Luminescence and EPR studies of Eu doped BaAl12O19 blue light emitting phosphors

Europium doped BaAl₁₂O₁₉ powder phosphors have been synthesized by combustion process within few minutes. The phosphors have been characterized by XRD, SEM, FT-IR, EPR and PL techniques. The EPR spectrum exhibits an intense resonance signal at g=1.96 characteristic of Eu²⁺ ions. In addition to this two weak resonance signals have been observed at g=2.28 and g=4.86. The population of the spin levels (N) for the resonance signal at g=1.96 is calculated as a function of temperature. By post-treating the phosphor at 1350 °C under a reducing atmosphere, it is observed that the population of spin levels has been increased five times. The excitation spectrum shows a peak at 326 nm with a shoulder at 290 nm. Upon excitation at 326 nm, the emission spectrum exhibits a well defined broad band with maximum at 444 nm emitting a blue light corresponding to 4f⁶5d→4f⁷ transition. The luminescence intensity also has been enhanced to 60% by post-treating the phosphor at 1350 °C under a reducing atmosphere.     

Characterization, EPR and luminescence studies of ZnAl2O4:Mn phosphors

ZnAl₂O₄:Mn green light emitting powder phosphors have been prepared by urea combustion technique involving furnace temperatures about 500 °C in a short time (<5 min). The prepared powders were characterized by X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectrometry and the surface area measurements by a Brunauer-Emmet-Teller (BET) adsorption isotherms. The EPR spectrum exhibits a resonance signal at g≈2.0, which shows a six-line hyperfine structure (hfs). From the EPR spectra the spin-Hamiltonian parameters have been evaluated at room temperature as well as at 110 K. EPR and photoluminescence (PL) studies revealed that manganese ions were present in divalent state and the site symmetry around Mn²⁺ ions is distorted tetrahedral. The spin concentration (N), the paramagnetic susceptibility (χ) and the zero-field splitting parameter (D) have been evaluated and discussed. The green emission at 511 nm in ZnAl₂O₄:Mn phosphor is assigned to a transition from the upper ⁴T₁→⁶A₁ ground state of Mn²⁺ ions.     

EPR and luminescence properties of LiGa5O8:Mn green emitting phosphor

Green emitting LiGa₅O₈:Mn powder phosphor has been prepared in a short time by solution combustion method. Powder X-ray diffraction pattern indicated a dominant phase of LiGa₅O₈ with another secondary LiGaO₂ phase. Morphology aspects were studied by using field emission scanning electron microscopy. Upon UV light excitation (296 nm), the phosphor exhibits a strong green luminescence (510 nm), which corresponds to the ⁴T₁→⁶A₁ transition of Mn²⁺ ions in an environment close to tetrahedral symmetry. EPR spectrum exhibits resonance signals characteristic of Mn²⁺ ions. It is observed that the spin-Hamiltonian parameters g and A do not vary with temperature. The magnitude of the hyperfine splitting constant (A) in the present study indicates that there exists a moderately covalent bonding between Mn²⁺ ions and the surrounding ligands. The zero-field splitting parameter (D), spin concentration (N) and paramagnetic susceptibility (χ) have also been evaluated.     

Combustion synthesis of Sr3MgSi2O8:Eu and Sr2MgSi2O7:Eu phosphors

Sr₃MgSi₂O₈:Eu²⁺ and Sr₂MgSi₂O₇:Eu²⁺ phosphors find uses in applications such as plasma display panel (PDP), solid-state lighting, longafter glow. Preparation of these phosphors by a modified combustion synthesis is described in this paper. As-prepared samples did not show photoluminescence. After reducing the samples at 900 °C, characteristic Eu²⁺ emission was observed. Preparation of these phosphors by using similar methods helped clarifying various results obtained for Sr₃MgSi₂O₈:Eu²⁺ by different investigators.     

EPR and photoluminescence properties of green light emitting LaAl11O18:Mn phosphors

The LaAl₁₁O₁₈:Mn²⁺ powder phosphor has been prepared using a self-propagating synthesis. Formation and homogeneity of the LaAl₁₁O₁₈:Mn²⁺ phosphor has been verified by X-ray diffraction and energy dispersive X-ray analysis respectively. The EPR spectra of Mn²⁺ ions exhibit resonance signals with effective g values at g≈4.8 and g≈1.978. The signal at g≈1.978 exhibits six-line hyperfine structure and is due to Mn²⁺ ions in an environment close to tetrahedral symmetry, whereas the resonance at g≈4.8 is attributed to the rhombic surroundings of the Mn²⁺ ions. It is observed that the number of spins participating in resonance for g≈1.978 increases with decreasing temperature obeying the Boltzmann law. Upon 451 nm excitation, the photoluminescence spectrum exhibits a green emission peak at 514 nm due to ⁴T₁ (G)→⁶A₁ (S) transition of Mn²⁺ ions. The crystal field parameter Dq and Racah inter-electronic repulsion parameters B and C have been evaluated from the excitation spectrum.     

Luminescence and EPR studies of Mn-activated SrAl12O19 phosphor prepared by facile combustion approach

Manganese-activated strontium hexa-aluminate (SrAl₁₂O₁₉) phosphor has been prepared at low temperature (500 °C) and in a very short time (<5 min) by urea combustion route. Powder X-ray diffraction pattern showed the presence of hexagonal SrAl₁₂O₁₉ phase. Scanning electron microscopy (SEM) indicated the presence of several particles with sizes of 200 nm. The luminescence of Mn²⁺ activated SrAl₁₂O₁₉ exhibits a strong green emission peak around 515 nm from the synthesized phosphor particles under excitation (451 nm). The luminescence is assigned to a transition from the upper ⁴T₁→⁶A₁ ground state of Mn²⁺ ions. EPR investigations also indicated the presence of Mn²⁺ ions in the prepared material. From the observed EPR spectrum, the spin-Hamiltonian parameters have been evaluated. The magnitude of the hyperfine splitting (A) constant indicates that there exists a moderately covalent bonding between Mn²⁺ ions and the surrounding ligands. The variation of zero-field splitting parameter (D) with temperature is measured and discussed. The mechanism involved in the generation of a green emission has been explained in detail.     

Combustion synthesized MgAl2O4:Cr phosphors—An EPR and optical study

Magnesium aluminate (MgAl₂O₄) doped with trivalent chromium (Cr³⁺) was synthesized by the combustion method. The prepared sample was characterized by X-ray powder diffraction, Brunauer-Emmet-Teller (BET) adsorption isotherms and diffuse-reflectance UV-vis spectroscopy techniques. Electron paramagnetic resonance (EPR) and photoluminescence (PL) studies have been performed at room temperature and at 110 K. The EPR spectrum exhibit resonance signals at g=5.37, 4.53, 3.82, 2.26 and 1.96 characteristic of Cr³⁺ ions. The luminescence of Cr³⁺-activated MgAl₂O₄ exhibits a red emission peak around 686 nm from the synthesized phosphor particles upon 551 nm excitation. The luminescence is assigned to a transition from the upper ²E_g→⁴A_2g ground state of Cr³⁺ ions. By correlating EPR and optical data the crystal field splitting parameter (D_q), Racah inter-electronic repulsion parameter (B) and the bonding parameters have been evaluated and discussed. The bonding parameters suggests that the ionic nature of Cr³⁺ ions with the ligands and the Cr³⁺ ions are in distorted octrahedral environment.     

Photoluminescence and EPR studies of BaMgAl10O17:Eu phosphor with blue-emission synthesized by the solution combustion method

A blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺, has been synthesized in the furnace at a temperature of 500 °C by solution combustion method. The formation of the as-prepared BaMgAl₁₀O₁₇:Eu²⁺ phosphor was confirmed by the powder X-ray diffraction technique. The EPR spectrum exhibited an intense resonance signal centered at g=4.63 at 150 mT along with a number of resonances in the vicinity of g>2.0 and g<2.0. The number of spins participating in resonance (N) and the susceptibility (c) for the resonance signal at g=4.63 have been calculated as a function of temperature. The excitation spectrum of BaMgAl₁₀O₁₇:Eu²⁺ phosphor showed a strong peak near 336 nm (4f⁷ (⁸S)→5d¹(t_2g) transition) with a staircase like structure in the region 376-400 nm owing to crystal field splitting of the Eu²⁺ d-orbital. The 336 nm excitation produced a broad blue emission at 450 nm corresponding to 4f⁶5d→4f⁷ transition. PL studies reveal the two emission centers one at 450 nm and the other at 490 nm in this phosphor.     

PL and CL degradation and characteristics of SrAl2O4: Eu,Dy phosphors

Strontium aluminate phosphors are ideal for luminescent infrastructure materials. Their brightness and persistent glow time are much higher than previously used sulphide phosphors. Strontium aluminates prepared by the sol–gel and combustion methods are compared with commercially available strontium aluminate. High luminescent efficient SrAl₂O₄:Eu²⁺,Dy³⁺ pulsed laser deposited (PLD) thin films were also produced using the commercially available powder. Photoluminescence (PL) degradation studies showed that the phosphor intensity decreased about 20% over a period of 2 weeks under ultraviolet (UV) irradiation. Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS) showed that cathodoluminescence (CL) degradation is due to the formation of SrO due to electron stimulated surface reactions. The light output mechanism of the phosphor is also discussed in more detail.     

Characterization of host-lattice emission and energy transfer in BaMgAl10O17:Eu

Host-lattice emission, energy transfer and degradation processes are characterized in undoped and Eu-doped BaMgAl₁₀O₁₇. Undoped BaMgAl₁₀O₁₇ exhibits a broad emission centered at 265 nm when excited at wavelengths shorter than 190 nm. This emission is assigned to exciton recombination at Ba-O groups in the cation layer of the lattice. The emission exhibits excellent overlap with the excitation band of Eu²⁺ in this host, providing a means of host-to-activator energy transfer in the doped phosphor. The exciton emission is relatively stable to thermal damage, but undergoes a peak shift and significant decrease in intensity after exposure to VUV radiation. Heating of VUV-damaged materials in air leads to some repair of the spectral properties.     

Investigation on Eu doped Sr2MgSi2O7 red-emitting phosphors for white-light-emitting diodes

In this work, we report the high temperature solid-state synthesis of red phosphors Sr₂MgSi₂O₇: Eu³⁺ with various Eu³⁺ concentrations. Their luminescent properties at room temperature are investigated. The X-ray diffraction patterns indicate that the red phosphors powder conforms to the tetragonal Sr₂MgSi₂O₇. Impurity structure appears when more than 20% Eu³⁺ is doped. The samples show a strong emission line at 615 nm and the intensity increases with the increase of Eu³⁺ concentration until concentration quenching occurs. Charge compensation assists in the reduction of the impurity structure and vacancies; hence the luminescent intensity is enhanced. The decay measurement indicates that the lifetime of Eu³⁺ emission is about 2-3 ms. Some of the Eu³⁺ can be reduced to Eu²⁺; this is also discussed.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Enhanced photoluminescence of Sm/Bi co-doped Gd2O3 phosphors by combustion synthesis

Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ powders were prepared by a combustion method. Their structures were determined using X-ray diffraction. UV-visible absorption and photoluminescence spectra were investigated for Gd₂O₃:Sm³⁺ and Gd₂O₃:Sm³⁺,Bi³⁺ at different annealing temperatures and different doping concentrations. The emission spectra of all samples presented the characteristic emission narrow lines arising from the ⁴G_5/2→⁶H_J transitions (J=5/2, 7/2, and 9/2) of Sm³⁺ ions upon excitation with UV irradiation. The emission intensity of Sm³⁺ ions was largely enhanced with introducing Bi³⁺ ions into Gd₂O₃:Sm³⁺ and the maximum occurred at a Bi³⁺ concentration of 0.5 mol%. The relevant mechanisms were discussed with the sensitization theory by Dexter and the aggregation behavior of Bi³⁺ ions.     

Photoluminescence of Eu in SrGa2S4

A photoluminescence (PL) study of the green-emitting SrGa₂S₄:Eu²⁺ phosphor is reported. Diffuse reflectance, excitation, and emission spectra were examined with the aim to enlarge the fundamental knowledge about the emission of the Eu²⁺ ion in this lattice. The thermal dependence of the radiative properties was investigated. In particular, the Stokes shift, the crystal field splitting and the activation energy of the thermal quenching were determined. By combining these results with the information presented in literature, we discussed the location of the Eu²⁺ levels relative to the valence and conduction bands of SrGa₂S₄.     

Thermoluminescence spectroscopy of Eu and Mn doped BaMgAl10O17

Thermoluminescence (TL) studies of Eu²⁺ and Mn²⁺ doped BaMgAl₁₀O₁₇ (BAM) are reported and discussed. The TL spectra that are measured after irradiation with ultraviolet (120-) show a series of TL peaks between 100 and . The TL spectra are similar for BAM with the two dopants, which suggest that the shallow traps are typical for the BAM host lattice. Using the Hoogstraaten analysis trap depths between 0.1 and are determined. A model is proposed based on thermally activated recombination in local TL centres (not via the conduction band). Further support for this model is obtained from the observation that the TL signal is strongest for excitation around the band edge of BAM . Upon heating the samples in air all low temperature TL peaks decrease in intensity. In addition a new peak appears in the TL spectrum, which is connected with a deeper trap and also a partial oxidation of Eu²⁺ to Eu³⁺ is observed. The luminescence efficiency is lower and the UV induced degradation is faster after annealing in air. These results indicate that the shallow traps are related to oxygen vacancies. The shallow traps do not have a negative influence on performance (efficiency and degradation) of BAM as a lighting phosphor. The luminescence efficiency and stability are strongly influenced by the formation of Eu³⁺ and a deeper trap during annealing in air. Subsequent annealing in a reducing atmosphere restores the original properties.     

Synthesis of nano-size BaMgAl10O17:Eu blue phosphor by a rapid exothermic reaction

Ultrafine particles of BaMgAl₁₀O₁₇:Eu²⁺ (BAM) phosphor were synthesized by a solid-state combustion reaction in a powder bed of 0.9BaCO₃+MgO+5Al₂O₃+0.05Eu₂O₃+k(KClO₃+1.5C) composition. A large exothermic reaction of the mixture (KClO₃+1.5C) leads to a self-sustaining combustion mode. Under optimized combustion conditions, the product consisted of BAM powder and KCl was obtained. BAM ultrafine particles resulting from the combustion process were easily obtained by simply washing the salt by-product with water. Combustion-processed BAM phosphor shows a homogeneous grain size of 100-500 nm, good dispersity, regular morphology, and improved luminescence properties.     

Red, green and blue (RGB) emission doped Y3Al5O12 (YAG) phosphors prepared by non-hydrolytic sol-gel route

An evolutionary optimization process involving combination chemistry was employed in an attempt to develop Y₃Al₅O₁₂ (YAG). The combination chemistry process utilized here consisted the doping of the YAG host with appropriate amounts of red (R), green (G), and blue (B) dopants in a single layer, for use in tricolor white light. The doped YAG was acieved by means of the non-hydrolytic sol-gel route. Four samples were prepared, three of which were mono-doped samples containing 1.0% of a certain lanthanide (Eu³⁺, Tb³⁺, or Tm³⁺) ion, while the fourth contained the three ions. The samples were characterized by X-ray diffractometry and photoluminescence. The diffraction pattern of the mono-doped samples synthered at 800 °C for 16 h displayed peaks corresponding to the Y₃Al₅O₁₂ (YAG) phase, while the sample doped with the three ions revealed the presence of a mixture of Y₃Al₅O₁₂ (YAG) and Y₄Al₂O₉ (YAM) phases. The emission spectra of the three mono-doped YAG samples displayed the typical bands of the blue, green, and red emission of the corresponding lanthanide ions. As for the sample doped with the three lanthanide ions; it simultaneously emitted R, G and B lights. The green emission (546 nm) was more intense and narrow in relation to the red and blue emissions, which may be due to differences in the size of the three incorporated ions.     

Synthesis and properties of submicron range CaSO4:Eu particles

CaSO₄:Eu with particle size in submicron range was synthesized. Radiation induced Eu³⁺↔Eu²⁺ conversion as well as thermal conversion was studied. The samples showed thermal conversion above 400 °C. However, no radiation induced conversion in submicron range particles was observed. Particles heated above 400 °C coalesce and when heated at 925 °C bigger particles of 20 μm size were formed. Optical microscopy of these particles reveals red inclusion of about 5 μm inside CaSO₄ particle. It is speculated that the red inclusion is CaS:Eu²⁺.     

Blue light emission from Eu ions in sol-gel-derived Al2O3-SiO2 glasses

Blue light-emitting glasses were successfully prepared by doping Eu²⁺ ions in the system Al₂O₃-SiO₂. The Al₂O₃-SiO₂ glasses doped with Eu³⁺ ions were synthesized using a sol-gel method, followed by heating in hydrogen gas atmosphere to reduce into the Eu²⁺ ions. The obtained glasses exhibited emission spectra with peak at ∼450 nm due to 4f⁶5d→4f⁷ (⁸S_7/2) transition, the intensities of which strongly changed depending on their glass composition and heating conditions. The emission quantum efficiency of 48% was achieved by heating the glass with the ratio of Al³⁺ to Eu³⁺ at about 6 at 1000 °C in hydrogen gas atmosphere. It was found that the Al₂O₃-SiO₂ glasses were appropriate not only for homogeneously doping the Eu³⁺ ions in glass structure but also reducing to Eu²⁺ ions, resulting in enhanced blue light-emission properties.     

Energy transfers between Sm and Eu in YPO4, LaP5O14 and LaP3O9 phosphates. Potential quantum cutters for red emitting phosphors

This work concerns the studies of energy transfers between Sm³⁺ and Eu³⁺ ions in some phosphates as new luminescent materials emitting in the orange-red color. The choose of ions is based on the possibility of quantum cutting process and the matrices are selected according to the 5d bands position of Sm³⁺ ion. The Sm³⁺ and Eu³⁺ doped YPO₄, LaP₅O₁₄ and LaP₃O₉ are synthesized and spectroscopic studies in ultraviolet and vacuum ultraviolet ranges have been achieved.