The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2

Glasses with the compositions xNa₂O · 10MgO · (90 − x)SiO₂, 10Na₂O · xMgO · (90 − x)SiO₂, 5Na₂O · 15MgO · xAl₂O₃ · (80 − x)SiO₂, xNa₂O · 10MgO · 10Al₂O₃ · (80 − x)SiO₂, 10Na₂O · 10MgO · xAl₂O₃ · (80 − x)SiO₂, 10Na₂O · 5MgO · 10Al₂O₃ · (80 − x)SiO₂ were melted and studied using UV-vis-NIR spectroscopy in the wavenumber range from 5000 to 30 000 cm⁻¹. At [Al₂O₃] > [Na₂O], the UV-cut off is strongly shifted to smaller wavenumbers and the NIR peak at around 10 000 cm⁻¹ attributed to Fe²⁺ in sixfold coordination gets narrower. Furthermore, the intensity of the NIR peak at 5500 cm⁻¹ increases. This is explained by the incorporation of iron in the respective glass structures.     

Effect of P2O5 content in two series of soda lime phosphosilicate glasses on structure and properties - Part II: Physical properties

The effect of the variation in phosphate (P₂O₅) content on the properties of two series of bioactive glasses in the quaternary system SiO₂-Na₂O-CaO-P₂O₅ was studied. The first series (I) was a simple substitution of P₂O₅ for SiO₂ keeping the Na₂O:CaO ratio fixed (1:0.87). The second series (II) was designed to ensure charge neutrality in the orthophosphate (), therefore as P₂O₅ was added the Na₂O and CaO content was varied to provide sufficient Na⁺ and Ca²⁺ cations to charge balance the orthophosphate present. Network connectivity’s of the glasses were calculated, and densities and thermal expansion coefficients predicted using the Appen and Doweidar models, respectively. Theoretical densities were measured using the Archimedes principle. Characteristic temperatures, namely the glass transition temperature, T_g, and crystallization temperatures, T_x, were obtained using differential analysis (DTA). Two crystallization exotherms were observed for both glass series (T_xi and T_xii). Both T_g and T_x decreased with P₂O₅ addition for both series. The working range of the glasses, T_x-T_g was shown to increase to a maximum at around 4 mol% P₂O₅ then decrease at higher P₂O₅ contents for both series. Thermal expansion coefficients were measured using dilatometry increasing with P₂O₅ addition and showed good agreement with the Appen values. Dilatometric softening points, T_s, were also measured, which increased with P₂O₅ addition. X-ray diffraction (XRD) was performed on the glasses to confirm their amorphous nature. The glass containing 9.25 mol% P₂O₅ from series I exhibited well-defined peaks on the XRD trace, indicating the presence of a crystalline phase.     

Effect of P2O5 content in two series of soda lime phosphosilicate glasses on structure and properties - Part I: NMR

The effect of the variation in phosphate (P₂O₅) content on the structure of two series of bioactive glasses in the quaternary system SiO₂-Na₂O-CaO-P₂O₅ was studied. The first series (I) was a simple substitution of P₂O₅ for SiO₂ keeping the Na₂O:CaO ratio fixed (1.00:0.87). The second series was designed to ensure charge neutrality in the orthophosphate , therefore as P₂O₅ was added the Na₂O and CaO content was varied to provide sufficient Na⁺ and Ca²⁺ cations to charge balance the orthophosphate present. The glass network connectivity (NC) was calculated for each glass and a modification for the presence of a separate P₂O₅ phase was included (NC′). ³¹P and ²⁹Si magic-angle-spinning nuclear magnetic resonance (MAS-NMR) spectroscopy was performed on glass series I and II to determine the structural units present and their relation to glass properties. ³¹P MAS-NMR spectra of series I resulted in a broad resonance around 9 ppm corresponding to orthophosphate in an amorphous environment. The 9.25 mol% P₂O₅ glass shown to be partially crystalline by X-ray diffraction was heat treated, and the ³¹P MAS-NMR spectrum showed a sharp peak around 3 ppm corresponding to calcium orthophosphate or sodium pyrophosphate and overlapping broader peaks at 8.5, 10.5 and 14 ppm possibly corresponding to two mixed calcium-sodium orthophosphate phases and amorphous sodium orthophosphate respectively. ³¹P MAS-NMR spectra of series II resulted in a broad resonance around 10.5 ppm corresponding to orthophosphate in an amorphous environment. ²⁹Si MAS-NMR spectra of glasses from series I showed a shift in the resonance peak from around −78 to −86 ppm indicating an increase in Q³ species in the glass and a reduction in Q² with phosphate addition confirming the presence of orthophosphate. The heat treated sample showed a sharp ²⁹Si-NMR resonance at −88 ppm, indicating a crystalline Q² six-membered combeite (Na₂O · 2CaO · 3SiO₂) silicate-type phase, which was confirmed by powder X-ray diffraction. ²⁹Si MAS-NMR spectra of glasses from series II showed no shift in the resonance at around −78 ppm across the series, confirming an orthophosphate environment.     

Anionic structure and elasticity of Na2O-MgO-SiO2 glasses

The structure and elastic properties of a series of xNa₂O · MgO · 4SiO₂ glasses have been studied using both Raman and Brillouin spectroscopy. Relative to Na₂O-SiO₂ glasses, the maximum abundance for phyllosilicate structural units in the present glasses shows a lag of 0.5 units in the number of non-bridging oxygen per silicon atom (NBO/Si). This phenomenon has been attributed to the decrease in the average coordination number of modifying cations due to the presence of Mg²⁺. It has also been found that the decomposition of both metasilicate and disilicate (dimerized SiO₄) anionic structural units in Na₂O-SiO₂ glasses are enhanced by the addition of MgO. However, the presence of Mg²⁺ does not cause a considerable effect on the decomposition of phyllosilicate structural unit. The acoustic data have revealed that both shear and Young’s moduli of the present glasses decrease with increasing NBO/Si (the variation in bulk modulus is reversed, however). The resistance to shear deformation for the anionic structural units in silicate glasses has been found to decrease in the following order: tectosilicate > phyllosilicate > metasilicate > disilicate > orthosilicate. The relative contribution of the various anionic structural units to the bulk modulus of a glass remains to be determined. The ideal mixing model using Makishima-Mackenzie’s relationship for predicting Young’s modulus is not applicable to the present glasses.     

Structural analysis and devitrification of glasses based on the CaO-MgO-SiO2 system with B2O3, Na2O, CaF2 and P2O5 additives

Glasses, whose basic composition was based on the CaO-MgO-SiO₂ system and doped with B₂O₃, P₂O₅, Na₂O, and CaF₂, were prepared by melting at 1400 °C for 1 h. Raman and infrared (IR) spectroscopy revealed that the main structural units in the glass network were predominantly Q¹ and Q² silicate species. The presence of phosphate and borate units in the structure of the glasses was also evident in these spectra. X-ray analysis showed that the investigated glasses devitrified at 750 °C and higher temperatures. The crystalline phases of diopside and wollastonite dominated, but weak peaks, assigned to akermanite and fluorapatite, were also registered in the diffractograms. The presence of B₂O₃, Na₂O, and CaF₂ had a negligible influence on the assemblage of the crystallized phases, but it caused a reduction of crystallization temperature, comparing to similar glasses of the CaO-MgO-SiO₂ system.     

Glasses and glass-ceramics in the oxyfluoride ternary system Pb(PO3)2-WO3-PbF2

Glasses were prepared by the melt-quenching method in the ternary system Pb(PO₃)₂-WO₃-PbF₂ and doped with Er³⁺ in order to prepare luminescent transparent glass-ceramics. This work focused on thermal and structural characterization of tungsten lead-phosphate glasses and crystallization study for preparing transparent glass-ceramics. Thermal properties such as thermal stability and crystallization behavior upon heating were investigated by DSC in function of PbF₂ content. For low PbF₂ concentrations, only one crystallization peak due to Pb₃(PO₄)₂ is observed whereas samples containing more than 15% of PbF₂ present another exothermic event at lower temperatures related with precipitation of PbF₂, Pb₂P₂O₇ and Pb₂OF₂. Structural investigations by Raman spectroscopy suggest that PbF₂ modifies the tungsten-phosphate network through the formation of P―F and P―O―Pb bonds but the average network connectivity remains almost constant. A crystallization study has been performed by DSC to investigate the dominant crystallization mechanisms in these glasses and it has been established that Pb₃(PO₄)₂ is nucleated on the surface whereas PbF₂, Pb₂P₂O₇ and Pb₂OF₂ crystallize dominantly from the glassy bulk. Transparent glass-ceramics containing nanosized PbF₂ crystallites were also prepared by suitable heat-treatment on the glass sample containing 20% of PbF₂ and Raman microscopy of these glass-ceramics supports the crystallization mechanisms determined by DSC.     

Structure and properties of glasses in the MI + M2S + (0.1Ga2S3 + 0.9GeS2), M = Li, Na, K and Cs, system

The structure and properties of glasses in the MI + M₂S + (0.1Ga₂S₃ + 0.9GeS₂), M = Li, Na, K and Cs, system were studied using Raman, IR spectroscopy, DSC and density measurements to help better understand the ionic transport in these glasses. The glass forming ranges of these ternary glasses were compared to those of the binary alkali sulfide and germanium sulfide systems. The more extensive glass forming range in the Na₂S system was used to examine the more extensive changes of structure and properties of these glasses as a function of Na₂S content. As expected, non-bridging sulfurs (NBS) form with the addition of alkali sulfide. Unlike their oxide counterparts, however, the alkali sulfide doped glasses appear to support longer-range super-structural units. For example, evidence that the adamantine-like structure exists in the K₂S and Cs₂S modified glasses is found in the Raman spectra of the glasses. The structural role of the alkali iodide addition was also explored since the addition of alkali iodide helps to improve the conductivity. For most of these glasses, as observed in many other oxide glasses, the added MI dissolves interstitially into the glass structure network without changing the alkali sulfide network structure. In 0.6Na₂S + 0.4(0.1Ga₂S₃ + 0.9GeS₂) glasses, however, the added NaI may affect the glass structure as it causes systematic changes in the frequency of the Ge-S network mode as seen in the Raman spectra.     

Considerations on the structure and physical properties of B2O3-SiO2 and GeO2-SiO2 glasses

Data of density, refractive index and thermal expansion coefficient for B₂O₃-SiO₂ and GeO_2-SiO₂ glasses have been analyzed. The volumes of the structural units are the same found for the vitreous B₂O₃, GeO₂ and SiO₂. The volume of any structural unit is constant over the entire composition region of the glass system. The same has been found for the differential refraction and unit refraction of the structural units in these glasses. Different features are observed for the differential expansion of the structural units. There is a considerable change with composition in the differential expansion of BO₃, GeO₄ and SiO₄ units. The effect is attributed to a change in the asymmetry of vibrations with the number of Si-O-B or Si-O-Ge linkages in the matrix. The thermal expansion coefficient is mainly determined by the contribution of B₂O₃ or GeO₂ in the concerned glasses.     

Physicochemical studies of phosphate based P2O5-Na2O-CaO-TiO2 glasses for biomedical applications

Glasses P₂O₅-Na₂O-CaO-TiO₂ with different TiO₂ contents and fixed P₂O₅ (45 wt%) and CaO (24 wt%) have been prepared employing the normal melting and annealing technique. Measurements such as ultrasonic velocity, attenuation, solubility and pH have been carried out in all the compositions of the glasses. It is interesting to note that the above measured ultrasonic parameters exhibit an abnormal behavior (minimum) at 0.5 wt% of TiO₂ content, beyond which an increase in these parameters with increasing TiO₂ content is observed. The maximum pH values and Ca²⁺ ion release have been observed for the TiO₂ free glass those compositions with and the low TiO₂(?1.0 wt%) content. As the content of the TiO₂ increases, the solubility of the glasses decreases. The observed weight loss reveals two stages of phosphate dissolution kinetics i.e. the first stage, in which the weight loss is proportional to t^1/2, and a second stage in which a linear behavior is observed.     

Physical properties of lead iron phosphate glasses containing Cr2O3

The influence of Cr₂O₃ on glass forming characteristics and physical properties of PbO-Fe₂O₃-P₂O₅ glasses has been investigated by Raman and Mössbauer spectroscopies, X-ray diffraction analysis (XRD), Differential Thermal Analysis (DTA), Scanning Electron Microscopy (SEM) and impedance spectroscopy. Glasses of the general composition xCr₂O₃-(28.3-x)PbO-28.7Fe₂O₃-43.0P₂O₅, 0 ≤ × ≤ 10, (mol%) were prepared by conventional melt-quenching technique. The compositions containing up to 4 mol% Cr₂O₃ formed fully amorphous samples and their Raman spectra show systematic increase in the fraction of orthophosphate Q⁰ units with increasing Cr₂O₃ content and O/P ratio.On the other hand, compositions containing 8 and 10 mol% Cr₂O₃ partially crystallized during cooling and annealing to Fe₇(PO₄)₆, Fe₂Pb₃(PO₄)₄ and Cr₂Pb₃(PO₄)₄. A high tendency for crystallization of these melts is related to the high O/P (> 4) and Fe²⁺/Fe_tot (≈ 0.60) ratios.Electrical conductivity of xCr₂O₃-(28.3-x)PbO-28.7Fe₂O₃-43.0P₂O₅, 0 ≤ × ≤ 10, (mol%) compositions is independent of Cr₂O₃ and controlled entirely by the polaron transfer between Fe²⁺ and Fe³⁺ ions.     

Refractive index-structure correlations in Na2O-Al2O3-SiO2 glasses

The current structural models have been used to analyse the refractive index data of Na₂O-Al₂O₃-SiO₂ glasses (Al₂O₃/Na₂O?1). The SiO₂ content is the sole factor that controls the refractive index. Values could be obtained for the factors with which each structural unit contributes in the refractive index. The content of Al₂O₃ or Na₂O has no effect on the refractive index. The factors (differential refraction) are constant and do not change with composition. They have the same values for Na₂O-SiO₂ glasses. The differential refraction of a structural unit increases linearly with increasing the number of non-bridging oxygen ions. The difference of the contribution to the refractive index from a silicate unit to the next equals to a half of that for AlO₄ tetrahedron. The effect could be attributed to the change in both the concentration and differential refraction of structural units. The obtained factors for the structural units are useful in calculating the refractive index with a high degree of accuracy.     

Structural study of PbO-MoO3-P2O5 glasses by Raman and NMR spectroscopy

Glasses in the ternary system PbO-MoO₃-P₂O₅ were prepared in three compositional series (100 − x)[0.5PbO-0.5P₂O₅]-xMoO₃ (A), 50PbO-yMoO₃-(50 − y)P₂O₅ (B) and (50 − z)PbO-xMoO₃-50P₂O₅ (C) and their structure was studied by Raman and ³¹P NMR spectroscopies. In the compositional series (100 − x)[0.5PbO-0.5P₂O₅]-xMoO₃ homogeneous glasses were prepared in the concentration region of 0-70 mol% MoO₃. Their glass transition temperature increases with increasing MoO₃ content having a maximum at x = 50 mol% MoO₃. ³¹P MAS NMR spectra reveal that in the glass series (A) the incorporation of MoO₃ results in the shortening of phosphate chains and gradual transformation Q² units into Q² and Q⁰ units, prevailing in glasses with a high MoO₃ content. Octahedral structural units MoO₆ dominate in most glass compositions and they are present also in the structure of Pb(MoO₂)₂(PO₄)₂ compound corresponding to the glass composition 50Pb(PO₃)₂-50MoO₃. The analysis of Raman spectra of glasses of the (B) series with a high MoO₃ content showed the transformation of octahedral MoO₆ units into tetrahedral MoO₄ units.     

Deep-UV Raman spectroscopic analysis of structure and dissolution rates of silica-rich sodium borosilicate glasses

As part of ongoing studies to evaluate relationships between structure and rates of dissolution of silicate glasses in aqueous media, sodium borosilicate glasses of composition Na₂O·xB₂O₃·(3 − x)SiO₂, with x ≤ 1 (Na₂O/B₂O₃ ratio ≥ 1), were analyzed using deep-UV Raman spectroscopy. Results were quantified in terms of the fraction of SiO₄ tetrahedra with one non-bridging oxygen (Q³) and then correlated with Na₂O and B₂O₃ content. The Q³ fraction was found to increase with increasing Na₂O content, in agreement with studies on related glasses, and, as long as the value of x was not too high, this contributed to higher rates of dissolution in single pass flow-through testing. In contrast, dissolution rates were less strongly determined by the Q³ fraction when the value of x was near unity, and appeared to grow larger upon further reduction of the Q³ fraction. Results were interpreted to indicate the increasingly important role of network hydrolysis in the glass dissolution mechanism as the BO₄ tetrahedron replaces the Q³ unit as the charge-compensating structure for Na⁺ ions. Finally, the use of deep-UV Raman spectroscopy was found to be advantageous in studying finely powdered glasses in cases where visible Raman spectroscopy suffered from weak Raman scattering and fluorescence interference.     

The comparative structure, properties, and ionic conductivity of LiI + Li2S + GeS2 glasses doped with Ga2S3 and La2S3

The well known and characterized fast ion conducting (FIC) LiI + Li₂S + GeS₂ glass-forming system has been further optimized for higher ionic conductivity and improved thermal and chemical stability required for next generation solid electrolyte applications by doping with Ga₂S₃ and La₂S₃. These trivalent dopants are expected to eliminate terminal and non-bridging sulfur (NBS) anions thereby increasing the network connectivity while at the same time increasing the Li⁺ ion conductivity by creating lower basicity [(Ga or La)S_4/2]⁻ anion sites. Consistent with the finding that the glass-forming range for the Ga₂S₃ doped compositions is larger than that for the La₂S₃ compositions, the addition of Ga₂S₃ is found to eliminate NBS units to create bridging sulfur (BS) units that not only gives an improvement to the thermal stability, but also maintains and in some cases increases the ionic conductivity. The compositions with the highest Ga₂S₃ content showed the highest T_gs of ∼325 °C. The addition of La₂S₃ to the base glasses, by comparison, is found to create NBS by forming high coordination octahedral LaS₆³⁻ sites, but yet still improved the chemical stability of the glass in dry air and retained its high ionic conductivity and thermal stability. Significantly, at comparable concentrations of Li₂S and Ga₂S₃ or La₂S₃, the La₂S₃-doped glasses showed the higher conductivities. The addition of the LiI to the glass compositions not only improved the glass-forming ability of the compositions, but also increased the ionic conductivity glasses. LiI concentrations from 0 to 40 mol% improved the conductivities of the Ga₂S₃ glasses from ∼10⁻⁵ to ∼10⁻³ (Ω cm)⁻¹ and of the La₂S₃ glasses from ∼10⁻⁴ to ∼10⁻³ (Ω cm)⁻¹ at room temperature. A maximum conductivity of ∼10⁻³ (Ω cm)⁻¹ at room temperature was observed for all of the glasses and this value is comparable to some of the best Li ion conductors in a sulfide glass system. Yet these new compositions are markedly more thermally and chemically stable than most Li⁺ ion conducting sulfide glasses. LiI additions decreased the T_gs and T_cs of the glasses, but increased the stability towards crystallization (T_c − T_g).     

Growth and shape control of orthorhombic Fe5(PO4)4(OH)3·2H2O single crystalline dendrites

Orthorhombic Fe₅(PO₄)₄(OH)₃·2H₂O single crystalline dendritic nanostructures have been synthesized by a facile and reproducible hydrothermal method without the aid of any surfactants. The influences of synthetic parameters, such as reaction time, temperature, the amount of H₂O₂ solution, pH values, and types of iron precursors, on the crystal structures and morphologies of the resulting products have been investigated. The formation process of Fe₅(PO₄)₄(OH)₃·2H₂O dendritic nanostructures is time dependent: amorphous FePO₄·nH₂O nanoparticles are formed firstly, and then Fe₅(PO₄)₄(OH)₃·2H₂O dendrites are assembled via a crystallization-orientation attachment process, accompanying a color change from yellow to green. The shapes and sizes of Fe₅(PO₄)₄(OH)₃·2H₂O products can be controlled by adjusting the amount of H₂O₂ solution, pH values, and types of iron precursors in the reaction system.     

Laser-induced crystallization of β′-RE2(MoO4)3 ferroelectrics (RE: Sm, Gd, Dy) in glasses and their surface morphologies

The glasses with the compositions of 21.25RE₂O₃-63.75MoO₃-15B₂O₃ (RE: Sm, Gd, Dy) were prepared and the formation of β′-RE₂(MoO₄)₃ ferroelectrics was confirmed in the crystallized glasses obtained through a conventional crystallization in an electric furnace. The features of the glass structure and crystallization behavior were clarified from measurements of Raman scattering spectra. Continuous-wave Nd:YAG laser with a wavelength of 1064 nm (laser power: 0.6-0.9 W, laser scanning speed: S = 1-16 μm/s) was irradiated to 10.625Sm₂O₃-10.625Gd₂O₃ (or Dy₂O₃)-63.75MoO₃-15B₂O₃ glasses, and the structural modification was induced at the glass surface. At the scanning speed of S = 10 μm/s, crystal lines consisting of β′-Gd_2−xSm_x(MoO₄)₃ or β′-Dy_2−xSm_x(MoO₄)₃ crystals were patterned on the glass surface. It was found that those crystal lines have the surface morphology with periodic bumps. At S = 1 μm/s, it was found that crystal lines consist of the mixture of paraelectric α-Gd_2−xSm_x(MoO₄)₃ and ferroelectric β′-Gd_2−xSm_x(MoO₄)₃ crystals, indicating the phase transformation from the β′ phase to the α phase during laser irradiation. Homogeneous crystal lines with β′-RE₂(MoO₄)₃ ferroelectrics have not been written in this study, but further research is continuing.     

Phase separation and crystallization in the system SiO2-Al2O3-P2O5-B2O3-Na2O glasses

The phase separation and crystallization behavior in the system (80 − X)SiO₂ · X(Al₂O₃ + P₂O₅) · 5B₂O₃ · 15Na₂O (mol%) glasses was investigated. Glasses with X = 20 and 30 phase separated into two phases, one of which is rich in Al₂O₃-P₂O₅-SiO₂ and forms a continuous phase. Glasses containing a larger amount of Al₂O₃-P₂O₅ (X = 40 and 50) readily crystallize and precipitates tridymite type AlPO₄ crystals. It is estimated that the phase separation occurs forming continuous Al₂O₃-P₂O₅-SiO₂ phase at first, and then tridymite type AlPO₄ crystals precipitate and grow in this phase. Highly transparent glass-ceramics comparable to glass can be successfully obtained by controlling heat treatment precisely. The crystal size and percent crystallinity of these transparent glass-ceramics are 20-30 nm and about 50%, respectively.     

Structural analysis of Na2OGa2O3SiO2 glasses by the X-ray diffraction method

The structure of Na₂OGa₂O₃SiO₂ glasses of four different compositions containing up to 45 mol. % Ga₂O₃ has been determined by the X-ray diffraction method. The radial distribution function D(r) obtained indicates that Ga³⁺ ions are in fourfold coordination and GaO₄ tetrahedra are formed in these glasses. The reduced intensity function S·i(S) and radial distribution function D(r) which were calculated based on a structural model for A-25, 0.25(Ga₂O₃)·0.75(Na₂O·2SiO₂)/3 glass agreed well with the observed ones.     

The structure of SiO2-GeO2 glasses: A spectroscopic study

Four glasses of the SiO₂-GeO₂ binary system have been synthesized via a sol-gel route followed by a heat treatment and a quench. Glass structure has been determined by Ge K-edge X-ray absorption spectroscopy (XAS) at low temperature and Raman spectroscopy. These mixed glasses present a continuous random network of interconnected GeO₄ and SiO₄ tetrahedra, with GeO₄ tetrahedra similar to the GeO₄ units in GeO₂ glass and continuous compositional variations from GeO₂-rich regions to SiO₂-rich regions. Such a random mixture is consistent with physical properties of these binary glasses as well as with the chemical dependence of their polyamorphism at high pressure. This EXAFS-derived mean Ge-O-Si angles are close to the Ge-O-Ge mean angle in GeO₂ glass, 134° and 130°, respectively. This misfit with the Si-O-Si angles might explain the ease of formation of isolated and pair defects centers, which are suspected to be at the origin of photo-induced modifications of optical properties in Ge-bearing SiO₂ glasses.     

Phase separation, crystallization and leaching of microporous glass ceramics in the CaO-TiO2-P2O5 system

Microporous glass ceramics belonging to the CaO-TiO₂-P₂O₅ system were prepared with the assumption of a 2:1 mole ratio for β-Ca₃(PO₄)₂:CaTi₄(PO₄)₆, the anticipated crystalline phases in the end product. The glasses formulated according to the above composition were melted and cast onto a steel mold and were crystallized to glass ceramics containing the above phases. Dilatometric/differential thermal analysis (DTA) techniques were utilized to determine the appropriate phase separation-nucleation and crystallization temperatures. The crystalline products and resulting microstructures in various stages of process were determined and observed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). By leaching the resulting glass ceramics in HCl, β-Ca₃(PO₄)₂ was dissolved out leaving a porous skeleton of CaTi₄(PO₄)₆. It was found that the volume porosity, specific surface area and mean pore diameter of microporous glass ceramics can be managed through the proper selection of heat treatment conditions. In the optimized conditions for fabricating glass ceramics of minimum mean pore size the values of 41 ± 4%, 26 ± 3 m²/g and 14.3 ± 2 nm were obtained for porosity, surface area and pore diameter respectively.