Synthesis and Characterization of Fluorinated Polyimide Derived from 3,3′‐Diisopropyl‐4,4′‐diaminodiphenyl‐3′′,4′′‐difluorophenylmethane

A novel aromatic diamine monomer, 3,3′‐diisopropyl‐4,4′‐diaminodiphenyl‐3′′,4′′‐difluorophenylmethane (PAFM), was successfully synthesized by coupling of 2‐isopropylaniline and 3,4‐difluorobenzaldehyde. The aromatic diamine was adopted to synthesize a series of fluorinated polyimides by polycondensation with various dianhydrides: pyromellitic dianhydride (PMDA), 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA), 4,4′‐oxydiphthalic anhydride (ODPA) and 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA) via the conventional one‐step method. These polyimides presented excellent solubility in common organic solvents, such as N,N‐dimethylformamide (DMF), N,N‐dimethyl acetamide (DMAc), dimethyl sulfoxide (DMSO), N‐methyl‐2‐pyrrolidone (NMP), chloroform (CHCl₃), tetrahydrofuran (THF) and so on. The glass transition temperatures (T_g) of fluorinated polyimides were in the range of 260–306°C and the temperature at 10% weight loss in the range of 474–502°C. Their films showed the cut‐off wavelengths of 330–361 nm and higher than 80% transparency in a wavelength range of 385–463 nm. Moreover, polymer films exhibited low dielectric properties in the range of 2.76–2.96 at 1 MHz, as well as prominent mechanical properties with tensile strengths of 66.7–97.4 MPa, a tensile modulus of 1.7–2.1 GPa and elongation at break of 7.2%–12.9%. The polymer films also showed outstanding hydrophobicity with the contact angle in the range of 91.2°–97.9°.     

Novel fluorinated polyimides derived from an unsymmetrical diamine containing trifluoromethyl and methyl pendant groups

Novel fluorinated polyimides were prepared from an unsymmetrical diamine, 3‐methyl‐4‐(4‐amino‐2‐trifluoromethylphenoxy)‐4'‐aminobenzophenone ( 3 ), with four aromatic dianhydrides via a one‐step high‐temperature polycondensation procedure. All the obtained polyimides were soluble in some polar solvents such as NMP, DMAc, and DMF. Flexible and tough films were prepared by casting from polymer solution. These polyimide films exhibited high optical transparency, good mechanical and thermal properties. Moreover, they possessed low dielectric constants and low‐moisture absorption. Due to their properties, these fluorinated polyimides could be considered as photoelectric and microelectronic materials. Copyright © 2010 John Wiley & Sons, Ltd.     

New Soluble Polyimides with High Optical Transparency and Light Color Containing Pendant Trifluoromethyl and Methyl Groups

A new aromatic diamine containing trifluoromethyl and methyl groups, namely α,α‐bis(4‐amino‐3‐methylphenyl)‐4‐(trifluoromethyl)phenylmethane ( 1 ), was synthesized from 2‐methylaniline and 4‐(trifluoromethyl)benzaldehyde. A series of fluorinated polyimides (PIs) were prepared from the diamine with four commercially available aromatic tetracarboxylic dianhydrides using a one‐step high‐temperature polycondensation procedure. These obtained PIs showed excellent solubility, with the dissolvability at a concentration of 10 wt% in most solvents, and they could afford flexible and strong films. Thin films of these PIs exhibited high optical transparency and light color, with the cutoff wavelength at 324–357 nm and transmittance higher than 74% at 450 nm. Moreover, these PIs possessed eminent thermal stability and good mechanical properties.     

一种高可溶、高光学透明含氟聚酰亚胺的合成与表征

由自制芳香二胺单体9,9-双(3,5-二氟-4-胺基苯基)芴和商品化二酐单体4,4'-(六氟异丙基)双邻苯二甲酸酐经一步法高温缩聚制备了一种新型含氟聚酰亚胺.分别用FT-IR、1HNMR和19FNMR对所制聚酰亚胺结构进行了表征.结果证实其与所设计的结构完全一致,并且酰亚胺化反应完全.该含氟聚酰亚胺表现出高的溶解性:室温下在N-甲基-2-吡咯烷酮、N,N-二甲基乙酰胺、N,N-二甲基甲酰胺、氯仿、二氯甲烷、四氢呋喃等常规溶剂中的溶解度可达10wt%以上.由该聚酰亚胺溶液所制的薄膜无色透明,截断波长在315nm,400nm波长后的透光率在84%以上.此外该含氟聚酰亚胺还表现出良好的热学性能和机械性能:玻璃化转变温度在377℃,空气和氮气中10%热失重温度均在539℃以上;其薄膜的拉伸强度在70～80MPa,断裂伸长率在4%～8%,起始模量为2.6GPa.     

含氟聚酰亚胺及其在微电子工业中的研究进展Ⅱ含氟聚酰亚胺在微电子工业中的应用

综述了近年来国内外在含氟聚酰亚胺(PI)研究及应用领域中的最新进展情况。主要从现代微电子工业对相关材料的性能要求、标准型聚酰亚胺材料所面临的挑战以及新型含氟聚酰亚胺在微电子工业中的应用等几个方面进行了详细的综述。重点阐述了中国科学院化学研究所305组近几年在这方面的研究进展情况。并指出为了推动我国微电子工业的发展，研制开发低成本、高技术含量的含氟聚酰亚胺材料具有十分重要的现实意义．     

Novel Non‐Coplanar and Tertbutyl‐Substituted Polyimides: Solubility,Optical, Thermal and Dielectric Properties

A novel aromatic diamine monomer bearing tertbutyl and 4‐tertbutylphenyl groups, 3,3′‐ditertbutyl‐4,4′‐diaminodiphenyl‐4′′‐tertbutylphenylmethane (TADBP), was prepared and characterized. A series of non‐coplanar polyimides (PIs) were synthesized via a conventional one‐step polycondensation from TADBP and various aromatic dianhydrides including pyromellitic dianhydride (PMDA), 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA), 4,4′‐oxydiphthalic anhydride (OPDA), 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA) and 4,4′‐(hexafluoroisopropylidene)dipthalic anhydride (6FDA). All PIs exhibit excellent solubility in common organic solvents such as N,N‐dimethylformamide (DMF), N,N‐dimethylacetamide (DMAc), N‐methyl‐2‐pyrrolidone (NMP), dimethyl sulfoxide (DMSO), chloroform (CHCl₃), tetrahydrofuran (THF), and so on. Furthermore, the obtained transparent, strong and flexible polyimide films present good thermal stability and outstanding optical properties. Their glass transition temperatures (T_gs) are in the range of 298 to 347°C, and 10% weight loss temperatures are in excess of 490°C with more than 53% char yield at 800°C in nitrogen. All the polyimides can be cast into transparent and flexible films with tensile strength of 80.5–101 MPa, elongation at break of 8.4%–10.5%, and Young's modulus of 2.3–2.8 GPa. Meanwhile, the PIs show the cutoff wavelengths of 302–356 nm, as well as low moisture absorption (0.30% –0.55%) and low dielectric constant (2.78–3.12 at 1 MHz).     

DDBT类可溶性聚酰亚胺的合成与性能研究

由二甲基-5,5'-3,7-二苯并噻吩二胺（DDBT）和3,3',4,4'-二苯砚四羧酸二酐（DSDA）、2,2'-双（3,4-二羧酸）六氟丙烷二酐（……FDA）、均苯四羧酸二酐（PMDA）、联苯四羧酸二酐（BPDA）等多种二酐单体进行缩聚反应制备了新型可溶性聚酰亚胺。测定了其特性粘度为0.6-0.9dL/g;DDBT与DSDA、6FDA反应得到的聚酰亚胺在非质子强极性溶剂中具有良好的溶解性。用IR、热力学分析等手段对DDBT类聚酰亚胺进行了表征,并对可溶性DDBT-DSDA聚酰亚胺膜作了进一步的研究,推导出了苯在DDBT-DSDA聚酰亚胺膜中动态吸附初期的吸附方程。实验结果表明DDBT-DSDA聚酰亚胺膜对苯具有特殊的亲和力。     

Novel Soluble Polyimide Containing 4-tert-Butyltoluene Moiety: Synthesis and Characterization

Based on the synthesis of a rigid aromatic diamine, α,α‐bis(4‐aminophenyl)‐4‐(t‐butyl)toluene ( 1 ), a novel polyimide (PI) 3 was prepared from this diamine monomer and 4,4′‐oxydiphthalic dianhydride via a one‐step high‐temperature polycondensation. FT‐IR, ¹H NMR and elemental analysis were used to investigate the chemical structures of 1 and 3 . The results confirmed that they agreed with the proposed structures for both 1 and 3 completely. The obtained PI 3 showed excellent solubility in most common solvents such as N‐methyl‐2‐pyrrolidinone, N,N‐dimethylacetamide, N,N‐dimethylformamide, chloroform, dichloromethane and tetrahydrofuran. The resulting strong and flexible film exhibited high thermal stability with the glass transition temperature at 317°C and the temperature at 10% weight loss beyond 519°C in both air and nitrogen atmospheres. Moreover, the film also showed high optical transparency, low dielectric constant (3.13 at 1 MHz), low water absorption (0.40%) and hydrophobic character.     

含氟聚酰亚胺的研究进展

综述了含氟聚酰亚胺研究的新进展,介绍了含氟单体,聚合物合成方法及主要性质。着重介绍了含氟聚酰亚胺的物理化学性质,光学和电学性能以及气体选择透过性。同时简述全氟代聚酰亚胺的合成,性能及应用前景。     

Synthesis and characterization of organosoluble polyimides with trifluoromethyl‐substituted benzene in the side chain

New aromatic diamines substituted with a trifluoromethyl group in the side chain, 2,4‐diamino‐3′‐trifluoromethylazobenzene, 2,4‐diamino‐1‐[(4′‐trifluoromethylphenoxy) phenyl] aniline, and 3,5‐diamino‐1‐[(4′‐trifluoromethyl phenoxy) phenyl] benzamide were synthesized and characterized and used to prepare polyimides by a one‐step high‐temperature polycondensation method. Experimental results indicated that the prepared polyimides possess good solubility in strong organic solvents such as N‐methyl‐2‐pyrrolidinone, N,N′‐dimethylformamide, and N,N′‐dimethylacetamide. Homogeneous solutions with solid contents as high as 15–20% can be prepared, which are stable for storing longer than 2 weeks at room temperature. The polyimides exhibited glass‐transition temperatures of 249–292 °C and good thermal stability. The PI‐I_c and PI‐III_c films prepared by casting the fully imidized polymer solutions showed good transparency with cutoff wavelengths at 320–330 nm. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1572–1582, 2002     

Organosoluble and light‐colored fluorinated polyimides from 4,4′‐bis(4‐amino‐2‐trifluoromethylphenoxy)biphenyl and aromatic dianhydrides

A novel fluorinated diamine monomer based on 4,4′‐biphenol was synthesized via a straightforward, high‐yielding two‐step procedure. 4,4′‐Biphenol was reacted with 2‐chloro‐5‐nitrobenzotrifluoride in the presence of potassium carbonate to yield the intermediate dinitro compound, which was subsequently reduced to afford the fluorinated diamine, 4,4′‐bis(4‐amino‐3‐trifluoromethylphenoxy)biphenyl. A series of organosoluble fluorinated polyimides were prepared from the diamine with various aromatic dianhydrides via a conventional two‐step thermal imidization method. All polyimides were soluble in strong dipolar solvents such as N‐methyl‐2‐pyrrolidone and N,N‐dimethylacetamide. The polyimides showed excellent thermal and thermooxidative stability and good mechanical properties. No significant weight loss was observed below a temperature of 520 °C in nitrogen or in air, and the glass‐transition temperatures ranged from 247 to 313 °C. Low dielectric constants (2.57–3.65 at 10 kHz), low moisture absorption (0.1–0.7 wt %), and low color intensity were also observed. © 2002 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 524–534, 2002; DOI 10.1002/pola.10113     

Synthesis and properties of fluorinated polyimides from a new unsymmetrical diamine: 1,4‐(2′‐Trifluoromethyl‐4′,4′‐diaminodiphenoxy)benzene

A new aromatic, unsymmetrical ether diamine with a trifluoromethyl pendent group, 1,4‐(2′‐trifluoromethyl‐4′,4″‐diaminodiphenoxy)benzene, was successfully synthesized in three steps with hydroquinone as a starting material and polymerized with various aromatic tetracarboxylic acid dianhydrides, including 4,4′‐oxydiphthalic anhydride, 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride, 2,2′‐bis(3,4‐dicarboxyphenyl)‐hexafluoropropane dianhydride, and pyromellitic dianhydride, via a conventional two‐step thermal or chemical imidization method to produce a series of fluorinated polyimides. The polyimides were characterized with solubility tests, viscosity measurements, IR, ¹H NMR, and ¹³C NMR spectroscopy, X‐ray diffraction studies, and thermogravimetric analysis. The polyimides had inherent viscosities of 0.56–0.77 dL/g and were easily dissolved in both polar, aprotic solvents and common, low‐boiling‐point solvents. The resulting strong and flexible polyimide films exhibited excellent thermal stability, with decomposition temperatures (at 5% weight loss) above 522 °C and glass‐transition temperatures in the range of 232–272 °C. Moreover, the polymer films showed outstanding mechanical properties, with tensile strengths of 74.5–121.7 MPa, elongations at break of 6–13%, and initial moduli of 1.46–1.95 GPa, and good dielectric properties, with low dielectric constants of 1.82–2.53 at 10 MHz. Wide‐angle X‐ray diffraction measurements revealed that these polyimides were predominantly amorphous. These outstanding combined features ensure that the polymers are desirable candidate materials for advanced microelectronic applications. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6836–6846, 2006     

Synthesis and characterization of novel fluorinated polyimides based on 2,7‐bis(4‐amino‐2‐trifluoromethylphenoxy)naphthalene

A new trifluoromethyl‐substituted bis(ether amine) monomer, 2,7‐bis(4‐amino‐2‐trifluoromethylphenoxy)naphthalene, was synthesized. It led to a series of novel fluorinated polyimides by thermal and chemical imidization routes when reacted with various commercially available aromatic tetracarboxylic dianhydrides. Most of the polyimides obtained from both routes were soluble in many organic solvents, such as N,N‐dimethylacetamide. All the polyimides could afford transparent, flexible, and strong films with low moisture absorptions of 0.3–0.6%, low dielectric constants of 2.52–3.27 at 10 kHz, and an ultraviolet–visible absorption cutoff wavelength at 377–436 nm. The glass‐transition temperatures of the polyimides were in the range of 244–297 °C, and the 5% weight‐loss temperatures were higher than 550 °C. For a comparative study, a series of analogous polyimides based on 2,7‐bis(4‐aminophenoxy)naphthalene were also prepared and characterized. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2001–2018, 2003     

含苯并噻唑氟化聚酰亚胺制备及非线性光学性质

采用Mitsunobu反应将杂环偶氮生色分子键入氟化聚酰亚胺母体制备新型的侧链含氟聚酰亚胺非线性光学(NLO)材料.采用傅里叶变换红外(FT-IR)光谱、紫外-可见(UV-Vis)光谱、1H核磁共振(1HNMR)谱和凝胶色谱(GPC)对材料进行表征.热分析结果表明侧链型聚酰亚胺具有较高的玻璃化转变温度(Tg)(184-188℃),热分解温度(Td)高达322℃.采用简单全反射法于1550nm处测定聚酰亚胺的电光系数(γ33),含苯并噻唑偶氮苯胺的聚酰亚胺(PI1)具有较高的电光系数15pm·V-1.     

Synthesis and Characterization of Novel Polyimides Based on Pyridine-containing Diamine

A new aromatic diamine monomer containing pyridine unit, 2,6-bis （4-aminophenoxy- 4＇-benzoyl）pyridine（BABP）, was synthesized in three steps, starting from 2,6-pyridinedicarboxyl chloride. A series of novel pyridine-containing polyimides were prepared v/a the polycondensation of BABP with various aromatic dianhydrides through poly（amic acid） precursors, and thermal or chemical imidization of the precursors. The polyimides exhibit desirable properties, e.g., good solubility in N-methyl-2-pyrrolidone and m-cresol, excellent thermal stability and film-forming capability, as well as high inherent viscosity, indicating high molecular weight.     

High solubility,low‐dielectric constant,and optical transparency of novel polyimides derived from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4″‐isopropyltoluene

A series of novel polyimides (PIs) ( 3a–d ) were prepared from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4 ″ ‐isopropyltoluene ( 1 ) with four aromatic dianhydrides via a one‐step high temperature polycondensation procedure. The obtained PIs showed excellent solubility, with most of them dissoluble at a concentration of 10 wt % in amide polar solvents and chlorinated solvents. Their films were nearly colorless and exhibited high‐optical transparency, with the UV cutoff wavelength in the range of 328–353 nm and the transparency at 450 nm >80%. They also showed low‐dielectric constant (2.49–2.94 at 1 MHz) and low‐water absorptions (0.44–0.65%). Moreover, these PIs possessed high‐glass transition temperatures (T_g) beyond 327 °C and excellent thermal stability with 10% weight loss temperatures in the range of 530–555 °C in nitrogen atmosphere. In comparison with some fluorinated poly(ether imide)s derived from the trifluoromethyl‐substituted bis(ether amine)s, the resultant PIs 3a–d showed better solubility, lower cutoff wavelength, and higher T_g. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3309–3317, 2009     

Molecular Dynamics Simulations of Helium Permeation in Polyimides with a Bulky Dianhydride and a Fluorinated Diamine

Fully‐atomistic molecular dynamics (MD) simulations have been carried out to model helium transport through four different glassy polyimides. While the polymer matrices had been pre‐validated, specific parameters and combination rules were used here in order to describe helium‐helium and helium‐polymer interactions. Gas permeabilities are in very good agreement with experimental evidence. Two ways to decrease chain cohesion and improve gas transport were considered – the replacement of an ODPA by a bulky BCDA dianhydride, and the substitution of a site on an ODA diamine by a CF₃. The fluorinated polyimide appears to be the most promising material with more heterogeneity in the void‐space distribution, the highest model permeability and fewer constraints from an experimental point of view.

     

有机可溶性含氟不对称聚酰胺酰亚胺的合成与性能

采用不对称联苯二酐单体2,3,3′,4′-联苯四甲酸二酐(a-BPDA)与3-氨基-2,4,5-三氟苯甲酸(3FAB)反应制备了一种新型不对称二酸化合物2,3,3′,4′-联苯四甲酸-N,N′-双(3-羧基-2,5,6-三氟苯基)二酰亚胺 (a-BPFDI).以此两种酸为原料、N-甲基-2-吡咯烷酮(NMP)为溶剂、亚磷酸三苯酯(TPP)与吡啶为缩合剂、氯化钙为催化剂,通过Yamazaki-Higashi反应,直接与3种芳香族二胺单体反应制得一系列聚酰胺酰亚胺(PAI).研究表明:PAI材料在极性非质子性溶剂中具有优良的溶解性能,其薄膜的玻璃化转变温度超过250 ℃,氮气中起始热分解温度超过410 ℃.此外,PAI薄膜还具有良好的力学性能以及介电性能.厚度为10 μm左右的PAI薄膜在可见光区(400～700 nm)的透光率达到或超过80%.