Structure distortion, optical and electrical properties of ZnO thin films co-doped with Al and Sb by so--gel spin coating

ZnO thin films co-doped with Al and Sb with different concentrations and a fixed molar ratio of AlCl₃ to SbCl₃ at 1:2, are prepared by a sol--gel spin-coating method on glass annealed at 550 ℃ for 2 h in air. The x-ray diffraction results confirm that the ZnO thin films co-doped with Al and Sb are of wurtzite hexagonal ZnO with a very small distortion, and the biaxial stresses are 1.03×10⁸, 3.26×10⁸, 5.23×10⁸, and 6.97×10⁸ Pa, corresponding to those of the ZnO thin films co-doped with Al and Sb in concentrations of 1.5, 3.0, 4.5, 6.0 at% respectively. The optical properties reveal that the ZnO thin films co-doped with Al and Sb have obviously enhanced transmittance in the visible region. The electrical properties show that ZnO thin film co-doped with Al and Sb in a concentration of 1.5 at% has a lowest resistivity of 2.5Ω·cm.     

p型ZnO薄膜的制备及特性

采用射频磁控溅射在Si片上制备ZnO薄膜，通过离子注入对样品进行N掺杂，在不同温度下进行退火并实现了p型转变.用扫描电子显微镜、X射线衍射和Hall测量对薄膜进行了表征，结果表明薄膜具有良好的表面形貌和高度c轴择优取向，退火后p型ZnO薄膜的最高载流子浓度和最低电阻率分别为1.68×10¹⁶cm^-3和41.5Ω·cm.讨论并分析了退火温度和时间对ZnO薄膜p型转变的影响.     

透光导电ITO膜的制备及其光电特性的研究

采用溶胶-凝胶方法制备ITO膜,并从制备工艺上研究了各种因素对ITO膜光电特性的影响.最后制出的ITO膜厚度约为50nm,在可见光区平均透射比达97%,最高达99.55%,电阻率在2.0Ω·cm左右,最低达到0.31Ω·cm.     

衬底温度对MOCVD法沉积ZnO透明导电薄膜的影响

研究了衬底温度对MOCVD技术制备的ZnO薄膜的微观结构和光电特性影响. XRD和SEM的研究结果表明，衬底温度对ZnO薄膜的微观结构有显著影响，明显的形貌转变温度大约发生在175℃，低于175℃，薄膜呈镜面结构，晶粒为球状，高于177℃的较高温度范围，薄膜从“类金字塔”状的绒面结构演化为“岩石”状显微组织；随着温度增加，薄膜的晶粒尺寸明显增大.绒面结构的未掺杂ZnO薄膜具有17.96 cm²/V·s的高迁移率和3.28×10^-2 Ω·cm的低电阻率，对ZnO薄膜的进一步掺杂和结构优化有望应用于Si薄膜太阳电池的前电极. 关键词： MOCVD ZnO薄膜 透明导电氧化物 太阳电池     

Boron doped ZnO thin films fabricated by RF-magnetron sputtering

By using the radio frequency-magnetron sputtering (RF-MS) method, both pure ZnO and boron doped ZnO (ZnO:B) thin films were deposited on glass substrates at ambient temperature and then annealed at 450 °C for 2 h in air. It is found that both ZnO and ZnO:B thin films have wurtzite structure of ZnO with (0 0 2) preferred orientation and high average optical transmission (≥80%). Compared with the resistivity of 6.3 × 10² Ω cm for ZnO film, both as-deposited and annealed ZnO:B films exhibit much lower resistivity of 9.2 × 10⁻³ Ω cm and 7.5 × 10⁻³ Ω cm, respectively, due to increase in the carrier concentration. Furthermore, the optical band gaps of 3.38 eV and 3.42 eV for as-deposited and annealed ZnO:B films are broader than that of 3.35 eV for ZnO film. The first-principles calculations show that in ZnO:B thin films not only the band gap becomes narrower but also the Fermi level shifts up into the conduction band with respect to the pure ZnO film. These are consistent with their lower resistivities and suggest that in the process of annealing some substituted B in the lattice change into interstitial B because of its smaller ion radius and this transformation widens the optical band gap of ZnO:B thin film.     

Characteristics of ZnO:In thin films prepared by RF magnetron sputtering

In-doped ZnO (ZnO:In) transparent conductive thin films were deposited on glass substrates by RF magnetron sputtering. The effect of substrate temperature on the structural, electrical and optical properties of the ZnO:In thin films was investigated. It was found that higher temperature improves the crystallinity of the films and promotes In substitution easily. ZnO:In thin films with the best crystal quality were fabricated at 300 °C, which exhibit a larger grain size of 29 nm and small tensile strain of 0.9%. The transmittance of all the films was revealed to be over 85% in the visible range independence of the substrate temperatures and the lowest resistivity of ZnO:In thin films is 2.4×10⁻³ Ω cm.     

Investigation of reduced graphene oxide effects on ultra-violet detection of ZnO thin film

The reduced graphene oxide (rGO) incorporated ZnO thin films were fabricated by dip-coating method. The Raman and FT-IR spectra of 0.075 wt% incorporated composite film showed reduction of GO in composite film. The transmittanceProd. Type: FTP spectra have shown that rGO incorporation increase the visible light absorption of ZnO thin film while the calculated band gaps of samples were decreased from 3.28 to 3.25 eV by increasing the rGO content. The linear trend of I–V curve suggests an ohmic contact between ZnO and rGO. Besides, it was found that by increasing the rGO content, the electrical resistivity was decreased from 4.32×10² Ω cm for pure ZnO film to 2.4×10¹ Ω cm for 0.225 wt% rGO incorporated composite film. The composite photodetectors not only possessed a desirable UV photosensitivity, but also the response time of optimum sample containing 0.075 wt% rGO was reduced to about one-half of pure ZnO thin film. Also, the calculated signal to noise (SNR) showed that highly conductive rGO in composite thin films facilitate the carrier transportation by removing the trapping centers. The mechanism of photoresponsivity improvement of composite thin films was proposed by carrier transportation process.     

Highly transparent and conductive indium tin oxide thin films for solar cells grown by reactive thermal evaporation at low temperature

Transparent conductive tin-doped indium oxide (In₂O₃:Sn, ITO) thin films with various Sn-doping concentrations have been prepared using the low cost reactive thermal evaporation (RTE) technique at a low growth temperature of ~160 °C. The structural characteristics, optical and electrical properties of the ITO thin films were investigated. These polycrystalline ITO films exhibited preferential orientation along (222) plane and possessed low resistivities ranging from 3.51 to 5.71 × 10^?4 Ω cm. The decreased mobility was attributed to the scattering by ionized and neutral impurities at high doping concentrations. The optimized ITO thin film deposited with 6.0 wt% Sn-doping concentration exhibited a high average transparency of 87 % in the wavelength range of 380–900 nm and a low resistivity of 3.74 × 10^?4 Ω cm with a high Hall mobility of 47 cm² V^?1s^?1. A hydrogenated amorphous silicon and silicon–germanium (a-Si:H/a-SiGe:H) double-junction solar cell fabricated with the RTE-grown ITO electrodes presented a conversion efficiency of 10.51 %.     

Electrical and optical properties of Ga doped zinc oxide thin films deposited at room temperature by continuous composition spread

Ga doped ZnO (GZO) thin films were deposited on glass substrates at room temperature by continuous composition spread (CCS) method. CCS is thin films growth method of various Ga_xZn_1−xO(GZO) thin film compositions on a substrate, and evaluating critical properties as a function position, which is directly related to material composition. Various compositions of Ga doped ZnO deposited at room temperature were explored to find excellent electrical and optical properties. Optimized GZO thin films with a low resistivity of 1.46 × 10⁻³ Ω cm and an average transmittance above 90% in the 550 nm wavelength region were able to be formed at an Ar pressure of 2.66 Pa and a room temperature. Also, optimized composition of the GZO thin film which had the lowest resistivity and high transmittance was found at 0.8 wt.% Ga₂O₃ doped in ZnO.     

Effects of metal doping on the physical properties of ZnTe thin films

Zinc telluride (ZnTe) thin films were sublimated on a glass substrate using closed space sublimation (CSS) technique. ZnTe thin films of same thickness were tailored with copper (Cu) & silver (Ag) doping, considered for comparative study. X-ray diffraction (XRD) patterns of as-deposited ZnTe thin film and doped ZnTe samples exhibited polycrystalline behavior. The preferred orientation of (111) having cubic phase was observed. XRD patterns indicated that the crystallite size had increased after silver and copper immersion in as-deposited ZnTe thin films. Scanning electron microscopy (SEM) was used to observe the change of as-deposited and doped sample's grains sizes. EDX confirmed the presence of Cu and Ag in the ZnTe thin films after doping respectively. The optical studies showed the decreasing trend in energy band gap after Cu and Ag-doping. Transmission also decreased after doping. Resistivity of as-deposited ZnTe thin film was about 10⁶ Ω cm. The resistivity was reduced to 68.97 Ω cm after Cu immersion, and 10⁴ Ω cm after Ag immersion. Raman spectra were used to check the crystallinity of as-deposited, Cu and Ag-doped ZnTe thin film samples.     

Influence of polarity inversion on the electrical properties of Ga‐doped ZnO thin films

This study investigates how polarity inversion influences the relationship between the electrical properties of heavily Ga‐doped ZnO (GZO) films deposited by RF magnetron sputtering and their thickness. The electrical properties observed in very thin films are correlated with a change of polarity from O‐polar to Zn‐polar face upon increasing the film thickness based on results of valence band spectra measured by X‐ray photoelectron spectroscopy. It is found that the electrical properties of very thin GZO films deposited on Zn‐polar ZnO templates are significantly improved compared to those deposited on O‐polar face. A low resistivity of 2.62 × 10^–4 Ω cm, high Hall mobility of 26.9 cm²/V s, and high carrier concentration of 8.87 × 10²⁰ cm^–3 being achieved with 30 nm‐thick GZO films using Zn‐polar ZnO templates on a glass substrate. In contrast, the resistivity of 30 nm‐thick GZO films on bare glass that shows more likely O‐polar is very poor about 1.44 × 10^–3 Ω cm with mobility and carrier concentration are only 11.9 cm²/V s and 3.64 × 10²⁰ cm^–3, respectively. It is therefore proposed that polarity inversion plays an important role in determining the electrical properties of extremely thin GZO films. (© 2016 WILEY‐VCH Verlag GmbH &Co. KGaA, Weinheim)     

氧氩比对SnO2/Ag/SnO2透明导电膜光电性能的影响

在室温及不同的氧氩比条件下,采用射频磁控溅射Ag层和直流磁控溅射SnO₂层,在载玻片衬底上制备出了SnO₂/Ag/SnO₂多层薄膜.用霍尔效应测试仪、四探针电阻测试仪和紫外-可见-近红外光谱仪等表征了薄膜的电学性质和光学性质.实验结果表明:当氧氩比为1:14时,所制得的薄膜的光电性质优良指数最大,为1.69×10^-2 Ω^-1;此时,薄膜的电阻率为9.8×10^-5 Ω·cm,方电阻为9.68 Ω/sq,在400~800 nm可见光区的平均光学透射率达85%;并且,在氧氩比为1:14时,利用射频磁控溅射Ag层和直流磁控溅射SnO₂层在PET柔性衬底上制备出了光电性质优良的柔性透明导电膜,其在可见光区的平均光学透过率达85%以上,电阻率为1.22×10^-4 Ωcm,方电阻为12.05 Ω/sq.     

带隙可调的Al，Mg掺杂ZnO薄膜的制备

利用射频磁控溅射（RF-MS）方法,固定Al₂O₃掺杂量2 wt%,Mg掺杂量分别为1 wt%,3 wt%和5 wt%,在玻璃基底上制备了Al掺杂和Al,Mg共掺杂的ZnO薄膜,在500 ℃空气中退火2 h后,测量并比较了它们的光学和电学性质．结果表明,Al,Mg共掺杂的ZnO薄膜结晶质量良好,具有ZnO纤锌矿结构,具有较强的（002）面衍射峰,表明薄膜晶体沿c轴优先生长;与Al掺杂ZnO薄膜相比蓝端光透射率增加,1 wt%和3 wt% Mg掺杂薄 关键词： 射频磁控溅射 ZnO薄膜 Al Mg共掺杂     

Fine luminescent patterning on ZnO nanowires and films using focused electron-beam irradiation

ZnO thin films and nanowires (NWs) were precisely treated by focused electron-beam (E-beam) irradiation with a line width between 200 nm and 3 μm. For both ZnO films and NWs, an increased green emission was clearly observed for the E-beam-treated parts. Using a high-resolution laser confocal microscope, the photoluminescence intensities for E-beam-treated ZnO structures increased with increasing dose 1.0 × 10¹⁷–1.0 × 10¹⁸ electrons/cm². The resistivity of a single ZnO NW increased from 56 to 1800 Ω cm after the E-beam treatment. From the results for the annealed ZnO thin films, we analyzed that the variations in PL and resistivity were due to the formation of vacancies upon focused E-beam irradiation.     

Properties of ITO–AZO bilayer thin films prepared by magnetron sputtering for applications in thin-film silicon solar cells

In this paper we study the electro-optical behavior and the application of indium–tin oxide (ITO) and aluminum-doped zinc oxide (AZO) bilayer thin films for silicon solar cells. ITO–AZO bilayer thin films were deposited on glass substrates using radio-frequency magnetron sputtering. The experimental results show that a decrease in the electrical resistivity of the ITO–AZO bilayer thin films has been achieved without significant degradation of optical properties. In the best case the resistivity of the bilayer films reached a minimum of 5.075×10^?4 Ω?cm when the thickness of the AZO buffer layer was 12 nm. The ITO–AZO bilayer films were applied as the front electrodes of amorphous silicon solar cells and the short-circuit current density of the solar cells was considerably increased.     

The influence of different doping elements on microstructure, piezoelectric coefficient and resistivity of sputtered ZnO film

ZnO film is attractive for high frequency surface acoustic wave device application when it is coupled with diamond. In order to get good performance and reduce insertion loss of the device, it demands the ZnO film possessing high electrical resistivity and piezoelectric coefficient d₃₃. Doping ZnO film with some elements may be a desirable method. In this paper, the ZnO films undoped and doped with Cu, Ni, Co and Fe, respectively (doping concentration is 2.0 at.%) are prepared by magnetron sputtering. The effect of different dopants on the microstructure, piezoelectric coefficient d₃₃, and electrical resistivity of the film are investigated. The results indicate that Cu dopant can enhance the c-axis orientation and piezoelectric coefficient d₃₃, the Cu and Ni dopant can increase electrical resistivity of the ZnO film up to 10⁹ Ω cm. It is promising to fabricate the ZnO films doped with Cu for SAW device applications.     

Flexible thermoelectric module based on zinc oxide thin film grown via SILAR

In this work, we used the low temperature solution growth Successive Ionic Layer Adsorption and Reaction (SILAR) for a deposition of the nanostructured undoped and indium doped (ZnO and ZnO:In) thin films on flexible polyimide (PI) substrates for their use as cheap non-toxic thermoelectric materials in the flexible thermoelectric modules of planar type to power up portable and wearable electronics and miniature devices. The use of a zincate solution in the SILAR method allows to obtain ZnO:In film, which after post-growth annealing at 300 °C has low resistivity ρ ≈ 0.02 Ω m, and high Seebeck coefficient −147 μV/K and thermoelectric power factor ~1 μW K⁻² m⁻¹ at near-room temperatures. As evidence of the operability of the manufactured films as the basis of the TE device, we have designed and tested experimental lightweight thin-film thermoelectric module. This TE module is able to produce specific output power 0.8 μW/m² at ΔT = 50 K.     

Investigation on the effect of Zr doping in ZnO thin films by spray pyrolysis

Zirconium doped zinc oxide thin films with enhanced optical transparency were prepared on Corning 1737 glass substrates at the substrate temperature of 400 °C by spray pyrolysis method for various doping concentrations of zirconium (IV) chloride in the spray solution. The X-ray diffraction studies reveal that the films exhibit hexagonal crystal structure with polycrystalline grains oriented along (0 0 2) direction. The crystalline quality of the films is found to be deteriorating with the increase of doping concentration and acquires amorphous state for higher concentration of 8 at.% in precursor solution. The average transmittance for 5 at.% (solution) zirconium doped ZnO film is significantly increased to ∼92% in the visible region of 500-800 nm. The room temperature photoluminescence (PL) spectra of films show a band edge between 3.41 and 3.2 eV and strong blue emission at 2.8 eV irrespective of doping concentration and however intensity increases consistently with doping levels. The vacuum annealing at 400 °C reduced the resistivity of the films significantly due to the coalescence of grains and the lowest resistivity of 2 × 10⁻³ Ω cm is observed for 3 at.% (solution) Zr doped ZnO films which envisages that it is a good candidate for stable TCO material.     

High quality nitrogen-doped zinc oxide thin films grown on ITO by sol–gel method

Highly transparent N-doped ZnO thin films were deposited on ITO coated corning glass substrate by sol–gel method. Ammonium nitrate was used as a dopant source of N with varying the doping concentration 0, 0.5, 1.0, 2.0 and 3.0 at%. The DSC analysis of prepared NZO sols is observed a phase transition at 150 °C. X-ray diffraction pattern showed the preferred (002) peak of ZnO, which was deteriorated with increased N concentrations. The transmittance of NZO thin films was observed to be ~88%. The bandgap of NZO thin films increased from 3.28 to 3.70 eV with increased N concentration from 0 to 3 at%. The maximum carrier concentration 8.36×10¹⁷ cm⁻³ and minimum resistivity 1.64 Ω cm was observed for 3 at% N doped ZnO thin films deposited on glass substrate. These highly transparent ZnO thin films can be used as a window layer in solar cells and optoelectronic devices.     

Plasma-based sputtering of indium tin oxide for the application of photovoltaic cells

Transparent and conducting indium tin oxide (ITO) thin films were deposited on soda lime glass substrates by RF plasma magnetron sputtering at room temperature. The effect of thickness (100, 200 and 300?nm) on the physical (structural, optical, electrical) properties of ITO thin films was investigated systematically. It is observed that with an increase in thickness, the X-ray diffraction data indicate polycrystalline films with grain orientations predominantly along (222) and (400) directions; the average grain size increases from 10 to 30?nm; the optical band gap increases from 3.68 to 3.73?eV and the transmission decrease from 80% to 70% . Four-point probes show a low resistivity (2.4×10^?5?Ω?cm) values for film with a thickness 300?nm. Present work shows that the ITO is a promising transparent conductive oxide material for the solar cell application.