Real‐time SAXS and WAXS study of the multiple melting behavior of poly(ε‐caprolactone)

The multiple melting behavior of poly(ε‐caprolactone) (PCL) was investigated by real‐time small angle X‐ray scattering (SAXS) and wide angle X‐ray scattering (WAXS) measurements coupling with differential scanning calorimetry (DSC). Semicrystalline specimens prepared by a continuous cooling process showed lengthening of the Bragg period during the progress of double melting. A model of variable thickness of lamella was proposed to fit to the SAXS patterns and revealed that both the crystalline lamella and the amorphous layer contributed to the increase in Bragg period while the later dominated the contribution. The model of variable thickness although satisfied the SAXS data was unable to compromise the data from other probing tools. A modification of the model proposed that each lamella piling up to construct the stacks in the crystallites was itself nonuniform in thickness. The modification with the parallel occurrence of the mechanism of surface melting and crystallization successfully compromised the observations from SAXS, DSC, and optical microscopy and provided a new perspective for the explanation to lengthening of the Bragg period related to multiple melting behavior. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1777–1785, 2010     

Nonisothermal crystallization behavior of syndiotactic polystyrene/montmorillonite nanocomposites

X‐ray diffraction methods and differential scanning calorimetry were used to investigate the crystalline structure and crystallization kinetics of syndiotactic polystyrene (sPS)/clay nanocomposites. X‐ray diffraction data showed the presence of polymorphism in sPS/montmorillonite (MMT) nanocomposites, which was strongly dependent on the processing conditions (premelting temperature and cooling rate) of the sPS/MMT nanocomposites and on the content of MMT in the sPS/MMT nanocomposites. The α‐crystalline form could be transformed into β‐crystalline forms at higher premelting temperatures. The nonisothermal melt‐crystallization kinetics and melting behavior of the sPS/MMT nanocomposites were also studied at various cooling rates. The correlation of the crystallization kinetics, melting behavior, and crystalline structure of the sPS/MMT nanocomposites was examined. The results indicated that the addition of a small amount of MMT to sPS caused a change in the mechanism of nucleation and the crystal growth of the sPS crystallite. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 560–570, 2003     

Origin of double melting behavior of poly(p‐phenylene succinate)

The origin of double melting behavior of poly(p‐phenylene succinate) (PPSc) was investigated by differential scanning calorimetry (DSC) and wide‐angle X‐ray diffraction. As‐polymerized PPSc showed two melting peaks: the low melting (LM) and high melting (HM) peaks at 286 and 311 °C, respectively. When PPSc was annealed at 270 °C, the LM peak constantly shifted toward higher temperatures and grew in its area with annealing time, and eventually merged into the HM peak located at 308 °C. X‐ray diffractograms of PPSc annealed at 270 °C became sharper with increasing the annealing time while the peak positions did not change. The X‐ray diffractograms obtained from the LM and the HM peak exhibited the same diffraction peaks. It was concluded from these results that the double melting behavior of PPSc is due to the distribution of crystals having the same crystal form but differing in size and perfection. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1868–1871, 2000     

Crystal modifications and multiple melting behavior of poly(L‐lactic acid‐co‐D‐lactic acid)

The crystal modifications and multiple melting behavior of poly(L ‐lactic acid‐co‐D ‐lactic acid) (98/2) as a function of crystallization temperature were studied by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). It was found that the disorder (α′) and order (α) phases of poly(L ‐lactic acid) (PLLA) were formed in cold‐crystallized poly(L ‐lactic acid‐co‐D ‐lactic acid) samples at low (<110 °C) and high (≥110 °C) temperatures, respectively. A disorder‐to‐order (α′‐to‐α) phase transition occurred during the annealing process of the α′‐crystal at elevated temperatures, which proceeded quite slowly even at the peak temperature of the exotherm P_exo but much more rapidly at higher temperature close to the melting region. The presence or absence of an additional endothermic peak before the exotherm in the DSC thermograph of the α′‐crystal was strongly dependent on the heating rate, indicating that a melting process involved during the α′‐to‐α phase transition. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2011     

The double melting behavior of a liquid crystalline polyimide derived from PMDA and 1,3‐bis[4‐(4′‐aminophenoxyl) cumyl] benzene

The double melting behavior of a thermotropic liquid crystalline polyimide was studied by means of differential scanning calorimetry (DSC), polarized light microscopy (PLM), transmission electron microscopy (TEM), wide‐angle X‐ray diffraction (WAXD), and small‐angle X‐ray scattering (SAXS). This liquid crystalline polyimide exhibited a normal melting peak around 278 °C and transformed into a smectic A phase. The smectic A phase changed to nematic phase upon heating to 298 °C, then became isotropic melt around 345 °C. The samples annealed or isothermally crystallized at lower temperature showed double melting endotherms during heating scan. The annealing‐induced melting endotherm was highly dependent on annealing conditions, whereas the normal melting endotherm was almost not influenced by annealing when the annealing temperature was low. Various possibilities for the lower melting endotherm are discussed. The equilibrium melting points of both melting peaks were extrapolated to be 283.2 °C. Combined analytical results showed that the double melting peaks were from the melting of the two types of crystallites generated from two crystallization processes: a slow and a fast one. Fast crystallization may start from the well‐aligned liquid crystal domains, whereas the slow one may be from the fringed or amorphous regions. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 3018–3031, 2000     

Influence of additives on the crystal structure and melting behavior of poly(ethylene‐2,6‐naphthalene dicarboxylate)

The influence of additives on the crystal modification and melting behavior of poly(ethylene‐2,6‐naphthalene dicarboxylate) (PEN) was investigated with wide‐angle X‐ray diffraction and differential scanning calorimetry (DSC). The addition of a nucleating promoter, Ceraflour 993, had no effect on the crystal modification and melting behavior of PEN crystallized under all chosen experimental conditions. However, the addition of a nucleating agent, sodium benzoate (SB), did affect the crystal modification and melting behavior of PEN when PEN/SB was crystallized at a higher temperature, but not at a lower temperature. A mixture of α and β modifications of PEN was obtained, and an overlapped dual melting peak was observed in DSC curves when PEN was crystallized at a higher temperature in the presence of SB, instead of a single crystal form and a single melting peak for the crystallization of pure PEN. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 296–301, 2004     

Morphology of homogeneous copolymers of ethylene and 1‐octene. III. Structural changes during heating as revealed by time‐resolved SAXS and WAXD

The structural changes of two linear polyethylenes, LPEs, with different molar mass and of two homogeneous copolymers of ethylene and 1‐octene with comparable comonomer content but different molar mass were monitored during heating at 10 °C per minute using synchrotron radiation SAXS. Two sets of samples, cooled at 0.1 °C per minute and quenched in liquid nitrogen, respectively, were studied. All LPEs display surface melting between room temperature and the end melting temperature, whereas complete melting, according to lamellar thickness, only occurs at the highest temperatures where DSC displays a pronounced melting peak. There is recrystallization followed by isothermal lamellar thickening if annealing steps are inserted. The lamellar crystals of slowly cooled homogeneous copolymers melt in the reverse order of their formation, that is, crystals melt according to their thickness. Quenching creates unstable crystals through the cocrystallization of ethylene sequences with different length. These crystals repeatedly melt and co‐recrystallize during heating. The exothermic heat due to recrystallization partially compensates the endothermic heat due to melting resulting in a narrow overall DSC melting peak with its maximum at a higher temperature than the melting peak of slowly cooled copolymers. With increasing temperature, the crystallinity of quenched copolymers overtakes the one of slowly cooled samples due to co‐recrystallization by which an overcrowding of leaving chains at the crystal surfaces is avoided. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1975–1991, 2000     

不同初始结构间规聚丙烯纤维熔融过程中的结晶转变行为

通过熔融纺丝及随后的热处理制备了具有不同初始结构的间规聚丙烯纤维(sPP).采用差示扫描量热仪(DSC)和变温广角X-射线衍射仪详细研究了sPP纤维在升温过程中的结构转变和熔融行为.结果表明,不同初始结构sPP纤维的晶型不同,卷绕纤维和退火处理纤维以Ⅰ型和Ⅱ型晶型为主,牵伸纤维介晶相占优;升高温度导致Ⅰ型和Ⅱ型两种晶型直接熔融,没有出现Ⅱ型向Ⅰ型的晶型转变;初始结构为介晶相的纤维在升温过程中部分介晶相直接转变为Ⅱ型晶型,还有一部分介晶相直接熔融,并在随后的升温过程中,形成Ⅰ型晶型.sPP纤维的多重熔融行为与其初始结构和纤维制备条件密切相关.     

Crystallization of poly(ethylene terephthalate–co–isophthalate)

Melt crystallization behaviors of poly(ethylene terephthalate) (PET) and poly(ethylene terephthalate‐co‐isophthalate) (PETI) containing 2 and 12 mol % of noncrystallizable isophthalate components were investigated. Differential scanning calorimetry (DSC) isothermal results revealed that the introduction of 2 mol % isophthalate into PET caused a change of the crystal growth process from a two‐dimensional to a three‐dimensional spherulitic growth. The addition of more isophthalate up to 12 mol % into the PET structure induced a change in the crystal growth from a three‐dimensional to a two‐dimensional crystal growth. DSC heating scans after completion of isothermal crystallization at various T_c's showed three melting endotherms for PET and four melting endotherms for PETI‐2 and PETI‐12. The presence of an additional melting endotherm is attributed to the melting of copolyester crystallite composed of ethylene glycol, tere‐phthalate, and isophthalate (IPA) or the melting of molecular chains near IPA formed by melting the secondary crystallite T_m (I) and then recrystallizing during heating. Analyses of both Avrami and Lauritzen‐Hoffman equations revealed that PETI containing 2 mol % of isophthalate had the highest Avrami exponent n, growth rate constant G_o, and product of lateral and end surface free energies σσ_e. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2515–2524, 2000     

New insight into melting and crystallization behavior in semicrystalline poly(ethylene terephthalate)

After isothermal crystallization, poly(ethylene terephthalate) (PET) showed double endothermic behavior in the differential scanning calorimetry (DSC) heating scan. During the heating scans of semicrystalline PET, a metastable melt which comes from melting thinner lamellar crystal populations formed between the low and the upper endothermic temperatures. The metastable melt can recrystallize immediately just above the low melting temperature and form thicker lamellae than the original ones. The thickness and perfection depends on the crystallization time and crystallization temperature. The crystallization kinetics of this metastable melt can be determined by means of DSC. The kinetics analysis showed that the isothermal crystallization of the metastable PET melt proceeds with an Avrami exponent of n = 1.0 ∼ 1.2, probably reflecting one‐dimensional or irregular line growth of the crystal occurring between the existing main lamellae with heterogeneous nucleation. This is in agreement with the hypothesis that the melting peaks are associated with two distinct crystal populations with different thicknesses. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 53–60, 2000     

Analysis of dual melting behavior in cold-crystallized poly(ether diphenyl ether metaketone)

By focusing on cold-crystallized poly(ether diphenyl ether metaketone) (PEKm), a more in-depth understanding of the nature of the crystalline morphology has been gained, which may lead to thorough mechanisms for interpreting the observed thermal behavior in PEKm. Apparently, cold-crystallized PEKm containing initially only a single P1 crystal can exhibit dual melting peaks (300 and 320 °C), with the second high-melting peak corresponding to the P2 crystal that was subsequently formed via P1 melting/repacking during the scan. However, dual morphism (preexisting P1 and P2 crystals) could be intentionally introduced into PEKm if it was cold-crystallized at temperature schemes of decreasing order. The P1 and P2 crystals possess the same unit cells (orthorhombic) and thus they differ only in the lamellae populations. The dual lamellar morphism in this PEKm sample also exhibited similar dual melting peaks during scanning, which correspond to melting of the individual P1 and P2 in a sequential order. This study has thus provided important clues in and shed new light on the interpretation of multiple melting with respect to polymorphism in polymers. Relationships between the low-melting and high-melting lamellae in cold-crystallized polyketone polymer have been thoroughly explored. Received: 9 January 2001/Accepted: 3 February 2001     

Thermal and X‐ray analysis of polymorphic crystals,melting, and crystalline transformation in poly(butylene adipate)

Polymorphic crystals and complex multiple melting behavior in an aliphatic biodegradable polyester, poly(butylene adipate) (PBA), were thoroughly examined by wide‐angle X‐ray diffraction (WAXD) and differential scanning calorimetry (DSC). Further clarification on mechanisms of multiple melting peaks related to polymorphic crystal forms in PBA was attempted. More stable α‐form crystal is normally favored for crystallization from melt at higher temperatures (31–35 °C), or upon slow cooling from the melt; while the β‐form is the favored species for crystallization at low temperatures (25–28 °C). We further proved that PBA crystallization could also result in all α‐form even at low temperatures (25–28 °C) if it crystallized with the presence of prior α‐form nuclei. PBA packed with both crystal forms could display as many as four melting peaks (P1 ? P4, in ascending temperature order). However, PBA initially containing only the α‐crystal exhibited dual melting peaks of P1 and P3, which are attributed to dual lamellar distributions of the α‐crystal. By contrast, PBA initially containing only the β‐crystal could also exhibit dual melting peaks (P2 and P4) upon scanning. While P2 is clearly associated with melting of the initial β‐crystal, the fourth melting peak (P4), appearing rather broad, was determined to be associated with superimposed thermal events of crystal transformation from β‐ to α‐crystal and final re‐melting of the new re‐organized α‐crystal. Crystal transformation from one to the other or vice versa, lamellae thickening, annealing at molten state, and influence on crystal polymorphism in PBA were analyzed. Relationships and mechanisms of dual peaks for isolate α‐ or β‐crystals in PBA are discussed. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 1662–1672, 2005     

Multiple melting endotherms in isothermally melt-crystallized poly(butylene terephthalate)

The melting behavior of poly(butylene terephthalate) crystallized isothermally for various times was examined using differential scanning calorimetry. After short crystallization times, the DSC analysis gave two melting peaks, but after longer times, the analysis gave three peaks. The latter triplet of DSC peaks can be denoted as low, middle, and high, starting with the lowest temperature endotherm. The DSC peaks were simulated using a measured recrystallization rate and behavior for PBT and an assumed initial melting point distribution. The low and middle peaks represent the original melting peaks arising from isothermal crystallization. The high melting peak arises from recrystallization during the DSC heating scan. © 1998 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 36: 1757–1767, 1998     

Effect of the premelting temperature and sample thickness on the polymorphic behavior of syndiotactic polystyrene/clay nanocomposites

X‐ray diffraction methods and differential scanning calorimetry thermal analysis have been used to investigate the structural changes of syndiotactic polystyrene (sPS)/clay nanocomposites. sPS/clay nanocomposites have been prepared by the mixing of sPS polymer solutions with organically modified montmorillonite. X‐ray diffraction data and differential scanning calorimetry results indicate that the dominating crystal forms and their relative fractions in sPS and sPS/clay nanocomposites are different for various premelting temperatures (T_max's). Higher T_max's favor the formation of the thermodynamically more stable β‐crystalline form, and its relative fraction has been obtained from the X‐ray diffraction data in the range of 11.5–13°. The intensity of the X‐ray diffraction data in the range of 11.5–13° decreases as the thickness of sPS/clay nanocomposites decreases from 150 to 20 μm. At the same time, the intensity of the X‐ray data in the range of 6–7° becomes sharper as the thickness of sPS/clay nanocomposites decreases. The calculation ratio based on the peak intensities at 6.2 and 6.8° for sPS/clay nanocomposites of equal thickness and crystallinity in the pure β and α forms has also been determined in this study. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1730–1738, 2003     

Thermal Behavior of Syndiotactic Polystyrene/1,2‐Dichloroethane Gels and Stoichiometry of Polymer‐Solvent Compounds

Abstract

The phase behavior of syndiotactic polystyrene (sPS)/1,2‐dichloroethane (DCE) gels has been investigated by differential scanning calorimetry (DSC) and wide angle x‐ray diffraction (WAXD) for different gel formation conditions. DSC data show that the gel melting temperatures are independent of the cooling conditions leading to gel formation, whereas the melting enthalpies of the gels depend on the cooling history. WAXD measurements show that for low concentration gels the sPS/DCE clathrate structure is obtained, whereas for high concentration gels both the clathrate structure and the solvent‐free β phase can be obtained. Furthermore, the onset of formation of the β phase is dependent on the cooling rate. In light of combined DSC and WAXD data, the reliability of the DSC in evaluating the absolute stoichiometry of polymer‐solvent compounds formed in sPS/DCE gels is discussed.     

Crystallization and melting of a branched polyethylene with precisely controlled chemical structure

The heat capacity of a linear polyethylene with dimethyl branches, at every 21st backbone atom was analyzed by differential scanning calorimetry (DSC) and quasi-isothermal temperature-modulated DSC. This novel copolyethylene (PE2M) is relatively difficult to crystallize from the melt. On subsequent heating, a first, sharp melting peak is followed by a sharp cold-crystallization and crystal perfection and a smaller endotherm, before reaching the main melting at 315–320 K, close to the melting temperatures of eicosane and tetracontane. The low-temperature melting is sensitive to the cooling rate and disappears below 1.0 K min⁻¹. The cold crystallization can be avoided by heating with rates faster than 80 K min⁻¹. The PE2M exhibits some reversing and reversible melting, which is typical for chain-folded polymers. The glass transition of semicrystalline PE2M is broadened and reaches its upper limit at about 260 K (midpoint at about 0.355 K). Above this temperature, the crystals seem to have a heat capacity similar to that of the liquid. A hypothesis is that the melting transition can be explained by changes in crystal perfection without major alteration of the crystal structure and the lamellar morphology. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3461–3474, 2006     

Step-scan TMDSC and high rate DSC study of the multiple melting behavior of poly(1,3-propylene terephthalate)

The multiple melting behavior of poly(1,3-propylene terephthalate) (PPT) samples after isothermal crystallization from the melt was studied. The step-scan temperature-modulated differential scanning calorimetry (TMDSC) and high rate DSC were used to investigate this behavior in conjunction with standard DSC, wide-angle X-ray diffraction (WAXD) and polarizing light microscopy (PLM). The effect of PPT average molecular weight on the melting was also examined. In general multiple endotherms after isothermal crystallization of PPT were attributed to a continuous crystal perfection process during the subsequent heating scan via melting-recrystallization-remelting. Multiple melting behavior was more pronounced for the low molecular weight PPT. Step-scan TMDSC showed that extensive recrystallization occurs in PPT samples, especially after rapid isothermal crystallization. In fact two recrystallization exothermic peaks were observed. High rate DSC revealed the initial morphology generated during the isothermal step and showed that the low and middle peaks are associated with melting of primary crystals while the high temperature peak should be attributed to melting of recrystallized material.     

The multiple melting endotherms from poly(butylene terephthalate)

The melting behavior of poly(butylene terephthalate) (PBT) has been investigated, and a simulation has been performed to determine whether the multiple melting endotherms observed during the thermal analysis of PBT can be explained by the simultaneous melting and recrystallization of an initial distribution of crystal melting temperatures that contains only one maximum and two inflection points. Specimens that were cooled at constant rates from the melt showed between one and three melting endotherms upon heating in a differential scanning calorimeter (DSC). The position and breadth of the crystallization exotherms upon cooling from the melt and small-angle x-ray scattering showed that as the cooling rate is increased, the distribution of melting temperatures broadens and shifts to lower temperatures. By combining temperature-dependent recrystallization with an initial distribution of melting temperatures, simulated DSC curves were produced that agreed well with experimental DSC curves. In instances of triple peaked curves, the high temperature peak was due to crystals formed during the scanning process, and the middle and low temperature peaks were due to crystals originally present in the material. Satisfactory agreement between the experimental and simulated curves was found without considering additional crystallization from the amorphous regions during the scanning process.     

Polydispersity of ethylene sequence length in metallocene ethylene/α‐olefin copolymers. II. Influence on crystallization and melting behavior

In this work, crystallization and melting behavior of metallocene ethylene/α‐olefin copolymers were investigated by differential scanning calorimetry (DSC) and atomic force microscopy (AFM). The results indicated that the crystallization and melting temperatures for all the samples were directly related to the long ethylene sequences instead of the average sequence length (ASL), whereas the crystallization enthalpy and crystallinity were directly related to ASL, that is, both parameters decreased with a decreasing ASL. Multiple melting peaks were analyzed by thermal analysis. Three phenomena contributed to the multiple melting behaviors after isothermal crystallization, that is, the melting of crystals formed during quenching, the melting‐recrystallization process, and the coexistence of different crystal morphologies. Two types of crystal morphologies could coexist in samples having a high comonomer content after isothermal crystallization. They were the chain‐folded lamellae formed by long ethylene sequences and the bundlelike crystals formed by short ethylene sequences. The coexistence phenomenon was further proved by the AFM morphological observation. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 822–830, 2002     

New insights into the multiple melting behaviors of the semicrystalline ethylene‐hexene copolymer: Origins of quintuple melting peaks

A semicrystalline ethylene‐hexene copolymer (PEH) was subjected to a simple thermal treatment procedure as follows: the sample was isothermally crystallized at a certain isothermal crystallization temperature from melt, and then was quenched in liquid nitrogen. Quintuple melting peaks could be observed in heating scan of the sample by using differential scanning calorimeter (DSC). Particularly, an intriguing endothermic peak (termed as Peak 0) was found to locate at about 45 °C. The multiple melting behaviors for this semicrystalline ethylene‐hexene copolymer were investigated in details by using DSC. Wide‐angle X‐ray diffraction (WAXD) technique was applied to examine the crystal forms to provide complementary information for interpreting the multiple melting behaviors. Convincing results indicated that Peak 0 was due to the melting of crystals formed at room temperature from the much highly branched ethylene sequences. Direct heating scans from isothermal crystallization temperature (T_c, 104–118 °C) were examined for comparison, which indicated that the multiple melting behaviors depended on isothermal crystallization temperature and time. A triple melting behavior could be observed after a relatively short isothermal crystallization time at a low T_c (104–112 °C), which could be attributed to a combination of melting of two coexistent lamellar stack populations with different lamellar thicknesses and the melting‐recrystallization‐remelting (mrr) event. A dual melting behavior could be observed for isothermal crystallization with both a long enough time at a low T_c and a short or long time at an intermediate T_c (114 °C), which was ascribed to two different crystal populations. At a high T_c (116–118 °C), crystallizable ethylene sequences were so few that only one single broad melting peak could be observed. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 2100–2115, 2008