Iridium‐Catalyst‐Based Autonomous Bubble‐Propelled Graphene Micromotors with Ultralow Catalyst Loading

A novel concept of an iridium‐based bubble‐propelled Janus‐particle‐type graphene micromotor with very high surface area and with very low catalyst loading is described. The low loading of Ir catalyst (0.54 at %) allows for fast motion of graphene microparticles with high surface area of 316.2 m² g^?1. The micromotor was prepared with a simple and scalable method by thermal exfoliation of iridium‐doped graphite oxide precursor composite in hydrogen atmosphere. Oxygen bubbles generated from the decomposition of hydrogen peroxide at the iridium catalytic sites provide robust propulsion thrust for the graphene micromotor. The high surface area and low iridium catalyst loading of the bubble‐propelled graphene motors offer great possibilities for dramatically enhanced cargo delivery.     

Superior Lithium‐Ion Storage Properties of Si‐Based Composite Powders with Unique Si@Carbon@Void@Graphene Configuration

Composite powders of the configuration Si@carbon@void@graphene were prepared by a one‐step spray pyrolysis process, by adding polyvinylpyrrolidone (PVP) to a precursor solution containing graphene oxide (GO) sheets and silicon nanoparticles (NPs). Morphological analysis indicates that the individual Si NPs are coated with amorphous carbon and encapsulated in a micrometer‐sized graphene ball structure that offers a large amount of buffer space. The addition of PVP improves the stability of the colloidal spray solution containing the GO sheets and the Si NPs. Consequently, the prepared Si@C@void@graphene composite powders have a relatively more uniform morphology than the Si@void@graphene composite powders prepared from the spray solution without PVP. The first charge and discharge capacities of the Si@C@void@graphene electrode measured at 0.1 A g^?1 are as high as 3102 and 2215 mA h g^?1, respectively. With an increase in the current rate from 0.5 to 11 A g^?1, 46 % of the original capacity (i.e., 2134 mA h g^?1) is maintained. After 500 cycles at a high rate of 7 A g^?1, the Si@C@void@graphene electrode shows 84 % capacity retention and 99.8 % of the average Coulombic efficiency. The superior cycling and rate capabilities of the prepared Si@C@void@graphene electrode could be attributed to the uniform carbon coating of the Si NPs and the graphene ball structure, which facilitates efficient diffusion of Li ions and prevents the penetration of electrolyte into graphene ball during cycling.     

Synthesis of Hierarchically Porous Sandwich‐Like Carbon Materials for High‐Performance Supercapacitors

For the first time, hierarchically porous carbon materials with a sandwich‐like structure are synthesized through a facile and efficient tri‐template approach. The hierarchically porous microstructures consist of abundant macropores and numerous micropores embedded into the crosslinked mesoporous walls. As a result, the obtained carbon material with a unique sandwich‐like structure has a relatively high specific surface (1235 m² g^?1), large pore volume (1.30 cm³ g^?1), and appropriate pore size distribution. These merits lead to a comparably high specific capacitance of 274.8 F g^?1 at 0.2 A g^?1 and satisfying rate performance (87.7 % retention from 1 to 20 A g^?1). More importantly, the symmetric supercapacitor with two identical as‐prepared carbon samples shows a superior energy density of 18.47 Wh kg^?1 at a power density of 179.9 W kg^?1. The asymmetric supercapacitor based on as‐obtained carbon sample and its composite with manganese dioxide (MnO₂) can reach up to an energy density of 25.93 Wh kg^?1 at a power density of 199.9 W kg^?1. Therefore, these unique carbon material open a promising prospect for future development and utilization in the field of energy storage.     

Biomass‐Derived Porous Carbon with Micropores and Small Mesopores for High‐Performance Lithium–Sulfur Batteries

Biomass‐derived porous carbon BPC‐700, incorporating micropores and small mesopores, was prepared through pyrolysis of banana peel followed by activation with KOH. A high specific BET surface area (2741 m² g^?1), large specific pore volume (1.23 cm³ g^?1), and well‐controlled pore size distribution (0.6–5.0 nm) were obtained and up to 65 wt % sulfur content could be loaded into the pores of the BPC‐700 sample. When the resultant C/S composite, BPC‐700‐S65, was used as the cathode of a Li–S battery, a large initial discharge capacity (ca. 1200 mAh g^?1) was obtained, indicating a good sulfur utilization rate. An excellent discharge capacity (590 mAh g^?1) was also achieved for BPC‐700‐S65 at the high current rate of 4 C (12.72 mA cm^?2), showing its extremely high rate capability. A reversible capacity of about 570 mAh g^?1 was achieved for BPC‐700‐S65 after 500 cycles at 1 C (3.18 mA cm^?2), indicating an outstanding cycling stability.     

Optimizing adsorptive removal of malachite green and methyl orange dyes from simulated wastewater by Mn‐doped CuO‐Nanoparticles loaded on activated carbon using CCD‐RSM: Mechanism,regeneration, isotherm,kinetic, and thermodynamic studies

In the present work, Mn‐doped CuO‐NPs‐AC was prepared by a simple method, characterized using various techniques such as FESEM, EDX, XRD, PSD, and pH_pzc and finally used for the adsorption of malachite green (MG) and methyl orange (MO) in a number of single and binary solutions. A series of adsorption experiments were conducted to investigate and optimize the influence of various factors (such as different pH, concentration of MG and MO, adsorbent mass, and sonication time) on the simultaneous adsorption of MG and MO using response surface methodology. Under optimal conditions of pH 10, adsorbent dose of 0.02 g, MG concentration of 30 mg L^?1, MO concentration of 30 mg L^?1, and sonication time of 4.5 min at room temperature, the maximum predicted adsorption was observed to be 100.0%, for both MG and MO, showing that there is a favorable harmony between the experimental data and model predictions. The adsorption isotherm of MO and MG by Mn‐doped CuO‐NPs‐AC could be well clarified by the Langmuir model with maximum adsorption capacity of 320.69 mg g^?1 and 290.11 mg g^?1 in the single solution and 233.02 mg g^?1 and 205.53 mg g^?1 in the binary solution by 0.005 g of adsorbent mass for MG and MO, respectively. Kinetic studies also revealed that both MG and MO adsorption were better defined by the pseudo‐second order model for both solutions. In addition, the thermodynamic constant studies disclosed that the adsorption of MG and MO was likely to be influenced by a physisorption mechanism. Eventually, the reusability of the Mn‐doped CuO‐NPs‐AC after six times showed a reduction in the adsorption percentage of MG and MO.     

Polypyrrole Shell@3D‐Ni Metal Core Structured Electrodes for High‐Performance Supercapacitors

Three‐dimensional (3D) nanometal films serving as current collectors have attracted much interest recently owing to their promising application in high‐performance supercapacitors. In the process of the electrochemical reaction, the 3D structure can provide a short diffusion path for fast ion transport, and the highly conductive nanometal may serve as a backbone for facile electron transfer. In this work, a novel polypyrrole (PPy) shell@3D‐Ni‐core composite is developed to enhance the electrochemical performance of conventional PPy. With the introduction of a Ni metal core, the as‐prepared material exhibits a high specific capacitance (726 F g^?1 at a charge/discharge rate of 1 A g^?1), good rate capability (a decay of 33 % in C_sp with charge/discharge rates increasing from 1 to 20 A g^?1), and high cycle stability (only a small decrease of 4.2 % in C_sp after 1000 cycles at a scan rate of 100 mV s^?1). Furthermore, an aqueous symmetric supercapacitor device is fabricated by using the as‐prepared composite as electrodes; the device demonstrates a high energy density (≈21.2 Wh kg^?1) and superior long‐term cycle ability (only 4.4 % and 18.6 % loss in C_sp after 2000 and 5000 cycles, respectively).     

Effective removal of 2,4,6‐trinitrophenol over hexagonal metal–organic framework NH2‐MIL‐88B(Fe)

A nanostructured organic–inorganic framework, hexagonal NH₂‐MIL‐88B, has been prepared through a facile one‐pot reflux reaction and then it was characterized using various techniques. The as‐prepared sample with high specific surface area (414 m² g^?1) showed excellent adsorption for 2,4,6‐trinitrophenol (TNP) in the liquid phase. Detailed studies of the adsorption kinetics, adsorption mechanism, adsorption isotherm, activation energy and various thermodynamic parameters were conducted. The adsorption mechanism of NH₂‐MIL‐88B for TNP may be ascribed to hydrogen bond interaction, and the complexation between ─OH in TNP and unsaturated Fe(III) on the surface of NH₂‐MIL‐88B. The maximum adsorption capacity of NH₂‐MIL‐88B for TNP based on the Langmuir isotherm was 163.66 mg g^?1. The as‐prepared NH₂‐MIL‐88B adsorbent seems to be a promising material in practice for TNP removal from aqueous solution.     

Synthesis and kinetic study on the thermal degradation of triblock copolymer of polycaprolactone‐poly (glycidyl nitrate)‐polycaprolactone (PCL‐PGN‐PCL) as an energetic binder

In this study, an energetic binder is synthesized via ring opening copolymerization of ε‐caprolactone with poly (glycidyl nitrate) (PGN) of low molecular weight (M_n = 1350 g mol^?1) as a macroinitiator to form triblock copolymer polycaprolactone‐PGN‐polycaprolactone (PCL‐PGN‐PCL) (M_n = 4128 g mol^?1). The effects of catalyst type and its concentration, reaction time, and solvent are investigated in this polymerization reaction. The resulting triblock copolymer is characterized by Fourier transform infrared spectroscopy (FT‐IR), nuclear magnetic resonance spectroscopy (NMR), gel permeation chromatography (GPC), differential scanning calorimetry (DSC), and thermal gravimetric analysis (TGA). The DSC result shows that the glass transition temperature of triblock copolymer (T_g = ?50°C) is lower than PGN (T_g = ?35°C). Also, the decomposition kinetics of this energetic binder is studied by DSC, TGA, and its derivative (DTG). An advanced isoconversional method is applied for kinetic analysis. Activation energy is calculated by Flynn‐Wall‐Ozawa (FWO) and Kissinger methods. The resulting activation energy from Kissinger method for the first and the second steps are 42.98 and 74.56 kJ mol^?1, respectively. Also, it is found from FWO results that the activation energy for the copolymer increases with degradation degree (α).     

An Advanced NiCoFeO/Polyaniline Composite for High‐Performance Supercapacitors

To reduce the charge‐transfer resistance of supercapacitors and achieve faster reversible redox reactions, ternary Ni‐Co‐Fe layered double hydroxide was prepared by using the urea method and then calcined to give NiCoFe oxide (NiCoFeO). To enhance conductivity, a polyaniline (PANI) conductive layer was assembled on the surface of the NiCoFeO particles by in situ oxidative polymerization of aniline monomers. The as‐prepared NiCoFeO/PANI composite was successful employed as a supercapacitor electrode. It was found that the NiCoFeO/PANI composite displayed good cycling stability, with a capacity loss of only 29.54 % after 5000 cycles. Furthermore, the NiCoFeO/PANI composite also exhibited excellent supercapacitor performance, with a high specific capacity of 843 F g^?1 at a current density of 2 A g^?1, whereas NiCoFeO showed a specific capacity of only 478 F g^?1. This result was attributed to the synergistic effect between NiCoFeO and PANI. The facile synthesis strategy and excellent electrochemical performance suggest that NiCoFeO/PANI is a promising economical electrode material for applications in supercapacitors.     

Effect of inorganic oxide supports on the activity of chromium‐based catalysts in ethylene trimerization

Novel heterogeneous catalysts were prepared using immobilization of bis(2‐decylsulfanylethyl)amine–CrCl₃ (Cr‐SNS‐D) on various supports, namely commercial TiO₂, Al₂O₃ and magnetic Fe₃O₄@SiO₂ nanoparticles, to yield solid catalysts denoted as support@Cr‐SNS‐D. The structure of the catalysts was confirmed on the basis of spectroscopic analyses, N₂ adsorption–desorption and inductively coupled plasma (ICP) analysis. The surface areas of Al₂O₃@Cr‐SNS‐D, Fe₃O₄@SiO₂@Cr‐SNS‐D and TiO₂@Cr‐SNS‐D catalysts were determined to be 70, 23 and 41 m² g^?1, respectively. A decrease in surface area from that of the supports clearly establishes accurate immobilization of Cr‐SNS‐D catalyst on the surface of the parent carriers. The loading of Cr was determined to be 0.02, 0.16 and 0.11 mmol g^?1 for Cr‐SNS‐D supported on TiO₂, Al₂O₃ and Fe₃O₄@SiO₂, respectively, using ICP analysis. After preparation and full characterization of the catalysts, ethylene trimerization reaction was accomplished in 40 ml of dry toluene, at 80°C and 25 bar ethylene pressure and in the presence of methylaluminoxane (Al/Cr = 700) within 30 min. The supported chromium catalysts were found to be efficient and selective for the ethylene trimerization reaction. The highest activity (74 650 g_1‐hexene g_Cr^?1 h^?1), as well as no polyethylene formation during reaction processes, was observed when TiO₂ was used as the catalyst support.     

Superior Lithium‐Ion Storage Properties of Mesoporous CuO–Reduced Graphene Oxide Composite Powder Prepared by a Two‐Step Spray‐Drying Process

Mesoporous CuO–reduced graphene oxide (rGO) composite powders were prepared by using a two‐step spray‐drying process. In the first step, hollow CuO powders were prepared from a spray solution of copper nitrate trihydrate with citric acid and were wet milled to obtain a colloidal spray solution. In the second step, spray drying of the colloidal solution that contained dispersed GO nanosheets produced mesoporous CuO–rGO composite powders with particle sizes of several microns. Thermal reduction of GO nanosheets to rGO nanosheets occurred during post‐treatment at 300 °C. Initial discharge capacities of the hollow CuO, bare CuO aggregate, and CuO–rGO composite powders at a current density of 2 A g^?1 were 838, 1145, and 1238 mA h g^?1, respectively. Their discharge capacities after 200 cycles were 259, 380, and 676 mA h g^?1, respectively, and their corresponding capacity retentions measured from the second cycle were 67, 48, and 76 %, respectively. The mesoporous CuO–rGO composite powders have high structural stability and high conductivity because of the rGO nanosheets, and display good cycling and rate performances.     

The preparation of covalent triazine‐based framework via Friedel‐Crafts reaction of 2,4,6‐trichloro‐1,3,5‐triazine with N,N′‐diphenyl‐N,N′‐di(m‐tolyl)benzidine for capturing and sensing to iodine

The covalent triazine‐based framework (TDPDB) has been prepared by Friedel‐Crafts polymerization reaction of N,N′‐diphenyl‐N,N′‐di(m‐tolyl)benzidine (DPDB) with 2,4,6‐trichloro‐1,3,5‐triazine (TCT) catalyzed by methanesulfonic acid. The yield of the reaction (94.85%) is very high. TDPDB was provided with Brunauer‐Emmett‐Teller specific surface area of 592.18 m² g^?1 and pore volume of 0.5241 cm³ g^?1. TDPDB demonstrated an excellent capacity for capturing iodine (3.93 g g^?1) and an outstanding ability to fluorescent sensing to iodine with Ksv of 5.83 × 10⁴ L mol^?1. It also showed high fluorescent sensing sensitivity to picric acid.     

A New Concept for Obtaining SnO2 Fiber‐in‐Tube Nanostructures with Superior Electrochemical Properties

Tin oxide (SnO₂) nanotubes with a fiber‐in‐tube structure have been prepared by electrospinning and the mechanism of their formation has been investigated. Tin oxide‐carbon composite nanofibers with a filled structure were formed as an intermediate product, which were then transformed into SnO₂ nanotubes with a fiber‐in‐tube structure during heat treatment at 500 °C. Nanofibers with a diameter of 85 nm were found to be located inside hollow nanotubes with an outer diameter of 260 nm. The prepared SnO₂ nanotubes had well‐developed mesopores. The discharge capacities of the SnO₂ nanotubes at the 2nd and 300th cycles at a current density of 1 A g^?1 were measured as 720 and 640 mA h g^?1, respectively, and the corresponding capacity retention measured from the 2nd cycle was 88 %. The discharge capacities of the SnO₂ nanotubes at incrementally increased current densities of 0.5, 1.5, 3, and 5 A g^?1 were 774, 711, 652, and 591 mA h g^?1, respectively. The SnO₂ nanotubes with a fiber‐in‐tube structure showed superior cycling and rate performances compared to those of SnO₂ nanopowder. The unique structure of the SnO₂ nanotubes with a fiber@void@tube configuration improves their electrochemical properties by reducing the diffusion length of the lithium ions, and also imparts greater stability during electrochemical cycling.     

N‐heterocyclic carbene–palladium(II) complex supported on magnetic mesoporous silica for Heck cross‐coupling reaction

Magnetic mesoporous silica was prepared via embedding magnetite nanoparticles between channels of mesoporous silica (SBA‐15). The prepared composite (Fe₃O₄@SiO₂‐SBA) was then reacted with 3‐chloropropyltriethoxysilane, sodium imidazolide and 2‐bromopyridine to give 3‐(pyridin‐2‐yl)‐1H‐imidazol‐3‐iumpropyl‐functionalized Fe₃O₄@SiO₂‐SBA as a supported pincer ligand for Pd(II). The functionalized magnetic mesoporous silica was further reacted with [PdCl₂(SMe₂)₂] to produce a supported N‐heterocyclic carbene–Pd(II) complex. The obtained catalyst was characterized using Fourier transform infrared spectroscopy, scanning electron microscopy, energy‐dispersive X‐ray analysis, vibrating sample magnetometry, Brunauer–Emmett–Teller surface area measurement and X‐ray diffraction. The amount of the loaded complex was 80.3 mg g^?1, as calculated through thermogravimetric analysis. The formation of the ordered mesoporous structure of SBA‐15 was confirmed using low‐angle X‐ray diffraction and transmission electron microscopy. Also, X‐ray photoelectron spectroscopy confirmed the presence of the Pd(II) complex on the magnetic support. The prepared magnetic catalyst was then effectively used in the coupling reaction of olefins with aryl halides, i.e. the Heck reaction, in the presence of a base. The reaction parameters, such as solvent, base, temperature, amount of catalyst and reactant ratio, were optimized by choosing the coupling reaction of 1‐bromonaphthalene and styrene as a model Heck reaction. N‐Methylpyrrolidone as solvent, 0.25 mol% catalyst, K₂CO₃ as base, reaction temperature of 120°C and ultrasonication of the catalyst for 10 min before use provided the best conditions for the Heck cross‐coupling reaction. The best results were observed for aryl bromides and iodides while aryl chlorides were found to be less reactive. The catalyst exhibited noticeable stability and reusability.     

Sulfur‐Impregnated Core–Shell Hierarchical Porous Carbon for Lithium–Sulfur Batteries

Core–shell hierarchical porous carbon spheres (HPCs) were synthesized by a facile hydrothermal method and used as host to incorporate sulfur. The microstructure, morphology, and specific surface areas of the resultant samples have been systematically characterized. The results indicate that most of sulfur is well dispersed over the core area of HPCs after the impregnation of sulfur. Meanwhile, the shell of HPCs with void pores is serving as a retard against the dissolution of lithium polysulfides. This structure can enhance the transport of electron and lithium ions as well as alleviate the stress caused by volume change during the charge–discharge process. The as‐prepared HPC‐sulfur (HPC‐S) composite with 65.3 wt % sulfur delivers a high specific capacity of 1397.9 mA h g^?1 at a current density of 335 mA g^?1 (0.2 C) as a cathode material for lithium–sulfur (Li‐S) batteries, and the discharge capacity of the electrode could still reach 753.2 mA h g^?1 at 6700 mA g^?1 (4 C). Moreover, the composite electrode exhibited an excellent cycling capacity of 830.5 mA h g^?1 after 200 cycles.     

Hierarchical Activated Mesoporous Phenolic‐Resin‐Based Carbons for Supercapacitors

A series of hierarchical activated mesoporous carbons (AMCs) were prepared by the activation of highly ordered, body‐centered cubic mesoporous phenolic‐resin‐based carbon with KOH. The effect of the KOH/carbon‐weight ratio on the textural properties and capacitive performance of the AMCs was investigated in detail. An AMC prepared with a KOH/carbon‐weight ratio of 6:1 possessed the largest specific surface area (1118 m² g^?1), with retention of the ordered mesoporous structure, and exhibited the highest specific capacitance of 260 F g^?1 at a current density of 0.1 A g^?1 in 1 M H₂SO₄ aqueous electrolyte. This material also showed excellent rate capability (163 F g^?1 retained at 20 A g^?1) and good long‐term electrochemical stability. This superior capacitive performance could be attributed to a large specific surface area and an optimized micro‐mesopore structure, which not only increased the effective specific surface area for charge storage but also provided a favorable pathway for efficient ion transport.     

A Self‐Standing and Flexible Electrode of Yolk–Shell CoS2 Spheres Encapsulated with Nitrogen‐Doped Graphene for High‐Performance Lithium‐Ion Batteries

Flexible lithium‐ion batteries (LIBs) have recently attracted increasing attention with the fast development of bendable electronic systems. Herein, a facile and template‐free solvothermal method is presented for the fabrication of hybrid yolk–shell CoS₂ and nitrogen‐doped graphene (NG) sheets. The yolk–shell architecture of CoS₂ encapsulated with NG coating is designed for the dual protection of CoS₂ to address the structural and interfacial stability concerns facing the CoS₂ anode. The as‐prepared composite can be assembled into a film, which can be used as a binder‐free and flexible electrode for LIBs that does not require any carbon black conducting additives or current collectors. When evaluating lithium‐storage properties, such a flexible electrode exhibits a high specific capacity of 992 mAh g^?1 in the first reversible discharge capacity at a current rate of 100 mA g^?1 and high reversible capacity of 882 mAh g^?1 after 150 cycles with excellent capacity retention of 89.91 %. Furthermore, a reversible capacity as high as 655 mAh g^?1 is still achieved after 50 cycles even at a high rate of 5 C due to the yolk–shell structure and NG coating, which not only provide short Li‐ion and electron pathways, but also accommodate large volume variation.     

Plant‐supported silver nanoparticles: Efficient,economically viable and easily recoverable catalyst for the reduction of organic pollutants

Ginger rhizome powder was used for the synthesis of supported metallic nanoparticle catalysts. A simple and novel adsorption method was used for the synthesis of silver nanoparticles loaded on ginger powder (Ag/GP), copper on ginger powder (Cu/GP) and nickel on ginger powder (Ni/GP). Among these, Ag/GP showed selective reduction of methyl orange and was used for further reactions. The prepared nanomaterials were characterized through X‐ray diffraction, transmission electron microscopy, field emission scanning electron microscopy, fourier transform infrared spectroscopy and energy‐dispersive X‐ray spectroscopy. The prepared Ag/GP catalyst was employed in the catalytic reduction of 4‐nitrophenol (4‐NP), 2‐nitrophenol (2‐NP), rhodamine B, methyl red and congo red. Ag/GP showed excellent catalytic reduction activity, the rate constants being 1.26 × 10^?3 and 2.38 × 10^?3 s^?1 for 2‐NP and 4‐NP, respectively. The turnover frequency reached 1.06 min^?1 for 2‐NP and 1.16 min^?1 for 4‐NP when using the Ag/GP catalyst. The prepared Ag/GP catalyst demonstrated outstanding activity for the degradation of a mixed solution of dyes. Also, stability and reusability of the prepared catalyst were investigated, which showed outstanding reusability up to five times and was stable up to five days.     

MnO2 Nanosheets Grown on Nitrogen‐Doped Hollow Carbon Shells as a High‐Performance Electrode for Asymmetric Supercapacitors

A hierarchical hollow hybrid composite, namely, MnO₂ nanosheets grown on nitrogen‐doped hollow carbon shells (NHCSs@MnO₂), was synthesized by a facile in situ growth process followed by calcination. The composite has a high surface area (251 m²g^?1) and mesopores (4.5 nm in diameter), which can efficiently facilitate transport during electrochemical cycling. Owing to the synergistic effect of NHCSs and MnO₂, the composite shows a high specific capacitance of 306 F g^?1, good rate capability, and an excellent cycling stability of 95.2 % after 5000 cycles at a high current density of 8 A g^?1. More importantly, an asymmetric supercapacitor (ASC) assembled by using NHCSs@MnO₂ and activated carbon as the positive and negative electrodes exhibits high specific capacitance (105.5 F g^?1 at 0.5 A g^?1 and 78.5 F g^?1 at 10 A g^?1) with excellent rate capability, achieves a maximum energy density of 43.9 Wh kg^?1 at a power density of 408 W kg^?1, and has high stability, whereby the ASC retains 81.4 % of its initial capacitance at a current density of 5 A g^?1 after 4000 cycles. Therefore, the NHCSs@MnO₂ electrode material is a promising candidate for future energy‐storage systems.     

Preparation of a NiAl‐Oxide@Polypyrrole Composite for High‐Performance Supercapacitors

A core‐shell NiAlO@polypyrrole composite (NiAlO@PPy) with a 3D “sand rose”‐like morphology was prepared via a facile in situ oxidative polymerization of pyrrole monomer, where the role of PPy coating thickness was investigated for high‐performance supercapacitors. Microstructure analyses indicated that the PPy was successfully coated onto the NiAlO surface to form a core‐shell structure. The NiAlO@PPy exhibited a better electrochemical performance than pure NiAlO, and the moderate thickness of the PPy shell layer was beneficial for expediting the electron transfer in the redox reaction. It was found that the NiAlO@PPy₅ prepared at 5.0 mL L^?1 addition amount of pyrrole monomer demonstrated the best electrochemical performance with a high specific capacitance of 883.2 F g^?1 at a current density of 1 A g^?1 and excellent capacitance retention of 91.82 % of its initial capacitance after 1000 cycles at 3 A g^?1. The outstanding electrochemical performance of NiAlO@PPy₅ were due to the synergistic effect of NiAlO and PPy, where the uniform network‐like PPy shell with the optimal thickness made electrolyte ions more easily accessible for faradic reactions. This work provided a simple approach for designing organic–inorganic core‐shell materials as high‐performance electrode materials for electrochemical supercapacitors.