Physicochemical properties and mixed electronic and ionic conduction of composite ceramics in the system ZrO<Subscript>2</Subscript>-Bi<Subscript>2</Subscript>CuO<Subscript>4</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>

Composites ZrO₂-(Bi₂CuO₄+ 20 wt % Bi₂O₃) (50–80 vol % ZrO₂) are synthesized and their physicochemical properties are studied. It is demonstrated that the composites comprise triple-phase mixtures of ZrO₂ of a monoclinic modification, Bi₂CuO₄, and solid solution Bi_2?x Zr _x O_{3 + x/2} and retain their mechanical strength up to 800°C. Impedance spectroscopy is used to examine their electroconductivity at 700–800°C in the interval of partial oxygen pressures extending from 37 to 2.1 × 10⁴ Pa. Contributions made by electronic and ionic constituents to their overall conductivity are evaluated. The best specimens’ conductivity is ～0.01 S cm^?1, with the electronic and ionic transport numbers nearly equal. The composite consisting of 50 vol % ZrO₂ and 50 vol % (Bi₂CuO₄ + 20 wt % Bi₂CuO₄) is tested in the role of an oxygen-separating membrane. The selective flux of oxygen in the temperature interval 750–800°C amounts to (2.2–6.3) × 10^?8 mol cm^?2 s^?1, testifying that these materials may be used as gas-separating membranes.     

Conductivity of Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-NiO composites

The conductivity and transport number of oxygen ions of Bi₂O₃-(10, 30, 50) vol % NiO composites are measured using the four-probe and coulomb-volumetric methods at various temperatures. It is shown that the Bi₂O₃-50 vol % NiO composite exhibits a high mixed ionic-electronic conductivity in the temperature range from 730 to 800°C.     

Lab Scale Study on Humidity Sensing and D.C. Conductivity of Polypyrrole/Strontium Arsenate (Sr<Subscript>3</Subscript>(AsO<Subscript>4</Subscript>)<Subscript>2</Subscript>) Ceramic Composites

In-situ polymerization of pyrrole was carried out with strontium arsenate (ceramics) in the existence of oxidizing agent ammonium persulphate to synthesize polypyrrole/strontium arsenate composites by chemical oxidation method. The polypyrrole/strontium arsenate composites were synthesized with various compositions viz., 10 to 50 wt % of strontium arsenate was placed in polypyrrole. The surface morphologies of these composites were analyzed using Scanning Electron Microscopy (SEM) which confirmed the embedment of strontium arsenate particles in PPy chain. The Fourier Transform Infra-Red spectra (FTIR) revealed the shift of lengthens frequencies towards elevated frequency area. The powder X-ray diffraction patterns (XRD) disclosed the crystalline behavior exhibition of the composites. Thermographs of thermal analysis (TG/DTA) exposed the stronger stability of polypyrrole/strontium arsenate composites than PPy. D.C. conductivity reveals that, the strontium arsenate concentration in polypyrrole is accountable for the variant of conductivity of the composites. The results of the study signify the increment of D.C. conductivity for 40 wt % of strontium arsenate in polypyrrole. The temperature reliant conductivity dimension shows the thermally activated exponential behavior of PPy/Sr₃(AsO₄)₂ composites. The reduction in electrical resistance was experienced, when the polymer composites were bare to the wide range of relative humidity (Rh) (from 30 to 95%). This reduce is due to enhance in surface electrical conductivity ensuing from humidity fascination and also due to capillary abridgment of water causing change in conductivity within the sensing materials. The composite shows sensitivity in the range 30 to 95% Rh, we also studied response and recovery time.     

The structural-phase state of C<Subscript>60</Subscript>-C<Subscript>70</Subscript> fullerene mixtures

The structural and phase state of the C₆₀-C₇₀ system at various C₆₀/C₇₀ ratios in mixtures obtained by the vaporization of solutions in toluene at ∼98°C was studied by X-ray structure analysis, differential scanning calorimetry, and infrared spectroscopy. Solid solutions based on the face-centered cubic packing of C₆₀ are not formed in the C₆₀-C₇₀ system at C₇₀ contents from 0.5 to 50 wt %. The hexagonal close packing of a solid solution of C₆₀ in C₇₀ can be formed as a result of the thermally activated decomposition of the ternary crystal solvate in the C₆₀-C₇₀-C₆H₅CH₃ system. The structural state of multiphase mixtures formed under conditions far from equilibrium is characterized by a high degree of structure imperfection and greater ability to undergo oxidation compared with C₆₀ and C₇₀.     

Lithium AlPO<Subscript>4</Subscript> composite polymer battery with nanostructured LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> cathode

The borate ester plasticized AlPO₄ composite solid polymer electrolytes (SPE) have been synthesized and studied as candidates for lithium polymer battery (LPB) application. The electrochemical and thermal properties of SPE were shown to be suitable for practical LPB. Nanostructured LiMn₂O₄ with spherical particles was synthesized via ultrasonic spray pyrolysis technique and has shown a superior performance to the one prepared via conventional methods as cathode for LPB. Furthermore, the AlPO₄ addition to the polymer electrolyte has improved the polymer battery performance. Based on the AC impedance spectroscopy data, the performance improvement was suggested as being due to the cathode/polymer electrolyte interface stabilization in the presence of AlPO₄. The Li/composite polymer electrolyte/nanostructured LiMn₂O₄ electrochemical cell showed stable cyclability during the various current density tests, and its performance was found to be quite acceptable for practical utilities at ambient temperature and showed remarkable improvements at 60 °C compared with the solid state reaction counterpart.     

Electrochemical behavior of composite cathodes in contact with solid electrolyte La<Subscript>10</Subscript>Ge<Subscript>6</Subscript>O<Subscript>27</Subscript>

The cathodic overvoltage of composite cathodes 50 wt % La_0.8Sr_0.2MnO₃ (LSM) + 50 wt % La₁₀Ge₆O₂₇ (LGO) (further on, LSM-LGO), LSM-SSZ (Zr_0.835Sc_0.165O_2?δ), Ag-Pd-LGO, and Ag-Pd-SSZ in contact with the LGO electrolyte is measured. The temperature dependences of the polarization conductivity and the working-current densities of the same composite cathodes are investigated. The study is performed at 700–900°C. A comparison with the SSZ electrolyte is conducted. The chemical interaction in the LSM-LGO composition is studied. It is demonstrated that the interaction of lanthanum-strontium manganite with lanthanum germanate occurs with the dissolution of the initial phases in one another and with the formation of fresh phases at elevated temperatures. Coefficients of linear thermal expansion of the LGO and SSZ electrolytes and the LSM, LSM-LGO, and LSM-SSZ electrode materials are compared at 40–900°C. Most of the studied electrodes in contact with the LGO electrolyte demonstrate thermomechanical stability and high electrochemical activity.     

Solid vitreous inorganic electrolytes in Li<Subscript>2</Subscript>O-LiF-P<Subscript>2</Subscript>O<Subscript>5</Subscript> system for rechargeable lithium power sources: Ionic conductivity and activation energy

The effect of chemical composition to ionic conductivity and activation energy of vitreous solid electrolytes (SE) based on Li₂O-P₂O₅-LiF system (Li₂O ≥ 45.4 mol %) was detected. The temperature effect to conductivity and activation energy was studied. An original technology was designed to prepare vitreous SEs in Li₂O-P₂O₅-LiF system containing up to 20 mol % LiF and characterized with ionic conductivity up to 4.4 × 10^?7 S cm^?1 (24°C) and activation energy about 0.567 eV. The synthesized materials are characterized with high X-ray amorphism and technological performance.     

Nafion-based composite solid electrolytes containing water-soluble fullerene C<Subscript>60</Subscript> derivatives

Nafion-based composite solid polyelectrolytes containing fullerene C₆₀ and its water-soluble derivatives fullerenol-C₆₀ and tris-malonate-C60 were studied by the impedance spectroscopy method. It was found that introduction of these dopants in Nafion leads to a substantial increase in proton conductivity of the composites in the region of low relative humidity. The reasons for the influence of dopants on proton conductivity of composites were discussed.     

Synthesis and structure of allylated derivatives of fullerenes C<Subscript>60</Subscript> and C<Subscript>70</Subscript>

New chromatographically pure monoand hexamethanofullerenes C₆₀ and C₇₀ containing active allylic groups were synthesized by Bingel—Hirsch reaction. These compounds are promising for the studies of biological activity, as well as for obtaining on their basis new fullerenecontaining materials. The purity and composition of the synthesized compounds were confirmed by MALDI-TOF mass spectrometry and HPLC, their structure was established by ¹H and ¹³C NMR spectroscopy and X-ray diffraction.     

Synthesis of BaSnO<Subscript>3</Subscript>/SnO<Subscript>2</Subscript> Nanocomposites as Heterogeneous Additive for Composite Solid Electrolytes

Method of differential thermal analysis was used to study the thermolysis of a mixture of barium oxalate hydrate and α-SnO₂·H₂O, produced by precipitation from hydrochloric solutions. The methods of X-ray diffraction analysis, electron microscopy, and low-temperature nitrogen adsorption were used to examine the reaction products formed at various heating temperatures and determine their phase composition. The nanocomposite BaSnO₃/SnO₂ is the final product of thermolysis and subsequent heating to 950°C. The nanocomposite was used as a heterogeneous oxide additive for obtaining a CsNO₂–BaSnO₃/SnO₂ composite solid electrolyte. The conductivity of the composite exceeds that of the starting salt by more than order of magnitude.     

Synthesis and electrochemical performance of the Li-rich cathode material Li<Subscript>1.17</Subscript>Ni<Subscript>0.12</Subscript>Co<Subscript>0.13</Subscript>Mn<Subscript>0.58</Subscript>O<Subscript>2</Subscript> for lithium-ion batteries

Lithium-riched cathode material for lithium-ion batteries, Li_1.17Ni_0.12Co_0.13Mn_0.58O₂, was synthesized via crystallization from a solution of metal acetates, followed by a thermal treatment of the material obtained as a powder. The phase, elemental, and granulometric compositions of the material were examined, as well as the morphology of the powder particles obtained. The discharge capacity of the material in relation to the charging voltage was found from the results of electrochemical tests, and endurance tests were performed. The discharge capacity upon 85 charge/discharge cycles at voltages in the range 2.8–4.8 and a current of 0.1C was about 180 mA h g^–1.     

Electrodeposition of PbO<Subscript>2</Subscript>-ZrO<Subscript>2</Subscript> composite materials

The regularities of electrodeposition of composite materials based on PbO₂ containing zirconium dioxide particles are studied. The contents of various phases in the composite depend on the electrolyte composition and conditions of deposition. When a dispersed phase is incorporated into the composite coating, the dimensions of lead dioxide crystals decrease to submicrons.     

Electrospun Li<Subscript>4</Subscript>Ti<Subscript>5</Subscript>O<Subscript>12</Subscript>/Li<Subscript>2</Subscript>TiO<Subscript>3</Subscript> composite nanofibers for enhanced high-rate lithium ion batteries

Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers with the mean diameter of ca. 60 nm have been synthesized via facile electrospinning. When the molar ratio of Li to Ti is 4.8:5, the Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers exhibit initial discharge capacity of 216.07 mAh g^?1 at 0.1 C, rate capability of 151 mAh g^?1 after being cycled at 20 C, and cycling stability of 122.93 mAh g^?1 after 1000 cycles at 20 C. Compared with pure Li₄Ti₅O₁₂ nanofibers and Li₂TiO₃ nanofibers, Li₄Ti₅O₁₂/Li₂TiO₃ composite nanofibers show better performance when used as anode materials for lithium ion batteries. The enhanced electrochemical performances are explained by the incorporation of appropriate Li₂TiO₃ which could strengthen the structure stability of the hosted materials and has fast Li⁺-conductor characteristics, and the nanostructure of nanofibers which could offer high specific area between the active materials and electrolyte and shorten diffusion paths for ionic transport and electronic conduction. Our new findings provide an effective synthetic way to produce high-performance Li₄Ti₅O₁₂ anodes for lithium rechargeable batteries.     

Facile synthesis of Fe@Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> core-shell nanowires as O<Subscript>2</Subscript> electrode for high-energy Li-O<Subscript>2</Subscript> batteries

Fe@Fe₂O₃ core-shell nanowires were synthesized via the reduction of Fe³⁺ ions by sodium borohydride in an aqueous solution with a subsequent heat treatment to form Fe₂O₃ shell and employed as a cathode catalyst for non aqueous Li-air batteries. The synthesized core-shell nanowires with an average diameter of 50–100 nm manifest superior catalytic activity for oxygen evolution reaction (OER) in Li-O₂ batteries with the charge voltage plateau reduced to ～3.8 V. An outstanding performance of cycling stability was also achieved with a cutoff specific capacity of 1000 milliampere hour per gram over 40 cycles at a current density of 100 mA g^?1. The excellent electrochemical properties of Fe@Fe₂O₃ as an O₂ electrode are ascribed to the high surface area of the nanowires’ structure and high electron conductivity. This study indicates that the resulting iron-containing nanostructures are promising catalyst in Li-O₂ batteries.     

Conductivity and thermal expansion of the Ce<Subscript>0.8</Subscript>Gd<Subscript>0.2</Subscript>O<Subscript>1.9</Subscript> solid electrolyte in the oxidizing and reducing atmospheres

Highly compact (99%) solid electrolyte Ce_0.8Gd_0.2O_1.9 with submicron (0.3 μm) grains is synthesized. The dilatometric (20–850°C) and conductivity (180–350°C) measurements are performed on the electrolyte in air and as a function of the partial oxygen pressure \(p_{O_2 } \) (0.21?1×10^?25 atm) at 600, 700, and 800°C. An inflection is found in the temperature dependences of the thermal coefficient of linear expansion and conductivity (impedance measurements) at ～230°C, which is the evidence for a phase transition. The activation energies for conduction in the grain bulk and boundaries differ only slightly, indicating that the grain boundaries’ resistance is caused not by the precipitation of the second phase at the boundaries, but most probably by the presence of intergranular nanopores. The dilatometric measurements confirm a significant increase in the linear dimensions of Ce_0.8Gd_0.2O_1.9 in the reducing atmospheres with a parallel increase in its electron conductivity. The electron conductivity and specific elongation increase proportionally to \(p_{O_2 }^{ - 1/4} \) at all temperatures. The \(p_{O_2 } \) values, at which the transport numbers of ions t _i = 0.5, are determined. They are 10^?22.5, 10^?20, and 10^?18 atm at 600, 700, and 800°C, respectively.     

Electrophysical properties of layered perovskites LnBaCo<Subscript>2 − <Emphasis Type="Italic">x</Emphasis></Subscript>Cu<Subscript><Emphasis Type="Italic">x</Emphasis></Subscript>O<Subscript>5 + δ</Subscript> (Ln = Sm,Nd) for solid oxide fuel cells

The influence of doping with copper oxide on the phase composition, electric conductivity, and linear thermal expansion coefficient (LTEC) of SmBaCo₂O_{5 + δ} and NdBaCo₂O_{5 + δ} was studied. The sample homogeneity region has been determined with using XRD. The samples conductivity decreased as the dopant concentration increased. The character of the temperature dependence of conductivity changed at high copper contents. In a reductive atmosphere, the conductivity of the samples at first decreased and then remained constant. The linear thermal expansion coefficient decreased as the amount of the incorporated dopant increased.     

Preparation and electrochemical properties of Li<Subscript>0.97</Subscript>Er<Subscript>0.01</Subscript>FePO<Subscript>4</Subscript>/C composite for lithium-ion batteries

Li_0.97Er_0.01FePO₄/C composite was prepared by solid-state reaction, using particle modification with amorphous carbon from the decomposition of glucose and lattice doping with supervalent cation Er³⁺. All samples were characterized by X-ray diffraction, scanning electron microscopy, multi-point Brunauer Emmett and Teller methodes. The electrochemical tests show Li_0.97Er_0.01FePO₄/C composite obtains the highest discharge specific capacity of 154 mAh g⁻¹ at C/10 rate and the best rate capability. Its specific capacity reaches 131 mAh g⁻¹ at 2C rate. Its capacity loss is only 14.9 % when the rate varies from C/10 to 2C.     

Conductivity of SnO<Subscript>2</Subscript>-In<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocrystalline composite films

The conductivity of films consisting of a mixture of SnO₂ and In₂O₃ nanocrystals at 200–500°C was studied. Based on the experimental data, it was assumed that in films containing less than 20 wt % In₂O₃, the current flows along SnO₂ nanocrystals. A model of conductivity in these films is presented; it includes an electron transfer from In₂O₃ to SnO₂, which forms positively charged In₂O₃ nanocrystals that contact the negatively charged SnO₂ nanocrystals. In the presence of In₂O₃ nanocrystals, the activation energy of the electron transfer between SnO₂ nanocrystals decreased substantially because of a decrease in the barrier of electron transfer between SnO₂ crystals under the action of the negative charge. As a result, a percolation cluster of charged SnO₂ crystals formed. At high contents of In₂O₃ (over 20 wt %), the conductivity increased dramatically. The curve of the temperature dependence of conductivity changed because of the appearance of a percolation cluster of In₂O₃ nanocrystals, in which the current passed. The conductivity of a mixed film of this kind differed from that of the nanocrystalline film of pure In₂O₃.     

Synthesis and characterization of Co<Subscript>0.8</Subscript>Zn<Subscript>0.2</Subscript>Fe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles

Cobalt zinc ferrite, Co_0.8Zn_0.2Fe₂O₄, nanoparticles have been synthesized via autocatalytic decomposition of the precursor, cobalt zinc ferrous fumarato hydrazinate. The X-ray powder diffraction of the ‘as prepared’ oxide confirms the formation of single phase nanocrystalline cobalt zinc ferrite nanoparticles. The thermal decomposition of the precursor has been studied by isothermal, thermogravimetric and differential thermal analysis. The precursor has also been characterized by FTIR, and chemical analysis and its chemical composition has been determined as Co_0.8Zn_0.2Fe₂(C₄H₂O₄)₃·6N₂H_4. The Curie temperature of the ‘as-prepared oxide’ was determined by AC susceptibility measurements.     

The thermodynamic properties of the [(Me<Subscript>3</Subscript>Si)<Subscript>7</Subscript>C<Subscript>60</Subscript>]<Subscript>2</Subscript> fullerene complex

The temperature dependence of the heat capacity C _p ^o of the [(Me₃Si)₇C₆₀]₂ fullerene complex was measured for the first time using precision adiabatic vacuum calorimetry over the temperature range 6.7–340 K and high-accuracy differential scanning calorimetry at 320–635 K. For the most part, the error in the C _p ^o values was about ±0.5%. An irreversible endothermic effect caused by the splitting of the dimeric bond between fullerene fragments and the thermal decomposition of the complex was observed at 448–570 K. The thermodynamic characteristics of this transformation were calculated and analyzed. Multifractal analysis of the low-temperature (T < 50 K) heat capacity was performed, and conclusions were drawn concerning the character of the heterodynamicity of the structure. The experimental data obtained were used to calculate the standard thermodynamic functions C _p ^o (T), H ^o (T) ? H ^o (0), S ^o (T) ? S ^o (0), and G ^o (T) ? H ^o (0) over the temperature range from T → 0 to 445 K and estimate the standard entropy of formation of the compound from simple substances at 298.15 K. The standard thermodynamic properties of [(Me₃Si)₇C₆₀]₂ are compared with those of the (C₆₀)₂ dimer, the [(η⁶-Ph₂)₂Cr]⁺[C₆₀]^?? fulleride, and the initial C₆₀ fullerene.