane diisocyanate (MDI) and 1,4‐butanediol (BDO) as a hard segment were systematically synthesized. Soft segments, which were block copolymers of L ‐lactide (LA) and polydiols such as poly(ethylene glycol) and poly(trimethylene ether glycol), were prepared via ring opening polymerization. Glass transition temperatures (T_g) of the obtained PEUs were found strongly dependent on properties of copolymer soft segments. By simply changing composition ratio, type and molecular weight of polydiols in the soft segment preparation step, T_g of PEU can be varied in the broad range of 0–57°C. The synthesized PEUs exhibited shape memory behavior at their transition temperatures. PEUs with hard segment ratio higher than 65 mole percent showed good shape recovery. These findings suggested that it is important to manipulate molecular structure of the copolymer soft segment for a desirable transition temperature and design optimal soft to hard segment ratio in PEU for good shape recovery. Copyright © 2011 John Wiley & Sons, Ltd.     

Synthesis and Characterization of Large Dimension PBA-P(MMA-ITA) Latex Particles with Core-Shell Morphology

In this paper, a novel large dimension poly(n-butyl acrylate)-poly(methyl methacrylate-itaconic acid) (PBA-P(MMA-ITA)) core-shell latex particles (CSR) with diameter of 200 nm～300 nm were successfully synthesized via pre-emulsion and semi-continuous seeded emulsion polymerization process. The analysis on the surface tension and coagulation rate of polymeric system, size and distribution of latex particles indicated that the composite emulsifier of sodium dodecyl sulfonate/polyoxyethylene nonyl phenyl ether (SDS/OP-10) had the best emulsified effect. The optimal ratio of SDS/OP-10 was 1:1 and its optimum dosage was 1.0% of monomer amount. FTIR analysis results confirmed that ITA participated in the copolymerization reaction and the chemical bond between P(MMA-ITA) copolymer and PBA core existed in the interfacial of core and shell. DSC analysis results showed that the glass transition temperature (T _g) of P(MMA-ITA) copolymer increased with the increase of the ITA dosage and decreased with the increase of the core shell mass ratio. TEM images revealed that CSR particles had core-shell morphology indeed, but the particles’ core-shell morphology would be changed at higher ITA dosage and core shell mass ratio. The size of CSR particles was 330 nm, and the diameter of PBA core was 290 nm. ITA content in the shell of CSR particles was analyzed by non-aqueous acid-base titration. ITA content was the highest at 6% of ITA dosage, ITA amount which chemically bonded with PBA core was the highest at 8% of ITA dosage. When the core shell mass ratio was 60/40, ITA content and ITA amount which grafted onto PBA core were both the highest. ITA content of CSR particles achieved above 1.11% in this work, and it is completely possible for using CSR particles toughening and compatibilizing polyamide 6 (PA 6).     

Novel method for preparation of poly(benzoxazinone‐imide)

A novel method was developed to prepare poly(benzoxazinone‐imide) by the dealcoholization of poly(amide‐imide), having pendent ethoxycarbonyl groups, which was prepared from poly(amide acid). The poly(amide acid) was prepared from the reaction of pyromellitic dianhydride and 4,4′‐diamino‐6‐ethoxycarbonyl benzanilide. The curing behavior of the poly(amide acid) was monitored by DSC, which indicated the presence of two broad endotherms, one with maximum at 153 °C due to imide‐ring formation and the other with maximum at 359 °C due to benzoxazinone‐ring formation. The poly(amide acid) was thermally treated at 300 °C/1 h to get poly(amide‐imide) with pendent ester groups, then at 350 °C/2 h to convert into poly(benzoxazinone‐imide) by dealcoholization. Viscoelastic measurements of the poly(amide‐imide) showed that the storage modulus dropped at about 280 °C with glass‐transition temperature (T_g ) at about 340 °C. The storage modulus of poly(benzoxazinone‐imide), however, was almost constant up to 400 °C and no T_g was detected below 400 °C. Also, the tensile modulus and tensile strength of the poly(benzoxazinone‐imide) was much higher than that of the poly(amide‐imide). The 5% decomposition of poly(benzoxazinone‐imide) film was at 535 °C, which reflects its excellent thermal stability. Also, poly(benzoxazinone‐imide) showed more hydrolytic stability against alkali in comparison to polyimides. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1647–1655, 2000     

Miscibility of poly(styrene‐co‐butyl acrylate) with poly(ethyl methacrylate): Existence of both UCST and LCST

A miscible homopolymer–copolymer pair viz., poly(ethyl methacrylate) (PEMA)–poly(styrene‐co‐butyl acrylate) (SBA) is reported. The miscibility has been studied using differential scanning calorimetry. While 1 : 1 (w/w) blends with SBA containing 23 and 34 wt % styrene (ST) become miscible only above 225 and 185 °C respectively indicating existence of UCST, those with SBA containing 63 wt % ST is miscible at the lowest mixing temperature (i.e., T_g's) but become immiscible when heated at ca 250 °C indicating the existence of LCST. Miscibility for blends with SBA of still higher ST content could not be determined by this method because of the closeness of the T_g's of the components. The miscibility window at 230 °C refers to the two copolymer compositions of which one with the lower ST content is near the UCST, while the other with the higher ST content is near the LCST. Using these compositions and the mean field theory binary interaction parameters between the monomer residues have been calculated. The values are χ_ST‐BA = 0.087 and χ_EMA‐BA = 0.013 at 230 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 369–375, 2000     

Effect of temperature and water as additive on the MW and thermal properties of copoly(p-phenylene/biphenylene sulfide)s

Copoly(p-phenylene/biphenylene sulfide)s, PPBS were prepared from sodium sulfide trihydate(Na₂S·3H₂O), p-dichlorobenzene (DCB), and 4,4′-dibromobiphenyl (DBB) comonomers in N-methyl-2-pyrrolidinone (NMP) solvent using an autoclave. The molecular weights of PPBS copolymers were determined by high temperature (210°C) GPC in 1-chloronaphthalene solvent. The reaction temperature had little effect on the molecular weights of PPBS copolymers with water as additive at the level of 3 mol H₂O per 1 mol Na₂S. PPBS copolymer, however, showed maximum molecular weight of M_w = 24.1 × 10³ with the total water content of 9 mol H₂O per 1 mol Na₂S at an optimum polymerization temperature of 270°C. The resulting PPBS copolymer sample showed higher T_g (by 30°C) and lower T_m (by 10°C) than PPS homopolymer prepared under similar conditions. © 1996 John Wiley & Sons, Inc.     

Block/segmented polymers. A new method of synthesis of copoly(amide-ester)-ester polymer

A new method of preparation of segmented copolymer amide-ester type is described here starting from two oligomers, one hard crystallizable (A) having a glass transition temperature (T_g) above room temperature and the other soft, amorphous (B) having T_g well below room temperature. A, an oligo amide-ester terminated with hydroxyl groups has been synthesized from bis(hydroxy acylo amide) alkane, a reaction product of a lactone and diamine and dicarboxylic acid. B, an oligoester hydroxyl terminated was synthesized by the conventional method. The two oligomers A and B were transesterified removing diol as by-product to obtain segmented (amide-ester)-ester copolymer. The polymer showed mostly two T_gs one at ?40 to ?50°C and other at +40 to +50°C; and one melting temperature 200°C. Max^m inherent viscosity was recorded at 1.75 dL/gm. © 1993 John Wiley & Sons, Inc.     

Synthesis and properties of the ionomer diblock copolymer poly(4‐vinylbenzyl triethyl ammonium bromide)‐b‐polyisobutene

A new amphiphilic diblock copolymer containing an ionomer segment, poly[(4‐vinylbenzyl triethyl ammonium bromide)‐co‐(4‐methylstyrene)‐co‐(4‐bromomethylstyrene)]‐b‐polyisobutene [poly(4‐VBTEAB)‐b‐PIB], was synthesized by the chemical modification of poly(4‐methylstyrene)‐b‐polyisobutene [poly(4‐MSt)‐b‐PIB]. First, the 4‐methylstyrene moiety in poly(4‐MSt)‐b‐PIB was brominated with azobisisobutyronitrile as an initiator at 60 °C in CCl₄, and then the highly reactive benzyl bromide groups were ionized by a reaction with triethylamine in a toluene/isopropyl alcohol (80/20 v/v) mixture at about 85 °C to produce the ionomer diblock copolymer poly(4‐VBTEAB)‐b‐PIB. The solubility of the ionomer block copolymer was quite different from that of the corresponding poly[(4‐methylstyrene)‐co‐(4‐bromomethylstyrene)]‐b‐polyisobutene {poly[(4‐MSt)‐co‐(4‐BrMSt)]‐b‐PIB}. Transmission electron microscopy observations demonstrated that all three diblock copolymers had microphase‐separation structures in which polyisobutene (PIB) domains existed in the continuous phase of the poly(4‐methylstyrene) segment or its derivative segment matrix. Dynamic mechanical thermal analysis measurements showed that poly[(4‐MSt)‐co‐(4‐BrMSt)]‐b‐PIB had two glass‐transition temperatures (T_g's), ?56 °C for the PIB segment and 62 °C for the poly[(4‐MSt)‐co‐(4‐BrMSt)] domain, whereas poly(4‐VBTEAB)‐b‐PIB showed one T_g at ?8 °C of the PIB domain; T_g of the poly[(4‐vinylbenzyl triethyl ammonium bromide)‐co‐(4‐methylstyrene)‐co‐(4‐bromomethylstyrene)] domain was not observable because of the strong ionic interactions resulting in a higher T_g and a retention of modulus up to 124 °C. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2755–2764, 2003     

Novel method for the preparation of poly(urethane–imide)s and their properties

A polymer blend consisting of polyimide (PI) and polyurethane (PU) was prepared by means of a novel approach. PU prepolymer was prepared by the reaction of polyester polyol and 2,4-tolylenediisocyanate (2,4-TDI) and then end-capped with phenol. Poly(amide acid) was prepared from pyromellitic dianhydride (PMDA) and oxydianiline (ODA). A series of oligo(amide acid)s were also prepared by controlling the molar ratio of PMDA and ODA. The PU prepolymer and poly(amide acid) or oligo(amide acid) solution were blended at room temperature in various weight ratios. The cast films were obtained from the blend solution and treated at various temperatures. With the increase of polyurethane component, the films changed from plastic to brittle and then to elastic. The poly(urethane–imide) elastomers showed excellent mechanical properties and moderate thermal stability. The elongation of films with elasticity was more than 300%. The elongation set after the breaking of films was small. From the dynamic mechanical analysis, all the samples showed a glass transition temperature (T_g) at ca. −15°C, corresponding to T_g of the urethane component, suggesting that phase separation occurred between the two polymer components, irrespective of polyimide content. TGA and DSC studies indicated that the thermal degradation of poly(urethane–imide) was in the temperature range 250–270°C. © 1997 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 35: 3745–3753, 1997     

Grafting by in situ coupling of epoxy groups of a living copolymer with an anionic living polymer

A tetrahydrofuran (THF) solution of the living random copolymer of methyl methacrylate (MMA) and glycidyl methacrylate (GMA) was prepared by the living anionic copolymerization of the two monomers, using 1,1‐diphenylhexyllithium (DPHLi) as initiator, in the presence of LiCl ([LiCl]/[DPHLi]₀ = 3), at −50°C. The copolymer thus obtained has a controlled composition and molecular weight and a narrow molecular weight distribution. By introduction of an anionic living polystyrene (poly(St)) or anionic living polyisoprene (poly(Is)) solution into the above system at −30°C, a coupling reaction took place and a graft copolymer with a polar backbone and nonpolar side chains was produced. The solvent used in the preparation of the living poly(St) or poly(Is) affects the coupling reaction. When benzene was the solvent, a graft copolymer of high purity, controlled graft number and molecular weight, and narrow molecular weight distribution (M_w/M_n = 1.11–1.21) was obtained. In the coupling reaction, the living poly(St) reacted only with the epoxy groups and not with the carbonyls of the backbone polymer. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 105–112, 1999     

Synthesis and properties of novel aromatic polyhydrazides and poly(amide–hydrazide)s based on the bis(ether benzoic acid)s from hydroquinone and substituted hydroquinones

4,4′‐(1,4‐Phenylenedioxy)dibenzoic acid as well as the 2‐methyl‐, 2‐tert‐butyl‐, or 2‐phenyl‐substituted derivatives of this dicarboxylic acid were synthesized in two main steps from p‐fluorobenzonitrile and hydroquinone or its methyl‐, tert‐butyl‐, or phenyl‐substituted derivatives. Polyhydrazides and poly(amide–hydrazide)s were prepared from these bis(ether benzoic acid)s or their diacyl chlorides with terephthalic dihydrazide, isophthalic dihydrazide, or p‐aminobenzoyl hydrazide by means of the phosphorylation reaction or low‐temperature solution polycondensation. Most of the hydrazide polymers and copolymers are amorphous and readily soluble in various polar solvents such as N‐methyl‐2‐pyrrolidone (NMP) and dimethyl sulfoxide. They could be solution‐cast into transparent, flexible, and tough films. These polyhydrazides and poly(amide–hydrazide)s had T_gs in the range of 167–237°C and could be thermally cyclodehydrated into the corresponding poly(1,3,4‐oxadiazole)s and poly(amide–1,3,4‐oxadiazole)s approximately in the region of 250–350°C, as evidenced by the DSC thermograms. All the tert‐butyl‐substituted oxadiazole polymers and those derived from isophthalic dihydrazide were organic soluble. The thermally converted oxadiazole polymers exhibited T_gs in the range of 208–243°C and did not show significant weight loss before 450°C either in nitrogen or in air. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1169–1181, 1999     

Highly phenylated poly(aryl ether phthalazine)s

Two series of novel amorphous poly(aryl ether phthalazine)s have been prepared via an intramolecular ring closure reaction of poly(aryl ether ketone)s (PAEKs) with hydrazine monohydrate. Fluorinated PAEKs, which display solubility in solvents incorporating a ketone functionality such as acetone or ethyl acetate, were converted to poly(aryl ether phthalazine)s to observe if these polymers would display similar solubility characteristics. The poly(aryl ether phthalazine)s have glass transition temperatures in the range of 278–320°C and show 5% weight loss points greater than 500°C in air and nitrogen atmospheres. The fluorinated poly(aryl ether phthalazine)s were not soluble in ketonic solvents. A series of poly(aryl ether phthalazine)s incorporating pendant 2-naphthalenyl moieties has been prepared in an attempt to produce amorphous, thermally stable polymers with high glass transition temperatures. The polymers have glass transition temperatures in the range of 287–334°C and show 5% weight loss points greater than 500°C in air and nitrogen atmospheres. Poly(aryl ether phthalazine)s undergo an exothermic reaction above the glass transition temperature. The major product of this reaction is a rearrangement of the phthalazine moieties to quiazoline moieties, however some crosslinking of the polymers occurs. Cured samples of the poly(aryl ether phthalazine)s show a small increase in the polymer T_g and are insoluble in all solvents tested. © 1996 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 34:1897–1905, 1996     

Thermal properties of poly(methyl methacrylate-co-butyl acrylate-co-acrylic acid) modified with divinyl benzene and vinyltrimethoxysilane

The effect of butyl acrylate (BA), divinyl benzene (DVB) and vinyltrimethoxysilane (TMVS) on the thermal properties of poly(methyl methacrylate-co-butyl acrylate-co-acrylic acid) was investigated. Glass transition temperature (T_g), melting temperature (T_m) and specific heat capacity of the copolymers were investigated using Differential Scanning Calorimetry. Thermal stability of the copolymers which is associated with the degradation temperature (T_d) was studied by Thermogravimetric Analysis. Polyacrylates with T_g ranges between -19°Cand 19°C were obtained. With the incorporation of >7 wt% of DVB, the T_g of the copolymer increases from about ?17°C to ?10°C even though they have not undergone UV irradiation. Gel content results prove that crosslinking has occurred in the copolymers. With increasing amount of TMVS from 0 wt% to 7 wt%, the T_m of the copolymers prepared at acidic pH is about 40-60°C higher than that at the alkaline pH. However, the addition of TMVS gives no significant effect to the T_g and T_d of the copolymer films. The thermal stability of the copolymer has improved with increasing amount of BA and DVB, with DVB being more effective. The highest T_d of 425°C with 8% of DVB has been obtained. Consequently, a polyacrylate copolymer with a T_g of about ?13°C, a T_m of 170 °C and a T_d of about 424°C has been successfully synthesized. Hence, the soft polyacrylate with its relatively high T_m and T_d could serve as a superb material especially to be applied in the areas that require high melting temperature and good thermal stability.     

Polymerization and self‐assembly of thermally responsive in‐chain functionalized double‐hydrophilic macromonomers

Double‐hydrophilic in‐chain functionalized macromonomers consisting of poly(N‐isopropylacrylamide) (PNIPAM) and poly(ethylene oxide) were prepared by a multistep procedure including esterification of PNIPAM monoester of maleic acid with α‐methoxy‐ω‐hydroxypolyoxyethylene or its amidation with α‐methoxy‐ω‐aminopolyoxyethylene. The polymerization of the macromonomers was carried out in aqueous solutions. The temperature was the key parameter controlling the polymerization process that was performed in the organized domains formed by the macromonomers below and above the phase transition temperature (T_tr). Polymacromonomers with higher degrees of polymerization were prepared at temperatures just below the T_tr. Static light scattering measurements on dilute aqueous solutions of thermally‐responsive macromonomers and their polymerization products demonstrated that they formed aggregates below the T_tr. Supramolecular structures with low density cores, formed by the polymacromonomers at room temperature, were imaged by SEM. Morphological tuning was achieved by varying both the composition of the copolymer and the concentration of the aqueous solution. The rheological behavior of the polymacromonomers in 25 wt % aqueous solution was compared to that of the respective macromonomers. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4720–4732, 2007     

Synthesis and properties of novel soluble poly(aryl amine ketone)s as high-performance polymers

A series of poly(aryl amine ketone)s have been obtained by the condensation polymerization of different aromatic dibromides with different primary aromatic diamines via palladium-catalyzed aryl amination reaction. The structures of polymers are characterized by means of FT-IR, 1H NMR spectroscopy, and elemental analysis. The results show an agreement with the proposed structures. DSC and TG measurements show that polymers possess high glass transition temperature (Tg>170℃) and good thermal stability with high decomposition temperatures (TD>450℃). These novel polymers also exhibit good mechanical behaviors and good solubility.     

Synthesis and Photosensitive Properties of Poly(aryl imino) Containing Azobenzene Group (PAI-A)

Using 4,4′‐dibromobenzophenone and 4,4′‐diaminoazobenzene as monomers, poly(aryl imino) containing azobenzene unit (PAI‐A) was synthesized via palladium‐catalyzed amination, and structurally characterized by means of FT‐IR, ¹H NMR spectra and elemental analysis, the results of which show an agreement with the proposed structure. The UV absorption spectra were tested under different conditions. Additionally, differential scanning calorimetry (DSC) and thermogravimetric (TG) measurements show that PAI‐A possesses high glass transition temperature (T_g>176°C) and good thermal stability with high decomposition temperatures in nitrogen atmosphere (T_D>410°C).     

Synthesis and characterization of poly(vinylcyclohexane) derivatives

Six nearly monodisperse substituted poly(styrene) homopolymers, poly(styrene) (PS), poly(2-methylstyrene) (P2MS), poly(3-methylstyrene) (P3MS), poly(4-methylstyrene) (P4MS), poly(tertiary-butylstyrene) (PtBS), and poly(α-methylstyrene) (FαMS) were anionically polymerized and subsequently saturated using heterogeneous hydrogenation techniques to poly(vinylcyclohexane) (PVCH), poly(2-methylvinylcyclohexane) (P2MVCH), poly(3-methylvinylcyclohexane) (P3MVCH), poly(4-methylvinylcyclohexane) (P4MVCH), and poly(tertiary-butylvinylcyclohexane) (PtBVCH), respectively. In each case, except PαMS, the materials were saturated to > 99% conversion with no chain degradation. PS hydrogenations required the addition of small amounts of tetrahydrofuran to the reaction solvent cyclohexane to enhance miscibility and eliminate large-scale chain degradation. Density gradient and differential scanning calorimetry (DSC) measurements were used to characterize the density and glass transition temperature, T_g, of the unsaturated and saturated polymers. Saturation reduces the density by 3% to 11% and changes T_g substantially. The greatest variation in T_g is obtained with the 3-methyl substituted species where a 63°C increase is observed, while the highest measured T_g is 186°C for P2MVCH. Small-angle neutron scattering (SANS) experiments on binary mixtures of hydrogenous and deuterium labeled PVCH derivatives provided a determination of bulk chain statistics. The statistical segment length is relatively insensitive to vinylcyclohexane ring substitution, except with P3MVCH where a 20% greater value is obtained. ©1995 John Wiley & Sons, Inc.     

Synthesis of methyl methacrylate,styrene, and isobutylene multiblock copolymers using atom transfer and cationic polymerization

ABCBA‐type pentablock copolymers of methyl methacrylate, styrene, and isobutylene (IB) were prepared by the cationic polymerization of IB in the presence of the α,ω‐dichloro‐PS‐b‐PMMA‐b‐PS triblock copolymer [where PS is polystyrene and PMMA is poly(methyl methacrylate)] as a macroinitiator in conjunction with diethylaluminum chloride (Et₂AlCl) as a coinitiator. The macroinitiator was prepared by a two‐step copper‐based atom transfer radical polymerization (ATRP). The reaction temperature, ?78 or ?25 °C, significantly affected the IB content in the resulting copolymers; a higher content was obtained at ?78 °C. The formation of the PIB‐b‐PS‐b‐PMMA‐b‐PS‐b‐PIB copolymers (where PIB is polyisobutylene), prepared at ?25 (20.3 mol % IB) or ?78 °C (61.3 mol % IB; rubbery material), with relatively narrow molecular weight distributions provided direct evidence of the presence of labile chlorine atoms at both ends of the macroinitiator capable of initiation of cationic polymerization of IB. One glass‐transition temperature (T_g), 104.5 °C, was observed for the aforementioned triblock copolymer, and the pentablock copolymer containing 61.3 mol % IB showed two well‐defined T_g's: ?73.0 °C for PIB and 95.6 °C for the PS–PMMA blocks. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3823–3830, 2005     

Synthesis of transition‐metal‐ion‐selective poly(N‐isopropylacrylamide) hydrogels by the incorporation of an Aza crown ether

A functionalized cyclam was synthesized by the attachment of a polymerizable acryloyl group to one of the four nitrogens on the cyclam molecule. The polymerization of the functionalized cyclam was performed with N‐isopropylacrylamide and N,N′‐methylene bisacrylamide, and the gels obtained were studied in the presence of different transition‐metal‐ion solutions. There was a drastic difference in the phase‐transition temperature (T_c) of the poly(N‐isopropylacrylamide) (PNIPAAm)/cyclam gel in comparison with the pure PNIPAAm gel. For the described system, a T_c shift of 15 °C was obtained. The presence of functionalized cyclam increased the hydrophilicity and T_c of the aforementioned polymer gels in deionized water (at pH 6) because of the presence of protonated amino moieties. The PNIPAAm/cyclam gels showed a dependence of the swelling behavior on pH. T_c of the pure PNIPAAm gel was weakly influenced by the presence of any transition‐metal ions, such as Cu²⁺, Ni²⁺, Zn²⁺, and Mn²⁺. The addition of Cu²⁺ or Ni²⁺ to the PNIPAAm/cyclam gel reduced T_c of the polymer gel, and a shift of approximately 12 °C was observed. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 1594–1602, 2003