Auger electron/X-ray photoelectron and cathodoluminescent spectroscopic studies of pulsed laser ablated SrAl2O4:Eu,Dy thin films

Auger electron/X-ray photoelectron and cathodoluminescent (CL) spectroscopic studies were conducted on pulsed laser deposited SrAl₂O₄:Eu²⁺,Dy³⁺ thin films and the correlation between the surface chemical reactions and the decrease in the CL intensity was determined. The Auger electron and the CL data were collected simultaneously in a vacuum chamber either maintained at base pressure or backfilled with oxygen gas. The data were collected when the films were irradiated for 14 h with 2 keV electrons. The CL emission peak attributed to the 4f⁶5d¹ → 4f⁷ transitions was observed at ∼521 nm and the CL intensity of the peaks degraded at different rates in different vacuum conditions. X-ray photoelectron spectroscopy (XPS) data collected from degraded films suggest that strontium oxide (SrO) and aliminium oxide (Al₂O₃) were formed on the surface of the film as a result of electron stimulated surface chemical reaction (ESSCR).     

Surface characterization and luminescent properties of SrAl2O4:Eu,Dy nano thin films

SrAl₂O₄:Eu²⁺, Dy³⁺ thin films were grown on Si (1 0 0) substrates in different atmospheres using the pulsed laser deposition (PLD) technique. The effects of vacuum, oxygen (O₂) and argon (Ar) deposition atmospheres on the structural, morphological and photoluminescence (PL) properties of the films were investigated. The films were ablated using a 248 nm KrF excimer laser. Improved PL intensities were obtained from the unannealed films prepared in Ar and O₂ atmospheres compared to those prepared in vacuum. A stable green emission peak at 520 nm, attributed to 4f⁶5d¹→4f⁷ Eu²⁺ transitions was obtained. After annealing the films prepared in vacuum at 800 °C for 2 h, the intensity of the green emission (520 nm) of the thin film increased considerably. The amorphous thin film was crystalline after the annealing process. The diffusion of adventitious C into the nanostructured layers deposited in the Ar and O₂ atmospheres was most probably responsible for the quenching of the PL intensity after annealing.     

The influence of the number of pulses on the morphological and photoluminescence properties of SrAl2O4:Eu,Dy thin films prepared by pulsed laser deposition

The current work reports on the influence of the number of laser pulses on the morphological and photoluminescence properties of SrAl₂O₄:Eu²⁺,Dy³⁺ thin films prepared by the pulsed laser deposition (PLD) technique. Atomic force microscopy (AFM) was used to study the surface topography and morphology of the films. The AFM data showed that the film deposited using a higher number of laser pulses was packed with a uniform layer of coarse grains. In addition, the surface of this film was shown to be relatively rougher than the films deposited at a lower number of pulses. Photoluminescence (PL) data were collected using the Cary Eclipse fluorescence spectrophotometer equipped with a monochromatic xenon lamp. An intense green photoluminescence was observed at 517 nm from the films prepared using a higher number of laser pulses. Consistent with the PL data, the decay time of the film deposited using a higher number of pulses was characteristically longer than those of the other films. The effects of laser pulses on morphology, topography and photoluminescence intensity of the SrAl₂O₄:Eu²⁺,Dy³⁺ thin films are discussed.     

PL and CL degradation and characteristics of SrAl2O4: Eu,Dy phosphors

Strontium aluminate phosphors are ideal for luminescent infrastructure materials. Their brightness and persistent glow time are much higher than previously used sulphide phosphors. Strontium aluminates prepared by the sol–gel and combustion methods are compared with commercially available strontium aluminate. High luminescent efficient SrAl₂O₄:Eu²⁺,Dy³⁺ pulsed laser deposited (PLD) thin films were also produced using the commercially available powder. Photoluminescence (PL) degradation studies showed that the phosphor intensity decreased about 20% over a period of 2 weeks under ultraviolet (UV) irradiation. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) showed that cathodoluminescence (CL) degradation is due to the formation of SrO due to electron stimulated surface reactions. The light output mechanism of the phosphor is also discussed in more detail.     

Phosphorescent and thermoluminescent properties of SrAl2O4:Eu,Dy phosphors prepared by solid state reaction method

Long persistent SrAl₂O₄:Eu²⁺ phosphors co-doped with Dy³⁺ were prepared by the solid state reaction method. The main diffraction peaks of the monoclinic structure of SrAl₂O₄ were observed in all the samples. The broad band emission spectra at 497 nm for SrAl₂O₄:Eu²⁺, Dy³⁺ were observed and the emission is attributed to the 4f⁶5d¹ to 4f⁷ transition of Eu²⁺ ions. The samples annealed at 1100–1200 °C showed similar broad TL glow curves centered at 120 °C. The similar TL glow curves suggest that the traps responsible for them are similar. The long afterglow displayed by the phosphors annealed at different temperatures, may be attributed to the Dy³⁺ ions acting as the hole trap levels, which play an important role in prolonging the duration of luminescence.     

Enhanced luminescent properties of long-persistent Sr2MgSi2O7:Eu, Dy phosphor prepared by the co-precipitation method

Sr₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors were prepared by the (aminopropyl)-triethoxysilane (APTES) co-precipitation method. Effects of synthesis temperature on the crystal characteristics, luminescent properties and afterglow performance of Sr₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors have been discussed in detail and compared with the corresponding commercial product. The experimental results indicated that the sample could be synthesized at a relatively lower temperature and had better performance on the above-mentioned properties using the co-precipitation method.     

Preparation and luminescent properties of cubic Eu:Y2O3 nanocrystals and comparison to bulk Eu:Y2O3

Y₂O₃:Eu³⁺ nanocrystals were prepared by combustion synthesis. The particle size estimated by X-ray powder diffraction (XRD) was about 10 nm. A blue-shift of the charge-transfer (CT) band in excitation spectra was observed in Y₂O₃:Eu³⁺ nanocrystals compared with bulk Y₂O₃:Eu³⁺. The electronic structure of Y₂O₃ is calculated by density functional method and exchange and correlation have been treated by the generalized gradient approximation (GGA) within the scheme due to Perdew-Burke-Ernzerhof (PBE). The calculated results show that the energy centroid of 5d orbital in nanocrystal has increasing trend compared with that in the bulk material. The bond length and bond covalency are calculated by chemical bond theory. The bond lengths of Y₂O₃:Eu³⁺ nanocrystal are shorter than those of the bulk counterpart and the bond covalency of Y₂O₃:Eu³⁺ nanocrystal also has an increasing trend. By combining centroid shift and crystal-field splitting, the blue-shift of the CT band is interpreted.     

Effect of Eu,Tb codoping on the luminescent properties of Y2O3 nanorods

Red-emitting Y₂O₃:Eu³⁺ and green-emitting Y₂O₃:Tb³⁺ and Y₂O₃:Eu³⁺, Tb³⁺ nanorods were synthesized by hydrothermal method. Their structure and micromorphology have been analyzed by X-ray powder diffraction (XRD) and transmission electron microscopy (TEM). The photoluminescence (PL) property of Y₂O₃:Eu³⁺,Tb³⁺ phosphor was investigated. In the same host (Y₂O₃), upon excitation with ultraviolet (UV) irradiation, it is shown that there are strong emissions at around 610 and 545 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺ and ⁵D₄-⁷F₅ transition of Tb³⁺, respectively. Different qualities of Eu³⁺and Tb³⁺ ions are induced into the Y₂O₃ lattice. From the excitation spectrum, we speculate that there exists energy transfer from Tb³⁺ to Eu³⁺ ions .The emission color of powders reveals regular change in the separation of light emission. These powders can meet with the request of optical display material for different colors or can be potentially used as labels for biological molecules.     

The influence of Pr co-doping on the luminescent properties of Lu2O3:5 mol% Eu films

Uniform and crack free polycrystalline lutetium oxide (Lu₂O₃:(Eu,Pr)) films were fabricated by Pechini sol-gel method combined with the spin-coating technique. X-ray diffraction (XRD) and atomic force microscope (AFM) characterizations indicated that the obtained film was composed of polycrystalline cubic Lu₂O₃ phase with an average grain size around 30 nm. The photoluminescence(PL) spectra and decay performances of the Lu₂O₃:5 mol% Eu films co-doped by 0-0.5 mol% Pr³⁺ with different concentrations were characterized. It was found that the afterglow was reduced obviously due to the introduction of 0-0.5 mol% Pr³⁺ in the Lu₂O₃:5 mol% Eu films coupled by decrease in the emission intensity at 612 nm. The mechanism of afterglow diminishing was discussed based on the thermoluminescence measurements.     

X-ray photoelectron spectroscopy analysis for undegraded and degraded Gd2O2S:Tb phosphor thin films

This paper presents the X-ray Photoelectron Spectroscopy (XPS) analysis for the undegraded and degraded Gd₂O₂S:Tb³⁺ thin film phosphor. The thin films were grown with the pulsed laser deposition (PLD) technique. XPS measurements were done on Gd₂O₂S:Tb³⁺ phosphor thin films before and after electron degradation. The XPS technique has proven the presence of Gd₂O₃ on the degraded and undegraded thin film spots. The presence of the SO₂ bonding was also detected after degradation. This clearly indicates that surface reactions did occur during prolonged electron bombardment in an oxygen atmosphere.     

Synthesis and properties of colloidal ternary ZnGa2O4:Eu nanocrystals

A nonhydrolytic hot solution synthesis technique was used to grow monodisperse ternary oxide nanocrystals of ZnGa₂O₄:Eu³⁺. The shape of ZnGa₂O₄:Eu³⁺ nanocrystals was a function of the type of precursor, and their size was controlled by changing the concentration ratio of Zn precursor to surfactant. The crystal structure of synthesized ZnGa₂O₄ nanocrystals was a cubic spinel with no detectable secondary phases. Photoluminescence of red-emitting ZnGa₂O₄:Eu³⁺ nanocrystals resulted in a high (⁵D₀-⁷F₂)/(⁵D₀-⁷F₁) intensity ratio, suggesting that the Eu³⁺ ions occupy tetrahedral Zn²⁺ sites or distorted octahedral Ga³⁺ sites with no inversion symmetry in ZnGa₂O₄ nanocrystals.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

Thermoluminescent and stuctural properties of BaAl2O4:Eu,Nd,Gdphosphors prepared by combustion method

BaAl₂O₄:Eu²⁺,Nd³⁺,Gd³⁺ phosphors were prepared by a combustion method at different initiating temperatures (400–1200 °C), using urea as a comburent. The powders were annealed at different temperatures in the range of 400–1100 °C for 3 h. X-ray diffraction data show that the crystallinity of the BaAl₂O₄ structure greatly improved with increasing annealing temperature. Blue-green photoluminescence, with persistent/long afterglow, was observed at 498 nm. This emission was attributed to the 4f⁶5d¹–4f⁷ transitions of Eu²⁺ ions. The phosphorescence decay curves were obtained by irradiating the samples with a 365 nm UV light. The glow curves of the as-prepared and the annealed samples were investigated in this study. The thermoluminescent (TL) glow peaks of the samples prepared at 600 °C and 1200 °C were both stable at ∼72 °C suggesting that the traps responsible for the bands were fixed at this position irrespective of annealing temperature. These bands are at a similar position, which suggests that the traps responsible for these bands are similar. The rate of decay of the sample annealed at 600 °C was faster than that of the sample prepared at 1200 °C.     

Synthesis and luminescent properties of nanoparticles LaSrAl3O7:Eu, Tb

Phosphors of nanoparticles LaSrAl₃O₇:RE³⁺(REEu, Tb) have been prepared by a sol–gel method. The structure and luminescent properties of LaSrAl₃O₇:Eu³⁺ and LaSrAl₃O₇:Tb³⁺ phosphors were characterized by X-ray diffraction and atomic force microscopy (AFM), photoluminescence excitation and emission spectra were utilized. From X-ray diffraction (XRD) patterns, it is indicated that the phosphor LaSrAl₃O₇ forms without impurity phase at 900 °C. From atomic force microscopy (AFM) images, it is shown that the crystal size of the phosphores are about 60–80 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀–⁷F₂ transition of Eu³⁺, and at around 545 nm corresponding to the ⁵D₄–⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺(or Tb³⁺) concentration and annealing temperature were also studied in detail.     

Synthesis and luminescent properties of Y6W2O15:Eu phosphors

In this paper, a novel phosphor, Y₆W₂O₁₅:Eu³⁺ was synthesized by thermal decomposition and phase transition of its decatungstate gel precursor. With stepwise increase of temperature to 750 °C, a crystalline phase of Y₆W₂O₁₅:Eu³⁺forms that gives intense red emission when excited at 466 nm, the emission is attributed to the Eu³⁺ ions transitions from ⁵D₀ excited states to ⁷F_J (J=0-4) ground states. The long excitation wavelength proves the Eu³⁺ transition follows the photoexcitation of the oxygen-metal (O→W lmct) charge transfer bands in yttrium tungstate. Some structural information regarding Y₆W₂O₁₅ provided by luminescence is in accord with that characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The long-wavelength excitation properties of this material may find application in the production of red phosphors for white light-emitting diodes (LEDs).     

Luminescent properties of Dy doped SrMoO4 phosphor

Trivalent dysprosium ions (Dy³⁺) doped strontium molybdate (SrMoO₄) phosphors were synthesized by solid-state reaction and their photoluminescence (PL) properties were investigated. X-ray powder diffraction (XRD) analysis confirmed the formation of SrMoO₄:Dy³⁺. PL measurements indicated that the phosphor exhibited intense emission at 482, 490 (⁴F_9/2→⁶H_15/2) and 575 nm (⁴F_9/2→⁶H_13/2) under UV excitation. The effect of the doping concentration of Dy³⁺in SrMoO₄:Dy³⁺ on the PL was investigated in detail. Na⁺ ion was a good charge compensator for SrMoO₄:Dy³⁺.     

Highly water resistant surface coating by fluoride on long persistent Sr4Al14O25:Eu/Dy phosphor

A novel and efficient method of providing moisture resistance of inorganic particles such as divalent europium activated strontium aluminate phosphors (Sr₄Al₁₄O₂₅:Eu²⁺/Dy³⁺) was developed by firing the phosphor in the presence of appropriate amount of ammonium fluoride at a temperature of 600-700 °C. Scanning electron microscopy, X-ray diffraction, FT-IR, EDAX and Photoluminescence measurements were carried out to characterize the uncoated and coated samples. The pH measurements were carried out for the water resistivity measurements. The phosphor particles became coated with a moisture-impervious thin coating that did not suppress the luminescence of the phosphor and can withstand complete immersion in water for long periods of time, showing very high water resistivity.     

Modification on luminescent properties of SrAl2O4:Eu, Dy phosphor by Yb ions doping

The modification effect of the doping of Yb³⁺ ions, as an auxiliary activator, onto the luminescent properties of SrAl₂O₄:Eu²⁺, Dy³⁺ phosphor was studied for the first time. The phosphorescent nanoparticles were prepared by the combustion method. The experimental results indicate that the appropriate doping of Yb³⁺ ions largely improves phosphorescence of the phosphors with more intense luminescence, higher brightness, and no change in emission spectrum peaked at 513 nm. Meanwhile the decay speed of the phosphor nanoparticles rises increasingly with the doping ratio of Yb³⁺ ions, whereas an excessive Yb³⁺ ions doping leads to the disappearance of the pure monoclinic phase of SrAl₂O₄ and the appearance of the weak diffraction lines of the YbAlO₃ phase. The phosphorescent mechanism of the phosphors could be well understood based on the hole, thermally released from the trap levels of Dy³⁺ and Yb³⁺.     

PrS0→Cr energy transfer and ESR investigation in Pr and Cr activated SrAl12O19 quantum cutting phosphor

With the help of the Dexter's theory, the energy transfer mechanism from Pr³⁺¹S₀ to Cr³⁺ is investigated theoretically in SrAl₁₂O₁₉:Pr³⁺, Cr³⁺ quantum cutting phosphors. The electron spin resonance (ESR) spectra of Pr³⁺ and Cr³⁺-doped SrAl₁₂O₁₉ with magnetoplumbite structure have been studied. The Cr³⁺ ion is found to enter the Al4(4f) site, which is very close to the Sr(2d) site replaced by the Pr³⁺ ions in the host. The theoretical results indicate that the efficient Pr³⁺¹S₀→Cr³⁺ energy transfer can only take place in the intermediate mirror planes, in which for the nearest and next-nearest Pr³⁺-Cr³⁺ pairs, both dipole-dipole and dipole-quadrupole interactions can play their parts in the transfer. Finally, an overview is given about the research on the energy transfer from Pr³⁺¹S₀ to codopants in their co-doped materials.     

Photoluminescence characterization of Ce and Dy doped Li2CaGeO4 phosphors

Ce³⁺ and Dy³⁺ activated Li₂CaGeO₄ phosphors were prepared by a solid-state reaction method, and characterized by XRD (X-ray diffraction) and photoluminescence techniques. The characteristic emission bands of Dy³⁺ due to ⁴F_9/2→⁶H_15/2 (blue) and ⁴F_9/2→⁶H_13/2 (yellow) transitions were detected in the emission spectra of Li₂CaGeO₄:Dy³⁺. Ce³⁺ broad band emission was observed in Li₂CaGeO₄:Ce³⁺ phosphors at 372 and 400 nm due to 5d→4f transition when excited at 353 nm. Co-doping of Ce³⁺ enhanced the luminescence of Dy³⁺ significantly and concentration quenching occurs when Dy³⁺ is beyond 0.04 mol%. White-light with different hues can be realized by tuning Dy³⁺ concentration in the phosphors.