Spectral characterization and energy levels of Cr:Sc2(MoO4)3 crystal

This paper reports the spectral properties and energy levels of Cr³⁺:Sc₂(MoO₄)₃ crystal. The crystal field strength Dq, Racah parameter B and C were calculated to be 1408 cm⁻¹, 608 cm⁻¹ and 3054 cm⁻¹, respectively. The absorption cross sections σ_α of ⁴A₂→⁴T₁ and ⁴A₂→⁴T₂ transitions were 3.74×10⁻¹⁹ cm² at 499 nm and 3.21×10⁻¹⁹ cm² at 710 nm, respectively. The emission cross section σ_e was 375×10⁻²⁰ cm² at 880 nm. Cr³⁺:Sc₂(MoO₄)₃ crystal has a broad emission band with a broad FWHM of 176 nm (2179 cm⁻¹). Therefore, Cr³⁺:Sc₂(MoO₄)₃ crystal may be regarded as a potential tunable laser gain medium.     

MoO3/Al2O3催化剂中Mo分散的正电子研究

用浸渍法制备了一系列不同Mo含量的MoO₃/Al₂O₃催化剂.测量了这些样品的正电子湮没寿命谱(PALS)与符合多普勒展宽(CDB)谱,以研究其孔洞结构以及Mo分散.正电子寿命测量结果表明,Al₂O₃载体中存在两种不同尺寸的孔洞.掺入MoO₃之后,Mo原子主要进入Al₂O₃的大孔中,使孔洞体积减小.符合多普勒展宽谱结果表明,当MoO 关键词： 3/Al₂O₃催化剂')" href="#">MoO₃/Al₂O₃催化剂 正电子湮没寿命谱 符合多普勒展宽 Mo 分散     

花状NaY(MoO4)2的合成和(MoO4)2:Eu3+的光学性质

用微波辅助水热-煅烧法成功合成了花状NaY(MoO₄)₂颗粒,用XRD、XPS、FESEM进行了表征,提出了花状NaY(MoO₄)₂颗粒可能的形成机理. 采用相同的方法合成了NaY(MoO₄)₂:Eu³⁺荧光体,该荧光材料在612 nm处有一个强的发射峰,可用作白色发光二极管的红色磷光剂. 此外,微波辅助水热-煅烧法可能发展成为制备其他花状稀土钼酸盐的有效途径.     

CO2 adsorption on Cr(1 1 0) and Cr2O3(0 0 0 1)/Cr(1 1 0)

We attempt to correlate qualitatively the surface structure with the chemical activity for a metal surface, Cr(1 1 0), and one of its surface oxides, Cr₂O₃(0 0 0 1)/Cr(1 1 0). The kinetics and dynamics of CO₂ adsorption have been studied by low energy electron diffraction (LEED), Aug er electron spectroscopy (AES), and thermal desorption spectroscopy (TDS), as well as adsorption probability measurements conducted for impact energies of E_i = 0.1-1.1 eV and adsorption temperatures of T_s = 92-135 K. The Cr(1 1 0) surface is characterized by a square shaped LEED pattern, contamination free Cr AES, and a single dominant TDS peak (binding energy E_d = 33.3 kJ/mol, first order pre-exponential 1 × 10¹³ s⁻¹). The oxide exhibits a hexagonal shaped LEED pattern, Cr AES with an additional O-line, and two TDS peaks (E_d = 39.5 and 30.5 kJ/mol). The initial adsorption probability, S₀, is independent of T_s for both systems and decreases exponentially from 0.69 to 0.22 for Cr(1 1 0) with increasing E_i, with S₀ smaller by ∼0.15 for the surface oxide. The coverage dependence of the adsorption probability, S(Θ), at low E_i is approx. independent of coverage (Kisliuk-shape) and increases initially at large E_i with coverage (adsorbate-assisted adsorption). CO₂ physisorbs on both systems and the adsorption is non-activated and precursor mediated. Monte Carlo simulations (MCS) have been used to parameterize the beam scattering data. The coverage dependence of E_d has been obtained by means of a Redhead analysis of the TDS curves.     

Influences of laser remelting on microstructure of nanostructured Al2O3-13 wt.% TiO2 coatings fabricated by plasma spraying

The effects of laser remelting on microstructure of nanostructured Al₂O₃-13 wt.% TiO₂ ceramic coatings prepared by plasma spraying with agglomerated powders were studied. The microstructure of the feedstock, as-sprayed and laser-remelted coatings were investigated by using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffractometry (XRD). The results indicate that the plasma-sprayed ceramic coating consists of both fully melted regions and partially melted regions. The totally ceramic coating, especially the fully melted regions, has a typical plasma-sprayed lamellar-like structure as the conventional coating, and has some pores. According to the difference of microstructures, the partially melted regions can be divided into liquid-phase sintered regions (a three-dimensional net or skeleton-like structure: Al₂O₃-rich submicron particles embedded in the TiO₂-rich matrix) and solid-phase sintered regions (remained nanoparticles). The lamellar defect of the as-sprayed coating is erased, and the compactness of the coating is improved significantly after laser remelting. The laser-remelted region composed of fine equiaxed grains, which are different from the conventional column-like crystals along the direction of the heat current. Due to the rapid solidification of laser remelting process, there are still some nanoparticles in the remelted region because of an insufficient time for grains growth.     

Adsorption of water on thin V2O3(0 0 0 1) films

V₂O₃(0 0 0 1) films have been grown epitaxially on Au(1 1 1) and W(1 1 0). Under typical UHV conditions these films are terminated by a layer of vanadyl groups as has been shown previously [A.-C. Dupuis, M. Abu Haija, B. Richter, H. Kuhlenbeck, H.-J. Freund, V₂O₃(0 0 0 1) on Au(1 1 1) and W(1 1 0): growth, termination and electronic structure, Surf. Sci. 539 (2003) 99]. Electron irradiation may remove the oxygen atoms of this layer. H₂O adsorption on the vanadyl terminated surface and on the reduced surface has been studied with thermal desorption spectroscopy (TDS), vibrational spectroscopy (IRAS) and electron spectroscopy (XPS) using light from the BESSY II electron storage ring in Berlin. It is shown that water molecules interact only weakly with the vanadyl terminated surface: water is adsorbed molecularly and desorbs below room temperature. On the reduced surface water partially dissociates and forms a layer of hydroxyl groups which may be detected on the surface up to T ∼ 600 K. Below ∼330 K also co-adsorbed molecular water is detected. The water dissociation products desorb as molecular water which means that they recombine before desorption. No sign of surface re-oxidation could be detected after desorption, indicating that the dissociation products desorb completely.     

Luminescence studies on ZnO-P2O5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Zinc phosphate glasses doped with Gd₂O₃:Eu nanoparticles and Eu₂O₃ were prepared by conventional melt-quench method and characterized for their luminescence properties. Binary ZnO-P₂O₅ glass is characterized by an intrinsic defect centre emission around 324 nm. Strong energy transfer from these defect centres to Eu³⁺ ions has been observed when Eu₂O₃ is incorporated in ZnO-P₂O₅ glasses. Lack of energy transfer from these defect centres to Eu³⁺ in Gd₂O₃:Eu nanoparticles doped ZnO-P₂O₅ glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between the luminescent centre and Eu³⁺ ions. Both doped and undoped glasses have the same glass transition temperature, suggesting that the phosphate network is not significantly affected by the Gd₂O₃:Eu nanoparticles or Eu₂O₃ incorporation.     

Epitaxial MoOx nanostructures on TiO2(1 1 0) obtained using thermal decomposition of Mo(CO)6

Stoichiometric and highly-defective TiO₂(1 1 0) surfaces (called as yellow and blue, respectively) were exposed to Mo(CO)₆ vapours in UHV and in a reactive O₂ atmosphere. In the case of yellow-TiO₂, an O₂ reactive atmosphere was necessary to obtain the Mo(CO)₆ decomposition at 450 °C with deposition of MoO_x nanostructures where, according to core level photoemission data, the Mo⁺⁴ state is predominant. In the case of blue-TiO₂ it was possible to obtain Mo deposition both in UHV and in an O₂ atmosphere. A high dose of Mo(CO)₆ in UHV on blue-TiO₂ allowed the deposition of a thick metallic Mo layer. An air treatment of this sample at 580 °C led to the elimination of Mo as MoO₃ and to the formation of a transformed layer of stoichiometry of Ti_(1−x)Mo_xO₂ (where x is close to 0.1) which, according to photoelectron diffraction data, can be described as a substitutional near-surface alloy, where Mo⁺⁴ ions are embedded into the titania lattice. This embedding procedure results in a stabilization of the Mo⁺⁴ ions, which are capable to survive to air exposure for a rather long period of time. After exposure of the blue-TiO₂(1 1 0) substrate to Mo(CO)₆ vapours at 450 °C in an O₂ atmosphere it was possible to obtain a MoO₂ epitaxial ultrathin layer, whose photoelectron diffraction data demonstrate that is pseudomorphic to the substrate.     

Effect of BiFeO3 addition on Bi2O3–ZnO–Nb2O5 based ceramics

In this paper, low temperature sintering of the Bi₂(Zn_1/3Nb_2/3)₂O₇ (β-BZN) dielectric ceramics was studied with the use of BiFeO₃ as a sintering aid. The effects of BiFeO₃ contents and the sintering temperature on the phase structure, density and dielectric properties were investigated. The results showed that the sintering temperature could be decreased and the dielectric properties could be retained by the addition of BiFeO₃. The structure of BiFeO₃ doped β-BZN was still the monoclinic pyrochlore phase. The sintering temperature of BiFeO₃ doped β-BZN ceramics was reduced from 1000 °C to 920 °C. In the case of 0.15 wt.% BiFeO₃ addition, the β-BZN ceramics sintered at 920 °C exhibited good dielectric properties, which were listed as follows: ε_r = 79 and tan δ = 0.00086 at a frequency of 1 MHz. The obtained properties make this composition to be a good candidate for the LTCC application.     

Er3+/Yb3+共掺Gd3Sc2Ga3O12晶体的上转换发光

研究了提拉法生长的Er³⁺/Yb³⁺:Gd₃Sc₂Ga₃O₁₂和Er³⁺:Gd₃Sc₂Ga₃O₁₂晶体在室温下320—1700nm范围的吸收光谱和500—750nm范围内的上转换荧光谱,同时对其上转换荧光的可能发生机制、途径以及上转换过程可能对Er^{3+相似文献}   

Characterization of single-crystalline In2O3 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

Epitaxial In₂O₃ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates by metalorganic chemical vapor deposition (MOCVD). The films were deposited at different substrate temperatures (450-750 °C). The film deposited at 650 °C has the best crystalline quality, and observation of the interface area shows a clear cube-on-cube epitaxial relationship of In₂O₃(1 0 0)||YSZ(1 0 0) with In₂O₃[0 0 1]||YSZ[0 0 1]. The Hall mobility of the single-crystalline In₂O₃ film deposited at 650 °C is as high as 66.5 cm² V⁻¹ s⁻¹ with carrier concentration of 1.5 × 10¹⁹ cm⁻³ and resistivity of 6.3 × 10⁻³ Ω cm. The absolute average transmittance of the obtained films in the visible range exceeds 95%.     

Ionic liquid-assisted hydrothermal synthesis of dendrite-like NaY(MoO4)2:Tb phosphor

Micro-sized NaY(MoO₄)₂:Tb³⁺ phosphors with dendritic morphology was synthesized by a ionic liquid-assisted hydrothermal process. X-ray diffraction (XRD) indicated that the as-prepared product is pure tetragonal phase of NaY(MoO₄)₂. Field emission scanning electron microscopy (FE-SEM) images showed that the as-prepared NaY(MoO₄)₂:Tb³⁺ phosphors have dendritic morphology. The photoluminescent (PL) spectra displayed that the as-prepared NaY(MoO₄)₂:Tb³⁺ phosphors show a stronger green emission with main emission wavelength 545 nm corresponding to the ⁵D₄→⁷F₅ transition of Tb³⁺ ion, and the optimal Tb³⁺ doping concentration for obtaining maximum emission intensity was confirmed to be 10 mol%. Based on Van Uitert's and Dexter's models the electric dipole–dipole (D–D) interaction was confirmed to be responsible for the concentration quenching of ⁵D₄ fluorescence of Tb³⁺ in the NaY(MoO₄)₂:Tb³⁺ phosphors. The intrinsic radiative transition lifetime of ⁵D₄ level is found to be 0.703 ms.     

Low temperature adsorption of oxygen on reduced V2O3(0 0 0 1) surfaces

Well ordered V₂O₃(0 0 0 1) films were prepared on Au(1 1 1) and W(1 1 0) substrates. These films are terminated by a layer of vanadyl groups under typical UHV conditions. Reduction by electron bombardment may remove the oxygen atoms of the vanadyl layer, leading to a surface terminated by vanadium atoms. The interaction of oxygen with the reduced V₂O₃(0 0 0 1) surface has been studied in the temperature range from 80 to 610 K. Thermal desorption spectroscopy (TDS), infrared reflection absorption spectroscopy (IRAS), high resolution electron energy loss spectroscopy (HREELS), X-ray photoelectron spectroscopy (XPS), and density functional theory (DFT) were used to study the adsorbed oxygen species. Low temperature adsorption of oxygen on reduced V₂O₃(0 0 0 1) occurs both dissociatively and molecularly. At 90 K a negatively charged molecular oxygen species is observed. Upon annealing the adsorbed oxygen species dissociates, re-oxidizing the reduced surface by the formation of vanadyl species. Density functional theory was employed to calculate the structure and the vibrational frequencies of the O₂ species on the surface. Using both cluster and periodic models, the surface species could be identified as η²-peroxo () lying flat on surface, bonded to the surface vanadium atoms. Although the O-O vibrational normal mode involves motions almost parallel to the surface, it can be detected by infrared spectroscopy because it is connected with a change of the dipole moment perpendicular to the surface.     

Investigation on spectral features of tungsten ions in PbO-Bi2O3-As2O3 glass matrix

Lead bismuth arsenate glasses mixed with different concentrations of WO₃ (ranging from 0 to 6.0 mol%) were synthesized. Differential thermal analysis (DTA), optical absorption, ESR and IR spectral studies have been carried out. The results of DTA have indicated that there is a gradual decrease in the resistance of the glass against devitrification with increase in the concentration of WO₃ upto 4.0 mol%.The optical absorption spectra of these glasses exhibited a relatively broad band peaking at about 880 nm identified due to d_xy→d_x²_−y² transition of W⁵⁺ ions; this band is observed to be more intense in the spectrum of glass containing 4.0 mol% of WO₃. Further, two prominent kinks attributed to ³P₀→¹S₀, ¹D₂ transitions of Bi³⁺ ions have also been located in the absorption spectra. The ESR spectra of these glasses recorded at room temperature exhibited an asymmetric signal at g_⊥∼1.71 and g_ll∼1.61. The intensity of the signal is observed to be maximal for the spectrum of the glass W₄. The quantitative analysis of optical absorption and ESR spectral studies have indicated that there is a maximum reduction of tungsten ions from W⁶⁺ state to W⁵⁺ state in the glass containing 4.0 mol% of WO₃. The IR spectral studies have indicated that there is a increasing degree of disorder in the glass network with increase in the concentration of WO₃ upto 4.0 mol%.     

External cavity tunable diode laser spectra of the ν1 + 2ν4 stretch-bend combination bands of NH3 and NH3

The ammonia ν₁ + 2ν₄ perpendicular stretch-bend combination band has been investigated in spectra of ¹⁴NH₃ and ¹⁵NH₃ recorded in the 6400-6800 cm⁻¹ region with an external cavity tunable diode laser (ECTDL) spectrometer. For ¹⁴NH₃, new assignments were determined initially by extrapolating from published low-J jet-cooled beam results up to transitions of higher J and K. Corresponding ν₁ + 2ν₄ transitions for the ¹⁵NH₃ species were then found by identifying similar patterns of lines with a characteristic downshift of approximately 9.7 cm⁻¹. Assignments were confirmed employing ground-state combination differences. Term values, a-s inversion splittings, l-doubling energies and parameter estimates from simple single-state fits are reported for the two ammonia species.     

Emission features of Ho ion in Nb2O5, Ta2O5 and La2O3 mixed Li2O-ZrO2-SiO2 glasses

Li₂O-ZrO₂-SiO₂: Ho³⁺ glasses mixed with three interesting d-block elemental oxides, viz., Nb₂O₅, Ta₂O₅ and La₂O₃, were prepared. Optical absorption and photoluminescence spectra of these glasses have been recorded at room temperature. The luminescence spectra of Nb₂O₅ and Ta₂O₅ mixed Li₂O-ZrO₂-SiO₂ glasses (free of Ho³⁺ ions) have also exhibited broad emission band in the blue region. This band is attributed to radiative recombination of self-trapped excitons (STEs) localized on substitutionally positioned octahedral Ta⁵⁺ and Nb⁵⁺ ions in the glass network. The Judd-Ofelt theory was successfully applied to characterize Ho³⁺ spectra of all the three glasses. From this theory various radiative properties, like transition probability A, branching ratio β_r and the radiative lifetime τ_r, for ⁵S₂ emission levels in the spectra of these glasses have been evaluated. The radiative lifetime for ⁵S₂ level of Ho³⁺ ions has also been measured and quantum efficiencies were estimated. Among the three glasses studied the La₂O₃ mixed glass exhibited the highest quantum efficiency. The reasons for such higher value have been discussed based on the relationship between the structural modifications taking place around the Ho³⁺ ions.     

Gd2O3:Eu3+纳米晶的燃烧合成及光致发光性质

采用柠檬酸作燃烧剂用燃烧合成法制备了Gd₂O₃:Eu³⁺纳米晶.用X射线衍射仪(XRD)、高分辨透射电子显微镜(HRTEM)和荧光分光光度计等对Gd₂O₃:Eu³⁺纳米晶的结构、形貌和发光性能进行了分析.结果表明：不同柠檬酸与稀土离子配比(C/M)制备的样品经800℃ 退火1 h后，均得到了纯立方相的Gd₂O₃:Eu³⁺纳米晶，晶粒尺寸约为30 nm，尺寸分布较窄，其中以C/M=1.0时制备的纳米晶结晶性最好，发光强度最大.Gd₂O₃:Eu³⁺纳米晶主发射峰位置均在612 nm处 (⁵D₀→⁷F₂跃迁)，激发光谱中电荷迁移态发生红移，观察到Gd³⁺向Eu³⁺的有效能量传递.对柠檬酸与稀土离子配比(C/M)对结晶度、发光性质等的影响也进行了分析和讨论.     

Subsolidus phase relation in the Bi_2O_3–Fe_2O_3–La_2O_3 system

Bismuth-containing semiconductor material is a hot topic in photocatalysts because of its effective absorption under the visible light.In this paper,we expect to explore a new bismuth-based photocatalyst by studying the subsolidus phase relations of the Bi2O3–Fe2O3–La2O3system.The X-ray diffraction data shows that in this ternary system the ternary compound does not exist,while seven binary compounds(including one solid solution series Bi1 xLaxO1.5with 0.167≤x≤0.339)are obtained and eight compatibility triangles are determined.     

Growth and properties of air-processed GdBa2Cu3O7−δ superconductors with fined Gd2BaCuO5 and Gd2Ba4CuFeOy additions

We have succeeded in synthesizing a powder form of Gd₂Ba₄CuFeO_y (Gd2411) in air. GdBa₂Cu₃O_7−δ (Gd123)/Gd₂BaCuO₅ (Gd211) precursor powders added with different amounts of Gd₂Ba₄CuFeO_y (x = 0, 0.002, 0.004, 0.02) in molar ratio to Gd123 have been fabricated successfully into the form of large, single grains by the top seeded melt growth (TSMG) process. The relation between the additions amounts of Gd2411/Gd211 and critical current density (J_C) was analyzed. We found Gd2411 particles stably exist in the Gd123 matrix without degradation of superconducting properties owing to the existence of the Fe magnetic ion. The trapped field was observed to increase significantly compared with the bulk without Gd2411 additions.     

Optical properties of (ZnO)0.5(P2O5)0.5 glasses doped with Gd2O3:Eu nanoparticles and Eu2O3

Binary (ZnO)_0.5(P₂O₅)_0.5 glasses doped with Eu₂O₃ and nanoparticles of Gd₂O₃:Eu were prepared by conventional melt-quench method and their luminescence properties were compared. Undoped (ZnO)_0.5(P₂O₅)_0.5 glass is characterized by a luminescent defect centre (similar to L-centre present in Na₂O-SiO₂ glasses) with emission around 324 nm and having an excited state lifetime of 18 ns. Such defect centres can transfer the energy to Eu³⁺ ions leading to improved Eu³⁺ luminescence from such glasses. Based on the decay curves corresponding to the ⁵D₀ level of Eu³⁺ ions in both Gd₂O₃:Eu nanoparticles incorporated as well as Eu₂O₃ incorporated glasses, a significant clustering of Eu³⁺ ions taking place with the latter sample is confirmed. From the lifetime studies of the excited state of L-centre emission from (ZnO)_0.5(P₂O₅)_0.5 glass doped with Gd₂O₃:Eu nanoparticles, it is established that there exists weak energy transfer from L-centres to Eu³⁺ ions. Poor energy transfer from the defect centres to Eu³⁺ ions in Gd₂O₃:Eu nanoparticles doped (ZnO)_0.5(P₂O₅)_0.5 glass has been attributed to effective shielding of Eu³⁺ ions from the luminescence centre by Gd-O-P type of linkages, leading to an increased distance between luminescent centre and Eu³⁺ ions.