Synthesis of electroluminescent copoly(aryl ether)s containing alternate 1,4‐distyrylbenzene derivatives and aromatic 1,3,4‐oxadiazole or 3,3″‐terphenyldicarbonitrile segments

New copoly(aryl ether)s ( P1 – P3 ) containing alternate 2,5‐dihexyloxy‐1,4‐di(m‐ethoxystyryl)benzene ( P1 , P2 ) or 2,5‐dihexyloxy‐1,4‐distyrylbenzene ( P3 ) chromophores and aromatic 1,3,4‐oxadiazole ( P1 ) or 3,3″‐terphenyldicarbonitrile ( P2 , P3 ) segments were prepared by Horner reaction ( P1 and P2 ) or nucleophilic displacement reaction ( P3 ). They are basically amorphous materials with 5% weight‐loss temperature above 410 °C. Their absorption, photoluminescence spectra, and quantum yields are dependent on the composition of the isolated fluorophores. The emissions are exclusively dominated by 1,4‐distyrylbenzene segments via excitation energy transfer from electron‐transporting 1,3,4‐oxadiazole ( P1 ) or 3,3″‐terphenyldicarbonitrile ( P2 , P3 ) chromophores. The HOMO and LUMO energy levels have been estimated from their cyclic voltammograms, and the observations confirm that oxidation and reduction start from the emitting 1,4‐distyrylbenzene and electron‐transporting segments, respectively, indicating that both carriers affinity can be enhanced simultaneously. Among the two‐layer PLED devices (ITO/PEDOT/ P1 – P3 /Al), P1 exhibits the best performance with a turn‐on field of 4 × 10⁵ V/cm and a maximum luminance of 225 cd/m². However, P2 emits green–yellow light (555 nm), owing to the excimer emission. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5009–5022, 2005     

Synthesis and optoelectronic properties of luminescent poly(p‐phenylenevinylene) derivatives containing electron‐transporting 1,3,4‐oxadiazole groups

Three random copolymers ( P1–P3 ) comprising phenylenevinylene and electron‐transporting aromatic 1,3,4‐oxadiazole segments (11, 18, 28 mol %, respectively) were prepared by Gilch polymerization to investigate the influence of oxadiazole content on their photophysical, electrochemical, and electroluminescent properties. For comparative study, homopolymer poly[2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐p‐phenylenevinylene] ( P0 ) was also prepared by the same process. The polymers ( P0–P3 ) are soluble in common organic solvents and thermally stable up to 410 °C under a nitrogen atmosphere. Their optical properties were investigated by absorption and photoluminescence spectroscopy. The optical results reveal that the aromatic 1,3,4‐oxadiazole chromophores in P1–P3 suppress the intermolecular interactions. The HOMO and LUMO levels of these polymers were estimated from their cyclic voltammograms. The HOMO levels of P0–P3 are very similar (?5.02 to ?5.03 eV), whereas their LUMO levels decrease readily with increasing oxadiazole content (?2.7, ?3.08, ?3.11, and ?3.19 eV, respectively). Therefore, the electron affinity of the poly(p‐phenylenevinylene) chain can be gradually enhanced by incorporating 1,3,4‐oxadiazole segments. Among the polymers, P1 (11 mol % 1,3,4‐oxadiazole) shows the best EL performance (maximal luminance: 3490 cd/m², maximal current efficiency: 0.1 cd/A). Further increase in oxadiazole content results in micro‐phase separation that leads to performance deterioration. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4377–4388, 2007     

Synthesis and opto‐electrical properties of dendron‐containing poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives

A new series of poly(2,3‐diphenyl‐1,4‐phenylenevinylene) derivatives containing dendritic side groups were synthesized. Different generations of dendrons were integrated on the pendant phenyl ring to investigate their effect on optical and electrical properties of final polymers. Homopolymers can not be obtained via the Gilch polymerization because of sterically bulky dendrons. By controlling the feed ratio of different monomers during polymerization, dendron‐containing copolymers with high molecular weights were obtained. The UV–vis absorption and photoluminescent spectra of the thin films are pretty close; however, quantum efficiency is significantly enhanced with increasing the generation of dendrons. The electrochemical analysis reveals that hole‐injection is also improved by increasing dendritic generation. Double‐layer light‐emitting devices with the configuration of ITO/PEDOT:PSS/polymer/Ca/Al were fabricated. High generation dendrons bring benefit of improved device performance. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 3440–3450, 2007     

Homologous series of alkylsilylphenyl‐substituted poly (p‐phenylenevinylene)s for light‐emitting diodes

Substituent‐induced electroluminescence polymers—poly[2‐(2‐dimethyldodecylsilylphenyl)‐1,4‐phenylenevinylene] [(o‐R₃Si)PhPPV], poly[2‐(3‐dimethyldodecylsilylphenyl)‐1,4‐phenylenevinylene] [(m‐R₃Si)PhPPV], and poly[2‐(4‐dimethyldodecylsilylphenyl)‐1,4‐phenylenevinylene] [(p‐R₃Si)PhPPV]—were synthesized according to the Gilch polymerization method. The band gap and spectroscopic data were tuned by the dimethyldodecylsilyl substituent being changed from the ortho position to the para position in the phenyl side group along the polymer backbone. The weight‐average molecular weights and polydispersities were 8.0–96 × 10⁴ and 3.0–3.4, respectively. The maximum photoluminescence wavelengths for (o‐R₃Si)PhPPV, (m‐R₃Si)PhPPV, and (p‐R₃Si)PhPPV appeared around 500–530 nm in the green emission region. Double‐layer light‐emitting diodes with an indium tin oxide/poly(3,4‐ethylenedioxythiophene)/polymer/Al configuration were fabricated with these polymers. The turn‐on voltages and the maximum brightness of (o‐R₃Si)PhPPV, (m‐R₃Si)PhPPV, and (p‐R₃Si)PhPPV were 6.5–8.7 V and 1986–5895 cd/m², respectively. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2347–2355, 2004     

Green‐emitting poly[(1,3‐phenylenevinylene)‐alt‐ (1,4‐phenylenevinylene)]s: Effect of the substitution patterns on the optical properties

Green‐emitting substituted poly[(2‐hexyloxy‐5‐methyl‐1,3‐phenylenevinylene)‐alt‐(2,5‐dihexyloxy‐1,4‐phenylenevinylene)]s ( 6 ) were synthesized via the Wittig–Horner reaction. The polymers were yellow resins with molecular weights of 10,600. The ultraviolet–visible (UV–vis) absorption of 6 (λ_max = 332 or 415 nm) was about 30 nm redshifted from that of poly[(2‐hexyloxy‐5‐methyl‐1,3‐phenylenevinylene)‐alt‐(1,4‐phenylenevinylene)] ( 2 ) but was only 5 nm redshifted with respect to that of poly[(1,3‐phenylenevinylene)‐alt‐(2,5‐dihexyloxy‐1,4‐phenylenevinylene)] ( 1 ). A comparison of the optical properties of 1 , 2 , and 6 showed that substitution on m‐ or p‐phenylene could slightly affect their energy gap and luminescence efficiency, thereby fine‐tuning the optical properties of the poly[(m‐phenylene vinylene)‐alt‐(p‐phenylene vinylene)] materials. The vibronic structures were assigned with the aid of low‐temperature UV–vis and fluorescence spectroscopy. Light‐emitting‐diode devices with 6 produced a green electroluminescence output (emission λ_max ～ 533 nm) with an external quantum efficiency of 0.32%. Substitution at m‐phenylene appeared to be effective in perturbing the charge‐injection process in LED devices. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1820–1829, 2004     

Crosslinkable poly(p‐phenylenevinylene) derivative

To simplify the fabrication of multilayer light‐emitting diodes, we prepared a p‐phenylenevinylene‐based polymer capped with crosslinkable styrene through a Wittig reaction. Insoluble poly(p‐phenylenevinylene) derivative (PPVD) films were prepared by a thermal treatment. The photoluminescence and ultraviolet–visible (UV–vis) absorbance of crosslinked films and noncrosslinked films were studied. We also studied the solvent resistance of crosslinked PPV films with UV–vis absorption spectra and atomic force microscopy. Double‐layer devices using crosslinked PPVD as an emitting layer, 2‐(4‐tert‐butylphenyl)‐5‐phenyl‐1,3,4‐oxadiazole (PBD) in poly(methyl methacrylate) as an electron‐transporting layer, and calcium as a cathode were fabricated. A maximum luminance efficiency of 0.70 cd/A and a maximum brightness of 740 cd/m² at 16 V were demonstrated. A 12‐fold improvement in the luminance efficiency with respect to that of single‐layer devices was realized. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2124–2129, 2004     

Versatile route for tuning optical properties of poly(2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐phenylenevinylene)

In this contribution, we report a versatile method for tuning optical properties of poly(2‐methoxy‐5‐(2′‐ethylhexyloxy)‐1,4‐phenylenevinylene) (MEH‐PPV) in its solution with 1,2‐dichloroethane, accomplished by reacting with pyridinium formate (PF), a volatile organic salt. We can systematically control the positions of absorption and photoluminescent (PL) spectra of MEH‐PPV by adjusting the concentration of PF in the solution. The addition of 10 vol % PF caused a blue‐shift in the absorption spectra by about 65 nm. When the concentration of PF decreased to 0.1 vol %, the blue‐shift occurred to a lesser extent, about 25 nm. The measurements of PL spectra showed similar behaviors. The λ_max shifted from 558 nm to 546 and 552 nm when 10 and 0.1 vol % of PF were added, respectively. The changes of PL colors from orange to yellow and green, respectively, were observed by naked eyes. Structural investigation by nuclear magnetic resonance and Fourier‐transformed infrared spectroscopy indicated that the changes of the optical properties were due to chemical modifications along the main chain and the side groups of MEH‐PPV. These results implied a simple route for engineering the HOMO–LUMO energy gap of MEH‐PPV, which could be utilized in advanced applications such as organic light‐emitting devices and solar cells. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 696–705, 2009     

Polyfluorenes minimally doped with 1,4‐bis(2‐thienyl‐2‐cyanovinyl)benzene chromophore: Their synthesis,characterization, and application to white‐light‐emitting materials

Copolyfluorenes ( PFR1 and PFR2 ), chemically doped with 0.1 and 0.025 mol % 2,5‐dihexyloxy‐1,4‐bis(2‐thienyl‐2‐cyanovinyl)benzene (MR chromophere) were synthesized by the Suzuki coupling reaction. The PFR s were used to fabricate white‐light‐emitting devices through incomplete energy transfer. Because of the low content of the MR chromophore, the optical, thermal, and electrochemical properties of the PFR s were almost identical to those of polyfluorene, except for their photoluminescent (PL) and electroluminescent (EL) properties. The copolymer films showed PL peaks at about 428 and 570 nm originating from fluorene segments and MR chromophores, respectively. Compared with the model compound ( MR ), the polymer chains extended the conjugation length of the MR chromophores and exhibited a 20–48 nm red‐shift in the emission band. In addition, the lower LUMO level of the MR (?3.27 eV) was expected to improve the electron injection. The EL devices [ITO/PEDOT:PSS/ PFR s/Ca (50 nm)/Al (100 nm)] showed a broad emission band, covering the entire visible region, with chromaticity coordinates of (0.36, 0.35) and (0.32, 0.30) for PFR1 and PFR2 devices, respectively. The emission color of the PFR2 device was very similar to that of a pure white light (0.33, 0.33); and the maximal brightness and current efficiency were 3011 cd/m² and 1.98 cd/A, respectively, which surpass those found for polyfluorene devices (1005 cd/m², 0.28 cd/A). A). © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3703–3713, 2008     

Synthesis and characterization of novel germanium‐containing poly(p‐phenylenevinylene) derivatives

Novel blue‐emitting germanium‐containing poly(p‐phenylenevinylene) (PPV) derivatives with well‐defined conjugation lengths were synthesized via Wittig‐condensation polymerizations. The polymers can be color‐tuned by the introduction of various chromophores into the PPV‐based polymer backbones. The photoluminescence (PL) spectra of the polymers, GePVK (containing carbazole moieties), GeMEH (containing dialkoxybenzene moieties), and GePTH (containing phenothiazine moieties), were found to exhibit blue, greenish blue, and green emissions, respectively. GePTH produces more red‐shifted emission than GeMEH and GEPVK, resulting in green emission, and the solution and solid state PL spectra of GePVK consist of almost blue emission. The electroluminescence spectra of GeMEH and GePTH contain yellowy green and yellow colors, respectively. Interestingly, GePVK exhibits white emission with CIE coordinates of (0.33, 0.37) due to electroplex emission in the light‐emitting diodes. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 979–988, 2008     

Synthesis and characterization of indeno[1,2‐b]fluorene‐based white light‐emitting copolymer

An indenofluorene‐based copolymer containing blue‐, green‐, and red light‐emitting moieties was synthesized by Suzuki polymerization and examined for application in white organic light‐emitting diodes (WOLEDs). Tetraoctylindenofluorene (IF), 2,1,3‐benzothiadiazole (BT), and 4,7‐bis(2‐thienyl)‐2,1,3‐benzothiadiazole (DBT) derivatives were used as the blue‐, green‐, and red‐light emitting structures, respectively. The number‐average molecular weight of the polymer was determined to be 25,900 g/mol with a polydispersity index of 2.02. The polymer was thermally stable (T_d = ～398 °C) and quite soluble in common organic solvents, forming an optical‐quality film by spin casting. The EL characteristics were fine‐tuned from the single copolymer through incomplete fluorescence energy transfer by adjusting the composition of the red/green/blue units in the copolymer. The EL device using the indenofluorene‐based copolymer containing 0.01 mol % BT and 0.02 mol % DBT units ( PIF‐BT01‐DBT02 ) showed a maximum brightness of 4088 cd/m² at 8 V and a maximum current efficiency of 0.36 cd/A with Commission Internationale de L'Eclairage (CIE) coordinates of (0.34, 0.32). The EL emission of PIF‐BT01‐DBT02 was stable with respect to changes in voltage. The color emitted was dependent on the thickness of the active polymer layer; layer (～60 nm) too thin was unsuitable for realizing WOLED via energy transfer. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3467–3479, 2009     

Luminescent copolyethers containing isolated 1,4‐distyrylbenzene derivatives backbone and 7‐oxy‐4‐methylcoumarin side group: Synthesis and characterization

Four new copolyethers ( P1 – P4 ) consisting of two isolated emitting chromophores [2,5‐dihexyloxy‐1,4‐distyrylbenzene (HODSB) and 2,5‐dihexyloxy‐1,4‐di(4‐methylenestyryl)benzene (HOMDSB) for P1 and P2 , 2,5‐dihexyl‐1,4‐distyrylbenzene (HDSB) and HOMDSB for P3 and P4 ] in the backbone, in which P2 and P4 further contain electron‐transporting chromophores [7‐oxy‐4‐methylcoumarin (OMC)] in the side chain, were successfully prepared by the Heck coupling reaction. The photoluminescence spectra and quantum yields of the copolymers depended mainly on compositions of the isolated fluorophores. Their highest occupied molecular orbital and lowest unoccupied molecular orbital energy levels were estimated from their cyclic voltammograms. Electrochemical investigations proved that the oxidation started at hole‐transporting DSB segments, whereas reduction began at electron‐transporting OMC groups in P2 and P4 . The electron affinity of P2 and P4 was enhanced by introducing electron‐transporting OMC chromophores. Double‐layer light‐emitting diodes (ITO/PEDOT:PSS / polymer/Al) of P1 and P2 revealed green electroluminescence, and those of P3 and P4 emitted blue light. Moreover, incorporation of OMC side groups effectively reduced turn‐on electric field and enhanced luminance efficiency of the EL devices due to increased electron affinity. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 211–221, 2007     

Optical and electroluminescent properties of novel poly(aryl ether)s with isolated carbazole and p‐quaterphenyl fluorophores

We report the optical and electroluminescent properties of four novel poly(aryl ether)s ( P1 – P4 ) consisting of alternate isolated hole‐transporting [carbazole or 3,6‐bis(styryl)carbazole] and electron‐transporting [dicyano‐p‐quaterphenyl or bis(trifluoromethyl)‐p‐quaterphenyl] fluorophores. The photoluminescence (PL) spectra of the four polymeric films show maximum peaks around 407–413 nm for P1 , P2 and 442–447 nm for P3 , P4 . The PL spectra of P1 ～ P4 are dependent on the composition of the two isolated fluorophores. According to the observation of relative quantum yield in poor solvent (cyclohexane), P2 containing more bulky trifluoromethyl groups in p‐quaterphenyl segments prevented aggregate quenching processes more than P1 . Compared with P1 and P2 with carbazole segments, P3 and P4 with 3,6‐bis(styryl)carbazole segments exhibited less interchain interaction and a low threshold electric field in a single‐layer device. The p‐quaterphenyl and carbazole [or 3,6‐bis(styryl)carbazole] segments were regarded as electron‐transporting and hole‐transporting units, respectively, in the single‐layer light‐emitting diodes (Al/ P1 – P4 /ITO). In the double‐layer device (ITO/MEH‐PPV/ P2 /Al), the maximum luminance was doubled, and the threshold electric fields diminished because P2 functioned as an electron‐transporting and hole‐blocking layer. Furthermore, the voltage‐tunable multicolor emission from orange to green was observed. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 333–340, 2004     

Luminescent copoly(aryl ether)s with new electron‐transporting bis(3‐(trifluoromethyl)phenyl)‐1,3,4‐oxadiazole or bis(3‐(trifluoromethyl)phenyl)‐4‐(4‐hexyloxyphenyl)‐4H‐1,2,4‐triazole segments

To investigate the effect of trifluoromethyl groups in enhancing electron affinity of aromatic oxadiazole and triazole chromophores, we prepared four new copoly(aryl ether)s ( P1 – P4 ) consisting of bis(3‐(trifluoromethyl) phenyl)‐1,3,4‐oxadiazole (ETO) or bis(3‐(trifluoromethyl)phenyl)‐4‐(4‐hexyloxyphenyl)‐4H‐1,2,4‐triazole (ETT) segments and hole‐transporting segments [2,5‐distyrylbenzene (HTB) or bis(styryl)fluorine (HTF)]. Molecular spectra (absorption and photoluminescence) and cyclic voltammetry were used to investigate their optical and electrochemical properties. The emissions of P1 – P4 are dominated by the hole‐transporting fluorophores with longer emissive wavelengths around 442–453 nm via efficient excitation energy transfer. The highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels of P1 – P4 , estimated from electrochemical data, are ?5.15, ?5.18, ?5.30, ?5.27, ?3.39, ?3.49, ?3.36, and ?3.48 eV, respectively. The LUMO levels of ETO and ETT segments are significantly reduced to ?3.39～?3.36 eV and ?3.48～?3.49 eV, respectively, as compared with ?2.45 eV of P5 containing a 2,5‐diphenyl‐1,3,4‐oxadiazole segment. Moreover, electron and hole affinity can be enhanced simultaneously by introducing isolated hole‐ and electron‐transporting segments in the backbone. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 5900–5910, 2004     

Luminescent copoly(aryl ether)s consisting of alternate oxadiazole and 1,4‐distyrylbenzene derivatives: Synthesis and characterization

In an effort to decrease the electron‐injection barrier from the anode electrode, four copoly(aryl ether)s ( P1 – P4 ), consisting of alternating isolated electron‐transporting [2,5‐diphenyl‐1,3,4‐oxadiazole for P1 and P3 and 5,5′‐diphenyl‐2,2′‐p‐(2,5‐bishexyloxyphenylene)‐bis‐1,3,4‐oxadiazole for P2 and P4 ] and emitting chromophores (1,4‐distyryl‐2,5‐dihexyloxybenzene for P1 and P2 and 1,4‐distyryl‐2,5‐dihexylbenzene for P3 and P4 ), have been synthesized by the nucleophilic displacement reaction between bisfluoride and bisphenol monomers. They are basically amorphous materials with 5% weight‐loss temperature above 400 °C. The photoluminescence spectra and quantum yields of these copolymers are dependent on the compositions of the two isolated fluorophores. The highest occupied molecular orbital and lowest unoccupied molecular orbital energy levels of these copolymers have been estimated from their cyclic voltammograms. All the observations directly prove that the oxidation starts at the hole‐transporting segments. The electron affinity can be enhanced by the introduction of isolated electron‐transporting segments that lead to a charge‐injection balance. Single‐layer light‐emitting diodes (Al/ P1 – P4 /ITO glass) have been fabricated. P1 and P2 reveal blue electroluminescence, and P3 and P4 reveal purple‐blue electroluminescence. Moreover, the incorporation of bisoxadiazole units increases the electron affinity and reduces the turn‐on electric field better than one oxadiazole unit. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2765–2777, 2003     

Synthesis and electrochemical and electroluminescent properties of N‐phenylcarbazole‐substituted poly(p‐phenylenevinylene)

An N‐phenylcarbazole‐containing poly(p‐phenylenevinylene) (PPV), poly[(2‐(4′‐carbazol‐9‐yl‐phenyl)‐5‐octyloxy‐1,4‐phenylenevinylene)‐alt‐(2‐(2′‐ethylhexyloxy)‐5‐methoxy‐1,4‐phenylenevinylene)] (Cz‐PPV), was synthesized, and its optical, electrochemical, and electroluminescent properties were studied. The molecular structures of the key intermediates, the carbazole‐containing boronic ester and the dialdehyde monomer, were crystallographically characterized. The polymer was soluble in common organic solvents and exhibited good thermal stability with a 5% weight loss at temperatures above 420 °C in nitrogen. A cyclic voltammogram showed the oxidation peak potentials of both the pendant carbazole group and the PPV main chain, indicating that the hole‐injection ability of the polymer would be improved by the introduction of the carbazole‐functional group. A single‐layer light‐emitting diode (LED) with a simple configuration of indium tin oxide (ITO)/Cz‐PPV (80 nm)/Ca/Al exhibited a bright yellow emission with a brightness of 1560 cd/m² at a bias of 11 V and a current density of 565 mA/cm². A double‐layer LED device with the configuration of ITO/poly(3,4‐ethylenedioxy‐2,5‐thiophene):poly (styrenesulfonic acid) (60 nm)/Cz‐PPV (80 nm)/Ca/Al gave a low turn‐on voltage at 3 V and a maximum brightness of 6600 cd/m² at a bias of 8 V. The maximum electroluminescent efficiency corresponding to the double‐layer device was 1.15 cd/A, 0.42 lm/W, and 0.5%. The desired electroluminescence results demonstrated that the incorporation of hole‐transporting functional groups into the PPVs was effective for enhancing the electroluminescent performance. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 5765–5773, 2005     

Efficient blue‐green‐emitting poly[(5‐diphenylamino‐1,3‐phenylenevinylene)‐alt‐(2,5‐dihexyloxy‐1,4‐phenylenevinylene)] derivatives: Synthesis and optical properties

New poly(phenylene vinylene) derivatives with a 5‐diphenylamino‐1,3‐phenylene linkage (including polymers 2 , 3 , and 5 ) have been synthesized to improve the charge‐injection properties. These polymers are highly photoluminescent with fluorescent quantum yields as high as 76% in tetrahydrofuran solutions. With effective π‐conjugation interruption at adjacent m‐phenylene units, chromophores of different conjugation lengths can be incorporated into the polymer chain in a controllable manner. In polymer 2 , the structural regularity leads to an isolated, well‐defined emitting chromophore. Isomeric polymer 3 of a random chain sequence, however, allows the effective emitting chromophores to be joined in sequence by sharing a common m‐phenylene linkage (as shown in a molecular fragment). Double‐layer light‐emitting‐diode devices using 2 , 3 , and 5 as emitting layers have turn‐on voltages of about 3.5 V and produce blue‐green emissions with peaks at 493, 492, and 482 nm and external quantum efficiencies up to 1.42, 0.98, and 1.53%, respectively. In comparison with a light‐emitting diode using 2 , a device using 3 shows improved charge injection and displays increased brightness by a factor of ～3 to 1400 cd/m² at an 8‐V bias. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2307–2315, 2006     

Synthesis,photophysics, and electroluminescent performance of stable blue‐light‐emitting copoly(9,9‐diarylfluorene)s

A series of fluorene derivatives containing nonsymmetric and bulky aromatic groups at C‐9 position were synthesized and used for the preparation of blue‐light‐emitting copolyfluorenes ( P1 – P4 ) by the Suzuki coupling polycondensation. The copolymers were characterized by molecular weight determination, elemental analysis, differential scanning calorimeter, thermogravimetric analysis, absorption and emission spectroscopy, cyclic voltammetry, and differential pulse voltammetry. Their decomposition temperatures and glass transition temperatures are 423–441 °C and >120 °C, respectively. In film state, the copolyfluorenes exhibit blue photoluminescence at 425–450 nm, which remains almost unchanged after annealing at 200 °C in air for 60 min. Polymer light‐emitting diodes [ITO/PEDOT:PSS/ P1 – P4 /Ca(50 nm)/Al(100 nm)] show stable blue‐light emission under device operation with the CIE co‐ordinates being between (0.16, 0.07) and (0.17, 0.09). The light‐emitting diodes devices from P1 and P3 containing electron‐deficient oxadiazole units display enhanced performance, with the maximum brightness and maximum current efficiency being (4510 cd/m² and 2.40 cd/A) and (2930 cd/m², 1.19 cd/A), respectively. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 2821–2834, 2009     

Novel Spectrally Stable Saturated Blue‐Light‐Emitting Poly[(fluorene)‐co‐(dioctyldibenzothiophene‐S,S‐dioxide)]s

Novel poly[(fluorene)‐co‐(2,8‐dioctyldibenzothiophene‐S,S‐dioxide‐3,7‐diyl)]s were synthesized. The octyl group on the 2,8‐dioctyldibenzothiophene‐S,S‐dioxide (DOSO) unit improved the solubility of the polymers and broadened the optical band gap from 2.95 to 3.20 eV as the content of DOSO unit increases. The electroluminescence (EL) spectra of polymers show CIE coordinates around (0.16, 0.07) independent of the ratio of DOSO units in the polymers, owing to the ICT and steric hindrance dual‐function. A high efficiency of 3.1 cd · A⁻¹ (EQE = 3.9%) was obtained with the configuration of ITO/PEDOT:PSS/polymer/Ba/Al. The results indicate that PF‐3,7DOSOs could be a promising candidate for saturated blue‐emitting polymers with spectral stability and high efficiency.