Physical and electrochemical characterization of activated carbons with high mesoporous ratio for supercapacitors based on ionic liquid as the electrolyte

A series of activated carbons with high mesoporous ratio were prepared by KOH reactivation based on activated carbon as the precursor. As the KOH/AC mass ratio was increased to 4:1, the mesoporous ratio increases from 60% to 76%, and the average pore size from 2.23 to 3.14?nm. Moreover, the specific capacitance for the activated carbon in ionic liquid 1-ethyl-3-methylmidazolium tetrafluoroborate ([EMIm]BF₄) can reach the maximum value of 189?F?g^?1 (8.0???F?cm^?2). In addition, the decrease of specific capacitance for activated carbons by KOH reactivation with current density increase shows two regimes, suggesting that activated carbons with high mesoporous ratio are much fit for charge?Cdischarge at larger current density.     

Preparation of activated carbon from waste Camellia oleifera shell for supercapacitor application

The cost-effective activated carbons derived from waste Camellia oleifera shell (COS) by ZnCl₂ activation method are investigated as the active electrode material in electric double-layer capacitors (EDLCs) for the first time. The activation temperature and ZnCl₂/COS impregnation ratio are two key factors affecting the surface area and pore structure of the prepared activated carbons, which accordingly affect their capacitive performances. Electrochemical investigations indicate that the activated carbon (AC-3-600) obtained at the activation temperature of 600 °C and impregnation ratio of 3 shows the maximum specific capacitance of 374 and 266 F?g^?1 in 1 mol L^?1 H₂SO₄ and 6 mol L^?1 KOH electrolytes at 0.2 A g^?1, respectively. The high capacitance of the AC-3-600 is attributed to its high surface area (1,935 m² g^?1), high total pore volume (1.02 cm³ g^?1), and especially the large percentage of micropores (735 m² g^?1). Meanwhile, the activated carbon presents good cycle stability in both acid and alkaline electrolytes during 5,000 cycles at a fair current density of 4 A g^?1. So, we had reasons to believe that the activated carbons from waste COS by ZnCl₂ activation might be one of the innovative carbon electrode materials for EDLCs application.     

Hierarchical Activated Mesoporous Phenolic‐Resin‐Based Carbons for Supercapacitors

A series of hierarchical activated mesoporous carbons (AMCs) were prepared by the activation of highly ordered, body‐centered cubic mesoporous phenolic‐resin‐based carbon with KOH. The effect of the KOH/carbon‐weight ratio on the textural properties and capacitive performance of the AMCs was investigated in detail. An AMC prepared with a KOH/carbon‐weight ratio of 6:1 possessed the largest specific surface area (1118 m² g^?1), with retention of the ordered mesoporous structure, and exhibited the highest specific capacitance of 260 F g^?1 at a current density of 0.1 A g^?1 in 1 M H₂SO₄ aqueous electrolyte. This material also showed excellent rate capability (163 F g^?1 retained at 20 A g^?1) and good long‐term electrochemical stability. This superior capacitive performance could be attributed to a large specific surface area and an optimized micro‐mesopore structure, which not only increased the effective specific surface area for charge storage but also provided a favorable pathway for efficient ion transport.     

Highly stable performance of supercapacitors using microporous carbon derived from phenol–melamine–formaldehyde resin

A series of microporous carbons were prepared by simple carbonization and activation of phenol–melamine–formaldehyde resin. The morphology, surface area, and elemental composition of the samples were investigated by scanning electron microscope, Brunauer–Emmett–Teller measurement, Raman spectra, and elemental analysis, respectively. Electrochemical characteristics were evaluated by cyclic voltammograms, galvanostatic charge/discharge, and electrochemical impedance spectroscopy measurements in 6.0?mol?L^?1 KOH. The microporous carbon activated by KOH presented a high specific capacitance of 202?F?g^?1 at a scan rate of 2?mV?s^?1. Furthermore, the KOH-activated microporous carbon electrode exhibited durable operation, the total loss of capacitance after 20,000 cycles is 2% at a current density of 500?mA?g^?1. The good electrochemical performance of the activated carbon was ascribed to well-developed micropores, high surface area, larger pore volume as well as oxygen groups.     

KOH‐Activated Porous Carbons Derived from Chestnut Shell with Superior Capacitive Performance

Porous carbons (PC) were prepared from a waste biomass named chestnut shell via a two‐step method involving carbonization and KOH activation. The morphology, pore structure and surface chemical properties were investigated by scanning electron microscopy (SEM), N₂ sorption, Raman spectroscopy, X‐ray diffraction (XRD) and X‐ray photoelectron spectroscopy (XPS). The carbons have been evaluated as the electrode materials for supercapacitors by a two‐electrode system in 6 mol/L KOH electrolyte. Benefiting from the porous texture, high surface area and high oxygen content, the PCs derived from chestnut shell have exhibited high specific capacitance of 198.2 (PC‐1), 217.2 (PC‐2) and 238.2 F·g^?1 (PC‐3) at a current density of 0.1 A·g^?1, good rate capability of 55.7%, 56.6% and 54.9% in a range of 0.1–20 A·g^?1 and high energy density of 5.6, 6.1 and 6.7 Wh·kg^?1, respectively. This is believed to be due to electric double layer capacitance induced by the abundant micropores and extra pseudo‐capacitance generated by oxygen‐containing groups. At a power density of 9000 Wh·kg^?1, the energy density is 3.1, 3.5 and 3.7 Wh·kg^?1 for PC‐1, PC‐2 and PC‐3, respectively, demonstrating the potential of the carbons derived from chestnut shells in energy storage devices.     

The effect of activation technology on the electrochemical performance of calcium carbide skeleton carbon

Porous CaC₂-derived carbon (CCDC) was synthesized by one-step route from CaC₂ in a freshly prepared chlorine environment at lower temperature. As-prepared CCDC was activated by H₃PO₄, ZnCl₂, and KOH, respectively. The effects of the activation technology on the structure and morphology of CCDC were studied by X-ray diffraction, physical N₂ adsorption/desorption, and transmission electron microscopy. It has been found that the pore structure and specific surface area of CCDC are apparently improved after activation; the CCDC activated by KOH especially showed an excellent specific surface area of 1,100?m²?g^?1. The electrochemical performance of supercapacitors using activated CCDC as electrode active material was studied by cyclic voltammery, galvanostatic charge/discharge, and cycle life measurements. The results indicated that the CCDCs activated by H₃PO₄, ZnCl₂, and KOH revealed enhanced capacitances of 172.6, 198.1, and 250.1?F?g^?1 in 6?M KOH electrolyte, which were increased by 11.4, 27.8, and 61.2?% compared with the pristine CCDC (155?F?g^?1), respectively. Furthermore, the supercapacitors using all activated CCDCs as electrode active material exhibited excellent cycle stability, and the specific capacitance for all activated CCDC samples had nearly no change after 5,000 cycles.     

Preparation and performance of polyvinyl alcohol-based activated carbon as electrode material in both aqueous and organic electrolytes

Porous carbon materials with high surface area and different pore structure have been successfully prepared by phenolic resin combined with polyvinyl alcohol (PVA) and KOH as activation agents. The surface morphology, structure, and specific surface area of the carbon materials were studied by scanning electron microscopy, X-ray diffraction, and nitrogen sorption measurement, respectively. Furthermore, the effects of specific surface area, pore structure, and electrolyte on electrochemical properties were investigated by galvanostatic charge–discharge measurement. The results show that KOH–PVA-activated carbon materials display specific capacitance as high as 218 F?g^?1 in 30 wt.% KOH aqueous electrolyte, 147 F?g^?1 in 1 M LiPF₆/(ethylene carbonate (EC) + dimethyl carbonate) (1:1?v/v), and 115 F?g^?1 in 1 M Et₃MeNBF₄/propylene carbonate organic electrolyte, respectively. In addition, the carbon materials demonstrate long-term cycle stability, especially the AK3P-0.30 in aqueous electrolyte and the AK2P-0.30 with excellent rate capability in organic electrolyte. These reveal that the existence of a micro-mesoporous structure of activated carbon is beneficial to store energy in an aqueous supercapacitor and broad pore size distribution of activated carbon is favorable to energy storage in an organic supercapacitor. The carbon materials with pore size distribution in different ranges improve the electrochemical performance of supercapacitor in different electrolytes. A new pore-expand agent (PVA combining with KOH) was used to obtain porous carbons with enhanced properties for supercapacitor.     

Facile synthesis of biomass-derived hierarchical porous carbon microbeads for supercapacitors

Using the facile method of solvent evaporation, the leonardite fulvic acids (LFA)-based porous carbon microbeads (PCM) have been successfully prepared at ambient pressure, followed by carbonization and KOH activation (a low mass ratio alkali/LFA = 1.5) in an inert atmosphere. The effects of KOH treatment on pore structures and the formation mechanism of the PCM were discussed. The results showed that the sample exhibited remarkable improvement in textural properties. The activated carbon microbeads had high surface area (2269 m² g^?1), large pore volume (1.97 cm³ g^?1), and displayed excellent capacitive performances, compared with carbon powder. The porous carbon material electrodes with the “porous core structure” behaved superiorly at a specific capacitance of 320 F g^?1 at a current density of 0.05 A g^?1 in 6 M KOH electrolyte, which could still remain 193 F g^?1 when the current density increased to 100 A g^?1. Remarkably, in the 1 M TEABF₄/PC electrolyte, the PCM samples could reach 156 F g^?1 at 0.05 A g^?1, possess an outstanding energy density of 39.50 Wh kg^?1, and maintain at 22.05 Wh kg^?1 even when the power density rose up to 5880 W kg^?1. The balance of structural characteristic and high performance makes the porous carbon microbeads a competitive and promising supercapacitor electrode material.     

The production of activated carbon from cation exchange resin for high-performance supercapacitor

High-performance activated carbon for electrochemical double-layer capacitors (EDLC) has been prepared from cation exchange resin by carbonization and subsequent activation with KOH. The activation temperature has a key role in the determination of porous carbon possessing high surface areas, and large pore structures. The porous carbon activated at 700 °C (carbon-700-1:4) has high surface area (2236 m²?g^?1) and large total pore volume (1.15 cm³?g^?1), which also displays best capacitive performances due to its well-balanced micro- or mesoporosity distribution. In details, specific capacitances of the carbon-700-1:4 sample are 336.5 F?g^?1 at a current density of 1 A?g^?1 and 331.8 F?g^?1 at 2 A?g^?1. At high current density as 20 A?g^?1, the retention of its specific capacitance is 68.4 %. The carbon-700-1:4 sample also exhibits high performance of energy density (46.7 Wh?kg^?1) and long cycle stability (～8.9 % loss after 3,000 cycles). More importantly, due to the amount of waste ion-exchange resins increasing all over the world, the present synthetic method might be adopted to dispose them, producing high-performance porous carbons for EDLC electrode materials.     

Activated nitrogen-doped carbons from polyvinyl chloride for high-performance electrochemical capacitors

Activated nitrogen-doped carbons (ANCs) were prepared by carbonization/activation approach using aminated polyvinyl chloride (PVC) as precursor. ANCs exhibit larger porosities and higher specific surface areas than those of their nitrogen-free counterparts for the same KOH/carbon ratio. The specific surface area of ANC-1 is up to 1,398 m² g^?1 even at a low KOH/carbon ratio of 1:1. Fourier transform infrared spectroscopy investigation of the nitrogen-enriched resin precursor indicates the efficient dehydrochlorination of PVC by ethylenediamine at a low temperature. The nitrogen content and the population of nitrogen functionalities strongly depend on the KOH/carbon ratios and decrease drastically after KOH activation as seen from the elemental and X-ray photoelectron spectroscopy analysis. The surface concentration of N-6 and N-Q almost disappears and the dominant nitrogen groups become N-5 after KOH activation. The highest specific capacitance of ANCs is up to 345 F g^?1 at a current density of 50 mA g^?1 in 6 M KOH electrolyte. ANCs also exhibit a good capacitive behavior at a high scan rate of 200 mV s^?1 and an excellent cyclability with a capacitance retention ratio as high as ～93 % at a current density of 2,000 mA g^?1 for 5,000 cycles.     

Nitric acid oxidation of ordered mesoporous carbons for use in electrochemical supercapacitors

Ordered mesoporous carbon materials with high microporosity were synthesized by a low temperature autoclaving of citric acid-catalyzed polymerized resorcinol/formaldehyde in the presence of the triblock copolymer F127 and were activated by nitric acid oxidation. The materials were used as electrode materials in electrochemical supercapacitors. A bimodal pore size distribution of 2.1–2.3 and 5.3 nm with a surface area of 465–578 m² g^?1 and pore volume of 0.44–0.54 cm³ g^?1 was obtained with the retention of an ordered mesoporous structure after nitric acid (2 M) treatment. The introduced functional groups produced a pseudocapacitance, which resulted in an increase in the specific capacitance. The electrochemical capacitance of the resulting mesoporous carbons showed a marked increase after 3 h of nitric acid activation, exhibiting a high value of 295 F g^?1 at the scan rate of 10 mV s^?1 in 6 M KOH aqueous solution and good cycling stability with specific capacitance retention over 500 cycles.     

Porous Nitrogen‐Doped Carbon Microspheres Derived from Microporous Polymeric Organic Frameworks for High Performance Electric Double‐Layer Capacitors

This research presents a simple and efficient method to synthesize porous nitrogen‐doped carbon microspheres (PNCM) by the carbonization of microporous poly(terephthalaldehyde‐pyrrole) organic frameworks (PtpOF). The common KOH activation process is used to tune the porous texture of the PNCM and produce an activated‐PNCM (A‐PNCM). The PNCM and A‐PNCM with specific surface area of 921 and 1303 m² g^?1, respectively, are demonstrated as promising candidates for EDLCs. At a current density of 0.5 A g^?1, the specific capacitances of the PNCM and A‐PNCM are 248 and 282 F g^?1, respectively. At the relatively high current density of 20 A g^?1, the capacitance remaining is 95 and 154 F g^?1, respectively. Capacity retention of the A‐PNCM is more than 92 % after 10 000 charge/discharge cycles at a current density of 2 A g^?1.     

One-step synthesis of nitrogen-doped porous carbon for supercapacitors utilizing KNO<Subscript>3</Subscript> as an electrolyte

Nitrogen-doped porous carbons were prepared using a facile method, with low-biotechnology fulvic acid potassium salts as a precursor. The prepared carbons had a high surface area (1623 m² g^?1) and good electrochemical properties, making them suitable electrode materials for supercapacitors. Nitrogen-doped porous carbons were tested as an electrode in both 6 M KOH aqueous solution and different concentrations KNO₃ aqueous solution. The nitrogen-doped porous carbons with unique microstructure and nitrogen functionalities exhibited a capacitance of 235 F g^?1 in a 6 M KOH aqueous solution. Electrochemical investigation showed that the nitrogen-doped porous carbons exhibited a broad potential operational window in a 2.5 M KNO₃ aqueous solution. Furthermore, a high capacitance retention of 88.1 % was achieved even after 5000 cycles at 1.7 V. Potassium nitrate solutions in a wide range of concentrations were also proven to be promising electrolytes for electrochemical capacitors because they are cheap, noncorrosive, electrochemically stable, and compatible to diverse current collectors.     

The superior electrochemical performance of oxygen-rich activated carbons prepared from bituminous coal

Oxygen-rich activated carbons (OAC) were prepared from bituminous coal through a quick KOH activation. OAC exhibited a moderately large surface area of 1950 m²/g, a relative wide pore size distribution, good conductivity and very high oxygen content (up to 12 wt.%). Compared with high surface area activated carbons prepared by the conventional KOH activation, OAC have superior capacitive behavior, power output and high energy density in electrochemical double layer capacitors (EDLC). OAC presented a high specific capacitance of 370 F/g in 3 M KOH electrolyte at a low current density of 50 mA/g and still remained 270 F/g even at a high current density of 20 A/g.     

Influence of KMnO4 oxidation on the electrochemical performance of pitch-based activated carbons

In this work, activated carbons (ACs) are obtained from petroleum pitch by the combination of a chemical treatment with different potassium permanganate (KMnO₄) amounts, i.e., 0, 0.5, 1.0, and 2.0 g, and a chemical activation with KOH at a constant KOH/pitch ratio of 3/1. The effects of the chemical activating agent on the surface morphology and porosity are evaluated with scanning electron microscopy and N₂ adsorption isotherms at 77 K, respectively. The specific surface area of the pitch-based ACs is increased with increasing the amount of KMnO₄ pre-treatment and showed the highest value of 2,334 m² g^?1 at 2 g of KMnO₄ amount. The electrochemical performance of AC electrodes is examined by cyclic voltammetry and galvanostatic charge/discharge characteristics in 6 M KOH electrolyte. Among the prepared ACs, 2.0 K-ACs possesses a specific capacitance as high as 237 F g^?1 and showed excellent electrochemical performance due to its suitable porous structure and low interface resistance.     

Improving the electrochemical performances of active carbon-based supercapacitors through the combination of introducing functional groups and using redox additive electrolyte

High-performance and low-cost electrochemical capacitors (ECs) are essential for large-scale applications in energy storage. In this work, the specific capacitance of active carbon (AC) electrode was significantly improved through the combination of introducing functional groups on the surface of AC and adding redox-active molecules (K₃Fe(CN)₆) into 2?M KOH aqueous electrolytes. The surface-oxygen functionalized AC (FAC) was synthesized using HNO₃ echoed as the electrode and 2?M KOH with 0.1?M K₃Fe(CN)₆ as the electrolyte. The surface functional groups of the AC not only contribute to the pseudocapacitance but also increase the active sites of the electrode/electrolyte interface, which enhances the electrochemical activity of the Fe(CN)₆^3?/Fe(CN)₆^4? redox pair, thus leading to high capacitance. In the redox electrolyte, the specific capacitance was much higher in 229.17?F?g^?1 (1?A?g^?1) achieved for those FAC than in raw AC (only 147.06?F?g^?1). Similarly, the FAC electrode suggested high energy density and extended cycling stability in the KOH?+?K₃Fe(CN)₆ electrolyte.     

MnO2 Nanosheets Grown on Nitrogen‐Doped Hollow Carbon Shells as a High‐Performance Electrode for Asymmetric Supercapacitors

A hierarchical hollow hybrid composite, namely, MnO₂ nanosheets grown on nitrogen‐doped hollow carbon shells (NHCSs@MnO₂), was synthesized by a facile in situ growth process followed by calcination. The composite has a high surface area (251 m²g^?1) and mesopores (4.5 nm in diameter), which can efficiently facilitate transport during electrochemical cycling. Owing to the synergistic effect of NHCSs and MnO₂, the composite shows a high specific capacitance of 306 F g^?1, good rate capability, and an excellent cycling stability of 95.2 % after 5000 cycles at a high current density of 8 A g^?1. More importantly, an asymmetric supercapacitor (ASC) assembled by using NHCSs@MnO₂ and activated carbon as the positive and negative electrodes exhibits high specific capacitance (105.5 F g^?1 at 0.5 A g^?1 and 78.5 F g^?1 at 10 A g^?1) with excellent rate capability, achieves a maximum energy density of 43.9 Wh kg^?1 at a power density of 408 W kg^?1, and has high stability, whereby the ASC retains 81.4 % of its initial capacitance at a current density of 5 A g^?1 after 4000 cycles. Therefore, the NHCSs@MnO₂ electrode material is a promising candidate for future energy‐storage systems.     

Supercapacitive behaviors of the nitrogen-enriched activated mesocarbon microbead in aqueous electrolytes

The activated nitrogen-enriched novel carbons (a-NENCs) have been prepared by direct carbonization of polyaniline/activated mesocarbon microbead composites and further activated by 16 M?HNO₃. The electrochemical performances and supercapacitive behaviors of the a-NENCs in 6 M KOH, 1 M?H₂SO₄, and 0.5 M?K₂SO₄ solutions are evaluated by cyclic voltammetry, galvanostatic charge/discharge, electrochemical impedance spectroscopy, cyclic life, leakage current, and self-discharge measurements. The results demonstrate that the supercapacitors perform definitely supercapacitive behaviors; especially in 6 M KOH electrolyte, the supercapacitor represents much better electrochemical performance with more excellent reversibility, shorter relaxation time of 1.11 s, and nearly ideal polarizability. The maximum specific capacitance of the supercapacitors using a-NENCs as active electrode material is 85.1 F?g^?1 at a rate of 500 mA?g^?1 in 6 M?KOH. These outcomes indicate that the 6 M?KOH aqueous solution is a promising electrolyte for the supercapacitor with a-NENCs as electrode material.     

Perovskite SrCo0.9Nb0.1O3−δ as an Anion‐Intercalated Electrode Material for Supercapacitors with Ultrahigh Volumetric Energy Density

We have synthesized and characterized perovskite‐type SrCo_0.9Nb_0.1O_3−δ (SCN) as a novel anion‐intercalated electrode material for supercapacitors in an aqueous KOH electrolyte, demonstrating a very high volumetric capacitance of about 2034.6 F cm⁻³ (and gravimetric capacitance of ca. 773.6 F g⁻¹) at a current density of 0.5 A g⁻¹ while maintaining excellent cycling stability with a capacity retention of 95.7 % after 3000 cycles. When coupled with an activated carbon (AC) electrode, the SCN/AC asymmetric supercapacitor delivered a specific energy density as high as 37.6 Wh kg⁻¹ with robust long‐term stability.     

Preparation of activated carbon from cotton stalk and its application in supercapacitor

High specific capacitance and low cost are the critical requirements for a practical supercapacitor. In this paper, a new activated carbon with high specific capacitance and low cost was prepared, employing cotton stalk as the raw material, by using the phosphoric acid (H₃PO₄) chemical activation method. The optimized conditions were as follows: the cotton stalk and activating agent with a mass ratio of 1:4 at an activation temperature of 800 °C for 2 h. The samples were characterized by nitrogen adsorption isotherms at 77 K. The specific surface area and pore volume of activated carbon were calculated by Brunauer–Emmett–Teller (BET) and t-plot methods. With these experimental conditions, an activated carbon with a BET surface area of 1,481 cm²?g^?1 and micropore volume of 0.0377 cm³?g^?1 was obtained. The capacitance of the prepared activated carbon was as high as 114 F?g^?1.The results indicate that cotton stalk can produce activated carbon electrode materials with low cost and high performance for electric double-layer capacitor.