在永磁体强磁场中Mn1.2Fe0.8P1-xSix系列化合物热磁发电研究

研究了处于永磁体强磁场中Mn_1.2Fe_0.8P_1-xSi_x 系列化合物的热磁发电性能, 采用高性能球磨和固相烧结合成方法制备了Mn_1.2Fe_0.8P_1-xSi_x 系列化合物, 并对该系列化合物的物相结构、磁性和热磁发电性能进行了测量. 结果表明: Mn_1.2Fe_0.8P_0.37Si_0.63和Mn_1.2Fe_0.8P_0.35Si_0.65化合物是具有Fe₂P型六角结构的一级相变软磁性材料, 两者居里温度分别为334 K和348 K, 处于工业余热温区. 根据一级相变磁性材料在居里温度磁化强度发生突变这一特性, 研制热磁发电演示装置, 测量了Mn_1.2Fe_0.8P_0.37Si_0.63和Mn_1.2Fe_0.8P_0.35Si_0.65这两种材料铁磁相变产生感应电流大小与线圈匝数、热磁发电材料质量、表面积、表面上温度梯度的关系. 研究结果表明, Mn_1.2Fe_0.8P_1-xSi_x系列化合物具有很好的热磁发电性能, 有望成为热磁发电候选材料.     

Magnetic properties of the Bi1.95Sr2.05−xLaxCuOy (Bi-2201) superconducting phase

We have investigated the reversible mixed-state magnetization M of three lanthanum substituted Bi_1.95Sr_2.05−xLa_xCuO_y (Bi-2201) ceramic samples having different critical temperatures T_c ranging from 20.0 to 35.5 K. As for the Bi₂Sr₂CaCu₂O_8+δ (Bi-2212) phase, we found that anisotropy of Bi-2201 is large. A manifestation of this anisotropy is the field independent magnetization M^* observed at a temperature T^*. In the framework of the London model, and including thermal fluctuations of vortices, we found for the temperature dependence of the penetration depth λ_ab(T) = λ_ab(0)[1 − (T/T_c0)ⁿ]^−1/2, with n 1.7 and λ_ab (T = 0) 4000 Å. The estimated upper critical fields μ₀H_c2,c are of the order of 10 T. We observe a peculiar negative slope M/T at low temperature and sufficiently high external magnetic field. This feature seems to be a characteristic of the Bi-2201 phase. However, we do not know whether it is associated with the superconducting mixed-state. A small amount of magnetic impurities could also be responsible for this behavior. Finally, the behavior of the reversible magnetization of the Bi-2201 samples investigated, which are situated at the optimal and in the overdoped region, did not indicate any unusual temperature dependence for the upper critical field H_c2,c.     

NMR study of coexistence of ferro- and antiferromagnetism in (Zr1−xNbx)Fe2

The magnetic phase diagram has been investigated in the C14 type (Zr_1−xNb_x)Fe₂ with x0.7 from ⁹³Nb NMR and magnetization measurements. In the compound with x = 0.825 a first order-like transition has been found to occur around 25 K from a canted state with the ferromagnetic moment in the basal plane to a ferromagnetic state with decreasing temperature.     

The order of magnetic phase transition in La(Fe1−xCox)11.4Si1.6 compounds

Magnetic transitions in La(Fe_1−xCo_x)_11.4Si_1.6 compounds with x=0–0.08, have been studied by DC magnetic measurements and Mössbauer spectroscopy. The temperature dependence of the Landau coefficients has been derived by fitting the magnetization, M(μ₀H), using the Landau expansion of the magnetic free energy. For x0.02 there is a strongly first-order magnetic phase transition between ferromagnetic and paramagnetic (F–P) states in zero external field and a metamagnetic transition from paramagnetic to ferromagnetic (P–F) above T_c. Increasing the cobalt content drives the F–P transition towards second order and eliminates the metamagnetic transition.     

Spin fluctuations in weakly itinerant ferromagnets Y(Co1−xAlx)2

The nuclear spin-lattice relaxation rate, 1/T₁, has been measured in weak itinerant ferromagnets Y(Co_1−xAl_x)₂. The temperature and magnetic field dependence of 1/T₁T has been found to be well described by the self-consistent renormalization (SCR) theory of spin fluctuations. The parameters characterizing spin fluctuations in this system were estimated from NMR and magnetic measurements. The temperature dependence of susceptibility calculated from these parameters well reproduces the experimental results.     

多铁材料Bi1-xCaxFeO3的介电、铁磁特性和高温磁相变

采用溶胶凝胶法制备Bi_1-xCa_xFeO₃ (x=0, 0.05, 0.1, 0.15, 0.2)陶瓷样品. X衍射图谱表明所有样品的主衍射峰均与纯相BiFeO₃相符合且具有良好的晶体结构. 随着x的增大, Bi_1-xCa_xFeO₃样品的主衍射峰由双峰(104)与(110) 逐渐重叠为单峰(110), 当x ≥0.15时, 样品呈现正方晶系结构; 扫描电镜形貌分析可知, 晶粒由原来的0.5 μm逐渐增大到2 μm. Bi_1-xCa_xFeO₃样品介电常数和介电损耗随着x 的增加先增大而后减小. 当f=1 kHz, Bi_0.9Ca_0.1FeO₃ 的介电常数达到最大值, 是BiFeO₃的7.5倍, 而Bi_0.8Ca_0.2FeO₃的介电常数达到最小值, 仅仅是BiFeO₃的十分之一. Bi_1-xCa_xFeO₃样品所呈现的介电特性是由偶极子取向极化和空间电荷限制电流两种极化机理共同作用的结果. 随着Ca²⁺ 的引入, BiFeO₃ 样品的铁磁性显著提高. X射线光电子能谱图表明Fe²⁺和Fe³⁺ 共存于Bi_1-xCa_xFeO₃ 样品中, Fe²⁺/Fe³⁺比例随着Ca²⁺ 掺杂量的增加而增大, 证明Ca²⁺掺杂增加了Fe²⁺的含量, 增强BiFeO₃的铁磁特性. 从M-T曲线观察到BiFeO₃样品在878 K附近发生铁磁相变, 示差扫描量热法测试再次证明BiFeO₃ 在878 K发生相变. Ca²⁺掺杂使BiFeO₃样品的T_N略有变化而T_M基本不变, 其主要原因是Fe-O-Fe反铁磁超交换作用的强弱和磁结构相对稳定.     

Harmonic generation in TlBa2Ca3Cu4Oy superconductor

We have studied harmonic generation in the magnetic response of bulk samples of the ceramic superconductor TlBa₂Ca₃Cu₄O_y. Dependence of the odd and even harmonics of magnetization on the DC magnetic field, amplitude of the AC magnetic field and temperature was investigate experimentally. We have used a critical state model recently developed by Müller et al. to calculate the full harmonic response. At fixed temperature, the dependence of the odd order harmonic response on the amplitude of the AC magnetic field H_m shows an unambiguous crossover from an H²_m behaviour (Bean-like) at small amplitudes to an H³_m behaviour for larger H_m, in quantitative agreement with the modified critical state model.     

Ferromagnetic Zr1−xMnxCo2 laves phase compounds

Structure and magnetic properties of the Zr_1−xMn_xCo_2+δ alloys were studied for 0 x <0.7, δ=0, 0.45. The cubic C15 Laves phase structure shows Mn solubility up to x≈0.4. The other Laves phase with the hexagonal C36 structure found for x0.5 apparently has a small region of Mn solubility in the vicinity of Zr_0.4Mn_0.6Co₂. Though the parent Mn-free compounds are known to be paramagnetic, the Mn-substituted alloys show ferromagnetic behavior with the Curie temperatures up to 625 K and the room-temperature saturation magnetization of about 100 emu/g. The onset of ferromagnetism with the Mn substitution for Zr may be caused by polarization of itinerant 3d electrons, like it was earlier supposed for the off-stoichiometric ZrCo_2+δ. The universal composition dependencies of the intrinsic magnetic properties for different δ can be obtained, if plotted against the amount of zirconium atoms missing in its sublattice. The room-temperature anisotropy with the noticeable anisotropy field of 24 kOe and the 1 1 0 easy magnetization direction laying in a basal plane was found in the hexagonal Zr_0.5Mn_0.5Co₂.     

Magnetic properties of the pyrite type FexCo1−x−yNiyS2 system

The magnetic phase diagram of the Fe_xCo_1−x−yNi_yS₂ system was determined. Ferromagnetic (F)-, antiferromagnetic (AF )- and paramagnetic (P) phases were found. In the triangular diagram, the F-phase appears along the CoS₂-FeS₂ line, the AF-phase around NiS₂ and the P-phase between the F- and AF-phases. Discussions are given on the F-phase.     

Magnetic behavior of 3d dopants in superconducting REBa2Cu3−xFexO7+δ (RE=Dy, Er)

Mössbauer studies on ⁵⁷Fe-doped superconducting REBa₂Cu₃O_7+δ (RE=Er, Dy) were made as a function of temperature for x=0.15 and 0.30. The magnetic behavior of the 3d dopants, which mainly occupy Cu(1) sites, undergoes antiferromagnetic ordering which is coexistent with superconductivity at low temperature. The dimensionality of the magnetic interaction changes from 2D to 3D when the rare earth changes from Er to Dy. the line-widths of the Mössbauer subspectra are characteristic of magnetic fluctuation behavior in the vicinity of a phase transition. Combining these results with those of Fe-doped Y-123 (pseudo 1D) and Gd (3D), the magnitude of the rare earth moments appears to be strongly correlated with the dimensionality of the magnetic interaction of Fe dopants in these compounds. However, the Mössbauer spectrum for ¹⁵⁵Gd in GdBa₂Cu_2.85Fe_0.15O_7+δ (T_{N(Fe) 14 K}) shows no magnetic order at 4.9 K.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part II: Al NMR investigation and proposal of clustering process

A ²⁷Al nuclear magnetic resonance (NMR) investigation at room temperature of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is carried out. Two different types of aluminium ions are identified and their ratio is determined as a function of x. A clustering process based on the formation of column clusters, more and more extended when x increases, is proposed on the basis of results issued from the ¹⁹F (Part I) and ²⁷Al NMR investigations.     

(Fe1-xCox)3BO5纳米棒磁性的研究

本文采用高温有机溶剂法制备了(Fe_1-xCo_x)₃BO₅纳米棒, 通过控制反应物中乙酰丙酮钴的含量合成了不同Co含量的(Fe_1-xCo_x)₃BO₅. 利用高分辨透射电子显微镜(HRTEM)、超导量子干涉磁强计(SQUID)对其形貌和磁性能进行了表征. 高分辨透射电子显微镜结果表明制备出的纳米(Fe_1-xCo_x)₃BO₅为多晶棒状, 且具有多折孪晶结构; 磁性测量的结果表明,(Fe_1-xCo_x)₃BO₅纳米棒在室温下表现出铁磁性, 随着Co含量的增加, 纳米棒的铁磁性逐渐增加, 该纳米棒有望用来研究生物大分子的机械性能.     

The static and dynamic lattice effects in La1−xCaxMnO3

The structural and magnetic behavior of the perovskite insulator La_0.9Ca_0.1MnO₃ were studied as a function of temperature from 15 to 300 K by neutron powder diffraction. Although this compound shows an anomalous response of the lattice parameters around T_c (150 K), the behavior of the oxygen/manganese Debye-Waller factors is in clear contrast to its “colossal magnetoresistance” (CMR) counterpart La_0.65Ca_0.35MnO₃. We speculate that the difference is intimately associated with the metal-insulator transition in the latter compound.     

Positive linear magnetoresistance in Fex–C1−x composites

A large positive magnetoresistance (MR) has been found in micro-sized Fe_x–C_1−x composites. At a magnetic field of 5 T, the Fe_0.2–C_0.8 composite has the largest MR, 53.8% and 190% at room temperature and at 5 K, respectively. The magnetic field dependence of the MR can be described approximately as MR∝Bⁿ, and the value of exponent n is determined by the Fe weight concentration and temperature, ranging from 1/4 to 6/4. It appears that Fe_x–C_1−x has a linear field dependence of the positive MR at different temperatures. The possible mechanism for the positive MR is discussed.     

强自旋轨道耦合化合物Sr2-xLaxIrO4的掺杂和拉曼谱学

利用固相反应法成功制备了Sr_2-xLa_xIrO₄系列掺杂样品, 并详细研究了样品晶体结构随掺杂的演变. 拉曼散射峰向高频移动和X射线衍射谱的结构精修数据发现随着掺杂量的增加, c轴晶格常数减小, 顶角Ir–O1键键长随之减小, 表明掺杂导致晶格收缩, 而且IrO₆八面体畸变程度减弱. 变温拉曼散射谱显示随着温度降低也出现蓝移现象, 且与顶角氧相关的拉曼振动模式的蓝移在110 K附近出现明显跳变, 表明在该温度附近出现了结构变化和磁性质转变.     

Short-range order and F ion diffusion inside the Pb1 − xAlxF2 + x solid solution Part I: F-NMR investigation

A ¹⁹F-NMR investigation of the Pb_{1 − x}Al_xF_{2 + x} (0 ≤ x ≤ 0.12) solid solution and of the ordered Pb₉Al₂F₂₄ phase is undertaken as a function of temperature. Several F⁻ ion groups become progressively mobile at the NMR time scale at increasing temperature, the first, (F_i)_pb and (F_n)_pb, are located in the surroundings of Pb²⁺ cations, the second ones, (F_rd)_AI and (F_ra)_Al, in that of Al³⁺ cations. Four types of fluoride ions are distinguished in the ¹⁹F-NMR spectra of rigid lattice at low temperature (T = 175 K) and the distribution of fluoride ions among the four sites is determined by deconvolution of the spectra registered. The sites occupied by the (F_n)_pb anions are identified with the normal anionic sites of the fluorite network, the others with different interstitial sites.     

A Raman study of the structural properties of YBa2(Cu1 − xFex)3Oy

The effects of Fe-substitution of YBa₂Cu₃O_y have been investigated by means of Raman scattering, X-ray diffraction, resistivity and susceptibility measurements. A series of samples of YBa₂(Cu_{1 − x}Fe_x)₃O_y with different dopant concentration (0 x 0.15) has been prepared in two batches, the second set having undergone twice the heat and mechanical treatment used to produce the first batch. Considerable improvement in the superconducting transition temperature, T_c, is obtained upon reprocessing. A phase transformation from orthorhombic to tetragonal symmetry is observed for x=0.05 from the X-ray measurements in agreement with previous work. Using a micro-Raman technique, all five A_g vibrational modes have been measured and their dependence on Fe-concentration is analyzed. There are indications that iron substitutes for copper at both sites and that the structure is a mixture of orthorhombic and tetragonal microdomains for all x.     

Synthesis and characterization of the Aurivillius phases Bi2 − xPbxSr1 − xNdxNb2O9

The n = 2 Aurivillius phase Bi_{2 − x}Pb_xSr_{1 − x}Nd₂O₉ was successfully synthesized as a ceramic material over the whole range of simultaneous, charge compensated substitution x = 0–1.0. Structural investigations were performed by Rietveld refinement applying different space groups Fmmm and A2₁am, and additionally by X-ray absorption spectroscopy (EXAFS) on the Nd L_III-edge, confirming the accommodation of Nd on the atomic sites of Sr, which implies the substitution of Bi³⁺ by the isoelectronic Pb²⁺. The ferroelectric transition temperature T_c = 270 °C of the substituted powders with x = 0.4 and 1.0 is distinctly reduced compared to the unsubstituted sample with T_c = 450 °C. In temperature resolved powder X-ray diffraction patterns no structural phase transition could be detected.     

Phase formation and superconductivity in REBaSrCu3−x(PO4)xOy (0 ≤ x ≤ 0.3)

Oxy-anion (PO₄³⁻) substituted phases of the composition REBaSrCu_2.8(PO₄)_0.2O_y have been synthesized. Single phase formation is achieved only for the larger rare earths (La → Ho and Y) and all the phases crystallize in the tetragonal 123 structure. IR studies confirm the presence of a phosphate group in the structure. The total oxygen content (including that associated with the oxy-anion PO₄³⁻) has been found to be in the range 7.01 to 7.10 per formula unit. Except for RE = La, Nd, Yb and Lu, all the phases exhibit superconductivity and the T_c,zero values vary from 18 to 38 K. The T_c,zero increases with decreasing size of RE³⁺. ErBaSrCu₃O₇ is multiphasic and single phase formation is achieved for the first time by phosphate substitution at the copper site. Single phase formation is encountered for x = 0.10 and 0.15 with T_c,zero values of 54 and 37 K respectively.     

Magnetic behavior of Pr1 − xMxCo5 compounds (M = Ti, Zr and Hf)

Magnetic characteristics of Ti-, Zr- and Hf-substituted PrCo₅ alloys have been studied over the temperature range from 77 to 300 K and for applied fields up to 20 kOe. It is established that Ti, Zr and Hf substitute for Pr. Single-phase materials are formed for all values of x up to 0.2 in the system Pr_1−xZr_xCo₅ but for x only up to 0.1 for Pr_1−xTi_x Co₅ and Pr_1−xHfxCo₅ alloys. Larger amounts of Zr can be substituted if the material is made hyperstoichiometric in Co, e.g., Pr_0.7Zr_0.3Co_5.5. All the alloys show a decrease in magnetic moment and an increase in Curie temperature as x increases. Anisotropy fields decrease as x increases at 295 K. Anomalous behavior is observed at 77 K, suggested that these ternary alloys may have a cone structure at this temperature.