Study on the surface erosion route to the fabrication of TiO2 hollow spheres

Three-dimensional (3D) architecture of TiO₂ hollow sphere has many excellent and interesting performances that attract significant attention nowadays. In this paper, a simple surface erosion approach to the fabrication of TiO₂ hollow spheres via the hydrothermal process has been developed. The morphologies and the phase were characterized by scanning electron microscopy (SEM) and X-ray diffractometer (XRD). The results indicate that the anatase-type TiO₂ hollow spheres with a diameter of ∼1 μm are successfully synthesized. The shell thickness of TiO₂ hollow spheres is ∼150 nm and the size of hollow cavity is ∼600 nm. By the control experiments, the influence of ammonium fluoride and hydrogen peroxide on the hollow spherical structures was studied. Hydrogen peroxide acts as both the oxidant and the bubble generator, ammonium fluoride is crucial for the erosion and dissolution of titanium, the detailed dissolution-crystallization mechanism for the formation of TiO₂ hollow spheres was also proposed.     

Photocatalytic behavior of heavy La-doped TiO2 films deposited by pulsed laser deposition using non-sintered target

We have investigated the control of photocatalytic behavior under deposited conditions of non-sintered target of different molar ratios with TiO₂ and La₂O₃ from 1:0 to 1:2 for heavily La doping, and post-annealing temperature from 600 °C to 1000 °C for crystallizing by pulsed laser deposition. We have successfully crystallized heavily La-doped TiO₂ films with post-annealing temperature over 800 °C and with molar ratio of TiO₂:La₂O₃ over 1:1 on a quartz substrate. Heavily La-doped TiO₂ films are observed the decomposition of methylene blue and a water-splitting reaction in photocatalytic behavior under Xe light irradiation. When stoichiometric La-doped TiO₂ (TiO₂:La₂O₃ = 1: 1) is synthesized with heat-treatment at 900 °C, the best results are obtained under photocatalytic behavior and pure La₂Ti₂O₇ crystalline were obtained.     

Optical properties of ITO/TiO2 single and double layer thin films deposited by RPLAD

Indium tin oxide (ITO) and titanium dioxide (TiO₂) single layer and double layer ITO/TiO₂ films were prepared using reactive pulsed laser ablation deposition (RPLAD) with an ArF excimer laser for applications in dye-sensitized solar cells (DSSCs). The films were deposited on SiO₂ substrates either at room temperatures (RT) or heated to 200-400 °C. Under optimized conditions, transmission of ITO films in the visible (vis) range was above 89% for films produced at RT and 93% for the ones deposited at higher temperatures. Increasing the substrate temperature from RT to 400 °C enhances the transmission of TiO₂ films in the vis-NIR from about 70% to 92%. High transmission (≈90%) was observed for the double layer ITO/TiO₂ with a transmission cut-off above 900 nm. From the transmission data, the energies gaps (E_g), as well as the refractive indexes (n) for the films were estimated. n ≈ 2.03 and 2.04, respectively for ITO films and TiO₂ film deposited at 400 °C in the visible region. Post-annealing of the TiO₂ films for 3 h at 300 and 500 °C was performed to enhance n. The refractive index of the TiO₂ films increases with the post-annealing temperature. The direct band gap is 3.6, 3.74 and 3.82 eV for ITO films deposited at RT, 200, and 400 °C, respectively. The TiO₂ films present a direct band gap of 3.51 and 3.37 eV for as deposited TiO₂ films and when annealed at 400 °C, respectively. There is a shift of about 0.1 eV between ITO and ITO/TiO₂ films deposited at 200 °C. The shift decreases by half when the TiO₂ film was deposited at 400 °C. Post-annealing was also performed on double layer ITO/TiO₂.     

Effect of heat treatment on morphology, crystalline structure and photocatalysis properties of TiO2 nanotubes on Ti substrate and freestanding membrane

Highly ordered titanium oxide (TiO₂) nanotubes were prepared by electrolytic anodization of titanium electrodes. Morphological evolution and phase transformations of TiO₂ nanotubes on a Ti substrate and that of freestanding TiO₂ membranes during the calcinations process were studied by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction microscopy. The detailed results and mechanisms on the morphology and crystalline structure were presented. Our results show that a compact layer exists between the tubular layer and Ti substrate at 600 °C, and the length of the nanotubes shortens dramatically at 750 °C. The freestanding membranes have many particles on their tubes during calcinations from 450 to 900 °C. The TiO₂ nanotubes on the Ti substrate transform to rutile crystals at 600 °C, while the freestanding TiO₂ membranes retain an anatase crystal with increasing temperature to 800 °C. The photocatalytic activity of TiO₂ nanotubes on a Ti substrate annealed at different temperatures was investigated by the degradation of methyl orange in aqueous solution under UV light irradiation. Due to the anatase crystals in the tubular layer and rutile crystals in the compact layer, TiO₂ nanotubes annealed at 450 °C with pure anatase crystals have a better photocatalytic activity than those annealed at 600 °C or 750 °C.     

Synthesis of hollow silver spheres using poly-(styrene-methyl acrylic acid) as templates in the presence of sodium polyacrylate

Hollow silver spheres were successfully prepared by reducing AgNO₃ with ascorbic acid and using negatively charged poly-(styrene-methyl acrylic acid) (PSA) spheres as templates in the presence of sodium polyacrylate as a stabilizer. Firstly, silver cations adsorbed on the surface of PSA spheres via electrostatic attraction between the carboxyl groups and silver cations were reduced in situ by ascorbic acid. The silver nanoparticles deposited on the surface of PSA spheres served as seeds for the further growth of silver shells. After that, extra amount of AgNO₃ and ascorbic acid solutions were added to form PSA/Ag composites with thick silver shells. In order to obtain compact silver shells, the as-prepared PSA/Ag composites were heated at 150 °C for 3 h. Then hollow silver spheres were prepared by dissolving PSA templates with tetrahydrofuran.     

Synthesis, characterization and photodegradation study of mixed-phase titania hollow submicrospheres with rough surface

Titania hollow submicrospheres with mixed phase (anatase-brookite or anatase-rutile) were synthesized via the combination of hydrothermal treatment and calcination of submicrospheres consisting of a polystyrene core and an amorphous TiO₂ shell. After hydrothermal treatment, amorphous titania shell could be transformed to anatase-brookite shell consisting of loose packed titania nanocrystals, which could be further converted to anatase-brookite (below 700 °C) or anatase-rutile titania (700-800 °C) hollow spheres with rough surface via calcination. The loose packing of titania nanocrystals not only inhibited the transformation temperature from anatase to rutile, but also provided titania hollow submicrospheres with high photodegradation activity of Rhodamine B. The photocatalytic activity of titania hollow spheres increased firstly then decreased when the calcination temperature was varied in the range of 450-800 °C, while hollow spheres obtained via calcinating at 700 °C exhibited the highest photocatalytic activity, which was five times higher than that of counterpart without hydrothermal treatment.     

A novel approach towards high-performance composite photocatalyst of TiO2 deposited on activated carbon

TiO₂ photocatalysts deposited on activated carbon (TiO₂/AC) were prepared by dip-hydrothermal method at 180 °C using peroxotitanate as a precursor, then calcinated at 300-800 °C. The samples were characterized by X-ray diffraction, scanning electron microscopy, Raman spectroscopy and the nitrogen absorption. Their photocatalytic activity was evaluated by degradation of methyl orange (MO). The results showed that TiO₂ particles of anatase type were well deposited on the activated carbon surface. TiO₂/AC calcinated at 600 °C exhibited the best photocatalytic performance. For the comparison, the same photocatalysis experiment was carried out for two mixtures of commercial TiO₂ (Degussa P25) with AC and synthetic TiO₂ with AC. It was found that the composite catalyst TiO₂/AC was better than the two mixtures. Besides, different from fine powdered TiO₂, the granular TiO₂/AC photocatalysts could be easily separated from the bulk solution and reused; indeed, its photocatalytic ability was hardly decreased after a five-cycle for MO degradation. The kinetics of the MO degradation fitted well the Langmuir-Hinshelwood model.     

Effect of annealing on TiO2 nanoparticles

TiO₂ nanoparticles have been prepared by simple chemical precipitation method and annealed at different temperatures. The as-prepared TiO₂ are amorphous, and they transform into anatase phase on annealing at 450 °C, and rutile phase on annealing at 900 °C. The X-ray diffraction results showed that TiO₂ nanoparticles with grain size in the range of 21–24 nm for anatase phase and 69–74 nm for rutile phase have been obtained. FESEM images show the formation of TiO₂ nanoparticles with small size in structure. The FTIR and Raman spectra exhibited peaks corresponding to the anatase and rutile structure phases of TiO₂. Optical absorption studies reveal that the absorption edge shifts towards longer wavelength (red shift) with increase of annealing temperature.     

Preparation and photocatalytic activity of nitrogen-doped TiO2 hollow nanospheres

TiO₂ hollow nanospheres were prepared using silicon oxide as a template. N-doped titanium oxide hollow spheres, TiO_2−xN_x were synthesized by reacting TiO₂ hollow spheres with thiourea at 500 °C. XRD and XPS data showed that oxygen was successfully substituted by nitrogen through the nitrogen-doping reaction, and finally N-doped TiO₂ hollow spheres were formed. The N-doped TiO₂ hollow spheres showed new absorption shoulder in visible light region so that they were expected to exhibit photocatalytic activity in the visible light. The photocatalytic activity of N-doped TiO₂ hollow spheres under visible light was similar to that of normal spherical TiO_2−xN_x in spite of the structural difference.     

Preparation and characterization of iodine-doped mesoporous TiO2 by hydrothermal method

Iodine-doped mesoporous TiO₂ (I/TiO₂) was prepared by hydrothermal method, using tetrabutyl titanate as precursor, potassium iodate as iodine sources. The as-prepared I/TiO₂ catalysts were characterized by UV-vis, XRD, TEM, BET, TG/DTA, XPS and photoluminescence (PL) spectroscopy. Production of OH radicals on the I/TiO₂ surface was detected by the PL technique using terephthalic acid as a probe molecule. The effects of hydrothermal reaction temperature, calcination temperature and iodine doping content on the structure and properties of the catalysts were investigated. The results showed that iodine-doped TiO₂ calcinated at 300 °C have good anatase crystal. The optimal hydrothermal conditions have been determined to be that reaction temperature 120 °C, calcinated temperature 300 °C and added 1.16 mmol iodine dopants. The average particle size of I/TiO₂ synthesized under optimal condition (I-3 sample) is about 3.9 nm. The I-3 photocatalyst contains 100% anatase crystalline phase of TiO₂. BET specific surface area of I-3 sample is184.8 m² g⁻¹ and is 3.67 times that of pure TiO₂ (50.37 m² g⁻¹). Iodine in I/TiO₂ catalyst mainly exists in the form of I₂, and photoactivity of I/TiO₂ catalyst in visible light comes from photosensitize of I₂. I/TiO₂ catalysis shows very high efficiency for the degradation of phenol under visible light.     

Influence of growth temperature of TiO2 buffer on structure and PL properties of ZnO films

A series of ZnO films with TiO₂ buffer on Si (1 0 0) substrates were prepared by DC reactive sputtering. Growth temperature of TiO₂ buffer changed from 100 °C to 400 °C, and the influence on the crystal structures and optical properties of ZnO films have been investigated. The XRD results show that the ZnO films with TiO₂ buffer have a hexagonal wurtzite structure with random orientation, and with the increase of growth temperature of TiO₂ buffer, the residual stresses were released gradually. Specially, the UV emission enhanced distinctly and FWHMs (full width half maximum) decreased linearly with the increasing TiO₂ growth temperature. The results all come from the improvement of crystal quality of ZnO films.     

Effects of depositing temperatures on structure and optical properties of TiO2 film deposited by ion beam assisted electron beam evaporation

TiO₂, which is high in refractive index and dielectric constant, plays an important role in the fields of optics and electronics. In this work, TiO₂ films were prepared on glass substrates by the technique of ion beam assisted electron beam evaporation. The films were deposited at 50, 150 and 300 °C, respectively. Then the as-deposited TiO₂ films were annealed at 450 °C for 1 h in vacuum atmosphere. Structures and optical properties of TiO₂ films were characterized by XRD, SEM, ellipsometry and spectrophotometer. As a result, the structure and the refractive index of films were improved by both the annealing and the increasing of the deposition temperature. The UV-vis transmittance spectra also confirmed that the deposition temperature has a significant effect on the transparency of the thin films. The highest transparency over the visible wavelength region of spectra was obtained at the deposition temperature of 300 °C. The allowed direct band gap at the deposition temperature ranging from 50 to 300 °C was estimated to be in the range from 3.81 to 3.92 eV.     

Influence of temperature on structure as well as adhesion and friction and wear behavior of hydrogenated carbon nitride films prepared on silicon substrate

Hydrogenated-carbon nitride (CN_x:H) films were synthesized on silicon substrate in a large quantity by the pyrolysis of ethylenediamine in a temperature range of 700-950 °C. The influence of temperature on the morphology, structure, adhesion to substrate, and friction and wear behavior of CN_x:H films was investigated. It has been found that CN_x:H films obtained at 700 °C and 800 °C are amorphous, and those prepared at 900 °C and 950 °C consist of carbon nitride nanocrystal. Besides, CN_x:H film sample obtained at 700 °C has the maximum N content of 9.1 at.% but the poorest adhesion to Si substrate, while the one prepared at 900 °C has the lower N content and the highest adhesion to substrate. As a result, nanocrystalline CN_x:H (nc-CN_x:H) film synthesized at 900 °C possesses the best wear resistance when slides against stainless steel counterpart. N atom is incorporated into the graphitic network in three different bonding forms, and their relative content is closely related to temperature, corresponding to different adhesion as well as friction and wear behavior of the films obtained at different temperatures. Furthermore, the friction coefficient and antiwear life of as-deposited CN_x:H films vary with varying deposition temperature and thickness, and the film with thickness of 1.3 μm, obtained at 900 °C, has the longest antiwear life of over 180,000 s.     

Correlation between microstructure and optical properties of nano-crystalline TiO2 thin films prepared by sol-gel dip coating

Titanium dioxide thin films have been prepared from tetrabutyl-orthotitanate solution and methanol as a solvent by sol-gel dip coating technique. TiO₂ thin films prepared using a sol-gel process have been analyzed for different annealing temperatures. Structural properties in terms of crystal structure were investigated by Raman spectroscopy. The surface morphology and composition of the films were investigated by atomic force microscopy (AFM). The optical transmittance and reflectance spectra of TiO₂ thin films deposited on silicon substrate were also determined. Spectroscopic ellipsometry study was used to determine the annealing temperature effect on the optical properties and the optical gap of the TiO₂ thin films. The results show that the TiO₂ thin films crystallize in anatase phase between 400 and 800 °C, and into the anatase-rutile phase at 1000 °C, and further into the rutile phase at 1200 °C. We have found that the films consist of titanium dioxide nano-crystals. The AFM surface morphology results indicate that the particle size increases from 5 to 41 nm by increasing the annealing temperature. The TiO₂ thin films have high transparency in the visible range. For annealing temperatures between 1000 and 1400 °C, the transmittance of the films was reduced significantly in the wavelength range of 300-800 nm due to the change of crystallite phase and composition in the films. We have demonstrated as well the decrease of the optical band gap with the increase of the annealing temperature.     

Optimization of nickel adsorption from aqueous solution by using activated carbon prepared from waste apricot by chemical activation

Waste apricot supplied by Malatya apricot plant (Turkey) was activated by using chemical activation method and K₂CO₃ was chosen for this purpose. Activation temperature was varied over the temperature range of 400-900 °C and N₂ atmosphere was used with 10 °C/min heat rate. The maximum surface area (1214 m²/g) and micropore volume (0.355 cm³/g) were obtained at 900 °C, but activated carbon was predominantly microporous at 700 °C. The resulting activated carbons were used for removal of Ni(II) ions from aqueous solution and adsorption properties have been investigated under various conditions such as pH, activation temperature, adsorbent dosage and nickel concentration. Adsorption parameters were determined by using Langmuir model. Optimal condition was determined as; pH 5, 0.7 g/10 ml adsorbent dosage, 10 mg/l Ni(II) concentration and 60 min contact time. The results indicate that the effective uptake of Ni(II) ions was obtained by activating the carbon at 900 °C.     

Surface study of fine MgFe2O4 ferrite powder prepared by chemical methods

To study surface behaviors, MgFe₂O₄ ferrite materials having different grain sizes were synthesized by two different chemical methods, i.e., a polymerization method and a reverse coprecipitation method. The single phase of the cubic MgFe₂O₄ was confirmed by the X-ray diffraction method for both the precursors decomposed at 600-1000 °C except for a very small peak of Fe₂O₃ was detected for the samples calcined at 600 and 700 °C by the polymerization method. The crystal size and particle size increased with an increase in the sintering temperature using both methods. The conductance of the MgFe₂O₄ decreased when the atmosphere was changed from ambient air to air containing 10.0 ppm NO₂. The conductance change, C = G(air)/G(10 ppm NO₂), was reduced with an increase in the operating temperature. For the polymerization method, the maximum C-value was ca. 40 at 300 °C for the samples sintered at 900 °C. However, the samples sintered at 1000 °C showed a low conductance change in the 10 ppm NO₂ gas, because the ratio of the O₂ gas adsorption sites on the particle surface is smaller than those of the samples having a high C-value. The low Mg content on the surface affects the low ratio of the gas adsorption sites. For the reverse coprecipitation method, the particle size was smaller than that of the polymerization method. Although a stable conductance was obtained for the sample sintered at 900 and 1000 °C, its conductance change was less than that of the polymerization method.     

Nanostructure of photocatalytic TiO2 films sputtered at temperatures below 200 °C

The article reports on correlations between the process parameters of reactive pulsed dc magnetron sputtering, physical properties and the photocatalytic activity (PCA) of TiO₂ films sputtered at substrate surface temperature T_surf ≤ 180 °C. Films were deposited using a dual magnetron system equipped with Ti (Ø50 mm) targets in Ar + O₂ atmosphere in oxide mode of sputtering. The TiO₂ films with highly photoactive anatase phase were prepared without a post-deposition thermal annealing. The decomposition rate of the acid orange 7 (AO7) solution during the photoactivation of the TiO₂ film with UV light was used for characterization of the film PCA. It was found that (i) the partial pressure of oxygen pO₂ and the total sputtering gas pressure p_T are the key deposition parameters influencing the TiO₂ film phase composition that directly affects its PCA, (ii) the structure of sputtered TiO₂ films varies along the growth direction from the film/substrate interface to the film surface, (iii) ∼500 nm thick anatase TiO₂ films with high PCA were prepared and (iv) the structure of sputtered TiO₂ films is not affected by the substrate surface temperature T_surf when T_surf < 180 °C. The interruption of the sputtering process and deposition in long (tens of minutes) pulses alternating with cooling pauses has no effect on the structure and the PCA of TiO₂ films and results in a decrease of maximum value of T_surf necessary for the creation of nanocrystalline nc-TiO₂ film. It was demonstrated that crystalline TiO₂ films with high PCA can be sputtered at T_surf ≤ 130 °C. Based on obtained results a phase zone model of TiO₂ films was developed.     

Nano-sized silica hollow spheres: Preparation, mechanism analysis and its water retention property

In this article, synthesis of nano-sized silica hollow spheres applying positive charged polystyrene as sacrificial templates was introduced. Firstly, nano-sized polystyrene particles were synthesized by emulsifier-free emulsion polymerization under solvothermal condition. Secondly, silica hollow nanospheres were formed through a simultaneous ‘coating-etching’ process. PVP played a key role in the evolution of nano-sized hollow spheres even if the templates were positive charged and the formation mechanism was different from that of previous studies. TEM results revealed that the morphologies of nano-sized silica hollow spheres not only strongly relied on the amount of reactant, but also the sequence of adding them. TGA illustrated that the interiors of nano-sized silica hollow spheres were not completely ‘hollow’. Brunauer-Emmett-Teller (BET) analysis showed that this material had a specific area of 399 m²/g. The water retention property of the materials was also investigated.     

Effect of TiO2/Al2O3 film coated diamond abrasive particles by sol-gel technique

The diamond abrasive particles were coated with the TiO₂/Al₂O₃ film by the sol-gel technique. Compared with the uncoated diamonds, the TiO₂/Al₂O₃ film was excellent material for the protection of the diamonds. The results showed that the incipient oxidation temperature of the TiO₂/Al₂O₃ film coated diamonds in air atmosphere was 775 °C, which was higher 175 °C than that of the uncoated diamonds. And the coated diamonds also had better the diamond's single particle compressive strength and the impact toughness than that of uncoated diamonds after sintering at 750 °C. For the vitrified bond grinding wheels, replacing the uncoated diamonds with the TiO₂/Al₂O₃ film coated diamonds, the volume expansion of the grinding wheels decreased from 6.2% to 3.4%, the porosity decreased from 35.7% to 25.7%, the hardness increased from 61.2H_RC to 66.5H_RC and the grinding ratio of the vitrified bond grinding wheels to carbide alloy (YG8) increased from 11.5 to 19.1.     

Effects of forming gas annealing on LiNbO3 single crystals

Z-cut congruent LiNbO₃ single crystals were annealed in 95%N₂+5%H₂ at high temperatures. X-ray diffraction showed that 2θ of (0 0 0 6) peak is obviously reduced by 0.6° and 1.0° for the samples annealed at 600 and 900 °C, respectively. A new peak appears at the high-energy side of O 1s spectrum in X-ray photoelelectron spectroscopy (XPS) analyses, and the leakage current is greatly increased. It is proposed that hydrogen is incorporated in LiNbO₃ single crystals through forming gas annealing at temperatures up to 900 °C and exists in LiNbO₃ as a proton bound to an oxygen ion through O-H bond with its electron donated.