PLD of Fe3O4 thin films: Influence of background gas on surface morphology and magnetic properties

Ablation of Fe₃O₄ targets has been performed using a pulsed UV laser (KrF, λ = 248 nm, 30 ns pulse duration) onto Si(100) substrates, in reactive atmospheres of O₂ and/or Ar, with different oxygen partial pressures. The as-deposited films were characterised by atomic force microscopy (AFM), X-ray diffraction (XRD), conversion electron Mössbauer spectroscopy (CEMS) and extraction magnetometry, in order to optimise the deposition conditions in the low temperature range. The results show that a background mixture of oxygen and argon improves the Fe:O ratio in the films as long as the oxygen partial pressure is maintained in the 10⁻² Pa range. Thin films of almost stoichiometric single phase polycrystalline magnetite, Fe_2.99O₄, have been obtained at 483 K and working pressure of 7.8 × 10⁻² Pa, with a high-field magnetization of ∼490 emu/cm³ and Verwey transition temperature of 112 K, close to the values reported in the literature for bulk magnetite.     

Femtosecond Z-scan measurement of third-order optical nonlinearities in anatase TiO2 thin films

Anatase phase TiO₂ films have been grown on fused silica substrate by pulsed laser deposition technique at substrate temperature of 750 °C under the oxygen pressure of 5 Pa. From the transmission spectra, the optical band gap and linear refractive index of the TiO₂ films were determined. The third-order optical nonlinearities of the films were measured by Z-scan method using a femtosecond laser (50 fs) at the wavelength of 800 nm. The real and imaginary parts of third-order nonlinear susceptibility χ⁽³⁾ were determined to be −7.1 × 10⁻¹¹esu and −4.42 × 10⁻¹²esu, respectively. The figure of merit, T, defined by T=βλ/n₂, was calculated to be 0.8, which meets the requirement of all-optical switching devices. The results show that the anatase TiO₂ films have great potential applications for nonlinear optical devices.     

Preparation of transparent conductive TiO2:Nb thin films by pulsed laser deposition

This study investigated the optical and electrical properties of Nb-doped TiO₂ thin films prepared by pulsed laser deposition (PLD). The PLD conditions were optimized to fabricate Nb-doped TiO₂ thin films with an improved electrical conductivity and crystalline structure. XRD analyses revealed that the deposition at room temperature in 0.92 Pa O₂ was suitable to produce anatase-type TiO₂. A Nb-doped TiO₂ thin film attained a resistivity as low as 6.7 × 10⁻⁴ Ω cm after annealing at 350 °C in vacuum (<10⁻⁵ Pa), thereby maintaining the transmittance as high as 60% in the UV-vis region.     

Annealing temperature influence on electrical properties of ion beam sputtered Bi2Te3 thin films

Ion beam sputtering process was used to deposit n-type fine-grained Bi₂Te₃ thin films on BK7 glass substrates at room temperature. In order to enhance the thermoelectric properties, thin films are annealed at the temperatures ranging from 100 to 400 °C. X-ray diffraction (XRD) shows that the films have preferred orientations in the c-axis direction. It is confirmed that grain growth and crystallization along the c-axis are enhanced as the annealing temperature increased. However, broad impurity peaks related to some oxygen traces increase when the annealing temperature reached 400 °C. Thermoelectric properties of Bi₂Te₃ thin films were investigated at room temperature. The Bi₂Te₃ thin films, including as-deposited, exhibit the Seebeck coefficients of −90 to −168 μV K⁻¹ and the electrical conductivities of 3.92×10²-7.20×10² S cm⁻¹ after annealing. The Bi₂Te₃ film with a maximum power factor of 1.10×10⁻³ Wm⁻¹ K⁻² is achieved when annealed at 300 °C. As a result, both structural and transport properties have been found to be strongly affected by annealing treatment. It was considered that the annealing conditions reduce the number of potential scattering sites at grain boundaries and defects, thus improving the thermoelectric properties.     

The luminescence and optoelectrical properties of ITO films prepared by a sputter type negative metal ion deposition

Transparent conducting indium tin oxide (ITO) thin films were prepared on glass substrates by a magnetron sputter type negative ion source which requires cesium (Cs) vapor injection for surface negative ionization on the ITO target surface. Although the film was prepared at 70 °C, it attained high optical transmittance, 88% and low resistivity, 2.03 × 10⁻⁴ Ω cm, at an optimized Cs partial pressure of P_Cs = 1.7 × 10⁻³ Pa. The as-deposited ITO films have a poly-crystalline structure with (2 1 1), (2 2 2), (4 0 0), (4 1 1) and (4 4 0) reflections.Also, ITO films prepared at P_Cs = 1.7 × 10⁻³ Pa were post-deposition vacuum annealed at 300 °C for 30 min. The films had a resistivity of 1.8 × 10⁻⁴ Ω cm and a transparency of 89.2%. The post-deposition vacuum annealed ITO film was used as an anode for a transparent organic light emitting diode (TOLED). A maximum luminance of 19,000 cd/m² was obtained.     

X-ray photoelectron spectroscopic studies on initial oxidation of iron and manganese mono-silicides

Initial oxidation of iron and manganese mono-silicides (FeSi and MnSi) surfaces was studied by X-ray photoelectron spectroscopy (XPS). Clean surfaces of these silicides were prepared by fracturing in an ultra high vacuum, and then the fractured surfaces were oxidized by exposing to high-purity oxygen at pressures up to 1.3 Pa. For the clean FeSi surface, positive chemical shifts of the Fe 2p_3/2 and Si 2p peaks from elemental Fe and Si were 0.5 eV and 0.1 eV, respectively. For the clean MnSi surface, a negative chemical shift of the Si 2p peak from elemental Si was 0.1 eV. Iron on the FeSi surface was oxidized at an oxygen pressure of 1.3 Pa, whereas the silicon was oxidized under the pressure of 1.3 × 10⁻⁶ Pa, indicating that oxidation of silicon occurred prior to that of iron. Manganese and silicon on the MnSi were simultaneously oxidized in the range from 1.3 × 10⁻⁶ Pa to 1.3 × 10⁻³ Pa; however, over the pressure of 1.3 Pa, the oxidation of manganese occurs prior to that of silicon. These oxidation behaviors at low oxygen pressures were similar to those of the FeSi and MnSi fractured in air.     

Metallo-organic decomposition derived (Ca, Sr)ZrO3 dielectric thin films on Pt coated Si substrate

Metallo-organic decomposition derived dielectric thin films of calcium zirconate doped with various concentrations of strontium ((Ca, Sr)ZrO₃) were prepared on Pt coated silicon substrate. Mainly in this paper, we present the investigations of their structural developments and present their electric and dielectric properties as well. The structural developments show that the CaZrO₃ film has amorphous structure with carbonate existing when annealed at 600 °C, while annealed at 650 °C and above, the carbonate is decomposed and those films crystallize into perovskite phase without preferred orientation. In addition, the prepared (Ca, Sr)ZrO₃ films with their Zr-O bonds affected by strontium doping are homogenous and stable as solid solutions in any concentration of strontium and all Bragg diffraction characteristics for the films shift downward with the increase in the concentration of strontium. Moreover, the electric properties show that the (Ca, Sr)ZrO₃ films have very low leakage current density and high breakdown strength; typically, the CaZrO₃ film annealed at 650 °C has the leakage current density approximately 9.5 × 10⁻⁸ A cm⁻² in the field strength of 2.6 MV cm⁻¹. Furthermore, the dielectric properties show that their dielectric constants are higher than 12.8 with very little dispersion in the frequency range from 100 Hz to 1 MHz and are independent of applied dc bias as well. The dielectric properties, in combination with the electric properties, make the materials promising candidates for high-voltage and high-reliability capacitor applications.     

Chemical composition of ZrC thin films grown by pulsed laser deposition

ZrC films were grown on (1 0 0) Si substrates by the pulsed laser deposition (PLD) technique using a KrF excimer laser working at 40 Hz. The nominal substrate temperature during depositions was set at 300 °C and the cooling rate was 5 °C/min. X-ray diffraction investigations showed that films deposited under residual vacuum or under 2 × 10⁻³ Pa of CH₄ atmosphere were crystalline, exhibiting a (2 0 0)-axis texture, while those deposited under 2 × 10⁻² Pa of CH₄ atmosphere were found to be equiaxed and with smaller grain size. The surface elemental composition of as-deposited films, analyzed by Auger electron spectroscopy (AES) and X-ray photoelectron spectroscopy (XPS), showed the usual high oxygen contamination of carbides. Once the topmost 2-4 nm region was removed, the oxygen concentration rapidly decreased, down to around 3-8% only in bulk. Simulations of the X-ray reflectivity (XRR) curves indicated a smooth surface morphology, with roughness values below 1 nm (rms) and films density values of around 6.30-6.45 g/cm³, very close to the bulk density. The growth rate, estimated from thickness measurements by XRR was around 8.25 nm/min. Nanoindentation results showed for the best quality ZrC films a hardness of 27.6 GPa and a reduced modulus of 228 GPa.     

Effect of oxygen pressure on structure and properties of Bi1.5Zn1.0Nb1.5O7 pyrochlore thin films prepared by pulsed laser deposition

The Bi₂O₃-ZnO-Nb₂O₅ (BZN) cubic pyrochlore thin films were prepared on Pt/TiO₂/SiO₂/Si(1 0 0) substrates by using pulsed laser deposition process. The oxygen pressure was varied in the range of 5-50 Pa to investigate its effect on the structure and dielectric properties of BZN thin films. It is found that oxygen pressure during deposition plays an important role on structure and other properties of BZN films. The BZN films deposited at temperature of 650 °C and at O₂ pressure of 5 Pa have an amorphous BZN and Nb₂O₅ phases but exhibits a cubic pyrochlore structure with a preferential (2 2 2) orientation when the oxygen pressure increases to 10 Pa. Dielectric constant and loss tangent of the films deposited at 10 Pa are 185 and 0.0008 at 10 kHz, respectively. The dielectric tunability is about 10% at a dc bias field of 0.9 MV/cm.     

Influence of oxygen partial pressure on the properties of pulsed laser deposited nanocrystalline zirconia thin films

ZrO₂ thin films were deposited at various oxygen partial pressures (2.0 × 10⁻⁵-3.5 × 10⁻¹ mbar) at 973 K on (1 0 0) silicon and quartz substrates by pulsed laser deposition. The influence of oxygen partial pressure on structure, surface morphology and optical properties of the films were investigated. X-ray diffraction results indicated that the films are polycrystalline containing both monoclinic and tetragonal phases. The films prepared in the oxygen partial pressures range 2.0 × 10⁻⁵-3.5 × 10⁻¹ mbar contain nanocrystals of sizes in the range 54-31 nm for tetragonal phase. The peak intensity of the tetragonal phase decreases with the increase of oxygen partial pressures. Surface morphology of the films examined by AFM shows the formation of nanostructures. The RMS surface roughness of the film prepared at 2.0 × 10⁻⁵ mbar is 1.3 nm while it is 3.2 nm at 3.5 × 10⁻¹ mbar. The optical properties of the films were investigated using UV-visible spectroscopy technique in the wavelength range of 200-800 nm. The refractive index is found to decrease from 2.26 to 1.87 as the oxygen partial pressure increases from 2.0 × 10⁻⁵ to 3.5 × 10⁻¹ mbar. The optical studies show two different absorption edges corresponding to monoclinic and tetragonal phases.     

CuInS2 thin films obtained through the annealing of chemically deposited In2S3-CuS thin films

In this work, we report the formation of CuInS₂ thin films on glass substrates by heating chemically deposited multilayers of copper sulfide (CuS) and indium sulfide (In₂S₃) at 300 and 350 °C in nitrogen atmosphere at 10 Torr. CIS thin films were prepared by varying the CuS layer thickness in the multilayers with indium sulfide. The XRD analysis showed that the crystallographic structure of the CuInS₂ (JCPDS 27-0159) is present on the deposited films. From the optical analysis it was estimated the band gap value for the CIS film (1.49 eV). The electrical conductivity varies from 3 × 10⁻⁸ to 3 Ω⁻¹ cm⁻¹ depending on the thickness of the CuS film. CIS films showed p-type conductivity.     

Electrical properties of La2O3 thin films grown on TiN/Si substrates via atomic layer deposition

The electrical as well as the structural properties of La₂O₃ thin films on TiN substrates were investigated. Amorphous stoichiometric La₂O₃ thin films were grown at 300 °C via atomic layer deposition technique by using lanthanum 2,2,6,6-tetramethyl-3,5-heptanedione [La(TMHD)₃] and H₂O as precursors. Post-annealing of the grown film induced dramatic changes in structural and the electrical properties. Crystalline phases of the La₂O₃ film emerged with the increase of the post-annealing temperature. Metal-insulator-metal (MIM) capacitor was fabricated to measure the electrical properties of the grown film. The dielectric constant of the La₂O₃ thin films increased with annealing temperature to reach the value of 17.3 at 500 °C. The leakage current density of the film post-annealed at 400 °C was estimated to be 2.78 × 10⁻¹⁰ and 2.1 × 10⁻⁸ A/cm² at ±1 V, respectively.     

Nonlinear optical absorption studies of an organo-metallic complex by Z-scan technique

An organo-metallic complex, [(CH₃)₄N][Ni(dmit)₂] (dmit²⁻ = (1,3-dithiole-2-thione-4,5-dithiolate), abbreviated as MeNi, is synthesized. The nonlinear optical absorption properties of MeNi dissolved in acetone have been studied using the open-aperture Z-scan technique with 40 ps pulse width at 1064 nm and 1 ns, 15 ns pulse width at 1053 nm, respectively. Strong saturable absorption has been found when the sample solution is irradiated by 40 ps and 1 ns laser pulses. While irradiated with 15 ns laser pulse, a stronger reverse saturable absorption has been found. The nonlinear optical absorption coefficients are −1.03 × 10⁻¹¹ m/W, −1.85 × 10⁻¹¹ m/W and 3.84 × 10⁻¹⁰ m/W, respectively. The mechanism responsible for the difference between the results is analyzed. All the results suggest that this material may be a promising candidate for the application to laser pulse compression in the near-infrared waveband.     

Characteristics of sandwich-structured Al2O3/HfO2/Al2O3 gate dielectric films on ultra-thin silicon-on-insulator substrates

Sandwich-structure Al₂O₃/HfO₂/Al₂O₃ gate dielectric films were grown on ultra-thin silicon-on-insulator (SOI) substrates by vacuum electron beam evaporation (EB-PVD) method. AFM and TEM observations showed that the films remained amorphous even after post-annealing treatment at 950 °C with smooth surface and clean silicon interface. EDX- and XPS-analysis results revealed no silicate or silicide at the silicon interface. The equivalent oxide thickness was 3 nm and the dielectric constant was around 7.2, as determined by electrical measurements. A fixed charge density of 3 × 10¹⁰ cm⁻² and a leakage current of 5 × 10⁻⁷A/cm² at 2 V gate bias were achieved for Au/gate stack /Si/SiO₂/Si/Au MIS capacitors. Post-annealing treatment was found to effectively reduce trap density, but increase in annealing temperature did not made any significant difference in the electrical performance.     

Fabrication and vacuum annealing of transparent conductive Ga-doped Zn0.9Mg0.1O thin films prepared by pulsed laser deposition technique

In this study, highly transparent conductive Ga-doped Zn_0.9Mg_0.1O (ZMO:Ga) thin films have been deposited on glass substrates by pulsed laser deposition (PLD) technique. The effects of substrate temperature and post-deposition vacuum annealing on structural, electrical and optical properties of ZMO:Ga thin films were investigated. The properties of the films have been characterized through Hall effect, double beam spectrophotometer and X-ray diffraction. The experimental results show that the electrical resistivity of film deposited at 200 °C is 8.12 × 10⁻⁴ Ω cm, and can be further decreased to 4.74 × 10⁻⁴ Ω cm with post-deposition annealing at 400 °C for 2 h under 3 × 10⁻³ Pa. In the meantime, its band gap energy can be increased to 3.90 eV from 3.83 eV. The annealing process leads to improvement of (0 0 2) orientation, wider band gap, increased carrier concentration and blue-shift of absorption edge in the transmission spectra of ZMO:Ga thin films.     

Structure and properties of DLC–MoS2 thin films synthesized by BTIBD method

Diamond-like carbon (DLC)–MoS₂ composite thin films were synthesized using a biased target ion beam deposition (BTIBD) technique in which MoS₂ was produced by sputtering a MoS₂ target using Ar ion beams while DLC was deposited by ion beam deposition with CH₄ gas as carbon source. The structure and properties of the synthesized films were characterized by X-ray diffraction, X-ray absorption near edge structure (XANES), Raman spectroscopy, nanoindentation, ball-on-disk testing, and corrosion testing. The effect of MoS₂ target bias voltage, ranging from −200 to −800 V, on the structure and properties of the DLC–MoS₂ films was further investigated. The results showed that the hardness decreases from 9.1 GPa to 7 GPa, the Young?s modulus decreases from 100 GPa to 78 GPa, the coefficient of friction (COF) increases from 0.02 to 0.17, and the specific wear rate coefficient (k) increases from 5×10⁻⁷ to 5×10⁻⁶ mm³ N⁻¹ m⁻¹, with increasing the biasing voltage from 200 V to 800 V. Also, the corrosion resistance of the DLC–MoS₂ films decreased with the raise of biasing voltage. Comparing with the pure DLC and pure MoS₂ films, the DLC–MoS₂ films deposited at low biasing voltages showed better tribological properties including lower COF and k in ambient air environment.     

Magnetoresistance of magnetite thin films grown by pulsed laser deposition on GaAs(1 0 0) and Al2O3(0 0 0 1)

Magnetotransport properties of magnetite thin films deposited on gallium arsenide and sapphire substrates at growth temperatures between 473 and 673 K are presented. The films were grown by UV pulsed laser ablation in reactive atmospheres of O₂ and Ar, at working pressure of 8 × 10⁻² Pa. Film stoichiometry was determined in the range from Fe_2.95O₄ to Fe_2.97O₄. Randomly oriented polycrystalline thin films were grown on GaAs(1 0 0) while for the Al₂O₃(0 0 0 1) substrates the films developed a (1 1 1) preferred orientation. Interfacial Fe³⁺ diffusion was found for both substrates affecting the magnetic behaviour. The temperature dependence of the resistance and magnetoresistance of the films were measured for fields up to 6 T. Negative magnetoresistance values of ∼5% at room temperature and ∼10% at 90 K were obtained for the as-deposited magnetite films either on GaAs(1 0 0) or Al₂O₃(0 0 0 1).     

Low-temperature thermoelectric properties of Bi85Sb15−xNbx alloys prepared by high-press sintering

The nanocrystalline materials with the general formula Bi₈₅Sb_15−xNb_x (x=0, 0.5, 1, 2, 3) were prepared by mechanical alloying and subsequent high-pressure sintering. Their transport properties involving electrical conductivity, Seebeck coefficient and thermal conductivity have been investigated in the temperature range of 80-300 K. The absolute value of Seebeck coefficient of Bi₈₅Sb₁₃Nb₂ reaches a maximum of 161 μV/K at 105 K, which is 69% larger than that of Bi₈₅Sb₁₅ at the same temperature. The power factor and figure-of-merit are 4.45×10⁻³ WK⁻²m⁻¹ at 220 K and 1.79×10⁻³ K⁻¹ at 196 K, respectively. These results suggest that thermoelectric properties of Bi₈₅Sb₁₅ based material can be improved by Nb doping.     

Microstructure and dielectric properties of La2O3 doped amorphous SiO2 films as gate dielectric material

As a potential gate dielectric material, the La₂O₃ doped SiO₂ (LSO, the mole ratio is about 1:5) films were fabricated on n-Si (0 0 1) substrates by using pulsed laser deposition technique. By virtue of several measurements, the microstructure and electrical properties of the LSO films were characterized. The LSO films keep the amorphous state up to a high annealing temperature of 800 °C. From HRTEM and XPS results, these La atoms of the LSO films do not react with silicon substrate to form any La-compound at interfacial layer. However, these O atoms of the LSO films diffuse from the film toward the silicon substrate so as to form a SiO₂ interfacial layer. The thickness of SiO₂ layer is only about two atomic layers. A possible explanation for interfacial reaction has been proposed. The scanning electron microscope image shows the surface of the amorphous LSO film very flat. The LSO film shows a dielectric constant of 12.8 at 1 MHz. For the LSO film with thickness of 3 nm, a small equivalent oxide thickness of 1.2 nm is obtained. The leakage current density of the LSO film is 1.54 × 10⁻⁴ A/cm² at a gate bias voltage of 1 V.     

Ion irradiation induced Al-Ti interaction in nano-scaled Al/Ti multilayers

Interactions induced in Al/Ti multilayers by implantation of Ar ions at room temperature were investgated. Initial structures consisted of (Al/Ti) × 5 multilayers deposited by d.c. ion sputtering on Si(1 0 0) wafers, to a total thickness of ∼250 nm. They were irradiated with 200 keV Ar⁺ ions, to the fluences from 5 × 10¹⁵ to 4 × 10¹⁶ ions/cm². It was found that ion irradiation induced a progressed intermixing of the multilayer constituents and Al-Ti nanoalloying for the highest applied fluence. The resulting nanocrystalline structure had a graded composition with non-reacted or interdiffused Al and Ti, and γ-AlTi and AlTi₃ intermetallic phases. Most intense reactivity was observed around mid depth of the multilayers, where most energy was deposited by the impact ions. It is presumed that Al-Ti chemical reaction is triggered by thermal spikes and further enhanced by chemical driving forces. The applied processing can be interesting for fabrication of tightly bond multilayered structures with gradual changes of their composition and properties.