Dielectric and dynamic mechanical relaxation studies on poly(aryl ether ketone)s

The relaxation behavior of four amorphous poly(aryl ether ketone)s was investigated using dielectric relaxation spectroscopy and dynamic mechanical analysis. The temperature dependence of the relaxation times of the glass transition process and the cooperative nature of this process were unaffected by changes in polymer structure. The temperature location of the loss peaks for all polymers progressed smoothly between the low frequency of the mechanical measurements and the higher frequencies of the dielectric probe. Differences were observed in mechanical activation energy and dielectric relaxation strength for one polymer which contained a significant concentration of meta linkages, compared with the para-linked polymers, while relaxation broadness was generally greater in the dynamic mechanical mode. Changes in chemical structure had little effect on the shape, intensity, and location of the β-relaxation peak, the main observation being that the Arrhenius activation energy measured by dynamic mechanical analysis was significantly higher than that calculated from the dielectric data. The dielectric β-relaxation was sensitive to absorbed moisture. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 851–859, 1998     

Dynamics in disordered block copolymers and miscible blends composed of poly(vinyl ethylene) and polyisoprene

We investigated the segmental and terminal relaxation dynamics of a well‐characterized disordered diblock copolymer, poly(isoprene‐b‐vinyl ethylene) (PI‐PVE), and miscible blends of polyisoprene (PI)/poly(vinyl ethylene) (PVE), using dielectric and viscoelastic spectroscopies. Generally, the concentration fluctuation (CF) amplitude of a disordered diblock copolymer is smaller than that of the miscible blend, especially in a length scale longer than the size of the whole block chain. To test whether the difference in the CF amplitudes causes the difference in the segmental relaxation spectra, we compared the shape of the dielectric loss curves between PI‐PVE and PI/PVE with the same composition (PI/PVE ratio = 17:83). However, no appreciable difference was observed, indicating that the CF amplitudes in PI‐PVE and PI/PVE are not so different in the length scale of the segmental motions. We also examined the effect of distinct friction coefficients of the PI and PVE chains on the terminal relaxation dynamics by comparisons of the viscoelastic and dielectric normal mode relaxations in PI‐PVE. The former probes the whole chain motion and the latter probes motions of the PI block. Shift factors (a_T) for the viscoelastic and dielectric relaxations were compared. The dielectric normal mode a_T was found to have weaker temperature dependence than the viscoelastic a_T, which indicates that the friction for the PI block chain is lower than the average friction for the PI‐PVE chain. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 4084–4094, 2004     

Study of the α-relaxation of PVC, EVA and 50/50 EVA70/PVC blend

The dipole dynamics and α-relaxation behaviour of polyvinyl chloride PVC, poly(ethylene-co-vinyl-acetate) EVA₇₀ and blend of them EVA₇₀/PVC have been investigated by differential scanning calorimetry (DSC) and dielectric relaxation spectroscopy (DRS). The differential scanning calorimetry (DSC) thermograms measured on samples show a single glass transition in the analysed temperature range. These three polymers are wholly amorphous and pure PVC and pure EVA₇₀ are miscible in the ratio 1:1. The glass transition temperature T_g decreases significantly with presence of EVA₇₀. Furthermore, the values of apparent activation energies for molecular motions at the α-relaxation and the values of fragility index have also been determined for each sample using Moynihan expression for DSC results and Vogel-Fulcher-Tammann-Hesse (VFTH) form for DRS results. It is shown a large dependence of all the values of these parameters with the content of EVA₇₀. Comparing these three polymers, we found that the more fragile glass forming liquid is the PVC. Fragility decreases drastically with EVA₇₀ content. EVA₇₀ and EVA₇₀/PVC blend exhibit practically the same behaviour. The effect of inter- and intra-molecular interactions on fragility is discussed to explain these variations.     

Evidence of dynamic heterogeneity as obtained from dielectric and brillouin light-scattering studies of poly(n-hexylmethacrylate)

We report dielectric relaxation and Rayleigh-Brillouin spectroscopic measurements on the side chain polymer poly(n-hexylmethacrylate), PHMA (T_g = 268 K), exhibiting a broad glass transition region. The dielectric loss curves can be represented by single Havriliak-Negami functions in the temperature range of 260–450 K. The width of the distribution relaxation function is a decreasing function of temperature up to T = 333 K ≊ 1.24 × T_g and remains virtually constant above that temperature. This is interpreted as marking the merging of the α-process with a slow β-relaxation in agreement with the value of the cooperativity length associated with the α-mode. Hence above that temperature, the relaxation times confirm well to an Arrhenius temperature dependence. The hypersonic dispersion deduced from the Brillouin spectra (210–550 K) surprisingly peaks at temperatures near T_g which bears no relation to the main α-relaxation. This structural relaxation is rather associated with the side hexyl group motion showing striking resemblance with the hypersonic dispersion in molecular liquids. It is conceivable that the observed damping in PHMA is dynamically related to the internal plasticization effect of the hexyl group. © 1996 John Wiley & Sons, Inc.     

Molecular dynamics of amorphous/crystalline polymer blends studied by broadband dielectric spectroscopy

The molecular dynamics of poly(vinyl acetate), PVAc, and poly(hydroxy butyrate), PHB, as an amorphous/crystalline polymer blend has been investigated using broadband dielectric spectroscopy over wide ranges of frequency (10⁻² to 10⁵ Hz), temperature, and blend composition. Two dielectric relaxation processes were detected for pure PHB at high and low frequency ranges at a given constant temperature above the T_g. These two relaxation peaks are related to the α and α′ of the amorphous and rigid amorphous regions in the sample, respectively. The α′-relaxation process was found to be temperature and composition dependent and related to the constrained amorphous region located between adjacent lamellae inside the lamellar stacks. In addition, the α′-relaxation process behaves as a typical glass relaxation process, i.e., originated from the micro-Brownian cooperative reorientation of highly constraints polymeric segments. The α-relaxation process is related to the amorphous regions located between the lamellar crystals stacks. In the PHB/PVAc blends, only one α-relaxation process has been observed for all measured blends located in the temperature ranges between the T_g’s of the pure components. This last finding suggested that the relaxation processes of the two components are coupled together due to the small difference in the T_g’s (ΔT_g = 35 °C) and the favorable thermodynamics interaction between the two polymer components and consequently less dynamic heterogeneity in the blends. The T_g’s of the blends measured by DSC were followed a linear behavior with composition indicating that the two components are miscible over the entire range of composition. The α′-relaxation process was also observed in the blends of rich PHB content up to 30 wt% PHB. The molecular dynamics of α and α′-relaxation processes were found to be greatly influenced by blending, i.e., the dielectric strength, the peak broadness, and the dielectric loss peak maximum were found to be composition dependent. The dielectric measurements also confirmed the slowing down of the crystallization process of PHB in the blends.     

Dielectric relaxation of LC-thermotropic poly(ester imide)s

Two different series of poly(ester imide)s, which are distinguished from each other in the orientation of the ester linkages and show well-differentiated thermotropic behavior, are investigated by means of model calculations and dielectric relaxation spectroscopy. Model calculations show that the orientation of the ester linkages has a strong influence on the rotational energy barriers. The dielectric relaxation spectra of both series shows three relaxation regions in the temperature range between 100 and 400 K that have been identified as the α-, β- and γ-relaxation processes. A difference of about two orders of magnitude between the characteristic rates of the γ-relaxation is the main feature observed in the dielectric response. However, the β-relaxation shows very similar behavior for both series. The differences in the relaxation behavior in the solid state are interpreted on the basis of the rotational barriers deduced from the model calculation results. © 1997 John Wiley & Sons, Inc.     

Dielectric relaxation study of atactic poly(epichlorohydrin)/poly(3-hydroxybutyrate) blends

Binary blends of atactic poly(epichlorohydrin) (aPECH) and poly(3-hydroxybutyrate) (PHB) were investigated as a function of blend composition and crystallization conditions by dielectric relaxation spectroscopy. The quenched samples were found to be miscible in the whole composition range by detecting only one glass transition relaxation, for each composition, which could be closely described by the Gorden-Taylor equation. The cold-crystallized blends displayed two glass transition relaxations at all blend ratios indicating the coexisting of two amorphous populations: a pure aPECH phase dispersed mainly in the interfibrillar zones and a mixed amorphous phase held between crystal lamellae. The interlamellar trapping of aPECH was small and decreases with increasing the overall PHB content in the blend. At high crystallization temperatures the aPECH molecules was found to reside mainly in the interfibrillar regions due to its high mobility relative to the crystal growth rate of PHB. Our results suggest that because the intersegmental interaction in aPECH/PHB blends is weak, the mobility of the amorphous component at a given crystallization temperature decides diluent segregation.     

Effects of the oriented mesophase on the cold crystallization of syndiotactic polystyrene and its blend with poly(2,6‐dimethyl‐1,4‐phenylene oxide)

The effects of molecular orientation on the crystallization and polymorphic behaviors of syndiotactic polystyrene (sPS) and sPS/poly(2,6‐dimethyl‐1,4‐phenylene oxide) (PPO) blends were studied with wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry. The oriented amorphous films of sPS and sPS/PPO blends were crystallized under constraint at crystallization temperatures ranging from 140 to 240°C. The degree of crystallinity was lower in the cold‐crystallized oriented film than in the cold‐crystallized isotropic film. This was in contrast to the case of the cold crystallization of other polymers such as poly(ethylene terephthalate) and isotactic polystyrene, in which the molecular orientation induced crystallization and accelerated crystal growth. It was thought that the oriented mesophase was obtained in drawn films of sPS and that the crystallization of sPS was suppressed in that phase. The WAXD measurements showed that the crystal phase was more ordered in an sPS/PPO blend than in pure sPS under the same annealing conditions. The crystalline order recovered in the cold‐crystallized sPS/PPO blends in comparison with the cold‐crystallized pure sPS because of the decrease in the mesophase content. The crystal forms depended on the crystallization temperature, blend composition, and molecular orientation. Only the α′‐crystalline form was obtained in cold‐crystallized pure sPS, regardless of molecular orientation, whereas α′, α″, and β′ forms coexisted in the cold‐crystallized sPS/PPO blends prepared at higher crystallization temperatures (200–240°C). The β′‐form content was much lower in the oriented sPS/PPO blend than in the isotropic blend sample at the same temperature and composition. It was concluded that the oriented mesophase suppressed the crystallization of the stable β′ form more than that of the metastable α′ and α″ forms during the cold crystallization of sPS/PPO blends. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1665–1675, 2003     

Fundamentals of ionic conductivity relaxation gained from study of procaine hydrochloride and procainamide hydrochloride at ambient and elevated pressure

The pharmaceuticals, procaine hydrochloride and procainamide hydrochloride, are glass-forming as well as ionically conducting materials. We have made dielectric measurements at ambient and elevated pressures to characterize the dynamics of the ion conductivity relaxation in these pharmaceuticals, and calorimetric measurements for the structural relaxation. Perhaps due to their special chemical and physical structures, novel features are found in the ionic conductivity relaxation of these pharmaceuticals. Data of conductivity relaxation in most ionic conductors when represented by the electric loss modulus usually show a single resolved peak in the electric modulus loss M(")(f) spectra. However, in procaine hydrochloride and procainamide hydrochloride we find in addition another resolved loss peak at higher frequencies over a temperature range spanning across T(g). The situation is analogous to many non-ionic glass-formers showing the presence of the structural α-relaxation together with the Johari-Goldstein (JG) β-relaxation. Naturally the analogy leads us to name the slower and faster processes resolved in procaine hydrochloride and procainamide hydrochloride as the primary α-conductivity relaxation and the secondary β-conductivity relaxation, respectively. The analogy of the β-conductivity relaxation in procaine HCl and procainamide HCl with JG β-relaxation in non-ionic glass-formers goes further by the finding that the β-conductivity is strongly related to the α-conductivity relaxation at temperatures above and below T(g). At elevated pressure but compensated by raising temperature to maintain α-conductivity relaxation time constant, the data show invariance of the ratio between the β- and the α-conductivity relaxation times to changes of thermodynamic condition. This property indicates that the β-conductivity relaxation has fundamental importance and is indispensable as the precursor of the α-conductivity relaxation, analogous to the relation found between the Johari-Goldstein β-relaxation and the structural α-relaxation in non-ionic glass-forming systems. The novel features of the ionic conductivity relaxation are brought out by presenting the measurements in terms of the electric modulus or permittivity. If presented in terms of conductivity, the novel features are lost. This warns against insisting that a log-log plot of conductivity vs. frequency is optimal to reveal and interpret the dynamics of ionic conductors.     

A dielectric study of poly(ethylene-co-vinylacetate)–poly(vinyl chloride) blends. I. Miscibility and phase behavior

Measurements of the complex permittivity were used to study miscibility and phase behavior in blends of poly(vinyl chloride) (PVC) with two random ethylene—vinyl acetate (EVA) copolymers containing 45 and 70 wt % of vinyl acetate. The dielectric β relaxation of the pure polymers and blends was followed as a function of temperature and frequency for different blend compositions and thermal treatments. Blends of EVA 70/PVC were found to be miscible for compositions of about 25% EVA 70 and higher. Blends of lower EVA 70 content showed evidence of two-phase behavior. EVA 45/PVC blends were found to be miscible only at the composition extremes; at intermediate compositions these blends were two-phase, partially miscible. Both blend systems showed lower critical solution temperature behavior. Phase separation studies revealed that in the EVA 45/PVC blends, PVC was capable of diffusing into the higher T_g phase at temperatures below the T_g of the upper phase. In the blends, ion transport losses were significant above the loss peak temperatures, and in the two-phase systems, often obscured the upper temperature loss process. It was shown possible, however, to correct the loss curves for this transport contribution.     

All-organic polymer blend dielectrics of poly (arylene ether urea) and polyimide: Toward high energy density and high temperature applications

The development of high-performance dielectric films with high energy density and temperature stability is extremely desired for modern electronics and power systems. Herein, a simple and low-cost approach is proposed to fabricate all-organic blend films prepared from poly (arylene ether urea) (PEEU) and polyimide (PI) via solution casting and thermal imidization process. The incorporation of PEEU in PI matrix significantly improved dielectric breakdown strength and dielectric constant of PI. More precisely, blend film with 15 wt% PEEU exhibited highest energy density 5.14 J/cm³ at 495.65 MV/m, with enhanced dielectric constant of 4.73 and very low dissipation factor of 0.299%. Furthermore, the dielectric properties of the PEEU/PI blend displayed wonderful temperature stability in the range of − 50–+ 250°C, and great frequency stability between 10 and 10⁶ Hz. The blend film also exhibited excellent heat resistance and presented valuable potential in thin film capacitors for high voltage direct current system.     

Influence of Phase Morphology on Molecular Mobility of Poly(propylene)-(ethylene-vinyl acetate) Copolymer Blends

The dynamic mechanical and dielectric behaviours of Polypropylene (PP) and (Ethylene-Vinyl Acetate) Copolymer (EVA) blends are reported as a function of the morphology. For EVA contents lower than 20%, blends show the two-phase morphology characteristic of immiscible blends, with spherical EVA droplets finely dispersed in the PP matrix. After stretching in the molten state, the morphology of EVA fibers is observed. Mechanical Relaxation Spectroscopy display three relaxation processes: the EVA and PP α-relaxations associated to the glass transitions and a β-transition corresponding to a PP crystalline phase relaxation. The PP α-relaxation shifts to higher temperatures when EVA presents a fiber morphology, corresponding to a decrease of PP chain mobility since it is hindered by the reinforcement effect of EVA fibers. Quite different results are obtained by DRS analysis. In blends containing EVA fibers, only one main relaxation associated to the EVA α-transition is observed whereas one additional relaxation can be noticed in the blends containing EVA droplets. This new relaxation might be assigned to interfacial polarization effects, phenomena that are sometimes observed in heterogeneous polymer blends when a low content of one polar component is embedded in a non conductive matrix. In this case, the occurrence of a characteristic interfacial polarization relaxation appears to be correlated to the accessible experimental frequency.     

Relaxation properties of plasticised poly(vinyl chloride) and PVC blends

The temperature-frequency dependence of dielectric parameters for several PVC-plasticizer systems and PVC blends was obtained. Kinetic and activation parameters and α-relaxation spectra were estimated. The increase of the polar group number and size in the plasticizer molecules results in the narrowing of the relaxation spectra and in the increase of inner mobility of PVC segments. It was found for PVC-ABS and PVC-Paraloid blends that all relaxation characteristics depend on the miscibility of components. The results were also confirmed by the cloud point data.     

Vitrification/devitrification phenomena during isothermal and nonisothermal crystallization of poly(aryl–ether–ether–ketone) (PEEK) and PEEK/poly(ether–imide) blends

We have established time–temperature transformation and continuous-heating transformation diagrams for poly(ether–ether–ketone) (PEEK) and PEEK/poly(ether–imide) (PEI) blends, in order to analyze the effects of relaxation control on crystallization. Similar diagrams are widely used in the field of thermosetting resins. Upon crystallization, the glass transition temperature (T_g) of PEEK and PEEK/PEI blends is found to increase significantly. In the case of PEEK, the shift of the α-relaxation is due to the progressive constraining of amorphous regions by nearby crystals. This phenomenon results in the isothermal vitrification of PEEK during its latest crystallization stages for crystallization temperatures near the initial T_g of PEEK. However, vitrification/devitrification effects are found to be of minor importance for anisothermal crystallization, above 0.1°C/min heating rate. In the case of PEEK/PEI blends, amorphous regions are progressively enriched in PEI upon PEEK crystallization. This promotes a shift of the α-relaxation of these regions to higher temperatures, with a consequent vitrification of the material when crystallized below the T_g of PEI. The data obtained for the blends in anisothermal regimes allow one to detect a region in the (temperature/heating rate) plane where crystallization proceeds in the continuously close proximity of the glass transition (dynamic vitrification). These experimental findings are in agreement with simple simulations based on a modified Avrami model coupled with the Fox equation. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 919–930, 1998     

Interchain coupled chain dynamics of poly(ethylene oxide) in blends with poly(methyl methacrylate): coupling model analysis

Quasielastic neutron scattering and molecular dynamics simulation data from poly(ethylene oxide) (PEO)/poly(methyl methacrylate) (PMMA) blends found that for short times the self-dynamics of PEO chain follows the Rouse model, but at longer times past t(c) = 1-2 ns it becomes slower and departs from the Rouse model in dependences on time, momentum transfer, and temperature. To explain the anomalies, others had proposed the random Rouse model (RRM) in which each monomer has different mobility taken from a broad log-normal distribution. Despite the success of the RRM, Diddens et al. [Eur. Phys. Lett. 95, 56003 (2011)] extracted the distribution of friction coefficients from the MD simulations of a PEO/PMMA blend and found that the distribution is much narrower than expected from the RRM. We propose a simpler alternative explanation of the data by utilizing alone the observed crossover of PEO chain dynamics at t(c). The present problem is just a special case of a general property of relaxation in interacting systems, which is the crossover from independent relaxation to coupled many-body relaxation at some t(c) determined by the interaction potential and intermolecular coupling/constraints. The generality is brought out vividly by pointing out that the crossover also had been observed by neutron scattering from entangled chains relaxation in monodisperse homopolymers, and from the segmental α-relaxation of PEO in blends with PMMA. The properties of all the relaxation processes in connection with the crossover are similar, despite the length scales of the relaxation in these systems are widely different.     

Miscibility and surface characterization of a poly(vinylidene fluoride)‐poly(vinyl methyl ketone) blend by inverse gas chromatography

The miscibility of blends of semicrystalline poly(vinylidene fluoride)(PVF₂) and poly(vinyl methyl ketone) (PVMK) along with surface characterization were investigated using the inverse gas chromatography method (IGC), over a range of blend compositions and temperatures. Three chemically different families, alkanes, acetates, and alcohols, were utilized for this study. The values of the PVF₂‐PVMK interaction parameters were found to be slightly positive for most of the solutes used, although some degree of miscibility was found at all compositions. Miscibility was greatest at a 50:50 w/w composition of the blend. The interaction parameters obtained from IGC are in excellent agreement with those obtained using calorimetry on the same blends. The calculated molar heat of sorption of alkanes, acetates, and alcohols into the blend layer reveal the impact of the combination of dispersive and hydrogen bonding forces on the interaction of solutes with the blend's backbone. The dispersive component of the surface energy was found to range from 18.70–64.30 mJ/m² in the temperature range of 82–163 °C. A comparison of the blend's surface energy with that of mercury and other polymers is given. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1155–1166, 2000     

Physical properties of sol-gel derived poly(Vinylidene Fluoride)/Silica hybrid

Poly(vinylidene fluoride) (PVDF) was incorporated in situ with silica by a sol-gel process involving tetraethoxysilane. The mechanical properties of these in situ hybrids were compared with those of PVDF composites mechanically blended with 14-nm diameter fumed silica particles. The ultimate strength of the in situ hybrids was higher than that of the blend composites, since fumed silica particles aggregate and act as mechanically weak points. The thermal analysis, dynamic viscoelastic properties, and dielectric properties were compared. The β-relaxation of PVDF caused by the glass transition was observed at around −40°C in the differential scanning calorimetry (DSC) and the mechanical tan δ curves and at −30°C in the dielectric loss factor (ϵ”) curve. The αc-relaxation due to the molecular motion in the crystalline phase occurred at 61°C in DSC curve, at 100°C in the tan δ curve, and at 80°C in the ϵ” curve. The peak positions of these relaxations did not change, but the peak intensities were decreased with the increase in silica content for both the in situ hybrids and blend composites. The activation energies for PVDF were calculated as 136 kJ/mol for the β-relaxation and 96 kJ/mol for the αc-relaxation. The result that these activation energies did not depend on silica content may indicate the weak interaction between PVDF and silica.     

Segmental and secondary dynamics in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) blends

Broadband dielectric spectroscopy was used to study the segmental (α) and secondary (β) relaxations in hydrogen‐bonded poly(4‐vinylphenol)/poly(methyl methacrylate) (PVPh/PMMA) blends with PVPh concentrations of 20–80% and at temperatures from ?30 to approximately glass‐transition temperature (T_g) + 80 °C. Miscible blends were obtained by solution casting from methyl ethyl ketone solution, as confirmed by single differential scanning calorimetry T_g and single segmental relaxation process for each blend. The β relaxation of PMMA maintains similar characteristics in blends with PVPh, compared with neat PMMA. Its relaxation time and activation energy are nearly the same in all blends. Furthermore, the dielectric relaxation strength of PMMA β process in the blends is proportional to the concentration of PMMA, suggesting that blending and intermolecular hydrogen bonding do not modify the local intramolecular motion. The α process, however, represents the segmental motions of both components and becomes slower with increasing PVPh concentration because of the higher T_g. This leads to well‐defined α and β relaxations in the blends above the corresponding T_g, which cannot be reliably resolved in neat PMMA without ambiguous curve deconvolution. The PMMA β process still follows an Arrhenius temperature dependence above T_g, but with an activation energy larger than that observed below T_g because of increased relaxation amplitude. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3405–3415, 2004     

Immiscibility,upper critical solution temperature,and miscibility in blends of poly(vinyl ether)s with polyacrylics: Effects of pendant groups

Various phase behavior of blends of poly(vinyl ether)s with homologous acrylic polymers (polymethacrylates or polyacrylates) were examined using differential scanning calorimetry, optical microscopy (OM), and Fourier‐transformed infrared spectroscopy. Effects of varying the pendant groups of either of constituent polymers on the phase behavior of the blends were analyzed. A series of interestingly different phase behavior in the blends has been revealed in that as the pendant group in the acrylic polymer series gets longer, polymethacrylate/poly(vinyl methyl ether) (PVME) blends exhibit immiscibility, upper critical solution temperature (UCST), and miscibility, respectively. This study found that the true phase behavior of poly(propyl methacrylate)/PVME [and poly(isopropyl methacrylate)/PVME)] blend systems, though immiscible at ambient, actually displayed a rare UCST upon heating to higher temperatures. Similarly, as the methyl pendant group in PVE is lengthened to ethyl (i.e., PVME replaced by PVEE), phase behavior of its blends with series of polymethacrylates or polyacrylates changes correspondingly. Analyses and quantitative comparisons on four series of blends of PVE/acrylic polymer were performed to thoroughly understand the effects of pendant groups in either polyethers (PVE's) or acrylic polymers on the phase behavior of the blends of these two constituents. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1521–1534, 2007     

A dielectric study of poly(ethylene-co-vinyl acetate)–poly(vinyl chloride) blends. II. Loss curve broadening and correlation parameters

Normalized dielectric loss curves for blends of PVC with an EVA copolymer containing 70% vinyl acetate showed significant broadening with increasing PVC content. In conjunction with phase separation studies it was concluded that increasing loss curve broadness correlated with increasing tendency toward phase separation. Calculation of correlation parameters for the blends revealed differences in intermolecular correlations with blend composition.