Underlayer diffusion-induced enhancement of coercivity in high anisotropy FePt thin films

The L1₀ ordered FePt films have been prepared at 300 °C with a basic structure of CrRu/MgO/FePt, followed by a post-annealing process at temperatures from 200 to 350 °C. The magnetic properties and the microstructure of the films were investigated. It is found that coercivity of FePt films increases greatly from 3.57 to 9.1 kOe with the increasing annealing temperature from 200 to 350 °C. The loop slope of the M–H curves decreases with the increasing annealing temperature, which is due to the grain isolation induced by MgO underlayer diffusion during the annealing process. The underlayer diffusion could be a useful approach to prepare the FePt-based composite films for high-density recording media.     

Effect of thermal annealing on ohmic contacts properties of undoped and Si-doped AlxGa1−xN on Si (1 1 1) substrate grown by PA-MBE

In this work, we study the ohmic contact properties of titanium (Ti)/aluminum (Al) bi-layer contacts on undoped and n-type doped Al_xGa_1−xN grown on silicon (1 1 1) substrates by radio frequency nitrogen plasma-assisted molecular beam epitaxy (PA-MBE). The electrical stability of the contacts at various annealing temperatures of 400, 500, 600 and 700 °C were investigated. Specific contact resistivity was determined using transmission line method (TLM) and current–voltage (I–V) measurements. The results reveal that the bi-layer scheme was sensitive to the change of annealing temperatures and annealing time. The optimal value of specific contact resistivities was obtained at annealing temperature of 600 °C for both samples. However, the values of n-type doped sample exhibited better results compared with the undoped sample.     

Thermal stability of Ag films in air prepared by thermal evaporation

The thermal stability of silver films in air has been studied. Pure Ag films, 250 nm in thickness, were prepared on glass substrates by thermal evaporation process, and subsequently annealed in air for 1 h at temperatures between 200 and 400 °C. The structure and morphology of the samples were investigated by X-ray diffraction, Raman spectra and atomic force microscopy. It is found that the crystallization enhances for the annealed films, and film surface becomes oxidized when annealing temperature is higher than 350 °C. The electrical and optical properties of the films were studied by van der Pauw method and spectrophotometer, respectively. Reflectance drops sharply as Ag films are annealed at temperatures above 250 °C. Film annealed at 250 °C has the maximum surface roughness and the minimum reflectance at 600 nm optical wavelength. Film annealed at 200 °C has the minimum resistivity, and resistivity increases with the increasing of the annealing temperature when temperature is above 200 °C. The results show that both oxidization on film surface and agglomeration of silver film result in infinite of electrical resistivity as the annealing temperature is above 350 °C.     

Solution processed amorphous InGaZnO semiconductor thin films and transistors

Amorphous indium gallium zinc oxide (a-IGZO) semiconductor thin films and transistors were deposited on alkali-free glasses by the sol–gel route. The atomic ratio of In:Ga:Zn in the solution was 0.7:0.3:1. In this study, the effects of annealing temperature on the structural, surface condition, optical transmittance, and electrical resistivity of a-IGZO semiconductor thin films were investigated. GIXRD measurements and TEM-NBD analysis indicated that all annealed IGZO thin films had an amorphous phase structure. The dried IGZO sol–gel films annealed at a temperature higher than 425 °C had a flat surface and exhibited high transparency (>89%) in the visible region. According to results from TGA, FT-IR and XPS, the residual organic compounds in the dried IGZO sol–gel films were completely removed at the annealing temperatures higher than 450 °C. Therefore, we chose the 450 °C annealed thin film as the active channel layer in the bottom-gate, bottom-contact (BGBC) thin-film transistor (TFT) in the present study. Current–voltage (I–V) characteristics of the 450 °C annealed a-IGZO TFT revealed that it operated in n-type behavior with a positive threshold voltage (enhancement mode).     

Dry air effects on the copper oxides sensitive layers formation for ethanol vapor detection

The copper oxide films have been deposited by thermal evaporation and annealed under ambient air and dry air respectively, at different temperatures. The structural characteristics of the films were investigated by X-ray diffraction. They showed the presences of two hydroxy-carbonate minerals of copper for annealing temperatures below 250 °C. Above this temperature the conductivity measurements during the annealing process, show a transition phase from metallic copper to copper oxides. The copper oxides sensitivity toward ethanol were performed using conductivity measurements at the working temperature of 200 °C. A decrease of conductivity was observed under ethanol vapor, showing the p-type semi-conducting characters of obtained copper oxide films. It was found that the sensing properties of copper oxide toward ethanol depend mainly on the annealing conditions. The best responses were obtained with copper layers annealed under dry air.     

The influence of substrate temperature on the morphology, optical and electrical properties of thermal-evaporated ZnTe Thin Films

The structural, morphological, optical and electrical properties of ZnTe films deposited by evaporation were investigated as a function of substrate temperature (at −123 and 27 °C) and post-deposition annealing temperature (at 200, 300 and 400 °C). It was determined that films deposited at both substrate temperatures were polycrystalline in nature with zinc-blende structure and a strong (1 1 1) texture. A small Te peak was detected in XRD spectra for both substrate temperatures, indicating that as-deposited ZnTe films were slightly rich in Te. Larger grains and a tighter grain size distribution were obtained with increased substrate temperature. Scanning electron microscopy (SEM) studies showed that the microstructures of the as-deposited films agreed well with the expectations from structure zone model. Post-deposition annealing induced further grain growth and tightened the grain size distribution. Annealing at 400 °C resulted in randomization in the texture of films deposited at both substrate temperatures. Optical spectroscopy results of the films indicated that the optical band gap value increased from 2.13 to 2.16 eV with increased substrate temperature. Increasing the annealing temperature sharpened the band-edge. Resistivity measurements showed that the resistivity of films deposited at substrate temperatures of −123 and 27 °C were 32 Ω cm, and 1.0 × 10⁴ Ω cm, respectively with corresponding carrier concentrations of 8.9 × 10¹⁵ cm⁻³ and 1.5 × 10¹⁴ cm⁻³. Annealing caused opposite changes in the film resistivity between the samples prepared at substrate temperatures of −123 and 27 °C.     

Comparison of annealing effects on Zn-doped GaMnAs and undoped GaMnAs epilayers

To compare the annealing effects on GaMnAs-doped with Zn (GaMnAs:Zn) and undoped GaMnAs (u-GaMnAs) epilayers, we grew GaMnAs thin films at 200 °C by molecular beam epitaxy (MBE) on GaAs substrates, and they were annealed at temperatures ranging from 220 °C to 380 °C for 100 min in air. These epilayers were characterized by high-resolution X-ray diffraction (XRD), electrical, and magnetic measurements. A maximum resistivity at temperatures T_m close to the Curie temperatures T_c was observed from the measurement of the temperature-dependent resistivity ρ(T) for both the GaMnAs:Zn and the u-GaMnAs samples. We found, however, that the maximum temperature T_m observed for GaMnAs:Zn epilayers increased with increasing annealing temperature, which was different from the result with the u-GaMnAs epilayers. The formation of GaAs:Zn and MnAs or Mn-Zn-As complexes with increasing annealing temperature is most likely responsible for the differences in appearance.     

Crystallization and electrochemical performance of La0.6Sr0.4Co0.2Fe0.8O3 − δ-Ce0.8Gd0.2O1.9 thin film cathodes processed by single solution spray pyrolysis

La_0.6Sr_0.4Co_0.2Fe_0.8O_3 − δ-Ce_0.8Gd_0.2O_1.9 (LSCF-CGO) thin films obtained by spray pyrolysis of a single precursor solution were investigated by XRD, TEM and impedance spectroscopy at annealing temperatures ranging from 500 to 900 °C. Films annealed at 600 °C contained a mixture of amorphous regions and crystalline regions composed of fine crystallites (< 5 nm). Annealing above 600 °C increased the ratio of crystalline to amorphous material, led to the segregation of the films into distinct LSCF and CGO phases, and promoted grain growth. The electrical behavior of the films depended on annealing temperature. At testing temperatures of 400 °C and below, the polarization resistance of films with lower annealing temperatures was larger than the polarization resistance of films with higher annealing temperatures. However, at testing temperatures of 500 °C and above the polarization resistance of films with lower annealing temperatures was equal to or lower than the polarization resistance of films with higher annealing temperatures. This was reflected by the activation energy that decreased with increasing annealing temperature. The varying electrical behavior may be related to microstructural changes that caused bulk diffusion to be the rate-limiting step in films with lower annealing temperatures and oxygen dissociation to be the rate-limiting step in films with higher annealing temperatures.     

Influence of films thickness and structure on the photo-response of ZnO films

ZnO thin films were grown using Successive Ionic Layer Adsorption and Reaction (SILAR) method on glass substrates at room temperature. Annealing temperatures and film thickness effect on the structural, morphological, optical and electrical properties of the films were studied. For this as-deposited films were annealed at 200, 300, 400 and 500 °C for 30 min in oxygen atmosphere. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) studies showed that the films are covered well with glass substrates and have good polycrystalline structure and crystalline levels. The film thickness effect on band gap values was investigated and band gap values were found to be within the range of 3.49-3.19 eV. The annealing temperature and light effect on electrical properties of the films were investigated and it was found that the current increased with increasing light intensity. The resistivity values were found as 10⁵ Ω-cm for as-deposited films from electrical measurements. The resistivity decreased decuple with annealing temperature and decreased centuple with light emission for annealed films.     

Optoelectronic characterization of Au/Ni/n-AlGaN photodiodes after annealing at different temperatures

The optoelectronic characteristics of Ni/Au Schottky photodiodes based on Al_0.35Ga_0.65N were investigated. The transmission of the Ni (50 Å)/Au (50 Å) layer was determined by evaporating it on a quartz substrate. As evaporated, the transmission coefficient in the 200–350 nm wavelength range was found to be 43 to 48%. Annealing at temperatures of up to 400 °C did not influence the transmission coefficient. After annealing at 500 °C, the transmission coefficient increased from 50 to 68% over the 200–350 nm range. The reverse bias current was optimised in terms of annealing temperature and was found to be as low as 1.94×10⁻¹³ A after annealing at 400 °C for a 0.6 mm diameter contact. The Schottky barrier heights increased with annealing temperature reaching as high as 1.46 and 1.89 eV for I–V and C–V measurements, respectively. The quantum efficiency was measured to be 20.5% and the responsivity reached its peak of 0.046 A/W at 275 nm. The cut-off wavelength was 292 nm.     

Solid phase epitaxy of Ge films on CaF2/Si(1 1 1)

At room temperature deposited Ge films (thickness < 3 nm) homogeneously wet CaF₂/Si(1 1 1). The films are crystalline but exhibit granular structure. The grain size decreases with increasing film thickness. The quality of the homogeneous films is improved by annealing up to 200 °C. Ge films break up into islands if higher annealing temperatures are used as demonstrated combining spot profile analysis low energy electron diffraction (SPA-LEED) with auger electron spectroscopy (AES). Annealing up to 600 °C reduces the lateral size of the Ge islands while the surface fraction covered by Ge islands is constant. The CaF₂ film is decomposed if higher annealing temperatures are used. This effect is probably due to the formation of GeF_x complexes which desorb at these temperatures.     

Temperature dependence of the stability of written bits in a magnetic hard-disk medium investigated by magnetic force microscopy

The thermal stability of written bits in a magnetic hard-disk medium has been investigated with a magnetic force microscope (MFM), which was equipped with an in situ heating system capable of heating the medium up to 300 °C. It is shown that both the annealing temperature and the duration have significant effect on the decay of the MFM signal. No signal decay is observed when annealing for 30 min up to temperatures of 200 °C. The MFM signal decays rapidly with increasing temperature, for temperatures over 200 °C. Repeated annealing at 280 °C with a duration below 10 min does not cause any signal decay.     

Effects of the substrate temperature on the properties of CuIn5S8 thin films

Structural, optical and electrical properties of CuIn₅S₈ thin films grown by thermal evaporation have been studied relating the effects of substrate heating conditions of these properties. The CuIn₅S₈ thin films were carried out at substrate temperatures in the temperature range 100-300 °C. The effects of heated substrate on their physico-chemical properties were investigated using X-ray diffraction (XRD), energy-dispersive X-ray spectroscopy (EDX), optical transmission and hot probe method. X-ray diffraction revealed that the films are strong preferred orientation along the (3 1 1) plane upon substrate temperature 200 °C and amorphous for the substrate temperatures below 200 °C. No secondary phases are observed for all the films. The composition is greatly affected by heated substrate. From the optical transmission and reflection, an important absorption coefficient exceeds 10⁵ cm⁻¹ at 800 nm was found. As increasing the substrate temperature, the optical energy band gap decreases from 1.70 eV for the unheated films to 1.25 eV for the deposited films at 300 °C. It was found that CuIn₅S₈ thin film is an n-type semiconductor at 250° C.     

Influence of annealing temperature on the properties of ZnO thin films deposited by thermal evaporation

ZnO thin films were deposited by thermal evaporation of a ZnO powder. The as-deposited films are dark brown, rich zinc and present a low transmittance. Then, these films were annealed in air atmosphere at different temperatures between 100 and 400 °C. Their microstructure and composition were studied using XRD and RBS measurements respectively. By increasing the temperature, it was found that film oxidation starts at 250 °C. XRD peaks related to ZnO appear and peaks related to Zn decrease. At 300 °C, zinc was totally oxidised and the films became totally transparent. The electrical conductivity measurement that were carried out in function of the annealing temperature showed the transition from highly conductive Zn thin film to a lower conductive ZnO thin film. The optical gap (E_g) was deduced from the UV-vis transmittance, and its variation was linked to the formation of ZnO.     

Effect of post annealing temperature on structural and optical properties of ZnCdO thin films deposited by sol–gel method

Ternary ZnCdO thin films oriented along c-axis have been successfully deposited on p-Si (1 0 0) substrates using sol–gel spin coating route. To optimize most suitable annealing temperature for the Zn_1−xCd_xO thin films; these films with selected cadmium content x = 0.10 were treated at annealing temperatures from 300 °C up to 800 °C in oxygen ambient after deposition. The structural and optical properties of deposited thin films have been characterized by X-ray diffraction, energy dispersive spectroscopy, atomic force microscopy, UV–Vis spectroscopy, and photoluminescence spectra. The results show that the obtained films possess high crystallinity with wurtzite structure. The crystallite size, lattice parameters, lattice strain and stress in the deposited films are determined from X-ray diffraction analysis. The band gap energy increased as a function of annealing temperatures as observed from optical reflectance spectra of samples. The presence of Cd in the deposited films is confirmed by energy dispersive spectrum and it is observed that Cd re-evaporate from the lattice with annealing. The photoluminescence measurements as performed at room temperature did not exhibit any luminescence related to oxygen vacancies defects for lower annealing temperatures, as normally displayed by ZnO films. The green yellow luminescence associated to these defects was observed at higher annealing temperatures (≥700 °C).     

Correlation between microstructure and optical properties of nano-crystalline TiO2 thin films prepared by sol-gel dip coating

Titanium dioxide thin films have been prepared from tetrabutyl-orthotitanate solution and methanol as a solvent by sol-gel dip coating technique. TiO₂ thin films prepared using a sol-gel process have been analyzed for different annealing temperatures. Structural properties in terms of crystal structure were investigated by Raman spectroscopy. The surface morphology and composition of the films were investigated by atomic force microscopy (AFM). The optical transmittance and reflectance spectra of TiO₂ thin films deposited on silicon substrate were also determined. Spectroscopic ellipsometry study was used to determine the annealing temperature effect on the optical properties and the optical gap of the TiO₂ thin films. The results show that the TiO₂ thin films crystallize in anatase phase between 400 and 800 °C, and into the anatase-rutile phase at 1000 °C, and further into the rutile phase at 1200 °C. We have found that the films consist of titanium dioxide nano-crystals. The AFM surface morphology results indicate that the particle size increases from 5 to 41 nm by increasing the annealing temperature. The TiO₂ thin films have high transparency in the visible range. For annealing temperatures between 1000 and 1400 °C, the transmittance of the films was reduced significantly in the wavelength range of 300-800 nm due to the change of crystallite phase and composition in the films. We have demonstrated as well the decrease of the optical band gap with the increase of the annealing temperature.     

Comparative study on the effect of annealing treatments on RTL mechanism in natural quartz from different origins

The behaviour of trap centres and luminescence centres has been investigated for fired and unfired natural quartz from bricks and sediments irradiated at 100 Gy and annealed at different temperatures in the range 350-700 °C. The annealing treatment affects thermoluminescence (TL) glow curve as various changes were observed. The higher sensitization occurred for an annealing in the region 550-600 °C. At this annealing temperature, it has been observed the emergence of two peaks arising at 96 and 180 °C. At lower annealing temperatures, these peaks are overlapped by the peaks localized at 90 and 195 °C, respectively. Concerning the fired quartz, the higher sensitization occurred for an annealing in the region 500-550 °C for peak temperature around 200 °C and an unusual desensitization for the peak temperature around 100 °C. The behaviour of the two types of quartz is analyzed regarding to their kinetic parameters and luminescence emission and compared to literature data.     

Influence of annealing temperature on structural and optical properties of ZnO: In thin films prepared by ultrasonic spray technique

Transparent conducting indium doped zinc oxide was deposited on glass substrate by ultrasonic spray method. The In doped ZnO samples with indium concentration of 3 wt.% were deposited at 300, 350 and 400 °C with 2 min of deposition time. The effects of substrate temperature and annealing temperature on the structural, electrical and optical properties were examined. The DRX analyses indicated that In doped ZnO films have polycrystalline nature and hexagonal wurtzite structure with (0 0 2) preferential orientation and the maximum average crystallite size of ZnO: In before and annealed at 500 °C were 45.78 and 55.47 nm at a substrate temperature of 350 °C. The crystallinity of the thin films increased by increasing the substrate temperature up 350 °C, the crystallinity improved after annealing temperature at 500 °C. The film annealed at 500 °C and deposited at 350 °C show lower absorption within the visible wavelength region. The band gap energy increased from E_g = 3.25 to 3.36 eV for without annealing and annealed films at 500 °C, respectively, indicating that the increase in the transition tail width. This is due to the increase in the electrical conductivity of the films after annealing temperature.     

Photoluminescence of thermal-annealed nanocolumnar ZnO thin films grown by electrodeposition

Nanostructured zinc oxide thin films formed by partially oriented hexagonal columns with dimensions of about 100 nm × 300 nm have been prepared by cathodic electrodeposition on conducting glass substrates. After subsequent thermal annealing in air at different temperatures (100-500 °C), structural information on the films was obtained by means of non-resonant Raman spectroscopy. Increasing the annealing temperature leads to a higher degree of crystallinity. The photoluminescence activity of the samples (at low temperature) also improves for increasing annealing temperatures in two ways: increasing the intensity of the near-band edge emission and decreasing the width of the excitonic peak. No emission band in the visible is detected, which attests the high quality of the ZnO nanocolumnar films.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.