Thermal behavior and intermolecular interactions in blends of poly(3‐hydroxybutyrate) and maleated poly(3‐hydroxybutyrate) with chitosan

The thermal behavior and intermolecular interactions of blends of poly(3‐hydroxybutyrate) (PHB) and maleated PHB with chitosan were studied with differential scanning calorimetry, Fourier transform infrared (FTIR), wide‐angle X‐ray diffraction (WAXD), and X‐ray photoelectron spectroscopy (XPS). The differences in the two blend systems with respect to their thermal behavior and intermolecular interactions were investigated. The melting temperatures, melting enthalpies, and crystallinities of the two blend systems gradually decreased as the chitosan content in the blends increased. Compared with that of the PHB component with the same composition, the crystallization of the maleated PHB component was more intensively suppressed by the chitosan component in the blends because of the rigid chitosan molecular chains and the intermolecular hydrogen bonds between the components. FTIR, WAXD, and XPS showed that the intermolecular hydrogen bonds in the blends were caused by the carbonyls of PHB or maleated PHB and chitosan aminos, and their existence depended on the compositions of the blends. The introduction of maleic anhydride groups onto PHB chains promoted intermolecular interactions between the maleated PHB and chitosan components. In addition, the intermolecular interactions disturbed the original crystal structures of the PHB, maleated PHB, and chitosan components; this was further proven by WAXD results. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 35–47, 2005     

Reversible and irreversible heat capacity of poly(trimethylene terephthalate) analyzed by temperature‐modulated differential scanning calorimetry

The heat capacity of poly(trimethylene terephthalate) (PTT) has been analyzed using temperature‐modulated differential scanning calorimetry (TMDSC) and compared with results obtained earlier from adiabatic calorimetry and standard differential scanning calorimetry (DSC). Using quasi‐isothermal TMDSC, the apparent reversing and nonreversing heat capacities were determined from 220 to 540 K, including glass and melting transitions. Truly reversible and time‐dependent irreversible heat effects were separated. The extrapolated vibrational heat capacity of the solid and the total heat capacity of the liquid served as baselines for the analysis. As one approaches the melting region from lower temperature, semicrystalline PTT shows a reversing heat capacity, which is larger than that of the liquid, an observation that is common also for other polymers. This higher heat capacity is interpreted as a reversible surface or bulk melting and crystallization, which does not need to undergo molecular nucleation. Additional time‐dependent, reversing contributions, dominating at temperatures even closer to the melting peak, are linked to reorganization and recrystallization (annealing), while the major melting is fully irreversible (nonreversing contribution). © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 622–631, 2000     

Crystallization and morphology of poly(vinylidene fluoride)/poly(3‐hydroxybutyrate) blends. II. Morphology and crystallization kinetics by time resolved X‐ray scattering

The development of the morphology in poly(vinylidene fluoride)/poly(3‐hydroxybutyrate) (PVDF/PHB) blends upon isothermal and anisothermal crystallization is investigated by time‐resolved small‐ and wide‐angle X‐ray scattering. The components are completely miscible in the melt but crystallize separately; they crystallize stepwise at different temperatures or sequentially with isothermal or anisothermal conditions, respectively. The PVDF crystallizes undisturbed whereas PHB crystallizes in a confined space that is determined by the existing supermolecular structure of the PVDF. The investigations reveal that composition inhomogeneities may initially develop in the remaining melt or in the amorphous phases of the PVDF upon crystallization of that component. The subsequent crystallization of the PHB depends on these heterogeneities and the supermolecular structure of PVDF (dendritically or globularly spherulitic). PHB may form separate spherulites that start to grow from the melt, or it may develop “interlocking spherulites” that start to grow from inside a PVDF spherulite. Occasionally, a large number of PVDF spherulites may be incorporated into PHB interlocking spherulites. The separate PHB spherulites may intrude into the PVDF spherulites upon further growth, which results in “interpenetrating spherulites.” Interlocking and interpenetrating are realized by the growth of separate lamellar stacks (“fibrils”) of the blend components. There is no interlamellar growth. The growth direction of the PHB fibrils follows that of the existing PVDF fibrils. Depending on the distribution of the PHB molecules on the interlamellar and interfibrillar PVDF regions, the lamellar arrangement of the PVDF may contract or expand upon PHB crystallization and the adjacent fibrils of the two components are linked or clearly separated. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 974–985, 2004     

Electrospun fiber mats of poly(3‐hydroxybutyrate), poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate), and their blends

Electrospinning of poly(3‐hydroxybutyrate) (PHB), poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV), and their blends was first carried out in chloroform at 50 °C on a stationary collector. The average diameter of the as‐spun fiber from PHB and PHBV solutions decreased with increasing collection distance and increased with increasing solution concentration and applied electrical potential. In all of the spinning conditions investigated, the average diameter of the as‐spun pure fibers ranged between 1.6 and 8.8 μm. Electrospinning of PHB, PHBV, and their blends was carried out further at a fixed solution concentration of 14% w/v on a homemade rotating cylindrical collector. Well‐aligned, cross‐sectionally round fibers without beads were obtained. The average diameter of the as‐spun pure and blend fibers ranged between 2.3 and 4.0 μm. The as‐spun fiber mats appeared to be more hydrophobic than the corresponding films and much improvement in the tensile strength and the elongation at break was observed for the blend fiber mats over those of the pure fiber ones. Lastly, indirect cytotoxicity evaluation of the as‐spun pure and blend fiber mats with mouse fibroblasts (L929) indicated that these mats posed no threat to the cells. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2923–2933, 2006     

Enthalpy of fusion of poly(3‐hexylthiophene) by differential scanning calorimetry

The enthalpy of fusion for a perfect, infinite poly(3‐hexylthiophene) (P3HT) crystal () must be known to evaluate the absolute crystallinity of P3HT. This value, however, is still ambiguous as different values have been reported using various experimental techniques. Here, we extrapolate the enthalpy of fusion for extended chain crystals of oligomeric P3HT to infinite molecular weight and obtain a value of 42.9 ± 2 J/g employing differential scanning calorimetry with a correction based on grazing incidence small angle X‐ray scattering data. Also, we define the onset of chain folding within P3HT crystallites at a chain length of 5 Kuhn segments. Knowledge of allows calculation of P3HT percent crystallinity in thin films for applications such as organic field effect transistors and solar cells. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 1469–1475     

Temperature‐modulated differential scanning calorimetry studies on the origin of double melting peaks in isothermally melt‐crystallized poly(L‐lactic acid)

In this work, the melting behaviors of nonisothermally and isothermally melt‐crystallized poly(L ‐lactic acid) (PLLA) from the melt were investigated with differential scanning calorimetry (DSC) and temperature‐modulated differential scanning calorimetry (TMDSC). The isothermal melt crystallizations of PLLA at a temperature in the range of 100–110 °C for 120 min or at 110 °C for a time in the range of 10–180 min appeared to exhibit double melting peaks in the DSC heating curves of 10 °C/min. TMDSC analysis revealed that the melting–recrystallization mechanism dominated the formation of the double melting peaks in PLLA samples following melt crystallizations at 110 °C for a shorter time (≤30 min) or at a lower temperature (100, 103, or 105 °C) for 120 min, whereas the double lamellar thickness model dominated the formation of the double melting peaks in those PLLA samples crystallized at a higher temperature (108 or 110 °C) for 120 min or at 110 °C for a longer time (≥45 min). © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 466–474, 2007     

Effect of poly(vinyl alcohol) fine particles as a novel biodegradable nucleating agent on the crystallization of poly(3‐hydroxybutyrate)

The effect of poly(vinyl alcohol)(PVA) fine particles as the nucleating agent on the crystallization behavior of bacterial poly(3‐hydroxybutyrate)(PHB) was studied using differential scanning calorimetry measurements and polarized light microscope observation. The results were compared with the effect of PVA conventionally blended with PHB. The PVA fine particles were found to be able to greatly enhance the crystallization of PHB, while the conventionally blended PVA extremely retarded the crystallization of PHB. The nucleating effect of PVA fine particles is almost comparable to that of the talc powder. Considering the biodegradability and biocompatibility of PVA, the usage of PVA particle as a nucleating agent provides marked benefits over the currently employed nonbiodegradable nucleating agents, such as talc and boron nitride. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44:1813–1820, 2006     

Nonisothermal crystallization and melting behavior of poly(β‐hydroxybutyrate)–Poly(vinyl‐acetate) blends

Nonisothermal crystallization and melting behavior of poly(β‐hydroxybutyrate) (PHB)–poly(vinyl acetate) (PVAc) blends from the melt were investigated by differential scanning calorimetry using various cooling rates. The results show that crystallization of PHB from the melt in the PHB–PVAc blends depends greatly upon cooling rates and blend compositions. For a given composition, the crystallization process begins at higher temperatures when slower scanning rates are used. At a given cooling rate, the presence of PVAc reduces the overall PHB crystallization rate. The Avrami analysis modified by Jeziorny and a new method were used to describe the nonisothermal crystallization process of PHB–PVAc blends very well. The double‐melting phenomenon is found to be caused by crystallization during heating in DSC. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 443–450, 1999     

Effect of aging on fractional crystallization of poly(ethylene oxide) component in poly(ethylene oxide)/poly(3‐hydroxybutyrate) blends

The effect of aging on the fractional crystallization of the poly(ethylene oxide) (PEO) component in the PEO/poly(3‐hydroxybutyrate) (PHB) blend has been investigated. The partial miscibility of the PEO/PHB blends with high PEO molecular weight (M_v = 2.0 × 10⁵ g/mol) was confirmed by differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis. The fractional crystallization behavior of the PEO component in the PEO/PHB blends with low PEO content (not more than 30 wt% of PEO), before and after aging under vacuum at 25 °C for 6 months, were compared by DSC, fourier transform infrared microscopic spectroscopy, small angle X‐ray diffraction, and scanning electron microscopy. It was confirmed that nearly all the PEO components remain trapped within interlamellar regions of PHB for the PEO/PHB blends before aging. Under this condition, the crystallization of PEO is basically induced by much less active heterogeneities or homogeneous nucleation at high supercoolings. While, after the same PEO/PHB samples were stored at 25 °C in vacuum for 6 months, a part of the PEO component was expelled from the interlamellar region of PHB. Under this condition, the expelled PEO forms many separate domains with bigger size and crystallizes at low supercoolings by active heterogeneous nucleation, whereas the crystallization of PEO in the interlamellar region is still mainly induced by less active heterogeneities or homogeneous nucleation at extreme supercoolings. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2665–2676, 2005     

Influence of multiple processing on selected properties of poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate)

The effect of multiple (up to 10 times) injection molding of processed poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate) (P(3,4HB)) on its phase transition temperatures, degree of crystallinity, degradation temperature, mass flow rate, mechanical properties, dynamic mechanical properties, and Charpy's impact strength is presented. The studies have shown that the multiple injection lowers the degree of crystallinity and the thermal stability of P(3,4HB). The mass flow rate values increased with increasing the injection number. It was found that the multiple injections had no substantial effect on the tensile strength up to 10 injection cycles and the tensile strength at break, tensile strain at tensile strength, and tensile strain at break up to 6 injection cycles. The maximum value of storage modulus at 30 °C and impact strength were recorded for sample after 4 cycles of injection, while the values of storage modulus at 120 °C increased with increase of the injection cycles. Copyright © 2015 John Wiley & Sons, Ltd.     

Antibacterial poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate) fibrous membranes containing quaternary ammonium salts

In this study, antimicrobial membranes based on biodegradable material poly(3‐hydroxybutyrate‐co‐4‐hydroxybutyrate) [P(3HB‐4HB)] and quaternary ammonium salts (QASs) by two methods have been performed. Three QASs with varied alkyl chain lengths have been synthesized successfully and characterized by ¹H nuclear magnetic resonance and Fourier transform infrared. The synthesized QASs were blended with P(3HB‐4HB) and electrospun into composite fibrous membranes or casted into conventional membranes. Electrospun fibrous membranes with large surface areas are a superior type of antimicrobial biomaterials, and they exhibit preferable properties than solution casting membranes. Specifically, electrospun fibrous membranes are tougher and can inactivate both Gram‐positive Staphylococcus aureus and Gram‐negative Escherichia coli O157:H7 in a contact time of 30 min, whereas the solution casting membranes cannot. The length of alkyl chain in the quaternary ammonium groups on the modified P(3HB‐4HB) membranes is able to influence the antimicrobial activity. This type of antimicrobial material may have potential applications in biomaterial field. Copyright © 2016 John Wiley & Sons, Ltd.     

Miscibility,crystallization kinetics,and morphology of poly(β‐hydroxybutyrate) and poly(methyl acrylate) blends

The miscibility, spherulite growth kinetics, and morphology of binary blends of poly(β‐hydroxybutyrate) (PHB) and poly(methyl acrylate) (PMA) were studied with differential scanning calorimetry, optical microscopy, and small‐angle X‐ray scattering (SAXS). As the PMA content increases in the blends, the glass‐transition temperature and cold‐crystallization temperature increase, but the melting point decreases. The interaction parameter between PHB and PMA, obtained from an analysis of the equilibrium‐melting‐point depression, is −0.074. The presence of an amorphous PMA component results in a reduction in the rate of spherulite growth of PHB. The radial growth rates of spherulites were analyzed with the Lauritzen–Hoffman model. The spherulites of PHB were volume‐filled, indicating the inclusion of PMA within the spherulites. The long period obtained from SAXS increases with increased PMA content, implying that the amorphous PMA is entrapped in the interlamellar region of PHB during the crystallization process of PHB. All the results presented show that PHB and PMA are miscible in the melt. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1860–1867, 2000     

Compatibility and thermal properties of poly(3‐hydroxybutyrate)/poly(glycidyl methacrylate) blends

Poly(3‐hydroxybutyrate) (PHB)/poly(glycidyl methacrylate) (PGMA) blends were prepared by a solution‐precipitation procedure. The compatibility and thermal decomposition behavior of the PHB/PGMA blends was studied with differential scanning calorimetry, thermogravimetric analysis, and differential thermal analysis (DTA). The blends were immiscible in the as‐blended state, but for the blends with PGMA contents of 50 wt % or more, the compatibility was dramatically changed after 1 min of annealing at 200 °C. In addition, PHB/PGMA blends showed higher thermal stability, as measured by maximum decomposition temperatures and residual weight during thermal degradation. This was probably due to crosslinking reactions of the epoxide groups in the PGMA component with the carboxyl chain ends of PHB fragments during the degradation process, and the occurrence of such reactions can be assigned to the exothermic peaks in the DTA thermograms. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 351–358, 2002     

Synthesis and characterization of poly(β‐hydroxybutyrate) and poly(ϵ‐caprolactone) copolyester by transesterification

To synthesize the copolyester of poly(β‐hydroxybutyrate) (PHB) and poly(?‐caprolactone) (PCL), the transesterification of PHB and PCL was carried out in the liquid phase with stannous octoate as the catalyzer. The effects of reaction conditions on the transesterification, including catalyzer concentration, reaction temperature, and reaction time, were investigated. The results showed that both rising reaction temperature and increasing reaction time were advantageous to the transesterification. The sequence distribution, thermal behavior, and thermal stability of the copolyesters were investigated by ¹³C NMR, Fourier transform infrared spectroscopy, differential scanning calorimetry, wide‐angle X‐ray diffraction, optical microscopy, and thermogravimetric analysis. The transesterification of PHB and PCL was confirmed to produce the block copolymers. With an increasing PCL content in the copolyesters, the thermal behavior of the copolyesters changed evidently. However, the introduction of PCL segments into PHB chains did not affect its crystalline structure. Moreover, thermal stability of the copolyesters was little improved in air as compared with that of pure PHB. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1893–1903, 2002     

Reversible melting of polyethylene extended‐chain crystals detected by temperature‐modulated calorimetry

The melting and crystallization of extended‐chain crystals of polyethylene are analyzed with standard differential scanning calorimetry and temperature‐modulated differential scanning calorimetry. For short‐chain, flexible paraffins and polyethylene fractions up to 10 nm length, fully reversible melting was possible for extended‐chain crystals, as is expected for small molecules in the presence of crystal nuclei. Up to 100 nm length, full eutectic separation occurs with decreasingly reversible melting. The higher‐molar‐mass polymers form solid solution crystals and retain a rapidly decreasing reversible component during their melting that decreases to zero about 1.5 K before the end of melting. An attempt is made to link this reversible melting to the known, detailed morphology and phase diagram of the analyzed sample that was pressure‐crystallized to reach chain extension and practically complete crystallization. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2219–2227, 2002     

Wide‐angle X‐ray diffraction and differential scanning calorimetry study of the crystallization of poly(ethylene naphthalate), poly(butylene naphthalate), and their copolymers

The crystallization behavior of a series of poly(ethylene‐co‐butylene naphthalate) (PEBN) random copolymers was studied. Wide‐angle X‐ray diffraction (WAXD) patterns showed that the crystallization of these copolymers could occur over the entire range of compositions. This resulted in the formation of poly(ethylene naphthalate) or poly(butylene naphthalate) crystals, depending on the composition of the copolymers. Sharp diffraction peaks were observed, except for 50/50 PEBN. Eutectic behavior was also observed. This showed isodimorphic cocrystallization of the PEBN copolymers. The variation of the enthalpy of fusion of the copolymers with the composition was estimated. The isothermal and nonisothermal crystallization kinetics were studied. The crystallization rates were found to decrease as the comonomer unit content increased. The tensile properties were also measured and were found to decrease as the butylene naphthalate content of the copolymers increased. For initially amorphous specimens, orientation was proved by WAXD patterns after drawing, but no crystalline reflections were observed. However, the fast crystallization of drawn specimens occurred when they were heated above the glass‐transition temperature. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 843–860, 2004     

Isothermal crystallization kinetics of poly(3‐hydroxybutyrate)/layered double hydroxide nanocomposites

Poly(3‐hydroxybutyrate) (PHB)/layered double hydroxides (LDHs) nanocomposites were prepared by mixing PHB and poly(ethylene glycol) phosphonates (PEOPAs)‐modified LDH (PMLDH) in chloroform solution. Both X‐ray diffraction data and TEM micrographs of PHB/PMLDH nanocomposites indicate that the PMLDHs are randomly dispersed and exfoliated into the PHB matrix. In this study, the effect of PMLDH on the isothermal crystallization behavior of PHB was investigated using a differential scanning calorimeter (DSC) and polarized optical microscopy. Isothermal crystallization results of PHB/PMLDH nanocomposites show that the addition of 2 wt % PMLDH into PHB induced more heterogeneous nucleation in the crystallization significantly increasing the crystallization rate and reducing their activation energy. By adding more PMLDH into the PHB probably causes more steric hindrance of the diffusion of PHB, reducing the transportation ability of polymer chains during crystallization, thus increasing the activation energy. The correlation among crystallization kinetics, melting behavior and crystalline structure of PHB/PMLDH nanocomposites can also be discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3337–3347, 2006     

Compatibilizing effect of a graft copolymer on bacterial poly(3‐hydroxybutyrate)/poly(methyl methacrylate) blends

Blends of isotactic (natural) poly(3‐hydroxybutyrate) (PHB) and poly(methyl methacrylate) (PMMA) are partially miscible, and PHB in excess of 20 wt % segregates as a partially crystalline pure phase. Copolymers containing atactic PHB chains grafted onto a PMMA backbone are used to compatibilize phase‐separated PHB/PMMA blends. Two poly(methyl methacrylate‐g‐hydroxybutyrate) [P(MMA‐g‐HB)] copolymers with different grafting densities and the same length of the grafted chain have been investigated. The copolymer with higher grafting density, containing 67 mol % hydroxybutyrate units, has a beneficial effect on the mechanical properties of PHB/PMMA blends with 30–50% PHB content, which show a remarkable increase in ductility. The main effect of copolymer addition is the inhibition of PHB crystallization. No compatibilizing effect on PHB/PMMA blends with PHB contents higher than 50% is observed with various amounts of P(MMA‐g‐HB) copolymer. In these blends, the graft copolymer is not able to prevent PHB crystallization, and the ternary PHB/PMMA/P(MMA‐g‐HB) blends remain crystalline and brittle. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1390–1399, 2002     

Melting and crystallization of poly(butylene terephthalate) by temperature‐modulated and superfast calorimetry

Quantitative temperature‐modulated differential scanning calorimetry (TMDSC) and superfast thin‐film chip calorimetry (SFCC) are applied to poly(butylene terephthalate)s (PBT) of different thermal histories. The data are compared with those of earlier measured heat capacities of semicrystalline PBT by adiabatic calorimetry and standard DSC. The solid and liquid heat capacities, which were linked to the vibrational and conformational molecular motion, serve as references for the quantitative analyses. Using TMDSC, the thermodynamic and kinetic responses are separated between glass and melting temperature. The changes in crystallinity are evaluated, along with the mobile–amorphous and rigid–amorphous fractions with glass transitions centered at 314 and 375 K. The SFCC showed a surprising bimodal change in crystallization rates with temperature, which stretches down to 300 K. The earlier reported thermal activity at about 248 K was followed by SFCC and TMDSC and could be shown to be an irreversible endotherm and is not caused by a glass transition and rigid–amorphous fraction, as assumed earlier. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1364–1377, 2006     

Crystallization and morphology of poly(vinylidene fluoride)/poly(3‐hydroxybutyrate) blends. I. Spherulitic morphology and growth by polarized microscopy

The development of the poly(3‐hydroxybutyrate) (PHB) morphology in the presence of already existent poly(vinylidene fluoride) (PVDF) spherulites was studied by two‐stage solidification with two separate crystallization temperatures. PVDF formed irregular dendrites at lower temperatures and regular, banded spherulites at elevated temperatures. The transition temperature of the spherulitic morphology from dendrites to regular, banded spherulites increased with increasing PVDF content. A remarkable amount of PHB was included in the PVDF dendrites, whereas PHB was rejected into the remaining melt from the banded spherulites. When PVDF crystallized as banded spherulites, PHB could consequently crystallize only around them, if at all. In contrast, PHB crystallized with a common growth front, starting from a defined site in the interfibrillar regions of volume‐filling PVDF dendrites. It formed by itself dendritic spherulites that included a large number of PVDF spherulites. For blends with a PHB content of more than 80 wt %, for which the PVDF dendrites were not volume‐filling, PHB first formed regular spherulites. Their growth started from outside the PVDF dendrites but could later interpenetrate them, and this made their own morphology dendritic. These PHB spherulites melted stepwise because the lamellae inside the PVDF dendrites melted at a lower temperature than those from outside. This reflected the regularity of the two fractions of the lamellae because that of those inside the dendrites of PVDF was controlled by the intraspherulitic order of PVDF, whereas that from outside was only controlled by the temperature and the melt composition. The described morphologies developed without mutual nucleating efficiency of the components. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 873–882, 2003