萘在贵金属Pd、Pt及Pd-Pt催化剂上的加氢活性及耐硫性能

采用等体积浸渍法制备了SiO2-Al2O3负载的Pd、Pt单金属催化剂及Pd/Pt摩尔比分别为1∶1、1∶4、4∶1的双金属催化剂(Pd1Pt1、Pd1Pt4、Pd4Pt1),对其进行X射线衍射(XRD)、透射电镜(TEM)、CO化学吸附和X射线光电子能谱(XPS)表征,并详细考察了各催化剂的萘加氢活性和耐硫性能.结果表明,在实验考察范围内,Pd4Pt1催化剂上的萘转化率最高可达98.2%,全饱和产物十氢萘选择性最高可达93.6%,十氢萘反/顺生成率之比最高可达7.8,均高于单金属Pd(97.5%,59.1%,4.3)和Pt(96.8%,39.9%,2.9)催化剂的值.萘在三种催化剂上的加氢速率顺序为vPd4Pt1vPdvPt.添加二苯并噻吩(DBT)后Pd4Pt1上的萘转化率和十氢萘选择性仍然最高,十氢萘反/顺比在Pt催化剂上不受影响,在Pd4Pt1催化剂上稍有降低,而在Pd催化剂上降低明显.在三种不同Pd/Pt摩尔比的双金属催化剂中,Pd4Pt1催化剂上的萘转化率和十氢萘选择性在添加DBT前后都是最佳的.     

Tuning the electrocatalytic activity and durability of low cost Pd70Co30 nanoalloy for oxygen reduction reaction in fuel cells

The factors controlling the electrocatalytic activity for the oxygen reduction reaction (ORR) in fuel cells have been tuned and investigated systematically with the low cost carbon-supported Pd₇₀Co₃₀ nanoalloy. The catalytic activity decreases with increasing annealing temperature due to an increasing degree of alloying (Co content in the Pd lattice) and crystallite size. With a controlled crystallite size of ∼8 nm, the activity is found to decrease with increasing degree of alloying from 18 to 30 at.% Co. However, the catalyst durability increases considerably with annealing temperature due to the alloying of Pd with Co and an increase in crystallite size.     

Highly Selective Pd–Cu/α-Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Catalysts for Liquid-Phase Hydrogenation: The Influence of the Pd: Cu Ratio on the Structure and Catalytic Characteristics

The structure and catalytic characteristics of a series of Pd–Cu/α-Al₂O₃ catalysts with Pd: Cu ratio varied from Pd₁–Cu_0.5 to Pd₁–Cu₄ were studied. The use of α-Al₂O₃ with a small surface area (S_sp = 8 m²/g) as a support made it possible to minimize the effect of diffusion on the catalytic characteristics and to study the structure of Pd–Cu nanoparticles by X-ray diffraction (XRD) analysis. The XRD analysis and transmission electron microscopy (TEM) data indicated the formation of uniform bimetallic Pd–Cu nanoparticles (d = 20–60 nm), whose composition corresponded to a ratio between the metals in the catalyst, and also the absence of monometallic Pd⁰ and Cu⁰ nanoparticles. The study of catalytic properties in the liquid-phase hydrogenation of diphenylacetylene (DPA) showed that the activity of the catalysts rapidly decreased with the Cu content increase; however, in this case, the yield of a desired alkene compound significantly increased. The selectivity of alkene formation on the catalysts with the ratios Pd: Cu = 1: 3 and 1: 4 was superior to the commercial Lindlar catalyst.     

Gold, palladium and gold–palladium supported on silica catalysts prepared by sol–gel method: synthesis, characterization and catalytic behavior in the ethanol steam reforming

Noble-metal-based catalysts supported on silica (Au/SiO₂, Pd/SiO₂ and Au–Pd/SiO₂) were prepared by the sol–gel method and were evaluated in the steam reforming of ethanol for hydrogen production. The catalysts were characterized by N₂ physisorption (BET/BJH methods), X-ray diffraction, temperature programmed reduction analysis, H₂ chemisorption, atomic absorption spectrophotometry and Raman spectroscopy. The structural characterization of the Au- and Pd-containing catalysts after calcination showed that the solids are predominantly formed by Au⁰, Pd⁰ and PdO species and was observed that the metallic Pd dispersion diminished in the presence of Au⁰. The results revealed that the catalytic behavior could be influenced by the experimental conditions and the nature of the catalyst employed. The Pd/SiO₂ catalyst showed the best performance among the catalysts tested at the highest reaction temperature (600 °C) due to the more effective action of the metallic active phase, which covers a greater area in this sample. At this same reaction temperature, the Au–Pd/SiO₂ catalyst showed a significant deactivation, probably due to the lower Pd dispersion presented by this catalyst.     

Catalytic partial oxidation of methanol over Au–Pd bimetallic catalysts: a comparative study of SBA-16, SBA-16-CeO<Subscript>2</Subscript>, and CeO<Subscript>2</Subscript> as supports

Au–Pd catalysts supported on SBA-16, SBA-16-CeO₂, and CeO₂ had been studied for partial oxidation of methanol to produce H₂. The physicochemical characteristics of the catalysts prepared by deposition–precipitation using urea hydrolysis were examined by inductively coupled plasma atomic emission spectroscopy (ICP-AES), Brunauer-Emmett-Teller (BET), X-ray powder diffraction (XRD), Temperature-programmed reduction (TPR), and H₂ temperature-programmed desorption (H₂-TPD) analyses. The results show that Au_xPd_y alloys are observed in Au–Pd/SBA-16 and Au–Pd/SBA-16-CeO₂ catalysts. The catalytic results demonstrate that both Au–Pd/SBA-16 and Au–Pd/SBA-16-CeO₂ catalysts exhibit higher activity and lower CO selectivity than the Au–Pd/CeO₂ catalyst. This could be ascribed to the formation of Au_xPd_y alloys. The comparison of the Au–Pd/SBA-16 and Au–Pd/SBA-16-CeO₂ catalysts reveals that the Au–Pd/SBA-16-CeO₂ shows the lower CO selectivity, probably due to the presence of CeO₂.     

钯掺杂的25-原子和38-原子金纳米团簇

In this work, we describe two synthetic procedures for preparing palladium doped 25-atom nanoclusters (referred to as Pd₁Au₂₄(SR)₁₈, where ―SR represents thiolate, R=C₂H₄Ph). Pure Pd₁Au₂₄(SC₂H₄Ph)₁₈ nanoclusters are isolated by solvent extraction and size exclusion chromatography. Mass spectrometry and optical spectroscopy analyses demonstrate that the Pd₁Au₂₄(SC₂H₄Ph)₁₈ nanocluster adopts the same core-shell structure as that of the homogold Au₂₅(SC₂H₄Ph)₁₈ nanocluster, that is, a Pd- or Au-centered icosahedron surrounded by six Au₂(SR)₃ “staple”-like motifs. Similar doping behavior has also been observed in 38-atom M₃₈(SR)₂₄ (M: metal) nanoclusters, indicating the unique behavior of Pd dopant being preferentially located in the icosahedral center. The catalytic activity of Pd₁Au₂₄(SC₂H₄Ph)₁₈ has also been evaluated for the selective hydrogenation of α,β-unsaturated ketone (e.g., benzalacetone) to α,β- unsaturated alcohol, and a 42% conversion of benzalacetone is attained.     

Pd nanoparticles supported on CeO2 as efficient catalyst for hydrogen generation from formaldehyde solution at room temperature

A facile and efficient method for facilitating hydrogen generation from formaldehyde aqueous solution was developed using Pd nanoparticles supported on CeO₂ (Pd/CeO₂) as the catalyst. The prepared Pd/CeO₂ catalyst exhibited 100% H₂ selectivity and excellent catalytic activity for formaldehyde dehydrogenation with the initial rate of 2089 ml min⁻¹ g_Pd⁻¹ at room temperature and atmospheric pressure without any extra additive. The prepared catalyst was stable and reusable, and its catalytic activity kept almost unchanged after it was reused for the fifth run. Therefore, it is considered that this Pd/CeO₂ based hydrogen generation system may serve as an alternative hydrogen supply candidate for practical application.     

Pd/Co双金属纳米颗粒的制备及催化制氢性能

采用聚乙烯吡咯烷酮(PVP)保护的化学共还原法制备了Pd/Co双金属纳米颗粒, 研究了PVP及还原剂(NaBH₄)的用量、金属盐浓度、金属比例等对Pd/Co双金属纳米颗粒催化NaBH₄制氢性能的影响. 透射电子显微镜(TEM)的结果表明, 所制备的Pd/Co双金属纳米颗粒的平均粒径在1.5-2.8 nm之间. Pd/Co双金属纳米颗粒(BNPs)的催化活性远高于Pd与Co单金属纳米颗粒的活性; 当Pd/Co的理论原子比为1/9时, 双金属纳米颗粒的催化活性最高可达15570 mol·mol^-1·h^-1 (文中纳米颗粒的催化活性均为每摩尔Pd的活性). 密度泛函理论(DFT)的计算结果表明, Pd原子与Co原子之间发生电荷转移, 使得Pd原子带负电而Co原子带正电, 荷电的Pd和Co原子进而成为催化反应的活性中心. 所制备的Pd/Co双金属纳米颗粒具有很好的催化耐久性, 即使重复使用5次后, 该催化剂仍具有较高的催化活性, 且使用后的纳米颗粒催化剂也没有出现团聚现象. 双金属纳米颗粒催化NaBH₄水解反应的活化能约为54 kJ·mol^-1.     

Preparation of magnetic Fe3O4/P (GMA‐DVB)‐PEI/Pd highly efficient catalyst with core‐shell structure

In this paper, a simple route for palladium (Pd) nanoparticles attached to the surface of hollow magnetic Fe₃O₄/P (GMA‐DVB)‐polyethyleneimine (PEI) microspheres was established. Due to the large amount of imidogen groups and tertiary amine groups presenting in the PEI, Pd²⁺ ions could be anchored to the support by complexation with a polyfunctional organic ligand. Thereafter, a magnetic Pd catalyst having a high loading amount and good dispersibility was obtained by reducing Pd²⁺ ions. Afterwards, the prepared catalyst was characterized by TEM, SEM, FTIR, XRD, TGA, VSM, and UV–vis in detail. Ultimately, their catalytic activity was evaluated using the reduction of 4‐nitrophenol (4‐NP). Research showed that the Fe₃O₄/P (GMA‐DVB)‐PEI/Pd catalyst possessed high catalytic performances for the reduction of 4‐NP with a conversion rate of 98.43% within 540 s. Furthermore, the catalyst could be easily recovered and reused at least for nine successive cycles.     

Influence of Pd deposition pH value on the performance of Pd-CuO/SiO2 catalyst for semi-hydrogenation of 2-methyl-3-butyn-2-ol（MBY）

The selective hydrogenation of C≡C to C=C bonds is an important step, yet remains to be a great challenge in chemical industry. In this study, we have revealed the influence of Pd deposition pH value on the catalytic performance of Pd-CuO/SiO₂ catalyst for the semi-hydrogenation of 2-methyl-3-butyn-2-ol（MBY）. Trace amount of Pd（about 500 ppm） was loaded via deposition-reduction method on CuO/SiO₂ support by using H₂PdCl₄ solution as precursor and NaBH<...     

Surface composition of PdCuAu ternary alloys: a combined LEIS and XPS study

PdCuAu ternary alloy samples with different composition were synthesized on top of ZrO₂‐modified porous stainless steel disks by the sequential electroless deposition technique. The structure, morphology and bulk composition of the samples were characterized by X‐ray diffraction (XRD), scanning electron microscopy and energy dispersive X‐ray spectroscopy (EDX). Complete alloy formation with a pure fcc phase for the Pd₇₁Cu₂₆Au₃, Pd₇₀Cu₂₅Au₅ and Pd₆₇Cu₂₄Au₉ samples and a bcc structure for the Pd₆₂Cu₃₆Au₂ and Pd₆₀Cu₃₇Au₃ samples were obtained upon annealing at 500 °C for 120 h as revealed by XRD. A combination of low‐energy ion scattering (LEIS) and X‐ray photoelectron spectroscopy (XPS) was used to investigate the surface properties of the PdCuAu alloys. XPS results confirmed alloy formation under the annealing conditions. XPS analysis also revealed that the near‐surface regions of the alloys became enriched in Pd with respect to the bulk composition determined by EDX. In contrast, LEIS and angle‐resolved XPS analyses showed that the top‐most surface layers in all samples were copper‐rich compared with the bulk composition. This high Cu surface concentration could impart resistance to bulk sulfide formation to the PdCuAu alloy membranes. Copyright © 2015 John Wiley & Sons, Ltd.     

Adsorption-Induced Segregation as a Method for the Target-Oriented Modification of the Surface of a Bimetallic Pd–Ag Catalyst

The effect of palladium segregation was studied which resulted from the effect of CO and O₂ on the surface structure and catalytic characteristics of the Pd–Ag₂/Al₂O₃ catalyst. The IR-spectroscopic study of adsorbed CO showed that Pd₁ centers isolated from each other by silver atoms predominated on the surface of reduced Pd–Ag₂/Al₂O₃, as evidenced by the almost complete absence of absorption bands typical for the multicentred CO adsorption. In the course of catalyst treatment with CO and O₂, the intensity of absorption bands characteristic of the multicenter CO adsorption considerably increased due to the transformation of a portion of monatomic Pd₁ centers into multiatomic Pd_n ones as a result of the surface segregation of Pd. In this case, a substantial increase in the catalyst activity in the liquid-phase hydrogenation of diphenylacetylene was observed. It was established that, after treatment with CO, the catalyst selectivity for the formation of a target olefin (stilbene) remained almost constant, whereas the treatment with O₂ led to a decrease in the selectivity because of more considerable surface modification.     

Highly Stable Carbon-Shell Encapsulated Ni−Cu Bimetallic Catalysts for Efficient Conversion of Levulinic Acid to γ-Valerolactone

Non-noble Ni−Cu alloys serve as an alternative catalytic material for noble metal-based catalysts that could be applied in the efficient conversion of levulinic acid (LA) into the high value γ-valerolactone (GVL). However, maintaining the catalytic stability for Ni−Cu nanoparticles in the LA hydrogenation process remains a substantial challenge, Herein, this problem is solved by constructing carbon-protected catalytic sites within carbon layer-coated Ni−Cu nanoalloy composite via pyrolysis of NiCu_x(OH)/glucose precursor. The optimized NiCu_0.68@C catalyst exhibits excellent stability and selectivity to GVL (>99 %) in the hydrogenation of LA reaction. Various characterization indicates that the enhancement in stability originates from the protective effect of the carbon layer, which prevents the metal leaching, oxidation and aggregation of Ni−Cu nanoparticles during the reaction process. This work greatly advances non-noble metal-catalyzed conversion of LA to GVL and helps the rational design of bimetallic catalysts.     

High performance Fe and N-codoped graphene quantum dot supported Pd3Co catalyst with synergistically improved oxygen reduction activity and great methanol tolerance

Designing high-performance and durable non-platinum catalysts as oxygen reduction reaction (ORR) catalysts is still a major barrier of fuel cell commercialization. In this work, simple hydrothermal and impregnation routes were applied to prepare non-platinum Pd-Co bimetallic nano-catalysts such as Fe-N doped graphene quantum dot (Fe-N-GQD) supported Pd₃Co (Pd₃Co/Fe-N-GQD 10 wt%), carbon supported Pd₃Co/C (10 wt%), graphene quantum dot supported Pd₃Co/C (10 wt%). The synthesized catalysts were physico-chemically characterized by X-ray diffraction (XRD), Raman spectroscopy, transmission electronmicroscopy (TEM), and X-ray photoelectron spectroscopy (XPS). The electrochemical investigation was carried out in three electrode half-cell system to evaluate the catalyst activity for oxygen reduction reaction (ORR), the tolerance to methanol crossover and durability. In comparison to commercial Pt/C (ETEK, 20 wt%), the Pd₃Co/Fe-N-GQD with lower weight percentage catalyst (∼10 wt%) displayed comparable electrocatalytic activity toward ORR with even higher methanol-tolerance capability and durability. The fabricated Pd₃Co/Fe-N-GQD with (10 wt %) metal loading exhibited only 20% lower activity than Pt/C (ETEK, 20 wt%) toward ORR. Nevertheless the durability study of the catalyst in acidic media showed that the Pd₃Co/Fe-N-GQD preserve 40% of its activity while Pt/C (ETEK, 20 wt%) exhibited only 20% of its initial catalytic activity for ORR. Moreover the activity loss in the presence of methanol (0.1 M) was obtained for Pt/C (ETEK, 20 wt%) and Pd₃Co/Fe-N-GQD 35% and 14%, respectively. To investigate the role of catalyst support, catalytic activities of Pd₃Co/Fe-N-GQD, Pd₃Co/C, Pd₃Co/GQD and Pd/Fe-N-GQD were compared. The results demonstrated superior catalytic activity of Pd₃Co/Fe-N-GQD which could be related to the cocatalytic role of Fe-N-GQD due to the presence numerous of active sites exposed to the reactants.     

Influence of phosphorus concentration on the state of the surface layer of Pd–P hydrogenation catalysts

Phase composition and surface layer state of the Pd–P hydrogenation catalyst formed at various P/Pd ratios from Pd(acac)₂ and white phosphorus in a hydrogen atmosphere were determined. Palladium on the catalyst surface is mainly in two chemical states: as Pd(0) clusters and as palladium phosphides. As the P/Pd ratio increases, the fraction and size of palladium clusters decrease, and also the phase composition of formed palladium phosphides changes: Pd₃P_0.8 → Pd₅P₂ → PdP₂. The causes of the modifying action of phosphorus on the properties of palladium catalysts for hydrogenation of unsaturated compounds were considered.     

Fe3O4‐SAHPG‐Pd0 nanoparticles: A ligand‐free and low Pd loading quasiheterogeneous catalyst active for mild Suzuki–Miyaura coupling and C?H activation of pyrimidine cores

This paper reports a green magnetic quasiheterogeneous efficient palladium catalyst in which Pd⁰ nanoparticles have been immobilized in self‐assembled hyperbranched polyglycidole (SAHPG)‐coated magnetic Fe₃O₄ nanoparticles (Fe₃O₄‐SAHPG‐Pd⁰). This catalyst has been used for effective ligandless Pd catalyzed Suzuki–Miyaura coupling reactions of different aryl halides with substituted boronic acids at room temperature and in aqueous media. Herein, SAHPG is used as support; it also acts as a reducing agent and stabilizer to promote the transformation of Pd^II to Pd⁰ nanoparticles. Also, this environmental friendly quasiheterogeneous catalyst is employed for the first time in the synthesis of new pyrimido[4,5‐b]indoles via oxidative addition/C? H activation reactions on the pyrimidine rings, which were obtained with higher yield and faster than when Pd(OAc)₂ was used as the catalyst. Interestingly, the above‐mentioned catalyst could be recovered in a facile manner from the reaction mixture by applying an external magnet device and recycled several times with no significant decrease in the catalytic activity.     

The Role of Pd2+/Pd0 in Hydrogenation by [Pd(2‐pymo)2]n: An X‐ray Absorption and IR Spectroscopic Study

The metal–organic framework (MOF) [Pd(2‐pymo)₂]_n (2‐pymo=2‐pyrimidinolate) was used as catalyst in the hydrogenation of 1‐octene. During catalytic hydrogenation, the changes at the metal nodes and linkers of the MOF were investigated by in situ X‐ray absorption spectroscopy (XAS) and IR spectroscopy. With the help of extended X‐ray absorption fine structure and X‐ray absorption near edge structure data, Quick‐XAS, and IR spectroscopy, detailed insights into the catalytic relevance of Pd²⁺/Pd⁰ in the hydrogenation of 1‐octene could be achieved. Shortly after exposure of the catalyst to H₂ and simultaneously with the hydrogenation of 1‐octene, the aromatic rings of the linker molecules are hydrogenated rapidly. Up to this point, the MOF structure remained intact. After completion of linker hydrogenation, the linkers were also protonated. When half of the linker molecules were protonated, the onset of reduction of the Pd²⁺ centers to Pd⁰ was observed and the hydrogenation activity decreased, followed by fast reduction of the palladium centers and collapse of the MOF structure. Major fractions of Pd⁰ are only observed when the hydrogenation of 1‐octene is almost finished. Consequently, the Pd²⁺ nodes of the MOF [Pd(2‐pymo)₂]_n are identified as active centers in the hydrogenation of 1‐octene.     

Supported Pd–Cu Bimetallic Nanoparticles That Have High Activity for the Electrochemical Oxidation of Methanol

Monodisperse bimetallic Pd–Cu nanoparticles with controllable size and composition were synthesized by a one‐step multiphase ethylene glycol (EG) method. Adjusting the stoichiometric ratio of the Pd and Cu precursors afforded nanoparticles with different compositions, such as Pd₈₅–Cu₁₅, Pd₅₆–Cu₄₄, and Pd₃₉–Cu₆₁. The nanoparticles were separated from the solution mixture by extraction with non‐polar solvents, such as n‐hexane. Monodisperse bimetallic Pd–Cu nanoparticles with narrow size‐distribution were obtained without the need for a size‐selection process. Capping ligands that were bound to the surface of the particles were removed through heat treatment when the as‐prepared nanoparticles were loaded onto a Vulcan XC‐72 carbon support. Supported bimetallic Pd–Cu nanoparticles showed enhanced electrocatalytic activity towards methanol oxidation compared with supported Pd nanoparticles that were fabricated according to the same EG method. For a bimetallic Pd–Cu catalyst that contained 15 % Cu, the activity was even comparable to the state‐of‐the‐art commercially available Pt/C catalysts. A STEM‐HAADF study indicated that the formation of random solid‐solution alloy structures in the bimetallic Pd₈₅–Cu₁₅/C catalysts played a key role in improving the electrochemical activity.     

Theoretical research on Pd cluster catalysts for the direct dehydrogenation of propane to propylene

In this article, the feasibility of catalytic dehydrogenation of propane by Pd clusters (Pd₇, Pd₆C, Pd₆Si, Pd₆Ge, and Pd₆Sn) was investigated by using density functional theory (DFT). It was found that Pd₆Sn has the strongest electron mobility and the ability to activate C H bonds, and the highest adsorption barrier (−75.16 kcal/mol) with propylene. The first pathway of the Pd₆Sn-catalyzed primary reaction has the lowest decisive step barrier (16.65 kcal/mol), and the second pathway of the secondary reaction has the highest decisive step barrier (62.25 kcal/mol). It was demonstrated that both the catalyst's electron-leaping ability and the ability to activate C H bonds were the key factors affecting the activity, and the adsorption strength of the catalyst to the product was the main factor affecting the selectivity. It was shown that Pd cluster-catalyzed PDH is theoretically feasible and Pd₆Sn is likely to be a potential cluster catalyst for propane dehydrogenation.     

Augmented formic acid electro-oxidation at a co-electrodeposited Pd/Au nanoparticle catalyst

In this study, the formic acid electro-oxidation reaction (FAEOR) was catalyzed on a Pd-Au co-electrodeposited binary catalyst. The kinetics of FAEOR were intensively impacted by changing the Pd²⁺:Au³⁺ molar ratio in the deposition medium. The Pd₁-Au₁ catalyst (for which the Pd²⁺:Au³⁺ molar ratio was 1:1) acquired the highest activity with a peak current density for the direct FAEOR (I_p) of 4.14 mA cm^?2 (ca. 13- times higher than that (ca. 0.33 mA cm^?2) of the pristine Pd₁-Au₀ catalyst). It also retained the highest stability that was denoted in fulfilling ca. 0.292 mA cm^?2 (ca. 19-times higher than 0.015 mA cm^?2 of the pristine Pd₁-Au₀ catalyst) after 3600 s of continuous electrolysis at 0.05 V. The CO stripping and impedance measurements confirmed, respectively, the geometrical and electronic enhancements in the proposed catalyst.