Sol–gel synthesis of Eu<Superscript>3+</Superscript>: Tb<Subscript>3</Subscript>Al<Subscript>5</Subscript>O<Subscript>12</Subscript> nanophosphor

Eu (0.1, 0.5 and 1.0 mol%) doped Tb₃Al₅O₁₂ (TAG) was prepared by sol–gel technique through nitrate-citrate route followed by sintering in air (1,100 °C maximum temperature). XRD analysis showed that Eu³⁺ enters the TAG lattice substitutionally replacing the Tb³⁺ ion. Both XRD as well as FTIR investigation showed improvement in crystalline phase with the increase in the sintering temperature. SEM and TEM analysis showed that the powder contains the particles in 5–20 nm size with almost spherical morphology. The excitation spectrum recorded in 300–500 nm showed dominant absorption due to Tb³⁺ while the emission spectra recorded with 380 nm excitation had strong red emission characteristic of Eu³⁺. The intensity of this emission increases with the increase of the Eu concentration from 0.1 to 0.5 mol%. However, the emission intensity decreased on further increase in Eu concentration to 1.0 mol%. This intensity variation with dopant concentration is attributed to well-known “concentration quenching” observed in rare-earth doped materials. Reasonably strong red emission due to Eu was observed when excited with the blue (480 nm) radiation of a Xe lamp indicating the usefulness of the material for the realization of white light LED.     

Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Eu<Superscript>3+</Superscript>,Tb<Superscript>3+</Superscript> thin films prepared by sol–gel method: structural and optical studies

Y₂O₃: Eu³⁺,Tb³⁺ transparent, high density and optical quality thin films were prepared by the sol–gel dip-coating technique. Yttrium (III) 2,4-pentadionate was used as a precursor by its hydrolysis in ethanol. The doping agents were incorporated in the form of europium and terbium nitrate. Structural, morphological and optical properties of prepared films were investigated for different annealing temperatures in order to establish the ideal processing route that enhances the luminescent properties. X-ray diffraction (XRD) analysis shows the cubic phase for 10-layer films and annealing temperatures higher than 500°C. At 700°C, highly densified (4.52 g cm⁻³) and very smooth films (1.4 nm at 700°C) are produced, composed of crystallites with a grain size of 11 nm. The film thickness, refractive index and porosity, as well as the luminescent properties, were found to vary with treatment temperature.     

Sol–gel synthesis of Eu<Superscript>3+</Superscript> incorporated CaMoO<Subscript>4</Subscript>: the enhanced luminescence performance

In order to develop high efficiency red emitting phosphors, Ca_0.76MoO₄: Eu _0.24 ³⁺ samples are investigated via sol–gel and solid state reaction. The XRD analysis reveals that both methods can synthesize phosphors with tetragonal CaMoO₄ phase successfully. Smaller crystal size of samples prepared by sol–gel can be observed, and the grain size of these samples are around 100–200 nm, which is also smaller than the one prepared by solid state reaction. All phosphors present a red emission at 616 nm wavelength and one sol–gel synthesized sample exhibits the strongest emission intensity because of the higher quantum efficiency. It is attributed to the removal of lattice defects by sol–gel, in which way luminescent efficiency is enhanced. This can be reflected by the longer fluorescent lifetime of phosphors.     

Single-phased white-light emitting CaAl<Subscript>2</Subscript>Si<Subscript>2</Subscript>O<Subscript>8</Subscript>: Eu<Superscript>2+</Superscript>, Mn<Superscript>2+</Superscript> phosphors prepared by a sol–gel method

CaAl₂Si₂O₈: Eu²⁺, Mn²⁺ phosphors have been prepared by a sol–gel method. X-ray diffractometer, spectrofluorometer and UV–Vis spectrometer were used to characterize structural and optical properties of the samples. The results indicate that anorthite (CaAl₂Si₂O₈) directly crystallizes at 1000 °C in the sol–gel process. CaAl₂Si₂O₈: Eu²⁺, Mn²⁺ phosphors show two emission bands excited by ultraviolet light. Blue (around 415 nm) and yellow (around 575 nm) emissions originate from Eu²⁺ and Mn²⁺, respectively. With appropriate tuning of Mn²⁺ content, CaAl₂Si₂O₈: Eu²⁺, Mn²⁺ phosphors exhibit different hues and relative color temperatures.     

Sol–gel synthesis and characterization of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–TiO<Subscript>2</Subscript> nanocrystalline powder

Al₂O₃–TiO₂ nanocrystalline powders were synthesized by sol–gel process. Aluminum sec-butoxide and titanium isopropoxide chemicals were used as precursors and ethyl acetoacetate was used as chelating agent. Thermal and crystallization behaviors of the precursor powders were investigated by thermal gravimetric-differential thermal analysis, Fourier-transform infrared spectrum and X-ray diffraction. The average crystalline size of heat treated Al₂O₃–TiO₂ powders at 1,100 °C is ~100 nm.     

Strong visible up-conversion emissions and thermometric applications of Er<Superscript>3+</Superscript>–Yb<Superscript>3+</Superscript> codoped Al<Subscript>2</Subscript>O<Subscript>3</Subscript> prepared by the sol–gel method

The Er³⁺–Yb³⁺ codoped Al₂O₃ has been prepared by the sol–gel method using the aluminium isopropoxide [Al(OC₃H₇)₃]-derived Al₂O₃ sols with addition of the erbium nitrate [Er(NO₃)₃ · 5H₂O] and ytterbium nitrate [Yb(NO₃)₃ · 5H₂O]. The phase structure, including only two crystalline types of doped Al₂O₃ phases, θ and γ, was obtained for the 1 mol% Er³⁺ and 5 mol% Yb³⁺ codoped Al₂O₃ at the sintering temperature of 1,273 K. By a 978 nm semiconductor laser diodes excitation, the visible up-conversion emissions centered at about 523, 545, and 660 nm were obtained. The temperature dependence of the green up-conversion emissions was studied over a wide temperature range of 300–825 K, and the reasonable agreement between the calculated temperature by the fluorescence intensity ratio (FIR) theory and the measured temperature proved that Er³⁺–Yb³⁺ codoped Al₂O₃ plays an important role in the application of high temperature sensor.     

Synthesis of Ca<Subscript>3</Subscript>Al<Subscript>6</Subscript>Si<Subscript>2</Subscript>O<Subscript>16</Subscript>: Ce<Superscript>3+</Superscript>, Tb<Superscript>3+</Superscript> phosphors by sol–gel method and optical properties

Ca₃Al₆Si₂O₁₆: Ce³⁺, Tb³⁺ phosphors have been prepared by sol–gel method. The structure and photoluminescence properties were studied with careful. The results indicated that the single-phased Ca₃Al₆Si₂O₁₆ phosphors crystallize at 1,000 °C for 2 h in conventional furnace. With appropriate concentrations of Ce³⁺ and Tb³⁺ ions into Ca₃Al₆Si₂O₁₆ matrix, these materials exhibit blue phosphors and white light under ultraviolet radiation. White-light emission can be achieved because of a 400 nm emission ascribed to transitions of Ce³⁺ ions and three sharp peaks at 487, 543, 585 nm, respectively, resulting from transitions of Tb³⁺ ions.     

Luminescence and long-lasting afterglow in Mn<Superscript>2+</Superscript> and Eu<Superscript>3+</Superscript> co-doped ZnO–GeO<Subscript>2</Subscript> glasses and glass ceramics prepared by sol–gel method

To develop new fluorescent and afterglow materials, Mn²⁺ and Eu³⁺ co-doped ZnO–GeO₂ glasses and glass ceramics were prepared by a sol–gel method and their optical properties were investigated by measuring luminescence, excitation and afterglow spectra, and luminescence quantum yield (QY). Under UV irradiation at 254 nm, some glasses and all of the glass ceramics showed green luminescence peaking at 534 nm due to the ⁴T₁ → ⁶A₁ transition of tetrahedrally coordinated Mn²⁺ ions. The strongest luminescence was observed in a glass ceramic of 0.1MnO–0.3Eu₂O₃–25ZnO–75GeO₂ heat treated at 900 °C, with QY of 49.8%. All of the green-luminescent glasses and glass ceramics showed green afterglow, and the afterglow lasting for more than 60 min was obtained in a glass ceramic heat treated at 900 °C. It is considered that the Eu³⁺ ions may behave as electron trapping centers to be associated with the occurrence of the green afterglow due to the Mn²⁺ ions in the co-doped system.     

Yb<Superscript>3+</Superscript> → Er<Superscript>3+</Superscript> energy transfer in Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and temperature characteristic of near-infrared photoluminescence

For the Er³⁺–Yb³⁺ codoped Al₂O₃ powders, the strong near-infrared photoluminescence (PL) centered at 1.535 μm derived from the energy transfer (ET) from Yb³⁺ to Er³⁺ was detected by a 978 nm laser diode excitation. Compared with that of Er³⁺ doped Al₂O₃ powders, the PL intensity enhanced about 9 times, the full width at half maximum (FWHM) extended from 82 to 90 nm, and the lifetime increased from 3.22 to 4.17 ms for Er³⁺–Yb³⁺ codoped Al₂O₃ powders at room temperature. The ET coefficient of 2.18 × 10⁻¹⁸ cm³ s⁻¹ from Yb³⁺ to Er³⁺ was obtained based on the rate equations. The decrease of PL intensity with increasing temperature in the range of 298–733 K was observed, due to thermally enhanced nonradiative relaxation ⁴I_13/2 → ⁴I_15/2 dominated over thermally enhanced phonon-assisted ET in the Er³⁺–Yb³⁺ codoped Al₂O₃.     

Colour tuneability and white light generation in Yb<Superscript>3+</Superscript>–Ho<Superscript>3+</Superscript>–Tm<Superscript>3+</Superscript> co-doped SiO<Subscript>2</Subscript>–LaF<Subscript>3</Subscript> nano-glass-ceramics prepared by sol–gel method

Nanostructured transparent glass-ceramics with composition of 95SiO₂–5LaF₃ co-doped with 0.3Yb³⁺, 0.1Ho³⁺ and 0.1Tm³⁺ (mol%) were synthesized by thermal treatment of precursor sol–gel derived glasses. X-ray diffraction and transmission electron microscopy analysis point out the precipitation of hexagonal LaF₃ nanocrystals with diameter ranging from 11 to 20 nm in these nano-glass-ceramics. White light generation by means of efficient blue, green and red up-conversion luminescence under infrared excitation at 980 nm was observed and involved mechanisms were analyzed. Colour tuneability is achieved by varying the up-conversion emission ratios as a function of pump power.     

Sol–gel synthesis and characterization of polycrystalline GdFeO<Subscript>3</Subscript> and Gd<Subscript>3</Subscript>Fe<Subscript>5</Subscript>O<Subscript>12</Subscript> thin films

Thin films of the perovskite and garnet structured gadolinium ferrites GdFeO₃ and Gd₃Fe₅O₁₂ have been synthesized by a sol–gel method, based on stoichiometric mixtures of acetyl acetone chelated Gd³⁺ and Fe³⁺ dissolved in 2-methoxy ethanol. After spin coating onto Si wafers, and heating in air at 700 °C for 20 h, neatly grown essentially single phase films were obtained. From X-ray photoelectron spectroscopy an iron deficiency is observed in the uppermost layer of both films, implying that the crystallites preferably end in planes rich in Gd and O but not in Fe. The films were also characterized by X-ray powder diffraction, scanning electron microscopy, infrared spectroscopy, and magnetic measurements.     

Flame synthesized Y<Subscript>2</Subscript>O<Subscript>3</Subscript>:Tb<Superscript>3+</Superscript>–Yb<Superscript>3+</Superscript> phosphors as spectral convertors for solar cells

Near-infrared (NIR) quantum cutting phosphors serve as a potential material for fabricating photovoltaic spectral convertors. In many cases, quantum cutting phosphors are obtained via a wet chemical method coupled with a post-annealing treatment—a very costly process. In this report, we used continuous flame spray pyrolysis (FSP) for fabricating Y₂O₃:Tb³⁺–Yb³⁺ quantum-cutting phosphors without any post-treatment. Based on characterizations by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction, we found that as-synthesized Y₂O₃:Tb³⁺–Yb³⁺ phosphors exhibit hollow and shell-like micro-structures composed of highly crystalline and pure cubic-phase nanoparticles (< 50 nm). Photoluminescence studies of the phosphors revealed that NIR emissions appeared with the introduction of Yb to Y₂O₃:Tb³⁺. Phosphor size was successfully controlled by managing the concentration of the metal precursor solution for FSP. The Y₂O₃:Tb³⁺–Yb³⁺ phosphors were then embedded into transparent poly-ethylene-co-vinyl acetate (EVA) film to form a spectral convertor. The composite films of Y₂O₃:Tb³⁺–Yb³⁺ phosphors and poly-EVA were found to be highly transparent in the visible range (> 500 nm), making them suitable as spectral photovoltaic convertors.     

Sol–gel synthesis and transport property of nanocrystalline La<Subscript>2</Subscript>Mo<Subscript>2</Subscript>O<Subscript>9</Subscript> thin films

La₂Mo₂O₉ films were successfully synthesized on silicon (100) and poly-alumina substrates via modified sol–gel method with inorganic salts of La(NO₃)₃ and (NH₄)₆Mo₇O₂₄ as precursors. Pure La₂Mo₂O₉ phase was confirmed by XRD if the annealing temperature was higher than 500 °C. Energy dispersive spectrometry (EDS) of TEM revealed that the molar ratio of La to Mo was nearly 1:1. Field-emission SEM characterization showed that the films were dense, crack-free and uniform. The grain size of the films ranged from 30 to 400 nm depending upon the calcination temperature and duration time. The roughness calculated from AFM topography varied in the range between 10 and 35 nm. The thickness of the films was more than 200 nm for single-layered films. The electrical conductivity of the films reaches 0.06 S/cm at 600 °C that was almost more than one order of magnitude higher than that of the corresponding bulk material.     

Sol–gel synthesis and characterization of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> · CeO<Subscript>2</Subscript> doped with Pr ceramic pigments

Undoped x · α-Fe₂O₃ y · CeO₂ and doped with praseodymium ceramic pigments were obtained by the sol–gel method after heat treatment at 800 °C for 2 h. These pigments were characterized by XRD, nitrogen adsorption, scanning electron microscopy, ultraviolet-visible absorption spectroscopy and colorimetrical measurements. Red and brown colors with several tonalities were observed after changes with Ce and Pr concentration.     

Preparation and Characteristics of Nb<Superscript>5+</Superscript>, Ta<Superscript>5+</Superscript>/TiO<Subscript>2</Subscript> Nanoscale Powders by Sol–Gel Process Using TiCl<Subscript>3</Subscript>

Nanoscale TiO₂ powders doping with niobium and tantalum were prepared using TiCl₃ as a source matter. Characterization of the materials was performed by Thermoanalys, particle size, XRD, BET, FTIR, Magnetic Susceptibility. The influence of niobium and tantalum ions on the phase transition was studied, the changes in the crystal size and microstain distributions obtained at 400C were analyzed. The results show that the substitutes of Nb^{5 +}, Ta^{5 +} for Ti⁴⁺ in the anatase structure cause distortions and improve to form rutile. When the dopant content is over certain molar percent, biphase reappears. The IR spectra and magnetic susceptibility indicate the Nb–Nb (or Ta–Ta) bonds along c-axis in rutile by two Nb^{5 +} (Ta^{5 +}) ions located in sites adjacent along the c-axis appear with the dopant content. The magnetic characteristics at rutile showed a weak paramagnetism.     

Formation of solid solutions of multiferroics in the Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>–Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> system

The sequence of phases appearance during the formation of Bi_1–xNd_xFeO₃ solid solutions in powder oxides mixtures of bismuth, neodymium, and iron has been determined. It has been shown that the closeness of the reaction mixture composition to that of the individual compound (BiFeO₃ or NdFeO₃) is essential for the realization of the series of phase transformations yielding solid solutions of multiferroics Bi_1–xNd_xFeO₃ as the final product, due to the prevalence of various interphase contacts in the starting reaction zone.     

Sol gel derived Pd/Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–ZrO<Subscript>2</Subscript> as catalysts for methane combustion: effect of zirconium loading

A series of Pd/Al₂O₃–ZrO₂ materials have been prepared via sol gel method as an attractive route to obtain more homogeneous binary oxides Al₂O₃–ZrO₂. A Zr loading between 2 and 15 wt% was used to investigate the Zr promotion of Pd/Al₂O₃ materials. The prepared catalysts were calcined at two different temperatures. Very interesting results have been obtained at low zirconium content. A small amount of Zr is seen to be sufficient to stabilize the activity and to obtain good catalytic performances with developed textural properties compared to conventional catalysts used to oxidize methane. The increase of the zirconium loading is seen to decrease the catalytic activity may be due to the development of tetragonal zirconia phase detected by XRD. Similar effect has been observed after heating catalysts at high temperatures. A loss in BET surface area and in metal dispersion has been also observed for zirconium rich catalysts. A contradictory effect on textural and structural properties is seen after their calcination at 700 °C.     

Atmospheric control of gel-oxide transformation in sol–gel derived Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Y<Subscript>2</Subscript>O<Subscript>3</Subscript> fibers

Via sol–gel processing metal–organic fibers were produced and dried up to 140 °C. For these gel fibers the influence of a treatment in different atmospheres was investigated for the temperature range of 200–850 °C. The atmospheres were nitrogen, water vapor, evaporated nitric and hydrochloric acid and evaporated hydrogen peroxide. In the presence of moisture and especially with acidic moisture fibers were transformed almost completely to their oxide composition (82 mol% Al₂O₃·18 mol% Y₂O₃). In these inorganic amorphous structures considerable differences were observed on several structural levels. On the atomic scale, the coordination of Al ions was investigated by ²⁷Al MAS NMR and skeletal density by He-pycnometry. Porosity in the nm scale was characterized by N₂-sorption. As a macroscopic effect of different treatment atmospheres, the longitudinal shrinkage was observed. For fibers treated at 500 °C the relative shrinkage varied by 100% (comparing water vapor and nitrogen atmosphere). No simple correlation between the release of organic constituents, the formation of porosity and the shrinkage could be found. These aspects were controlled by the rigidity of the inorganic network against atomic reconstitution. The kind of atmosphere was found to be an effective parameter to control various aspects of the xerogel structure.     

Effects of Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> on the crystallization and structure of CaO–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> glass ceramics

Radiation-induced degradation of the weakly and strongly 4-vinylpyridine basic ion exchange resins by gamma radiolysis was investigated in the presence of air and liquid water. This study is focused on evaluating the radiolytic gases (H₂, CO, CO₂ and CH₄) and liquid products (water-solute TOC and NH₄ ⁺). The weakly basic resin yielded lower amounts of H₂ and CO and higher amounts of CO₂ than those of the strongly basic resin. Moreover, the strong basic resin tended to yield greater amounts of NH₄ ⁺. Resins were characterized by the FTIR spectroscopy technique and the results showed that the resins structures are relatively stable.