Germanium and iron co-substituted SrCoO2.5+δ as oxygen permeable membrane

Germanium and iron co-doped SrCoO_2.5+δ was investigated in terms of phase stability, oxygen permeability and electrical conductivity. The favorable high-temperature cubic structure of SrCoO_2.5+δ was stabilized to lower temperatures by co-doping Ge (10 mol%) and Fe (10 mol%) that substituted for Co, which however could not be achieved by doping Ge (20 mol%) alone. In contrast to SrCo_0.8Ge_0.2O_2.5+δ sample which showed a sharp decrease in oxygen permeability at temperature of 875 °C upon cooling, SrGe_0.1Co_0.8Fe_0.1O_3−δ sample remained well-permeable to oxygen at lower temperatures down to at least 820 °C; an abrupt change in electrical conductivity in SrCo_0.8Ge_0.2O_2.5+δ also occurred accompanying the phase transition. The oxygen permeation flux for SrGe_0.1Co_0.8Fe_0.1O_3−δ increased significantly with the decrease of the membrane thickness, indicating the transport of oxygen ions in the bulk of the membrane as the rate-limiting step.     

Transport properties of SrCe0.95Y0.05O3−δ and its application for hydrogen separation

Transport properties of SrCe_0.95Y_0.05O_3−δ were studied by impedance spectroscopy and by measuring open-cell voltage (OCV) and gas permeation. Ionic transference numbers were determined by measuring the OCV of concentration cells and water vapor evolution of an O₂/H₂ fuel cell. We observed interfacial polarization on the basis of the I–V curves obtained by discharging a hydrogen concentration cell or an O₂/H₂ fuel cell. The observed high protonic conductivity (high proton and low oxide ion transference numbers) makes SrCe_0.95Y_0.05O_3−δ a potential material for hydrogen separation. From proton conductivity measurements, under a given hydrogen partial pressure difference of 4%/0.488%, the hydrogen permeation rate (of a dense membrane with 0.11 cm in thickness) was calculated to be ≈0.072 cm³ (STP) cm⁻² min⁻¹ at 800°C, whereas the permeation rate calculated from short-circuit current measurements was ≈0.023 cm³ (STP) cm⁻² min⁻¹ at 800°C. The difference between calculated and observed permeation rates is probably due to interfacial polarization.     

Perovskite-like system (Sr,La)(Fe,Ga)O3−δ: structure and ionic transport under oxidizing conditions

The maximum solid solubility of gallium in the perovskite-type La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.40–0.80; y=0–0.60) was found to vary in the approximate range y=0.25–0.45, decreasing when x increases. Crystal lattice of the perovskite phases, formed in atmospheric air, was studied by X-ray diffraction (XRD) and neutron diffraction and identified as cubic. Doping with Ga results in increasing unit cell volume, while the thermal expansion and total conductivity of (La,Sr)(Fe,Ga)O_3−δ in air decrease with gallium additions. The average thermal expansion coefficients (TECs) are in the range (11.7–16.0)×10⁻⁶ K⁻¹ at 300–800 K and (19.3–26.7)×10⁻⁶ K⁻¹ at 800–1100 K. At oxygen partial pressures close to atmospheric air, the oxygen permeation fluxes through La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.7–0.8; y=0.2–0.4) membranes are determined by the bulk ambipolar conductivity; the limiting effect of the oxygen surface exchange was found negligible. Decreasing strontium and gallium concentrations leads to a greater role of the exchange processes. As for many other perovskite systems, the oxygen ionic conductivity of La_1−xSr_xFe_1−yGa_yO_3−δ increases with strontium content up to x=0.70 and decreases on further doping, probably due to association of oxygen vacancies. Incorporation of moderate amounts of gallium into the B sublattice results in increasing structural disorder, higher ionic conductivity at temperatures below 1170 K, and lower activation energy for the ionic transport.     

Deuterium conductivity, diffusion and implantation in Sr-doped LaYO3

A study of deuterium conductivity and diffusion in the oxide perovskite La_0.9Sr_0.1YO_3−δ is presented in this work. Deuterium ions were implanted into La_0.9Sr_0.1YO_3−δ (50 keV, 1×10¹⁶ atoms/cm²) and the corresponding deuterium depth profile was determined by SIMS and compared with a Monte Carlo simulation (TRIM96). This implant was used as a standard for the determination of deuterium concentration in a La_0.9Sr_0.1YO_3−δ sample pre-treated in D₂O atmosphere. In this way, it was fully confirmed that La_0.9Sr_0.1YO_3−δ incorporates water at high temperatures. The conductivity of La_0.9Sr_0.1YO_3−δ was measured in D₂O atmosphere and compared with other proton (deuteron) conductors. Concentration and conductivity data were used in conjunction to estimate the deuterium diffusivity and the constant of reaction of (heavy) water incorporation into LaYO₃. Some comments on the catalytic activity of this oxide are made.     

Effects of cation- or oxide ion-defect on conductivities of apatite-type La–Ge–O system ceramics

A series of apatite-type La–Ge–O ceramics were prepared and their cation-defect at the 4f+6h sites and oxide ion-defect at 2a site were investigated. In La_xGe₆O_12+1.5x ceramics of x=6–12, the higher conductivities were obtained in the region of apatite composition, La_x(GeO₄)₆O_1.5x−12 (x=8–9.33), and the highest conductivity was achieved for La₉(GeO₄)₆O_1.5 (x=9), where the number of cation (La³⁺) occupying the 4f+6h sites is 9 and the number of oxide ion occupying the 2a site is 1.5. The ceramics with cation- and oxide ion-defects were La_9−0.66xSr_x(GeO₄)₆O_1.5 (x=0–1), La_9−1.33xZr_x(GeO₄)₆O_1.5 (x=0–1), La_9−xSr_x(GeO₄)₆O_1.5−0.5x (x=0–3), La_9−xZr_x(GeO₄)₆O_1.5+0.5x (x=0–1), La_x(GeO₄)_3x−21(AsO₄)_27−3xO_1.5 (x=0–3), La_x(GeO₄)_33−3x(AlO₄)_3x−27O_1.5 (x=0–3), La₉(GeO₄)_6−x (AlO₄)_xO_1.5−0.5x (x=0–3), La₉(GeO₄)_6−x(AsO₄)_xO_1.5+0.5x (x=0–1), La_9.33−xSr_x(GeO₄)₆O_2−0.5x (x=0–1.2) and La_x(GeO₄)_4.5(AlO₄)_1.5O_1.5x−12.75 (x=8.8–9.83), which were prepared by the partial substitution of La³⁺and GeO₄⁴⁻of the basic apatite La₉(GeO₄)₆O_1.5 with Sr²⁺ or Zr⁴⁺ and AlO₄⁵⁻ or AsO₄³⁻. Such substitutions lowered the conductivity of La₉(GeO₄)₆O_1.5. These results were discussed by the electrostatic interaction between Sr²⁺, Zr⁴⁺, AlO₄⁵⁻ or AsO₄³⁻ and oxide ion as a conductive species.     

The effect of rare earth substitution on the magnetic properties of Ni0.5Zn0.5MxFe2−xO4 (M: rare earth)

Variation of the complex permeability with frequency of Ni_1−xZn_xFe₂O₄ (x=0.5, 0.6 and 0.7) prepared by a combustion method has been measured over a wide range of frequency, up to 1.8 GHz. Zn content improves permeability but moves the onset of resonance to lower frequencies.

The influence on some properties of samples prepared by the insertion of small amounts of Ruthenium, Yttrium and rare-earth cations into the Ni_0.5Zn_0.5M_xFe_2−xO₄ ferrite has been also investigated. Relative losses and Curie temperature of all the samples have been measured. Ferrites substituted with Ru and Gd improve microwave behavior compared to non-substituted samples.     

Simultaneous doping with La and Y for Ba- and Ce-sites in BaCeO3 and the ionic conduction

Powder X-ray diffraction (XRD) analysis showed that the single phase perovskite-type structure of Ba_1−xLa_xCe_0.90−xY_0.10+xO₃₋ (0 x 0.40, =0.05) could be maintained in a wide region of doping level by simultaneous partial substitution of La³⁺ for Ba²⁺-site and Y³⁺ for Ce⁴⁺-site in BaCeO₃. The conduction properties of these oxides were investigated using various electrochemical methods in the same concentration of oxygen vacancy (=0.05). At high oxygen partial pressure, these oxides exhibited a mixed oxide ionic and p-type electronic conduction while at low oxygen partial pressure their conduction was almost protonic. Among these oxides, BaCe_0.90Y_0.10O₃₋ exhibited the highest conductivities with a value of 1.24×10⁻¹ S/cm in dry oxygen, and 5.65×10⁻² S/cm in wet hydrogen at 1000°C. Both of the proton and oxide ion conductivities under oxygen and under hydrogen atmospheres decreased monotonically with the increasing substitution for Ba²⁺- and Ce⁴⁺-sites. The decreases in ion conductivities appear to relate to the decreased free volume (V_f) of crystal lattice as well as the increased distortion of lattice from ideal cubic perovskite structure.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Niobium based tetragonal tungsten bronzes as potential anodes for solid oxide fuel cells: synthesis and electrical characterisation

In this paper we report studies on a range of niobate based tungsten bronzes, with a view to analysing their potential as anode materials in SOFCs. Six systems were studied, (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃, Sr_0.6−xLa_xTi_0.2+xNb_0.8−xO₃, (Sr_0.4−xBa_x)Na_0.2NbO₃, (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃, Ba_0.5−xA_xNbO₃ (A=Ca, Sr), and Ba_0.3NbO_2.8, and the electrical conductivities were examined over a range of oxygen partial pressures (10⁻²⁰–1 bar). All the systems showed good conductivity in low oxygen partial pressures, with values as high as 8 S cm⁻¹ at 930°C (P(O₂)=10⁻²⁰ bar). As the oxygen partial pressure was raised the conductivity dropped showing in most cases an approximate [P(O₂)]^−1/4 dependence and good re-oxidation kinetics. Of all the samples studied the (Sr_1−xBa_x)_0.6Ti_0.2Nb_0.8O₃ and (Ba_1−xCa_x)_0.6Ti_0.2Nb_0.8O₃ systems appear most promising for potential use as anode materials in SOFCs.     

(Tl, Pb, Cu)Sr2(Tl, Pb, Cu)2Cu2O8−δ: a nonsuperconducting Tl-1222 cuprate with both heavy atom single and oxygen depleted double layer motifs

An account is given of the synthesis and structural investigation of a newly discovered tetragonal (Tl, Pb, Cu)Sr₂(Tl, Pb, Cu)₂Cu₂O_8−δ compound (Tl-1222^* phase) with both (Tl, Pb, Cu)O single and oxygen depleted (Tl, Pb, Cu)₂O_x double layer motifs, space group I4/mmm, lattice parameters a=3.8405(2), c=29.2536(5) Å, and D_x=7.46 g cm⁻³. Micaceous and highly reflecting black single crystals of 1 mm×1 mm×3–5 μm size were obtained from a Tl₂O₃- and CuO-rich partial melt. The as-grown compound is nonsuperconducting. The very thin crystals are extremely liable to bend out of shape. Deterioration could not be observed within the period of a year under ambient conditions. The complex crystal structure has been solved using single crystals. We take note of the similarity of the unit cell dimensions to superconducting (Tl, Cu)₂Ba₂(Ca, Tl)Cu₂O₈ (Tl-2212 phase) with TlO double rocksalt layers, and compare crystal-chemical details of similar compounds. Apart from the possibility of obtaining superconducting properties by suitable doping, the mechanical properties of the new material are very attractive from the point of view of its use as highly scattering composite layers of an X-ray monochromator.     

Oxygen permeability of La2Cu(Co)O4+δ solid solutions

Formation of the La₂Cu_1−xCo_xO_4+δ solid solutions with orthorhombic K₂NiF₄-type structure was found to be in the range of 0≤x≤0.30 at temperatures above 1270 K. Incorporating cobalt into the copper sublattice of lanthanum cuprate leads to increasing oxygen hyperstoichiometry and decreasing electrical conductivity. Thermal expansion coefficients of the La₂Cu_1−xCo_xO_4+δ (x=0.02–0.30) ceramics at 470–1100 K were calculated from the dilatometric data to vary in the range (12.2–13.2)×10⁻⁶ K⁻¹. Studying the dependence of oxygen permeation fluxes through La₂Cu(Co)O_4+δ on the membrane thickness demonstrated that the oxygen transport at the thickness values below 1 mm is limited by both surface exchange rate and bulk ionic conductivity. Oxygen permeability of the La₂Cu_1−xCo_xO_4+δ solid solutions was ascertained to increase with cobalt concentration at x=0.02–0.10 and to decrease with further dopant additions, indicating a participation of interstitial oxygen in the ionic transport.     

Superconducting Nd1.85Ce0.15CuO4 films grown by the pulsed electron deposition technique

Nd_1.85Ce_0.15CuO_4−δ superconducting thin films were prepared on (1 0 0) SrTiO₃ substrates by pulsed electron deposition technique without reducing atmosphere. Oxygen content is finely controlled by high temperature vacuum annealing, and optimal superconductivity has been obtained. The deposition conditions of the film are discussed in details. Higher deposition temperature and lower gas pressure result in the loss of copper and the appearance of the foreign phase Ce_0.5Nd_0.5O_1.75. High quality Nd_1.85Ce_0.15CuO_4−δ epitaxial films are deposited at 840–870 °C in the mixed gas with a ratio of O₂:Ar = 1:3.     

An electrochemical investigation of Li intercalation in the sol-gel LiMn2O4 spinel oxide

An alternative approach for obtaining the LiMn₂O₄ spinel phase is provided by the use of the sol-gel method in aqueous solution. The main electrochemical properties of the sol-gel LiMn₂O₄ phase are reported. In addition to chronopotentiometric and voltammetric experiments, the kinetics of the electrochemical insertion–extraction of lithium in Li_xMn₂O₄ (0.25<x<1) has been investigated using ac impedance spectroscopy. The strong variation of the chemical diffusion coefficient D_Li vs x, in the range 10⁻⁸–10⁻¹¹ cm² s⁻¹ (D_Li is found to be maximum for x=0.55) is critically discussed.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Intercalation thermodynamics and chemical diffusion of oxygen in the solid solution YBa2Cu3−xCoxO6+δ

The equilibrium oxygen content as a function of the temperature and oxygen pressure was measured for the solid solution YBa₂Cu_3−xCo_xO_6+δ, where x=0, 0.2, 0.4, 0.6, 0.8, by using coulometric titration in the temperature range 600–850°C and oxygen pressures between 10⁻⁵ and 1.0 atm. The change in the partial molar enthalpy and entropy of the intercalated oxygen was determined at different oxygen and cobalt contents. The oxygen chemical diffusion was studied by thermogravimetric relaxation in the oxygen-controlled atmosphere. The thermodynamic data were employed to determine how the chemical diffusion coefficient, the thermodynamic factor and the random-diffusion coefficient depend on oxygen content in specimens with different cobalt concentration. The oxygen intercalation thermodynamics and diffusivity results provide evidence of ordering phenomena on a microscopic scale in the basal plane of the tetragonal solid solution YBa₂Cu_3−xCo_xO_6+δ. A model for the oxygen diffusion is suggested to explain the large difference between the random and tracer diffusion coefficients in YBa₂Cu₃O_6+δ     

Oxygen diffusion and surface exchange in La1−xSrxFe0.8Cr0.2O3−δ (x=0.2, 0.4 and 0.6)

Oxygen tracer diffusion (D*) and surface exchange rate constant (k*) have been measured, using isotopic exchange and depth profiling by secondary ion mass spectrometry (SIMS), in La_1−xSr_xFe_0.8Cr_0.2O_3−δ (x=0.2, 0.4 and 0.6). Measurements were made as a function of temperature (700–1000 °C) and oxygen partial pressure (0.21–10⁻²¹ atm) in dry oxygen, water vapour and water vapour/hydrogen/nitrogen mixtures. At high oxygen activity, D* was found to increase with increasing temperature and Sr content. The activation energies for D* in air are 2.13 eV (x=0.2), 1.53 eV (x=0.4) and 1.21 eV (x=0.6). As the oxygen activity decreases, D* increases as expected qualitatively from the increase in oxygen vacancy concentration. Under strongly reducing conditions, the measured values of D* at 1000 °C range from 10⁻⁸ cm² s⁻¹ for x=0.2 to 10⁻⁷ cm² s⁻¹ for x=0.4 and 0.6. The activation energies determined at constant H₂O/H₂ ratio are 1.21 eV (x=0.2), 1.59 eV (x=0.4) and 0.82 eV (x=0.6).

The surface exchange rate constant of oxygen for the H₂O molecule is similar in magnitude to that for the O₂ molecule and both increase with increasing Sr concentration.     

Evidence for pinning by (Sr,Ca)2CuOy particles in partial-melting processed bulk Bi2Sr2CaCu2O8+δ ceramics

Flux distributions of partial-melting processed Bi₂Sr₂CaCu₂O_8+δ ceramics are obtained using magneto-optic imaging. In remanent states (μ₀H_a=0 T), large amounts of trapped flux are observed along (Sr,Ca)₂CuO_y particles embedded in the Bi₂Sr₂CaCu₂O_8+δ matrix. Despite the relatively large size of these particles (up to 30 μm), the pinning effect is similar to that of Y₂BaCuO₅ particles in melt-processed YBa₂Cu₃O_7−δ. Furthermore, we discuss how the pinning capability of non-superconducting particles of different sizes and densities will show up in magneto-optic images.     

A study on the nonstoichiometry of tin oxides by coulometric titration

In this investigation, nonstoichiometries and defect structures of tin oxides were studied between 694 and 990 K by coulometric titration using solid state electrolyte (YSZ) cells. The relationship between nonstoichiometry of the oxide (x) and equilibrium oxygen partial pressure (P_o2) was expressed by the proportionality: xP_O2^−1/6. An intermediate oxide phase, Sn₃O₄ between Sn and SnO₂ was observed in the temperature range of 696–732 K. The standard Gibbs energy of formation of Sn₃O₄ via the reaction; was found to be ΔG^o_Sn3O4 = −1163960+417.36 T (J/mol). The standard Gibbs energy change for the defect formation reaction in SnO_2−x was calculated to be ΔG^o_SnO2−x = 3.05×10⁵−38.97 T (J/mol)).     

Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.