WC/TiO2纳米复合材料的制备及其电催化性能

以TiCl4为原料, 采用溶胶水解法合成了金红石型纳米TiO2颗粒, 并以其为载体制备了WC/TiO2纳米复合材料. 采用X射线衍射(XRD)、扫描电子显微镜(SEM)和X射线能谱(EDS)等手段分析了WC/TiO2纳米复合材料的晶相组成和表面形貌. 结果显示样品是由WC, TiO2和W组成, 纳米WC颗粒均匀地包覆在TiO2的表面, 并与TiO2构成了WC/TiO2纳米复合材料. 采用循环伏安法和计时电流法研究了WC/TiO2纳米复合材料对硝基苯的电催化性能. 结果表明, WC/TiO2纳米复合材料对硝基苯的电催化活性和电化学稳定性均优于介孔结构碳化钨(meso-WC)和纳米WC颗粒(part-WC).     

Ag/Au/Pt复合催化剂的制备及其对甲酸的电催化氧化

利用化学-电化学方法制备了Ag/Au/Pt复合催化剂. 该催化剂以100 nm左右的Ag颗粒为基底, 以化学方法沉积金再电沉积铂, 这降低了贵金属Au和Pt的用量. 通过SEM, EDX和XRD对样品进行表征, 并测试对甲酸的电催化氧化性能. 研究表明, 当Pt∶Au原子数比小于1∶10时, 主要表现为直接氧化, 在较低的Pt负载量(0.71 μg/cm²)情况下, Ag/Au/Pt复合催化剂对甲酸氧化的直接氧化峰电流密度达到最大. 甲酸的电催化氧化稳定性实验表明, 当Pt载量为0.05 μg时, 相对于最大峰电流密度, 循环伏安扫描第100圈时甲酸氧化的直接氧化峰电流密度仅衰减了2.29%. 同时CO氧化剥离实验表明, 当Pt∶Au＝1∶6时, Ag/Au/Pt复合催化剂对CO氧化峰电势最负, 相对于纯Pt催化剂负移了大约0.13 V, 表明该复合催化剂具有更好的抗CO毒化能力.     

Pt/Au原子比对活性炭负载Au-Pt直接甲酸燃料电池阴极催化剂性能的影响

制备了不同Pt/Au原子比的活性炭负载Au-Pt催化剂(Au-Pt/C),研究了Au/Pt原子比对Au-Pt/C催化剂氧还原电催化性能和抗甲酸性能的影响.结果表明,与Au/C催化剂相比,Au-Pt/C具有更好的电催化性能.当Pt/Au原子比从0/50增加到2/48时,Au-Pt/C催化剂表现出良好的氧还原电催化性能和抗...     

TiO_2/PtO-Pt复合膜和SnO_2/PtO-Pt复合膜氢敏性能的研究

将PtO Pt纳米粒子膜与TiO2 ,SnO2 纳米粒子膜复合 ,利用PtO Pt纳米粒子膜作为插入电极和催化剂 ,设计并研制出一类新型双层结构复合膜气体传感器 .采用TEM和SEM对薄膜的显微结构进行了表征 .对空气中 4 0 %H2 的氢敏性能研究表明 :2 0 0℃时 ,TiO2 /PtO Pt复合膜对氢气的灵敏度为 70 % ,而TiO2 纳米粒子膜无响应 .10 0℃时 ,SnO2 /PtO Pt复合膜的灵敏度为 92 % ,同样条件下 ,SnO2 纳米粒子膜的灵敏度仅为 4% .说明PtO Pt纳米粒子膜的催化作用能够显著提高TiO2 和SnO2 膜的氢敏性能 .另外 ,TiO2 /PtO Pt复合膜和SnO2 /PtO Pt复合膜均对空气中H2 有很高的选择性     

组合型Pt/TiO_2催化剂用于低温催化甲苯完全氧化

将均匀分布的纳米Pt粒子直接吸附到TiO2载体上,即制得了组合型Pt/TiO2催化剂(Pt/TiO2-AS).与浸渍法制备的Pt/TiO2催化剂(Pt/TiO2-WI)比较,Pt/TiO2-AS催化剂在催化甲苯完全氧化反应中表现出了很好的催化性能,甲苯转化率为100%时的反应温度低至150°C,而且即使在较高甲苯浓度和较高气体空速下,该催化剂也能保持较好的催化性能.通过X射线衍射(XRD)、N2吸附-脱附(BET)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、氢气程序升温还原(H2-TPR)及傅里叶变换红外(FTIR)光谱等对两种Pt/TiO2催化剂的结构和表面性能进行了表征.结果表明组合型Pt/TiO2-AS催化剂粒径小(2.5 nm),活性组分主要以Pt0形式存在且分布在载体表面,而且载体表面Ti―O键活化使催化剂具有较强的催化氧化能力.另外,活性中心的价态变化(Pt0→Ptδ+)是导致Pt/TiO2-AS催化剂失活的主要原因.     

微波辅助溶剂热法制备Pt/石墨烯-TiO2及其催化性能

质子交换膜燃料电池具有比能量高、结构简单、工作温度低、高效清洁和安静无摩擦等优点,是一种非常具有发展前景的电源.燃料电池借用电催化剂把燃料与氧化剂中的化学能转化为电能,通常采用碳粉负载的Pt催化剂.在燃料电池的工作环境下,碳粉载体容易腐蚀和团聚,降低了催化剂活性和稳定性,进而降低了燃料电池的使用寿命.因此,探索高稳定性的催化剂载体有利于提高催化剂的稳定性,促进燃料电池的实用化进程.为增强催化剂载体的抗腐蚀能力,一些金属氧化物如SnO2,WO3,CeO2和TiO2等被用作催化剂载体.其中,TiO2因具有稳定的化学性能以及与金属之间的"强相互作用"而备受研究者关注.但TiO2载体比表面积小和导电能力弱等缺点限制了它在燃料电池中的应用.石墨烯具有卓越的导电性和比表面积,却容易发生团聚.利用TiO2与碳材料间存在的协同作用,将TiO2与石墨烯复合来制备复合载体,能够增强TiO2的导电能力,抑制石墨烯的团聚,提高催化剂载体的化学稳定性和比表面积.本文采用微波辅助溶剂热法制备了石墨烯-TiO2复合载体和Pt/石墨烯-TiO2催化剂,研究了TiO2含量对催化剂活性和稳定性的影响.采用X射线衍射(XRD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)对制备的样品进行了微观结构和成分表征.结果表明,Pt/石墨烯-TiO2催化剂中TiO2为立方状纳米颗粒,粒径约为60 nm,均匀地分布在石墨烯上;Pt纳米粒子倾向于锚定在TiO2与石墨烯之间,而且分布均匀.采用线性伏安扫描(LSV)和循环伏安法(CV)测试了不同TiO2含量的Pt/石墨烯-TiO2催化剂的活性和稳定性.发现TiO2的加入确实能够提高催化剂的稳定性,随着TiO2含量的提高,催化剂稳定性增加.当TiO2含量为20%时,催化剂的起始电压与极限电流均与Pt/C催化剂接近.经过循环伏安扫描3000圈的快速老化测试后,Pt/石墨烯-TiO2催化剂起始电压的负移明显低于Pt/C催化剂,呈现了优良的稳定性和催化活性.     

Pt-TiO2/Graphene催化剂的氧还原和甲醇氧化电催化性能研究

以二(2-羟基丙酸)二氢氧化二铵合钛（TBA）和氧化石墨烯（GO）为前驱体,通过水热法合成出不同TiO₂含量的TiO₂/Graphene（TiO2/G）复合材料,随之用微波醇热法还原Pt前驱体可得Pt-TiO₂/G催化剂. 实验结果表明,TiO₂可与Pt相互作用,添入适量TiO₂的Pt-TiO₂/G催化剂具有较高的氧还原电催化活性及甲醇氧化的电催化活性与稳定性. 但TiO₂电导率偏低,过量TiO₂的添入反而使其电催化性能降低.     

Pt-TiO2/CeO2-MnO2复合催化剂光热降解气相苯

 用溶胶-凝胶法制备Ce-Mn储氧材料,并于该储氧材料上分别负载光催化剂TiO2 和贵金属Pt制备出Pt-TiO2/CeO2-MnO2复合催化剂. 用X射线衍射、 X射线能谱分析、程序升温还原和漫反射紫外-可见光谱等技术对复合催化剂进行了表征,并以光热催化降解气相苯评价了复合催化剂的活性. 结果表明, Mn分别进入到TiO2和CeO2的晶格中形成固溶体; Pt均匀分散在复合催化剂表面; Ce-Mn储氧材料在250 ℃下具有较好的储氧性能; 复合催化剂对紫外及可见光的吸收较强; 1.6%Pt-40%TiO2/CeO2-MnO2复合催化剂的活性较高,光热催化10 h时,苯降解率可达94.5%.     

碳化钨和Vulcan XC-72炭黑载钯催化剂对甲酸氧化的电催化性能

研究了碳化钨(WC)和Vulcan XC-72炭黑(XC)作混合载体的Pd/WC-XC催化剂对甲酸氧化的电催化性能.发现Pd/WC-XC催化剂对甲酸氧化的电催化性能优于Pd/XC催化剂.而且,Pd/WC-XC催化剂的电催化性能与WC和XC的质量比有关,当质量比为3:1时,催化剂对甲酸氧化的电催化活性最好,当质量比为2:1时,催化剂对甲酸氧化的电催化稳定性性最好.     

Pt/RuO2/CNTs纳米催化剂中RuO2含量对甲醇电催化氧化性能的影响

制备了一种新的甲醇直接燃料电池Pt/RuO2/CNTs阳极催化剂,在相同Pt负载量下,其甲醇电催化氧化活性是Pt/CNTs的3倍.采用循环伏安法研究发现Pt/RuO2/CNTs纳米催化剂中RuO2含量对甲醇电催化氧化活性有明显影响,当Pt和RuO2在碳纳米管上含量分别为15%和9.5%时,Pt/RuO2/CNTs催化剂具有最佳的甲醇电催化氧化活性.RuO2负载在碳纳米管上比电容的变化,反映了水合RuO2结构中质子与电子传输平衡的能力,分析表明,催化剂中RuO2含量不同导致电容的变化是影响甲醇电催化氧化活性的主要原因.当催化剂结构中质子与电子传输达到平衡时,催化剂比电容最大,电催化氧化活性最高.这种基于电容关联电催化剂的观点对甲醇直接燃料电池阳极催化剂的设计非常有意义.     

Kinetics of Photogenerated Electrons Involved in Photocatalytic Reaction of Methanol on Pt/TiO2

Time-resolved IR spectroscopy was used to detect the photocatalytic reaction of methanol for H2 production on Pt/TiO2 catalysts. There exists an optimal amount of Pt loading in the Pt/TiO2 catalysts for the reaction of the photogenerated long-lived electrons. For a given amount of Pt loading, the reaction rate of the long-lived electrons on Pt/TiO2 catalysts varies greatly with the di?erent reduction temperature of the catalysts. The possible reason is that the Pt particles occupy the surface active sites for methanol adsorption on Pt/TiO2 catalysts reduced at high temperature. This phenomenon is not observed obviously on Pt/TiO2 catalysts reduced at low temperature. The decay rate of the long-lived electrons evaluated by time-resolved IR method qualitatively correlates well with the activity of H2 production under steady-state irradiation conditions.     

Three-dimensionally ordered macro-porous Pt/TiO2 catalyst used for water-gas shift reaction

Three-dimensionally ordered macro-porous (3DOM) Pt/TiO2 catalysts were prepared by template and impregna-tion methods, and the resultant samples were characterized by using TG-DTA, XRD, SEM, TEM, and TPR techniques. The catalytic performance for water-gas shift (WGS) reaction was tested, and the influences of some conditions, such as reduction temperature of catalysts, the amount of Pt loadings and space velocity on catalytic performance were investigated. It was shown that Pt particles were homogeneously dispersed on 3DOM TiO2. The reduction of TiO2 surface was important for the catalyticperformance. The activity test results showed that the 3DOM Pt/TiO2 catalysts exhibited very good catalytic performance for WGS reaction even at high space velocity, which was owing to the better mass transfer of 3DOM porous structure besides the high intrinsic activity of Pt/TiO2.     

Preparation of Pt／C Catalyst with a New and Simple Organic Sol Method

It is reported for the first time that the Pt/C catalyst can be prepared with a new and simple organic sol method using SnCl2 as the reductant. It was found that the average size of the Pt particles in the Pt/C catalysts could be controlled with controlling the preparation conditions. The effect of the average sizes of the Pt particles in the Pt/C catalysts obtained with this method on the electrocatalytical activity of the oxidation of methanol was investigated.     

热解二氧化钛/聚苯胺制备高效非贵金属氧还原电催化剂

为了克服传统Pt系催化剂价格昂贵、稳定性差的缺点,采用热解新型Ti O2/聚苯胺(PANI)复合物的方法合成了Ti O2/C催化剂.用扫描电子显微镜、X射线光电子能谱、X射线衍射、傅里叶变换红外光谱、拉曼光谱、透射电子显微镜、循环伏安法和线性扫描伏安法等方法研究了热处理和PANI复合比例对复合物的形貌、成键、晶相组成及氧还原性能的影响.结果表明,PANI与Ti O2间存在相互作用,可以抑制Ti O2的团聚和锐钛矿向金红石的转变.热处理制得Ti O2/C的氧还原活性随着PANI载体含量增加先升高后降低,PANI和Ti O2质量比为35/100时,催化剂的氧还原活性最高.同时,循环伏安和时间-电流曲线测试表明,已制备的复合材料在催化氧还原反应进行时具有较好的稳定性.     

水热法合成多孔Ag_2S敏化二氧化钛催化剂及其可见光催化活性(英文)

Porous Ag2S sensitized TiO2 catalysts were synthesized by the hydrothermal process.The crystallization and porous structure of the Ag2S/TiO2 composite photocatalysts were investigated by X-ray diffraction,scanning electron microscopy with energy dispersive X-ray analysis,UV-Vis diffuse reflectance spectroscopy,and N2 adsorption.The Ag2S/TiO2 composites were mainly composed of anatase TiO2 and acanthite Ag2S.The absorption edge wavelengths of TiO2 and the Ag2S/TiO2 composite prepared with 3 mmol Na2S.5H2O were 400 and 800 nm,respectively,that is,the absorption edge of the composite had a pronounced red shift.The photocatalytic activity under visible light was investigated by the degradation of methylene blue with a UV-Vis spectrophotometer.The photocatalytic activities under visible light of the Ag2S/TiO2 photocatalysts were much higher than that of TiO2.     

嵌段共聚物模板法一步制备WC/C基底电极材料

以酚醛树脂作为碳源,采用嵌段共聚物模板法一步制备新型有序介孔碳化钨/碳（WC/C）纳米颗粒. WC/C颗粒的比表面积为414 m²·g^-1,表面的平均孔径约为38 nm,处于介孔范围内（2 ~ 50 nm）. 通过调节树脂预聚时间以及碳化温度等条件制备出结构形貌较优的WC/C复合材料,并探讨了材料形成机理. 使用X射线衍射、扫描电镜、透射电镜及氮气吸脱附等方法表征了复合材料的结构. 将贵金属铂负载于WC/C表面制备得新电催化材料Pt-WC/C,使用循环伏安法和计时电流法对Pt-WC/C复合材料的电化学性能进行检测,并与商用碳载铂（Pt/C）材料进行对比. 测试结果发现,Pt-WC/C对甲醇的电催化活性以及稳定性等方面都表现出优于商用Pt/C材料的活性,这主要归功于碳化钨高度分散于碳表面.     

溶胶-凝胶法制备复合MxOy-TiO2光催化剂

以无机盐TiCl4为原料制备TiO2溶胶,并利用溶胶胶粒修饰法制备SiO2 TiO2、ZrO2 TiO2、WO3 TiO3、MoO3 TiO2及Pt/TiO2光催化剂,用于光催化氧化甲醛反应,考察添加物对 催化剂光催化性能的影响.其中,SiO2 TiO2催化剂的光催化氧化降解甲醛性能最好,而MoO3 TiO2的催化性能最差.SiO2 TiO2催化剂优良的光催化性能可归于SiO2 TiO2催化剂的高 比表面积,高空隙率,小晶粒粒径和强吸光性能等性质的综合影响.     

TiO2对Ni/Al2O3催化剂CO甲烷化性能的影响

采用溶胶凝胶法制备了一系列不同TiO₂含量的TiO₂-Al₂O₃复合载体,并通过浸渍法制备了NiO/TiO₂-Al₂O₃催化剂。分别考察了不同TiO₂含量的NiO/TiO₂-Al₂O₃催化剂及反应温度对CO甲烷化催化性能的影响。实验结果表明,当复合载体中TiO₂质量分数为30%,反应温度为350～450 ℃时,催化剂催化活性较高。利用N₂吸附-脱附(BET)、X射线衍射(XRD)及H₂程序升温还原(H₂-TPR)等手段对催化剂物化性能进行了表征。结果表明,加入适量的TiO₂能抑制镍铝尖晶石NiAl₂O₄物种的生成,改善NiO的表面分散性能,避免大晶粒NiO的形成,也改善了催化剂的还原性能,从而提高催化剂的CO甲烷化活性。     

Platinized mesoporous tungsten carbide for electrochemical methanol oxidation

Mesoporous WC with hexagonal crystal structure was synthesized by a surfactant-assisted polymer method. A new electrocatalyst composed of a small amount of Pt supported on the mesoporous WC exhibited higher activity for electrooxidation of methanol than microporous Pt/WC or Pt/W₂C as well as commercial Pt–Ru(1:1)/C catalysts. The mesoporosity and the phase of WC appear important for the high activity. Compared to the commercial Pt–Ru/C catalyst, the Pt/WC (mesoporous) showed the higher activity per mass of Pt by a factor of six even without Ru. Since the catalyst is also stable in electrochemical environment, it could become an alternative electrocatalyst for direct methanol fuel cells.