Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.     

Spectroscopic investigation and optical characterization of novel highly thulium doped tellurite glasses

In this paper, optical properties of 75TeO₂-20ZnO-5Na₂O host glass doped with concentration of Tm³⁺ up to 10 %mol were studied in order to assess the most suitable rare earth content for short cavity fiber lasers. Raman spectroscopy revealed a change in the glass structure while increasing Tm³⁺ content, similar to the well known addition of alkali ions in a glass. Influence of the fabrication process on the OH⁻ content was determined by FTIR measurements. Refractive index of Tm³⁺ doped tellurite glasses was measured at five different wavelengths ranging from 533 nm to 1533 nm. Lifetime and emission spectra measurements of the Tm³⁺ doped tellurite glasses are reported.     

Sulfur behavior in silicate glasses and melts: Implications for sulfate incorporation in nuclear waste glasses as a function of alkali cation and V2O5 content

The presence of sulfur in radioactive waste to be incorporated in borosilicate glasses entails difficulties mainly due to the relatively low solubility of sulfates in the vitreous phase. In this work a study is presented on the effects of the ratio R = [Na₂O]/[B₂O₃], the type of sulfate added and the addition of V₂O₅ on the incorporation of sulfates in borosilicate glasses. Glass samples were prepared at the laboratory scale (up to 50-100 g) by melting oxide and sulfate powders under air in Pt/Au crucibles. XRF and ICP/AES chemical analysis, SEM/EDS, microprobe WDS and Raman spectroscopy were employed to characterize the fabricated samples. The main experimental results confirm that the incorporation of sulfates in borosilicate glasses is favored by the network depolymerization, which evolves with the ratio R. The addition of V₂O₅ seems to accelerate the kinetics of sulfur incorporation in the glass and, probably, increase the sulfate solubility by modifying the borate network and fostering the formation of voids of shape and size compatible with the sulfur coordination polyhedron in the glassy network. The kinetics of X₂SO₄ incorporation in the glass seems to be slower when X = Cs.     

Structure and lattice dynamics of binary lead silicate glasses investigated by infrared spectroscopy

The polar lattices dynamics of seven binary lead silicate glasses have been studied by infrared spectroscopy. The analysis of the reflectivity spectra with a dielectric function model, based on a modified Gaussian profile, allows a quantitative evaluation of the presence of lead cations within different structural sites. From the role of the lead cations versus the degree of polymerization of the silicate network and the comparison with literature results, we may to give a scenario for explaining the observed structural evolution of the glass matrix and more particularly the drastic change occurring around 45% of lead content. Below this threshold, lead cations act only as modifiers of the silicate network. Above, the glass structure is deeply modified; a lead network involving around 10% of the lead content appears in glasses whose composition is just above the threshold and progressively grows at the expense of the silicate network with the increase of lead content. For high lead content, lead cations can act as modifiers of the silicate network or as network formers. Results also show that the analysis of far infrared measurements combined with the knowledge of the UV edge optical response is very promising to characterize the local disorder around cations in glasses.     

Synthesis and characterization of SnO-containing phosphorous oxynitride glasses

SnO-containing oxynitride phosphate glasses have been obtained by ammonolysis and their structure studied by nuclear magnetic resonance. The nitrided glasses are characterized by tetrahedral units P(O,N)₄ in which nitrogen atoms have substituted both bridging and non-bridging oxygen atoms. The N/O substitution in the anionic network induces important changes in the glass properties such as an increase in the glass transition temperature and a decrease in the coefficient of thermal expansion. ³¹P MAS NMR shows that PO₄, PO₃N and PO₂N₂ units coexist within the vitreous network and their relative proportions are a function of the nitrogen content as well as of the base glass composition. The influence of the different modifiers on the nitridation process is explained through a comparative study of the LiNaSnPON and LiNaPbPON systems. Unlike lead in oxynitride glasses, tin affects the nitridation mechanism by limiting the nitrogen/oxygen substitution in the anionic network, so that the substitution model is assumed to be closer to the one taking place in alkali phosphate glasses LiNaPON.     

Crystallization of monoclinic WO3 in tungstate fluorophosphate glasses

Tungstate fluorophosphate glass compositions with high WO₃ concentration were prepared in the ternary system (80−0.8x)NaPO₃-(20−0.2x)BaF₂-xWO₃ with x = 40,50 and 60 mol%. Transparency decreases as WO₃ concentration increases but can be improved by addition of oxidizing systems such as CeO₂ or Sb₂O₃/NaNO₃. Characterizations by thermal analysis (DSC) point out that an increase in the amount of WO₃ results in a higher glass transition temperature. In addition, such compositions are very stable against devitrification since samples containing 40% and 50% of WO₃ donot even exhibit the expected crystallization event. In these samples, the stability against crystallization decreases with the WO₃ content and vitreous sample containing 60% of WO₃ exhibits an endothermic event around 620 °C due to crystallization of monoclinic WO₃ phase. In these glasses, it was shown that the nucleation stage can be induced by thermal-treatment when external nucleating agents such as Ti or Sb are used. Finally, gold-doped samples exhibit a higher crystallization tendency and monoclinic WO₃ phase can be grown in such glasses.     

Structural characterization of phosphate glasses doped with silver

The present paper reports the influence of silver oxide addition on the local structure of 2P₂O₅ · CaO · 0.05ZnO glass matrix. The glass samples were investigated through several methods: X-ray powder diffraction (XRD), scanning electron microscopy (SEM), infrared absorption (FT-IR) and Raman scattering. The X-ray diffraction patterns confirm the vitreous character of these samples over the explored compositional range and the SEM pictures confirm this information. The phosphate structural units of the network former are assessed from FT-IR and Raman spectra as ultra-, meta-, pyro- and orthophosphate units. A slight structural depolymerization process of these phosphate-based glasses was evidenced for higher silver oxide content. In vitro behavior of the bulk glass sample with the highest silver oxide content was tested by immersion in simulated body fluid (SBF). X-ray diffraction and SEM measurements made on the SBF treated sample revealed growth of a crystalline phase on the surface sample.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Structural investigation of bismuth borate glasses and crystalline phases

Glasses of the system: xBi₂O₃-(100−x)B₂O₃ (x = 20 to 66 mol%) were prepared and characterized by density, DSC, UV-visible absorption and ¹¹B MAS-NMR spectroscopy. Glass molar volume increases while the glass transition temperature decreases with Bi₂O₃ concentration. Densities of some bismuth borate glasses are found to be greater or very close to those of single crystal phases with equal composition. B¹¹ MAS-NMR studies determined that the fraction of tetrahedrally coordinated borons (N₄) is maximum at 42 mol% of Bi₂O₃ and that there is a local maxima in N₄ at Bi₂O₃ concentration of 50 mol%. Glasses containing Bi₂O₃ concentration of 33 mol% and higher show an unusual, intense absorption band just below the optical band gap. Two crystalline phases: Bi₃B₅O₁₂ and Bi₄B₂O₉ were prepared by devitrification of glasses and characterized by X-ray diffraction, FTIR and ¹¹B MAS-NMR studies. Both crystalline phases contained significantly lower N₄ than glasses with equal composition.     

Anionic structure and elasticity of Na2O-MgO-SiO2 glasses

The structure and elastic properties of a series of xNa₂O · MgO · 4SiO₂ glasses have been studied using both Raman and Brillouin spectroscopy. Relative to Na₂O-SiO₂ glasses, the maximum abundance for phyllosilicate structural units in the present glasses shows a lag of 0.5 units in the number of non-bridging oxygen per silicon atom (NBO/Si). This phenomenon has been attributed to the decrease in the average coordination number of modifying cations due to the presence of Mg²⁺. It has also been found that the decomposition of both metasilicate and disilicate (dimerized SiO₄) anionic structural units in Na₂O-SiO₂ glasses are enhanced by the addition of MgO. However, the presence of Mg²⁺ does not cause a considerable effect on the decomposition of phyllosilicate structural unit. The acoustic data have revealed that both shear and Young’s moduli of the present glasses decrease with increasing NBO/Si (the variation in bulk modulus is reversed, however). The resistance to shear deformation for the anionic structural units in silicate glasses has been found to decrease in the following order: tectosilicate > phyllosilicate > metasilicate > disilicate > orthosilicate. The relative contribution of the various anionic structural units to the bulk modulus of a glass remains to be determined. The ideal mixing model using Makishima-Mackenzie’s relationship for predicting Young’s modulus is not applicable to the present glasses.     

Investigation of infrared emission and lifetime in Tm-doped 75TeO2:20ZnO:5Na2O (mol%) glasses: Effect of Ho and Yb co-doping

In this paper we describe fabrication and characterization of rare-earth-doped active tellurite glasses to be used as active laser media for fiber lasers emitting in the 2 μm region. The base composition is (mol%): 75TeO₂-20ZnO-5Na₂O with different concentrations of Tm³⁺, Yb³⁺ and Ho³⁺ as dopants or co-dopants. Optical properties of doped glasses were studied and pumping at 800 nm and at 980 nm were tested in order to compare the efficiency of two pumping mechanisms. Optical characterization carried out on glasses containing only Tm³⁺ ions indicated the optimum concentration of Tm₂O₃ in terms of emission efficiency as 1 wt%. The addition of 5 wt% of Yb₂O₃ to Tm³⁺-doped glasses led to the best results in terms of intensity of fluorescence emission and of lifetime values. Yb and Ho co-doped Tm-tellurite glass was measured in emission.     

Near infrared and blue cooperative emissions in Yb-doped GeO2-PbO glasses

In previous years there has been great interest in new materials for photonic devices operating at infrared (IR) and visible (VIS) regions. We report here near infrared and blue cooperative luminescence properties for Yb³⁺-doped GeO₂-PbO glasses. Luminescence and lifetime measurements in the VIS and near-IR regions were performed to investigate the spectroscopic characteristics of the glasses. Intense emissions around 507 and 1010 nm were observed using 980 and 808 nm excitation, respectively. The VIS lifetimes (∼0.4 ms) are about half of their respective near infrared ones (∼0.8 ms), as expected for materials in which the VIS emission is caused by the cooperative effect. Regarding the IR emission, the glasses exhibited a high absorption cross-section (1.2 × 10⁻²⁰ cm²) at 978 nm and an emission cross-section of 0.6 × 10⁻²⁰ cm², at 1010 nm, with a minimum pump intensity of 2.8 kW/cm². These results suggest this glass composition as a potential material to be used in devices operating in the VIS and IR spectral range, such as 3-D displays and infrared lasers.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.     

Raman amplification in nanoparticles doped glasses

Resonant Raman effects are studied for CdS_xSe_1−x nanoparticles in a silicate glass matrix in order to explore new possibilities of Raman amplification for telecommunication fibers. Nanoparticles with diameters ranging from less than 2 nm up to 6 nm are excited with the 458 nm, 488 nm and 633 nm laser lines corresponding both to resonance and off-resonance conditions. Due to confinement effects the resonance conditions are achieved at a given frequency by varying the size of the nanoparticles. In resonance no enhancement is observed for the silicate glass matrix but the (1LO-CdS), (2LO-CdS), (1LO CdSe + 1 LO CdS) modes are strongly enhanced showing the possibility of resonant Raman amplification of the discrete frequencies of the LO modes and of their overtones.     

Growth of cadmium mercury thiocyanate single crystals using acetone–water mixed solvent and their characterization studies

Cadmium mercury tetrathiocyanate single crystals were grown from acetone–water (4:1) mixed solvent by slow evaporation solution technique. The structure of the grown crystal was confirmed by single-crystal X-ray diffraction analysis. The crystalline perfection of cadmium mercury thiocyanate (CMTC) was ascertained by high-resolution X-ray diffraction (HRXRD) analysis. The presence of functional groups and the coordination of thiocyanate ion in the CMTC compound were confirmed by laser Raman spectroscopy. The optical transparency of CMTC single crystal was studied by UV–vis spectroscopy. Single-shot surface laser damage threshold of CMTC estimated using an Nd-YAG laser of wavelength 1064 nm was found to be 4.59 GW/cm² and second harmonic generation (SHG) output power was estimated through the Kurtz powder method. Dielectric constant and dielectric loss for various frequencies and temperatures were performed on CMTC single crystal.     

Structure and properties of glasses in the MI + M2S + (0.1Ga2S3 + 0.9GeS2), M = Li, Na, K and Cs, system

The structure and properties of glasses in the MI + M₂S + (0.1Ga₂S₃ + 0.9GeS₂), M = Li, Na, K and Cs, system were studied using Raman, IR spectroscopy, DSC and density measurements to help better understand the ionic transport in these glasses. The glass forming ranges of these ternary glasses were compared to those of the binary alkali sulfide and germanium sulfide systems. The more extensive glass forming range in the Na₂S system was used to examine the more extensive changes of structure and properties of these glasses as a function of Na₂S content. As expected, non-bridging sulfurs (NBS) form with the addition of alkali sulfide. Unlike their oxide counterparts, however, the alkali sulfide doped glasses appear to support longer-range super-structural units. For example, evidence that the adamantine-like structure exists in the K₂S and Cs₂S modified glasses is found in the Raman spectra of the glasses. The structural role of the alkali iodide addition was also explored since the addition of alkali iodide helps to improve the conductivity. For most of these glasses, as observed in many other oxide glasses, the added MI dissolves interstitially into the glass structure network without changing the alkali sulfide network structure. In 0.6Na₂S + 0.4(0.1Ga₂S₃ + 0.9GeS₂) glasses, however, the added NaI may affect the glass structure as it causes systematic changes in the frequency of the Ge-S network mode as seen in the Raman spectra.     

Preparation and optical properties of samarium doped sol-gel materials

Transparent crack-free glassy monoliths containing up to 0.2 Sm/Si are prepared at room temperature by sol-gel technique. The sol-gel preparation conditions are: acid catalyzed hydrolysis followed by basic catalyzed gelation and controlled drying. The prepared xerogels are characterized by X-ray diffraction, thermogravimetry with Fourier transforming infrared spectroscopy, scanning electron microscopy and optical spectroscopy. The values of the phenomenological Ω-intensity parameters of Sm(III) ions in the gels are (in 10⁻²⁰ cm²) Ω₂ = 76 ± 16.71, Ω₄ = 3.01 ± 0.21, Ω₆ = 2.99 ± 0.41. The oscillator strengths of the Sm(III) ions in the gels are calculated. The results show a linear concentration dependence of Sm(III) in UV/Vis absorption spectra and formation of a Sm(NO₃)₃ · 6H₂O complex at high samarium concentrations.     

Enthalpy relaxation in hyperquenched glasses of different fragility

The enthalpy relaxation in hyperquenched (HQ) glasses with a wide range of fragilities is studied by performing annealing and differential scanning calorimetric (DSC) experiments. In this work, the enthalpy relaxation behavior of annealed HQ glasses is characterized in terms of the excess heat capacity (C_p,exc) given by the difference between the first and the second DSC measurements on the HQ glasses. The shape of the C_p,exc curves depends on the fragility of the glass system, which implies that during annealing the mechanism of the structural relaxation of the HQ strong systems differs from that of the HQ fragile systems. The details of the fragility dependence of the C_p,exc curves have been discussed in terms of the energy landscape and the structure of the liquids.     

Ab initio calculation of vibrational frequencies of GexPxS1−2x glass

The vibrational frequencies of GeS₄, GeP₄, Ge₂S₆, GeP₃, Ge₃P, Ge₂P₂, P₂S₂, P₃S, P₄S₃, α-P₄S₄, β-P₄S₄, α-P₄S₅, β-P₄S₅, P₄S₇, P₄S₉ and P₄S₁₀ are theoretically computed from the first principles. The Raman frequencies of Ge_xP_xS_1−2x glass are obtained for x varying from 0.05 to 0.019. The computed fundamental frequencies of clusters are compared with those experimentally found. In this way, we are able to identify the vibrating clusters in the real glass. The clusters identified in the real glass are found to be Ge₂P₂, P₄S₃, α-P₄S₄, β-P₄S₄, β-P₄S₅, P₄S₇, P₄S₉, β-P₄S₅, Ge₂S₆, Ge₃P.     

Effect of antimony addition on the thermal and electrical-switching behavior of bulk Se-Te glasses

The thermal properties and electrical-switching behavior of semiconducting chalcogenide Sb_xSe_55−xTe₄₅ (2 ? x ? 9) glasses have been investigated by alternating differential scanning calorimetry and electrical-switching experiments, respectively. The addition of Sb is found to enhance the glass forming tendency and stability as revealed by the decrease in non-reversing enthalpy ΔH_nr, and an increase in the glass-transition width ΔT_g. Further, the glass-transition temperature of Sb_xSe_55−xTe₄₅ glasses, which is a measure of network connectivity, exhibits a subtle increase, suggesting a meager network growth with the addition of Sb. The crystallization temperature is also observed to increase with Sb content. The Sb_xSe_55−xTe₄₅ glasses (2 ? x ? 9) are found to exhibit memory type of electrical switching, which can be attributed to the polymeric nature of network and high devitrifying ability. The metallicity factor has been found to dominate over the network connectivity and rigidity in the compositional dependence of switching voltage, which shows a profound decrease with the addition of Sb.