戊二醛交联前后明胶微球热转变研究

在空气和氮气气氛中,对未交联的明胶微球(GMs)和戊二醛交联明胶微球(CGMs)进行了受热转变研究,并利用250℃热处理的明胶球制备出具有多孔内核的明胶基结构.经过热重分析(TGA)、差示扫描量热法(DSC)、扫描电子显微镜(SEM)和付里叶变换红外光谱(FTIR)等分析测试表明:戊二醛交联明胶微球300℃后热失重略大于未交联明胶微球,两者的熔化温度Tm都为228℃;在空气中250℃热处理7 h的未交联明胶微球经过稀硫酸处理后可以得到多孔内核结构,多孔内核含碳、氧元素,外壳以碳元素为主;105℃和190℃热处理的明胶球化学成分基本相同,250℃热处理使明胶分子中的酰胺键减少、并发生三级结构的转变.     

磁性SiO2/PSt中空复合微球的细乳液法制备及表征

采用双原位细乳液聚合工艺,将疏水改性的磁性纳米粒子(MNP)加入到细乳液反应体系的油相中,利用增长的聚合物和单体TEOS之间的相分离原理,实现了聚合物的生成和TEOS的水解缩合同步进行,一步获得了磁性SiO2/PSt中空复合微球.通过红外光谱(FTIR)、透射电镜(TEM)、热重差热分析(TGA/DSC)和振动磁强计(VSM)对中空复合微球进行了表征.结果表明,制备的SiO2/PSt中空复合微球的尺寸范围为300～600 nm,当加入磁性纳米粒子后,得到的磁性SiO2/PSt中空微球保持了原来的中空结构,中空复合微球内腔的大小可以通过改变单体TEOS的加入量来控制.SiO2/PSt中空微球对磁性纳米粒子的包封率达到了86%.磁性SiO2/PSt中空复合微球具有超顺磁性,饱和磁强度值为14.7 emu/g.     

中空SiO_2纳米微球的制备与表征

在乙醇/氨水介质中,将SiO2包覆在聚乙烯吡咯烷酮(PVP)功能化的聚苯乙烯(PS)微粒表面,利用一步法得到了中空纳米二氧化硅微球;研究了影响中空纳米二氧化硅微球形成的主要因素,并探讨了中空纳米SiO2微球的可能形成机理.结果表明,在一定的反应时间下,当氨水用量为0.6 mL、温度为70℃时,可以获得空心结构的SiO2纳米微球;通过控制四乙基原硅酸盐(TEOS)的量可以调节微球的包覆层厚度.     

模板法制备大孔硅胶微球及其在高效液相色谱蛋白质分离中的应用

以弱阳离子交换聚合物微球(WCX)为模板、N-三甲氧基硅基丙基-N,N,N-三甲基氯化铵(TMSPTMA)为结构导向剂、四乙氧基硅烷(TEOS)为硅胶前驱体,在三乙醇胺弱碱催化作用下,水解缩合形成有机聚合物与二氧化硅复合微球,将此复合微球煅烧后得到大孔二氧化硅微球。探索了不同反应条件对二氧化硅微球的形貌、表面结构和分散性的影响;当TMSPTMA、TEOS与三乙醇胺的体积比为1∶2∶2时可以得到孔径在50~150 nm之间、粒径在2μm左右的硅胶微球。对所制备的大孔硅胶微球表面进行C18(十八烷基二甲基氯硅烷)键合修饰,然后将键合的填料装填到50 mm×4.6 mm的色谱柱中,考察了其对常见的几种标准蛋白质和市售大豆分离蛋白质的分离效果,结果显示这种填料在高效液相色谱蛋白质分离中具有一定的潜力。     

高压静电法制备多孔磁性壳聚糖微球

以壳聚糖(Chitosan, CS)为基质, 通过共混法引入四氧化三铁磁性颗粒, 以硅胶(Silicagel, S)为致孔剂, 在热的NaOH溶液中溶出硅胶致孔, 采用高压静电法制备磁性壳聚糖微球. 通过SEM观察了微球的结构和形貌, 并对微球结构和形貌的影响因素及其制备工艺进行了系统的研究, 结果表明, 高压静电法制备的磁性硅胶/壳聚糖微球粒径可通过微量进样器的针头大小来控制, 并且粒径分布均匀, 实验重复性及可控性好; 当以质量体积分数为5%的壳聚糖醋酸溶液(体积分数2％, mS∶mCS=4∶1), 用8号针头进样时, 制得直径约为600 μm, 孔洞分布均匀, 孔径约为50 μm的多孔磁性壳聚糖微球. 由于磁性多孔壳聚糖微球中含有大量的活性羟基和氨基, 因此显弱碱性, 对酸性物质和金属离子的吸附作用很好, 且可通过外加磁场进行有效分离. 磁性多孔壳聚糖微球在生物分离及污水中的酸性染料处理方面具有潜在的应用价值.     

内含Fe_3O_4和金纳米粒子的碳化微球的制备及其催化性能

通过蒸馏-沉淀聚合制备了丙烯酸-二乙烯苯共聚物微球,经离子交换吸附Fe2+离子,然后通过空气中加热、氩气气氛中高温碳化得到了含Fe3O4纳米粒子的多孔磁性碳化微球。在水介质中多孔磁性碳化微球吸附氯金酸,然后还原得到内含金纳米粒子的磁性碳化微球。以硼氢化钠还原对硝基苯酚生成对氨基苯酚反应为例,研究了内含金纳米粒子的磁性碳化微球的催化作用。结果表明,内含金纳米粒子的磁性碳化微球对该反应有很好的催化作用。通过外磁场很容易将磁性微球从反应液相中分离出来,微球重复使用10次后其催化活性基本未变。     

香草醛交联壳聚糖载药微球的性能及其成球机理分析

以壳聚糖溶液为水相、液体石蜡为油相形成油包水型乳液, 以香草醛为交联剂, 采用乳化交联法制得壳聚糖微球. 结合IR光谱和XRD测试, 分析了壳聚糖交联固化成球的机理: 壳聚糖和香草醛之间所发生的Schiff碱反应和氢键的形成以及缩醛化反应, 以此为基础共同形成交联结构从而使壳聚糖交联固化成球. 探讨了交联后壳聚糖微球结晶度降低的原因: 壳聚糖固化时分子链未充分进行有序的结晶排列, 交联后的壳聚糖结构较复杂, 从而破坏了原壳聚糖分子的规整性. 选用盐酸小檗碱为模型药物, 制备了香草醛交联的壳聚糖载药微球, SEM结果显示, 载药微球表面致密且球形度好, 微球粒径在5-15 μm之间. 此外, 采用分光光度计对载药微球的载药率、药物包封率和药物体外释放性质进行了测试和分析, 结果表明载药微球缓释效果明显.     

磁性明胶微球的制备及表征

生物高分子磁性微球作为性能优异的功能高分子材料在固定化酶、靶向药物、细胞分离和免疫分析等方面显示出强大的生命力。我们曾用凝胶-微乳液法化学剪裁技术制备了明胶包裹的复合磁性微粒,本文用共沉淀法制备磁性Fe3O4微晶作为磁性内核,明胶为包裹材料,     

侧链偶氮聚电解质在胶体微球表面的静电层层自组装和微胶囊制作

将侧链偶氮聚电解质应用于聚苯乙烯胶体微球表面的静电层层自组装,得到了偶氮聚电解质和聚二烯丙基二甲基氯化铵多层膜覆盖的核壳微球.实验表明,组装后偶氮苯基团发生了一定程度的解聚集,得到的胶体微球可表现出明显的光色效应.研究进一步采用含肉桂酸酯的光敏聚电解质作为交联的保护壳层,并通过光交联反应使表面层发生交联固化反应.将上述具有核壳结构的胶体球溶解去除聚苯乙烯内核后,得到了含光响应聚电解质的空心微胶囊.     

W/O乳化法制备明胶/β-磷酸三钙多孔复合微球及其热学性能

采用乳液、离子缔合法制备得到明胶(Gel)/β-纳米磷酸三钙(β-TCP)复合多孔微球,其尺寸可通过控制反应的搅拌速度进行调节. SEM和光学显微镜观察表明,明胶/β-TCP复合微球尺寸在20～40 μm之间,被包敷的磷酸三钙为200 nm左右,微球内部呈多孔结构. 当m(磷酸三钙)∶m(明胶)＞0.4∶1时,有大量花瓣状晶体附着于复合微球的表面,是磷酸三钙溶解和明胶分子诱导重结晶所致. XRD与IR图谱表明,磷酸三钙纳米粒子与明胶之间存在化学键合,明胶/β-纳米磷酸三钙复合微球的微观结构与自然骨相似. DSC-TGA结果显示,90%的TCP在乳化过程中与明胶复合. 本文所制备的复合微球,为添加各种药物和促骨生长因子并实现缓释提供了优良的载体.     

Synthesis of Fe3O4@poly(methylmethacrylate-co-divinylbenzene) magnetic porous microspheres and their application in the separation of phenol from aqueous solutions

A simple strategy to fabricate magnetic porous microspheres of Fe(3)O(4)@poly(methylmethacrylate-co-divinylbenzene) was demonstrated. The magnetic microspheres, consisting of polymer-coated iron oxide nanoparticles, were synthesized by the modified suspension polymerization of methacrylate and divinylbenzene in the presence of a magnetic fluid. The morphology and the properties of the magnetic porous microspheres were examined by scanning electron microscopy, transmission electron microscopy, superconducting quantum interference device, Fourier transform infrared spectroscopy, thermogravimetry, and X-ray powder diffraction. The pore size distribution and the specific surface area of the microspheres were measured by nitrogen sorption and mercury porosimetry technique. As predicted from the previous knowledge, the magnetic porous microspheres possessed a high specific surface area using n-hexane as a porogen. It was further found that the amounts of divinylbenzene and methacrylate, the ratio of porogens, and the dosage of ferrofluids affect the specific surface area of the microspheres. Furthermore, the microspheres were applied to remove phenol from aqueous solutions. The results showed that the microspheres had a high adsorption capacity for phenol and a high separation efficiency due to their porous structure, polar groups, and superparamagnetic characteristic.     

Preparation of PLGA microspheres with different porous morphologies

Poly(D,L-lactide-co-glycolide)(PLGA) microspheres were prepared by emulsion solvent evaporation method. The influences of inner aqueous phase, organic solvent, PLGA concentration on the morphology of microspheres were studied. The results showed that addition of porogen or surfactants to the inner aqueous phase, types of organic solvents and polymer concentration affected greatly the microsphere morphology. When dichloromethane was adopted as organic solvent, microspheres with porous structure were produced. When ethyl acetate served as organic solvent, two different morphologies were obtained. One was hollow microspheres with thin porous shell under a lower PLGA concentration, another was erythrocyte-like microspheres under a higher PLGA concentration. Three types of microspheres including porous, hollow core with thin porous shell(denoted by hollow in brief) and solid structures were finally selected for in vitro drug release tests. Bovine serum albumin(BSA) was chosen as model drug and encapsulated within the microspheres. The BSA encapsulation efficiency of porous, hollow and solid microspheres was respectively 90.4%, 79.8% and 0. And the ultimate accumulative release was respectively 74.5%, 58.9% and 0. The release rate of porous microspheres was much slower than that of hollow microspheres. The experiment results indicated that microspheres with different porous structures showed great potentials in controlling drug release behavior.     

Preparation,Characterization,and in vitro Release of Biodegradable Erythromycin-gelatin Microspheres

Blank and erythromycin-loaded gelatin microspheres were successfully fabricated via emulsion chemical- crosslinking technique. The surface morphology of the microspheres was characterized by scanning electron microscope（SEM） and optical microscope. The results show that the microspheres were spherical and smooth. The particle average size of erythromycin-loaded microspheres was found to be 20.6 μm, with a high purity of more than 90% and with a good dispersibility. The microspheres could be obtained in a high yield. Erythromycin released from the microspheres was monitored in buffer and artificial body fluid at 37 ℃. Average drug content was 27.2%, and erythromycin-loaded gelatin microspheres showed good release profiles with a nearly constant release during 4-8 h in artificial body fluid in vitro degradation studies. These gelatin microspheres are useful for studying and developing various drug-delivery systems.     

聚己二酸丁二酯纳米纤维构建的微球的制备

建立了采用异相成核和可控水解相结合的方法制备由纳米纤维构建的聚合物微球的新方法.根据多取代卞叉山梨醇(TM6)对聚己二酸丁二酯(PBA)的异相成核作用以及结晶形态的影响,采用两种乳液溶剂挥发法、并在聚合物溶液中加入成核剂TM6制备了PBA微球,研究了成核剂含量对PBA微球在酶促降解之后形态变化的影响.研究结果表明,二次乳液溶剂挥发法可以制备具有多孔结构的PBA微球,这种多孔结构有利于酶溶液进入到微球内部,促进PBA微球的均匀水解,最终获得由PBA纳米纤维构建的微球.当TM6的含量为3 wt%时,采用二次乳液溶剂挥发法制备的PBA微球,经过5 h酶促降解处理,可以得到表面和内部由PBA纳米纤维均匀组成的微球.进一步的细胞实验表明,微球的纳米纤维结构,有利于MG-63细胞在聚合物微球上的黏附、铺展和向内生长.     

不同溶剂制备的聚乳酸多孔微球的形成机理

利用改进的双乳液溶剂挥发法制备了多孔聚乳酸( PLA)微球.通过采用具有不同沸点和水溶性的有机溶剂制备得到不同多孔结构的PLA微球.结果发现以二氯甲烷、氯仿和甲苯为溶剂制备的微球具有相似的均匀多孔结构,而以乙酸乙酯制备的微球却具有中空结构和多孔的壳层.通过进一步的实验研究了溶剂种类对于微球多孔结构的影响.结果表明溶剂的...     

131I标记海藻酸钠包裹明胶微球的制备及性能评价

建立了明胶微球和海藻酸钠(SA)包裹微球的制备方法,并通过实验比较了明胶微球和包裹微球的各种特性,最后用氯胺T法将125I及131I分别标记在微球上.结果表明,包裹微球对碘有更高的负载量和稳定性;在相同条件下,包裹微球的降解时间比明胶微球的降解时间长;将标记后的明胶微球通过直接注射介入到新西兰大白兔的肝脏,采用发射单光...     

具有核壳结构磁性复合微球的制备与表征

采用两步法制备了具有核壳结构的Fe3O4/P(MMA/DVB)(core)-P(St/GMA/DVB)(shell)磁性复合微球.首先,用改进的细乳液聚合制备了Fe3O4/P(MMA/DVB)微球;然后,加入总量不同的苯乙烯(St)、甲基丙烯酸缩水甘油酯(GMA)和二乙烯基苯(DVB),通过种子乳液聚合,制备了不同磁含量的核壳结构的磁性复合微球.分别用X-射线衍射(XRD)、高倍透射电镜(HR-TEM)、热重分析(TGA)、振动样品磁力计(VSM)等手段对磁性微球的性能进行了表征.实验结果表明,Fe3O4/P(MMA/DVB)微球的磁含量为84 wt%;通过改变加入壳层单体的量,核壳复合微球的磁含量可控在20 wt%~76 wt%之间.该微球具有超顺磁性,相应的饱和磁化强度为12~50Am2/kg.     

单分散磁性P(St/BA/MAA)微球的制备

在共沉淀法合成超细磁流体的基础上 ,以苯乙烯 (St)、丙烯酸丁酯 (BA)和甲基丙烯酸 (MAA)为共聚单体 ,在不同的介质体系中采用无皂乳液聚合法制备了单分散 ,粒径范围为 80～ 2 30nm的磁性P(St BA MAA)微球 .详细探讨了介质极性、磁流体中表面活性剂含量对磁性高分子微球粒径和单分散性的影响 .实验结果表明 ,在一定范围内随介质极性降低 ,磁性高分子微球的单分散性提高 ,随表面活性剂用量增加 ,单分散性变差 .总体来看 ,磁性高分子微球的单分散性与其表面静电斥力密切相关 ,过大或过小的静电斥力均会导致磁性高分子微球单分散性的降低 .