Effect of Al2O3 on phase separation and crystallization in ZnO---Al2O3---B2O3---SiO2 glasses

The effect of alumina on the phase separation and the crystallization of the glasses of composition (mol%) 18ZnO·30B₂O₃·52SiO₂ and O-40 Al₂O₃ was studied using an electron microscope and IR spectroscopy. The main crystalline phase appears in the microphase for which the compositions are not nearer to the crystal stoichiometry than the mean. The addition of Al₂O₃ suppresses the immiscibility but enhances the crystallizability.     

Toughened glass-ceramics containing ZrO2 and Al2O3 prepared by the sol-gel process from metal alkoxides

Glasses of compositions 5ZrO₂·5SiO₂(ZS), 5ZrO₂·Al₂O₃·4SiO₂(ZAS) and 5 5ZrO₂·0.5Al₂O₃·0.5Na₂O·4SiO₂(ZANS) were prepared by the sol-gel process from metal alkoxides and sintered to make glass-ceramics. Tetragonal ZrO₂ was precipitated by heat treatment at 900 to 1300°C. The activation energy for tetragonal ZrO₂ crystal growth was extremely high in Al₂O₃ containing glasses. ZAS and ZS were sintered to the near theoretical densities above 1200°C, at which the predominant phase was tetragonal ZrO₂. On the other hand, for ZANS, high densification was not attained owing to the large pores enclosed by the glass phase. Strength and fracture toughness increased with the densification and the crystal growth of tetragonal ZrO₂, reaching 450 MPa and 9 MN/m^1.5, respectively.     

Surface crystallization of rare-earth aluminosilicate glasses

Surface crystallization in a rare-earth aluminosilicate glass (Nd₂O₃–Al₂O₃–SiO₂–TiO₂) was studied using an isothermal method and the crystal growth rate of the glasses was evaluated as a function of the composition. For measuring the surface crystal growth rate, two different methods: measurement of the crystal layer in the longitudinal and lateral growth direction. It was found that crystallization proceeded by surface crystallization only and TiO₂ did not act as a nucleating agent. The growth rate was strongly dependent on the viscosity of glass and agreed with prediction from the Preston model using the known viscosity and melting temperature. As the Si/Nd and Si/Al ratios decreased, the crystal growth rate increased. TiO₂ and Nd₂O₃ played the role of network modifier, which decreased the viscosity of the glass, facilitating crystallization of the rare-earth aluminosilicate glass.     

An infrared study of crystallization in sodium-disilicate glasses containing iron oxides

The infrared absorption spectra of sodium-disilicate glasses containing various amounts of Fe₂O₃ ([Na₂O · 2 SiO₂]_1−x [Fe₂O₃]_x, where X = 0.05, 0.1 and 0.2) were investigated in the wavenumber range from 200–2000 cm⁻¹. The addition of Fe₂O₃ to the sodium-disilicate glass does not seem to introduce any new absorption band as compared with the spectrum of a pure sodium-disilicate glass; nevertheless, a general shift of the existing absorption bands toward lower wavenumbers is observed. The amount of shift is, in fact, proportional to the content of Fe₂O₃ in the glass. This observation is consistent with the recently proposed structural model for the bonding of Fe³⁺ ions in the iron-sodium-silicate glass system.

Annealing of 20 mol% iron oxide glasses at 550 and 580°C produced an extra sharp infrared absorption peak at about 610 cm⁻¹ wavenumber. This new peak is believed to be related to the crystallized particles of the glass as concluded from both a scanning electron micrograph and an electron diffraction pattern.     

Internal friction in vanadium-phosphate glasses doped with Na2O

The internal friction of _xNa₂O·(0.5−x)V₂O₅·O.5P₂O₅(x = 0.025–0.3) glasses was studied using the low-frequency torsion pendulum technique. The temperature spectrum of internal friction reveals three maxima. Maximum 1, the so-called “electron” maximum, is the same as observed in binary vanadium-phosphate glasses. The origin of maximum 2 can be attributed to ion migration. Maximum 3 appears for glasses containing more than 10 mol.% Na₂O and is probably connected with sodium-proton interactions.     

Nuclear magnetic resonance studies of alkaline earth phosphosilicate and aluminoborosilicate glasses

The ¹¹B, ²⁷Al, ²⁹Si and ³¹P magic angle spinning (MAS) NMR spectra of MO–P₂O₅, MO–SiO₂–P₂O₅ and MO(M^′₂O)–SiO₂–Al₂O₃–B₂O₃ (M=Mg, Ca, Sr and Ba, M^′=Na) glasses were examined. In binary MO–P₂O₅ (M=Ca and Mg) glasses, the distributions of the phosphate sites, P(Q_n), can be expressed by a theoretical prediction that P₂O₅ reacts quantitatively with MO. In the ternary 0.30MO–0.05SiO₂–0.65P₂O₅ glasses, the 6-coordinated silicon sites were detected, whose population increases in the order of MgOxCaO–0.05SiO₂–(0.95−x)P₂O₅ glasses, its population increases with an increase in f (=([P₂O₅]−[MO]−[B₂O₃]−[Na₂O])/[SiO₂]) and has maximum at f=9. The signal due to the 5-coordinated silicon atoms is also observed when x is smaller than 0.45. When three network-forming oxides such as SiO₂, Al₂O₃ and B₂O₃ coexist, Al₂O₃ reacts preferably with MO. The populations of 4-coordinated boron atoms, N₄, are expressed well with r/(1−r), where r=([Na₂O]−[Al₂O₃])/([Na₂O]−[Al₂O₃]+[B₂O₃]). The correlation of the Raman signal at 1210 and 1350 cm⁻¹ with the NMR signal of Si(Q₆) at −215 ppm is also seen.     

Structure and Raman spectra of glasses containing several glass-forming oxides and no glass-modifying oxide

Binary glasses containing no modifying oxides, such as SiO₂---GeO₂, SiO₂---B₂O₃, SiO₂---P₂O₅, GeO₂---B₂O₃, Al₂O₃---P₂O₅ and ternary glasses SiO₂---GeO₂---P₂O₅, Al₂O₃---B₂O₃---P₂O₅, B₂O₃---SiO₂---P₂O₅, Al₂O₃---ZrO₂---P₂O₅ have been prepared by melting and CVD methods. The Raman spectra have also been measured. Structural characteristics of SiO₂, GeO₂, B₂O₃, P₂O₅ in different glass systems are analysed. There exist coordination number changes in B₂O₃- and GeO₂-containing glasses and linkage changes between tetrahedra (SiO₄) and (PO₄) in SiO₂ and P₂O₅ containing glasses. The structure of Al₂O₃ containing glasses is homogeneous and the structure of B₂O₃ containing glasses is inhomogeneous. These experimental results are in coincidence with the X-ray small angle scattering analysis.     

The effect of MgO on the thermodynamics of the Fe/Fe-redox equilibrium and the incorporation of iron in soda-magnesia-aluminosilicate melts

Melts with the basic compositions 10Na₂O · 10MgO · xAl₂O₃ · (80−x)SiO₂ (x=0, 5, 10, 15 and 20), 10Na₂O · xMgO · 10Al₂O₃ · (80−x)SiO₂ (x=5, 10, 15 and 20) and xNa₂O · 10MgO · 10Al₂O₃ · (80−x)SiO₂ (x=5, 10 and 15) all doped with 0.25 mol% Fe₂O₃ were studied using square-wave voltammetry. The temperatures applied were in the range of 1000–1600 °C. The square-wave voltammograms recorded show peaks caused by the reduction of Fe³⁺ to Fe²⁺. The attributed peak potentials measured decreased linearly with decreasing temperatures. Increasing the MgO-concentration led to more negative peak potentials. Introducing alumina in the melt first resulted in less negative peak potentials. If the molar Al₂O₃-concentration is equal to that of Na₂O (=10 mol%) the peak potentials are least negative. Further increase of the Al₂O₃-concentration led to more negative peak potentials. The variation of the Na₂O-concentration led to a maximum in the peak potentials at an Na₂O-concentration of 10 mol%. An empirical formula which allows the calculation of standard potentials from the chemical composition is proposed. Furthermore, a structural explanation for the effect of the chemical composition is given. Especially, the incorporation of Al₂O₃ as AlO₄⁻-tetrahedra at [Al₂O₃] < [Na₂O] and as network modifier at larger concentrations was structurally explained by the similarities of Fe²⁺ and Mg²⁺, with respect to cation radii and metal–oxygen bond lengths.     

Raman spectrum studies of the glasses in the system Na2O---Al2O3---P2O5

Raman spectra of ternary sodium aluminosphosphate glasses indicate that for glasses with Al₂O₃/P₂O₅<0.63, the glass network is mainly built up of (PO₃)_n^n- chains and rings or different kinds of phosphate groups and AlO₄ tetrahedra; for glasses with Al₂O₃/P₂O₅>0.63, the glass network is mainly built up of AlPO₄ groups.     

Precipitation of In2O3 nano-crystallites from glasses in the system Na2O/B2O3/Al2O3/In2O3

Glasses in the system Na₂O/B₂O₃/Al₂O₃/In₂O₃ were melted and subsequently tempered in the range from 500 to 700 °C. Depending on the chemical composition, various crystalline phases were observed. From samples without Al₂O₃, In₂O₃ could not be crystallized from homogeneous glasses, because either spontaneous In₂O₃ crystallization occurred during cooling, or other phases such as NaInO₂ were formed during tempering. The addition of alumina, however, controlled the crystallization of In₂O₃. Depending on the crystallization temperature applied, the crystallite sizes were in the range from 13 to 53 nm. The glass matrix can be dissolved by soaking the powdered glass in water. This procedure can be used to prepare nano-crystalline In₂O₃-powders.     

Ni-containing spinel aluminates glass-ceramic materials obtained from cordieritic bulk glasses

Monolithic glasses with compositions 2MO · 2Al₂O₃ · 5SiO₂, being M=Ni and equimolar mixtures of Ni and Mg, were prepared at 1650 °C by melting mixtures of raw materials. The crystallization of monoliths was produced by heat-treatment at several temperatures up to 1200 °C. The crystallization sequence was followed by differential thermal analysis (DTA), X-ray powder diffraction (XRD), field emission scanning electron microscopy (FESEM) and energy dispersive X-ray (EDX) and diffuse reflectance spectroscopies. Surprisingly, the only crystalline phase formed after heating up to 1100 °C was a nickel-containing aluminate spinel for both compositions. The microstructural characterization indicated the volume crystallization of well formed octahedral crystals of spinel with smaller size than 500 nm. Finally, it has been proved that nickel-containing aluminosilicate glasses could be converted into μ- or -cordierite- and spinel-based glass-ceramics by thermal treatment of powdered glasses and monolithic bodies, respectively.     

Surface crystallization of leucite in glasses

The aim of this paper was to study surface crystallization of leucite in glasses derived from an SiO₂-Al₂O₃-K₂O base glass in a comparative study with another glass based on SiO₂-Al₂O₃-MgO. Monolithic samples and glass powder of SiO₂-Al₂O₃-K₂O glass were studied and phase formations were determined by using scanning electron microscopy. Heterogeneous nucleation was promoted by seeding the surface of the monolithic glass samples with glass dust to produce a highly disordered crystal as the primary phase. In addition to leucite formation, growth of a highly symmetric, flat, almost two-dimensional crystal phase with controlled diffusion was also observed. In glass granules, leucite demonstrated rapid, almost dendritic growth, from the nucleating centers. Use of leucite ceramic as a restorative dental product is considered.     

Some characteristics of glass in the Al2O3---B2O3---SiO2 system from the gel

The colorless and transparent glasses in the Al₂O₃---B₂O₃---SiO₃ system with high B₂O₃ and SiO₂ content were prepared from gels at low temperature. Their IR spectra not only revealed the evolution of the gel to glass conversion, but also showed that the formation of mixed bonds in the glasses obtained did not show any effect due to the B₂O₃ content. The accuracy of the glass composition is dependent upon the SiO₂/B₂O₃ molar ratio. The higher the ratio, the less the deviation of the analyzed compositions of the resulting glasses from their original calculated values. It is obvious that the higher the ratio, the lower the thermal expansion coefficient and the higher the transformation temperature of the glass, and the temperature at which the thermal contraction reaches an equilibrium is higher.     

Electrical conductivities of mixed cation glasses

The electrical conductivities of (1−x) Li₂O · x BaO · 2 SiO₂, (1−x) Na₂O · x MgO ·2 SiO₂, (1−x) Na₂O · x CaO · SiO₂ and (1−x) Na₂O · x BaO · 2SiO₂ glasses were measured at temperature ranging from room temperature to 450°C. The transport numbers for Na⁺ ion in (1−x) Na₂O · x BaO · 2 SiO₂ glasses were measured. It was found that the alkali ion carried a significant part of the current in these glasses except one that had no alkali ions, and the conductivity decreased markedly as the alkali oxide was substituted by an alkaline earth oxide. The results of conductivity measurements combined with the data hitherto reported on mixed alkali glasses led to the proposal that the so-called mixed alkali effect could be explained on the basis of the independent path model in which it is assumed that cations can move only through vacant sites left by those of the same type.     

Sodium borosilicate glasses prepared by the sol-gel process

A sodium borosilicate gel of composition 80SiO₂·15B₂O₃·5Na₂O (wt%) was prepared from tetraethyl orthosilicate, trimethyl borate, sodium methylate, H₂O, and HCl as the catalyst. Variation of specific surface area and porosity as a function of heating temperature indicated that closed pores were opened at temperatures lower than 400°C and collapsed above 450°C. From TG and DTA curves, about 19% Si and B atoms are evaluated to have −OH bonds. X-ray diffraction patterns indicated crystallization of low-cristobalite out of the gel when it was heated at 700°C for 5 h, showing a difference from a melt-quenched glass of the same composition.     

Glass formation in the PbBr2–PbCl2–PbF2–PbO–P2O5 system

New glasses in the PbBr₂–PbCl₂–PbF₂–PbO–P₂O₅ system have been prepared and characterized. The glass-forming regions have been explored and the stability of the glasses against crystallization studied. Results show that the PbBr₂–PbCl₂–P₂O₅ ternary system has a broad glass-forming region which extends to 30 mol% P₂O₅. Most of the glasses in this system show strong stability against crystallization and some have glass transition temperatures as low as 146°C. When 5% PbO or 5% PbF₂ is introduced into the PbBr₂–PbCl₂–P₂O₅ system, the glass-forming region becomes smaller and the glass transition temperatures increase. However, the introduction of 2.5% PbF₂ and 2.5% PbO into the ternary system increases the glass transition temperature and broadens the glass-forming region. The introduction of PbF₂ alone improves the glass-forming ability of the system while the introduction of PbO alone lowers the glass-forming ability.     

Mössbauer studies on some glasses and crystals in the Na2O---Fe2O3---SiO2 system

Mössbauer absorption measurements have been made at room temperature on ⁵⁷Fe in iron sodium silicate glasses containing 3–15 mol% Fe₂O₃ and various iron alkali silicate crystals in order to study the state of iron in these glasses. The spectra of all the glasses gave one doublet with a quadrupole splitting varying from 0.73–0.78 mm s⁻¹, while those of Na₂O · Fe₂O₃ · 4 SiO₂ and 5 Na₂O · Fe₂O₃ · 8 SiO₂ crystals showed much smaller quadrupole splitting, 0.28 mm s⁻¹ and 0.10 mm s⁻¹, respectively, and an asymmetrical doublet of much narrower linewidth. When sodium was replaced by other alkali metals of larger size, such as K and Cs, in MFeSi₂O₆ and MFeSi₃O₈ crystals, the quadrupole splitting became wider and approached to 0.73 mm s⁻¹. Such a variation was not observed for glasses. These results suggest that a larger number of non-identical sites exist in iron sodium silicate glasses than in the corresponding crystals.     

A SAXS study of V2O5·nH2O sols and gels

Small-angle X-ray scattering (SAXS) measurements on V₂O₅·nH₂O sols and gels, prepared by dissolving V₂O₅ glass into water at room temperature, show that there are V₂O₅ polymeric fibers entangled like random coils in the sol of n 5000, while the deviation from the random coil behavior occurs in the dilute sol of n 6000.

A Bragg peak appears at the scattering vector h 0.02 Å⁻¹ to be superimposed on an asymptotic h⁻²-course in the SAXS curve of the concentrated sol of n 680. This means that the spatial correlation between V₂O₅ polymeric fibers takes place even in the fluid state.

V₂O₅·nH₂O sols completely lose fluidity at n 250 to transfer to the gel state, where V₂O₅ polymeric fibers begin to pile up in the parallel with a substrate surface. Such a layer structure is preserved up to the gel of n 4. However, V₂O₅ polymeric fibers are randomly oriented within each layer.     

Hydration of phosphate and borate glasses in an autoclave

Kinetics of hydration of CaO---Al₂O₃---P₂O₅ and Na₂O---CaO---B₂O₃---Al₂O₃ glasses in an autoclave at high temperatures and high pressures has been investigated. The hydration of the phosphate glasses may occur as a result of hydrolysis of glass constituents to form orthophosphate crystals. Cabal glasses which do not contain any alkali oxides have shown a quite high resistance to water. Substitution of sodium for calcium deteriorates the chemical durability of Cabal glasses.     

Low-frequency internal friction of metallic glasses near Tg A critique of the use of the torsion pendulum

The application of the torsion pendulum to internal friction measurements on metallic glasses near the glass transition is critically analysed. It is pointed out that a difference between the measured damping Q_t⁻¹ and the real internal friction Q_s⁻¹ of the mterial must be taken into account; quantitative expression are given for the inverted and Collette types of torsion pendulum. The Collette pendulum is found particularly useful for measuring the internal friction of metallic glasses during slow heating through the glass transition. The results obtained with this instrument on six different Pd- and Ni-based glasses, as well as theoretical evidence, suggest that the extremely large internal friction “peak” above T_g is generally due to the intervention of crystallization after a large eand monotonous increase of viscoelastic damping in the supercooled liquid. In particular, there is no vidence for a real internal friction peak due to the glass transition. This conclusion is contradictory to some internal friction results found in the literature which have been obtained with a conventional inverted torsion pendulum. For this type of pendulum, the difference between Q_t⁻¹ and Q_s⁻¹ has obviously not been sufficiently tajen into account.