Synthesis and magnetic properties of Fe100-xMox alloy nanowire arrays

The Fe100-xMox(13≤x≤25) alloy nanowire arrays are synthesized by electrodeposition of Fe 2+ and Mo 2+ with different ionic ratios into the anodic aluminum oxide templates.The crystals of Fe100-xMox alloy nanowires gradually change from polycrystalline phase to amorphous phase with the increase of the Mo content and the nanowires are of amorphous structure when the Mo content reaches 25 at%,which are revealed by the X-ray diffraction and the selected area electron diffraction patterns.As the Mo content increases,the magnetic hysteresis loops of Fe100-xMox alloy nanowires in parallel to the nanowire axis are not rectangular and the slopes of magnetic hysteresis loops increase.Those results indicate that the magnetostatic interactions between nanowires and the magnetocrystalline anisotropy both have significant influences on the magnetization reversal process of the nanowire arrays.     

CoxCu1-x复相纳米线阵列的制备及其磁性的研究

利用电化学沉积方法在同一种富Co²⁺溶液Co²⁺/Cu²⁺=10∶1中,利用不同的沉积电位成功地制备了一系列不同成分(x=0.38—0.87)和复合相结构的Co_xCu_1-x纳米线阵列.发现随着纳米线中Cu含量的变化,Co_xCu_1-x纳米线的复相结构随之发生规律的变化,最终导致纳米线的磁性也随之规律的变化.随着纳米线中Cu含量的不断增加,一部分Cu与Co形成面心立方结构(fcc)的CoCu固溶体,减弱了磁晶各向异性与形状各向异性的竞争,从而提高样品的方形度;一部分Cu以fcc结构的Cu单质的形式存在于纳米线中,并随着Cu颗粒大小的不同分别起到破坏磁晶各向异性和钉扎畴壁的作用,从而增加纳米线的方形度和矫顽力.对比不同成分的样品,发现Co_xCu_1-x纳米线的方形度和矫顽力的最大值分别出现在Co₇₅Cu₂₅和Co₆₀Cu₄₀中,并且由于其特殊的复相结构致使它们的值要好于相同直径的单相结构的结果. 关键词： 纳米线 电化学沉积 磁性     

组合结构化合物Ho2Ni7-xFex(x=0-3.0)的晶体结构、结构转变和磁性

在金属间化合物的结构演变中,原子尺寸因素起着重要的作用.由于密堆积效应,不同原子半径比的元素往往形成不同的结构.而自由电子填充于原子构成的晶体结构的间隙中,它对化合物的结构也有影响.基于组合结构化合物Ho2Ni7-xFex,结合原子尺寸与自由电子对晶体结构的不同影响,文章探讨一种单位体积内自由电子浓度的经验方法来判断Ho2Ni7-xFex化合物中两种异构体间的转变.随着Fe含量的增加,Ho2Ni7-xFex化合物先结晶成Gd2Co7型三方结构,然后结晶成Ce2Ni7型六方结构.利用Rietveld精修技术和磁测量,获得了化合物的晶体结构参数和饱和磁化强度.化合物晶胞常数随Fe含量增加而增加,饱和磁化强度则随之减少(dMs/dx=-2).分析结果表明,单位体积内自由电子浓度更高,化合物形成三方结构,反之则形成六方结构.     

Zn掺杂n型笼合物Ba8Ga16-2xZnxGe30+x的热电传输特性

用高温熔融结合放电等离子烧结法制备了Zn掺杂单相n型Ba₈Ga_16-2xZn_xGe_30+x笼合物,探索了Zn对Ga的取代对其热电传输特性的影响规律.研究结果表明,n型Ba₈Ga_16-2xZn_xGe_30+x化合物的电导率随着x的增加逐渐增 关键词： 热电传输性能 n型笼合物 框架取代     

Structural and magnetic properties of hydrides R3Fe29−xVxHy (R=Y, Ce, Nd, Sm, Gd, Tb, and Dy)

A systematic investigation of crystallographic and intrinsic magnetic properties of the hydrides R₃Fe_29−xV_xH_y (R=Y, Ce, Nd, Sm, Gd, Tb, and Dy) has been performed in this work. The lattice constants , and c and the unit cell volume of R₃Fe_29−xV_xH_y decrease with increasing rare-earth atomic number from Nd to Dy, except for Ce, reflecting the lanthanide contraction. Hydrogenation results in regular anisotropic expansions along the a-, b-, and c-axes in this series of hydrides. Abnormal crystallographic and magnetic properties of Ce₃Fe_27.5V_1.5H_6.5, like Ce₃Fe_27.5V_1.5, suggest that the Ce ion is non-triply ionized. Hydrogenation leads to the increase in both Curie temperature for all the compounds and in the saturation magnetization at 4.2 K and RT for R₃Fe_29−xV_x with R=Y, Ce, Nd, Sm, Gd, and Dy, except for Tb. Hydrogenation also leads to a decrease in the anisotropy field at 4.2 K and RT for R₃Fe_29−xV_x with R=Y, Ce, Nd, Gd, Tb, and Dy, except for Sm. The Ce₃Fe_27.5V_1.5 and Gd₃Fe_28.4V_0.6 show the larger storage of hydrogen with y=6.5 and 6.9 in these hydrides.     

Synthesis and characterization of structural and luminescence properties of blue — green BaAlxOy:Eu2+ phosphor by solution — combustion method

Europium-doped barium aluminate (BaAl _x O _y :Eu²⁺) phosphors were obtained at low temperatures (500°C) using the solution — combustion of corresponding metal nitrate-urea solution mixtures. The particle size and morphology and the structural and luminescent properties of the synthesized phosphors were examined by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), Electron diffraction spectroscopy (EDS) and photoluminescence (PL). It was found that the change in Ba: Al molar ratios showed greatly influence not only on the particle size and morphology, but also on their PL spectra and crystalline structure. The structure of BaAl _x O _y nanophosphors changes from a hexagonal Ba₂Al₁₀O₁₇ phase for samples with 6:100 molar ratios to a hexagonal BaAl₂O₄ one with an increase in Ba content. The peak of the emission band occurs at a longer wavelength (around 615 nm) with a decrease in Ba concentration but displays a broad blue-green emission band composed from two emissions with the maximum at 495 and 530nm coming from Eu²⁺ in two sites for increasing Ba content. The blue-green emission is probably due to the influence of 5d electron states of Eu²⁺ in the crystal field because of atomic size variation causing crystal defects while the red emission is due to f - f transitions. These findings clearly demonstrate the possibility of fine tuning the colour emission.     

Ti1－xCrxO2±δ体系的相关系、晶体结构和磁性能研究

采用溶胶凝胶法制备了Ti_1-xCr_xO_2±δ体系系列样品.利用扫描电子显微镜(SEM)，X射线光电子能谱(XPS)，粉末X射线衍射分析(XRD)方法研究了Ti_1-xCr_xO_2±δ系列样品的颗粒尺寸、形貌、组分化学态、相关系和固溶区范围；并利用超导量子干涉磁强计对样品的磁性能进行了研究.采用Rietveld结构精修的方法研究了Cr的不同掺杂量对TiO₂晶体结构的影响，研究表明，1000℃烧结的样品的固溶区范围是x=0—0.03，为金红石单相；随着Cr掺杂量的增加，金红石相晶胞参数规律性地减小；当x>0.03，为金红石相和CrO₂相两相共存.综合XRD和磁性测量结果，500℃烧结的样品的固溶区范围是x=0—0.02，为锐钛矿单相；随着Cr掺杂量的增加，锐钛矿相晶胞参数规律性地减小；当x≥0.04，为锐钛矿相和绿铬矿相(Cr₂O₃)两相共存.XPS实验结果表明，500℃和1000℃退火的样品中Cr都是以Cr⁺³和Cr⁺⁶两种化学态存在，1000℃烧结的样品中可能有更多的Cr³⁺转化为Cr⁶⁺.根据M-H和M-T曲线的测试结果发现，本文500℃烧结的Ti_1-xCr_xO_2±δ体系样品当x=0—0.02时，为室温铁磁性.当x≥0.04时，由铁磁相和顺磁相所组成，在低温下有较强的铁磁性；室温下主要是顺磁相，铁磁相只占据很小的体积分数. 关键词： 1-xCr_xO_2±δ体系')" href="#">Ti_1-xCr_xO_2±δ体系 相关系 固溶区 磁性能     

MnxSi1-x磁性薄膜的结构研究

利用X射线衍射(XRD)和X射线吸收近边结构(XANES)方法研究了在Si(100)衬底上及600℃温度条件下用分子束外延(MBE)共蒸发方法生长的Mn_xSi_1-x磁性薄膜的结构.由XRD结果表明,只有在高Mn含量(8％和17％)样品中存在着Mn₄Si₇化合物物相.而XANES结果则显示,对于Mn浓度在0.7%到17%之间的Mn_xSi_1-x样品,其Mn原子的XANES谱表现出了一致的谱线特征.基于多重散射的XANES理论计算进一步表明,只有根据Mn₄Si₇模型计算出的理论XANES谱才能够很好的重构出Mn_xSi_1-x样品的实验XANES谱.这些研究结果说明在Mn_xSi_1-x样品中,Mn原子主要是以镶嵌式的Mn₄Si₇化合物纳米晶颗粒存在于Si薄膜介质中,几乎不存在间隙位和替代位的Mn原子. 关键词： xSi_1-x磁性薄膜')" href="#">Mn_xSi_1-x磁性薄膜 分子束外延 XRD XANES     

Electrical properties of perovskite-type La(Cr1−xMnx)O3+δ

Perovskite-type La(Cr_1−xMn_x)O_3+δ (0.0x1.0) was synthesized using a sol–gel process. The crystal structure of La(Cr_1−xMn_x)O_3+δ changes from orthorhombic to rhombohedral at x=0.6. The Mn⁴⁺ ion content increases monotonically in the range 0.2x1.0. The magnetic measurement of La(Cr_1−xMn_x)O_3+δ indicates that a Mn³⁺ ion is a high-spin state with (d)³(dγ)¹. The variation of the average (Cr, Mn)-O distance is explained by ionic radii of the Cr³⁺, the Mn³⁺, the Mn⁴⁺ ions. Since the log σT–1/T curve is linear and the Seebeck coefficient (α) is independent of temperature, it is considered that La(Cr_1−xMn_x)O_3+δ is a p-type semiconductor and exhibits the hopping conductivity.     

脉冲激光沉积法制备的Ni1-xFexO稀磁半导体的结构和磁性研究

利用脉冲激光沉积方法制备出了具有室温铁磁性的Ni_1-xFe_xO(x=0.02,0.05)稀磁半导体.X射线衍射(XRD)结果表明Ni_1-xFe_xO的晶体结构为NaCl结构,并且在Fe含量较高的Ni_0.95Fe_0.05O中出现了少量的α-Fe₂O₃物相.X射线吸收近 关键词： 1-xFe_xO')" href="#">Ni_1-xFe_xO XANES 脉冲激光沉积方法     

发光二极管用红色荧光粉Sr0.8-xBaxEu0.2WO4的制备和性质研究

采用化学共沉淀法制备了不同Ba²⁺掺杂浓度、 不同煅烧温度的Sr_0.8-xBa_xEu_0.2WO₄红色荧光粉. 研究了样品的晶体取向和晶格 畸变对发光性质的影响, 实验结果表明: 合成的Sr_0.8-xBa_xEu_0.2WO₄红色荧光粉为四方相, 样品中Eu³⁺的⁵D₀–⁷F₂跃迁的红光能被近紫外光和蓝光有效激发. 适量的Ba²⁺离子取代部分的Sr²⁺提高了Sr_0.8Eu_0.2WO₄荧光粉的发光强度, Ba²⁺掺杂浓度的改变对基质的晶格参数、晶体对称性和发光性能影响较大, Ba²⁺的最佳掺杂量为30%.     

Global and local critical current density in superconducting SmFeAsO1−xFx measured by two methods

The critical current densities of polycrystalline bulk SmFeAsO_1−xF_x prepared by the powder-in-tube (PIT) method and by a conventional solid-state reaction were investigated using the remnant magnetic moment method and Campbell’s method. Two types of shielding current, corresponding to global and local critical current densities J_c were observed using both measurement methods. The global and local J_c were on the order of 10⁷ A/m² and 10¹⁰ A/m² at 5 K, respectively. The local J_c decreased slightly with increasing magnetic field. The global J_c was independent of the preparation method, while the local J_c was larger for samples prepared by PIT than for those prepared by solid-state reaction.     

Structural analysis and crystal-field calculations of Nd^3＋ in Gdx Lu1-x TaO4（x = 0.85） polycrytalline

The crystal structural parameters of Nd 3+-doped rare earth orthotantalate Gd x Lu 1 x TaO 4(x = 0.85) are determined by applying the Rietveld refinement to its X-ray diffraction,and its emission and excitation spectra at 77 K are analysed.The relativistic model of ab initio self-consistent DV-Xα method,which is applied to the cluster NdO 8 in Gd x Lu 1 x TaO 4,and the effective Hamiltonian model are used to investigate its spin-orbit and crystal-field parameters.The free-ions and crystal-field parameters are fitted to the experimental energy levels at 77 K with a root-mean-square deviation of 14.92 cm 1.According to the crystal-field calculations,96 levels of Nd 3+ are assigned.Finally,the fitting results of free-ions and crystal-field parameters are compared with those already reported for Nd 3+:YAlO 3.The results indicate that the free-ion parameters are similar to those of the Nd3+ in Gdx Lu1-x TaO4 and YAlO 3 hosts,and the crystal-field interaction of Nd3+ in Gdx Lu1-x TaO4 is stronger than that in YAlO 3.     

悬浮区域熔炼法制备LaB6单晶体与发射性能研究

采用区域熔炼法成功制备出了高质量,高纯度,大尺寸的LaB₆单晶体. 系统分析了制备过程中每个参数对LaB₆单晶生长的影响,确定了晶体生长最佳工艺为:样品转速为30 r/min,生长速度为8-10 mm/h. 分析了单晶LaB₆ (100) 晶面的热电子发射性能,结果表明,当阴极温度为1873 K时,最大热发射电流密度为44.36 A/cm²;利用 Richardson 直线法求出了绝对零度逸出功和有效逸出功分别为1.99和2.59 eV. 场发射测试结果表明,单晶LaB₆场发射单尖最大场发射电流密度达到4.9×10⁶ A/cm²,场发射因子为41500 cm^-1,表现出良好的场发射性能. 因此单晶LaB₆作为热阴极和冷阴极都具有很广阔的应用前景. 关键词： 区域熔炼法 6')" href="#">单晶LaB₆ 热发射性能 场发射性能     

Blue cathodoluminescence from thulium implanted AlxGa1−xN and InxAl1−xN

Room temperature cathodoluminescence (RTCL) was obtained from Tm implanted Al_xGa_1−xN with different AlN contents (in the range 0≤x≤0.2) and from implanted In_xAl_1−xN with different InN contents (x=0.13 and 0.19) close to the lattice match with GaN. The Tm³⁺ emission spectrum depends critically on the host material. The blue emission from Al_xGa_1−xN:Tm peaks in intensity for an AlN content of x0.11. The emission is enhanced by up to a factor of 50 times with an increase of annealing temperature from 1000 to 1300 C. The blue emission from In_0.13Al_0.87N:Tm, annealed at 1200 C, is more than ten times stronger than that from Al_xGa_1−xN:Tm, x≤0.2. However, the intensity decreases significantly as the InN fraction increases from 0.13 to 0.19.     

Systematic study on thermal lens effect and passive Q-switching of diode-pumped 1.34-μm Nd:GdxY1 ? xVO4 laser with different output couplers

The thermal lens effect and passively Q-switched laser performance of mixed Nd:Gd _x Y_{1 − x} VO₄ crystals at 1.34 μm with 5 and 10% as the output transmissions have been systematically studied. Compared with the single vanadate crystal Nd:GdVO₄, the mixed Nd:Gd _x Y_{1 − x} VO₄ crystals can enhance passively Q-switched laser characteristics due to their smaller emission cross sections, although they have stronger thermal lens effects which result in decreasing the average output power. The largest peak power and pulse energy, obtained for Nd:Gd_0.63Y_0.37VO₄, were 2.9 and 1.7 times as those of Nd:GdVO₄ under the uniform conditions.     

Magnetocaloric effects in Mn1.35Fe0.65P1-xSix compounds

The structural and magnetocaloric properties of Mn_1.35Fe_0.65P_1-xSi_x compounds are investigated. The Si-substituted compounds, Mn_1.35Fe_0.65P_1-xSi_x with x = 0.52, 0.54, 0.55, 0.56, and 0.57, are prepared by high-energy ball milling and the solid-state reaction. The X-ray diffraction shows that the compounds crystallize into the Fe₂P-type hexagonal structure with space group P62m. The magnetic measurements show that the Curie temperature of the compound increases from 253 K for x = 0.52 to 296 K for x = 0.56. The isothermal magnetic-entropy change of the Mn_1.35Fe_0.65P_1-xSi_x compound decreases with the Si content increasing. The maximal value of the magnetic-entropy change is about 7.0 J/kg稫 in the Mn_1.35Fe_0.65P_0.48Si_0.52 compound with a field change of 1.5 T. The compound quenched in water possesses a larger magnetic entropy change and a smaller thermal hysteresis than the non-quenched samples. The thermal hysteresis of the compound is less than 3.5 K. The maximum adiabatic temperature change is about 1.4 K in the Mn_1.35Fe_0.65P_0.45Si_0.55 compound with a field change of 1.48 T.     

Structural and magnetic properties of Pr3(Fe1−xCox)27.5Ti1.5 (x=0.0, 0.1, 0.2, 0.3)

A novel class of Co-substituted 3 : 29 materials, Pr₃(Fe_1−xCo_x)_27.5Ti_1.5 (x=0, 0.1, 0.2, 0.3) have been synthesized. Rietveld analysis of X-ray powder diffraction patterns for the x=0, 0.1 and 0.2 compositions showed that nearly all of the compounds are formed in monoclinic symmetry, with A2/m space group with traces of α-Fe, whereas, in x=0.3, additional traces of a (Co/Fe)–Ti (1 : 12) phase are also seen. The saturation magnetization increases with Co concentration both at 5 and 300 K and is explained on the basis of a rigid band model. A magnetic transition is observed for x=0.1 near 240 K. A large increase in Curie temperature, of about 180 K for x=0.1 and about 110 K for the other concentrations, is discussed on the basis of the strengthening of TM–TM exchange by the preferential occupation of Co in some of the Fe sites originally participating in antiferromagnetic bonds.     

Zn1-xCoxO稀磁半导体薄膜的结构及其磁性研究

利用X射线吸收精细结构、X射线衍射和磁性测量等技术研究脉冲激光气相沉积法制备的Zn_1-xCo_xO (x＝0.01,0.02)稀磁半导体薄膜的结构和磁性.磁性测量结果表明Zn₁-xCo_xO样品都具有室温铁磁性.X射线衍射结果显示其薄膜样品具有结晶良好的纤锌矿结构.荧光X射线吸收精细结构测试结果表明,脉冲激光气相沉积法制备的样品中的Co离子全部进入ZnO晶格中替代了部分Zn的格点位置,生成单一相的Zn_1-xCo_xO 稀磁半导体.通过对X射线吸收近边结构谱的分析,确定Zn_1-xCo_xO薄膜中存在O空位,表明Co离子与O空位的相互作用是诱导Zn_1-xCo_xO产生室温铁磁性的主要原因. 关键词： 1-xCo_xO稀磁半导体')" href="#">Zn_1-xCo_xO稀磁半导体 X射线吸收精细结构谱 脉冲激光气相沉积法     

Spin-phonon coupling in multiferroic manganites RMnO3: comparison of pure (R = Eu, Gd, Tb) and substituted (R = Eu1-xYx) compounds

For rare-earth manganite RMnO₃ compounds spin-phonon coupling manifests itself as a phonon softening in the temperature range of the magnetically ordered phases. Within this class of materials, a continuous tuning of the lattice and thus also of the magnetic properties of multiferroic manganites is achieved by Y doping in substituted Eu_{1- x} Y _x MnO₃. We compare the impact on spin-phonon coupling within this partial-substitution approach in a series of Eu_{1- x} Y _x MnO₃ samples 0 ≤ x ≤ 0.5) with the effect of a complete exchange of the rare earth ions R³⁺ in a series of pure RMnO₃ compounds (R = Eu, Gd, Tb). For this purpose we employ polarized Raman scattering in the 10–300 K temperature range. The low-temperature results show phonon softening in all investigated compounds. For decreasing R³⁺ radius, i.e. an increasing orthorhombic distortion and magnetic frustration, we observe in both systems a weakening of the spin-phonon coupling. For known sublattice magnetization within the MnO₂-plane, quantitative results for the spin-phonon coupling constant are derived for both cases within a molecular field approximation. Our results show, that the spin-phonon coupling strength in the magnetically ordered phases of the various investigated manganites does not correlate with the magnetization pattern. Instead, the pure RMnO₃ compounds and the substituted Eu_{1- x} Y _x MnO₃ fit excellently within a common scheme, in which the weakening of the spin-phonon coupling reflects the degree of tilting of the MnO₆ octahedra due to the orthorhombic distortion of the crystal lattice.