Glasses in the system Na₂O/B₂O₃/Al₂O₃/In₂O₃ were melted and subsequently tempered in the range from 500 to 700 °C. Depending on the chemical composition, various crystalline phases were observed. From samples without Al₂O₃, In₂O₃ could not be crystallized from homogeneous glasses, because either spontaneous In₂O₃ crystallization occurred during cooling, or other phases such as NaInO₂ were formed during tempering. The addition of alumina, however, controlled the crystallization of In₂O₃. Depending on the crystallization temperature applied, the crystallite sizes were in the range from 13 to 53 nm. The glass matrix can be dissolved by soaking the powdered glass in water. This procedure can be used to prepare nano-crystalline In₂O₃-powders.     

Glass formation and optical properties of glasses in the systems (R2O or R''O)-Ta2O5---Ga2O3

Gallate glasses containing no conventional glass formers were obtained in the systems (Na₂O, K₂O or Cs₂O)-Ta₂O₅---Ga₂O₃ and (Sr or BaO)-Ta₂O₅---Ga₂O₃ by an ordinary crucible-melting technique. The glasses showed high optical transmission in the infrared as well as in the visible region. Infrared spectroscopic analysis suggested that the Ga³⁺ ions are tetrahedrally coordinated in the glasses. The glass-forming tendency of the melt and the infrared transmission of the glasses are discussed in terms of the glass structure.     

Characteristics of ZnO–B2O3–CaO–Na2O–P2O5 glass powders prepared by spray pyrolysis

Fine-sized ZnO–B₂O₃–CaO–Na₂O–P₂O₅ glass powders with spherical shape were directly prepared by high temperature spray pyrolysis. The ZnO–B₂O₃–CaO–Na₂O–P₂O₅ powders prepared by spray pyrolysis at temperatures above 1200 °C had broad peaks at around 30° in the XRD patterns. The glass transition temperatures (T_g) of the glass powders obtained by spray pyrolysis at preparation temperatures between 900 °C and 1400 °C were near 480 °C regardless of the preparation temperatures. The dielectric layers formed from the glass powders prepared by spray pyrolysis at preparation temperatures above 1300 °C had clean surface and dense inner structure at the firing temperature of 580 °C. The transmittance of the dielectric layer formed from the glass powders obtained by spray pyrolysis at preparation temperature of 1400 °C was 90% at the firing temperature of 580 °C, in which the thickness of the dielectric layer was 13 μm. The UV cutoff edges gradually shift towards longer wavelength with increasing the preparation temperature of glass powders and the firing temperature of dielectric layers.     

B NMR investigations in xV2O5–B2O3 and xV2O5–B2O3–PbO glasses

11B (I=3/2) MAS NMR in the binary glass system xV₂O₅–B₂O₃ (x=0.053, 0.43) and the ternary glass system xV₂O₅–B₂O₃–PbO (0.1x1.5) has been investigated at room temperature. In the xV₂O₅–B₂O₃ glasses, one NMR line due to BO₃ unit was observed. Meanwhile in the xV₂O₅–B₂O₃–PbO, two NMR lines which arise from BO₃ and BO₄ units were detected, where the appearance of BO₄ units is produced by the presence of PbO. From the computer-simulation of the ¹¹B NMR central transition line (m=−1/2↔1/2), the quadrupole parameters (e²qQ/h and η) for BO₃ units in xV₂O₅–B₂O₃, and those for BO₃ and BO₄ units in xV₂O₅–B₂O₃–PbO were obtained as a function of x. As the V₂O₅ content increases in xV₂O₅–B₂O₃–PbO, the e²qQ/h and η values of the BO₃⁻ associated resonance are found to slightly decrease and increase, respectively. Meanwhile, the e²qQ/h and η values of BO₄⁻ associated resonance in xV₂O₅–B₂O₃–PbO are found to slightly increase and decrease, respectively. By comparing the intensities of the total transitions (m=−3/2↔−1/2,m=−1/2↔1/2, and 1/2↔3/2) for the ¹¹B NMR line of BO₃ and BO₄ units contained in xV₂O₅–B₂O₃–PbO with those of respective standard samples of 0.053V₂O₅–B₂O₃ and NaBH₄, the quantitative fractions of BO₃ and BO₄ in xV₂O₅–B₂O₃–PbO were obtained as a function of x.     

Some characteristics of glass in the Al2O3---B2O3---SiO2 system from the gel

The colorless and transparent glasses in the Al₂O₃---B₂O₃---SiO₃ system with high B₂O₃ and SiO₂ content were prepared from gels at low temperature. Their IR spectra not only revealed the evolution of the gel to glass conversion, but also showed that the formation of mixed bonds in the glasses obtained did not show any effect due to the B₂O₃ content. The accuracy of the glass composition is dependent upon the SiO₂/B₂O₃ molar ratio. The higher the ratio, the less the deviation of the analyzed compositions of the resulting glasses from their original calculated values. It is obvious that the higher the ratio, the lower the thermal expansion coefficient and the higher the transformation temperature of the glass, and the temperature at which the thermal contraction reaches an equilibrium is higher.     

Glass formation, properties and structure of glasses in the P2O5---WO3---K2O---Al2O3 system

Glass formation in the P₂O₅---WO₃---K₂O---Al₂O₃ system was investigated and the glass-forming regions are presented.

the properties of the glasses in the P₂O₅---WO₃---K₂O---Al₂O₃ system (Al₂O₃ 8 mol.%) are reported.

The colouration of glass was studied. It was found that W⁵⁺ ions make glass blue.

Infrared spectra were measured by means of making KBr pills. Results of the investigation suggest that P---O---P, P---O---W, and W---O---W bonds form a continuous network in the phosphate glasses. So we suggest that tungsten trioxide is a glass former.     

Optical absorption and elastic properties of Li2O---(LiCl)2---B2O3---Al2O3 glasses

Ultraviolet transmission, densities, and supersonic velocities of the Li₂O---(LiCl)₂---B₂O₃---Al₂O₃ glasses were measured. Adiabatic compressibilities of all these glasses were calculated. The results were interpreted from the viewpoint of the glass structure.     

Effects of SiO2 overlayer at initial growth stage of epitaxial Y2O3 film growth

We investigated the dependence of the Y₂O₃ film growth on Si surface at initial growth stage. The reflection high-energy electron diffraction, X-ray scattering, and atomic force microscopy showed that the film crystallinity and morphology strongly depended on whether Si surface contained O or not. In particular, the films grown on oxidized surfaces revealed significant improvement in crystallinity and surface smoothness. A well-ordered atomic structure of Y₂O₃ film was formed on 1.5 nm thick SiO₂ layer with the surface and interfacial roughness markedly enhanced, compared with the film grown on the clean Si surfaces. The epitaxial film on the oxidized Si surface exhibited extremely small mosaic structures at interface, while the film on the clean Si surface displayed an island-like growth with large mosaic structures. The nucleation sites for Y₂O₃ were provided by the reaction between SiO₂ and Y at the initial growth stage. The SiO₂ layer known to hinder crystal growth is found to enhance the nucleation of Y₂O₃, and provides a stable buffer layer against the silicide formation. Thus, the formation of the initial SiO₂ layer is the key to the high-quality epitaxial growth of Y₂O₃ on Si.     

Study of electrical properties of MoO3–Fe2O3–P2O5 and SrO–Fe2O3–P2O5 glasses by impedance spectroscopy. II

The electrical and dielectric properties for three series of MoO₃–Fe₂O₃–P₂O₅ and one series of SrO–Fe₂O₃–P₂O₅ glasses were measured by impedance spectroscopy in the frequency range from 0.01 Hz to 3 MHz and over the temperature range from 303 to 473 K. It was shown in Part I that the MoO₃ is incorporated into phosphate network and the structure/properties are strongly influenced by the overall O/P ratio. The Fe₂O₃ content and Fe(II)/Fe_tot ratio in these glasses have significant effects on the electrical conductivity and dielectric permittivity. With decreasing Fe₂O₃ content in MoO₃–Fe₂O₃–P₂O₅ glasses with O/P at 3.5 the dc conductivity, σ_dc(ω) decreases for two orders of magnitude, which indicates that the conductivity for these glasses depends on Fe₂O₃ and is independent of the MoO₃ content. Also, the dielectric properties such as ^′(ω), ^″(ω) and σ_ac(ω) and their variation with frequency and temperature indicates a decrease in relaxation intensity with increase in the concentration of MoO₃. On the other hand, the dc conductivity for MoO₃–Fe₂O₃–P₂O₅ glasses with O/P > 3.5 increases with the substitution of MoO₃ which has been explained by an increase in the number of non-bridging oxygens and formation of Fe–O–P bonds that are responsible for formation of small polarons. The increase in the dielectric permittivity, ^′(ω) with increasing MoO₃ content is attributed to the increase in the deformation of glass network with increasing bonding defects. For SrO–Fe₂O₃–P₂O₅ glasses the conductivity and dielectric permittivity remained constant with increasing SrO.     

Raman spectrum studies of the glasses in the system Na2O---Al2O3---P2O5

Raman spectra of ternary sodium aluminosphosphate glasses indicate that for glasses with Al₂O₃/P₂O₅<0.63, the glass network is mainly built up of (PO₃)_n^n- chains and rings or different kinds of phosphate groups and AlO₄ tetrahedra; for glasses with Al₂O₃/P₂O₅>0.63, the glass network is mainly built up of AlPO₄ groups.     

Glass formation and crystallization in the ZrO2---Al2O3---P2O5 system

The glass formation of the ZrO₂---Al₂O₃---P₂O₅ system in the high phosphate region is determined. The crystallization process and the crystal types formed during heat treatment have been studied. The structure of these glasses is discussed.     

Characterisation of semiconducting V2O5–Bi2O3–TeO2 glasses through ultrasonic measurements

Tellurite containing vanadate (50−x)V₂O₅–xBi₂O₃–50TeO₂ glasses with different bismuth (x=0, 5, 10, 15, 20 and 25 wt%) contents have been prepared by rapid quenching method. Ultrasonic velocities (both longitudinal and shear) and attenuation (for longitudinal waves only) measurements have been made using a transducer operated at the fundamental frequency of 5 MHz in the temperature range from 150 to 480 K. The elastic moduli, Debye temperature, and Poisson’s ratio have been obtained both as a function of temperature and Bi₂O₃ content. The room temperature study on ultrasonic velocities, attenuation, elastic moduli, Poisson’s ratio, Debye temperature and glass transition temperature show the absence of any anomalies with addition of Bi₂O₃ content. The observed results confirm that the addition of Bi₂O₃ modifier changes the rigid formula character of TeO₂ to a matrix of regular TeO₃ and ionic behaviour bonds (NBOs). A monotonic decrease in velocities and elastic moduli, and an increase in attenuation and acoustic loss as a function of temperature in all the glass samples reveal the loose packing structure, which is attributed to the instability of TeO₄ trigonal bipyramid units in the network as temperature increases. It is also inferred that the glasses with low Bi₂O₃ content are more stable than with high Bi₂O₃ content.     

An X-ray diffraction study of the structure of B2O3---Cs2O liquids

The short range structures of B₂O₃ (90 mol%)---Cs₂O (10 mol%) and B₂O₃ (80 mol%)---Cs₂O (20 mol%) liquids were analyzed at 973 and 1053 K, respectively, by an X-ray diffraction method, and the effects of Cs₂O addition on the boron-oxygen bonding were investigated. The existence of BO₃ triangles, which form the so-called boroxol ring structure, was confirmed in B₂O₃---Cs₂O liquids, as well as in B₂O₃ liquid, but some fraction of the BO₃ triangles was thought to be converted to BO₄ tetrahedra. Similar results have previously been observed also in B₂O₃---Cs₂O glasses. A Cs atom was found to be surrounded by six O atoms; four Cs---O interatomic distances were about 3.2 Å but the other two were at 3.8–3.9 Å. These distances indicate that distorted Cs---O octahedra may exist in these B₂O₃---Cs₂O liquids.     

Effect of Al2O3 on phase separation and crystallization in ZnO---Al2O3---B2O3---SiO2 glasses

The effect of alumina on the phase separation and the crystallization of the glasses of composition (mol%) 18ZnO·30B₂O₃·52SiO₂ and O-40 Al₂O₃ was studied using an electron microscope and IR spectroscopy. The main crystalline phase appears in the microphase for which the compositions are not nearer to the crystal stoichiometry than the mean. The addition of Al₂O₃ suppresses the immiscibility but enhances the crystallizability.     

Gel synthesis of glass powders in the BaO---Al2O3---SiO2 system

Homogeneous glass powders were prepared from multicomponent silicate gels in the BaO---Al₂O₃---SiO₂ system. Gels synthesized from TEOS, Al-sec-butoxide, and Ba-acetate were characterized by TGA, DSC, and single-point BET analysis. Amorphous oxide powders of controlled composition were obtained through an appropriate drying and heat treatment schedule. Inclusion-free clear oxynitride glasses were also prepared by co-melting gel synthesized oxide powders with silicon nitride powders.     

Solvothermal synthesis of K2V3O8 nanorods

A solvothermal route has been developed to synthesize K₂V₃O₈ nanorods via the reduction of V₂O₅ using ethanol as the reducing agent as well as the solvent at 200°C. X-ray diffraction and selected area electron diffraction analysis revealed that the as-synthesized products are of tetragonal structure K₂V₃O₈. Transmission electron spectroscopy image showed that the obtained K₂V₃O₈ comprises rod-like nanocrystallites. The formation mechanism of K₂V₃O₈ was studied.     

Crystal growth of NdAl3(BO3)4 from K2O/MoO3/Nd2O3/B2O3/KF flux

NdAl₃(BO₃)₄ single crystals were grown by the flux method and the TSSG technique using a K₂O/3MoO₃/B₂O₃/0.5Nd₂O₃/KF flux system. Light-violet clear crystals could be obtained. The effects of fluoride on the growth of NAB crystals were investigated. As the content of KF was gradually increased, the growth form of NAB was changed from the equant to the columnar and the primary crystalline region of NAB was shrinked. At the ratio of KF/K₂O = 0.75, NAB crystals could not be grown.     

Viscosity and IR investigations in the Li2O---B2O3 system

The high viscosity in melts of the Li₂O---B₂O₃ system makes it very difficult to grow large crystals of lithium triborate. The viscosity and IR characteristics of molten li₂O---B₂O₃ system are reported in this paper. When the temperature increases the viscosity of li₂O---B₂O₃ system decreases and follows an Arrhenius-type relationship. With an increasing 13203 ratio in Li₂O---B₂O₃ melts, the viscosity rises gradually to a maximum with a composition Li₂O: 3.513203 then it falls rapidly. In order to find active agents to reduce the viscosity, Na₂O, NaCl, LiF, P205, M003, W03 etc oxides were added to Li₂O---B₂O₃ samples respectively and investigated using the orthogonal method. The experimental results show that the addition of acidic oxides can significantly decrease the viscosity in the Li₂O---B₂O₃ system. For Li₂O: 4.513203, an ideal additive agent is 20wt% Li₂O:: 2MoO₃. Near the composition for crystal growth, the percentage reduction of viscosity is 62.2%. The IR spectra of Li₂O---B₂O₃ system revealed that the BO₄⁻/NO₃⁻ ratio is reduced in the melt using Li₂O: 2MoO₃ as an additive. It is proposed that the M003 reduced the concentration of bridging oxygen atoms of BO₄⁻. The change of structure explains the decline in the viscosity. In the crystal structures of lithium triborate, the matrix spaces are so small that larger other cations than Li+ are very difficult to enter the crystal matrix. So the use of additive agents to reduce the viscosity is a possible method if no new phase appears.     

Local structure of liquids Al2O3 and GeO2 under densification

Molecular dynamic simulation has been conducted to study the local structure of liquid Al₂O₃ and GeO₂ under densification. Those liquids are found to be a mixture of species of TO_x. Here T is Ge or Al and x = 4, 5 and 6. This result is supported by the fact that the density, fraction of oxygen connectivity and volume of different void kinds are a linear function of TO_x fraction. The microscopic mechanism of liquid densification is quantified and interpreted in term of the change in TO_x fraction.     

A study of alkali resistance of CaO---Al2O3---SiO2 glasses

The alkali resistance and structure of CaO---Al₂O₃---SiO₂ glasses are studied in this paper. The change of coordination number of aluminum ions in the glasses, caused by corrosion from the cement extract aqueous solution, was determined by means of X-ray fluorescence spectra and infrared absorption spectra. The interrelationship between glass compositions, structure, and alkali resistance is discussed.