The double melting behavior of a liquid crystalline polyimide derived from PMDA and 1,3‐bis[4‐(4′‐aminophenoxyl) cumyl] benzene

The double melting behavior of a thermotropic liquid crystalline polyimide was studied by means of differential scanning calorimetry (DSC), polarized light microscopy (PLM), transmission electron microscopy (TEM), wide‐angle X‐ray diffraction (WAXD), and small‐angle X‐ray scattering (SAXS). This liquid crystalline polyimide exhibited a normal melting peak around 278 °C and transformed into a smectic A phase. The smectic A phase changed to nematic phase upon heating to 298 °C, then became isotropic melt around 345 °C. The samples annealed or isothermally crystallized at lower temperature showed double melting endotherms during heating scan. The annealing‐induced melting endotherm was highly dependent on annealing conditions, whereas the normal melting endotherm was almost not influenced by annealing when the annealing temperature was low. Various possibilities for the lower melting endotherm are discussed. The equilibrium melting points of both melting peaks were extrapolated to be 283.2 °C. Combined analytical results showed that the double melting peaks were from the melting of the two types of crystallites generated from two crystallization processes: a slow and a fast one. Fast crystallization may start from the well‐aligned liquid crystal domains, whereas the slow one may be from the fringed or amorphous regions. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 3018–3031, 2000     

X‐ray studies on the double melting behavior of poly(butylene terephthalate)

The double melting behavior of poly(butylene terephthalate) (PBT) was studied with differential scanning calorimetry (DSC) and wide‐angle X‐ray analysis. DSC melting curves of melt‐crystallized PBT samples, which we prepared by cooling from the melt (250 °C) at various cooling rates, showed two endothermic peaks and an exothermic peak located between these melting peaks. The cooling rate effect on these peaks was investigated. The melt‐crystallized PBT sample cooled at 24 K min^?1 was heated at a rate of 1 K min^?1, and its diffraction patterns were obtained successively at a rate of one pattern per minute with an X‐ray measurement system equipped with a position‐sensitive proportional counter. The diffraction pattern did not change in the melting process, except for the change in its peak height. This suggests that the double melting behavior does not originate from a change in the crystal structure. The temperature dependence of the diffraction intensity was obtained from the diffraction patterns. With increasing temperature, the intensity decreased gradually in the low‐temperature region and then increased distinctly before a steep decrease due to the final melting. In other words, the temperature‐dependence curve of the diffraction intensity showed a peak that is interpreted as proof of the recrystallization in the melting process. The peak temperature was 216 °C. The temperature‐dependence curve of the enthalpy change obtained by the integration of the DSC curve almost coincided with that of the diffraction intensity. The double melting behavior in the heating process of PBT is concluded to originate from the increase of crystallinity, that is, recrystallization. © 2001 John Wiley & Sons, Inc. J Polym Sci Part B: Polym Phys 39: 2005–2015, 2001     

Structure development in multistage stretching of PTFE films

The structure of expanded poly(tetrafluoroethylene) (ePTFE) films that were produced by uniaxial or biaxial stretching of a calendared sheet were studied by wide angle X‐ray diffraction (WAXD), small angle X‐ray scattering, differential scanning calorimetry (DSC), and scanning electron microscopy. The molecular orientation of the stretched films was analyzed by WAXD flat films and pole figures. Biaxial orientation factors were computed to interpret the level of orientation quantitatively. DSC scans showed that oriented samples exhibited two melting peaks, one at the commonly observed temperature in the range 340–345 °C and one around 380 °C. The possible causes of this high‐temperature melting peak and its relation to previously described processes is discussed. The microporous nature of the ePTFE films is also briefly discussed. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Morphological changes during heating in poly(L‐lactic acid)/poly(butylene succinate) blend systems as studied by synchrotron X‐ray scattering

Blends of poly(L ‐lactic acid) (PLA) and poly(butylene succinate) (PBS) were prepared in various compositions via melt mixing, and the morphological changes were investigated with differential scanning calorimetry and synchrotron wide‐angle and small‐angle X‐ray scattering techniques at a heating rate of 10 °C/min. Differential scanning calorimetry thermograms of PLA/PBS blends showed two distinct melting peaks over the entire composition range. The exothermal peak for PLA shifted significantly to a lower temperature and overlapped with that of PBS around 100 °C. A depression of the melting point of the PLA component via blending was observed. The synchrotron wide‐angle X‐ray scattering during heating revealed that there was no cocrystallization or crystal modification via blending. The synchrotron small‐angle X‐ray scattering data showed that well‐defined double‐scattering peaks (or peaks with a clear scattering shoulder) appeared during crystallization, indicating that this system possessed dual lamellar stacks. These peaks were deconvoluted into two components with a peak separation computer program, and then the morphological parameters of each component were obtained by means of the correlation function. The long period and average lamellar thickness of the two components before melting decreased with an increasing content of the other polymer component. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1931–1939, 2002     

Analysis of the complex thermal behavior of poly(L‐lactic acid) film. I. Samples crystallized from the glassy state

The melting behavior of poly(L ‐lactic acid) film crystallized from the glassy state, either isothermally or nonisothermally, was studied by wide angle X‐ray diffraction (WAXD), small angle X‐ray scattering (SAXS), differential scanning calorimetry (DSC), and temperature‐modulated differential scanning calorimetry (TMDSC). Up to three crystallization and two melting peaks were observed. It was concluded that these effects could largely be accounted for on the basis of a “melt‐recrystallization” mechanism. When molecular weight is low, two melting endotherms are readily observed. But, without TMDSC, the double melting phenomena of high molecular weight PLLA is often masked by an exotherm just prior to the final melting, as metastable crystals undergo melt‐recrystallization during heating in the DSC. The appearance of a double cold‐crystallization peak during the DSC heating scan of amorphous PLLA film is the net effect of cold crystallization and melt‐recrystallization of metastable crystals formed during the initial cold crystallization. Samples cold‐crystallized at 80 and 90 °C did not exhibit a long period, although substantial crystallinity developed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3200–3214, 2006     

Large melting point depression of 2–3‐nm length‐scale nanocrystals formed by the self‐assembly of an associative polymer: Telechelic,pyrene‐labeled poly(dimethylsiloxane)

Large melting point depressions for organic nanocrystals, in comparison with those of the bulk, were observed in an associative polymer: telechelic, pyrene‐labeled poly(dimethylsiloxane) (Py‐PDMS‐Py). Nanocrystals formed within nanoaggregates of pyrenyl units that were immiscible in poly(dimethylsiloxane). For 5 and 7 kg/mol Py‐PDMS‐Py, physical gels resulted, with melting points exceeding 40 °C and with small‐angle X‐ray scattering peaks indicating that the crystals were nanoconfined, were 2–3 nm long, and contained roughly 18–30 pyrenyl dye end units. In contrast, 30 kg/mol Py‐PDMS‐PY was not a gel and exhibited no scattering peak at room temperature; however, after 12 h of annealing at ?5 °C, multiple melting peaks were present at 5–30 °C. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 3470–3475, 2004     

Control of thermal cross‐linking reactions and the degree of crystallinity of syndiotactic 1,2‐polybutadiene

Thermal stability, crystallization, morphological development, subsequently melting, and crystallinity control of a syndiotactic 1,2‐polybutadiene sample were carefully carried out by thermogravimetry (TGA), polarized optical microscopy (POM), differential scanning calorimetry (DSC), temperature‐modulated differential scanning calorimetry (TMDSC), and wide‐angle X‐ray diffraction (WAXD), respectively. The experiments indicate that thermal cross‐linking reaction rates under nitrogen protection and in air are different for this polymer at temperature above 155 °C. Under nitrogen protection, the thermal cross‐linking reaction rate is delayed and the mechanism of melt crystallization obtained from the DSC results is in good accordance with that from POM observation. TMDSC results indicate that melting–recrystallization–melting model is more proper to explain the double melting events of this sample. At the same time, the evolution of the degree of crystallinity as the function of the time was investigated by WAXD profiles for the samples firstly crystallized at 145 °C for 1 h and then kept at 163 °C mediated between the temperatures of the double peaks. It shows that as prolonging the annealing time at 163 °C thermal cross‐linking reactions possibly occur, leading to gradual reduction of the apparent crystallite sizes, evaluated by Scherrer equation and the degree of crystallinity. The changing sequence of the relative intensity of the stronger four diffraction peaks with time due to thermal cross‐linking reactions is (111)/(201) > (210) > (010) > (200)/(110). © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2885–2897, 2005     

Multiple melting behavior of poly(lactic acid) filled with modified carbon black

Two melting peaks are generally observed in a heating scan for isothermally crystallized poly(lactic acid) (PLA)/carbon black (CB) and PLA/modified carbon black (MCB) composites. To investigate the origin of the above double melting behavior, the melting behavior after isothermal crystallization was analyzed with differential scanning calorimetry, wide‐angle X‐ray diffraction, and small angel X‐ray scattering techniques. The double melting of the crystallized samples can be explained by the model of two populations of lamellae, the double peaks of low and high temperatures are contributed to the melting of the small lamellae produced by secondary crystallization and that of the major crystals formed in the primary crystallization process, respectively. Spherulitic growth rates of the neat PLA and PLA/MCB composite were analyzed and the occurrence of a regime transition was demonstrated. For the PLA, a clear regime transition was observed at around 125 °C. For the PLA/MCB, it occurred at 130 °C. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1971–1980, 2009     

High‐performance poly(ethylene‐2,6‐naphthalate) fiber prepared by high‐tension annealing

A high‐tension annealing (HTA) method has been applied to zone‐annealed poly(ethylene‐2,6‐naphthalate) (PEN) fibers in order to further improve their mechanical properties. The HTA treatment was carried out under an applied tension of 428 MPa at a treating temperature of 175 °C. The applied tension was close to the tensile strength at 175 °C. The resulting HTA fiber had a birefringence of 0.492 and degree of crystallinity of 57%. Wide‐angle X‐ray diffraction (WAXD) photographs of the HTA fibers showed three reflections (010, 100, and 1 10) attributed to an α form crystal, but no (020) reflection attributed to a β form was observed in the equator. The tensile modulus and tensile strength increased with processing, and the HTA fiber had a maximum modulus of 33 GPa, a tensile strength of 1.1 GPa, and a storage modulus of 33 GPa at 25 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 61–67, 2000     

Analysis of Polymorphism and Dual Crystalline Morphologies in Poly(hexamethylene terephthalate)

Summary: The polymorphisms in poly(hexamethylene terephthalate) (PHT), along with their associated melting and spherulite morphologies, were examined by differential scanning calorimetry (DSC), wide‐angle X‐ray diffraction (WAXD), and polarized‐light microscopy (PLM). The morphology and crystal cells were dependent on the temperature of crystallization. When melt‐crystallized at low temperatures (90–135 °C), PHT showed at least five melting peaks and two re‐crystallization peaks upon DSC scanning, and the samples displayed various fractions of both α and β crystals. However, only a single melting peak was obtained in PHT melt‐crystallized at 140 °C or above, which displayed a single type of β crystal. In addition, two different forms of spherulites were identified in melt‐crystallized PHT, with one being a typical Maltese‐cross spherulite containing the α crystal, and the other being a dendrite‐type packed mainly with the β crystal. This study provides timely evidence for a critical interpretation of the relationship between multiple melting and polymorphisms (unit cells and spherulites) in polymers, including semi‐crystalline polyesters.

WAXD diffractograms for PHT melt‐crystallized at 140 °C, revealing a single type of β‐crystal cell.     

Thermal and X‐ray analysis of polymorphic crystals,melting, and crystalline transformation in poly(butylene adipate)

Polymorphic crystals and complex multiple melting behavior in an aliphatic biodegradable polyester, poly(butylene adipate) (PBA), were thoroughly examined by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). Further clarification on mechanisms of multiple melting peaks related to polymorphic crystal forms in PBA was attempted. More stable α‐form crystal is normally favored for crystallization from melt at higher temperatures (31–35 °C), or upon slow cooling from the melt; while the β‐form is the favored species for crystallization at low temperatures (25–28 °C). We further proved that PBA crystallization could also result in all α‐form even at low temperatures (25–28 °C) if it crystallized with the presence of prior α‐form nuclei. PBA packed with both crystal forms could display as many as four melting peaks (P1 ? P4, in ascending temperature order). However, PBA initially containing only the α‐crystal exhibited dual melting peaks of P1 and P3, which are attributed to dual lamellar distributions of the α‐crystal. By contrast, PBA initially containing only the β‐crystal could also exhibit dual melting peaks (P2 and P4) upon scanning. While P2 is clearly associated with melting of the initial β‐crystal, the fourth melting peak (P4), appearing rather broad, was determined to be associated with superimposed thermal events of crystal transformation from β‐ to α‐crystal and final re‐melting of the new re‐organized α‐crystal. Crystal transformation from one to the other or vice versa, lamellae thickening, annealing at molten state, and influence on crystal polymorphism in PBA were analyzed. Relationships and mechanisms of dual peaks for isolate α‐ or β‐crystals in PBA are discussed. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 1662–1672, 2005     

Analysis of crystallization behavior and crystal modifications of poly(butylene‐2,6‐naphthalene dicarboxylate)

Information on the crystalline structure and the properties of poly(butylene‐2,6‐naphthalene dicarboxylate) (PBN) has not been well reported until now, but it is known that there are two different crystal modifications in PBN, as follows: one is formed in isotropic samples by annealing (α form); another appears by annealing with tension (β form). The relation between the crystal modifications and the kinetics of isothermal crystallization for PBN was investigated using in‐situ Fourier transform infrared spectroscopy (FTIR) and wide‐angle X‐ray diffraction (WAXD). The melting behavior of each crystalline form was also studied by means of FTIR and differential scanning calorimetry (DSC) measurements. From the analysis of the melt‐crystallized PBN specimens, the two crystalline forms coexisted in the isotropic samples melt‐crystallized at 230°C, but only the α crystal modification was observed in the films annealed at lower temperatures. In addition, it was revealed that, at 230°C, the β modification was formed only in the primary crystallization process. © 1999 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 37: 561–574, 1999     

Poly(vinylidene fluoride)/clay nanocomposites prepared by melt intercalation: Crystallization and dynamic mechanical behavior studies

The preparation and properties of poly(vinylidene fluoride) (PVDF)/clay nanocomposites are reported for the first time. PVDF/clay nanocomposites were prepared by melt intercalation with organophilic clay. The composites were characterized with X‐ray diffraction, differential scanning calorimetry, and dynamic mechanical analysis. X‐ray diffraction results indicated intercalation of the polymer into the interlayer spacing. PVDF in the nanocomposites crystallized in the β form. Differential scanning calorimetry nonisothermal curves showed an increase in the melting and crystallization temperatures along with a decrease in crystallinity, as evidenced by the melting and crystallization peaks. Isothermal crystallization studies showed an enhanced rate of crystallization with the addition of clay, as evidenced by a reduction in the crystallization time. Dynamic mechanical analysis indicated significant improvements in the storage modulus over a temperature range of ?100 to 150 °C. The tan δ peak signifying the glass‐transition temperature of PVDF shifted to higher temperatures. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1682–1689, 2002     

Analysis of the complex thermal behavior of poly(L‐lactic acid) film. II. Samples crystallized from the melt

The complex thermal behavior of poly(l ‐lactic acid) films crystallized from the melt, either isothermally or nonisothermally, was studied by differential scanning calorimetry (DSC), wide angle X‐ray diffraction, and small angle X‐ray scattering. The variation of the thermal behavior with crystallization temperature, time, and cooling rate was documented and analyzed. After nonisothermal crystallization at low cooling rates that develop high crystallinity, an obvious double melting peak appears at modest heating rates (e.g., 10 °C/min). At higher heating rates, these samples exhibit only single melting. However, an unusual form of double melting occurs under the majority of the conditions studied under either isothermal or nonisothermal conditions. In this case, double melting is marked by the appearance of a recrystallization exotherm just prior to the final melting that obscures the observation of the melting of the crystals formed during the initial crystallization process. The occurrence of double melting in melt‐crystallized samples was concluded to be the result of a melt‐recrystallization process occurring during the subsequent DSC heating scan; it is a function of crystalline perfection, not the initial crystallinity, nor whether or not the crystallization reached completion at the crystallization temperature. Many other very interesting observations are also discussed. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3378–3391, 2006     

Structure characterization of copolymers of ethylene and 1‐octadecene

Four ethylene‐1‐octadecene copolymers and the corresponding polyethylene homopolymer, synthesized with a metallocene catalyst, have been analyzed by using three characterization techniques in the solid state: differential scanning calorimetry, wide‐angle X‐ray diffraction, and Raman spectroscopy. Very important annealing effects are observed in the copolymers with higher comonomer content while standing at room temperature, in such a way that the enthalpies of melting derived from the first and second melting are different. The X‐ray diffractograms have been analyzed in terms of amorphous and crystalline components, determining both the crystallinity and the position of the different reflections. The variation of the unit cell parameters has been calculated from those reflections. No indication of a possible participation of the relatively long 1‐octadecene branches in the crystallization can be deduced from the X‐ray data. The degree of crystallinity has also been determined from the Raman spectra, following two procedures. The results indicate that the crystallinities deduced from the band at 1416 cm⁻¹ are much lower than those derived from the other two characterization techniques. On the contrary, the data from the 1060 cm⁻¹ band are practically coincident with the X‐ray determinations. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1440–1448, 2000     

Thermally stimulated depolarization currents of crosslinked polyethylene relaxations in the fusion range of temperatures

With thermally stimulated depolarization currents, we researched the relaxations of crosslinked polyethylene as it is used in medium‐voltage cable insulation. Through conventional polarization two heteropolar peaks stand up in the spectra, at 80 and 105 °C. As the sample is annealed, a homopolar peak is developed at about 99 °C. With window polarization, our results indicated that the 80 °C peak is a structured peak related to polar crosslinking subproducts and impurities. The 105 and 99 °C peaks are fitted to the general kinetic‐order model because the 105 °C peak is related to free‐charge detrapping at the crystalline phase, in the bulk and maybe at the amorphous‐crystal interphases, and the peak that is observed at 99 °C is due to injected charge. Annealing at high temperatures promotes the creation of traps in the material. Charge trapping at T < 70 °C seems to be related to the increased insulator resistivity with annealing time. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1412–1421, 2003     

Effect of postcasting heat‐treatment on the structure and properties of semicrystalline phase‐inversion poly(vinylidene fluoride) membranes

Microporous PVDF membranes were prepared by immersion‐precipitation in 1‐octanol of casting dopes dissolved at different temperatures, with dissolution temperature affecting strongly the membrane microstructure. The effect of postcoagulation thermal annealing, which is an additional thermal parameter, on membrane microstructure and properties is probed herein. Membranes obtained were annealed at temperatures up to 160 °C, which is close to the melting point of PVDF polymer. Annealing leads to a substantial modification of the nano‐scale fine structure of the membranes, while the overall‐microporous structure is preserved. At elevated annealing temperatures, nano‐grains, fibrils, and stick‐like crystalline entities gradually eclipse, while globules develop more robust connections based on wide bands of crystal elements. Probing by X‐ray diffraction and dynamic scanning calorimetry shows that crystallinity increases when annealing temperature and time are increased. As regards mechanical properties, the tensile strength of the membranes can be enhanced substantially, up to about 10 times, upon appropriate high temperature prolonged annealing. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1880–1893, 2009     

Crystallization and thermal properties of PLLA comb polymer

Poly(L ‐lactide) (PLLA) on poly(2‐hydroxyethyl methacrylate) (PHEMA) backbone was prepared by a combination of atom transfer radical polymerization (ATRP) and ring‐opening polymerization (ROP). The structure of the comb polymer was analyzed by wide angle X‐ray diffraction (WAXD), small angle X‐ray scattering (SAXS), and differential scanning calorimetry (DSC). WAXD result indicates that the comb polymer has α crystalline modification with a 10₃ helical conformation. Lamellar parameters of the crystalline structure were obtained by one‐dimension correlation function (1DCF) calculated from SAXS results. The calculations show that the thickness of crystalline layer is controlled by annealing temperature and comb structure. DSC was applied to study kinetics of the crystallization and melting behavior. Two melting peaks on melting curves of the comb polymer at different crystallization temperature were detected, and the peak at higher temperature is attributed to the melt‐recrystallization. The equilibrium melting temperature is found to be influenced by the comb structure. In this article the effects of the comb structure on Avrami exponent, equilibrium melting point and melting peak of the comb polymer were discussed. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 589–598, 2008     

Thermal and X‐ray powder diffraction studies of aliphatic polyester dendrimers

The syntheses and thermal and X‐ray powder diffraction analyses of three sets of aliphatic polyester dendrimers based on 2,2‐bis(hydroxymethyl)propionic acid as a repeating unit and 2,2‐dimethyl‐1,3‐propanediol, 1,5‐pentanediol, and 1,1,1‐tris(hydroxymethyl)ethane as core molecules are reported. These dendritic polyesters were prepared in high yields with the divergent method. The thermal properties of these biodendrimers were evaluated with thermogravimetric analysis and differential scanning calorimetry. The thermal decomposition of the compounds occurred around 250 °C for the hydroxyl‐ended dendrimers and around 150 °C for the acetonide‐protected dendrimers. In addition, the crystallinity of the lower generation dendrimers was evaluated with X‐ray powder diffraction. The highest crystallinity and the highest melting points were observed for the first‐generation dendritic compounds. The higher generation dendrimers showed weaker melting transitions during the first heating scan. Only the glass‐transition temperatures were observed in subsequent heating scans. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5574–5586, 2004     

Temperature‐modulated differential scanning calorimetry studies on the origin of double melting peaks in isothermally melt‐crystallized poly(L‐lactic acid)

In this work, the melting behaviors of nonisothermally and isothermally melt‐crystallized poly(L ‐lactic acid) (PLLA) from the melt were investigated with differential scanning calorimetry (DSC) and temperature‐modulated differential scanning calorimetry (TMDSC). The isothermal melt crystallizations of PLLA at a temperature in the range of 100–110 °C for 120 min or at 110 °C for a time in the range of 10–180 min appeared to exhibit double melting peaks in the DSC heating curves of 10 °C/min. TMDSC analysis revealed that the melting–recrystallization mechanism dominated the formation of the double melting peaks in PLLA samples following melt crystallizations at 110 °C for a shorter time (≤30 min) or at a lower temperature (100, 103, or 105 °C) for 120 min, whereas the double lamellar thickness model dominated the formation of the double melting peaks in those PLLA samples crystallized at a higher temperature (108 or 110 °C) for 120 min or at 110 °C for a longer time (≥45 min). © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 466–474, 2007