Carbon ceramic electrodes modified with mixed oxides SiO<Subscript>2</Subscript>/SnO<Subscript>2</Subscript> for determination of levofloxacin

The preparation of a carbon ceramic electrode modified with SnO₂ (CCE/SnO₂) using tin dibutyl diacetate as precursor was optimized by a 2³ factorial design. The factors analyzed were catalyst (HCl), graphite/organic precursor ratio, and inorganic precursor (dibutyltin diacetate). The statistical treatment of the data showed that only the second-order interaction effect, catalyst × inorganic precursor, was significant at 95% confidence level, for the electrochemical response of the system. The obtained material was characterized by scanning electron microscopy (MEV), X-ray diffraction (XRD), RAMAN spectroscopy, XPS spectra, and voltammetric techniques. From the XPS spectra, it was confirmed the formation of the Si–O–Sn bond by the shift in the binding energy values referred to Sn 3d3/2 due to the interaction of Sn with SiOH species. The incorporation of SnO₂ provided an increment of the electrode response for levofloxacin, with Ipa = 147.0 μA for the ECC and Ipa = 228.8 μA for ECC/SnO₂, indicating that SnO₂ when incorporated into the silica network enhances the electron transfer process. Under the optimized working conditions, the peak current increased linearly with the levofloxacin concentration in the range from 6.21×10^?5 to 6.97×10^?4 mol L^?1 with quantification and detection limits of 3.80×10^?5 mol L^?1 (14.07 mg L^?1) and 1.13×10^?5 mol L^?1 (4.18 mg L^?1), respectively.     

Synthesis,structural characterization and DNA-binding studies of a new cobalt (II) complex: (HAcr)<Subscript>4</Subscript>[Co(Sal)<Subscript>3</Subscript>]

A new cobalt (II) coordination compound was synthesized using proton transfer mechanism. The reaction between CoCl₂·2H₂O, Salicylic acid (H₂Sal) and acridine (Acr) gave a new coordination compound formulated as (HAcr)₄[Co(Sal)₃], which was characterized by elemental analysis, NMR, IR and UV/Vis spectroscopies. The interaction of this complex with DNA has been investigated in vitro using UV absorption, fluorescence spectroscopy, viscosity measurements and gel electrophoresis methods. The intrinsic binding constant has been estimated to be 5.8 × 10⁵ M^?1 using UV absorption. The interaction of DNA–Co (II) complex caused quenching in fluorescence. The binding constant, the number of binding site and Stern–Volmer quenching constant have been calculated to be 7.7 × 10⁴ M^?1, 1.143 and 1.5 × 10⁴ Lmol^?1, respectively. The increase in the viscosity of DNA with increasing the concentration of the Co (II) complex and the observations of other experiments suggest that the cobalt (II) complex binds to DNA by partial intercalation binding mode. Furthermore, the interaction of DNA–Co (II) complex was confirmed using gel electrophoresis studies. Moreover, molecular docking technique predicted partial intercalation binding mode for the complex.     

Nanofibers of V<Subscript>2</Subscript>O<Subscript>5</Subscript>/C@MWCNTs as the cathode material for lithium-ion batteries

Vanadium pentoxide (V₂O₅) nanofibers (NFs) with a thin carbon layer of 3–5 nm, which wrapped on V₂O₅ nanoparticles, and integrated multiwalled carbon nanotubes (MWCNTs) have been fabricated via simple electrospinning followed by carbonization process and post-sintering treatment. The obtained composite displays a NF structure with V₂O₅ nanoparticles connected to each other, and good electrochemical performance: delivering initial capacity of 320 mAh g^?1 (between 2.0 and 4.0 V vs. Li/Li⁺), good cycling stability (223 mAh g^?1 after 50 cycles), and good rate performance (~?150 mAh g^?1 at 2 A g^?1). This can attribute to the carbon wrapped on the V₂O₅ nanoparticles which can not only enhance the electric conductivity to decrease the impendence of the cathode materials but also maintain the structural stability to protect the nanostructure from the corruption of electrolyte and the strain stress due to the Li-ion intercalation/deintercalation during the charge/discharge process. And, the added MWCNTs play the role of framework of the unique V₂O₅ coated by carbon layer and composited with MWCNT NFs (V₂O₅/C@MWCNT NFs) to ensure the material is more stable.     

Correlation between the structural,electrical and electrochemical performance of layered Li(Ni<Subscript>0.33</Subscript>Co<Subscript>0.33</Subscript>Mn<Subscript>0.33</Subscript>)O<Subscript>2</Subscript> for lithium ion battery

The Li(Ni_0.33Co_0.33Mn_0.33)O₂ (LNCMO) cathode material is prepared by poly(vinyl pyrrolidone) (PVP)-assisted sol-gel/hydrothermal and poly(ethylene glycol)-block-poly(propylene glycol)-block-poly (ethylene glycol) (Pluronic-P123)-assisted hydrothermal methods. The compound prepared by PVP-assisted hydrothermal method shows a comparatively higher electrical conductivity of ~2?×?10^?5 S cm^?1 and exhibits a discharge capacity of 152 mAh g^?1 in the voltage range of 2.5 to 4.4 V, for a C-rate of 0.2 C, whereas the compounds prepared by P123-assisted hydrothermal method and PVP-assisted sol-gel method show a total electrical conductivity in the order of 10^?6 S cm^?1 and result in poor electrochemical performance. The structural and electrical properties of LNCMO (active material) and its electrochemical performance are correlated. The difference in percentage of ionic and electronic conductivity contribution to the total electrical conductivity is compared by transference number studies. The cation disorder is found to be the limiting factor for the lithium ion diffusion as determined from ionic conductivity values.     

Fabrication of a New Self-assembly Compound of CsTi<Subscript>2</Subscript>NbO<Subscript>7</Subscript> with Cationic Cobalt Porphyrin Utilized as an Ascorbic Acid Sensor

A novel sandwich-structured nanocomposite based on Ti₂NbO₇^? nanosheets and cobalt porphyrin (CoTMPyP) was fabricated through electrostatic interaction, in which CoTMPyP has been successfully inserted into the lamellar spacing of layered titanoniobate. The resultant Ti₂NbO₇/CoTMPyP nanocomposite was characterized by XRD, SEM, TEM, EDS, FT-IR, and UV-vis. It is demonstrated that the intercalated CoTMPyP molecules were found to be tilted approximately 63° against Ti₂NbO₇^? layers. The glass carbon electrode (GCE) modified by Ti₂NbO₇/CoTMPyP film showed a fine diffusion-controlled electrochemical redox process. Furthermore, the Ti₂NbO₇/CoTMPyP-modified electrode exhibited excellent electrocatalytic oxidation activity of ascorbic acid (AA). Differential pulse voltammetric studies demonstrated that the intercalated nanocomposite detects AA linearly over a concentration range of 4.99?×?10^?5 to 9.95?×?10^?4 mol L^?1 with a detection limit of 3.1?×?10^?5 mol L^?1 at a signal-to-noise ratio of 3.0.     

Synthesis and charge-discharge performance of Li<Subscript>5</Subscript>SiN<Subscript>3</Subscript> as a cathode material of lithium secondary batteries

Li₅SiN₃ crystals are synthesized by direct reaction between Li₃N and Si₃N₄ with the molar ratio Li₃N/Si₃N₄ of 10:1. Reaction is performed at 1073 K for 1 h under a nitrogen atmosphere of 700 Torr. The lattice constant determined by the X-ray powder diffraction method is 4.718 Å. Four broad Raman peaks are observed at 196, 286, 580, and 750 cm^?1. By analogy with LiMgN, the broad peak at 580 cm^?1 with a half width of 140 cm^?1 is attributed to homogenously random distribution of Li and Si atoms. The band gap of Li₅SiN₃ is found to be a direct gap of about 2.5 eV by optical absorption and photoacoustic spectroscopy methods. Comparison with the conventional cathode materials for lithium ion batteries, this gap value is close to d-d transition energy of Mn in LiMn₂O₄ (1.63 eV or 2.00 eV) and that of Co in LiCoO₂ (2.1 eV), suggesting that Li₅SiN₃ is a possible cathode material. The 5 × 5 mm²-sized lithium secondary battery of Li₅SiN₃ cathode/propylene carbonate + LiClO₄ electrolyte/Li anode structure shows a discharge capacity of 2.4 μAh cm^?2 for a discharge current of 1.0 μA.     

Layered LiNi<Subscript>0.80</Subscript>Co<Subscript>0.15</Subscript>Al<Subscript>0.05</Subscript>O<Subscript>2</Subscript> as cathode material for hybrid Li<Superscript>+</Superscript>/Na<Superscript>+</Superscript> batteries

LiNi_0.80Co_0.15Al_0.05O₂ (NCA) is explored to be applied in a hybrid Li⁺/Na⁺ battery for the first time. The cell is constructed with NCA as the positive electrode, sodium metal as the negative electrode, and 1 M NaClO₄ solution as the electrolyte. It is found that during electrochemical cycling both Na⁺ and Li⁺ ions are reversibly intercalated into/de-intercalated from NCA crystal lattice. The detailed electrochemical process is systematically investigated by inductively coupled plasma-optical emission spectrometry, ex situ X-ray diffraction, scanning electron microscopy, cyclic voltammetry, galvanostatic cycling, and electrochemical impedance spectroscopy. The NCA cathode can deliver initially a high capacity up to 174 mAh g^?1 and 95% coulombic efficiency under 0.1 C (1 C?=?120 mA g^?1) current rate between 1.5–4.1 V. It also shows excellent rate capability that reaches 92 mAh g^?1 at 10 C. Furthermore, this hybrid battery displays superior long-term cycle life with a capacity retention of 81% after 300 cycles in the voltage range from 2.0 to 4.0 V, offering a promising application in energy storage.     

LiMO<Subscript>2</Subscript>@Li<Subscript>2</Subscript>MnO<Subscript>3</Subscript> positive-electrode material for high energy density lithium ion batteries

Li[Ni_1/3Co_1/3Mn_1/3]O₂ (NCM 111) is a promising alternative to LiCoO₂, as it is less expensive, more structurally stable, and has better safety characteristics. However, its capacity of 155 mAh g^?1 is quite low, and cycling at potentials above 4.5 V leads to rapid capacity deterioration. Here, we report a successful synthesis of lithium-rich layered oxides (LLOs) with a core of LiMO₂ (R-3m, M?=?Ni, Co) and a shell of Li₂MnO₃ (C2/m) (the molar ratio of Ni, Co to Mn is the same as that in NCM 111). The core–shell structure of these LLOs was confirmed by XRD, TEM, and XPS. The Rietveld refinement data showed that these LLOs possess less Li⁺/Ni²⁺ cation disorder and stronger M*–O (M*?=?Mn, Co, Ni) bonds than NCM 111. The core–shell material Li_1.15Na_0.5(Ni_1/3Co_1/3)_core(Mn_1/3)_shellO₂ can be cycled to a high upper cutoff potential of 4.7 V, delivers a high discharge capacity of 218 mAh g^?1 at 20 mA g^?1, and retains 90 % of its discharge capacity at 100 mA g^?1 after 90 cycles; thus, the use of this material in lithium ion batteries could substantially increase their energy density.

Open image in new window

Graphical Abstract Average voltage vs. number of cycles for the core–shell and pristine materials at 20 mA g^?1 for 10 cycles followed by 90 cycles at 100 mA g^?1

     

Electrospun Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript>/Li<Subscript>2</Subscript>TiO<Subscript>3</Subscript> composite nanofibers for enhanced high-rate lithium ion batteries

Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers with the mean diameter of ca. 60 nm have been synthesized via facile electrospinning. When the molar ratio of Li to Ti is 4.8:5, the Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers exhibit initial discharge capacity of 216.07 mAh g^?1 at 0.1 C, rate capability of 151 mAh g^?1 after being cycled at 20 C, and cycling stability of 122.93 mAh g^?1 after 1000 cycles at 20 C. Compared with pure Li₄Ti₅O₁₂ nanofibers and Li₂TiO₃ nanofibers, Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers show better performance when used as anode materials for lithium ion batteries. The enhanced electrochemical performances are explained by the incorporation of appropriate Li₂TiO₃ which could strengthen the structure stability of the hosted materials and has fast Li⁺-conductor characteristics, and the nanostructure of nanofibers which could offer high specific area between the active materials and electrolyte and shorten diffusion paths for ionic transport and electronic conduction. Our new findings provide an effective synthetic way to produce high-performance Li₄Ti₅O₁₂ anodes for lithium rechargeable batteries.     

Synthesis and thermal decomposition of neodymium(III) peroxotitanate to Nd<Subscript>2</Subscript>TiO<Subscript>5</Subscript>

Neodymium(III) peroxotitanate is used as a precursor for obtaining Nd₂TiO₅. The last one possesses numerous valuable electrophysical properties. TiCl₄, Nd(NO₃)₃·6H₂O and H₂O₂ in mol ratio 1:2:10 were used as starting materials. The reaction ambience was alkalized to pH = 9 with a solution of NH₃. The obtained neodymium(III) peroxotitanate and intermediate compounds of the isothermal heating were proved by the help of quantitative analysis and infrared spectroscopy (IRS). It has Nd₄[Ti₂(O₂)₄(OH)₁₂]·7H₂O composition. The absorption band observed in IRS at 831 cm^?1 relates to a triangular bonding of the peroxo group of Ti, at 1062 cm^?1—terminal groups Ti–OH and at 1491 and 1384 cm^?1—the bridging OH^?-groups Ti–O(H)–Ti. Nd₂TiO₅ was obtained by thermal decomposition of neodymium(III) peroxotitanate. The isothermal conditions for decomposition were determined on the base of differential thermal analysis, thermogravimetric and differential scanning calorimetry results in the temperature range of 20–1000 °C. The mechanism of thermal decomposition of Nd₄[Ti₂(O₂)₄(OH)₁₂]·7H₂O to Nd₂TiO₅ was studied. In the temperature range of 20–208 °C, a simultaneous decomposition of the peroxo groups by the separation of oxygen and hydrate water is conducted and Nd₄[Ti₂O₄(OH)₁₂] is obtained. From 208 to 390 °C, the terminal OH^?-groups are separated and Nd₄[Ti₂O₇(OH)₆] is formed. In the range of 390–824 °C, the bridging OH^?-groups are completely decomposed to Nd₂TiO₅. The optimal conditions for obtaining nanocrystalline Nd₂TiO₅ are 900 °C for 6 h and 20–80 nm.     

Functionalized MgO,CeO<Subscript>2</Subscript> and ZnO nanoparticles with humic acid for the study of nitrate adsorption efficiency from water

In this study, the removal of nitrate using ZnO, MgO, and CeO₂ nanoparticles (NPs) modified by humic acid from water was tested. Nanoparticles were modified by humic acid using the microwave-assisted technique and then modified ZnO (Zn–H), modified MgO (Mg–H), and modified CeO₂ (Ce–H) were characterized through SEM, EDX, FTIR, and XRD analysis. Several important parameters influencing the removal of nitrate such as contact time, pH, adsorbent dosage and temperature were explored systematically by batch experiments. Isotherm studies were set up with the following optimum conditions: pH?=?5, adsorbent concentration of 1 g L^?1, 180 min and 25 °C. The results revealed that the adsorption were best fitted to pseudo-second order and simple Elovich kinetics models. Langmuir, Freundlich and linear adsorption models were fitted to describe adsorption isotherms and constants. The isotherm analysis indicated that the adsorption data can be represented by both Freundlich and linear isotherm models. The maximum adsorption capacity (q_m) was obtained at 55.1, 74.2 and 75.8 mg g^?1 for Zn–H, Ce–H, and Mg–H, respectively. The thermodynamic parameters such as free energy, enthalpy and entropy of adsorption were obtained. From the thermodynamic parameters, it is suggested that the adsorption of nitrate on modified NPs (MNPs) followed the exothermic and spontaneous processes. The obtained results showed that the MNPs were efficient adsorbents for removing nitrate from aqueous media.     

Synthesis and characterization of a new monophosphate (C<Subscript>6</Subscript>H<Subscript>16</Subscript>N<Subscript>2</Subscript>)(H<Subscript>2</Subscript>PO<Subscript>4</Subscript>)<Subscript>2</Subscript>

Chemical preparation, crystal structure, and NMR spectroscopy of a new trans-2,5-dimethylpiperazinium monophosphate are given. This new compound crystallizes in the triclinic system, with the space group P-1 and the following parameters: a = 6.5033(3), b = 7.6942(4), c = 8.1473(5) Å, α = 114.997(3), β = 92.341(3), γ = 113.136(3), V = 329.14(3) ų, Z = 1, and D_x = 1.565 g cm^?3. The crystal structure has been determined and refined to R = 0.030 and R _w(F ²) = 0.032 using 1558 independent reflections. The structure can be described as infinite [H₂PO₄] _n ^n? chains with (C₆H₁₆N₂)²⁺ organic cations anchored between adjacent polyanions to form columns of anions and cations running along the b axis. This compound has also been investigated by IR, thermal, and solid-state, ¹³C and ³¹P MAS NMR spectroscopies and Ab initio calculations.     

Simultaneous determination of trimethylamine,formaldehyde and benzene via the cataluminescence of In<Subscript>3</Subscript>LaTi<Subscript>2</Subscript>O<Subscript>10</Subscript> nanoparticles

The authors describe a cataluminescence (CTL) based sensing method via signals generated at the surface of In₃LaTi₂O₁₀ nanoparticles for simultaneous determination of trimethylamine, formaldehyde and benzene in air. The analytical wavelengths are 340 nm, 440 nm and 600 nm, and the best surface temperature of the catalytic material is 275 °C. The limits of detection of this method are 0.3 mg?m^?3 for trimethylamine, 0.07 mg?m^?3 for formaldehyde, and 0.2 mg?m^?3 for benzene. The linear ranges of CTL intensity versus gas/vapor concentration are from 1.0 to 65.1 mg?m^?3 for trimethylamine, from 0.2 to 72.5 mg?m^?3 for formaldehyde, and from 0.5 to 77.5 mg?m^?3 for benzene. The recoveries after testing 10 standard samples ranged from 98.1% to 102.6% for trimethylamine, from 98.1% to 102.6% for formaldehyde, and from 97.7% to 103.8% for benzene. Gaseous ammonia, acetaldehyde, toluene, ethylbenzene, ethanol, sulfur dioxide and carbon dioxide do not interfere. The relative deviation of the CTL signals after 200 h of continuous detection of trimethylamine, formaldehyde and benzene is <3%.

Open image in new window

Graphical abstract Schematic of a cataluminescence (CTL) based method for simultaneous determination of trimethylamine (TMA), formaldehyde (HCHO) and benzene (C₆H₆) in air. The linear ranges of CTL intensity versus gas/vapor concentration are from 1.0 to 65.1 mg?m^?3 for TMA, from 0.2 to 72.5 mg?m^?3 for HCHO, and from 0.5 to 77.5 mg?m^?3 for C₆H₆.

     

Preparation and characterization of H<Subscript>3</Subscript>PW<Subscript>12</Subscript>O<Subscript>40</Subscript>/ZrO<Subscript>2</Subscript> catalyst for carbonation of methanol into dimethyl carbonate

A H₃PW₁₂O₄₀/ZrO₂ catalyst for effective dimethyl carbonate (DMC) formation via methanol carbonation was prepared using the sol–gel method. X-ray photoelectron spectra showed that reactive and dominant (63%) W(VI) species, in WO₃ or H₂WO₄, enhanced the catalytic performances of the supported ZrO₂. The mesoporous structure of H₃PW₁₂O₄₀/ZrO₂ was identified by nitrogen adsorption–desorption isotherms. In particular, partial sintering of catalyst particles in the duration of methanol carbonation caused a decrease in the Brunauer–Emmett–Teller surface area of the catalyst from 39 to 19 m²/g. The strong acidity of H₃PW₁₂O₄₀/ZrO₂ was confirmed by the desorption peak observed at 415 °C in NH₃ temperature-programmed desorption curve. At various reaction temperatures (T?=?110, 170, and 220 °C) and CO₂/N₂ volumetric flow rate ratios (CO₂/N₂?=?1/4, 1/7, and 1/9), the calculated catalytic performances showed that the optimal methanol conversion, DMC selectivity, and DMC yield were 4.45, 89.93, and 4.00%, respectively, when T?=?170 °C and CO₂/N₂?=?1/7. Furthermore, linear regression of the pseudo-first-order model and Arrhenius equation deduced the optimal rate constant (4.24?×?10^?3 min^?1) and activation energy (E_a?=?15.54 kJ/mol) at 170 °C with CO₂/N₂?=?1/7 which were favorable for DMC formation.     

Preparation and methane adsorption of two-dimensional carbide Ti<Subscript>2</Subscript>C

Here a novel material for methane adsorption was synthesized and studied, which is a graphene-like two-dimensional (2D) carbide (Ti₂C, a member of MXenes), formed by exfoliating Ti₂AlC powders in a solution of lithium fluoride (LiF) and hydrochloric acid (HCl) at 40 °C for 48 h. Based on first-principles calculation, theoretically perfect Ti₂C with O termination has a specific surface area (SSA) of 671 m² g^?1 and methane storage capacity is 22.9 wt%. Experimentally, 2.85 % exfoliated Ti₂C with mesopores shown methane capacity of 11.58 cm³ (STP: 0 °C, 1 bar) g^?1 (0.82 wt%) under 5 MPa and the SSA was 19.1 m² g^?1. For Ti₂C sample intercalated with NH₃·H₂O, the adsorbed amount was increased to 16.81 cm³ (STP) g^?1 at same temperature. At the temperature of 323 K, the adsorbed amount of as-prepared Ti₂C was increased to 52.76 cm³ (STP) g^?1. For fully exfoliated Ti₂C, the methane capacity was supposed to be 28.8 wt% or 1148 V (STP)v^?1. Ti₂C theoretically has much larger volume methane capacity than current methane storage materials, though its SSA is not very high.     

A high mass loading electrode based on ultrathin Co<Subscript>3</Subscript>S<Subscript>4</Subscript> nanosheets for high performance supercapacitor

There is a growing need for the electrode with high mass loading of active materials, where both high energy and high power densities are required, in current and near-future applications of supercapacitor. Here, an ultrathin Co₃S₄ nanosheet decorated electrode (denoted as Co₃S₄/NF) with mass loading of 6 mg cm^?2 is successfully fabricated by using highly dispersive Co₃O₄ nanowires on Ni foam (NF) as template. The nanosheets contained lots of about 3～5 nm micropores benefiting for the electrochemical reaction and assembled into a three-dimensional, honeycomb-like network with 0.5～1 μm mesopore structure for promoting specific surface area of electrode. The improved electrochemical performance was achieved, including an excellent cycliability of 10,000 cycles at 10 A g^?1 and large specific capacitances of 2415 and 1152 F g^?1 at 1 and 20 A g^?1, respectively. Impressively, the asymmetric supercapacitor assembled with the activated carbon (AC) and Co₃S₄/NF electrode exhibits a high energy density of 79 Wh kg^?1 at a power density of 151 W kg^?1, a high power density of 3000 W kg^?1 at energy density of 30 Wh kg^?1 and 73 % retention of the initial capacitance after 10,000 charge-discharge cycles at 2 A g^?1. More importantly, the formation process of the ultrathin Co₃S₄ nanosheets upon reaction time is investigated, which is benefited from the gradual infiltration of sulfide ions and the template function of ultrafine Co₃O₄ nanowires in the anion-exchange reaction.

Open image in new window

Graphical abstract The ultrathin 2D Co₃S₄ nanosheets fabricated on 3D Ni foam and the formation process of the ultrathin Co₃S₄ nanosheets upon reaction times has been investigated. At the same time, the Co₃S₄/NF electrode displays an outstanding specific capacitance of 2420 F g^?1 at 1 A g^?1 with high mass loading of 6 mg cm^?2.

     

Carbon paste electrode modified with Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles and BMI.PF<Subscript>6</Subscript> ionic liquid for determination of estrone by square-wave voltammetry

A carbon paste electrode (CPE) modified with Fe₃O₄ nanoparticles (Fe₃O₄ NP) and the ionic liquid 1-butyl-3-methylimidazolium hexafluorophosphate (IL BMI.PF₆) was employed for the electroanalytical determination of estrone (E1) by square-wave voltammetry (SWV). At the modified electrode, cyclic voltammograms of E1 in B–R buffer (pH 12.0) showed an adsorption-controlled irreversible oxidation peak at around +0.365 V. The anodic current increased by a factor of five times and the peak potential shifted 65 mV to less positive values compared with the unmodified CPE. Under optimized conditions, the calibration curve obtained showed two linear ranges: from 4.0 to 9.0 μmol L^?1 and from 9.0 to 100.0 μmol L^?1. The limits of detection (LOD) and quantification (LOQ) attained were 0.47 and 4.0 μmol L^?1, respectively. The proposed modified electrode was applied to the determination of E1 in pork meat samples. Data provided by the proposed modified electrode were compared with data obtained by UV–vis spectroscopy. The outstanding performance of the electrochemical device indicates that Fe₃O₄ NP and the IL BMI.PF₆ are promising materials for the preparation of chemically modified electrodes for the determination of E1.     

Enhanced electrochemical properties of Li<Subscript>2</Subscript>ZnTi<Subscript>3</Subscript>O<Subscript>8</Subscript>/C nanocomposite synthesized with phenolic resin as carbon source

Li₂ZnTi₃O₈/C nanocomposite has been synthesized using phenolic resin as carbon source in this work. The structure, morphology, and electrochemical properties of the as-prepared Li₂ZnTi₃O₈ samples were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM), Raman spectroscopy (RS), galvanostatic charge–discharge, and AC impedance spectroscopy. SEM images show that Li₂ZnTi₃O₈/C was agglomerated with a primary particle size of ca. 40 nm. TEM images reveal that a homogeneous carbon layer (ca. 5 nm) formed on the surface of Li₂ZnTi₃O₈ particles which is favorable to improve the electronic conductivity and inhibit the growth of Li₂ZnTi₃O₈ during annealing process. The as-prepared Li₂ZnTi₃O₈/C composite with 6.0 wt.% carbon exhibited a high initial discharge capacity of 425 and 159 mAh g^?1 at 0.05 and 5 A g^?1, respectively. At a high current density of 1 A g^?1, 95.5 % of its initial value is obtained after 100 cycles.     

Natural graphite enhanced the electrochemical performance of Li<Subscript>3</Subscript>V<Subscript>2</Subscript>(PO<Subscript>4</Subscript>)<Subscript>3</Subscript> cathode material for lithium ion batteries

Natural graphite treated by mechanical activation can be directly applied to the preparation of Li₃V₂(PO₄)₃. The carbon-coated Li₃V₂(PO₄)₃ with monoclinic structure was successfully synthesized by using natural graphite as carbon source and reducing agent. The amount of activated graphite is optimized by X-ray diffraction, scanning electron microscope, transmission electron microscope, Raman spectrum, galvanostatic charge/discharge measurements, cyclic voltammetry, and electrochemical impedance spectroscopy tests. Our results show that Li₃V₂(PO₄)₃ (LVP)-10G exhibits the highest initial discharge capacity of 189 mAh g^?1 at 0.1 C and 162.9 mAh g^?1 at 1 C in the voltage range of 3.0–4.8 V. Therefore, natural graphite is a promising carbon source for LVP cathode material in lithium ion batteries.     

On-line packed magnetic in-tube solid phase microextraction of acidic drugs such as naproxen and indomethacin by using Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>@SiO<Subscript>2</Subscript>@layered double hydroxide nanoparticles with high anion exchange capacity

The authors describe a 3-component nanoparticle system composed of a silica-coated magnetite (Fe₃O₄) core and a layered double (Cu-Cr) hydroxide nanoplatelet shell. The sorbent has a high anion exchange capacity for extraction anionic species. A simple online system, referred to as "on-line packed magnetic-in-tube solid phase microextraction" was designed. The nanoparticles were placed in a stainless steel cartridge via dry packing. The cartridge was then applied to the preconcentration acidic drugs including naproxen and indomethacin from urine and plasma. Extraction and desorption times, pH values of the sample solution and flow rates of sample solution and eluent were optimized. Analytes were then quantified by HPLC with UV detection. Under optimal conditions, the limits of detection range from 70 to 800 ng L^?1, with linear responses from 0.1–500 μg L^?1 (water samples), 0.6–500 μg L^?1 (spiked urine), and 0.9–500 μg L^?1 (spiked plasma). The inter- and intra-assay precisions (RSDs, for n?=?5) are in the range of 2.2–5.4%, 2.8–4.9%, and 2.0–5.2% at concentration levels of 5, 25 and 50 μg L^?1, respectively. The method was applied to the analysis of the drugs in spiked human urine and plasma, and good results were achieved.

Open image in new window

Graphical abstract Fe₃O₄@SiO₂@CuCr-LDH magnetic nanoparticles were synthesized and packed in to a stainless steel column. The column was applied to solid phase microextraction of acidic drugs from biological samples.