Potassium-conducting solid electrolytes in the K3 − 2x Cd x PO4 system

New potassium-conducting solid electrolytes of the K_{3 ? 2x} Cd _x PO₄ system are synthesized and studied. A wide range of solid solutions reaching x ≈ 0.35 with the structure of high-temperature modification of potassium orthophosphate forms in the system. An addition of cadmium ions leads to an abrupt increase in the K₃PO₄ conductivity due to the formation of potassium vacancies. The highest conductivity is approximately 10^?2 S cm^?1 at 300°C and above 10^?1 S cm^?1 at 700°C.     

Synthesis and photoluminescent properties of Y1 − x La x PO4:Eu3+ nanophosphor

In this paper, Y_{1 ? x} La _x PO₄:Eu³⁺ (x = 0.5, 0.7, and 0.3) nanophosphors were synthesized by a rather simple method. The products present different morphologies. For Y_{1 ? x} La _x PO₄:Eu³⁺, they have similar phase composition of a mixture of monoclinic LaPO₄ and tetragonal YPO₄. Furthermore, the luminescence behavior of Eu³⁺ has been investigated in this type of matrices. In Y_{1 ? x} La _x PO₄:Eu³⁺, the ⁵D₀-⁷F₁ magnetic dipole transition is dominant, indicating that the Eu³⁺ site is inversion symmetry. The difference in the Eu-O charge transfer (CT) band with La³⁺ ion concentration suggests the difference in the ionicity of the Eu-O bond. Among those products, the red to orange intensity ratio (R/O) of ⁵D₀-⁷F₂ to ⁵D₀-⁷F₁ value of Eu³⁺ is different, furthermore, for La³⁺ x = 0.3, the R/O value of Eu³⁺ is the biggest on the contrary, indicating that the inversion symmetry Eu³⁺ is lowest.     

Synthesis of Calcium Phosphates by PO(OH)x(OBut)3−x and CaO2C2H4

In this work, an alkoxide solution route to synthesize Ca phosphates was developed. For the precursors, a CaO₂C₂H₄ solution was prepared by dissolving Ca metal powder into ethylene glycol, and a PO(OH)_x(OBut)_3–x solution was prepared by dissolving P₂O₅ inton -butanol under reflux conditions. In order to obtain a mixed solution of the two precursors, acetic acid was used as an additive. The experimental results show that (1) -2CaO · P₂O₅, -3CaO · P₂O₅, and hydroxyapatite can be easily synthesized by converting the corresponding mixed solutions to powder products in a hot plate, and calcining the as prepared products at 1100°C; (2) acetic acid behaves as a good agent for controlling the reactions between the two precursors by modifying the CaO₂C₂H₄ species in solution and decreasing the reactivity of the PO(OH)_x(OBut)_3–x species.     

Synthesis and characterization of a NASICON phase of variable composition Na1 − x Ni1 − x Sc1 + x (MoO4)3 (0 ≤ x ≤ 0.5)

Subsolidus phase ratios in the Na₂MoO₄-NiMoO₄-Sc₂(MoO₄)₃ system have been studied using X-ray diffraction, differential thermal analysis, and vibrational spectroscopy. A phase of variable composition Na_{1 ? x} Ni_{1 ? x} Sc_{1 + x} (MoO₄)₃ (0 ≤ x ≤ 0.5) having NASICON structure (space group \(R\bar 3c\) ) and a triple molybdate crystallizing in triclinic system (space group \(P\bar 1\) ) have been obtained. The high conductivity of Na_{1 ? x} Ni_{1 ? x} Sc_{1 + x} (MoO₄)₃ allows the phase of variable composition to be regarded as a promising sodiumion-conductive solid electrolyte.     

Sol-gel synthesis and structure of MZr2(AsO4)3 arsenates and MZr2(AsO4) x (PO4)3 − x arsenate phosphates (M = K,Rb, Cs)

MZr₂(AsO₄)₃ arsenates and MZr₂(AsO₄) _x (PO₄)_{3 ? x} arsenate phosphates (M = K, Rb, Cs) have been obtained by sol-gel synthesis followed by heat treatment and have been characterized by X-ray diffraction, electron probe microanalysis, and IR spectroscopy. Continuous series of substitutional solid solutions form in the MZr₂(AsO₄) _x (PO₄)_{3 ? x} systems (0 ≤ x ≤ 3). The solid solutions have a kosnarite structure (KZr₂(PO₄)₃, space group \(R\bar 3c\) ). The crystal structures of MZr₂(AsO₄)₃ and MZr₂(AsO₄)_1.5(PO₄)_1.5 have been refined by full-profile analysis. The structural frameworks of these phases are built from ZrO₆ octahedra and AsO₄ tetrahedra or (As,P)O₄ tetrahedra statistically populated by arsenic and phosphorus atoms. The alkali metal atoms occupy extraframework sites. The effect of the crystal chemical properties of alkali metals on the formation of the structures of MZr₂(AsO₄)₃ arsenates (M = Li-Cs) and MZr₂(AsO₄) _x (PO₄)_{3 ? x} solid solutions is discussed.     

Synthesis and Ionic Conductivity of LiZr2(VO4)x(PO4)3 – x

Russian Journal of Electrochemistry - Vanadate phosphates LiZr2(VO4)x(PO4)3 – x are synthesized by the sol-gel technique with subsequent annealing and studied using X-ray diffraction...     

Vibrational spectra and electrophysical properties of a NASICON phase of variable composition Na1 − x Co1 − x Sc1 + x (MoO4)3 (0 ≤ x ≤ 0.5)

Subsolidus phase ratios of the Na₂MoO₄-CoMoO₄-Sc₂(MoO₄)₃ system have been studied by X-ray diffraction, differential thermal analysis, and vibrational spectroscopy. A phase of variable composition Na_{1 ? x} Co_{1 ? x} Sc_{1 + x} (MoO₄)₃, 0 ≤ x ≤ 0.5 having NASICON structure (space group \(R\bar 3c\) ) and triple molybdate NaCo₃Sc(MoO₄)₅ crystallizing in triclinic system (space group \(P\bar 1\) ) have been obtained. The high conductivity of Na_{1 ? x} Co_{1 ? x} Sc_{1 + x} (MoO₄)₃ allows the phase of variable composition to be regarded as a promising sodium-ion conducting solid electrolyte.     

Synthesis and phase formation in M 0.5(1+x) 2+ FexTi2−x (PO4)3 phosphate series

New complex phosphates of titanium, iron, and alkaline-earth metals have been synthesized. X-ray powder diffraction, differential thermal analysis (DTA), and IR spectroscopy are used to study phase formation in the series of M_0.5(1+x)Fe_xTi_2?x (PO₄)₃ (M = Mg, Ca, Sr, Ba) phosphates. Individual compounds and solid solutions are found to crystallize in the NaZr₂(PO₄)₃ and K₂Mg₂(SO₄)₃ structure types. Their crystal parameters are calculated. CaFeTi(PO₄)₃ is studied using Mössbauer spectroscopy. Its structure is refined by the Rietveld method: space group $R\bar 3$ c, Z = 6, a = 8.5172(1), Å, c = 21.7739(4) Å, V = 1367.91(4) ų.     

Electroconductance of single-crystal Li2 + x Fe 2 − 2x 2+ Fe x 3+ (MoO4)3 (x = 0.22)

Electrophysical properties of single-crystal Li_{2 + x} Fe _{2 ? 2x} ²⁺ Fe _x ³⁺ (MoO₄)₃ (x = 0.22) are studied at 25–400°C. It is found that the conduction is of electronic nature and the conductivity equals 5 × 10^-2 S/cm at 300°C. The activation energy for the electron transport is 0.23 eV. The conductance in molybdate Li_2.22Fe _1.56 ²⁺ Fe _0.22 ³⁺ (MoO₄)₃ is markedly anisotropic.     

Solid potassium-conducting electrolytes in the K2 − 2x Ga2 − x V x O4 system

New potassium-conducting solid electrolytes based on potassium monogallate in the K_2?2x Ga_2?x V _x O₄ system are synthesized and studied. It is found that an introduction of V⁵⁺ ions leads to a considerable increase in the KGaO₂ conductivity due to the formation of vacancies in the potassium sublattice. The conductivity for optimal compositions is approximately 10^?3 S cm^?1 at 400°C and above 10^?2 S cm^?1 at 700°C. The results are compared with early obtained data for potassium monogallate dopped with four-charged cations.     

Ferrimagnetic spinels in hydrothermal and thermal treatment of MnxFe2−2x(OH)6−4x

Products of hydrothermal treatment of the initial amorphous system Mn_xFe_2–2x(OH)_6–4x for 0x1 in 0.1x intervals, and products of their further thermal treatment, were examined by chemical analysis, X-ray, IR, and DTA techniques supported by magnetic measurements. After hydrothermal growth for lowx, hematite and goethite phases occurred. Although the goethite phase was still identifiable atx=0.6, formation of a solid solution with the isostructural groutite was not found. The ferrimagnetic spinel phase, which resists heating up to 400C, was present at 0.5x0.9. At higher temperatures, it transformed into the rhombohedral hematite type phase or into the cubic bixbyite phase. AtT900C, a ferrimagnetic spinel structure reappeared up tox=0.8. For x=0.9, the low- and high-temperature forms of the hausmannite phase occurred, forx= 1 passing from one form into another through Mn₅O₈ and partritgeite.For a primary mixture Mn_0.5Fe(OH)₄, corresponding to the manganese ferrite structure, the lattice parameter of which passes from 8.43 å through 8.33 å to 8.50 å, the probable crystallochemical formula was suggested.We are grateful to KBN (The State Committee for Scientific Research, Poland) for grant No. 3 T09A 064 08, which contributed substantially to the materialization of this project.     

Osmotic and activity coefficients of {yNaH2PO4+(1−y)Na2SO4}(aq) at the temperature 298.15 K

The osmotic coefficients of the mixed electrolyte solution {yNaH₂PO₄+(1−y)Na₂SO₄}(aq) have been measured by the isopiestic method, at the temperature T=298.15 K. The activity coefficients of NaH₂PO₄ and Na₂SO₄ were calculated by Scatchard's neutral-electrolyte method and by Pitzer and Kim's treatment for mixed-electrolyte solutions. The Scatchard interaction parameters are used for calculation of the excess Gibbs energy as a function of ionic strength and ionic-strength fraction of NaH₂PO₄. Also, the Zdanovskii's rule of linearity is tested.     

Hopping conductivity of distorted K2NiF4-type (Ca1+xNd1−x)CrO4

Orthorhombic distorted K₂NiF₄-type (Ca_1+xNd_1?x)CrO₄ (0.00 ≤ x ≤ 0.15) was synthesized using a standard ceramic technique. The cell parameters (a and c) decreased, whereas the cell parameter (b) increased with the increase in x. The variation in the global instability index (GII) indicated that the crystal stability of (Ca_1+xNd_1?x)CrO₄ was not influenced by the Cr⁴⁺ ion content. At all temperatures, the electrical conductivity (σ) of (Ca_1+xNd_1?x)CrO₄ increased with the increase in x. (Ca_1+xNd_1?x)CrO₄ was a p-type semiconductor and exhibited hopping conductivity in a small-polaron model in the temperature range of 290 K ≤ T ≤ 713 K. The Cr⁴⁺ ion acts as an acceptor, and the electron transfer through the Cr³⁺–O–Cr⁴⁺ path becomes active as a result of the Cr⁴⁺ ion content and the Cr–O(1) distance.     

Phosphates M 0.5(1 + x) 2+ Cr x Ti2 − x (PO4)3: Synthesis, structure, and catalytic properties

Complex phosphates of titanium, chromium, and metals(2+) of the general formula M_{0.5(1 + x} )Cr _x Ti_{2 ? x} (PO₄)₃ (M = Mg, Ca, Mn, Ni, Sr, Ba, and Pb) were synthesized. Their phase formation was studied by means of X-ray powder diffraction, electron probe microanalysis, differential thermal analysis, and IR spectroscopy. Individual phases and solid solutions crystallizing in kosnarite and langbeinite structure types were identified; their crystallographic parameters were calculated. The catalytic properties of phosphates Ca_{0.5(1 + x} )Cr _x Ti_{2 ? x} (PO₄)₃ in methanol conversion were studied.     

Photocatalytic hydrogen generation of Pt-Sr(Zr1 − x Y x )O3 − δ -TiO2 heterojunction under the irradiation of simulated sunlight

The Pt-Sr(Zr_{1 − x} Y _x )O_{3 − δ} -TiO₂(Pt-SZYT) heterojunction photocatalysts were prepared by a photodeposition method. The composite particles were characterized by XRD, SEM, UV-Vis DRS, and PL techniques. Photocatalytic hydrogen generation in H₂C₂O₄ aqueous solution under the irradiation of simulated sunlight was used as a probe reaction to evaluate the photocatalytic activity of the photocatalysts. The effects of the content of Pt loading and the concentration of oxalic acid on the photocatalytic activity of the catalyst were discussed. The continuous photocatalytic activity of the Pt-SZYT and the relationship between PL intensity and hydrogen generation were also discussed. The results show that Pt-SZYT catalysts had high photocatalytic activity of hydrogen generation. The content of Pt loading and the concentration of oxalic acid have important influence on the photocatalytic hydrogen generation. The optimal loading content of platinum was 0.90 mass%. Under this condition, the average rate of photocatalytic hydrogen generation was 1.68 mmol·h⁻¹ when the concentration of oxalic acid was 50 mmol·L⁻¹. The higher the photocatalytic activity, the weaker the PL intensity, which was demonstrated by the analysis of PL spectra. __________ Translated from Acta Chimica Sinica, 2008, 61 (in Chinese)     

Glycolate Ti1 − x Fe x (OCH2CH2O)2 − x/2 as a precursor for the preparation of quasi-one-dimensional (1D) solid solutions Ti1 − x Fe x O2 − 2x/2 (0 ≤ x ≤ 0.1)

Quasi-one-dimensional (1D) solid solutions Ti_{1 ? x} Fe _x (OCH₂CH₂O)_{2 ? x/2} (0 < x ≤ 0.1) with the structure of anatase were prepared by heating the glycolate Ti_{1 ? x} Fe _x (OCH₂CH₂O)_{2 ? x/2} in an atmosphere of air at a temperature of >450°C. The conditions of formation and the properties of the new glycolate Ti₃Fe₂(OCH₂CH₂O)₉ were described. It was found that the synthesized Ti_{1 ? x} Fe _x O_{2 ? 2x/2} solid solutions exhibit photocatalytic activity in the reaction of hydroquinone oxidation in an aqueous solution on irradiation with UV light. A correlation between the rate of oxidation of hydroquinone and the concentration of iron in the catalyst was established. A procedure for the preparation of titanium dioxide with the structure of anatase doped with iron and carbon (Ti_{1 ? x} Fe _x O_{(2 ? x/2) ? yCy)} and also composites on its basis, which contain an excess amount of carbon, was proposed.     

Crystal structure and properties of the Na1−x Ru2O4 phase

Sodium ruthenium(III,IV) oxide Na_1−x Ru₂O₄ was synthesized by the solid state reaction of Na₂CO₃ and RuO₂ in inert atmosphere and characterized by X-ray powder diffraction, electron diffraction, and high-resolution transmission electron microscopy. The compound crystallizes in the CaFe₂O₄-type structure (space group Pnma, Z = 4, a = 9.2641(7) Å, b = 2.8249(3) Å, c = 11.1496(7) Å). Double rutile-like chains of the RuO₆ octahedra form a three-dimensional framework, whose tunnels contain sodium cations. The structure contains two crystallographically independent sites of ruthenium atoms randomly occupied by the Ru^III and Ru^IV cations. The superstructure with the doubled b parameter found for one of the samples under study using electron diffraction is caused, probably, by ordering of the Ru cations in the rutile-like chains. The Na_{1− x} Ru₂O₄ compound exhibits temperature-independent paramagnetism with χ₀ = 1.9·10⁻⁴ cm³ (mole of Ru⁻¹). Published in Russian in Izvestiya Akademii Nauk. Seriya Khimicheskaya, No. 10, pp. 1655–1660, October, 2006.     

Electrophysical properties of solid solutions of Zn2 − x (Zr a Sn b )1 − x Fe2x O4 compositions

The electrophysical properties of the multicomponent Zn₂ZrO₄ ? Zn₂SnO₄ ? ZnFe₂O₄ system are studied. The electrophysical parameters of solid solutions of Zn_{2 ? x} (Zr _a Sn _b )_{1 ? x} Fe_2x O₄ (x = 0–1.0, Δx = 0.1, a + b = 1) are determined. It is found that the formed solid solutions are semiconductors with electrophysical properties that change in a regular fashion with composition and are distinguished by high values of resistivity (107–1012 Ω cm).     

Synthesis and physical and chemical characterization of Ca10−xAgx(PO4)6(OH)2−xx apatites

The synthesis of calcium-silver hydroxyapatites of composition Ca_10−xAg_x(PO₄)₆(OH)_2−xx is discussed, together with their physical and chemical properties. Samples prepared both by dry process and by double decomposition were characterized using a variety of analytical techniques (chemical analysis, X-ray diffraction, infrared spectroscopy). The lattice parameters a and c increase linearly with the amount of silver added. The increase is attributed to the preferential substitution of the silver ion in site me (I) of these apatites.