脱氧La0.5Ca0.5MnO3样品的铁磁-反铁磁转变和电阻率变化

研究了氧空位对La0.5Ca0.5MnO3 (LCMO)多晶块材的电输运和磁性质的影响. 随着氧空位的增加, 样品在高温段的电阻率一直增加, 并满足绝热小极化子模型, 而低温段的电阻率先下降后上升, 并出现明显的dR/dT>0的行为, 直至最后变为绝缘的. 氧空位的增加抑止了反铁磁相的出现, 使得脱氧的LCMO样品不发生反铁磁转变, 进一步增加氧空位则会抑制铁磁相.     

Pr0.5Ca0.5MnO3/Si异质结输运特性和整流特性研究

利用固相反应法制备Pr_0.5Ca_0.5MnO₃(PCMO)靶材,并采用脉冲激光沉积法(PLD)在n型Si(111)基片上沉积PCMO外延薄膜,研究了薄膜的输运特性及薄膜与Si衬底形成异质结的整流特性.结果表明:在80—300 K温度范围内,PCMO薄膜的阻温关系符合变程跳跃模型,随着温度的升高表现出从一维到二维再到三维的转变,分析认为可能源于轨道自由度对电子输运特性的影响.PCMO/Si异质结在磁场作用下整流特性得到改善,且在正向电流方向出 关键词： 0.5Ca_0.5MnO₃')" href="#">Pr_0.5Ca_0.5MnO₃ Si 整流 正磁电阻     

电脉冲对多晶La0.7Ca0.3MnO3比热的影响

对电脉冲诱导的不同电阻态下La_0.7Ca_0.3MnO₃样品的比热进行了研究.实验结果表明,电脉冲导致La_0.7Ca_0.3MnO₃样品比热随电阻状态发生可逆变化.比热随电阻状态的减小而减小.低温比热拟合及不同电阻状态下的比热差与温度关系说明,声子对比热的贡献不随电阻状态变化,磁性和载流子对比热的贡献是导致La_0.7Ca_0.3MnO₃样品比热变化的原因.电脉冲诱导O离子沿一维扩展性缺陷的电化学迁移,导致材料中局部区域的O离子浓度发生变化.O离子浓度的变化导致载流子浓度的变化,同时载流子浓度的变化将使得低温下磁性耦合强度发生变化,从而导致比热发生变化. 关键词： 0.7Ca_0.3MnO₃')" href="#">La_0.7Ca_0.3MnO₃ 比热 氧离子迁移     

Y替代La2/3Ca1/3MnO3体系的结构与输运行为

系统研究了(La1-xYx)2/3Ca1/3MnO3(0.0≤x≤0.3)体系的结构和输运行为.结果表明，实验样品具有很好的单相结构，随Y掺杂浓度的增加，金属—绝缘体（M—I）转变温度T-MI向低温区移动，对应的峰值电阻率ρp升高，对x=0.3样品，较未替代样品（x=0.0）增幅达8个数量级.在外加磁场下，材料表现出很强的磁电阻效应.同时，从实验结果出发，直接给出了输运特性与晶体结构之间的关联，并从双交换模型和可变程跃迁理论出发，对实验结果进行了初步讨论. 关键词： La2/3Ca1/3MnO3锰氧化物 Y替代 晶体结构 输运行为     

La0.7Ca0.3MnO3和CeO2混合块状样品电输运性质及使用分形迭代电阻网络模型的计算模拟

固相反应方法制得的La_0.7Ca_0.3MnO₃ (LCMO)粉末与Ce O₂粉末均匀混合后压块烧结,对其进行了电阻率随温度变化的测量.观察到样品电阻率存在绝缘体-金属转变. 研究了烧结工艺、CeO₂的混合比例与样品的电阻率、结构和表面形貌的关系.结 果表明， 制备工艺对材料性能有相当大的影响，其中较低温度的烧结主要影响小晶粒及其晶粒间界， 而高温长时间烧结将影响大晶粒的形成.利用三维随机电阻网络（RRN）模型和蒙特卡罗方法 对这种混合块状样品的输运性质进行了模拟，模拟中使用了一种新的RRN平均方法.该模型得 到的数值模拟结果与实验结果在定性上是一致的.这说明以RRN模型来理解LCMO(x)-CeO ₂(1-x) 复合体系的导电状况是合理的，提出的随机电阻网络平均方法是合适的 . 关键词： 0.7Ca_0.3MnO₃')" href="#">La_0.7Ca_0.3MnO₃ 绝缘体-金属转变 随 机电阻网络 蒙特卡罗模拟     

La_(0.5)M_(0.5)MnO_3(M=Sr,Ba)的水热合成与表征

我们用水热法合成了钙钛矿锰氧化物La0.5M0.5MnO3(M=Sr,Ba)系列样品,研究了制备条件对结构、形貌和磁性的影响.     

多晶La0.7Sr0.3MnO3的低温输运性质和磁电阻效应

详细研究了由纳米晶粒组成的块体多晶La_0.7Sr_0.3MnO₃(LSM)的电阻率和磁电阻效应,以及它们的温度依赖性.随着温度从室温降低,电阻率(ρ)在250K附近存在一最大值,低于该温度后,样品表现为金属导电特性,随后在50K附近存在一极小值.也就是说在低于50K的温度范围内,随着温度降低ρ反而升高,表现为绝缘体性的导电特性.经研究发现,这种随温度降低ρ反而增加的现象与隧穿效应的理论模型(lnρ∝T^-1/2)符合得很好 关键词： 0.7Sr_0.3MnO₃')" href="#">多晶La_0.7Sr_0.3MnO₃ 隧道效应 隧道磁电阻效应     

La0.4Ca0.6MnO3系统中Mn位Fe和Cr掺杂效应的比较性研究

利用固相反应法制备了Mn位Fe³⁺和Cr³⁺掺杂的系列锰氧化物La_0.4Ca_0.6(Mn_1-x(y)B_x(y))O₃ (B=Fe³⁺ (0≤x≤0.1); Cr³⁺ (0≤y≤0.1)) 多晶样品,研究了掺杂对样品输运性质的影响.实验结果表明两种离子具有截 关键词： 锰氧化物 反铁磁 磁电阻效应     

La0.82Te0.18MnO3薄膜的输运特性和光诱导效应

用脉冲激光沉积法制备了非金属Te掺杂的钙钛矿锰氧化物La_0.82Te_0.18MnO₃单晶薄膜.该薄膜从83 K升温至373 K过程中发生金属-绝缘体相变，转变点温度为283 K.其电阻率在T<T_MI时符合电子-电子、电子-磁振子散射公式；在T>T_MI时为小极化子输运.薄膜在低温段连续激光(波长为532 nm，40 mW)作用下电阻率显著增大，电阻变化率在253 K达到最大值51.1%,该变化率远大于相同条件下的空穴掺杂材料；在高温段产生了较小的光电导，电阻变化率小于10%.这些现象主要与激光激励下自旋系统和小极化子的变化有关.La_0.82Te_0.18MnO₃薄膜在激光诱导下具有明显的与自旋相关的弛豫现象.激光开始作用时薄膜电阻率随时间的变化符合指数关系. 关键词： 0.82Te_0.18MnO₃薄膜')" href="#">La_0.82Te_0.18MnO₃薄膜 光诱导 输运特性 电子掺杂     

钙钛矿结构La0.9Sb0.1MnO3的庞磁电阻性质

一种新的钙钛矿结构的庞磁电阻氧化物La_0.9Sb_0.1MnO₃已用固态反应方法制 成，通过超导量子干涉器件(SQUID)装置测量研究了它的电输运性质和磁性质.x射线光电子 能谱分析证明，该氧化物中Sb的价态是+5价，因此该氧化物是一种新的电子掺杂型庞磁电阻 材料. 关键词： 钙钛矿结构 0.9Sb_0.1MnO₃')" href="#">La_0.9Sb_0.1MnO₃ 电子掺杂 庞磁电阻     

电脉冲对多晶La0.7Ca0.3MnO3比热的影响

对电脉冲诱导的不同电阻态下La_0.7Ca_0.3MnO₃样品的比热进行了研究.实验结果表明,电脉冲导致La_0.7Ca_0.3MnO₃样品比热随电阻状态发生可逆变化.比热随电阻状态的减小而减小.低温比热拟合及不同电阻状态下的比热差与温度关系说明,声子对比热的贡献不随电阻状态变化,磁性和载流子对比热的贡献是导致La_0.7Ca_0.3MnO₃样品比热变化的原因.电脉冲诱导O离子沿一维扩展性缺陷的电化学迁移,导致材料中局部区域的O离子浓度发生变化.O离子浓度的变化导致载流子浓度的变化,同时载流子浓度的变化将使得低温下磁性耦合强度发生变化,从而导致比热发生变化.     

Magnetotransport properties of epitaxial Pr0.5Ca0.5MnO3 films grown by a solution technique

Epitaxial Pr_0.5Ca_0.5MnO₃ films have been synthesized on (0 0 1) SrTiO₃ substrate using a chemical solution deposition technique and two-step post-annealing process. The zero field resistivity of the films shows semiconducting behavior and a characteristic of charge ordering is observed at 230 K. The resistivity of the 10 nm film did not show any effect with the magnetic field. However, melting of charge ordering was observed for the 120 nm film at an applied magnetic field of 4 T. Large decrease in the resistivity of the 120 nm film (<100 K) resulted in magnetoresistance of nearly −100% at 75 K.     

La0.9Sr0.1MnO3薄膜中电流效应研究

用直流磁控溅射法在(100)LaAlO₃衬底上制备了La_0.9Sr_0.1MnO₃薄膜.经退火处理后薄膜的原子力显微镜形貌观测和X射线衍射分析显示具有比较好的质量.电阻率-温度关系表明La_0.9Sr_0.1MnO₃薄膜在281 K处发生金属绝缘体转变.电流在0.01—4 mA范围内，薄膜的峰值电阻率随电流增大而减小，在4 mA下获得了30.5%的峰值电阻率变 关键词： 掺杂锰氧化合物 0.9Sr_0.1MnO₃薄膜')" href="#">La_0.9Sr_0.1MnO₃薄膜 电流诱导效应 相分离理论     

Homogeneous interface-type resistance switching in Au/La0.67Ca0.33MnO3/SrTiO3/F:SnO2 heterojunction memories

La0.67Ca0.33MnO3 thin films are fabricated on fluorine-doped tin oxide conducting glass substrates by a pulsed laser deposition technique with SrTiO3 used as a buffer layer. The current-voltage characteristics of the heterojunetions exhibit an asymmetric and resistance switching behaviour. A homogeneous interface-type conduction mechanism is also reported using impedance spectroscopy. The spatial homogeneity of the charge carrier distribution leads to field- induced potential-barrier change at the Au-La0.67Ca0.33MnO3 interface and a concomitant resistance switching effect. The ratio of the high resistance state to the low resistance state is found to be as high as 1.3 x 10^4% by simulating the AC electric field. This colossal resistance switching effect will greatly improve the signal-to-noise ratio in nonvolatile memory applications.     

Current-induced effect on resistivity and magnetoresistance of La0.67Ba0.33MnO3 manganite

The influence of dc biasing current on temperature dependence of resistivity and low-field magnetoresistance (MR) of La_0.67Ba_0.33MnO₃ bulk sample is reported. A prominent finding is the change in resistivity around the insulator-to-metal transition temperature (T_IM) and the change in MR around the ferromagnetic transition temperature (T_C). The decrease in MR around T_C at higher biasing current indicates a strong interaction between carrier spin and spin of Mn ions resulting in a higher alignment of Mn ion spins. Change in resistivity around T_IM is interpreted in the framework of percolative conduction model based on the mixed phase of itinerant electrons and localized magnetic polarons.     

Influence of epitaxial growth on phase competition in Pr0.5Sr0.5MnO3 films

A series of Pr_0.5Sr_0.5MnO₃ (PSMO) films with various thickness were epitaxially grown on substrates of (0 0 1)-oriented (LaAlO₃)_0.3(SrAl_0.5Ta_0.5O₃)_0.7 (LSAT), LaAlO₃ (LAO) and SrTiO₃ (STO), and (0 1 1)-oriented STO using pulse laser deposition. Influence of epitaxial growth on phase competition was investigated. A ferromagnetic metal to antiferromagnetic insulator (FMM-AFI) transition upon cooling is present in both largely compressed situations deposited on LAO (0 0 1) and tensile cases deposited on STO (0 0 1) but absent in little strained films grown on LSAT (0 0 1), indicating that the antiferromagnetic insulating state is favored by strains. On the other hand, the 400 nm films deposited on (0 1 1)-oriented STO as well as LAO substrates show FMM-AFI transition. These results reveal that both the orientation of epitaxial growth and substrate-induced strain affect the FMM-AFI transition.     

DC current effect on the magnetic phase and transport properties of polycrystalline La0.7Ca0.3MnO3

The influence of DC current on the resistivity and phase transition of polycrystalline La_0.7Ca_0.3MnO₃ has been investigated. The specific heat measurement found that charge carriers and ferromagnetic spin-wave contributions were changed after applied DC current. Applying high electric fields leads to the formation of ferromagnetic regions. The resistivity drops abruptly once the percolating current path is established. As current through the sample disappears, the larger ferromagnetic (FM) clusters, however, remain and are frozen in giving a measurable contribution to the specific heat of the system. The larger clusters should give rise to the value of spin-wave stiffness constant (D), as it is expected to increase the strength of the ferromagnetic coupling. The metallic ferromagnetic regions would make the charge carrier delocalization and attribute to specific heat linear term γ.     

ENHANCEMENT OF FERROMAGNETIC CLUSTER INDUCED BY MAGNETIC FIELD IN THE PHASE-SEPARATED La0.5Ca0.5MnO3

Magnetic and transport properties of La_0.5Ca_0.5MnO₃ have been investigated by measuring the magnetization and resistance in zero-field-cooled (ZFC) and field-cooled (FC) modes. Conspicuously irreversible behaviors of magnetization/resistance in the two different modes were observed below the charge ordering transition temperature (T_CO). The ZFC and FC magnetizations at 5K, as functions of the magnetic field, coincide for μ₀H≤1T. Afterwards, the ZFC magnetization tends to an approximate constant, but the FC one increases linearly with increasing field. There exists an excellent correspondence between magnetization and resistance below T_CO. All the results suggest that the ferromagnetic clusters embed in the charge-ordered matrix. The phenomenon of ferromagnetic clusters growing up easily in the FC procedure has been interpreted according to the model of thermally activated two-level system.