磺化侧苯基杂萘联苯聚醚酮酮的合成与性能

以4-(3-苯基-4-羟基苯基)-2,3-二氮杂萘-1-酮(DHPZ-P)、 4-(4-羟基苯基)-2,3-二氮杂萘-1-酮(DHPZ)和1,4-二(4'-氟苯甲酰基)苯(BFBB)为原料, 经溶液亲核取代缩聚反应, 通过调节DHPZ-P和DHPZ的比例, 合成了一系列侧苯基杂萘联苯聚醚酮酮(PPEKK-P), 然后以浓硫酸为磺化剂, 制备出一系列磺化侧苯基杂萘联苯聚醚酮酮(SPPEKK-P). 利用傅里叶变换红外光谱(FTIR)和氢核磁共振谱(¹H NMR)对聚合物结构进行表征, 结果表明, 磺酸基团引入到聚合物链的侧苯基上. 采用溶液浇铸法制备SPPEKK-P质子交换膜. SPPEKK-P膜的吸水率、 溶胀率和质子传导率均随离子交换容量(IEC)的增加而增加, 且具有较好的耐氧化性. IEC最高的SPPEKK-P-100膜的质子传导率在95℃能达到7.44×10^-2 S/cm, 且甲醇渗透系数为5.57×10^-8 cm²/s, 阻醇性能优于Nafion117膜.     

一种用于质子交换膜材料的磺化聚醚醚砜的合成

以发烟硫酸和4,4′-二氯二苯砜为原料,通过磺化反应,制得磺化二氯二苯砜,然后利用亲核缩聚反应,调整磺化单体和非磺化单体的比例,与四甲基联苯二酚进行聚合,制取了系列具有不同磺化度的聚醚醚砜,并对聚合物的结构进行了研究.     

Semi-interpenetrating polymer networks toward sulfonated poly(ether ether ketone) membranes for high concentration direct methanol fuel cell

Semi-IPNs were constructed by forming the crosslinking networks via the reaction between BPPO and diamine cross-linkers to overcome the dimensional swelling and methanol-permeation issues of SPEEK.     

一种新型的用于质子交换膜燃料电池的磺化聚醚醚酮酮

以发烟硫酸和4,4-二(4-氟苯甲酰基)苯[1,4-bi(4-fluorobenzoyl)benzene]为原料,通过磺化反应,制得磺化二氟三苯二酮[1,4-bi(3-sodiumsulfonate-4-fluorobenzoyl)benzene].利用亲核缩聚反应,调整磺化单体和非磺化单体的比例,与酚酞进行聚合,制取了具有不同磺化度的聚醚醚酮酮,并对聚合物的结构进行了表征.结果表明,此系列磺化聚醚醚酮酮的膜制品具有良好的离子交换特性,可望应用于燃料电池膜.     

侧链型磺化聚芳醚酮质子交换膜材料的制备

本文通过对聚合物的结构设计, 采用均聚的途径将柔顺的大侧基(甲氧基苯基)引入聚芳醚酮侧链, 然后通过室温后磺化的方法成功制备出侧链型磺化聚芳醚酮材料. 此类材料表现出较好的热稳定性; 力学性能优异; 聚合物的质子传导率比报道过的类似材料有较大程度的提高; 于80 ℃时的质子传导率在0.190 S/cm以上, 超过了Nafion 117 薄膜的传导率(0.175 S/cm). 因此这类材料有望在质子交换膜领域得到应用.     

Preliminary evaluation of sulfonated poly(ether ether ketone)/monoethanolamine/adipic acid composite membranes for direct methanol fuel cell applications

A series of sulfonated poly(ether ether ketone)/monoethanolamine/adipic acid (SPEEK/MEA/AA) composite membranes are prepared and investigated to assess their possibility as proton exchange membranes in direct methanol fuel cells (DMFCs). A preliminary evaluation shows that introducing MEA and AA into SPEEK matrix decreases the thermal stability of membrane. However, the degradation temperatures are still above 260 °C, satisfying the requirement for fuel cell operation. Compared with the pure SPEEK membrane, the composite membranes exhibit not only lower water uptake and swelling ratios but also better mechanical property and oxidative stability. Noticeably, the methanol diffusion coefficient of the composite membranes decrease significantly from 3.15 × 10^?6 to 0.76 × 10^?6 cm²/s with increasing MEA and AA content, accompanied by only a small sacrifice in proton conductivity. Although both the methanol diffusion coefficient and the proton conductivity of composite membranes are lower than those of pure SPEEK and Nafion® 117 membranes, their selectivity (conductivity/methanol diffusion coefficient) are higher. In addition, the composite membranes show excellent stability in aqueous methanol solution. The good thermal and chemical stability, low swelling ratio, excellent mechanical property, low methanol diffusion coefficient, and high selectivity make the use of these composite membranes in DMFCs quite attractive. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2871–2879, 2007     

Blend membranes of Nafion/sulfonated poly(aryl ether ketone) for direct methanol fuel cell

Sulfonated poly(aryl ether ketone) (sPAEK) synthesized by LG Chem. was confirmed by FT-IR. To estimate the thermal stability, glass transition temperature and decomposition temperature were investigated. They showed that sPAEK had good thermal properties. The proton conductivity, methanol permeability and water uptake of sPAEK were also measured. Nafion/sulfonated poly(aryl ether ketone) composite membranes were prepared by blending two materials. The blend ratios of sPAEK and Nafion were 2:1, 3:1, 5:1, and 7:1. The blend membranes showed phase separated morphology since they became immiscible during the solvent evaporation process. Due to the differences in specific gravity and solvent concentration profile during the solvent evaporation process, the upper region had lower Nafion volume fraction with smaller domains and the lower region had higher Nafion volume fraction with larger domains. Mechanical properties such as the stress at break, yield stress, Young's modulus, and elongation at break were measured. The sPAEK had better mechanical properties than Nafion. The mechanical properties increased with increasing sPAEK content. Proton conductivity and methanol permeability of the blend membranes were lower than those of Nafion. Both decreased with decreasing Nafion content. Since the methanol permeability of sPAEK was lower than that of Nafion, sPAEK acted as the methanol barrier. Water uptake of sPAEK was higher than that of Nafion.     

Investigation of sulfonated poly(ether ether ketone sulfone)/heteropolyacid composite membranes for high temperature fuel cell applications

The sulfonated poly(ether ether ketone sulfone) (SPEEKS)/heteropolyacid (HPA) composite membranes with different HPA content in SPEEKS copolymers matrix with different degree of sulfonation (DS) were investigated for high temperature proton exchange membrane fuel cells. Composite membranes were characterized by Fourier transfer infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). FTIR band shifts suggested that the sulfonic acid groups on the copolymer backbone strongly interact with HPA particles. SEM pictures showed that the HPA particles were uniformly distributed throughout the SPEEKS membranes matrix and particle sizes decreased with the increment of copolymers' DS. The holes were not found in SPEEKS‐4/HPA30 (consisting of 70% SPEEKS copolymers with DS = 0.8 and 30% HPA) composite membrane after composite membranes were treated with boiling water for 24 h. Thermal stabilities of the composite membranes were better than those of pure sulfonated copolymers membranes. Although the composite membranes possessed lower water uptake, it exhibited higher proton conductivity for SPEEKS‐4/HPA30 especially at high temperature (above 100 °C). Its proton conductivity linearly increased from 0.068 S/cm at 25 °C to 0.095 S/cm at 120 °C, which was higher than 0.06 S/cm of Nafion 117. In contrast, proton conductivity of pure SPEEKS‐4 membrane only increased from 0.062 S/cm at 25 °C to 0.078 S/cm at 80 °C. At 120 °C, proton conductivity decreased to poor 0.073 S/cm. The result indicated that composite membranes exhibited high proton conductivity at high temperature. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 1967–1978, 2006     

Ionic conducting membranes based on new sulfonated poly(arylene ether ketone)s for fuel cell applications

The synthesis and characterization of new di‐ and tetra‐sulfonated ether diketone monomers are described. From these monomers, a wide series of sulfonated poly(arylene ether ketone)s (SPAEK) are synthesized by varying the sulfonic acid repartition along the polymer backbones. Their chemical structures are thoroughly characterized by NMR. From these polymers tough membranes are obtained from solution casting method and their water uptake, ionic conductivity, and water/gas permeation properties are determined and compared with those of Nafion membrane. Preliminary fuel cell tests show that SPAEK membranes are promising candidates for fuel cell application. This work brings new insights concerning the beneficial effects of introducing densely sulfonated monomers in a polyarylether macromolecular structure along with fluorinated groups improving conductivity while reducing unwanted excessive swelling. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2017 , 55, 771–777     

高磺化度芳香聚醚醚酮的合成与表征

用3,3'-二磺酸钠基-4,4-二氟二苯酮合成了具有高磺化度的荷电聚醚醚酮.用红外吸收光谱及DSC对其进行了表征.研究了共聚物的组成、热稳定性、溶解性、成膜性及磺化度对共聚物性能的影响.     

Sulfonated poly(aryl ether ether ketone ketone)s containing fluorinated moieties as proton exchange membrane materials

A series of sulfonated poly(aryl ether ether ketone ketone)s statistical copolymers with high molecular weights were synthesized via an aromatic nucleophilic substitution polymerization. The sulfonation content (SC), defined as the number of sulfonic acid groups contained in an average repeat unit, could be controlled by the feed ratios of monomers. Flexible and strong membranes in sodium sulfonate form could be prepared by the solution casting method, and readily transformed to their proton forms by treating them in 2 N sulfuric acid. The polymers showed high T_gs, which increased with an increase in SC. Membranes prepared from the present sulfonated poly(ether ether ketone ketone) copolymers containing the hexafluoroisopropylidene moiety (SPEEKK‐6F) and copolymers containing the pendant 3,5‐ditrifluoromethylphenyl moiety (SPEEKK‐6FP) had lower water uptakes and lower swelling ratios in comparison with previously prepared copolymers containing 6F units. All of the polymers possessed proton conductivities higher than 1 × 10^?2 S/cm at room temperature, and proton conductivity values of several polymers were comparable to that of Nafion at high relative humidity. Their thermal stability, oxidative stability, and mechanical properties were also evaluated. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2299–2310, 2006     

Morphology control of sulfonated poly(ether ketone ketone) poly(ether imide) blends and their use in proton-exchange membranes

Polymer blends based on sulfonated poly(ether ketone ketone) (SPEKK) as the proton-conducting component and poly(ether imide) (PEI) as the second component were considered for proton-exchange membranes (PEMs). The PEI was added to improve the mechanical stability and lower the water swelling in the fuel cell environment. Membranes were cast from solution using N-methyl-2-pyrrolidone (NMP) and dimethylacetamide (DMAc). The ternary, polymer/polymer/solvent, phase diagram was determined to provide guidance on how to control the morphology during solvent casting of blend membranes.

For blends of SPEKK (ion-exchange capacity = 2 mequiv/g) with PEI as the minority component, the morphology consisted of dispersed particles of 0.5–6 μm. Larger particles were achieved by increasing the PEI content and/or lowering the casting temperature. High-temperature annealing after solution casting did not affect the morphology of blend membranes, due to the low mobility and compatibility of the two polymers.

The possible use of SPEKK/PEI blends in PEMs is discussed in terms of existing theories of ion transport in polymers.     

Synthesis and characterization of poly(aryl ether ketone) ionomers with sulfonic acid groups on pendant aliphatic chains for proton-exchange membrane fuel cells

A series of parent poly(aryl ether ketone)s bearing different content of unsaturated pendant propenyl groups were synthesized via nucleophilic substitution polymerization from 3,3′-diallyl-4,4′-dihydroxybiphenyl, 9,9′-bis(4-hydroxyphenyl) fluorene and 4,4′-difluorobenzophenone. The polymers with pendant aliphatic sulfonic acid groups were further synthesized by free radical thiol-ene coupling reactions between 3-mercapto-1-propanesulfonic sodium and the parent propenyl functional copolymers. The resulting sulfonated polymers with high inherent viscosity (1.83-4.69 dL/g) were soluble in polar organic solvents and can form flexible and transparent membranes by casting from their solutions. The copolymers with different ion exchange capacity could be conveniently synthesized by varying the monomers ratios. Transmission electron microscopy (TEM) was used to examine the microstructures of the membrane and the results revealed that significant hydrophilic/hydrophobic microphase separation with spherical, uniform-sized (5-10 nm) and well-dispersed hydrophilic domains was afforded. The proton conductivities of the as-prepared membranes and the state-of-the-art Nafion 117 membrane in fully hydrated state were investigated. The results revealed that the proton conductivity of the synthesized membranes increased more remarkably than that of Nafion 117 membrane with increasing temperature. The membrane with 1.69 mequiv/g of IEC had a conductivity of 2.5 × 10⁻² Scm⁻¹ at 100 °C. The membranes also possessed excellent mechanical properties, good thermal, oxidative, hydrolytic and dimensional stabilities.     

一种新型磺化聚醚醚酮的合成、表征和性能

以特丁基对苯二酚、3,3′-二磺酸钠基-4,4′-二氟二苯酮和4,4′-二氟二苯酮为单体,制备了具有高磺化度的聚醚醚酮.该系列聚合物可溶,并具有良好的成膜性.对聚合物及其膜的一些性能进行了研究.     

Proton conductive membranes of sulfonated poly(ether ketone ketone)

Poly(ether ketone ketone) was sulfonated using fumic sulfuric acid and used for preparation of proton conductive membranes. The sulfonation degree was evaluated by elemental and thermal analysis and the IEC values were determined by titration. The proton conductivity of membranes with sulfonation degrees up to 70% was determined as a function of temperature by impedance spectroscopy. Membranes with sulfonation degree 38–70% were tested in DMFC experiments. Their performance was comparable to Nafion^® with the same pretreatment and clearly better than sulfonated poly(ether ether ketone) membranes with similar functionalization. The methanol crossover was lower than that of Nafion^® in the same conditions.     

Preparation and properties of UV irradiation-induced crosslinked sulfonated poly(ether ether ketone) proton exchange membranes

The crosslinkable sulfonated poly(ether ether ketone)s (SPEEKs) were synthesized by nucleophilic substitution reaction of diallyl bisphenol A, tert-butylhydroquinone, 4,4′-difluorobenzophenone and sodium 5,5′-carbonylbis(2-fluorobenzene-sulfonate). The SPEEKs with high intrinsic viscosity showed good solubility and could be cast into flexible and transparent membranes. The SPEEK membranes containing benzophenone (BP) and triethylamine (TEA) photo-initiator system were treated by UV light to promote crosslinking. The experimental results revealed that the crosslinked membrane with 10 min irradiation time showed the most potential as proton exchange membrane for direct methanol fuel cell applications. When the irradiation time increased from 0 to 10 min, the water uptake decreased from 29.1 to 26.1%, and the tensile modulus and the tensile strength enhanced sharply from 0.80 to 1.44 GPa and from 40.3 to 63.4 MPa, respectively. In addition, the methanol diffusion coefficient reduced sharply from 1.70 × 10⁻⁶ to 7.42 × 10⁻⁷ cm²/s with only slight sacrifice in the proton conductivity, which made the crosslinked membrane with 10 min irradiation time possess the highest selectivity.     

燃料电池质子交换膜用新型磺化聚芳醚酮的合成和性能表征

报道了一种新型磺化聚芳醚酮材料的合成方法, 通过引入取代基对聚芳醚主链进行保护，用氯磺酸直接磺化方法在聚芳醚酮高分子侧基上引入磺酸功能基, 实现了聚合物磺化结构的可控定位合成, 得到了稳定性较好的磺化聚芳醚酮. 通过核磁共振(NMR)、 热重(TG)和凝胶渗透色谱(GPC)等分析方法对其结构及性能进行了表征. 用溶液浇膜法制备了质子交换膜, 考察了膜的各种性能, 并与商用Nafion膜进行了比较, 其导电性、 热稳定性和吸水性远优于Nafion膜, 抗氧化性、抗水解性和机械强度也达到了较高的指标.     

Studies on cellulose acetate and sulfonated poly(ether ether ketone) blend ultrafiltration membranes

New ultrafiltration membranes based on chemically and thermally stable arylene main-chain polymers have been prepared by blending the sulfonated poly(ether ether ketone) with cellulose acetate in various compositions in N,N^′-dimethylformamide as solvent by phase inversion technique. Prepared membranes have been subjected to ultrafiltration characterizations such as compaction, pure water flux, water content, and membrane hydraulic resistance. The pore statistics and molecular weight cut-off (MWCO) of the membranes have been estimated using proteins such as trypsin, pepsin, egg albumin and bovine serum albumin. The pore size increased with increasing concentrations of sulfonated poly(ether ether ketone) in the casting solution. Similarly, the MWCOs of the membranes ranged from 20 to 69 kDa, depending on the various polymer compositions. Surface and cross-sectional morphologies of membranes were analyzed using scanning electron microscopy. The effects of polymer compositions on the above parameters were analyzed and the results are compared and discussed with those of pure cellulose acetate membranes.     

新型的含芳香二腈基磺化聚芳醚腈酮的合成与表征

通过Diels-Alder反应合成了一种新型的含芳香二腈基的双酚单体, 并利用此单体与活性二卤化物共聚合成了一系列高分子量的磺化聚芳醚腈酮聚合物. 聚合物的结构通过元素分析和核磁共振谱进行表征. 结果表明, 该聚合物具有优良的导质子率、尺寸和化学稳定性及良好的力学性能.     

Characterization and performance of proton exchange membranes for direct methanol fuel cell: Blending of sulfonated poly(ether ether ketone) with charged surface modifying macromolecule

Modification of sulfonated poly(ether ether ketone) (SPEEK) membrane was attempted by blending charged surface modifying macromolecule (cSMM). The modified membrane was tested for direct methanol fuel cell (DMFC) application; i.e. a SPEEK/cSMM blend membrane was compared to a SPEEK membrane and a Nafion 112 membrane for the thermal and mechanical stability, methanol permeability, and proton conductivity. Thermal and mechanical stability of the blended membrane were slightly reduced from the SPEEK membrane but still higher than the Nafion 112 membrane. The blend membrane was found to be promising for DMFC applications because of its lower methanol diffusivity (2.75 × 10⁻⁷ cm² s⁻¹) and higher proton conductivity (6.4 × 10⁻³ S cm⁻¹), than the SPEEK membrane. A plausible explanation was given for the favorable effect of cSMM blending.