中空管状g-C3N4/Ag3PO4复合催化剂的制备及其可见光催化性能

用化学沉淀法制备中空管状g-C₃N₄/Ag₃PO₄复合催化剂。通过X射线衍射(XRD)、扫描电子显微镜(SEM)、紫外可见漫反射光谱(UV-Vis DRS)和荧光光谱对其结构、形貌和光学性能进行了表征。结果表明：Ag₃PO₄纳米颗粒均匀地分散在中空管状g-C₃N₄表面,两者紧密结合形成异质结。研究复合催化剂在可见光照射下降解盐酸四环素(TC)的光催化活性。结果显示：复合催化剂在80 min内对TC的降解率为98%,其降解反应速率常数是纯相Ag₃PO₄的3倍。经过5次循环实验后复合催化剂对于TC的降解率仍保持87%,具有优良的循环稳定性。捕获实验表明空穴(h⁺)和超氧负离子(·O^-₂)是光催化反应过程中的主要活性物种。根据能带理论,提出了复合催化剂异质结的Z型光催化机理。     

Ag/Ag3PO4/g-C3N4三元复合光催化剂的制备及其可见光驱动下的光催化活性增强

报道了一种新型Ag/Ag₃PO₄/g-C₃N₄三元复合光催化剂的制备及其半导体界面处的快速载流子分离所引起的光催化活性的显著增强效应。通过X射线衍射,扫描电子显微镜,紫外-可见吸收光谱以及光致发光光谱等就其晶体结构、形貌、组分、光学吸收以及载流子的快速分离行为进行了表征与分析。以罗丹明B作为模型化合物分子,研究发现,所制备的Ag/Ag₃PO₄/g-C₃N₄三元复合光催化剂在可见光照射下表现出比Ag₃PO₄以及Ag₃PO₄/g-C₃N₄二元催化剂更为优异的光催化活性。研究认为,Ag₃PO₄表面尺寸约为40 nm的Ag纳米粒子在可见光下受激所产生的等离子表面共振效应以及Ag₃PO₄与g-C₃N₄界面处所形成的类似异质结结构对所制备的Ag/Ag₃PO₄/g-C₃N₄三元复合光催化剂光催化活性的显著增强起到重要作用。     

Ag3PO4/Ag2S/g-C3N4复合光催化剂的制备与性能

通过沉积法和离子交换法成功地制备了Ag_3PO_4/Ag_2S/g-C_3N_4复合型光催化剂。利用X射线多晶粉末衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线光电子能谱(XPS)、N_2吸附-脱附等温线、紫外-可见漫反射光谱、荧光光谱等手段对样品进行了表征。通过降解罗丹明B考察其可见光催化活性及稳定性,研究了硫化钠与磷酸银物质的量的比值(n_(Na_2S)/n_(Ag_3PO_4))、g-C_3N_4添加量对所制备复合光催化材料性能的影响,同时对光催化机理进行了探讨。结果表明,随着n_(Na2S)/n_(Ag3PO4)的增加,所得复合催化材料活性先增加后降低;当n_(Na2S)/n_(Ag_3PO_4)为1.5%、g-C_3N_4与Ag_3PO_4的质量比为3∶7时制备的催化剂ASC1.5的光催化活性最好,在可见光照射下,40 min内可将罗丹明B完全降解,且5次循环使用后仍保持较高的催化活性。和Ag_3PO_4相比,Ag_3PO_4/Ag_2S/g-C_3N_4复合型光催化材料的活性与稳定性都得到明显提高,这主要归因于复合催化剂比表面积和孔结构的增加,载流子分离效率的提高。光催化机理研究表明,空穴(h~+)、超氧阴离子自由基(·O~(2-))和羟基自由基(·OH)都是光催化过程中的主要活性物种。三者作用大小依次为:h~+·O~(2-)·OH。     

g-C3N4纳米管的制备及其光催化降解性能

以三聚氰胺和碳酸氢铵混合物为原料,采用简便热解法制备g-C₃N₄纳米管。热解过程中碳酸氢铵分解释放出大量的NH₃,能够诱导纳米管的形成。利用X射线衍射（XRD）、扫描电子显微镜（SEM）、红外光谱（IR）、N₂吸附-脱附、紫外-可见漫反射光谱以及紫外可见光谱（UV）等分析测试方法对该光催化剂的微观形貌结构和催化性能进行了表征。以罗丹明光催化降解为模型反应研究了g-C₃N₄纳米管的光催化活性。g-C₃N₄纳米管的表面积明显增大,且能够有效地促进光生电子转移,在可见光下具有较强的光催化性能,降解率在60和120 min时分别能达到95%和99.4%,且循环重复利用5次后降解率不低于92%。     

g-C3N4纳米管的制备及其光催化降解性能

以三聚氰胺和碳酸氢铵混合物为原料,采用简便热解法制备g-C_3N_4纳米管。热解过程中碳酸氢铵分解释放出大量的NH3,能够诱导纳米管的形成。利用X射线衍射(XRD)、扫描电子显微镜(SEM)、红外光谱(IR)、N_2吸附-脱附、紫外-可见漫反射光谱以及紫外可见光谱(UV)等分析测试方法对该光催化剂的微观形貌结构和催化性能进行了表征。以罗丹明光催化降解为模型反应研究了g-C_3N_4纳米管的光催化活性。g-C_3N_4纳米管的表面积明显增大,且能够有效地促进光生电子转移,在可见光下具有较强的光催化性能,降解率在60和120 min时分别能达到95%和99.4%,且循环重复利用5次后降解率不低于92%。     

一锅法制备Co3O4/g-C3N4复合光催化剂及其光催化性能

以三聚氰胺和六水合氯化钴为原料,一锅法制备Co_3O_4负载的多孔石墨相氮化碳(Co_3O_4/g-C_3N_4)复合光催化材料。采用X射线衍射(XRD)、傅里叶变换红外(FT-IR)光谱、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、紫外-可见漫反射光谱(UV-Vis DRS)、光致发光光谱(PL)等手段对其结构和光学特性进行表征。以盐酸四环素(TC)为目标污染物,评价了不同负载量Co_3O_4/g-C_3N_4复合光催化剂的可见光催化性能。结果表明,所制备的Co_3O_4/g-C_3N_4复合光催化剂为多孔结构,其比表面积较大,并在可见光区域具有显著的吸收。利用原位生成的Co_3O_4纳米粒子在氮化碳表面形成异质结构,可有效转移光生载流子,降低光生电子-空穴的再结合率,从而提高光催化活性。并且存在最佳Co_3O_4复合量,当六水合氯化钴加入量为三聚氰胺的8%(w/w)时,所制备的复合光催化剂CoCN-8具有最佳的光催化性能。在可见光的照射下,60 min内可降解85%的TC,而同样条件下,纯g-C_3N_4仅降解23%的TC。     

单分散g-C3N4量子点修饰一维棒状BiPO4微晶的合成及其对光催化活性增强机理

利用水热法合成了一维棒状BiPO₄微晶,在此基础上采用浸渍-被烧法进行g-C₃N₄量子点表面修饰获得新颖的g-C₃N₄/BiPO₄异质结。借助X射线衍射(XRD)、场发射扫描电镜(FE-SEM)、透射电镜(HRTEM)、能谱(EDS)、紫外-可见漫反射(UV-Vis-DRS)等测试手段对所得样品的相组成、形貌和谱学特征进行了表征。选择罗丹明B(RhB)和苯酚作为模型污染物研究了所得在可见光下的催化活性。结果表明,样品16%(w/w) g-C₃N₄/BiPO₄对RhB降解的速率常数分别是纯和的g-C₃N₄和BiPO₄的16倍和4.6倍。g-C₃N₄量子点与BiPO₄之间形成异质结,抑制了光生电子-空穴对的复合,从而提高了催化剂的活性。自由基捕获实验进一步表明,超氧负离子自由基(·O₂-)是催化降解RhB和苯酚的主要活性物种。     

Ag_3PO_4/MoS_2纳米片复合催化剂制备及可见光催化性能

采用机械球磨法成功制备Ag_3PO_4/MoS_2纳米片复合催化剂。运用X射线衍射仪(XRD)、透射电子显微镜(TEM)、扫描电子显微镜(SEM)、紫外可见漫反射光谱(UV-Vis)和荧光发射光谱(PL)对复合催化剂的结构和形貌进行了表征。结果表明,Ag_3PO_4纳米粒子均匀地附着在MoS_2纳米片层结构上,两者形成紧密结合。以亚甲基蓝为模拟污染物,研究复合催化剂在可见光照射下的光催化特性;通过循环实验考察复合催化剂的稳定性。结果显示,含有1%的MoS_2纳米片与Ag_3PO_4形成的复合催化剂在30 min内对亚甲基蓝的降解率为95%,其降解动力学常数是纯相Ag_3PO_4的2倍。经过5次循环实验后复合催化剂对于亚甲基蓝的降解率为84%,而纯Ag_3PO_4对于亚甲基蓝的降解率仅为35%。Ag_3PO_4/MoS_2纳米片复合催化剂具有优良的光催化活性和高稳定性,主要归因于二硫化钼纳米片与磷酸银形成异质结,磷酸银激发的电子和二硫化钼纳米片产生的空穴直接复合,从而促使光生电子从磷酸银晶体表面快速分离,减轻了磷酸银的光电子腐蚀,同时也提高了复合物的光催化活性。     

碳化MoS2/掺硫g-C3N4异质结的合成及其在可见光下催化降解罗丹明B机理

为了进一步提高聚合物半导体类石墨相氮化碳（g-C₃N₄）降解有机物的活性,通过简单的水热法复合得到碳化MoS₂/掺硫g-C₃N₄异质结（MoSC/S-CN）,并在可见光下研究其罗丹明B （RhB）的降解性能。结果表明,相较于纯g-C₃N₄,最优化的MoSC/S-CN样品对可见光的吸收范围得到明显拓宽,并且在100 min内对RhB的降解效率为92.5%,比纯g-C₃N₄性能提高68.83%。一系列的结构和光学性质表明,掺硫后再进一步与碳化MoS₂耦合可以协同作用于g-C₃N₄,改善g-C₃N₄的能带结构,加速光生电子空穴对的分离,有效提高光催化活性。     

单分散g-C3N4量子点修饰一维棒状BiPO4微晶的合成及其对光催化活性增强机理

利用水热法合成了一维棒状BiPO₄微晶,在此基础上采用浸渍-焙烧法进行g-C₃N₄量子点表面修饰获得新颖的g-C₃N₄/BiPO₄异质结。借助X射线衍射（XRD）、场发射扫描电镜（FE-SEM）、透射电镜（HRTEM）、能谱（EDS）、紫外-可见漫反射（UV-Vis-DRS）等测试手段对所得样品的相组成、形貌和谱学特征进行了表征。选择罗丹明B（RhB）和苯酚作为模型污染物研究了所得在可见光下的催化活性。结果表明,样品16%（w/w） g-C₃N₄/BiPO₄对RhB降解的速率常数分别是纯g-C₃N₄和BiPO₄的4.6倍和15倍。g-C₃N₄量子点与BiPO₄之间形成异质结,抑制了光生电子-空穴对的复合,从而提高了催化剂的活性。自由基捕获实验进一步表明,超氧负离子自由基（·O₂^-）是催化降解RhB和苯酚的主要活性物种。     

Ag3PO4/MoS2纳米片复合催化剂制备及可见光催化性能

采用机械球磨法成功制备Ag₃PO₄/MoS₂纳米片复合催化剂。运用X射线衍射仪（XRD）、透射电子显微镜（TEM）、扫描电子显微镜（SEM）、紫外可见漫反射光谱（UV-Vis）和荧光发射光谱（PL）对复合催化剂的结构和形貌进行了表征。结果表明,Ag₃PO₄纳米粒子均匀地附着在MoS₂纳米片层结构上,两者形成紧密结合。以亚甲基蓝为模拟污染物,研究复合催化剂在可见光照射下的光催化特性;通过循环实验考察复合催化剂的稳定性。结果显示,含有1%的MoS₂纳米片与Ag₃PO₄形成的复合催化剂在30 min内对亚甲基蓝的降解率为95%,其降解动力学常数是纯相Ag₃PO₄的2倍。经过5次循环实验后复合催化剂对于亚甲基蓝的降解率为84%,而纯Ag₃PO₄对于亚甲基蓝的降解率仅为35%。Ag₃PO₄/MoS₂纳米片复合催化剂具有优良的光催化活性和高稳定性,主要归因于二硫化钼纳米片与磷酸银形成异质结,磷酸银激发的电子和二硫化钼纳米片产生的空穴直接复合,从而促使光生电子从磷酸银晶体表面快速分离,减轻了磷酸银的光电子腐蚀,同时也提高了复合物的光催化活性。     

Facile Synthesis of Porous g-C3N4 with Enhanced Visible-Light Photoactivity

Porous graphitic carbon nitride (g-C₃N₄) was prepared by dicyandiamide and urea via the pyrolysis method, which possessed enhanced visible-light-driven photocatalytic performance. Its surface area was increased from 17.12 to 48.00 m²/g. The porous structure not only enhanced the light capture capacity, but also accelerated the mass transfer ability. The Di (Dicyandiamide)/Ur (Urea) composite possessed better photocatalytic activity for Rhodamine B in visible light than that of g-C₃N₄. Moreover, the Di/Ur-4:5 composite showed the best photoactivity, which was almost 5.8 times that of g-C₃N₄. The enhanced photocatalytic activity showed that holes and superoxide radical played a key role in the process of photodegradation, which was ascribed to the enhanced separation of photogenerated carriers. The efficient separation of photogenerated electron-hole pairs may be owing to the higher surface area, O dopant, and pore volumes, which can not only improve the trapping opportunities of charge carriers but also the retarded charge carrier recombination. Therefore, it is expected that the composite would be a promising candidate material for organic pollutant degradation.     

g-C3N4-BiOBr复合材料制备及可见光催化性能

利用原位沉积法将Bi OBr纳米片生长到g-C_3N_4表面,制得g-C_3N_4-Bi OBr p-n型异质结复合光催化剂。采用X射线衍射(XRD)、红外光谱(FTIR)、场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)、紫外可见漫反射(UV-Vis-DRS)和荧光光谱(PL)等测试对光催化剂结构和性能进行表征。通过可见光辐照降解甲基橙水溶液检测评估复合光催化剂光催化活性。研究结果表明:复合光催化剂由Bi OBr和g-C_3N_4两相组成,Bi OBr纳米片在片状g-C_3N_4表面快速形核生长形成面-面复合结构。相比于纯相g-C_3N_4和Bi OBr,g-C_3N_4-Bi OBr复合材料具有更强可见光吸收能力,吸收带边红移。在可见光辐照100 min后,性能最佳的2:8 gC_3N_4-Bi OBr复合光催化剂光催化活性分别是纯相g-C_3N_4和Bi OBr的1.8和1.2倍,经过4次循环实验后,其降解率仍达84%,说明复合结构光催化剂催化性能和稳定性增强。复合光催化剂的荧光强度显著降低,说明光生载流子复合得到了有效抑制。复合光催化剂催化性能的提高归因于p-n型异质结促进电荷有效分离、抑制电子-空穴复合和吸收光波长范围的扩展,相比单一成分材料具有更好的催化活性和稳定性。自由基捕获实验证明,可见光降解甲基橙光催化过程中的主要活性成分为空穴,并据此提出了可能的光催化机理。     

p-n异质结BiPO_4/Ag_3PO_4的制备及其增强的模拟太阳光活性

采用一步水热合成法制备了BiPO_4、Ag_3PO_4和BiPO_4/Ag_3PO_4复合光催化剂,通过X射线粉末衍射(XRD)、X射线光电子能谱(XPS)、扫描电子显微镜(SEM)、紫外-可见漫反射(UV-Vis DRS)等表征手段对其组成结构、形貌及光吸收性质进行了表征,结果表明Ag_3PO_4呈块状结构,BiPO_4则分布在其表面,形成的BiPO_4/Ag_3PO_4复合光催化剂具有单斜相和立方晶相结构,带边吸收拓宽至571 nm。以甲基橙和加替沙星为目标污染物,考察了BiPO_4/Ag_3PO_4复合光催化剂在模拟太阳光照射下的降解矿化能力,结果表明复合催化剂比单一催化剂的降解矿化能力更强,稳定性更好。此外,自由基捕获实验表明空穴是该光催化过程中的主要活性物种,·O2-次之。p-n异质结的形成使BiPO_4/Ag_3PO_4复合光催化剂具有较强的电子空穴分离能力是光催化活性提高的主要原因,这与光电流和电化学阻抗谱测试结果相一致。基于以上结果,文中对BiPO_4/Ag_3PO_4光催化降解有机污染物的机理进行了推测。     

p-n异质结BiPO4/Ag3PO4的制备及其增强的模拟太阳光活性

采用一步水热合成法制备了BiPO₄、Ag₃PO₄和BiPO₄/Ag₃PO₄复合光催化剂,通过X射线粉末衍射（XRD）、X射线光电子能谱（XPS）、扫描电子显微镜（SEM）、紫外-可见漫反射（UV-Vis DRS）等表征手段对其组成结构、形貌及光吸收性质进行了表征,结果表明Ag₃PO₄呈块状结构,BiPO₄则分布在其表面,形成的BiPO₄/Ag₃PO₄复合光催化剂具有单斜相和立方晶相结构,带边吸收拓宽至571 nm。以甲基橙和加替沙星为目标污染物,考察了BiPO₄/Ag₃PO₄复合光催化剂在模拟太阳光照射下的降解矿化能力,结果表明复合催化剂比单一催化剂的降解矿化能力更强,稳定性更好。此外,自由基捕获实验表明空穴是该光催化过程中的主要活性物种,·O₂^-次之。p-n异质结的形成使BiPO₄/Ag₃PO₄复合光催化剂具有较强的电子空穴分离能力是光催化活性提高的主要原因,这与光电流和电化学阻抗谱测试结果相一致。基于以上结果,文中对BiPO₄/Ag₃PO₄光催化降解有机污染物的机理进行了推测。     

MoS_2/g-C_3N_4复合材料的制备及可见光催化性能

首先在N-甲基吡咯烷酮溶液中超声剥离得到少层的MoS_2,将其与石墨相氮化碳(g-C_3N_4)复合,制得MoS_2/g-C_3N_4复合材料。采用X射线衍射(XRD),扫描电镜(SEM),X射线光电子能谱(XPS),傅里叶变换红外光谱(FTIR),Raman光谱,紫外-可见漫反射吸收光谱(DRS)和光致荧光(PL)技术对复合材料进行表征。可见光下考察MoS_2/g-C_3N_4复合材料光催化降解罗丹明B(Rh B)的活性,结果表明:将少量MoS_2与g-C_3N_4复合可明显提高光催化活性,且1%(w/w)MoS_2/g-C_3N_4复合物的光催化活性最高,可能的原因是MoS_2和g-C_3N_4匹配的能带结构,增大了界面间电荷的传输,降低了光生电子-空穴的复合,进而提高了光催化活性。     

可见光响应的Co3(PO4)2/Ag3PO4纳米复合光催化剂的制备及表征

采用简单的化学偏聚法合成出Ag₃PO₄纳米颗粒、磷酸钴（Co₃（PO₄）₂,CoP）纳米片以及它们两者的纳米复合结构（CoP/Ag₃PO₄）,同时还比较了它们的可见光催化活性. 采用场发射扫描电镜（FESEM）、X 射线衍射（XRD）、紫外-可见（UV-Vis）吸收光谱以及光致发光谱等手段对其形貌、结构、光学以及可见光催化性能等进行表征. 结果表明,CoP/Ag₃PO₄复合纳米结构的可见光降解甲基橙（MO）的速率和循环稳定性均明显优于其它两种物质. 这表明CoP应该起着共催化剂的作用,它能够抑制光生电子与空穴之间的复合,并且提供大量高活性的光生空穴. 此外,我们还发现CoP/Ag₃PO₄降解另一种阳离子型染料——罗丹明B（RhB）的能力则远不如纯Ag₃PO₄,这可能是与光催化剂的表面性质发生改变有关,造成更低的RhB吸附能力. 本文提供了一种廉价制备高效可见光催化剂的新方法.     

MoS2/g-C3N4复合材料的制备及可见光催化性能

首先在N-甲基吡咯烷酮溶液中超声剥离得到少层的MoS₂,将其与石墨相氮化碳（g-C₃N₄）复合,制得MoS₂/g-C₃N₄复合材料。采用X射线衍射（XRD）,扫描电镜（SEM）,X射线光电子能谱（XPS）,傅里叶变换红外光谱（FTIR）,Raman光谱,紫外-可见漫反射吸收光谱（DRS）和光致荧光（PL）技术对复合材料进行表征。可见光下考察MoS₂/g-C₃N₄复合材料光催化降解罗丹明B（RhB）的活性,结果表明：将少量MoS₂与g-C₃N₄复合可明显提高光催化活性,且1%（w/w）MoS₂/g-C₃N₄复合物的光催化活性最高,可能的原因是MoS₂和g-C₃N₄匹配的能带结构,增大了界面间电荷的传输,降低了光生电子-空穴的复合,进而提高了光催化活性。     

可见光高催化活性GO/Ag3PO4/Ni复合薄膜的制备和性能

以磷酸铵和氧化石墨烯悬浊液的混合液为电解液,采用电化学共沉积法制备了Ag3PO4基GO/Ag3PO4/Ni复合薄膜。运用扫描电子显微镜(SEM)、能量色散谱(EDS)、X射线衍射(XRD)、拉曼光谱(Raman)和紫外可见漫反射光谱(UV-Vis DRS)等对其形貌、物相和光谱特性进行分析。最佳工艺制备的GO/Ag3PO4/Ni复合薄膜呈现出GO包覆在直径为100 nm左右的Ag3PO4纳米球外的表面形貌。GO片与Ag3PO4纳米球之间存在强电荷相互作用。与单独的Ag3PO4纳米球相比,GO片的附着导致带隙缩小,可见光区的吸收率增强。可见光下考察了复合薄膜降解罗丹明B的光催化活性和稳定性,并利用荧光光谱和捕获剂法对薄膜的光催化机理进行了探索。结果表明,GO片的加入不仅显著提高了Ag3PO4的光催化活性,而且提高了Ag3PO4的结构稳定性。光催化降解罗丹明B 60 min时,GO/Ag3PO4/Ni复合薄膜的降解率是Ag3PO4/Ni薄膜的1.32倍。在保持薄膜光催化活性基本不变的前提下可循环使用7次。GO优异的电荷传导性能,以及Ag3PO4纳米球与GO片之间的正协同效应是提高复合薄膜光催化性能的主要原因。     

g-C3N4-BiOBr复合材料制备及可见光催化性能

利用原位沉积法将BiOBr纳米片生长到g-C₃N₄表面,制得g-C₃N₄-BiOBr p-n型异质结复合光催化剂。采用X射线衍射(XRD)、红外光谱(FTIR)、场发射扫描电子显微镜(FE-SEM)、透射电子显微镜(TEM)、紫外可见漫反射(UV-Vis-DRS)和荧光光谱(PL)等测试对光催化剂结构和性能进行表征。通过可见光辐照降解甲基橙水溶液检测评估复合光催化剂光催化活性。研究结果表明:复合光催化剂由BiOBr和g-C₃N₄两相组成,BiOBr纳米片在片状g-C₃N₄表面快速形核生长形成面-面复合结构。相比于纯相g-C₃N₄和BiOBr,g-C₃N₄-BiOBr复合材料具有更强可见光吸收能力,吸收带边红移。在可见光辐照100 min后,性能最佳的2:8 g-C₃N₄-BiOBr复合光催化剂光催化活性分别是纯相g-C₃N₄和BiOBr的1.8和1.2倍,经过4次循环实验后,其降解率仍达84%,说明复合结构光催化剂催化性能和稳定性增强。复合光催化剂的荧光强度显著降低,说明光生载流子复合得到了有效抑制。复合光催化剂催化性能的提高归因于p-n型异质结促进电荷有效分离、抑制电子-空穴复合和吸收光波长范围的扩展,相比单一成分材料具有更好的催化活性和稳定性。自由基捕获实验证明,可见光降解甲基橙光催化过程中的主要活性成分为空穴,并据此提出了可能的光催化机理。