Synthesis of nanocrystalline Zn0.5Mn0.5Fe2O4 via in situ polymerization technique

Nanocrystalline Zn_0.5Mn_0.5Fe₂O₄ was synthesized through the pyrolysis of polyacrylate salt precursors prepared via in situ polymerization of the metal salts and acrylic acid. The pyrolysis behavior of the polymeric precursors was studied by use of thermal analysis. The as-obtained product was characterized by powder X-ray diffraction (XRD), transmission electron microscope (TEM), electron diffraction (ED) pattern, scanning electron microscopy (SEM) and electron dispersive X-ray (EDX) analysis. The results revealed that the particle size is in the range of 15–25 nm for Zn-Mn ferrites with good crystallinity. Magnetic properties of the sample at 300 K were measured using a vibrating sample magnetometer, which showed that the sample exhibited characteristics of superparamagnetism.     

针状纳米MnxNi0.5-xZn0.5Fe2O4的共沉淀法制备及表征

通过在碱液中共沉淀Mn²⁺、Ni²⁺和Fe²⁺后制备了棒状的前躯体,前躯体于不同温度煅烧后制得了Mn_xNi_0:5-xZn_0:5Fe₂O₄棒状体. 利用X射线衍射仪和透射电镜对棒状体的物相、形貌及粒径进行了表征,并利用振动样品磁强计对磁性能进行研究. 结果表明长径比大于15的棒状,随着x值的增加,Mn_xNi_0:5-xZn_0:5Fe₂O₄样品的直径增加,长度下降,长径比变小,当x=0.5时其直径在50 nm左右而长径比减小到7～8. 随着x值的增加,样品的矫顽力先增加后减少,x值达到0.4时样品的矫顽力再次增加,当煅烧温度为600 oC,x=0.5时样品的矫顽力最大为134.3 Oe. 饱和磁化强度随着x值的增加先增加后减少,当煅烧温度为800 oC和x=0.2时达到最大为68.5 Oe.     

Preparation and magnetic properties of BaFe12O19/Ni0.8Zn0.2Fe2O4 nanocomposite ferrite

Nanocomposite of hard (BaFe₁₂O₁₉)/soft ferrite (Ni_0.8Zn_0.2Fe₂O₄) have been prepared by the sol–gel process. The nanocomposite ferrite are formed when the calcining temperature is above 800 °C. It is found that the magnetic properties strongly depend on the presintering treatment and calcining temperature. The “bee waist” type hysteresis loops for samples disappear when the presintering temperature is 400 °C and the calcination temperature reaches 1100 °C owing to the exchange-coupling interaction. The remanence of BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite with the mass ratio of 5:1 is higher than a single phase ferrite. The specific saturation magnetization, remanence magnetization and coercivity are 63 emu/g, 36 emu/g and 2750 G, respectively. The exchange-coupling interaction in the BaFe₁₂O₁₉/Ni_0.8Zn_0.2Fe₂O₄ nanocomposite ferrite is discussed.     

(Bi,La)4Ti3O12-Sr(Bi,La)4Ti4O15共生结构铁电材料性能研究

采用固相烧结工艺，制备了不同La掺杂量(x=0.00，0.25，0.50，0.75，1.00，1.25和1.50) 的(Bi, La)₄Ti₃O₁₂-Sr(Bi, La)₄Ti4O₁₅ (SrBi_8-xLa_xT i₇O₂₇)共生结构铁电陶瓷样品.用x射线衍射对其进行微结构分析 ，并测量铁 关键词： 4Ti₃O₁₂-SrBi₄Ti₄O₁₅')" href="#">Bi₄Ti₃O₁₂-SrBi₄Ti_{4O15 La掺杂 铁电性能 居里温度 弛豫铁电}     

Synthesis and ferroelectric properties of bismuth layer-structured (Bi7−xSrx)(Fe3−xTi3+x)O21 solid solutions

Bismuth layer-structured (Bi_7−xSr_x)(Fe_3−xTi_3+x)O₂₁ (BSFT) ceramics were synthesized and the ferroelectric properties and crystal structure were investigated. X-ray powder diffraction profiles and refinement of the lattice parameters indicated single phase BSFT was obtained in the composition range 0-1.5. The lattice parameter b of BSFT remained almost constant, while a slight decrease in the lattice parameter a was observed by the Sr and Ti substitution for Bi and Fe, respectively, which indicated an increase in the orthorhombicity. The dependence of the BSFT lattice parameter on temperature implied a phase transition from the orthorhombic to the tetragonal phase, which was in good agreement with the Curie temperature. The remnant polarization P_r, of BSFT was significantly improved by the Sr and Ti substitution for Bi and Fe, and ranged from 9 to 16 μC/cm², although no remarkable variation in the coercive field E_c was observed. As a result, a well-saturated P-E hysteresis loop of BSFT ceramic was obtained at x=0.5 with a P_r of 30 μC/cm at an applied voltage of 280 kV/cm.     

CaCu3Ti4O12陶瓷的微观结构和电学性能

利用传统的固相反应工艺，在不同的烧结温度下制备了一系列的CaCu₃Ti₄O₁₂陶瓷样品，考察了其微观结构以及介电和复阻抗方面的电学性质.研究发现这些样品在微观结构方面可分为三种类型，高介电性与微观结构有着密切的关联性.室温下，样品的低频介电常数随陶瓷晶粒尺寸的增大而提高.随着测试温度的升高，不同微观结构类型的样品呈现出不同的电学性质的变化，但其中也存在着一些相同的特征.高温下，介电频谱呈现出一个低频介电响应和两个类Debye型弛豫色散，复阻抗谱呈现出三个Cole-Cole半圆弧.将实验上观测到的电学性质的起因归于陶瓷多晶微结构中的晶畴、晶界和晶粒内的缺陷. 关键词： 3Ti₄O₁₂')" href="#">CaCu₃Ti₄O₁₂ 微观结构 电学性质     

Microstructures and microwave dielectric properties of La1-xBx(Mg0.5Sn0.5)O3 ceramics

The microwave dielectric properties of La_1-xB_x(Mg_0.5Sn_0.5)O₃ ceramics were examined with a view to their exploitation for mobile communication. The La_1-xB_x(Mg_0.5Sn_0.5)O₃ ceramics were prepared by the conventional solid-state method with various sintering temperatures. The X-ray diffraction patterns of the La_0.995B_0.005(Mg_0.5Sn_0.5)O₃ ceramics revealed no significant variation of phase with sintering temperatures. A maximum apparent density of 6.58 g/cm³, a dielectric constant (ε_r) of 19.8, a quality factor (Q × f) of 41,800 GHz, and a temperature coefficient of resonant frequency (τ_f) of −86 ppm/°C were obtained for La_0.995B_0.005(Mg_0.5Sn_0.5)O₃ ceramics that were sintered at 1500 °C for 4 h.     

Ferroelectric properties of bilayer structured Pb(Zr0.52Ti0.48)O3/SrBi2Ta2O9 (PZT/SBT) thin films on Pt/TiO2/SiO2/Si substrates

Pb(Zr_0.52Ti_0.48)O₃ (PZT) thin films with large remanent polarization and SrBi₂Ta₂O₉ (SBT) thin films with excellent fatigue-resisting characteristic have been widely studied for non-volatile random access memories, respectively. To combine these two advantages_, bilayered Pb(Zr_0.52Ti_0.48)O₃/SrBi₂Ta₂O₉ (PZT/SBT) thin films were fabricated on Pt/TiO₂/SiO₂/Si substrates by chemical solution deposition method. X-ray diffraction patterns revealed that the diffraction peaks of PZT/SBT thin films were completely composed of PZT and SBT, and no other secondary phase was observed. The electrical properties of the bilayered structure PZT/SBT films have been investigated in comparison with pure PZT and SBT films. PZT/SBT bilayered thin films showed larger remanent polarization (2P_r) of 18.37 μC/cm² than pure SBT and less polarization fatigue up to 1 × 10⁹ switching cycles than pure PZT. These results indicated that this bilayered structure of PZT/SBT is a promising material combination for ferroelectric memory applications.     

Influence of Lu2O3 on electrical and microstructural properties of CaCu3Ti4O12 ceramics

In this work, the influence of Lu₂O₃ doped on the dielectric and electrical properties of CaCu₃Ti₄O₁₂ was reported. Lu₂O₃-doped CCTO was prepared by a conventional solid state technique using CuO, TiO₂, and CaCO₃ as starting materials. The samples were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM); dielectric measurements were measured in the 10² Hz–10⁷ Hz frequency range at room temperature; and the nonlinear behavior of all samples was measured. The doping of Lu₂O₃ resulted in an increase in the dielectric constant of CCTO, but decreased the stability of the frequency dependence. Increasing concentrations of Lu₂O₃ resulted in decreasing nonlinear coefficients.     

Microwave dielectric properties of (1 − x)(Mg0.95Co0.05)TiO3–x(Na0.5La0.5)TiO3 ceramic system

The microstructures and the microwave dielectric properties of the (1 − x)(Mg_0.95Co_0.05)TiO₃–x(Na_0.5La_0.5)TiO₃ ceramic system were investigated. Two-phase system was confirmed by the XRD patterns and the EDX analysis. A co-existed second phase (Mg_0.95Co_0.05)Ti₂O₅ was also detected. The microwave dielectric properties are strongly related to the density and the matrix of the specimen. A new microwave dielectric material 0.88(Mg_0.95Co_0.05)TiO₃–0.12(Na_0.5La_0.5)TiO₃, possessing an excellent combination of dielectric properties: ε_r  22.36, Q × f  110,000 GHz (at 9 GHz), τ_f  2.9 ppm/°C), is proposed as a candidate dielectric for GPS patch antennas.     

Synthesis and microwave absorption properties of graphene-oxide(GO)/polyaniline nanocomposite with Fe3O4 particles

In order to investigate the impedance matching properties of microwave absorbers,the ternary nanocomposites of GO/PANI/Fe₃O₄（GPF） are prepared via a two-step method,GO/PANI composites are synthesized by dilute polymerization in the presence of aniline monomer and GO,and GO/PANI/Fe₃O₄ is prepared via a co-precipitation method.The obtained nanocomposites are characterized by scanning electron microscopy（SEM）,X-ray diffraction（XRD）,and Fourier transform infrared spectroscopy（FTIR）,respectively.The microwave absorbability reveals enhanced microwave absorption properties compared with GO,PANI,and GO/PANI.The maximum reflection loss of GO/PANI/Fe₃O₄ is up to-27 dB at 14 GHz with its thickness being 2 mm,and its absorption bandwidths exceeding-10 dB are more than 11.2 GHz with its thickness values being in the range from 1.5 mm-4 mm.It provides that GO/PANI/Fe₃O₄ can be used as an attractive candidate for microwave absorbers.     

Green emitting long lasting phosphorescence (LLP) properties of Mg2SnO4:Mn phosphor

A novel long-lasting phosphorescence phosphor, Mn²⁺-activated Mg₂SnO₄, has been synthesized and its optical properties have been investigated. The Mg₂SnO₄:Mn²⁺ emits green light with high luminance, upon UV irradiation, centered at 499 nm from the spin forbidden transitions of the d-electrons in Mn²⁺ ions. The CIE chromaticity coordinates of the Mg₂SnO₄:Mn²⁺ phosphor are x=0.0875 and y=0.6083 under 254 nm UV excitation. The phosphorescence can be observed by the naked eyes (0.32 mcd/m²) in the dark clearly for over 5 h after the 5 min UV irradiation. Thermoluminescence has been studied and the mechanism of the long-lasting phosphorescence has been discussed.     

Electronic band structure and Fermi surface of new low-temperature Ni-based superconductors: 3.3 K (Ni2P2)(Sr4Sc2O6) and 2.7 K (Ni2As2)(Sr4Sc2O6) from first principles

Based on first-principle FLAPW-GGA calculations, we have investigated structural and electronic properties of the recently synthesized tetragonal (space group P4/nmm) nickel-based pnictide oxide superconductors: 3.3 K (Ni₂P₂)(Sr₄Sc₂O₆) and 2.7 K (Ni₂As₂)(Sr₄Sc₂O₆). Optimized structural data, electronic bands, total and partial densities of states, and Fermi surface topology have been obtained and discussed in comparison with available experiments and with their Fe-based (Fe₂P₂)(Sr₄Sc₂O₆) and (Fe₂As₂)(Sr₄Sc₂O₆) analogs.     

Effects of vanadium doping on structure and electrical properties of SrBi4Ti4O15 thin films

The effects of vanadium(V) doping into SrBi₄Ti₄O₁₅ (SBTi) thin films on the structure, ferroelectric, leakage current, dielectric, and fatigue properties have been studied. X-ray diffraction result showed that the crystal structure of the SBTi thin films with and without vanadium is the same. Enhanced ferroelectricity was observed in the V-doped SrBi₄Ti₄O₁₅ (SrBi_4−x/3Ti_4−xV_xO₁₅, SBTiV-x (x = 0.03, 0.06, and 0.09)) thin films compared to the pure SrBi₄Ti₄O₁₅ thin film. The values of remnant polarization (2P_r) and coercive field (2E_c) of the SBTiV-0.09 thin film capacitor were 40.9 μC/cm² and 105.6 kV/cm at an applied electric field of 187.5 kV/cm, respectively. The 2P_r value is over five times larger than that of the pure SBTi thin film capacitor. At 100 kHz, the values of dielectric constant and dielectric loss were 449 and 0.04, and 214 and 0.06 for the SBTiV-0.09 and the pure SBTi thin film capacitors, respectively. The leakage current density of the SBTiV-0.09 thin film capacitor measured at 100 kV/cm was 6.8 × 10⁻⁹ A/cm², which is more than two and a half orders of magnitude lower than that of the pure SBTi thin film capacitor. Furthermore, the SBTiV-0.09 thin film exhibited good fatigue endurance up to 10¹⁰ switching cycles. The improved electrical properties may be related to the reduction of internal defects such as bismuth and oxygen vacancies with changes in the grain size by doping of vanadium into SBTi.     

氧含量对CaCu3Ti4O12巨介电常数和介电过程的影响

本文研究了在真空、空气和氧气中烧结制备的三种 CaCu₃Ti₄O₁₂陶瓷材料的介电特性. 交流阻抗测量结果表明在10—300 K温度范围, 三种样品的介电温谱中均出现三个平台, 其电阻实部和电容虚部在相应温度出现损耗峰, 真空条件烧结的样品具有较高的介电平台和较明显的电阻实部与电容虚部峰值, 表明氧含量和氧空位对CaCu₃Ti₄O₁₂的介电性质具有重要影响, 介电温谱出现的三个平台分别源于晶粒、晶界及氧空位陷阱.温谱分析表明晶粒的激活能与烧结气氛有较大关系,氧空位引起的电子短程跳跃及跳跃产生的极化子是晶粒电导和电容的主要起源.氧空位陷阱的激活能基本与烧结气氛无关,约为0.46 eV. 氧空位对载流子的陷阱作用是CaCu₃Ti₄O₁₂ 低频高介电常数的重要起源.     

An easy and novel approach for the decoration of graphene oxide by Fe3O4 nanoparticles

A new and relatively general route was developed to fabricate graphene oxide (GO)-Fe₃O₄ hybrid. X-ray diffraction, transmission electron morphology, X-ray photoelectron spectroscopy (XPS) and energy-dispersive spectrum were used to demonstrate the successful attachment of iron oxide nanoparticles to GO sheets. Transmission electron microscopy observation indicates that the size of the Fe₃O₄ nanoparticles was about 2.7 nm with narrow size distribution. Moreover, this hybrid shows superparamagnetic property and allows the rapid separation under an external-magnetic field. In addition, the method could be extended to further development of graphene-based nanoelectronics.     

Significant effect of electron transfer between current collector and active material on high rate performance of Li4Ti5O12

The rate and cycling performances of the electrode materials are affected by many factors in a practical complicated electrode process. Learning about the limiting step in a practical electrochemical reaction is very important to effectively improve the electrochemical performances of the electrode materials. Li₄Ti₅O₁₂, as a zero-strain material, has been considered as a promising anode material for long life Li-ion batteries. In this study, our results show that the Li₄Ti₅O₁₂ pasted on Cu or graphite felt current collector exhibits unexpectedly higher rate performance than on Al current collector. For Li₄Ti₅O₁₂, the electron transfer between current collector and active material is the critical factor that affects its rate and cycling performances.     

The magnetic properties of diluted CoFe2O4 nanomaterials

The magnetic properties of （Cox Fe1-x）A （Zn1-x Fe1＋x）B O4 are studied using mean-field theory and the probability distribution law to obtain the saturation magnetization, the coercive field, the critical temperature, and the exchange interactions with different values of D （nm） and x. High-temperature series expansions （HTSEs） combined with the Pade approximant are used to calculate the critical temperature of （CoxFe1-x）A（Znl-xFe1＋x）BO4, and the critical exponent associated with magnetic susceptibility is obtained.     

Spectral characterization and energy levels of Cr:Sc2(MoO4)3 crystal

This paper reports the spectral properties and energy levels of Cr³⁺:Sc₂(MoO₄)₃ crystal. The crystal field strength Dq, Racah parameter B and C were calculated to be 1408 cm⁻¹, 608 cm⁻¹ and 3054 cm⁻¹, respectively. The absorption cross sections σ_α of ⁴A₂→⁴T₁ and ⁴A₂→⁴T₂ transitions were 3.74×10⁻¹⁹ cm² at 499 nm and 3.21×10⁻¹⁹ cm² at 710 nm, respectively. The emission cross section σ_e was 375×10⁻²⁰ cm² at 880 nm. Cr³⁺:Sc₂(MoO₄)₃ crystal has a broad emission band with a broad FWHM of 176 nm (2179 cm⁻¹). Therefore, Cr³⁺:Sc₂(MoO₄)₃ crystal may be regarded as a potential tunable laser gain medium.