Mutual spontaneous and electrosurface processes at heterophase interfaces WO<Subscript>3</Subscript>|Me<Subscript>2</Subscript>(WO<Subscript>4</Subscript>)<Subscript>3</Subscript> (Me = In,Eu, Sc)

For the first time ever it is demonstrated in this work that, in spontaneous conditions and following the imposition of an electric field, mutual penetration of components of WO₃ and Me₂(WO₄)₃ occurs at heterophase interfaces WO₃|Me₂(WO₄)₃ where Me = In, Eu, or Sc. Tungstic oxide WO₃ is pulled onto the inner surface of ceramic Me₂(WO₄)₃ and, in turn, components of Me₂(WO₄)₃ penetrate onto the surface of grains of ceramic WO₃, which is confirmed by the method of x-ray—fluorescence analysis. Data concerning the conductivity and transport numbers of Eu₂(WO₄)₃ and a composite on its basis, which was manufactured as a result the electrosurface transport of WO₃, are obtained for the first time ever. With allowance made for the data on the O_2? character of the ionic conduction in MeWO₄ and Eu₂(WO₄)₃ it is concluded that the type of ionic carriers in tungstates (Me ⁿ⁺)_2/n [WO₄] makes no impact on the mechanism of spontaneous and field-induced processes that are developing at the (Me ⁿ⁺)_2/n [WO₄]|WO₃ interfaces.     

A New Molybdophosphate Constructed From {Mo<Stack><Subscript>2</Subscript><Superscript>V</Superscript></Stack>O<Subscript>4</Subscript>(H<Subscript>2</Subscript>O)<Subscript>6</Subscript>}<Superscript>2+</Superscript> and 1-Hydroxyethylidenediphosphonate

A new molybdophosphate (NH₄)₈{Mo₂^VO₄[(Mo₂^VIO₆)CH₃C(O)(PO₃)₂]₂}·14H₂O (1), has been synthesized by the reaction of {Mo₂^VO₄(H₂O)₆}²⁺ fragments with 1-hydroxyethylidenediphosphonate (hedp HOC(CH₃)(PO₃H₂)₂), and it is characterized by ³¹P NMR, IR, UV, element analysis, TG and single-crystal X-ray analysis. The structure analysis reveals that the polyoxoanion can be described as two {(Mo₂^VIO₆)(CH₃C(O)(PO₃)₂} units connected by a {Mo₂^VO₄}²⁺ moiety. In the structure, the six Mo atoms are arranged into a new “W-shaped” structure, which represents a new kind of molybdophosphate.     

Solid-phase synthesis of sodium-bismuth tungstate NaBi(WO<Subscript>4</Subscript>)<Subscript>2</Subscript>

Results of a solid-phase synthesis of polycrystalline sodium-bismuth tungstate NaBi(WO₄)₂ from NaNO₃, Na₂WO₄, Bi₂O₃, and WO₃ are presented. The optimal synthesis conditions are determined and a technological flow chart for synthesis of a single-phase product is suggested.     

Synthesis and structure of the framework coordination polymer based on the cluster anion [Nb<Subscript>4</Subscript>OTe<Subscript>4</Subscript>(CN)<Subscript>12</Subscript>]<Superscript>6−</Superscript> and Mn<Superscript>II</Superscript> aqua complexes

Dark-brown plate crystals of the [Mn₇(H₂O)₂₆{Nb₄OTe₄(CN)₁₂} ₂](OH)₂·11H₂O compound (1) were prepared by the reaction of an aqueous ammonia solution of the K₆[Nb₄OTe₄(CN)₁₂]{K₂CO₃{KOH{8H₂O complex with a glycerol solution of manganese(II) nitrate. The structure of complex 1 was established by X-ray diffraction. Compound 1 has a polymer structure containing four types of manganese atoms. The nitrogen atoms of eight cyano groups of the tetranuclear niobium cluster are coordinated to the manganese atoms to form a {2,3,8}-connected three-dimensional network. Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 2, pp. 224–228, February, 2007.     

Electrochemistry of solid-phase reactions: Phase formation in the In2O3-WO3 system. Processes at the WO3|In2O3 and WO3|In6WO12 interfaces

Reactions of interactions at the WO₃|In₂O₃ and WO₃|In₆WO₁₂ heterophase reaction interfaces, whose main product is In₂(WO₄)₃, are studied by electrochemical methods for the first time ever. Due to a far greater n type conductance inherent in the initial substances, the reactions are a model object for the development of methodology of the electrochemical approach. Both reactions are discovered to proceed at the expense of the transport of components of WO₃ and no evidence is discovered for the contribution of In³⁺ into diffusion and migration. Consisted data are obtained between the polarity of a spontaneously generated reaction difference of potentials and the direction of the field that accelerates the reaction: the current that is passed through electrochemical cells accelerates the reactions exclusively at the (−)-potential of a brick of WO₃. A difference is discovered between the charge and mass transport paths—spontaneous and field-induced mass transport of WO₃ or its components occurs via heterophase interfaces and adjacent areas and does not touch upon the In₂(WO₄)₃ grains. Shown is the antibatic character of the behavior exhibited by dependences of identical properties of cells (potential drop across a cell) following a change in the dc polarity. A possible role of a reactionless electrosurface transport of WO₃ in the mechanism of reaction and evolution of electrochemical properties of model electrochemical cells is demonstrated. The obtained data may or may not testify in favor of a hypothesis that presumes a prevailing role of the {WO₄}²⁻ mobility in the In₂(WO₄)₃ structure. Original Russian Text ? A.Ya. Neiman, T.E. Kulikova, 2007, published in Elektrokhimiya, 2007, Vol. 43, No. 6, pp. 714–726. Based on the report delivered at the 8th International Meeting on Fundamental Problems of Solid-State Ionics, Chernogolovka (Russia), 2006.     

Kinetics of the uninhibited and ethanol-inhibited CoO,Co<Subscript>2</Subscript>O<Subscript>3</Subscript> and Ni<Subscript>2</Subscript>O<Subscript>3</Subscript> catalyzed autoxidation of sulfur(IV) in alkaline medium

For getting an insight into the mechanism of atmospheric autoxidation of sulfur(IV), the kinetics of this autoxidation reaction catalyzed by CoO, Co₂O₃ and Ni₂O₃ in buffered alkaline medium has been studied, and found to be defined by Eqs. I and II for catalysis by cobalt oxides and Ni₂O₃, respectively.

Kinetics of formation of barium tungstate in equimolar powder mixture of BaCO<Subscript>3</Subscript> and WO<Subscript>3</Subscript>

The formation of Barium monotungstate (BaWO₄) particles in equimolar powder mixtures of BaCO₃ and WO₃ was examined under isothermal and non-isothermal conditions upon heating in air at 25–1200 °C, using thermogravimetry. Concurrence of the observed mass loss (due to the release of CO₂) to the occurrence of the formation reaction was evidenced. Accordingly, the extent of reaction (x) was determined as a function of time (t) or temperature (T). The x–t and x–T data thus obtained were processed using well established mathematical apparatus and methods, in order to characterize nature of reaction rate-determining step, and derive isothermal and non-isothermal kinetic parameters. Moreover, the reaction mixture quenched at various temperatures (600–1,000 °C) in the reaction course was analyzed by various spectroscopic and microscopic techniques, for material characterization. The results obtained indicated that the reaction rate may be controlled by unidirectional diffusion of WO₃ species across the product layer (BaWO₄), which was implied to form on the barium carbonate particles. The isothermally determined activation energy (118–125 kJ/mol) was found to be more credible than that (245 kJ/mol) determined non-isothermally.     

Efficient and convenient oxidation of cyclohexene to adipic acid with H<Subscript>2</Subscript>O<Subscript>2</Subscript> catalyzed by H<Subscript>2</Subscript>WO<Subscript>4</Subscript> in acidic ionic liquids

A simple, efficient, and eco-friendly catalytic system for the oxidation of cyclohexene to adipic acid with H₂O₂ catalyzed by H₂WO₄ in Brønsted acidic ionic liquids under solvent-free conditions has been developed. Reaction conditions such as the catalysts, the types of anions and cations for Brønsted acidic ionic liquids, reaction temperature, and the amount of hydrogen peroxide, were investigated. Moreover, the Hammett acidity functions (H ₀) of Brønsted acidic ionic liquids were determined using UV–visible spectrophotometry. The optimum reaction condition identified was n(H₂WO₄):n(Brønsted acidic ionic liquids):n(cyclohexene):n(H₂O₂) = 0.02:0.02:1:4.4, and the yield of adipic acid was 96% under the reaction scale of 10 mmol. The catalytic system can be easily recovered and reused for four reaction runs without significant loss of catalytic activity. Simple operation of the catalyst system and avoidance of the emission of nitrous oxide are the benefits of this work.     

New ruthenocene-based ruthenium pincer complex bearing the C<Subscript>5</Subscript>Me<Subscript>4</Subscript>CF<Subscript>3</Subscript> ligand

The first (trifluoromethyl)tetramethylruthenocene-based ruthenium pincer complex RuCl(CO)[{2,5-(Bu ₂ ^t PCH₂)₂C₅H₂}Ru(C₅Me₄CF₃)] was synthesized by cyclometallation of the bisphosphine ligand {1,3-(Bu ₂ ^t PCH₂)₂C₅H₂}Ru(C₅Me₄CF₃) with RuCl₂(DMSO)₄ in 2-methoxyethanol in the presence of NEt₃. The new complex was fully characterized by ¹H, ¹⁹F, ³¹P{¹H}, ¹³C{¹H} NMR and IR spectroscopy.     

Thermoanalytical study of precursors for In<Subscript>2</Subscript>S<Subscript>3</Subscript> thin films deposited by spray pyrolysis

Thermal decomposition of precursors for In₂S₃ thin films obtained by drying aqueous solutions of InCl₃ and SC(NH₂)₂ at the In:S molar ratios of 1:3 (1) and 1:6 (2) was monitored by simultaneous TG/DTA/EGA-FTIR measurements in the dynamic 80%Ar + 20%O₂ atmosphere. XRD and FTIR were used to identify the dried precursors and products of the thermal decomposition. The precursors 1 and 2 are complex compounds, while in 2 free SC(NH₂)₂ is also present. The thermal degradation of 1 and 2 in the temperature range of 30–900 °C consists of four mass loss steps, the total mass loss being 89.1 and 78.5%, respectively. According to XRD, In₂S₃ is formed below 300 °C, crystalline In_2.24(NCN)₃ is detected only in 1 above 520 °C and In₂O₃ is the final decomposition product at 900 °C. The gaseous species evolved include CS₂, NH₃, H₂NCN, HNCS, which upon oxidation yield also COS, SO₂, HCN and CO₂.     

Effect of tungsten oxide loading on metathesis activity of ethene and 2-butene over WO<Subscript>3</Subscript>/SiO<Subscript>2</Subscript> catalysts

The metathesis of ethene and 2-butene to propene was studied over WO₃/SiO₂ catalysts with various WO₃ loadings (2, 4, 8, 12, 16, and 24 wt%). The 2-butene conversion and propene selectivity increased greatly with WO₃ loading increasing from 2 to 8 wt%, reached maximum at 8–12 wt% WO₃ loading, and then decreased when the WO₃ loading was higher than 12 wt%. From the above results and taking the economics into account, the optimal amount of WO₃ loading was ~8 wt%. The catalysts were characterized by physico-chemical and spectroscopic techniques to elucidate the effect of different tungsten oxide loadings on the metathesis reactivity of ethene and 2-butene. The characterization data indicated that three types of tungsten species (i.e., surface tetrahedral tungsten species, surface octahedral polytungstate species, and WO₃ crystallites) were present in the catalysts. It was found that WO₃ was not the active centers, and surface tetrahedral tungsten species might be more active than octahedral polytungstate species in metathesis reaction. The reduced form of tungsten species [W⁺⁴, W⁺⁵, and W^+(6−y) (0 < y < 1)] may be the suitable state of W species acting as metathesis active centers.     

Phase formation in the InPO<Subscript>4</Subscript>-Na<Subscript>3</Subscript>PO<Subscript>4</Subscript>-Li<Subscript>3</Subscript>PO<Subscript>4</Subscript> ternary system

The 950°C isothermal section of the InPO₄-Na₃PO₄-Li₃PO₄ ternary system was studied and constructed; one-, two, and three-phase fields are outlined. Five solid-solution regions exist in the system: solid solutions based on the complex phosphate LiNa₅(PO₄)₂ (olympite structure), the indium ion stabilized high-temperature Na₃PO₄ phase (Na_{3(1 − x)}In _x (PO₄); space group Fm [`3]\bar 3 m), the complex phosphate Na₃In₂(PO₄)₃, and the α and β phases of the compound Li₃In₂(PO₄)₃. A narrow region of melt was found in the vicinity of eutectic equilibria. All the phases detected in the system are derivatives of phases existing in the binary subsystems. Isovalent substitution of lithium for sodium in Na₃In₂(PO₄)₃ leads to a significant increase in the region of a NASICON-like solid solution.     

Syntheses and Structure of Gd<Subscript>3</Subscript>Rh<Subscript>1.940(7)</Subscript>In<Subscript>4</Subscript>

Summary. The gadolinium–rhodium–indide Gd₃Rh_1.940(7)In₄ was prepared by arc-melting of the elements and subsequent annealing in a corundum crucible in a sealed silica tube. Gd₃Rh_1.940(7)In₄ adopts the hexagonal Lu₃Co_1.87In₄ type, space group , a = 781.4(5), c = 383.8(3) pm, wR2 = 0.0285, BASF = 0.375(1) (merohedric twinning via a twofold axis (xx0)), 648 F² values, 22 variables. The structure is derived from the well known ZrNiAl type through an ordering of rhodium and indium atoms on the Ni2 sites. The Rh/In ordering forces a reduction of the space group symmetry from to , leading to merohedric twinning for the investigated crystal. The Rh1 site has an occupancy of only 94.0(7)%. The investigated crystal had a composition Gd₃Rh_1.940(7)In₄. The main geometrical motif are three types of centered, tricapped trigonal prisms, i.e., [Rh1In2₆Gd₃], [Rh2Gd₆In2₃], and [In1Gd₆In2₃]. The shortest interatomic distances occur for Rh–In (276–296 pm) followed by In–In (297 pm). Together, the rhodium and indium atoms build up a three-dimensional [Rh_1.940(7)In₄] network, in which the gadolinium atoms fill slightly distorted pentagonal channels. The crystal chemistry of Gd₃Rh_1.940(7)In₄ is discussed on the basis of a group-subgroup scheme.     

Preparation of novel visible-light-driven In<Subscript>2</Subscript>O<Subscript>3</Subscript>–CaIn<Subscript>2</Subscript>O<Subscript>4</Subscript> composite photocatalyst by sol–gel method

Novel visible-light-activated In₂O₃–CaIn₂O₄ photocatalysts were developed in this paper through a sol–gel method. The photocatalytic activities of In₂O₃–CaIn₂O₄ composite photocatalysts were investigated based on the decomposition of methyl orange under visible light irradiation (λ > 400 nm). The obtained samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrum (EDS), X-ray photoelectron spectroscopy (XPS) and UV–vis diffused reflectance spectroscopy (DRS). The results revealed that the In₂O₃–CaIn₂O₄ composite samples with different In₂O₃ and CaIn₂O₄ content can be obtained by controlling the synthesis temperature, and the composite photocatalysts extended the light absorption spectrum toward the visible region. The photocatalytic tests indicated that the composite samples demonstrated high visible-light activity for decomposition of methyl orange. The significant enhancement in the In₂O₃–CaIn₂O₄ photo-activity under visible light irradiation can be ascribed to the efficient separation of photo-generated carriers in the In₂O₃ and CaIn₂O₄ coupling semiconductors.     

Composition of the gas phase over Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and the enthalpies of atomization of AlO,Al<Subscript>2</Subscript>O,and Al<Subscript>2</Subscript>O<Subscript>2</Subscript>

The A1, O, AlO, A1₂O, Al₂O₂, WO₂, and WO₃, partial pressures in the vapor over Al₂O₃ in a tungsten Knudsen effusion cell between 2300 and 2600 K were derived from A1⁺, O⁺, AlO⁺, A1₂O⁺, Al₂O₂⁺, WO₂⁺, and WO₃⁺, ion intensities. The mass spectrometer was calibrated against the equilibrium constant of the WO₃(g) = WO₂(g) + O(g) reaction. Refined values of the ionization cross sections of AlO and A1₂O₂ were used in the partial pressure calculations. The enthalpies of atomization of aluminum suboxides were determined to be Δ_at H ^o(AlO, g, 0) = 510.7 ± 3.3 kJ mol⁻¹, Δ_at H ^o(Al₂O, g, 0) = 1067.2 ± 6.9 kJ mol⁻¹, and Δ_at H ^o(Al₂O₂, g, 0) = 1556.7 ± 9.9 kJ mol⁻¹.     

Electrochromic properties of WO<Subscript>3</Subscript> and WO<Subscript>3</Subscript>:P thin films

WO₃ and WO₃:P (5 mol% H₃PO₄) thin films were prepared using the sol-gel route and the electrochromic properties of the films were investigated using in situ spectroelectrochemical methods. The measurements were performed in propylene carbonate solution with 0.1 M LiClO₄ as electrolyte. During the cathodic polarization at –0.8 V a blue coloration is observed with a reversible variation between 14% and 84% of the transmittance at λ=633 nm. The kinetics for the bleaching process is faster for the WO₃:P film than for the undoped WO₃ film. Electronic Publication     

Kinetics and mechanisms of homogeneous catalytic reactions: Part 13. Regioselective reduction of quinoline catalysed by Rh(acac)(CO)[P(<Superscript>t</Superscript>Bu)(CH<Subscript>2</Subscript>CH=CH<Subscript>2</Subscript>)<Subscript>2</Subscript>]

The complex Rh(acac)(CO)[P(^tBu)(CH₂CH=CH₂)₂] (1) proved to be an efficient precatalyst for the regioselective hydrogenation of quinoline (Q) to 1,2,3,4-tetrahydroquinoline (THQ) under mild reaction conditions (125 °C and 4 atm H₂). A kinetic study of this reaction led to the rate law:

$$ r \, = \{ K_{1} k_{2} /(1 \, + \, K_{1} {\text{H}}_{ 2} )\} [{\text{Rh}}][{\text{H}}_{ 2} ]^{2} $$

which becomes

$$ r \, = \, K_{1} k_{2} [{\text{Rh}}][{\text{H}}_{ 2} ]^{2} $$

at hydrogen pressures below 4 atm. The active catalytic species is the cationic complex {Rh(Q)₂(CO)[P(^tBu)(CH₂CH=CH₂)₂]}⁺ (2). The mechanism involves the partial hydrogenation of one coordinated Q of (2) to yield a complex containing a 1,2-dihydroquinoline (DHQ) ligand, {Rh(DHQ)(Q)(CO)[P(^tBu)(CH₂CH=CH₂)₂]}⁺ (3), followed by hydrogenation of the DHQ ligand to give THQ and a coordinatively unsaturated species {Rh(Q)(CO)[P(^tBu)(CH₂CH=CH₂)₂]}⁺ (4); this reaction is considered to be the rate-determining step. Coordination of a new Q molecule to (4) regenerates the active species (2) and restarts the catalytic cycle.

     

Five-component reciprocal systems Na,K∥Cl,CO<Subscript>3</Subscript>,MoO<Subscript>4</Subscript>,WO<Subscript>4</Subscript> and Na,K∥F,CO<Subscript>3</Subscript>,MoO<Subscript>4</Subscript>,WO<Subscript>4</Subscript>

Five-component reciprocal systems Na,K∥Cl,CO₃,MoO₄,WO₄ and Na,K∥F,CO₃,MO₄,WO₄ have been studied by differential thermal analysis (DTA) and X-ray powder diffraction (XPD). The systems have been triangulated to phase simplexes. The main reciprocal and complex-formation reactions have been revealed. The stability of [Na,K]₂CO₃, Na₂[Mo,W]O₄, and K₂[Mo,W]O₄ binary solid solutions and the nonexistence of quintuple invariant points in the title systems have been verified.     

Deposition conditions,composition, and structure of chemically deposited In<Subscript>2</Subscript>Se<Subscript>3</Subscript> films

In₂Se₃ films up to 300 nm thick have been obtained for the first time by hydrochemical deposition on glass, glass ceramic, and molybdenum substrates in the In(NO₃)₃–C₄O₆H₆–CSeN₂H₄ system with the use of selenourea as a chalcogenizing agent. The phase and element composition and morphological features of layers obtained at 353 and 363 K have been studied by X-ray photoelectron spectroscopy, energy-dispersive electron probe X-ray microanalysis, and scanning electron microscopy. The optical band gap width has been determined.     

Interactions in the NdF<Subscript>3</Subscript>-Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>-MF<Subscript>2</Subscript> (M = Ba,Sr) systems

Isothermal anneals (at 873 K) and powder X-ray diffraction were used to study isothermal sections of phase diagrams of the NdF₃-Nd₂O₃-MF₂ (M = Ba, Sr) systems. In studying the NdF₃-Nd₂O₃-BaF₂ system, classical solid-phase synthesis was supplemented with mechanochemical activation of feedstock mixtures or BaF₂ activated with gaseous hydrogen fluoride was used. In both systems, a solid solution with the fluorite structure based on MF₂ and NdOF phases, a solid solution with the tysonite structure based on NdF₃, and an ordered fluorite-related phase Ba₄Nd₃F₁₇ were found. The NdOF-based solid solutions were shown to have polymorphism: β_trig ai α_cub at ≈800 K; a new trigonal phase of these solid solutions has been discovered. The effect of a dimensional factor $\left( {R_{Ba^{2 + } } > R_{Sr^{2 + } } } \right)$\left( {R_{Ba^{2 + } } > R_{Sr^{2 + } } } \right) on phase formation and unit cell parameters of the solid solutions was traced.