CoAl2O4/蜂窝陶瓷催化剂的制备及其催化臭氧化性能

采用涂覆法制备了CoAl₂O₄/蜂窝陶瓷催化剂。利用X射线衍射、N₂吸附-脱附和透射电镜等方法对所制备的催化剂进行了表征,并分析了其催化臭氧化降解对苯二酚的效能。结果表明,CoAl₂O₄/蜂窝陶瓷的晶相属于典型的尖晶石结构,具有较大的比表面积、孔容和孔径,分别达到77 m²·g^-1、0.001 7 cm³·g^-1和3.9 nm。CoAl₂O₄/蜂窝陶瓷催化臭氧化对苯二酚的去除率高达81.2%,COD去除率可达47.7%。在叔丁醇存在的条件下,对苯二酚的去除率显著下降,说明CoAl₂O₄/蜂窝陶瓷催化臭氧化遵循羟基自由基机理。     

CoAl_2O_4/蜂窝陶瓷催化剂的制备及其催化臭氧化性能

采用涂覆法制备了CoAl_2O_4/蜂窝陶瓷催化剂。利用X射线衍射、N_2吸附-脱附和透射电镜等方法对所制备的催化剂进行了表征,并分析了其催化臭氧化降解对苯二酚的效能。结果表明,CoAl_2O_4/蜂窝陶瓷的晶相属于典型的尖晶石结构,具有较大的比表面积、孔容和孔径,分别达到77 m~2·g~(-1)、0.001 7 cm~3·g~(-1)和3.9 nm。CoAl_2O_4/蜂窝陶瓷催化臭氧化对苯二酚的去除率高达81.2%,COD去除率可达47.7%。在叔丁醇存在的条件下,对苯二酚的去除率显著下降,说明CoAl_2O_4/蜂窝陶瓷催化臭氧化遵循羟基自由基机理。     

Combustion synthesis of mesoporous CoAl2O4 for peroxymonosulfate activation to degrade organic pollutants

A mesoporous cobalt aluminate (CoAl₂O₄) spinel is synthesized through a combustion method and adopted for the activation of peroxymonosulfate (PMS) to degrade organic pollutants. Multiple characterization procedures are conducted to investigate the morphology and physicochemical properties of the CoAl₂O₄ spinel. Due to its mesoporous structure, large surface area, and high electrical conductivity, the obtained CoAl₂O₄ exhibits remarkable catalytic activity for Rhodamine B (RhB) degradation. Its RhB degradation rate is 89.0 and 10.5 times greater than those of Co₃O₄ and CoAl₂O₄ spinel prepared by a precipitation method, respectively. Moreover, the mesoporous CoAl₂O₄ spinel demonstrates a broad operating pH range and excellent recyclability. The influence of several parameters (catalyst amount, PMS concentration, initial pH, and coexisting inorganic anions) on the oxidation of RhB is evaluated. Through quenching tests and electron paramagnetic resonance experiments, sulfate radicals are identified as the predominant reactive species in RhB degradation. This paper provides new insights for the development of efficient, stable, and reusable cobalt-based heterogeneous catalysts and promotes the application of persulfate activation technology for the treatment of refractory organic wastewater.     

Electrochemical study of Meldola's blue,methylene blue and toluidine blue immobilized on a SiO<Subscript>2</Subscript>/Sb<Subscript>2</Subscript>O3 binary oxide matrix obtained by the sol-gel processing method

SiO₂/Sb₂O₃ (SiSb), having a specific surface area, S _BET, of 788 m² g⁻¹, an average pore diameter of 1.9 nm and 4.7 wt% of Sb, was prepared by the sol-gel processing method. Meldola's blue (MeB), methylene blue (MB) and toluidine blue (TB) were immobilized on SiSb by an ion exchange reaction. The amounts of the dyes bonded to the substrate surface were 12.49, 14.26 and 22.78 μmol g⁻¹ for MeB, MB and TB, respectively. These materials were used to modify carbon paste electrodes. The midpoint potentials (E _m) of the immobilized dyes were −0.059, −0.17 and −0.18 V vs. SCE for SiSb/MeB, SiSb/MB and SiSb/TB modified carbon paste electrodes, respectively. A solution pH between 3 and 7 practically did not affect the midpoint potential of the immobilized dyes. The electrodes presented reproducible responses and were chemically stable under various oxidation-reduction cycles. Among the immobilized dyes, MeB was the most efficient to mediate the electron transfer for NADH oxidation in aqueous solution at pH 7. In this case, amperometric detection of NADH at an applied potential of 0 mV vs. SCE gives linear responses over the concentration range of 0.1–0.6 mmol L⁻¹, with a detection limit of 7 μmol L⁻¹.     

Effect of metal ions on structural,morphological and optical properties of nano-crystallite spinel cobalt-aluminate (CoAl2O4)

The bright blue nano crystallite cobalt aluminate (CoAl₂O₄) was synthesized by sol–gel method using a mixture of chelating agent of glycerol and citric acid. The effects of changing (0.05, 0.075, 0.10, 0.25, 0.50, and 0.75 mol/L) metal ion concentration on the structural, morphological and color properties of synthesized CoAl₂O₄ were characterized by using X-ray diffraction (XRD), Scanning electron microscopy (SEM), Energy dispersive X-ray spectroscopy (EDX), Fourier transform infrared spectroscopy (FTIR), Nanoparticle size analyzer, Simultaneous Thermal Analyzer (STA), UV–vis absorption spectroscopy, and CIE-LAB colorimetric analysis. From the X-ray peak profile analysis, the crystallite size was measured by Debye-Scherrer (D-S) equation, and three different models presenting average crystallite sizes between 88.3 and 125.4 nm.The average lattice strain, dislocation density, lattice constant, cell volume, and zeta potential were between 0.00021 and 0.0058, (1.73 to 12.8) × 10¹⁴ (lines/m²), 8.10658 to 8.11181 Å, 533.60 to 533.81 Å³, ?56.4 to ? 63.5 mV, respectively. Using UV–vis absorption spectroscopy, the band gap was calculated from Kubelka-Munk method, and the values of band gap increasing from 1.82 to 1.84 eV, respectively. The reflectance spectra and the CIE-L*a*b* values of cobalt aluminate is also measured which confirmed the formation of blue nano crystallite cobalt aluminate.     

Influence of aluminium precursor on physico-chemical properties of aluminium hydroxides and oxides Part II. Al(ClO4)3·9H2O

Aluminium hydroxide was precipitated during a hydrolysis of aluminium perchlorate in ammonia medium. The materials were studied with the following methods: thermal analysis, IR spectroscopy, X-ray diffraction, low-temperature nitrogen adsorption and adsorption–desorption of benzene vapours. Freshly precipitated boehmite had a high value of S_BET=211 m² g^–1 determined from nitrogen adsorption, good sorption capacity for benzene vapours, developed mesoporous structure and hydrophobic character. After prolonged refluxing at elevated temperature its crystallinity increased which was accompanied by an increase of specific surface determined from nitrogen adsorption up to 262m²g^–1 , decrease of sorption capacity for benzene vapours and stronger hydrophobic character. The calcinations of all boehmites at temperature up to 1200°C resulted in formation of à-Al₂O₃ via transition form of γ-, δ- and θ-Al₂O₃. The samples of aluminium oxides obtained after calcination at 550 and 900°C were characterised with high values of specific surface area of 205–220 and 138–153 m² g^–1 , respectively. The SBET values calculated for the oxide samples derived from aged hydroxides and calcined at 1200°C are higher than for the analogous sample prepared without the ageing step. It was concluded that the process of ageing at elevated temperature developed thermal stability of aluminium oxides.     

The heat capacities and thermodynamic properties of NiAl2O4 and CoAl2O4 measured by adiabatic calorimetry from T = (4 to 400) K

The low-temperature heat capacity of NiAl₂O₄ and CoAl₂O₄ was measured between T = (4 and 400) K and thermodynamic functions were derived from the results. The measured heat-capacity curves show sharp anomalies peaking at around T = 7.5 K for NiAl₂O₄ and at T = 9 K for CoAl₂O₄. The exact cause of these anomalies is unknown. From our results, we suggest a standard entropy for NiAl₂O₄ at T = 298.15 K of (97.1 ± 0.2) J · mol^?1 · K^?1 and for CoAl₂O₄ of (100.3 ± 0.2) J · mol^?1 · K^?1.     

大孔Mo-Ni/Al2O3催化剂的催化裂化柴油加氢性能研究

采用三次纳米自组装合成法,制备了一种以二次纳米自组装Al₂O₃为主体的大孔主客体催化剂FA-40,具有0.78cm³·g^-1的孔容、114m₂·g^-1的比表面积、27nm的平均孔径、6.0nm和40nm的双峰孔结构、孔分布在10~100nm高度集中、低堆积密度为0.56g·cm^-3、活性金属含量高达35.70%。XRD和TEM分析结果显示,活性金属以直径小于2nm的微晶态纳米粒子形式均匀分散于主体表面。采用劣质催化裂化柴油进行20h加氢实验评价,反应趋于稳定时,FA-40的脱硫、脱氮及芳烃饱和率分别达到94.4%、95.5%和67.9%,与F-5相比分别提高了20%、80%和140%。300h的长周期加氢实验表明,FA-40具有良好的加氢性能。     

Preparation of thiazolidin-4-one derivatives using ZnO–NiO–NiFe2O4 nano-composite system

The hydrothermal synthesis of ZnO–NiO–NiFe₂O₄ nano-composite is reported. The sample was utilized to characterize via XRD, FE-SEM, EDS, FT-IR, UV–Vis, and BET techniques. The sample consisted of three different phases as ZnO (hexagonal), NiO (cubic), and NiFe₂O₄ (cubic) with the average particle size as 34 nm and specific surface area, average pore diameter, and pore volume as 64.35 m² g^?1, 13.02 nm, and 0.201 cm³ g^?1, respectively. Catalytic behavior of the nano-composite was investigated on the synthesis of thiazolidin-4-one derivatives under thermal and ultrasonic irradiation condition. Our results show that the catalytic activity of ZnO–NiO–NiFe₂O₄ nano-composite is much higher than ZnO, NiO, and NiFe₂O₄ metal oxides. All products were prepared in high yields with short reaction times. In addition, the catalyst was recovered for at least five times.

     

Removal of sulfur from commercial kerosene using nanocrystalline NiFe2O4 based sorbents

This paper deals with the simultaneous removal of sulfur from commercial kerosene at room temperature using sorbents containing NiFe₂O₄ nanoparticles. The nanocrystalline NiFe₂O₄ based sorbents were prepared using the combustion route. The effect of fuel content on the surface properties and desulferization activity of Ni/Fe mixed oxide sorbents has been studied.It was observed that incorporation of metal cations (Ni²⁺) into the hematite (α-Fe₂O₃) crystal structure alters the surface properties and desulferization activity of the investigated oxides, which in turn depends on the nature and concentration of the incorporated metal cation and the released heat during the combustion process. The effect of fuel content in modifying the resultant surface area could be directly related to the variations in the rate of crystal growth of the solids studied depending upon preparation temperature. Interestingly, all the prepared ferrites exhibit a narrow pore size distribution in the range of 0.9–2 nm. The capacity of NiFe₂O₄ to adsorb sulfur from commercial kerosene was evaluated in terms of their textural and chemical characteristics.     

Structural,textural and catalytic properties of pure and Li-doped NiO/Al2O3 and CuO/Al2O3 catalysts

Pure and Li-doped NiO/Al₂O₃ and CuO/Al₂O₃ catalysts were prepared to contain 2, 4 and 8 wt.% of Ni and Cu, respectively. The structural properties were determined using DTA, XRD and FTIR techniques, and the textural properties of the catalysts were determined from their adsorption–desorption isotherms of nitrogen at 77 K. The chemisorption of hydrogen at 473–823 K with the pre-reduced catalysts was measured. The data obtained allowed the determination of the metal surface area, S (m²/g); the percentage of metal distribution, R; and the diameter of metal crystallite, d (nm). The amount of surface acidity, measured in mmol/g, was determined from the amount of chemisorbed pyridine necessary to completely inhibit the catalytic dehydration (DHD) of isopropanol. The conversion of isopropanol at 533–623 K was investigated using the micro-catalytic pulse technique. DTA, XRD and FTIR indicated that NiO and CuO exist as separate phases with crystallite sizes too small to be detected. No evidence has been gathered to indicate the existence of an aluminate phase.With the increase of metal loading, the surface area decreased whereas the total pore volume and the mean pore radius increased. Conversion of iso-propanol to propene proceeded via (DHD) on surface acid sites, and conversion of isopropanol to acetone proceeded via dehydrogenation (DHG) on redox sites. DHD and DHG exhibited first-order kinetics, and the rates of both reactions increased with temperature, with the latter being more temperature-dependent.     

Preparation and electrochemical performance of monodisperse Li4Ti5O12 hollow spheres

Monodisperse Li₄Ti₅O₁₂ hollow spheres were prepared by using carbon spheres as templates. Scanning electron microscopy images show hollow spheres that have an average outer diameter of 1.0 μm and an average wall thickness of 60 nm. Compared with Li₄Ti₅O₁₂ solids, the hollow spherical Li₄Ti₅O₁₂ exhibit an excellent rate capability and capacity retention and can be charged/discharged at 10 C (1.7 A g⁻¹) with a specific capacity of 100 mA h g⁻¹, and after 200 charge and discharge cycles at 2 C, their specific capacity remain very stable at 150 mA h g⁻¹. It is believed that the hollow structure has a relatively large contact surface between Li₄Ti₅O₁₂ and liquid electrolyte, resulting in a better electrochemical performance at high charge/discharge rate.     

Shape selective oxidation by a microporous platinum-polyoxometalate

Shape selective catalytic behaviour of a platinum-promoted polyoxometalate, 0.5 wt% Pt−Cs_2.1H_{0 9}PW₁₂O₄₀, has been studied for complete oxidation of methane and benzene. The pore size of this catalyst determined by adsorptions of n-butane and isobutane was close to the molecular size of n-butane (0.43 nm). Ar and N₂ porosimetries demonstrated that 0.5 wt% Pt−Cs_{2 1}H_{0 9}PW₁₂O₄₀ possesses unimodal distribution of pores in ultramicropore region. External surface area was estimated to be less than 3% that of the total surface area (61 m² g⁻¹) of the catalyst. Owing to the restricted pores, this exhibited efficient shape selectivity; methane (molecular size; 0.38 nm) was readily oxidized, while the oxidations of the larger molecule such as benzene (0.59 nm) were greatly suppressed. These results indicate that 0.5 wt% Pt−Cs_{2 1}H_{0 9}PW₁₂O₄₀ is a promising microporous catalyst.     

New synthesis of pure CexZr1?xO2 mixed oxides (0?≤?x?≤?1) by an epoxide sol–gel method

Pure ceria-zirconia mixed oxides Ce _x Zr_1−x O₂ with high specific surface area were synthesized with a new epoxyde driven sol–gel route and characterized by thermal analysis, X-ray diffraction studies and transmission electron microscopy. This sol–gel method is cheap and uses only a few steps. The Ce _x Zr_1−x O₂ mixed oxides were obtained in the range of 0 ≤ x ≤ 1 (except for x = 0.8) and crystallised at 350 °C after decomposition of the gels. This temperature is very low in comparison with the other methods. The studies of the influence of different synthesis parameters (concentration of the sol and decomposition temperature) allowed us to determine the conditions to obtain the best homogeneity in the gel to avoid the formation of a mixture of phases instead of mixed oxides. This approach leads to the synthesis of oxide with specific surface area above 100 m² g⁻¹. The elaboration of an ambigel could increase this value up to 195 m² g⁻¹ for x = 0.5. This sol–gel synthesis offers new perspectives for these oxides in several applications. Generally, these oxides are difficult to obtain pure in large range of composition at low-temperature and with high specific surface area by other methods.     

Synthesis of high surface area nanometer magnesia by solid-state chemical reaction

Nanometer MgO samples with high surface area, small crystal size and mesoporous texture were synthesized by thermal decomposition of MgC₂O₄ · 2H₂O prepared from solid-state chemical reaction between H₂C₂O₄ · 2H₂O and Mg (CH₃COO)₂ · 4H₂O. Steam produced during the decomposition process accelerated the sintering of MgO, and MgO with surface area as high as 412 m² · g⁻¹ was obtained through calcining its precursor in flowing dry nitrogen at 520°C for 4 h. The samples were characterized by X-ray diffraction, N₂ adsorption, transmission electron microscopy, thermogravimetry, and differential thermal analysis. The as-prepared MgO was composed of nanocrystals with a size of about 4–5 nm and formed a wormhole-like porous structure. The MgO also had good thermal stability, and its surface areas remained at 357 and 153 m²·g⁻¹ after calcination at 600 and 800°C for 2 h, respectively. Compared with the MgO sample prepared by the precipitation method, MgO prepared by solid-state chemical reaction has uniform pore size distribution, surface area, and crystal size. The solid-state chemical method has the advantages of low cost, low pollution, and high yield, therefore it appears to be a promising method in the industrial manufacture of nanometer MgO. Translated from Chinese Journal of Catalysis, 2006, 27(9): 793–798 (in Chinese)     

Investigation of the incorporation of electrolyte anions in porous anodic Al2O3 films by employing a suitable probe catalytic reaction

A new method has been developed capable of describing the incorporation of electrolyte anions along the pore wall surface and across both the barrier layer and the pore wall oxide after the establishment of the steady state of growth of porous anodic Al₂O₃ where other methods cannot be applied to obtain reliable results. The knowledge of the nature/composition of anodic oxides as regards the incorporation of species like electrolyte anions is of specific importance for both the understanding of the electrochemical mechanism of oxide production and growth and the scientific and technological applications of porous anodic Al₂O₃ films. The method consists of the selection and use of a suitable catalytic probe reaction on porous anodic oxides at thicknesses varying from a value near zero up to the maximum limiting thickness and the treatment of the experimental reaction rate results by a properly developed mathematical formalism. This method was employed in anodic Al₂O₃ films prepared in H₂SO₄ anodizing electrolyte at a constant bath temperature and different current densities using as a probe reaction the decomposition of HCOOH on these oxides, which is almost exclusively a dehydration reaction, at relatively high reaction temperatures, 350 °C and 390 °C, where the effect of other species except SO₄ ²⁻ incorporated in the oxide on the reaction rate is eliminated. It has been shown that the fraction of the intercrystallite surfaces occupied by SO₄ ²⁻ follows a parabola-like distribution. It has a significant value at the pore base surface, depending on the current density, then it passes through a maximum along the pore wall surface and across both the barrier layer and the pore walls near the pore bases at positions depending on the current density and then becomes almost zero at the mouths of the pores of the oxide with the maximum limiting thickness and at both the Al₂O₃/Al interface and cell boundaries. The maximum value of the surface coverage is almost independent of the current density and is always near 1, showing an almost complete saturation of intercrystalline surfaces at these positions. The above distribution of surface coverage predicts a qualitatively similar distribution of the SO₄ ²⁻ bulk concentration across both the barrier layer and pore wall oxide around the pore bases. The method may be improved and developed further either for a more detailed investigation of the above films or to investigate films prepared in other pore-forming electrolytes. Received: 30 July 1998 / Accepted: 30 September 1998     

Density and surface tension of the systems CaO-FeO-Fe2O3-MgO, CaO-FeO-Fe2O3-ZnO and CaO-Fe2O3-Cu2O

The density and surface tension of melts of the systems CaO-FeO-Fe₂O₃ MgO at the temperature 1623 K, CaO-FeO-Fe₂O₃-ZnO at 1573 K, and CaO-Fe₂O₃-Cu₂O at 1573 K were determined using the maximum bubble pressure method. The molar volume, the excess molar volume, and the excess surface tension were calculated on the basis of the obtained data. From these properties information on the interactions of components and possible chemical reactions between them was obtained. Due to the absence of silica and the low concentration of other network-forming oxides, only isolated FeO ₄ ⁵⁻ tetrahedra and the CaO·FeO ionic pairs are formed in these basic melts, the donor of the oxygen atoms being either CaO, FeO, or both CaO+FeO oxides. Even the observed ternary interactions may be attributed to the formation of the anions FeO ₄ ⁵⁻ only.     

Rational Construction of 2D Fe3O4@Carbon Core–Shell Nanosheets as Advanced Anode Materials for High-Performance Lithium-Ion Half/Full Cells

Transition metal oxides have vastly limited practical application as electrode materials for lithium-ion batteries (LIBs) due to their rapid capacity decay. Here, a versatile strategy to mitigate the volume expansion and low conductivity of Fe₃O₄ by coating a thin carbon layer on the surface of Fe₃O₄ nanosheets (NSs) was employed. Owing to the 2D core–shell structure, the Fe₃O₄@C NSs exhibit significantly improved rate performance and cycle capability compared with bare Fe₃O₄ NSs. After 200 cycles, the discharge capacity at 0.5 A g⁻¹ was 963 mA h g⁻¹ (93 % retained). Moreover, the reaction mechanism of lithium storage was studied in detail by ex situ XRD and HRTEM. When coupled with a commercial LiFePO₄ cathode, the resulting full cell retains a capacity of 133 mA h g⁻¹ after 100 cycles at 0.1 A g⁻¹, which demonstrates its superior energy storage performance. This work provides guidance for constructing 2D metal oxide/carbon composites with high performance and low cost for the field of energy storage.     

Catalytic properties of a (A=Ba, Ca, Sr and Y) modified lanthanum hexaaluminates for catalytic combustion of methane

A series of hexaaluminates, La_0.8A_0.2MnAl₁₁O_19−δ samples (A = Ba, Ca, Sr and Y) as new catalysts were prepared by carbonate precipitation and calcined at high temperature. The structure and properties of these samples were characterized by XRD, BET and XPS techniques. Upon calcination at 1200°C, the hexaaluminate structure was formed and it retained the specific surface area of 17∼20 m²g⁻¹. The La_0.8Ca_0.2MnAl₁₁O_19−δ catalyst has a surface area of 19.3 m²g⁻¹ and shows a good activity in CH₄ combustion.