Graphene aerogels (GA), prepared with an organic sol–gel process, possessing a high specific surface area of 793 m2 g?1, a high pore volume of 3 cm3 g?1, and a large average pore size of 17 nm, were applied as a support for manganese oxide for supercapacitor applications. The manganese oxide was electrochemically deposited into the highly porous GA to form MnO2/GA composites. The composites, at a high manganese oxide loading of 61 wt. %, exhibited a high specific capacitance of 410 F g?1 at 2 mV s?1. More importantly, the high rate specific capacitances measured at 1000 mV s?1 for these composites were two‐fold higher than those obtained with samples prepared in the absence of the GA support. The specific capacitance retention ratio, based on the specific capacitance obtained at 25 mV s?1, was maintained high, at 85 %, even at the high scan rate of 1000 mV s?1, in contrast with the significantly lower value of 67 % for the plain manganese oxide sample. For the cycling stability, the specific capacitance of the composite electrode decayed by only 5 % after 50,000 cycles at 1000 mV s?1. The success of this MnO2/GA composite may be attributed to the structural advantages of high specific surface areas, high pore volumes, large pore sizes, and three‐dimensionally well‐connected network of the GA support. These structural advantages made possible the high mass loading of the active material, manganese oxide, large amounts of electroactive surfaces for the superficial redox events, fast mass‐transfer within the porous structure, and well‐connected conductive paths for the involved charge transport. 相似文献
Graphene composites with metal or metal oxide nanoparticles have been extensively investigated owing to their potential applications in the fields of fuel cells, batteries, sensing, solar cells, and catalysis. Among them, much research has focused on supercapacitor applications and have come close to realization. Composites include monometal oxides of cobalt, nickel, manganese, and iron, as well as their binary and ternary oxides. In addition, their morphological control and hybrid systems of carbon nanotubes have also been investigated. This review presents the current trends in research on metal oxide/graphene composites for supercapacitors. Furthermore, methods are suggested to improve the properties of electrochemical capacitor electrodes. 相似文献
Graphene oxide (GO) nanosheets are readily reduced by aniline above room temperature in an aqueous acid medium, with the aniline simultaneously undergoing oxidative polymerization to produce the reduced graphene oxide‐polyaniline nanofiber (RGO‐PANi) composites. The resulting RGO‐PANi composites and RGO (after dissolution of PANi) were characterized by XPS, XRD analysis, TGA, UV–visible absorption spectroscopy, and TEM. It was also found that the RGO‐PANi composites exhibit good specific capacitance during galvanostatic charging–discharging when used as capacitor electrodes.
下载免费PDF全文