ZnO-B2O3玻璃对0.95(Mg0.9Zn0.1)TiO3-0.05CaTiO3陶瓷烧结特性和微波介电性能的影响

采用传统的固相烧结工艺制备0.95(Mg0.9Zn0.1) TiO3-0.05CaTiO3陶瓷.研究了ZnO-B2O3玻璃掺杂对0.95(Mg0.9Zn0.1)TiO3-0.05CaTiO3陶瓷烧结特性、晶相成分、微观结构和微波介电性能的影响.适量的ZnO-B2O3玻璃掺杂能有效地降低烧结温度,促进致密化,从而提高微波介电性能.随着烧结温度的升高,密度、介电常数εr和Q×f值均达到最大值之后再逐渐减小.当ZnO-B2O3玻璃添加量为5wt;时,0.95(Mg0.9Zn0.1) TiO3-0.05CaTiO3陶瓷在1075℃烧结3h,获得最佳微波介电性能:εr=19.5,Q×f=62100 GHz,τf=-13 ppm/℃.     

B2O3-CuO-Li2CO3对CSLST陶瓷微波介电性能影响的研究

研究了添加5;B2O3-CuO基础上再添加不同含量的Li2CO3 复合烧结助剂对(Ca0.9375Sr0.0625)0.3(Li0.5Sm0.5)0.7TiO3 (CSLST)陶瓷的烧结行为及微波介电性能的影响.研究结果表明:添加复合烧结助剂的陶瓷烧结后其晶相仍呈斜方钙钛矿结构.在不劣化微波介电性能的条件下,陶瓷的烧结温度可降至950 ℃,随Li2CO3含量的增加,添加复合烧结助剂的CSLST陶瓷的体积密度和介电常数εr 逐渐降低.当Li2CO3添加量为0.5 ;时,在950 ℃保温5 h,所制得的陶瓷具有优良的微波介电性能:εr=84.7,Qf=1929 GHz,τf=28.76×10-6 /℃.     

BBZS掺杂对BaO-Sm2O3-TiO2系微波介质陶瓷性能的影响

利用固相法制备BaO-Sm2O3-TiO2系微波介质陶瓷.通过复合添加氧化物ZnO、CuO和玻璃料Bi2O3-B2O3-ZnO-SiO2(BBZS),系统的烧结温度降至900℃.研究了玻璃料的添加量对介电性能的影响.按BaSm2Ti4O12+1wt;ZnO+1wt;CuO+xwt;BBZS(0相似文献   

添加LCB玻璃的CSLST微波介质陶瓷低温烧结及其性能研究

采用传统电子陶瓷工艺制备了添加Li2CO3-CuO-B2O3(LCB)玻璃为烧结助剂的(Ca0.9375 Sr0.0625)0.3(Li0.5Sm0.5)0.7TiO3 (CSLST)微波介质陶瓷,并对其烧结特性、晶相组成和介电性能进行了系统的研究.结果表明:通过液相烧结,LCB玻璃能有效降低CSLST烧结温度至900℃.XRD分析结果显示添加LCB玻璃后材料中均产生了杂相.性能分析结果发现随着LCB添加量的增大,陶瓷的体积密度、介电常数εr、品质因数与谐振频率乘积Q×f呈现先上升后下降的趋势,频率温度系数Tf则单调降低.添加质量分数为12.5;的LCB玻璃的CSLST陶瓷在900℃下保温5h可以完全烧结,并具有最佳的微波介电性能:εr=77.7,Q×f=1845 GHz,Tf=21.35 × 10-6/℃.     

Sr2+置换改性Ca0.25(Li1/2Sm1/2)0.75TiO3陶瓷的微波介电性能研究

采用固相法制备了(Ca1-xSrx)0.25(Li1/2Sm1/2)0.75TiO3(CSLST-x)( x= 0～1/10)系列微波介质陶瓷材料,研究不同含量的Sr2+含量对该体系的相组成、烧结性能和微波介电性能影响.在x=1/22～1/10范围内,Sr2+的掺杂不会改变晶体的结构;在1175～1200 ℃烧结时,相同烧结温度下随着Sr2+含量的增加,介电常数εr增大,无载品质因数与谐振频率乘积Qf值降低;置换离子Sr2+的添加使该体系的烧结温度降低了近200 ℃,并保持良好的微波介电性能.其中,x=1/16的CSLST陶瓷在1200 ℃烧结,保温5 h时具有较好的微波介电性能:εr=97.2,Qf=2490 GHz,τf =14.74 ppm/℃.     

B2O3掺杂对0.69CaTiO3-0.31LaAlO3微波介质陶瓷的性能影响

采用固相反应法,研究了B2O3对0.69CaTiO3-0.31LaAlO3微波介质陶瓷烧结性能与介电性能的影响.通过X射线衍射分析表明,B2O3的引入未改变陶瓷的晶相组成.添加适量B2O3的可有效的降低0.69CaTiO3-0.31LaAlO3介电陶瓷的烧结温度,增强致密性并提高介电性能.在1500℃烧结温度,B2O3掺杂量为0.3wt;时,0.69CaTiO3-0.31LaAlO3陶瓷获得最佳介电性能:εr≈45.4,Qf≈52800 GHz,τf≈8.78 ppm/℃.     

硼酸对BaAl2Si2O8陶瓷相转变和微波介电性能的影响

采用传统固相烧结工艺制备BaAl2Si2O8(BAS)基微波介质陶瓷。研究添加H3BO3对BaAl2Si2O8基微波介质陶瓷的烧结特性、相转变、微波介电性能以及微观结构的影响。结果表明,H3BO3可以将BAS陶瓷烧结温度降低200℃左右,可以有效促进六方钡长石向单斜钡长石转变。当H3BO3添加量为10mol%时,具有最佳的综合微波介电性能,εr=6.3,Q×f=14700 GHz。H3BO3添加量为30mol%时,τf值最接近零值,为-13 ppm/℃。     

复合烧结助剂对CSLST微波介质陶瓷的性能影响

研究了复合添加12.5wt; Li2CO3-B2O3-CuO (LBC)玻璃和不同含量(0～4.0wt;) Bi2O3对(Ca0.9375Sr0.0625)0.3 (Li0.5Sm0.5)0.7TiO3 (CSLST)微波介质陶瓷烧结特性、相组成和介电性能的影响,分析了CSLST陶瓷与银的共烧行为.结果表明:复合添加LBC玻璃和Bi2O3能有效降低CSLST陶瓷烧结温度至875℃,XRD分析结果显示添加0～ 1.0wt; Bi2O3有Cu3Ti3O和CaCu3Ti4O12新相产生,当Bi2O3的添加量大于2.0wt;,杂相消失.随着Bi2O3添加量的增加,陶瓷的频率温度系数Tf向负方向偏移.复合添加12.5wt;LBC玻璃和2.0wt; Bi2O3的CSLST陶瓷,在875℃保温5h烧结后,具有优良的微波介电性能:εr=78.9,Q×f=1852 GHz,τε=3×10-6/C.该材料与银共烧界面结合状况良好,无明显扩散,适合作为LTCC的材料.     

Zn0.99Cu0.01Al2O4-TiO2基微波介质陶瓷的研究

以分析纯ZnO、CuO、Al2O3以及TiO2为原料,采用传统固相法制备了(1-x)Zn0.99Cu0.01Al2O4-xTiO2(ZCAT,x=0-0.25)微波介质陶瓷.研究了不同TiO2的添加量对ZCAT陶瓷烧结性能、晶相组成、显微结构以及微波介电性能的影响.研究结果表明:Zn0.99Cu0.01Al2O4与TiO2以两相的形式共存,不会形成固溶体;烧结温度随着TiO2添加量的增大显著降低;ZCAT陶瓷的体积密度、品质因数随着TiO2含量的增多而减小,介电常数则随着TiO2含量的增多而增大,添加适量TiO2将ZCAT陶瓷的频率温度系数调节至近零.当x=0.23时,陶瓷可在1380℃烧结3h后获得最佳的微波介电性能:介电常数εr=11.4,品质因数Q ×f=38155 GHz以及谐振频率温度系数Υf=-2.4×106/℃.     

Al2O3掺杂对微波介质陶瓷Ca0.16Sr0.04Li0.4Nd0.4TiO3烧结特性和微波介电性能的影响

采用固相反应法在1300℃烧结4h得到了致密的具有钙钛矿结构的Ca0.16Sr0.04Li0.4Nd0.4TiO3微波介质陶瓷.通过X射线衍射仪、扫瞄电子显微镜和矢量网络分析仪系统的研究了不同含量Al2O3掺杂对Ca0.16Sr0.04Li0.4Nd0.4TiO3(CSLNT)陶瓷的烧结行为、晶体结构、显微形貌以及微波介电性能的影响.结果表明,对于CSLNT+ xwt;Al2O3陶瓷,随着Al2O3掺杂量的增加,介电常数(εr)有轻微的降低,而温度系数(τf)有所增加;由于第二相的出现导致了品质因子(Q·f)先增后减.当Al2O3掺杂量为2wt;时,其介电性能最佳的致密化烧结温度为1200℃,此时具有最佳的微波介电性能:εr=112.6,Q·f=1698 GHz和τf=31.9 ppm/℃.     

Optical properties of the germanate melilites Sr2MgGe2O7, Sr2ZnGe2O7 and Ba2ZnGe2O7

Refractive indices and their dispersion in the wavelength range from 365 nm to 2325 nm and transmission ranges of the tetragonal melilite‐type germanates Sr₂MgGe₂O₇, Sr₂ZnGe₂O₇ and Ba₂ZnGe₂O₇ were determined. The uniaxial positive crystals Sr₂MgGe₂O₇ and Ba₂ZnGe₂O₇ both offer the possibility for phase matched second harmonic generation, a detailed analysis of phase matching conditions is given. The refractive indices of Sr₂ZnGe₂O₇ show an isoindex (isotropic) point at 467 nm. The investigation was performed on Czochralski grown large single crystals. The crystal structure of all three germanates were determined by means of X ‐ray diffraction. The results corroborate unmodulated melilite‐type structures at room temperature. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Na2 O-B2O3-SiO2-CaO-P2O5-F生物微晶玻璃制备与性能研究

采用烧结法,选用Na2O-B2O3-SiO2为基础玻璃(NBS),按照氟磷灰石组成配比添加CaO,P2O5,CaF2三种组分,制备Na2O-B2O3-SiO2-CaO-P2O5-CaF2生物微晶玻璃.利用差热分析、X射线衍射分析及扫描电镜等测试手段对微晶玻璃物相、微观结构进行了测试和分析,并采用模拟体液对样品的生物活性进行了验证.结果表明:随着热处理温度升高,样品的晶化程度逐步提高,当热处理温度在750℃时,可以获得主晶相为氟磷灰石,晶粒尺寸在100 nm左右、其晶化率≥80;的微晶玻璃样品,通过模拟体液浸泡实验证明了样品具有一定的生物活性.     

微波加热Al_2O_3-ZrO_2-SiO_2系组成点的相分析

基于Al2O3-ZrO2-SiO2体系,选择不同组成点,在常规烧结后,进行不同条件下的微波处理,采用XRD检测不同处理后材料的组成变化,分析了微波与材料的相互作用,以及动力学条件与热力学条件对微波处理后相变化的影响。通过与传统Al2O3-ZrO2-SiO2体系相图的相组成比较,排除了升温制度、测温误差对实验结果的影响,对微波作用下的非热效应进行了分析。     

ZrB2/ZrO2复合粉体的放电等离子烧结行为

以高纯ZrB2粉末和ZrOCl2为原料,应用沉淀法制备了ZrO2包覆ZrB2复合粉体,并通过放电等离子烧结技术(SPS)得到高致密度的ZrB2/ZrO2复合材料.采用TEM、SEM、XRD对粉体及其烧结体进行测试,并对纯ZrB2粉体与包覆式复合粉体的烧结行为进行分析.研究结果表眀:利用沉淀法可以形成包裹结构;包覆式复合粉体的烧结性能大大优于纯ZrB2粉体,在1950℃的烧结温度下,保温10min,得到相对致密度97.8;的ZrB2/ZrO2复合材料.     

Ag2O/TiO2异质结的光催化活性及耐光腐蚀性研究

以钛酸丁酯、硝酸铋和硝酸银为原料,FTO为基底,采用水热法结合超声沉积法合成了Ag2 O/TiO2异质结光催化剂.采用场发射扫描电子显微镜(FESEM)、X射线衍射仪(XRD)、紫外-可见吸收光谱(UV-Vis)分析测试手段对样品的形貌和结构进行了表征.结果表明,Ag2O/TiO2异质结是由直径约200 ～ 300 nm的TiO2纳米棒镶嵌着Ag2O纳米颗粒组成,与TiO2纳米棒阵列相比,Ag2O/TiO2异质结在可见光区有明显的光吸收.Ag2O/TiO2异质结的光催化效率明显提高.尤为重要的是,经光处理后,最终得到稳定的Ag-Ag2O/TiO2三元体系,并对Ag-Ag2 O/TiO2三元体系提高光催化稳定性和活性的机理进行了分析.     

Sr2TiSi2O8的合成和非线性光学性质研究

采用固相反应法合成了具有硅钛钡石(Ba2TiSi2O8)结构的化合物Sr2TiSi2O8,合成温度在1250℃.对Sr2TiSi2O8的XRD衍射图进行指标化表明它属于四方晶系,晶胞系数为a=b=0.83135nm,c＝0.50190nm,α＝β＝γ＝90°.Sr2TiSi2O8的粉末倍频信号强度约是KH2PO4(KDP)的8倍.反射光谱显示其紫外吸收边为270nm左右.利用自发成核法进行了Sr2TiSi2O8晶体生长研究.     

白光LED用荧光粉SrAl_2Si_2O_8∶Eu~(2+)合成条件优化研究

Sr_(0.975)Al_2Si_2O_8∶Eu_(0.025)~(2+)系列荧光粉利用高温固相法合成,系统研究了预烧温度、预烧时间、烧成温度和助溶剂硼酸的量对荧光体晶体结构和发光性能的影响;研究结果表明,各试样均为单斜晶系SrAl_2Si_2O_8,荧光体的X射线衍射强度、荧光体的晶粒尺寸及荧光体的发射强度,均随着预烧温度、预烧时间、烧成温度和助溶剂硼酸量的增加,呈先增加后减小的变化趋势。当预烧温度为1000℃,预烧时间为150 min,烧成温度为1250℃,助溶剂硼酸的量为6wt%,制得的荧光体Sr_(0.975)Al_2Si_2O_8∶Eu_(0.025)~(2+)的发光强度最强,优化了合成条件。     

P2O5对CaO-MgO-Al2O3-SiO2系微晶玻璃析晶的影响

采用熔融法制备了不同P2O5含量的CaO-MgO-Al2O3-SiO2玻璃样品,研究了P2O5对该系微晶玻璃析晶的影响规律.结果表明:在所研究的CaO-MgO-Al2O3-SiO2玻璃中,P2O5的最大溶解量在10.0;质量分数左右,超过其饱和溶解度后将析出α-磷酸钙相.玻璃中添加4.0;质量分数P2O5时以表面析晶为主,析出晶体为钙长石和少量硅灰石.随着P2O5含量的提高, α-磷酸钙逐渐析出,同时钙长石和硅灰石的析出逐渐降低.进一步提高P2O5含量抑制了玻璃的表面析晶,促进了玻璃的分相和整体析晶.当P2O5的含量达到10;时,玻璃以整体析晶为主,在分相区内外区域析出晶体的形态非常相似,均呈现为细小粒状.     

TiO2/SiO2纤维的表征及其光催化活性

本文采用溶胶-凝胶法及离心甩丝,以TiCl4为钛源、乙酰丙酮为螯合剂成功制备了TiO2/SiO2纤维,并采用XRD 、FE-SEM、FT-IR和DSC -TG等手段对样品结构和性能进行表征.结果表明掺入SiO2可以抑制TiO2晶粒长大和晶型转变,700℃热处理后,未掺SiO2和掺15wt; SiO2的样品晶粒大小分别为32.4 nm和7.6 nm.TiO2/SiO2纤维直径为10～20μm,且表面含有大量纳米气孔.以活性艳红X-3B溶液为降解对象,研究了掺杂量、热处理温度对纤维光催化活性的影响,表明最优的方案为掺15wt; SiO2、热处理制度为700℃/2 h.     

溶剂热合成CuInS2纳米粉体及薄膜的制备

本文以氯化铜、氯化铟、硫脲为原料,以乙二醇为溶剂,采用溶剂热法在常压下合成了片状的CuInS2(CIS) 纳米粉体.研究了合成温度、合成时间、溶液浓度对合成产物CIS物相和形貌的影响.采用涂覆工艺对粉体成膜,研究了热处理对CIS薄膜的影响.采用X射线衍射(XRD)、场发射扫描电镜(FESEM)及能谱仪(EDS)对合成产物进行了分析表征.研究结果表明:随着合成温度的升高和合成时间的延长,合成粉体的纯度提高.随着溶液浓度的增大,衍射峰出现宽化现象,合成粉体的粒径变小.在合成温度为195 ℃,保温时间为12 h,反应溶液浓度为氯化铜0.02 mol/L、氯化铟0.02 mol/L、硫脲0.04 mol/L的条件下,制备得到单一的CIS片状纳米粉体,片状颗粒的大小为200~500 nm,最终经过热处理能获厚度在5~8 μm左右的相对致密的CIS薄膜.