La2−xCexCu1−yZnyO4 perovskites for high temperature water-gas shift reaction

The performance of La_2−xCe_xCu_1−yZn_yO₄ perovskites as catalysts for the high temperature water-gas shift reaction (HT-WGSR) was investigated. The catalysts were characterized by EDS, XRD, BET surface area, TPR, and XANES. The results showed that all the perovskites exhibited the La₂CuO₄ orthorhombic structure, so the Pechini method is suitable for the preparation of pure perovskite. However, the La_1.90Ce_0.10CuO₄ perovskite alone, when calcined at 350/700 °C, also showed a (La_0.935Ce_0.065)₂CuO₄ perovskite with tetragonal structure, which produced a surface area higher than the other perovskites. The perovskites that exhibited the best catalytic performance were those calcined at 350/700 °C and, among these, La_1.90Ce_0.10CuO₄ was outstanding, probably because of the high surface area associated with the presence of the (La_0.935Ce_0.065)₂CuO₄ perovskite with tetragonal structure and orthorhombic La₂CuO₄ phase.     

CuO/Ce0.5Ti0.5O2的制备与表征及其对NO+CO反应的催化活性

以Ce0.5Ti0.5O2为载体, 采用浸渍法制备了不同负载量的CuO/Ce0.5Ti0.5O2催化剂, 通过TPR、XRD和激光Raman光谱等技术对其进行了表征, 并在色谱-微反装置上考察了催化剂对NO+CO反应催化性能. 结果表明, CuO/Ce0.5Ti0.5O2催化剂对NO+CO反应的活性与CuO负载量有关; 500 ℃焙烧的催化剂, 当CuO的负载量(w)为22%时, 催化剂的活性最好; 14%CuO/Ce0.5Ti0.5O2在700 ℃焙烧具有最佳催化活性, 这可能与复合载体形成了CeTi2O6的结构有关. TPR结果表明, CuO在Ce0.5Ti0.5O2上出现了四种还原能力不同的物种, α和β峰是载体表面高度分散的CuO物种, γ峰是与Ce0.5Ti0.5O2相互作用较强的孤立CuO晶簇的还原峰, δ峰是载体表面晶相CuO的还原峰; XRD结果表明700 ℃焙烧的样品中已出现了新复合氧化物CeTi2O6的晶相峰, 随焙烧温度的升高, 此晶相峰也变得更加明显, 这说明高温焙烧有利于Ce与Ti发生固相反应而形成CeTi2O6结构; Raman结果表明, 焙烧后的Ce0.5Ti0.5O2并不是简单的TiO2和CeO2的复合, 而是形成了新的晶相结构, 这也进一步验证了CeTi2O6结构的生成.     

Cu掺杂对LaMnO3催化剂的结构和催化氧化性能的影响

采用非晶态多核配合的方法合成了La1-xCuxMnO3(x=0、0.05、0.1、0.2、0.3、0.4、0.5)系列催化剂, 并用X射线衍射(XRD)、透射电镜(TEM)、比表面测定仪(BET)等手段对催化剂的微观结构进行了表征. 研究了Cu掺杂对钙钛矿结构及其对CO催化氧化发光性能及催化氧化CO、CH4性能的影响规律. 结果表明, 当x≤0.1 时, Cu掺杂仍可形成单相的钙钛矿结构; 当x>0.1时, 过量掺杂的Cu以CuO杂相存在. Cu掺杂可改善La1-xCuxMnO3催化剂对CO和CH4的催化氧化活性. 经700 ℃焙烧3 h制备的La0.9Cu0.1MnO3催化剂具有最高CO催化氧化活性(T100%=170 ℃), 该结果与CO催化氧化发光结果一致.而La0.95Cu0.05MnO3催化剂对CH4的催化氧化活性最高(T95%=705 ℃).     

Ce0.35Zr0.55La0.10O1.95对低贵金属Pt-Rh型三效催化剂性能的影响

采用共沉淀技术制备了Ce0.35Zr0.55La0.10O1.95固溶体, 其织构和结构性能以及氧化还原性能分别采用BET、XRD和程序升温(TP)技术进行了表征. 制备了低贵金属Pt-Rh型三效催化剂, 考察了Ce0.35Zr0.55La0.10O1.95对催化剂性能的影响. XRD和BET的结果表明, 经600 ℃焙烧5 h后, Ce0.35Zr0.55La0.10O1.95具有与Ce0.50Zr0.50O2相似的立方结构和高的比表面积；经1000 ℃焙烧5 h后, 仍能保持稳定的立方结构和47.25 m2•g−1的比表面积, 表现出优越的织构性能和高的热稳定性. H2-TPR和O2-TPO的结果表明, Ce0.35Zr0.55La0.10O1.95具有比Ce0.50Zr0.50O2更好的氧化还原性能. 和含Ce0.50Zr0.50O2的催化剂相比, 含Ce0.35Zr0.55La0.10O1.95的催化剂具有较宽的工作窗口, 优越的低温起燃性能, 较强的水气变换能力；催化剂经1000 ℃高温水热老化5 h后, 仍具有良好的催化活性, 表现出了优异的抗老化性能.     

Effects of the partial replacement of La by M (M=Ce, Ca and Sr) in La2-xMxCuO4 perovskites on catalysis of the water-gas shift reaction

The performance of La2-xMxCuO4 perovskites (where M = Ce, Ca or Sr) as catalysts for the water-gas shift reaction was investigated at 290 ℃ and 360 ℃. The catalysts were characterized by EDS, XRD, N2 adsorption-desorption, XPS and XANES. The XRD results showed that all the perovskites exhibited a single phase (the presence of perovskite structure), suggesting the incorporation of metals in the perovskite structure. The XPS and XANES results showed the presence of Cu²⁺ on the surface. The perovskites that exhibited the best catalytic performance were La2-xCexCuO4 perovskites, with CO conversions of 85%-90%. Moreover, these perovskites have higher surface areas and larger amounts of Cu on the surface. And Ce has a higher filled energy level than the other metals, increasing the energy of the valence band of Ce and providing more electrons for the reaction. Besides, the La1.80Ca0.20CuO4 perovskite showed a good catalytic performance.     

CO催化氧化中氧化铜对CeO2的调变作用

采用柠檬酸络合法制备并应用XRD、ICP和微反活性等方法研究了Cu－Ce－O催化剂体系,当体系中铜含量较少,焙烧温度较低时,以萤石矿型结构存在,CuO掺杂进入CeO2的晶格中;当铜含量较多,焙烧温度较高时,除了以萤石矿型结构存在外,还伴随有单斜晶系CuO的生成,焙烧温度高达1000℃时,体系无其它结构型式的晶相形成,研究发现少量的CuO使体系催化氧化CO的活性大大提高;只有极少量的CuO进入CeO2的晶格内部,该催化剂最佳配方是Cu／（Cu＋Ce）原子百分比为15％,700℃焙烧4h,其中起高催化氧化作用的是由CuO掺杂调变而成的萤石矿型复合氧化物,其组成为Cu0.06Ce0.94O1.94。     

焙烧温度对酯加氢制醇Cu-Al-Ba催化剂性能的影响(英文)

通过共沉淀法在不同焙烧温度下制备了新型无铬Cu-Al-Ba催化剂.测试了其在高压釜中将棕榈油甲酯加氢制备高碳醇的反应性能.结果表明催化剂的焙烧温度对催化性能有较大影响.在从150℃升至750℃的过程中,高碳醇的收率显示了三个阶段的变化,相应地,催化剂前驱体的热重(TG-DTG)曲线也显示了三个阶段的失重.X射线衍射(XRD)、X射线荧光(XRF),透射电镜-能谱分析-选区电子衍射(TEM-EDS-SAED)、N2物理吸附和程序升温还原(TPR)表征表明,催化剂是由一种孔雀石-勃石-碳酸钡前驱体制得的.在300或550℃焙烧后,催化剂组成为晶态的CuO、BaCO3和非晶态的Al2O3.其中,非晶态的Al2O3为CuO的高分散提供了大的比表面,杆状的BaCO3组分有利于提供微孔结构.在更高的焙烧温度750℃,新物相BaAl2O4的形成破坏了催化剂中的非晶态结构,导致其比表面积和孔容的急剧下降,并引起CuO物种的聚结.550℃焙烧的催化剂显示了最高的高碳醇收率,达到92.3%,这归因于其大的比表面积、大孔容和较高的CuO分散性.     

不同组成和结构LaMnO_3钙钛矿负载Au催化剂的CO氧化活性

采用乙二醇溶胶-凝胶法制备了计量比LaMnO_3和非计量比LaMn_(1.2)O_3钙钛矿,并利用稀硝酸处理LaMnO_3制备得到LaMnO_3-AE,然后采用沉积沉淀法制备钙钛矿负载Au催化剂,以考察载体的结构和性质对Au的热稳定性以及催化剂活性的影响。通过X射线衍射(XRD)、透射电镜(TEM)、X射线光电子能谱(XPS)和H_2程序升温还原(H_2-TPR)等表征,发现LaMnO_3和LaMn_(1.2)O_3钙钛矿载体虽然有利于Au的分散,但是Au的热稳定性相对较差。相反,经稀硝酸刻蚀的LaMnO_3钙钛矿(LaMnO_3-AE)不利于Au的分散,但是有利于提高Au的热稳定性。在CO氧化反应中,当催化剂在低于500°C焙烧时,LaMn_(1.2)O_3钙钛矿负载Au催化剂的活性要显著高于LaMnO_3和LaMnO_3-AE负载Au催化剂的活性,而当催化剂焙烧温度升高至700°C以上时,LaMnO_3-AE负载Au催化剂却要显著优于LaMnO_3和LaMn_(1.2)O_3钙钛矿负载Au催化剂的活性。     

固体超强酸SO2-4/ZrO2的制备及其催化性能研究

以氧氯化锆为锆原,氨水为沉淀剂,硫酸溶液为浸渍液,通过沉淀-浸渍法制备SO2-4/ZrO2(SZ)酯化催化剂,其结构经BET、X-射线衍射(XRD)、傅立叶变换红外光谱(FT-IR)及扫描电子显微镜(SEM)表征.结果表明:随着焙烧温度升高,催化剂的比表面积依次降低,孔径增大,氧化锆的晶态由无定形态转化为四方晶态再转化为单斜晶态;于600℃焙烧时,催化剂形成的S=O键红外吸收峰最强;于700℃焙烧时,催化剂结构被破坏.在丙烯酸与十八醇的酯化反应中对催化剂进行活性测试.结果表明:600℃焙烧的催化剂产率最高(96.4%).     

焙烧温度对TiO2-ZrO2复合氧化物性质及其对十八醇脱水制十八烯反应性能的影响

通过在ZrO_2中掺杂TiO_2,并在350-500℃下焙烧,制备了系列TiO_2-ZrO_2复合氧化物催化剂,将其应用于十八醇脱水制十八烯反应。随焙烧温度的升高,催化剂表面的Lewis酸性位量逐渐增加,450℃焙烧的催化剂Lewis酸性位量最多,焙烧温度继续升高则Lewis酸性位量降低;催化剂中未发现Br?nsted酸性位。焙烧温度≤400℃的TiO_2-ZrO_2复合氧化物形成Ti-O-Zr键,呈无定形态;焙烧温度400℃的TiO_2-ZrO_2复合氧化物呈单斜相和四方相ZrO_2晶型。晶相结构和酸性位量综合影响催化剂的十八醇脱水性能,具有单斜相和四方相ZrO_2晶型的催化剂上酸性位活性很低,具有无定形相的催化剂上酸性位活性显著增加,400℃焙烧的催化剂1-十八烯收率最高。     

不同碱土金属掺杂对 Rh/Ce0.35Zr0.55M0.10O1.90+Pt/La-Al2O3 三效催化剂性能的影响

 采用共沉淀法制备了不同碱土金属掺杂的 Ce0.35Zr0.55M0.10O1.90 (CZM; M = Mg, Ca, Sr 或 Ba) 固溶体, 并采用 N2 吸附-脱附、储氧量测定、程序升温还原和 X 射线衍射对其进行了表征. 以 CZM 和 La-Al2O3 为载体, 制备了负载型低贵金属 Pt-Rh 三效催化剂, 并考察了其催化活性. 结果表明, 经 600 oC 焙烧 5 h 后, CZCa 样品的比表面积为 109 m2/g, 经 1 000 oC 老化 5 h 后仍有 47 m2/g. 所有新鲜样品均具有较低的还原温度和良好的还原性能. 老化后的 CZCa 仍具有较好的还原性能和较高的储氧量. 在 600 oC 下焙烧的样品均为立方晶相; 经 1 000 oC 老化 5 h 后, 只有 CZMg 发生相分离, 其余样品仍为稳定的立方晶相. 活性测试结果表明, 所有新鲜催化剂均具有良好的低温起燃性能; 经 1 000 oC 水热老化 5 h 后, 含有 CZCa 的催化剂仍具有较低的起燃温度, 表现出优异的抗老化性能.     

草酸盐热分解法制备CeO_2负载CuO催化剂用于CO优先氧化反应

采用草酸盐热分解-浸渍法制备了一系列不同CuO负载量的CuO/CeO_2催化剂,并将其用于CO优先氧化(PROX)研究.当CuO负载量为10%时催化剂活性最高,具有温区最宽且温度最低的CO完全转化窗口(96~160℃),并且当反应温度低于131℃时,产物中CO2选择性始终保持100%.研究结果表明,当负载少量CuO时,Cu~(2+)离子会进入CeO_2晶格形成固溶体;进一步提高CuO负载量会导致CuO在CeO_2表面聚集.对于CuO/CeO_2催化剂,形成Cu-Ce固溶体会在催化剂表面生成大量的表面氧空位和Ce3+;Ce3+则与Cu~(2+)作用产生更多的表面Cu~+,而Cu~+是CO PROX的活性中心,因此表面Ce3+含量的提高和Cu-Ce之间相互作用的增强是活性提高的主要原因.与普通沉淀-浸渍法制备的CuO/CeO_2催化剂相比,草酸盐热分解-浸渍法制备的催化剂更有利于Cu-Ce固溶体的形成,从而具有更多的表面Ce3+和更强的表面Cu-Ce相互作用,因此具有更高的CO优先氧化活性.     

CuO/Al2O3催化剂高温固相反应的原位XRD和Raman研究

采用原位XRD和激光Raman光谱等技术对CuO/Al2O3系列催化剂高温下的表面组成和体相结构的变化进行研究.结果表明,随着焙烧温度升高,CuO首先与载体Al2O3发生固相反应生成CuAl2O4.CuAl2O4层能阻止外层CuO进一步向载体Al2O3扩散,从而使部分CuO稳定在CuO/Al2O3催化剂的表层.     

稀土改性对SO42-/ZrO2固体酸催化剂结构与催化性能的影响

采用共沉淀法和浸渍法在不同条件下制备了稀土-SO₄^2-/ZrO₂系列固体酸催化剂。使用废油脂与甲醇的酯交换反应评价了催化剂活性,并通过X射线衍射、红外光谱、比表面积测定表征方法考察了催化剂结构和性能的关系。结果表明,La摩尔掺杂量4%、焙烧温度600℃时制得的SO₄^2-/ZrO₂-La₂O₃催化剂活性最高,此时脂肪酸甲酯的产率为64.68%,且具有较好的重复使用性。稀土的引入使活性四方相ZrO₂更加稳定,600℃焙烧使催化剂既具有较多活性四方相ZrO₂,又具有较大比表面积,从而提高了催化剂活性。催化剂中形成了固体超强酸结构,且改性后酸强度增大,催化剂活性中心数目增加。     

纳米晶La_(1-x)Eu_xFeO_3的合成、表征及催化甲苯燃烧反应活性(英文)

Nanostructured LaFeO3 and substituted La1-xEuxFeO3 (x = 0.1, 0.15, and 0.2) perovskites were synthesized by sol-gel auto-combustion and their activities during the combustion of toluene were evaluated. The structure and physico-chemical properties of the perovskites were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and BET surface area analyses. The compounds were crystallized as a perovskite phase with an orthorhombic structure. The mean particl...     

焙烧温度对甲醇水蒸气重整制氢Ce/Cu/Zn-Al水滑石衍生催化剂的影响

采用原位合成法在γ-Al_2O_3载体表面上合成了Zn-Al水滑石,再采用顺序浸渍法制备了一系列Ce/Cu/Zn-Al催化剂,并采用XRD、BET、H_2-TPR和XPS等手段对催化剂进行了表征,考察了焙烧温度对Ce/Cu/Zn-Al催化剂表面结构及其催化甲醇水蒸气重整制氢性能的影响。结果表明,焙烧温度主要影响了催化剂的Cu比表面积、表面氧空穴含量和Cu-Ce间相互作用。当焙烧温度为500℃时,催化剂Cu的比表面积较大,表面氧空穴含量较多,Cu-Ce间相互作用较强,因此,催化甲醇水蒸气重整制氢活性较好。当焙烧温度升高到700℃时,Cu物种主要以稳定的CuAl_2O_4尖晶石形式存在,不利于甲醇水蒸气重整制氢反应的进行,因此,催化活性较差。     

CuO/ZrO_2催化水煤气变换反应制氢:ZrO_2载体焙烧温度的影响

以经不同温度(120、250、350、450℃)焙烧处理的ZrO_2为载体,采用沉积-沉淀法制备了系列CuO/ZrO_2催化剂;考察了富氢气氛下催化剂的水煤气变换反应(WGS)催化性能。结果表明,CuO/ZrO_2催化剂的催化活性随ZrO_2载体焙烧温度的升高呈现先升高后降低的"火山型"变化趋势,在焙烧温度为250℃时取得最高值。采用X射线粉末衍射、N_2物理吸附-脱附、N_2O滴定、H_2程序升温还原和CO程序升温还原及质谱跟踪等技术研究了系列ZrO_2载体及CuO/ZrO_2催化剂的结构和还原性能。结果表明,随着ZrO_2焙烧温度的升高,一方面,CuO/ZrO_2催化剂的Cu分散度逐渐降低,与ZrO_2具有强相互作用的高分散活性Cu-[O]-Zr物种("[]"表示ZrO_2表面氧空位)逐渐减少;另一方面,Cu-[O]-Zr物种的还原能力逐渐增强,并诱导催化剂活性表面羟基的还原能力也相应增强(CO为还原剂),即降低了催化剂对WGS反应的起活温度。两方面的综合作用使得ZrO_2载体焙烧温度为250℃(中等温度)时,CuO/ZrO_2催化剂的WGS催化活性最高。     

NiO/LaMnO3催化剂用于乙醇水蒸气重整反应

采用柠檬酸络合-浸渍法制备了NiO/LaMnO3钙钛矿型复合氧化物催化剂并将其应用于乙醇水蒸汽重整制氢反应, 考察了NiO含量、焙烧温度对催化剂性能的影响, 采用XRD、TPR和热分析等手段对催化剂进行了表征. 结果表明, 该催化剂具有高活性、高选择性和良好的稳定性. 催化剂中的NiO含量和焙烧温度对催化性能有显著影响. 在原料气体积组成为20%(体积分数, φ) C2H5OH 和水以及80%(φ)N2, 其中水醇摩尔比为3:1, 空速为80000 mL·h-1·g-1 cat, 反应温度为400 ℃时, 15%(质量分数, w)的NiO/LaMnO3上, 乙醇转化率接近100%. 关联催化剂活性和TPR及XRD实验结果, 发现催化剂的高活性源于由催化剂前驱体中进入钙钛矿型复合氧化物晶格中的镍离子被还原所得的金属镍.     

稀土添加剂对超细ZrO2织构、结构的影响

Pure zirconia and zirconia containing Y or Ce were prepared by Supercritical Drying Method (SCD) followed by calcination in air at temperature up to 700℃. It was found that the zirconia containing Y or Ce possessed much higher specific surface area and larger pore volume than that of pure zirconia. The BET surface area of 3.4Y2O3-96.6ZrO2 without calcination and that calcined at 700℃ were 376.2 m2﹒g-1 and 80.0 m2﹒g-1 respectively, while the corresponding values of pure zirconia were 248.0 m2 ﹒g-1 and 47.8 m2﹒g-1 respectively. It was postulated that the better textural properties of zirconia containing Y or Ce were resulted from preventing zirconia particles sintering in the presence of Y or Ce additive. All of these samples made by SCD had a well-developed mesoporous texture.     

铈源对甲醇水蒸气重整制氢CuO/CeO2催化剂的影响

采用沉淀法合成了CeO_2载体,再经浸渍法负载活性组分得到CuO/CeO_2催化材料,探究了铈源(Ce(NO_3)_3·6H_2O、Ce Cl_3·6H_2O、Ce(NH_4)_2(NO_3)_6、Ce(SO_4)_2·4H_2O)对CuO/CeO_2催化性能的影响。通过采用XRD、SEM、N_2O滴定、BET和H_2-TPR等表征手段对催化材料的结构和性质研究发现,四种铈源合成的CuO/CeO_2催化材料在Cu比表面积、还原性能以及活性组分和载体间的相互作用方面存在着明显差别。其中,由Ce(NO_3)_3·6H_2O合成的CuO/CeO_2催化材料的Cu比表面积较大,CuO还原温度较低,CeO_2载体与CuO之间相互作用较强,在甲醇水蒸气重整反应过程中,表现出较佳的催化活性,在反应温度为553 K,水醇比n(H_2O)/n(MeOH)为1.2,甲醇水蒸气气体空速(GHSV)为1760 h~(-1)时,甲醇的转化率为100%,重整气中CO摩尔含量为0.84%。