Multiple melting behavior of poly(butylene succinate). I. Thermal analysis of melt‐crystallized samples

The multiple melting behavior of poly(butylene succinate) (PBSu) was studied with differential scanning calorimetry (DSC). Three different PBSu resins, with molecular weights of 1.1 × 10⁵, 1.8 × 10⁵, and 2.5 × 10⁵, were cooled from the melt (150 °C) at various cooling rates (CRs) ranging from 0.2 to 50 K min^?1. The peak crystallization temperature (T_c) of the DSC curve in the cooling process decreased almost linearly with the logarithm of the CR. DSC melting curves for the melt‐crystallized samples were obtained at 10 K min^?1. Double endothermic peaks, a high‐temperature peak H and a low‐temperature peak L, and an exothermic peak located between them appeared. Peak L decreased with increasing CR, whereas peak H increased. An endothermic shoulder peak appeared at the lower temperature of peak H. The CR dependence of the peak melting temperatures [T_m(L) and T_m(H)], recrystallization temperature (T_re), and heat of fusion (ΔH) was obtained. Their fitting curves were obtained as functions of log(CR). T_m(L), T_re, and ΔH decreased almost linearly with log(CR), whereas T_m(H) was almost constant. Peak H decreased with the molecular weight, whereas peak L increased. It was suggested that the rate of the recrystallization decreased with the molecular weight. T_m(L), T_m(H), T_re, and T_c for the lowest molecular weight sample were lower than those for the others. In contrast, ΔH for the highest molecular weight sample was lower than that for the others. If the molecular weight dependence of the melting temperature for PBSu is similar to that for polyethylene, the results for the molecular weight dependence of PBSu can be explained. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 2411–2420, 2002     

Multiple melting behavior of poly(butylene succinate). II. Thermal analysis of isothermal crystallization and melting process

The multiple melting behavior of poly(butylene succinate) (PBSu) was studied with differential scanning calorimetry (DSC). Three different PBSu resins, with molecular weights (MWs) of 1.1 × 10⁵, 1.8 × 10⁵, and 2.5 × 10⁵, were isothermally crystallized at various crystallization temperatures (T_c) ranging from 70 to 97.5 °C. The T_c dependence of crystallization half‐time (τ) was obtained. DSC melting curves for the isothermally crystallized samples were obtained at a heating rate of 10 K min⁻¹. Three endothermic peaks, an annealing peak, a low‐temperature peak L, and a high‐temperature peak H, and an exothermic peak located between peaks L and H clearly appeared in the DSC curve. In addition, an endothermic small peak S appeared at a lower temperature of peak H. Peak L increased with increasing T_c, whereas peak H decreased. The T_c dependence of the peak melting temperatures [T_m(L) and T_m(H)], recrystallization temperature (T_re), and heat of fusion (ΔH) was obtained. Their fitting curves were obtained as functions of T_c. T_m(L), T_re, and ΔH increased almost linearly with T_c, whereas T_m(H) was almost constant. The maximum rate of recrystallization occurred immediately after the melting. The mechanism of the multiple melting behavior is explained by the melt‐recrystallization model. The high MW samples showed similar T_c dependence of τ, and τ for the lowest MW sample was longer than that for the others. Peak L increased with MW, whereas peak H decreased. In spite of the difference of MW, T_m(L), T_m(H), and T_re almost coincided with each other at the same T_c. The ΔH values, that is crystallinity, for the highest MW sample were smaller than those for the other samples at the same T_c. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2039–2047, 2005     

Synthesis and characterization of poly(L‐lactic acid)–poly(ε‐caprolactone) multiblock copolymers by melt polycondensation

An Erratum has been published for this article in J. Polym. Sci. Part A: Polym. Chem. (2004) 42(22) 5845 New multiblock copolymers derived from poly(L‐lactic acid) (PLLA) and poly(ε‐caprolactone) (PCL) were prepared with the coupling reaction between PLLA and PCL oligomers with ? NCO terminals. Fourier transform infrared (FTIR), ¹³C NMR, and differential scanning calorimetry (DSC) were used to characterize the copolymers and the results showed that PLLA and PCL were coupled by the reaction between ? NCO groups at the end of the PCL and ? OH (or ? COOH) groups at the end of the PLLA. DSC data indicated that the different compositions of PLLA and PCL had an influence on the thermal and crystallization properties including the glass‐transition temperature (T_g), melting temperature (T_M), crystallizing temperature (T_c), melting enthalpy (ΔH_m), crystallizing enthalpy (ΔH_c), and crystallinity. Gel permeation chromatography (GPC) was employed to study the effect of the composition of PLLA and PCL and reaction time on the molecular weight and the molecular weight distribution of the copolymers. The weight‐average molecular weight of PLLA–PCL multiblock copolymers was up to 180,000 at a composition of 60% PLLA and 40% PCL, whereas that of the homopolymer of PLLA was only 14,000. A polarized optical microscope was used to observe the crystalline morphology of copolymers; the results showed that all polymers exhibited a spherulitic morphology. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5045–5053, 2004     

Effects of carbon nanotubes on crystallization and melting behavior of poly(L‐lactide) via DSC and TMDSC studies

In this work, multiwalled carbon nanotubes (MWNTs) were surface‐modified and grafted with poly(L ‐lactide) to obtain poly(L ‐lactide)‐grafted MWNTs (i.e. MWNTs‐g‐PLLA). Films of the PLLA/MWNTs‐g‐PLLA nanocomposites were then prepared by a solution casting method to investigate the effects of the MWNTs‐g‐PLLA on nonisothermal and isothermal melt‐crystallizations of the PLLA matrix using DSC and TMDSC. DSC data found that MWNTs significantly enhanced the nonisothermal melt‐crystallization from the melt and the cold‐crystallization rates of PLLA on the subsequent heating. Temperature‐modulated differential scanning calorimetry (TMDSC) analysis on the quenched PLLA nanocomposites found that, in addition to an exothermic cold‐crystallization peak in the range of 80–120 °C, an exothermic peak in the range of 150–165 °C, attributed to recrystallization, appeared before the main melting peak in the total and nonreversing heat flow curves. The presence of the recrystallization peak signified the ongoing process of crystal perfection and, if any, the formation of secondary crystals during the heating scan. Double melting endotherms appeared for the isothermally melt‐crystallized PLLA samples at 110 °C. TMDSC analysis found that the double lamellar thickness model, other than the melting‐recrystallization model, was responsible for the double melting peaks in PLLA nanocomposites. Polarized optical microscopy images found that the nucleation rate of PLLA was enhanced by MWNTs. TMDSC analysis found that the incorporation of MWNTs caused PLLA to decrease the heat‐capacity increase (namely, ΔC_p) and the C_p at glass transition temperature. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1870–1881, 2007     

Interfacial stability of compatibilizers dictated by the thermodynamic interactions in an immiscible system and the effects of micelles on the crystallization of PLLA

Poly(L-lactic acid) (PLLA) is blended with three acrylonitrile-butadiene-styrene (ABS) materials and compatibilized by a kind of poly(methyl methacrylate) (PMMA)-type reactive comb (RC) polymer (RC). The compatibilization efficiency is found to be dictated by the thermodynamic interactions between PMMA-type compatibilizers and ABS materials. For one type of ABS, which is composed of methyl methacrylate (MMA), styrene (St), acrylonitrile (AN), and butadiene (BD), the MMA component of ABS is able to strengthen the interaction between the PMMA-type compatibilizers and the ABS phase and thus the obtained compatibilized PLLA/ABS blends display a fine cocontinuous morphology and excellent mechanical properties. For the other two ABS materials, which are constituted by St, AN, and BD, it has been found that the PMMA-type compatibilizers are pulled out from the interface to form micelles in the PLLA phase, on account of the weakening interactions between ABS and PMMA-type compatibilizers. The thus formed micelles can interact with the crystallization of PLLA and the melting temperature (T_m) of PLLA is split into a lower and a higher peak firstly, compared to the T_m of neat PLLA, then significantly decrease to lower temperature, with increasing the amount of micelles in the PLLA phase. © 2020 Wiley Periodicals, Inc. J. Polym. Sci. 2020 , 58, 372–382     

High-temperature aging of Halar film. II. Analysis of melting behavior

Melting behavior of an experimental Halar film, a predominantly alternating 1:1 copolymer of ethylene (E) and chlorotrifluoroethylene (CTFE), has been studied. Differential scanning calorimetry (DSC) reveals single or double melting peaks, depending upon the thermal history. The lower-temperature melting peak T_m1 is produced only by the thermal treatment and shows a strong dependence on annealing time and temperature. On the basis of the DSC and x-ray data it can be suggested that T_m1 represents the melting of relatively small crystallites formed upon annealing. The higher-temperature melting peak T_m2 is always shown at 238°C. (Note: the specification for commercial Halar product is 240°C. The slightly lower melting temperature reported in this study is probably due to the fact that we are dealing with an experimental melt-processed material.) On the basis of the heating rate study we propose that Halar crystallizes with stable crystals (T_m2 = 238°C) regardless of the crystallization conditions, i.e., quenching, slow cooling, or even annealing. Crystals of Halar have a heat of fusion of approximately 35 cal/g or 146 kJ/kg. Detailed analysis of the melting behavior of Halar is presented.     

Effect of microstructure on hydrolytic degradation studies of poly (l-lactic acid) by FTIR spectroscopy and differential scanning calorimetry

Structural changes during thermally induced crystallization and alkaline hydrolysis of Poly(l-lactic acid) (PLLA) films were investigated using differential scanning calorimetry (DSC), FTIR spectroscopy, weight loss, HPLC and optical microscopy. It was shown that crystallinity (χ_c), glass transition temperature (T_g) and melting temperature (T_m) were found to be strongly annealing temperature (T_a) dependent. The FTIR study of PLLA films suggested that the bands at 921 and 956 cm⁻¹ could be used to monitor the structural changes of PLLA. An independent infrared spectroscopic method was developed for the first time to determine crystallinity of PLLA before degradation and it showed good qualitative correlation with DSC crystallinity. The higher crystallinity values determined by FTIR were attributed to the intermediate phase included in the IR crystallinity. Both the weight loss data and the percentage of lactic acid obtained by HPLC showed that the alkaline hydrolysis of PLLA films increased with increasing crystallinity. The DSC observation showed an increase in T_g and no significant change in T_m and heat of fusion, while IR showed an increase in IR crystallinity with increasing hydrolysis time. The increase in IR crystallinity and T_g with hydrolysis time suggested that degradation progressed from the edges of the crystalline lamellas without decreasing lamellar thickness, but increased the intermediate phase and the short-range order.     

Cold crystallization and multiple melting behavior of poly(l-lactide) in homogeneous and in multiphasic epoxy blends

Cold crystallization and melting of poly(l-lactide) (PLLA) blended with an uncured or with an amino-cured epoxy resin (diglycidyl ether of bisphenol-A [DGEBA]) were investigated. It was found that the uncured PLLA/DGEBA blends were miscible, as they exhibited a single composition-dependent glass transition temperature (T _g). Melting point depression measurements indicated the existence of some type of interaction between the blend components, which was confirmed by Fourier transform infrared spectroscopy. Depending on the crystallization conditions and on the blend composition, a mixture of α and α′ crystals have been detected in PLLA and in uncured DGEBA/PLLA blends when crystallized from the glassy state. At high DGEBA contents, preferably imperfect α crystals are formed. On the contrary, at low DGEBA contents, the α′ form predominates and an exotherm associated to the α′–α transformation appears on the differential scanning calorimetry (DSC) scan before the main melting peak. Upon curing, the system transforms from a homogeneous mixture with a single refractive index into an opaque multiphasic one, as revealed by the existence of two T _gs in the DSC scans. These cross-linked immiscible blends displayed a single crystallization exotherm which scarcely changed with composition, and PLLA cold crystallized mainly into the α′ form from an almost pure PLLA phase; subsequently, the α′ crystals transform into the α form just before melting during the DSC scan.     

Random multiblock poly(ester amide)s containing poly(L‐lactide) and cycloaliphatic amide segments: Synthesis and biodegradation studies

Novel multiblock poly(ester amide)s containing poly(L ‐lactide) and cycloaliphatic amide segments were synthesized from telechelic oligomer of α,ω‐hydroxyl terminated poly(L ‐lactide), 1,3‐cyclohexylbis(methylamine), and sebacoylchloride by the “two‐step” interfacial polycondensation method. The blocky nature of PEAs was established by FTIR and ¹H NMR spectroscopies. The effect of relative content of ester and amide segments on the crystallization nature of PEAs was investigated by WAXD and DSC analyses. PEAs having lower content of PLLA, PEA 1 and PEA 2, showed a crystallization pattern analogous to polyamides, whereas PEA 3, having higher content of PLLA, showed two crystalline phases characterized by polyester and polyamide segments. Random nature of PEAs was observed from single T_g values. Biodegradation studies using the enzyme lipase from Candida Cylindracea showed higher degradation rate for PEA 3 than that for PEA 1 and PEA 2. FTIR, ¹H NMR, and DSC analyses of the degraded products indicated the involvement of ester linkages in the degradation process. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3250–3260, 2006     

Calorimetric analysis of the multiple melting behavior of melt-crystallized poly(l-lactic acid) with a low optical purity

The polymorphous crystallization and multiple melting behavior of poly(l-lactic acid) (PLLA) with an optical purity of 92 % were investigated after isothermally crystallized from the melt state by wide-angle X-ray diffraction and differential scanning calorimetry. Owing to the low optical purity, it was found that the disordered (α′) and ordered (α) crystalline phases of PLLA were formed in the samples crystallized at lower (<95 °C) and higher (≥95 °C) temperatures, respectively. The melting behavior of PLLA is different in three regions of crystallization temperature (T _c) divided into Region I (T _c < 95 °C), Region II (95 °C ≤ T _c < 120 °C), and Region III (T _c ≥ 120 °C). In Region I, an exothermic peak was observed between the low-temperature and high-temperature endothermic peaks, which results from the solid–solid phase transition of α′-form crystal to α one. In Region II, the double-melting peaks can be mainly ascribed to the melting–recrystallization–remelting of less stable α crystals. In Region III, the single endotherm shows that the α crystals formed at higher temperatures are stable enough and melt directly without the recrystallization process during heating.     

A new route of manipulation of poly(L‐lactic acid) crystallization by self‐assembly of p‐tert‐butylcalix[8]arene and toluene

A novel nucleating agent (TBC8‐t), self‐assembled with p‐tert‐butylcalix[8]arene (TBC8) and toluene, was used to manipulate the crystallization behavior of poly(L ‐lactic acid) (PLLA). Toluene molecules were used to adjust the crystallization structure of TBC8. Differential scanning calorimetry results show that the crystallization peak temperature (T_c) and crystallization rate (ΔH_c/time) of PLLA nucleated with TBC8‐t are 132.3 °C and 0.24 J/gs, respectively, which are much higher than that with conventional nucleating agent‐talc (T_c = 119.3 °C, ΔH_c/time = 0.13 J/gs). The results of polarized optical microscopy demonstrate that TBC8‐t could greatly enhance the crystallization rate of PLLA by increasing the nucleation rate rather than crystal growth rate. Along with an improvement of the crystallization rate, the crystalline morphology of PLLA is also affected by TBC8‐t. The addition of TBC8‐t transforms most of the original spherulite crystals into sheaf‐like crystals. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1235–1243, 2010     

Study of the Crystallization of an Aromatic Poly-ether-ketone (PK99) by Calorimetric and X-ray Analysis

An analysis of the crystallization behaviour of a new poly(aryl-ether-ether-ketone-ketone), PK99, by differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) is presented. Isothermal crystallization TG were obtained in the whole range between the glass transition temperature (T _g) and the melting temperature (T _m) as a consequence of the slow crystallization kinetics stemming from the closeness of these transitions. The calorimetric results, compared with WAXD data, were applied to determine the theoretical melting temperature and crystallization enthalpy. The DSC and WAXD data were combined in order to calculate the total amount of the crystallizable fraction of the polymer, and a model was proposed to explain the difference between the fractions of crystallinity observed with these techniques. The thermal and X-ray data were also correlated with different lamellar morphologies arising from the crystallization conditions. Finally, DSC experiments on the crystallized sample were used to detect the presence of a rigid amorphous phase which does not relax at T _g. This revised version was published online in July 2006 with corrections to the Cover Date.     

A study of phase separation of crystalline and miscible polymer blends. Poly(ε-caprolactone)/poly(styrene-co-acrylonitrile)

The phase separation of a crystalline and miscible polymer blend, poly(ε-caprolactone) /poly(styrene-co-acrylonitrile) (PCL/SAN), has been studied by differential scanning calorimetry (DSC), using a SAN containing 28.3% of acrylonitrile units. Several phenomena can be associated with the occurrence of phase separation depending upon the composition of the mixture. Following annealing at high temperatures, below and above the phase separation temperature T_c, three cases can be distinguished. In Case I, there is no sign of crystallization during quenching and DSC scanning, but a melting peak is observed at T_c, and above. In Case II, there is no crystallization on quenching but it does occur during the DSC run; the shift of the crystallization peak can then be related to T_c. In Case III, there is crystallization on quenching, and additional crystallization during the DSC run; the change of area of the crystallization peak is indicative of T_c. From these observations, the phase diagram of the system was determined. © 1993 John Wiley & Sons, Inc.     

Isothermal crystallization behavior of poly(L‐lactide) in poly(L‐lactide)‐block‐poly(ethylene glycol) diblock copolymers

The crystal unit‐cell structures and the isothermal crystallization kinetics of poly(L ‐lactide) in biodegradable poly(L ‐lactide)‐block‐methoxy poly(ethylene glycol) (PLLA‐b‐MePEG) diblock copolymers have been analyzed by wide‐angle X‐ray diffraction and differential scanning calorimetry. In particular, the effects due to the presence of MePEG that is chemically connected to PLLA as well as the PLLA crystallization temperature T_C are examined. Though we observe no variation of both the PLLA and MePEG crystal unit‐cell structures with the block ratio between PLLA and MePEG and T_C, the isothermal crystallization kinetics of PLLA is greatly influenced by the presence of MePEG that is connected to it. In particular, the equilibrium melting temperature of PLLA, T, significantly decreases in the diblock copolymers. When the T_C is high so that the crystallization is controlled by nucleation, because of the decreasing T and thereafter the nucleation density with decreasing PLLA molecular weight, the crystallinity of PLLA also decreases with a decrease in the PLLA molecular weight. While, for the lower crystallization temperature regime controlled by the growth mechanism, the crystallizability of PLLA in copolymers is greater than that of pure PLLA. This suggests that the activation energy for the PLLA segment diffusing to the crystallization site decreases in the diblocks. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2438–2448, 2006     

溶剂诱导的聚乳酸/聚乳酸衍生物共结晶行为

通过溶液浇铸法制备不同组分的左旋聚乳酸(PLLA)和聚(L-2-羟基-3-甲基丁酸)(PL-2H3MB)共混物.运用差示扫描量热仪(DSC)、偏光显微镜(POM)、广角X射线衍射(WAXD)和热重分析仪(TGA)分析共混物的结晶、熔融行为和热稳定性.通过观察到DSC加热曲线中新的熔融峰判断PLLA和PL-2H3MB共晶...     

Effects of take‐up speed on the structure and properties of melt‐spun poly(L‐lactic acid) fibers

Poly(L ‐lactic acid) (PLLA) filament fibers were prepared by one‐step melt spinning process and the effects of variations in take‐up speed on their thermal properties, mechanical properties, and crystalline structures were investigated. Differential scanning calorimetry (DSC) results revealed that the PLLA fibers showed multiple melting peaks and that the melting peak appearing at a lower temperature moved lower while that at a higher temperature moved higher with increasing take‐up speed. The glass transition temperature (T_g) obtained from dynamic mechanical analysis (DMA) increased with increasing take‐up speed. The tenacity increased and the boiling water shrinkage (BWS) decreased with increasing take‐up speed. However, these mechanical and thermal properties were stabilized at take‐up speeds over 3500 m/min. The melt‐spun PLLA fibers of this study showed an α‐form crystal structure which was not affected by the take‐up speed. The change in the tendency of the thermal and mechanical properties at around 3500 m/min did not appear to result from the change in crystal form but rather from the change in crystallite size and crystallite orientation. Copyright © 2008 John Wiley & Sons, Ltd.     

Self-nucleation and recrystallization of isotactic polypropylene (α phase) investigated by differential scanning calorimetry

The crystallization behavior after partial or complete melting of the α phase of iPP is examined by combined differential scanning calorimetry (DSC) and optical microscopy: calorimetric results are directly correlated with corresponding morphologies of microtome sections of DSC samples. On partial melting at various temperatures (hereafter referred to as T_s) located in a narrow range (4°C) below and near T_m, the number of nuclei increases (as in classical self-nucleation experiments), by several orders of magnitude; on subsequent cooling, the crystallization peak is shifted by up to 25°C. After partial melting in the lower part of the T_s range and recrystallization, the polymers display a prominent morphology “memory effect” whereby a phantom pattern of the initial spherulite morphology is maintained. After partial melting in the upper part of the T_s range the initial morphology is erased and self-nucleation affects only the total number of nuclei. The present experimental procedures make it possible to define, under “standard” conditions, the crystallization range of the polymer and in particular, the maximum crystallization temperature achievable when “ideally” nucleated. © John Wiley & Sons, Inc.     

Preparation of oriented β‐form poly(L‐lactic acid) by solid‐state extrusion

Melt‐crystallized, low molecular weight poly(L ‐lactic acid) (PLLA) consisting of α crystals was uniaxially drawn by solid‐state extrusion at an extrusion temperature (T_ext) of 130–170 °C. A series of extrusion‐drawn samples were prepared at an optimum T_ext value of 170 °C, slightly below the melting temperature (T_m) of α crystals (～180 °C). The drawn products were characterized by deformation flow profiles, differential scanning calorimetry (DSC) melting thermograms, wide‐angle X‐ray scattering (WAXD), and small‐angle X‐ray scattering as a function of the extrusion draw ratio (EDR). The deformation mode in the solid‐state extrusion of semicrystalline PLLA was more variable and complex than that in the extensional deformation expected in tensile drawing, which generally gave a mixture of α and β crystals. The deformation profile was extensional at a low EDR and transformed to a parabolic shear pattern at a higher EDR. At a given EDR, the central portion of an extrudate showed extensional deformation and the shear component became progressively more significant, moving from the center to the surface region. The WAXD intensities of the (0010)_α and (003)_β reflections on the meridian as well as the DSC melting thermograms showed that the crystal transformation from the initial α form to the oriented β form proceeded rapidly with increasing EDR at an EDR greater than 4. Furthermore, WAXD showed that the crystal transformation proceeded slightly more rapidly at the sheath region than at the core region. This fact, combined with the deformation profiles (shear at the sheath and extensional at the core), indicated that the crystal transformation was promoted by shear deformation under a high pressure rather than by extensional deformation. Thus, a highly oriented rod consisting of only β crystals was obtained by solid‐state extrusion of melt‐crystallized, low molecular weight PLLA slightly below T_m. The structure and properties of the α‐ and β‐form crystals were also studied. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 40: 95–104, 2002     

Multiple melting behavior of poly(butylene succinate)

The multiple melting behavior of poly(butylenes succinate) (PBS) isothermally crystallized from the melt was investigated using differential scanning calorimetry (DSC), temperature modulated DSC (MDSC) and polarized optical microscopy. PBS exhibits at most four melting endotherms (denoted as T_m1, T_m2, T_m3, and T_m4 from high to low temperatures) and a crystallization exotherm (denoted as T_re) in the DSC heating trace. Multiple melting endotherms were observed even at high heating rates. The origins of each endothermal and exothermal peak were discussed in detail. It is suggested that: (i) the crystallization exothermic peak, T_re, relates to the recrystallization of the melt of the crystallites with lower thermal stability; (ii) the T_m1 is ascribed to the melting of crystallites formed through recrystallization; (iii) two crystal populations with different thermal stability are responsible for the T_m2 and T_m3; (iv) the T_m4, which is the annealing peak, represents the transition of the rigid amorphous fraction (RAF) from solid-like RAF into liquid-like amorphous fraction.     

Stepwise annealing of poly(butylene terephthalate)

Annealing of poly(butylene terephthalate) (PBT) was studied by differential scanning calorimetry (DSC) and small angle X‐ray scattering (SAXS) measurement. A PBT sample was annealed at a recrystallization temperature where recrystallization occurs with a maximum rate in the heating process of the sample. In the subsequent annealing steps, the annealed sample was annealed repeatedly at the recrystallization temperatures, and the stepwise annealing sample was obtained. Peak melting temperature (T_m) and sharpness of DSC peak of the stepwise annealing sample increased with the annealing step. A high melting‐temperature sample was obtained in a short time, and T_m increased up to 238.5°C which is higher than all the T_m values that appear in the literature. The long period calculated from SAXS curves of the stepwise annealing sample increased with the annealing step. The increase of crystallite size and perfection of the crystal in the stepwise annealing process is suggested. Annealing experiment indicated that T^°_m should be higher than about 235°C. T_m increased linearly with the annealing temperature of the final step in the stepwise annealing (T_a). The equilibrium melting temperature (T^°_m) for PBT was estimated to be 247°C by the application of a Hoffman–Weeks plot to the relation between T_m vs. T_a. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 2420–2429, 1999