Characteristics of Ni films deposited on SiO2/Si(1 0 0) and MgO(0 0 1) by direct current magnetron sputtering system with the oblique target

280 nm-thick Ni films were deposited on SiO₂/Si(1 0 0) and MgO(0 0 1) substrates at 300 K, 513 K and 663 K by a direct current magnetron sputtering system with the oblique target. The films deposited at 300 K mainly have a [1 1 0] crystalline orientation in the film growth direction. The [1 1 0]-orientation weakens and the [1 1 1]- and [1 0 0]-orientations enhance with increasing deposition temperature. The lattice constant of the Ni films is smaller than that of the Ni bulk, except for the film grown on MgO(0 0 1) at 663 K. Furthermore, as the deposition temperature increases, the lattice constant of the films grown on the SiO₂/Si(1 0 0) decreases whereas that of the films grown on the MgO(0 0 1) increases. The films deposited at 300 K and 513 K grow with columnar grains perpendicular to the substrate. For the films deposited at 663 K, however, the columnar grain structure is destroyed, i.e., an about 50 nm-thick layer consisting of granular grains is formed at the interface between the film and the substrate and then large grains grow on the layer. The Ni films deposited at 300 K consist of thin columnar grains and have many voids at the grain boundaries. The grains become thick and the voids decrease with increasing deposition temperature. The resistivity of the film decreases and the saturation magnetization increases with increasing deposition temperature.     

Magnetic and optical properties of self-organized InMnAs quantum dots

Ten layers of self-assembled InMnAs quantum dots with InGaAs barrier were grown on high resistivity (1 0 0) p-type GaAs substrates by molecular beam epitaxy (MBE). The presence of ferromagnetic structure was confirmed in the InMnAs diluted magnetic quantum dots. The ten layers of self-assembled InMnAs quantum dots were found to be semiconducting, and have ferromagnetic ordering with a Curie temperature, T_C=80 K. It is likely that the ferromagnetic exchange coupling of sample with T_C=80 K is hole mediated resulting in Mn substituting In and is due to the bound magnetic polarons co-existing in the system. PL emission spectra of InMnAs samples grown at temperature of 275, 260 and 240 °C show that the interband transition peak centered at 1.31 eV coming from the InMnAs quantum dot blueshifts because of the strong confinement effects with increasing growth temperature.     

Growth of manganese silicide films by co-deposition of Mn and Si on Si(1 1 1): A spectroscopic and morphological investigation

MnSi is a ferromagnetic compound with a Curie temperature of 29 K. Recent theoretical studies predict that 2 ML of MnSi epitaxially grown on Si show a ferromagnetic metallic ground state with spin polarization of about 50%. This would allow the development of spintronic devices based on the injection of spin-polarized current from a ferromagnetic metal into a semiconductor.In this context the possibility of growing in situ MnSi on the Si(1 1 1) surface has been explored. Thermal reaction, crystalline structure and electronic properties of the grown films have been studied in situ by photoemission spectroscopy (PES), X-ray absorption spectroscopy (XAS), and low energy electron diffraction (LEED). Depositing a thin film of Mn on Si(1 1 1) the formation of ordered islands (with dimensions dependent on the amount of deposited Mn) is driven by annealing at selected temperatures, as already observed. Our preliminary studies show that by simultaneously depositing Mn and Si in 1:1 stoichiometry on Si(1 1 1) a large improvement in the homogeneity of the MnSi films is achieved.     

Polarized neutron reflectometry of the influence of Fe/Si,Fe/FeSi2 and Au/Fe interfaces on the magnetic properties of epitaxial Fe films

The magnetic and structural properties of epitaxial Fe films grown on Si(1 1 1) are investigated by polarized neutron reflectometry (PNR) at room temperature. The influence of different types of interfaces, Fe/Si, Fe/FeSi₂ and Au/Fe on the magnetic properties of Fe films deposited by molecular beam epitaxy onto Si(1 1 1) are characterized. We observe a drastic reduction of the magnetic moment in the entire Fe film deposited directly on the silicon substrate essentially due to strong Si interdiffusion throughout the whole Fe layer thickness. The use of a silicide FeSi₂ template layer stops the interdiffusion and the value of the magnetic moment of the deposited Fe layer is close to its bulk value. We also evidence the asymmetric nature of the interfaces, Si/Fe and Fe/Si interfaces are magnetically very different. Finally, we show that the use of Au leads to an enhancement of the magnetization at the interface.     

Magnetic behavior of MnAs precipitates in Ga1−xMnxAs diluted magnetic semiconductor

Ferromagnetic Ga_1−xMn_xAs layers (where x≈4.7–5.5%) were grown on (1 0 0) GaAs substrates by molecular beam epitaxy. These p-type (Ga,Mn)As films were revealed to have a ferromagnetic structure and ferromagnetism is observed up to a Curie temperature of 318 K, which is ascribed to the presence of MnAs secondary magnetic phases within the film. It is highly likely that the phase segregation occurs due to the high Mn cell temperature around 890–920 °C, as it is well established that GaMnAs is unstable at such a high temperature. The MnAs precipitate in the samples with x≈4.7–5.5% has a Curie temperature T_c≈318 K, which was characterized from field-cooled and zero-field-cooled magnetization curves.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Dependence of the microstructural properties on the substrate temperature in strained CdTe (1 0 0)/GaAs (1 0 0) heterostructures

CdTe thin films were grown on GaAs (1 0 0) substrates by using molecular beam epitaxy at various temperatures. The bright-field transmission electron microscopy (TEM) images and the high-resolution TEM (HRTEM) images showed that the crystallinity of CdTe epilayers grown on GaAs substrates was improved by increasing the substrate temperature. The result of selected-area electron diffraction pattern (SADP) showed that the orientation of the grown CdTe thin films was the (1 0 0) orientation. The lattice constant the strain, and the stress of the CdTe thin film grown on the GaAs substrate were determined from the SADP result. Based on the SADP and HRTEM results, a possible atomic arrangement for the CdTe/GaAs heterostructure is presented.     

Properties of thin manganite films grown on semiconducting substrates for spintronics applications

La_0.7Sr_0.3MnO₃ (LSMO) manganite thin films were grown by pulsed plasma deposition on silicon (Si) and gallium arsenide (GaAs) substrates covered by an amorphous oxide. Manganite films are characterized by polycrystalline structure. Ferromagnetic transition is above room temperature and for 50 nm thick film the Curie temperature was as high as 325 K and 305 K for LSMO/SiO_x/Si and LSMO/AlO_x/GaAs, respectively.     

Impact of ZnTe buffer on the electrical properties of n-type GaSb:Te films

We have investigated on the molecular beam epitaxy (MBE) of Te-doped GaSb films on ZnTe buffer. Te-doped GaSb (GaSb:Te) films with and without ZnTe buffer were grown on (0 0 1) GaAs substrates. GaSb:Te/ZnTe/GaAs film revealed higher mobility (=631 cm²/V s) in comparison to GaSb:Te/GaAs film (=249 cm²/V s). To explain the higher mobility of GaSb:Te on ZnTe buffer, dislocation density and temperature dependence of Hall measurement results were analyzed. Temperature dependence of Hall measurement shows strong influence of the dislocation scattering, which indicates that dislocation reduction by the ZnTe buffer enhances the carrier mobility of GaSb films.     

Dependence of Curie temperature on surface strain in InMnAs epitaxial structures

Pairs of self-assembled InMnAs quantum dot structures and reference epitaxial layers (0 < x < 0.13) were prepared on GaAs substrates by low-pressure metal organic vapour phase epitaxy. Magnetic moment measurements indicated that reference epitaxial layer had a Curie temperature of 343 K independent on the composition. On the other hand, the quantum dots prepared under Stranski-Krastanov growth mode from the identical gas phase composition showed a lower value of Curie temperature. This value varied from 41 to 235 K in relation to the material composition. Moiré fringes at transmission electron microscopy plan view were used for characterization of strain in InMnAs quantum dot structures.     

Magnetoresistance of magnetite thin films grown by pulsed laser deposition on GaAs(1 0 0) and Al2O3(0 0 0 1)

Magnetotransport properties of magnetite thin films deposited on gallium arsenide and sapphire substrates at growth temperatures between 473 and 673 K are presented. The films were grown by UV pulsed laser ablation in reactive atmospheres of O₂ and Ar, at working pressure of 8 × 10⁻² Pa. Film stoichiometry was determined in the range from Fe_2.95O₄ to Fe_2.97O₄. Randomly oriented polycrystalline thin films were grown on GaAs(1 0 0) while for the Al₂O₃(0 0 0 1) substrates the films developed a (1 1 1) preferred orientation. Interfacial Fe³⁺ diffusion was found for both substrates affecting the magnetic behaviour. The temperature dependence of the resistance and magnetoresistance of the films were measured for fields up to 6 T. Negative magnetoresistance values of ∼5% at room temperature and ∼10% at 90 K were obtained for the as-deposited magnetite films either on GaAs(1 0 0) or Al₂O₃(0 0 0 1).     

Spin wave excitations in Fe films grown on GaAs(1 1 3)A substrates

The spin wave excitation and its size effect has been studied in Al-capped Fe films grown on low-symmetry GaAs(1 1 3)A substrates. The temperature dependence of saturation magnetization follows an effective Bloch's law as long as magnetization remains larger than about 70% of its saturation value. A significant increase of the spin wave parameter B is found in Al-capped ultrathin Fe films grown on GaAs(1 1 3)A compared to bulk Fe, Fe films on GaAs(0 0 1) and other systems. This is explained as a result of the reduction in uniaxial magnetic anisotropy observed in this orientation for the same thickness range. However, this observed uniaxial magnetic anisotropy is found to be a likely reason for stabilizing the ferromagnetism.     

Growth and characterization of rocksalt MnS/GaAs epilayers by hot-wall epitaxy

Epitaxial growth characteristics of α-MnS on GaAs(1 0 0) substrates have been investigated by X-ray diffraction and double crystal rocking curve measurements. Growth of stoichiometric α-MnS films has been performed by hot-wall epitaxy using Mn and ZnS as a source of sulfur. The films on GaAs(1 0 0) at low substrate temperature exhibit multiphase crystal structures of zincblende and rocksalt, and the main structure is changed to rocksalt with increasing substrate temperature. Photoluminescence spectrum of the α-MnS epilayer at 5 K exhibits broad emission bands, which are attributed to Mn²⁺ ions. The band gap energy of the α-MnS epilayer at room temperature was also estimated to be about 3.3 eV by reflection.     

Growth of Au thin film on Cu-modified Si(1 1 1) surface

Miniaturizing of electronic devices requires that conductive elements maintain advanced electrical characteristics upon reducing their geometrical sizes. For gold, which is valued for its high electrical conductivity and stability against ambient conditions, creation of extra-thin films on silicon is hampered by formation of the quite complex Au/Si interface. In the present work, by forming a Si(1 1 1)5.55 × 5.55-Cu surface reconstruction prior to Au deposition we formed Au films with smoother surface morphology and higher surface conductivity compared to Au film grown on a pristine Si(1 1 1)7 × 7 surface. Scanning tunnelling microscopy and four-point probe measurements were used to characterize the growth mode of the Au film on a Si(1 1 1)5.55 × 5.55-Cu reconstruction at room temperature.     

Magneto-transport and ferromagnetic resonance studies of polycrystalline La0.6Pb0.4MnO3 thin films

To understand the nature of grain boundaries in polycrystalline materials, magneto-transport and ferromagnetic resonance measurement have been performed in polycrystalline La_0.6Pb_0.4MnO₃ (LPMO) thin films prepared by pulsed laser deposition. Films are found to undergo a semiconductor to metal transition at 230 K and re-enter into the semiconducting state below 130 K. Microwave absorption measurements carried out as function of applied field show two components of resonant absorption signal. First component is in accordance with ferromagnetic transition of grains at Curie temperature and the second component shows antiferromagnetic transition of grain boundaries at 160 K. An additional non-resonant absorption signal centered at zero field has also been observed that supports transition from conducting to insulating grain boundaries at ∼160 K. Further, temperature dependence of resistance in semiconducting state at low temperatures is in accordance with coulomb blockade model indicating insulating nature of AFM grain boundaries.     

Spray pyrolysis deposition of ZnO thin films on FTO coated substrates from zinc acetate and zinc chloride precursor solution at different growth temperatures

ZnO thin films were fabricated using zinc chloride and zinc acetate precursors by the spray pyrolysis technique on FTO coated glass substrates. The ZnO films were grown in different deposition temperature ranges varying from 400 to 550 °C. Influences of substrate temperature and zinc precursors on crystal structure, morphology and optical property of the ZnO thin films were investigated. XRD patterns of the films deposited using chloride precursor indicate that (1 0 1) is dominant at low temperatures, while those deposited using acetate precursor show that (1 0 1) is dominant at high temperatures. SEM images show that deposition temperature and type of precursor have a strong effect on the surface morphology. Optical measurements show that ZnO films are obviously influenced by the substrate temperatures and different types of precursor solutions. It is observed that as temperature increases, transmittance decreases for ZnO films obtained using zinc chloride precursor, but the optical transmittance of ZnO films obtained using zinc acetate precursor increases as temperature increases.     

Buffer effects of Ag layers on magneto-optical Co/Ge(1 0 0) ultrathin films

Magnetic properties of the Co/Ag/Ge(1 0 0) films grown at room temperature and 200 K were studied by the surface magneto-optical Kerr effect (SMOKE). More than 1.5 monolayer Ag buffer layers not only effectively block the interdiffusion between the capped Co layers and the Ge(1 0 0) substrate but also stabilize the magnetic phase. The temperature and thickness dependence on coercivity measurements show that interactions upon the interfaces are strongly correlated to the microstructures.     

Growth dynamics of pulsed laser deposited indium oxide thin films: a substrate dependent study

Indium oxide films are deposited by pulsed laser deposition in the presence of oxygen atmosphere, on different substrates, namely GaAs, Si, quartz, and glass. The structural, morphological, and interface characteristics are studied. Cubic In₂O₃ phase is confirmed by high resolution X-ray diffraction measurements. While the films on Si, glass, and quartz substrates are polycrystalline, the films on GaAs exhibit a preferred orientation along (2 2 2) plane. The structure and crystalline nature of the films are also confirmed by Raman spectroscopy. Furthermore, Raman spectra show the appearance of gallium oxide modes arising due to Ga diffusion from the substrate. The morphology of the films deposited on different substrates is studied by atomic force microscopy and rms roughness values are obtained. A two-dimensional power spectral density analysis has been used to calculate the growth exponent (α). A value of α > 1 (α < 1) for films grown on GaAs/Si (quartz/glass) substrates suggests that the growth on crystalline substrates is governed by the linear diffusion model, whereas the growth on amorphous substrates follows the dynamic scaling behaviour. UV-visible study shows a high optical transmittance of >90% and a band gap value of 3.64 and 3.79 eV for the films deposited on quartz and glass substrates, respectively.     

Transport and optical properties of amorphous carbon and hydrogenated amorphous carbon films

In this paper we report on the electrical and optical properties of amorphous carbon (a-C) and hydrogenated amorphous carbon (a-C:H) films. Resistivity of both types of films decreases with increase in temperature. At lower temperatures (60-250 K) the electron transport is due to variable range hopping for the a-C films. At higher temperatures (300-430 K) it is thermally activated for both types of films. Analysis of the heterojunction between diamond-like carbon (DLC) and bulk silicon (Si) leads to the conclusion that our a-C films are of n-type and our a-C:H films are of p-type. The optical measurements with DLC revealed a Tauc bandgap of 0.6 eV for the a-C films and 1-1.2 eV for the a-C:H films. An Urbach energy around 170 meV could be determined for the a-C:H films. Strain versus resistance plots were measured resulting in piezoresistive gauge factors around 50 for the a-C films and in between 100 and 1200 for the a-C:H films.     

Effect of microstructure of MgO buffer layer on BaTiO3 grown on silicon substrates

MgO ultrathin films were grown on Si(1 0 0) substrates as buffer layers for the growth of ferroelectric BaTiO₃ thin films by laser molecular beam epitaxy (L-MBE). The deposition process of MgO buffer layers grown on silicon was in situ monitored by reflection high-energy electron diffraction (RHEED). The structure of BaTiO₃ films fabricated on MgO buffers was investigated by X-ray diffraction. Biaxially textured MgO was obtained at high laser energy density, but when the laser energy was lowered, MgO buffer was transformed to the form of texture with angular dispersion with the increase of the film thickness. BaTiO₃ films grown on the former buffer were completely (0 0 1) textured, while those on the latter were (0 0 1) preferred orientated. Furthermore, the fabricated MgO buffers and BaTiO₃ films had atomically smooth surface and interface. All these can reveal that the quality of textured MgO buffer is a key factor for the growth of BaTiO₃ films on silicon.