A novel ternary polymer electrolyte for LMP batteries based on thermal cross-linked poly(urethane acrylate) in presence of a lithium salt and an ionic liquid

A new ternary polymer electrolyte based on thermally cross-linked poly(urethane acrylate) (PUA), lithium bis(trifluoromethansulfonyl)imide (LiTFSI) and the ionic liquid N-butyl-N-methylpyrrolidinium TFSI (PYR₁₄TFSI) was developed and tested for application in LMP batteries. The polymer electrolyte was a transparent yellow self-standing material with quite good mechanical properties, i.e., comparable to that of a flexible rubber. The room temperature ionic conductivity of the dry polymer electrolyte was found to be as high as 0.1 mS cm⁻¹ for the compound containing 40 wt% of ionic liquid (PYR₁₄TFSI) and a O/Li ratio of 15/1 (Li⁺ from LiTFSI). The thermal analysis of the new cross-linked electrolyte showed that it was homogeneous, amorphous and stable over a wide temperature range extending from −40 °C to 100 °C. The homogeneity of the polymer electrolyte was also confirmed by SEM analysis.     

Synthesis and ionic conductivity of hyperbranched poly(glycidol)

A novel hyperbranched poly(glycidol) (HPG) was prepared and characterized. The synthesized HPG was used as a substrate of a polymer electrolyte. The ionic conductivity of a blend of HPG, polyurethane (PU), and salt was studied. The ionic conductivity of HPG/PU/LiClO₄ was about 6.6 × 10^?6 S · cm^?1 at 20 °C and 6.3 × 10^?4 S · cm^?1 at 60 °C. The results indicated that HPG showed higher solubility for salt than linear polyether when both had the same [O]/[Li⁺] molar ratio. The main reason was that more cavities and a lower degree of chain entanglement in HPG resulted in a lower glass‐transition temperature and were beneficial for decreasing the aggregation of salt or enhancing the ionic conductivity. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2225–2230, 2001     

Electrical and Structural Properties of Poly (Methyl Methacrylate) Doped Potassium Iodide (KI) Solid Polymer Electrolyte

A high-conducting salt-doped polymer electrolyte layer has been created here for use in photocell technologies. The solution casting method is used to produce ion conducting film where poly (methyl methacrylate) (PMMA) is used as the host polymer and potassium iodide (KI) as the dopant. The conductivity and amorphic increases of the polymer electrolytes with the addition of salt concentrations helps in the enhancement of the charge transfer properties. Using electrochemical impedance spectroscopy (EIS), ionic conductivity is evaluated where maximum conductivity is 3.99 × 10⁻⁶ S cm^-1 at 20 wt% KI concentration. Polarized optical microscopy (POM) shows the reduction in crystallinity by salt doping, while Fourier transforms infrared spectroscopy (FTIR) shows the complexation as well as composite nature of the film. Ionic transference number (t_ion) measurement shows the predominantly ionic nature of this polymer electrolyte.     

A greener electrochromic liquid crystal based on ionic liquid electrolytes

An electrochromic liquid crystal (ECLC) material composed of only liquid crystal (LC) and ionic liquid (IL) was developed. The LC containing the substituted diphenylacetylene serves as electrochromic (EC) material to realise transmittance and colour change under the direct current (DC) field, while the IL with the designable cation and anion served as electrolyte. Herein, a series of IL electrolytes was screened to investigate how IL tunes the electro-optic performance of the ECLC cell. By testing the electrochemistry window of ILs in EC cells, IL with the [NTf₂]^? anion shows adequate electrochemical stability when the EC material undergoes oxidation and reduction. The electro-optic performance of ECLC containing 1-ethoxy-4-[2-(4-pentylphenyl) ethynyl]-benzene (PEB) and IL was then evaluated by UV-vis spectrometry under the control of an electrochemical work station. Compared with other PEB-IL, PEB-[Bmim][NTf₂] with [Bmim][NTf₂] electrolyte shows a satisfactory transmittance at low operating voltage. Furthermore, Pd NPs in situ formed in [Bmim][NTf₂] reduced the EC potential and improved the light scattering of the ECLC cell. In this work, we also designed a bifunctional device based on polymer dispersed liquid crystal (PDLC) that hosts electrochromic guest molecules, and analysed the electro-optical and electrochromic properties of LC electrolyte mixtures, in order to gain control of the incident daylight and glare in building and automotive applications.     

Improved properties of polymer electrolyte by ionic liquid PP1.3TFSI for secondary lithium ion battery

A new kind of polymer electrolyte is prepared from N-methyl-N-propylpiperidinium bis (trifluoromethanesulfonyl) imide (PP1.3TFSI), polyethylene oxide (PEO), and lithium bis (trifluoromethanesulfonyl) imide (LiTFSI). IR and X-ray diffraction results demonstrate that the addition of ionic liquid decreases the crystallization of PEO. Thermal and electrochemical properties have been tested for the solid polymer electrolytes, the addition of the room temperature molten salt PP1.3TFSI to the conventional P(EO)₂₀LiTFSI polymer electrolyte leads to the improvement of the thermal stability and the ionic conductivity (x = 1.27, 2.06 × 10⁻⁴ S cm⁻¹ at room temperature), and the reasonable lithium transference number is also obtained. The Li/LiFePO₄ cell using this polymer electrolyte shows promising reversible capacity, 120 mAh g⁻¹ at room temperature and 164 mAh g⁻¹ at 55 °C.     

Synthesis and properties of all solid polymer electrolytes based on poly(vinyl acetate‐co‐acetyl ethylene oxide acrylate)

Poly(acetyl ethylene oxide acrylate‐co‐vinyl acetate) (P(AEOA‐VAc)) was synthesized and used as a host for lithium perchlorate to prepare an all solid polymer electrolyte. Introduction of carbonyl groups into the copolymer increased ionic conductivity. All solid polymer electrolytes based on P(AEOA‐VAc) at 14.3 wt% VAc with 12wt% LiClO₄ showed conductivity as high as 1.2 × 10^?4 S cm^?1 at room temperature. The temperature dependence of the ionic conductivity followed the VTF behavior, indicating that the ion transport was related to segmental movement of the polymer. FTIR was used to investigate the effect of the carbonyl group on ionic conductivity. The interaction between the lithium salt and carbonyl groups accelerated the dissociation of the lithium salt and thus resulted in a maximum ionic conductivity at a salt concentration higher than pure PAEO‐salts system. Copyright © 2010 John Wiley & Sons, Ltd.     

Modification of carbon electrode in ionic liquid through the reduction of phenyl diazonium salt. Electrochemical evidence in ionic liquid

Electrochemical reduction of the 4-nitrophenyl diazonium salt in ionic liquid media has been investigated at carbon electrode. The ionic liquid chosen for this study was 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide, [EMIM][TFSI]. The cyclic voltammetry study demonstrated the possibility of the electrochemical grafting of the nitrophenyl groups onto carbon electrode after the reduction of its corresponding diazonium in ionic liquid. The electrochemical characterization of the modified electrode achieved on ionic liquid displays the presence of the nitrophenyl group at the carbon surface. Moreover, the surface concentration of the attached group obtained in this media was found to be around 1.7 × 10⁻¹⁰ mol cm⁻², this value may suggest the possibility of the formation of monolayer. Furthermore, the characterization of the modified electrode in [EMIM][TFSI] showed the conversion of some NO₂-phenyl groups to NHOH-phenyl. This observation could indicate the presence of surface interaction between the reduced NO₂-phenyl and the ionic liquid cation, thanks to the presence of acidic proton in the ionic liquid cation.     

Preparation of Nylon-6 Particles in Ionic Liquids

Summary: Utilizing the thermal stability of ionic liquid, micrometer-sized Nylon-6 particles were successfully prepared by hydrolytic polymerization of ε-caprolactam at high temperature with polyvinyl pyrrolidone as stabilizer in ionic liquids, 1-butyl-3-methyl imidazolium tetrafluoroborate, [Bmim][BF₄] and N,N-diethyl-N-methyl-N-(2-methoxyethyl)ammonium bis(trifluoro-methanesulfonyl)amide, [DEME][TFSA]. The obtained particles had a unique shape because Nylon-6 is a crystalline polymer. Viscosity-average molecular weights of Nylon-6 prepared in [Bmim][BF₄] and [DEME][TFSA] at 180 °C for 48 h were 4200 and 2200, respectively.     

Effect of plasticizers (EC or PC) on the ionic conductivity and thermal properties of the (PEO)9LiTf: Al2O3 nanocomposite polymer electrolyte system

A new plasticized nanocomposite polymer electrolyte based on poly (ethylene oxide) (PEO)-LiTf dispersed with ceramic filler (Al₂O₃) and plasticized with propylene carbonate (PC), ethylene carbonate (EC), and a mixture of EC and PC (EC+PC) have been studied for their ionic conductivity and thermal properties. The incorporation of plasticizers alone will yield polymer electrolytes with enhanced conductivity but with poor mechanical properties. However, mechanical properties can be improved by incorporating ceramic fillers to the plasticized system. Nanocomposite solid polymer electrolyte films (200–600 μm) were prepared by common solvent-casting method. In present work, we have shown the ionic conductivity can be substantially enhanced by using the combined effect of the plasticizers as well as the inert filler. It was revealed that the incorporating 15 wt.% Al₂O₃ filler in to PEO: LiTf polymer electrolyte significantly enhanced the ionic conductivity [σ _RT (max)?=?7.8?×?10^?6 S cm^?1]. It was interesting to observe that the addition of PC, EC, and mixture of EC and PC to the PEO: LiTf: 15 wt.% Al₂O₃ CPE showed further conductivity enhancement. The conductivity enhancement with EC is higher than PC. However, mixture of plasticizer (EC+PC) showed maximum conductivity enhancement in the temperature range interest, giving the value [σ _RT (max)?=?1.2?×?10^?4 S cm^?1]. It is suggested that the addition of PC, EC, or a mixture of EC and PC leads to a lowering of glass transition temperature and increasing the amorphous phase of PEO and the fraction of PEO-Li⁺ complex, corresponding to conductivity enhancement. Al₂O₃ filler would contribute to conductivity enhancement by transient hydrogen bonding of migrating ionic species with O–OH groups at the filler grain surface. The differential scanning calorimetry thermograms points towards the decrease of T _g , crystallite melting temperature, and melting enthalpy of PEO: LiTf: Al₂O₃ CPE after introducing plasticizers. The reduction of crystallinity and the increase in the amorphous phase content of the electrolyte, caused by the filler, also contributes to the observed conductivity enhancement.     

Fabrication and characterization of electrochemical double layer capacitors using ionic liquid-based gel polymer electrolyte with chemically treated activated charcoal electrodes

The present investigation deals with electrochemical double layer capacitors (EDLCs) made up of ionic liquid (IL)-based gel polymer electrolytes with chemically treated activated charcoal electrodes. The gel polymer electrolyte comprising of poly(vinylidine fluoride-co-hexafluropropylene) (PVdF-HFP)–1-ethyl-2,3-dimethyl-imidazolium-tetrafluroborate [EDiMIM][BF₄]–propylene carbonate (PC)–magnesium perchlorate (Mg(ClO₄)₂) exhibits the highest ionic conductivity of ~8.4?×?10^?3?S?cm^?1 at room temperature (~20 °C), showing good mechanical and dimensional stability, suitable for their application in EDLCs. Activation of charcoal was done by impregnation method using potassium hydroxide (KOH) as activating agent. Brunauer–Emmett–Teller (BET) studies reveal that the effective surface area of treated activated charcoal powder (1,515 m²?g^?1) increases by more than double-fold compared to the untreated one (721 m²?g^?1). Performance of EDLCs has been tested using cyclic voltammetry, impedance spectroscopy, and charge–discharge techniques. Analysis shows that chemically treated activated charcoal electrodes have almost triple times more capacitance values as compared to the untreated one.     

Application of novel room temperature ionic liquids in flexible supercapacitors

This paper studied application of different types of room temperature ionic liquids (RTILs) into flexible supercapacitors. Typical RTILs including 1-buthyl-3-methyl-imidazolium [BMIM][Cl], trioctylmethylammonium bis(trifluoromethylsulfonyl)imide [OMA][TFSI] and triethylsulfonium bis(trifluoromethylsulfonyl)imide ([SET₃][TFSI]) were studied. [SET₃][TFSI] shows the best result as electrolyte in electrochemical double-layer (EDLC) supercapacitors with very high specific capacitance of 244 F/g at room temperature, overceiling the performance of conventional carbonate electrolyte such as dimethyl carbonate (DMC) with more stable performance and much larger electrochemical window.     

Employment of [Amim] Cl in the effort to upgrade the properties of cellulose acetate based polymer electrolytes

Transparent thin film polymer electrolytes were prepared by solvent casting technique with the doping of environmental-friendly ionic liquid, 1-allyl-3-methylimidazolium chloride ([Amim] Cl) into the matrix formed by cellulose acetate (CA) and lithium bis(trifluoromethanesulfonyl)imide (LiTFSI). The ionic conducting nature of this system improves significantly from the order of 10^?7–10^?2 S cm^?1 upon increasing doping of [Amim] Cl content till a maximum of 4.68 × 10^?2 S cm^?1 is attained for the composition CA:LiTFSI:[Amim] Cl (14:6:80 wt%). The improving trend in ionic conductivity results from the bond weakening between the connecting atoms in the crystalline region that induces to the increase in amorphous counterpart fractions in the CA matrix. This observation was proved via the accountancies in the reduction of relative viscosity, root mean square value and increase in void as increase in [Amim] Cl doping. The resultant phase conversion hence permits immense lithium ion (Li⁺) fluidity along the polymer backbone and assisting the improvement in ionic conductivity. The thin film polymer electrolyte is found to be elastic in the presence of crystalline fraction and radically deforms upon the chains diffusion into the amorphous fraction. The linear curvatures of the Arrhenius plot justify the conductivity improvement as via the increasing frequency of Li⁺ ions hopping as the temperature increases. The increasing addition of [Amim] Cl diminishes both the heat-resistivity and thermal stability of CA:LiTFSI:[Amim] Cl matrix.     

Silk‐Ion Jelly: a novel ion conducting polymeric material with high conductivity and excellent mechanical stability

In this work, a thin, flexible and mechanically stable polymer conducting material (Silk‐Ion Jelly) was developed though application of Ion Jelly on to silk fabrics. Ion Jelly was prepared through jellification of a room temperature ionic liquid, 1‐butyl‐3‐methyl‐imidazolium dicyanamide ([bmim][dca]) using gelatin and water and applied to silk fabrics using two different processes: impregnation and in‐situ. Various parameters influencing ionic conductivity such as Ion Jelly composition (ratio of [bmim][dca], water and gelatin) and incorporation as well as the type of application process were thoroughly investigated. It was observed that the Ion Jelly compositions containing lower gelatin and water ratio as well as application through in‐situ process at high temperature (200 °C) led to considerable improvement in conductivity, mainly due to increased [bmim][dca] concentration, structural flexibility and reduced silk crystallinity. Silk‐Ion Jelly prepared using optimized conditions showed excellent mechanical stability and possessed high room temperature conductivity (2.9 × 10^?3 S. cm^?1), similar to [bmim][dca], and therefore, this novel ion conducting material may find potential applications in electrochemical devices due to its eco‐friendly preparation route using biomaterials and green solvents. Copyright © 2012 John Wiley & Sons, Ltd.     

Catalytic performance of [Bmim][Co(CO)4] functional ionic liquids for preparation of 1,3-propanediol by coupling of hydroesterification-hydrogenation from ethylene oxide

In this paper, synthesis of 1,3-propanediol (1,3-PDO) through coupling of hydroesterification-hydrogenation from ethylene oxide (EO) catalyzed by 1-butyl-3-methylimidazolium cobalt tetracarbonyl [Bmim][Co(CO)₄] functional ionic liquid which was prepared by metathesis reaction between [Bmim]Cl and KCo(CO)₄ has been studied. The structure of [Bmim][Co(CO)₄] was characterized by FT-IR and ¹H NMR. Using [Bmim][Co(CO)₄] as catalyst and [Bmim]PF₆ as solvent, 1,3-PDO was prepared for the first time by coupling of hydroesterifaction of EO and hydrogenation of methyl 3-hydroxypropionate (3-HPM). The yield of 3-HPM can reach 90.8%, while the yield of 1,3-PDO up to 82.9%. The catalyst can be separated from the product mixture by extraction with deionized water and recycled several times without significant loss of catalytic efficiency. A possible reaction mechanism has also been proposed.     

Polyacrylamide-methanesulfonic acid gel polymer electrolytes for tin-air battery

The present work describes the synthesis and characterization of gel polymer electrolytes containing methanesulfonic acid (MSA) with Polyacrylamide (PAAm). The PAAm–MSA gel electrolytes were prepared with different concentrations of MSA. Addition of 0.5 M of MSA into the electrolyte increased the ionic conductivity of PAAm from 1.35 × 10^?3 to 1.56 × 10^?2 S cm^?1. The maximum ionic conductivity of 7.0 × 10^?1 S cm^?1 was obtained with 3 M MSA at room temperature. The chemical interaction between PAAm and MSA was studied by Fourier transformed infra-red. The performance as a polymer electrolyte was evaluated from the cell discharge and open circuit potential measurements of a tin-air cell. The tin-air cell supported relatively high current, up to 12 mA cm^?2 with a maximum power density of 5 mW cm^?2. The open-circuit potential of the cell was 1.27 V for 24 h.     

Ion Conducting Polyethylene Oxide-Based Polymer Electrolyte Dopped with Ionic Liquid-Trifluoromethanesulfonic Chloride

In last few decades, polymer electrolyte is the most promising candidate for the fabrication of electrochemical devices. In current work, the influence of adding the room-temperature ionic liquid (trifluoromethanesulfonic chloride – CClF3O2S) in polyethylene oxide (PEO): ammonium iodide (NH4I) polymer electrolyte has been studied. The IL-doped polymer electrolyte films are synthesized by solution casting method with varying stoichiometric ratios. Several experimental techniques including optical polarizing microscope, impedance spectroscopy, X-ray diffraction, Linear sweep voltammetry, Ionic transference number thermal analysis, and electrical conductivity measurements at room temperature have been studied in detail. The complex material's maximum conductivity has been determined to be 3.3 × 10⁻⁵ S cm⁻¹ at room temperature. The POM images show the increase in amorphous region which further confirm the improvement in ionic conductivity. Ionic transference number 0.96 shows the system is purely ionic in nature. The ESW of the IL doped polymer electrolyte is also sawed to be 3.32 V which is suitable for the fabrication of electrochemical devices.     

Effect of NiO nanofiller concentration on the properties of PEO-NiO-LiClO4 composite polymer electrolyte

Composite polymer electrolyte films comprising polyethylene oxide (PEO) as the polymer host, LiClO₄ as the dopant, and NiO nanoparticle as the inorganic filler was prepared by solution casting technique. NiO inorganic filler was synthesized via sol-gel method. The effect of NiO filler on the ionic conductivity, structure, and morphology of PEO-LiClO₄-based composite polymer electrolyte was investigated by AC impedance spectroscopy, X-ray diffraction, and scanning electron microscopy, respectively. It was observed that the conductivity of the electrolyte increases with NiO concentration. The highest room temperature conductivity of the electrolyte was 7.4?×?10^?4 S cm^?1 at 10 wt.% NiO. The observation on structure shows the highest conductivity appears in amorphous phase. This result has been supported by surface morphology analysis showing that the NiO filler are well distributed in the samples. As a conclusion, the addition of NiO nanofiller improves the conductivity of PEO-LiClO₄ composite polymer electrolyte.     

Structural,thermal, vibrational,and electrochemical behavior of lithium ion conducting solid polymer electrolyte based on poly(vinyl alcohol)/poly(vinylidene fluoride) blend

The present study focuses on the preparation and characterization of poly(vinyl alcohol)/poly(vinylidene fluoride) blend polymer electrolyte doped with lithium triflate (LiCF₃SO₃). Interaction of lithium triflate with the host polymer in the solid polymer electrolyte was studied using X-ray diffraction, Fourier transform infrared spectroscopy and differential scanning calorimetry analysis. It was found that 15% salt doped polymer electrolyte possesses the highest ionic conductivity (2.7 × 10^–3 S/cm) at 303 K, the higher thermal stability at 175°C. Linear sweep voltammetry results revealed that the film is electrochemically stable up to 3.4 V.     

Preparation of a novel polymer gel electrolyte based on N-methyl-quinoline iodide and its application in quasi-solid-state dye-sensitized solar cell

Using poly(acrylonitrile-co-styrene) as polymer host, 1,2-propanediol carbonate, dimethyl carbonate and ethylene carbonate as mixture solvent, N-methyl-quinoline iodide and iodine as the source of I⁻/I₃ ⁻, a novel polymer gel electrolyte with ionic conductivity of 5.12 × 10⁻³ S· cm⁻¹ at 25°C was prepared by sol-gel and hydrothermal methods. Based on the polymer gel electrolyte, a quasi-solid-state dye-sensitized solar cell was fabricated. The solar cell possess better long-term stability and light-to-electrical energy conversion efficiency of 4.04% under irradiation of 100 mW· cm⁻². The influences of polymer host, solvent, N-methyl-quinoline iodide and temperature on ionic conductivity of the polymer gel electrolyte and the performance of the dye-sensitized solar cell was discussed.     

Preparation of a Star Network PEG-based Gel Polymer Electrolyte and Its Application to Electrochromic Devices

A star network polymer with a pentaerythritol core linking four PEG-block polymeric arms was synthesized, and its corresponding gel polymer electrolyte based on lithium perchlorate and plasticizers EC/PC with the character being colorless and highly transparent has been also prepared. The polymer host was characterized and confirmed to be of a star network and an amorphous structure by FTIR, ^1H NMR and XRD studies. The polymer host hold good mechanical properties for pentaerythritol cross-linking. Maximum ionic conductivity of the prepared polymer electrolyte has reached 8.83 × 10 ^-4 S·cm^-1 at room temperature. Thermogravimetry （TG） of the polymer electrolyte showed that the thermal stability was up to at least 150 ℃. The gel polymer electrolyte was further evaluated in electrochromic devices fabricated by transparent PET-ITO and electrochromically active viologen derivative films, and its excellent performance promised the usage of the gel polymer electrolyte as ionic conductor material in electrochrornic devices.