可溶性聚对苯乙炔的合成及其电致发光性能

采用紫外－可见光谱跟踪用直接聚合法制备可溶性的聚对苯乙炔衍生物的反应过程,结果表明反应仍然经历了生成前聚物的过程。控制反应条件使聚合反应首先生成前聚物,在前聚物烯化反应阶段加入起增溶作用的长链醇,得到了具有良好的溶解性的、主链中含非共轭链段的聚对苯乙炔衍生物。用该聚合物制备的电致发光器件,在５－６Ｖ电压驱动下发光,发光峰位于５８０ｎｍ左右。     

可溶性聚对苯乙炔衍生物的合成

聚对苯乙炔（ＰＰＶ）具有独特的光电性能,经强氧化剂掺杂后是一类重要的导电材料［１］,而且具有良好的非线性光学（ＮＬＯ）性质［２］,也是目前性能最好的高分子电致发光材料［３,４］．可溶性的ＰＰＶ衍生物有望在显示领域广泛应用,从而成为电致发光领域研究的新...     

二苯乙炔类液晶的合成

以碘代烷基苯（或联苯）与烷基苯乙炔为中间体，采用二价镍为催化剂的方法合成了二苯乙炔类液晶化合物。其相变过程通过差热分析测试，该类化合物表现出优良的液晶性能。     

聚（2，5－二甲氧基对苯乙炔）的可溶性前聚物合成及表征

研究了合成聚（２，５－二甲氧圣对苯乙炔）的有机可溶性前聚物的反应条件与单体转化率和前聚物产率的关系。实验结果表明：ＮａＯＨ是聚合反应的有效引发剂。适宜的反应条件为：单体与ＮａＯＨ摩尔比为１：１，单体浓度０．０５～０．２ｍｏｌ／Ｌ聚合时间２ｈ，温度低于５℃。正已烷、石油醚作为有机提取剂可有效提高前聚物产率，用ＩＲ、ＵＶ－Ｖｉｓ、￣１ＨＮＭＲ、ＴＧＡ和ＤＳＣ对前聚物进行了表征。     

4,4′-二乙炔二苯甲烷与苯乙炔的共聚及共聚物的表征研究

 本文做了4,4′-二乙炔二苯甲烷的本体热均聚和催化均聚,并用(Ph₃P)₂PdCl₂为催化剂做了4,4′-二乙炔二苯甲烷与苯乙炔的共聚,对均聚和共聚物中的不溶不熔组分测定了密度、溶胀度、Huggins参数以及交联点间的平均分子量M_c。实验表明,该交联聚合物的最良溶剂是四氢呋喃,溶度参数为9.9ca1^0.5。cm^-1.5,当用四氢呋喃为溶剂时的Huggins参数为0.34,并且在单体摩尔比中4,4′-二乙炔二苯甲烷用量越多,溶胀度越小,交联度越大。红外光谱分析表明,所有均聚及共聚物都为反式结构。     

对苯醌二亚胺与对苯乙炔共聚物的金属配合物催化法合成与表征

在金属配合物的存在下,通过N,N′-二氯对苯醌二亚胺与1,4-二炔基-2,5-二（烷氧基）苯共聚,得到了一系列新型交替共聚物聚[N,N′-对苯醌二亚胺-1,4-二炔基-2,5-二（烷氧基）苯]（PAn-PPE）。采用FT-IR、1H-NMR、GPC、XRD、UV-Vis、PL、TGA等测试手段对共聚物的化学结构和性能进...     

4,4′-二乙炔二苯甲烷与苯乙炔的共聚及共聚物的表征研究

本文做了4,4′-二乙炔二苯甲烷的本体热均聚和催化均聚,并用(Ph_3P)_2PdCl_2为催化剂做了4,4′-二乙炔二苯甲烷与苯乙炔的共聚,对均聚和共聚物中的不溶不熔组分测定了密度、溶胀度、Huggins参数以及交联点间的平均分子量(?)_c。实验表明,该交联聚合物的最良溶剂是四氢呋喃,溶度参数为9.9ca1~0.5。cm~(-1.5),当用四氢呋喃为溶剂时的Huggins参数为0.34,并且在单体摩尔比中4,4′-二乙炔二苯甲烷用量越多,溶胀度越小,交联度越大。红外光谱分析表明,所有均聚及共聚物都为反式结构。     

脱氯化氢法合成聚(2,5-二乙氧基对苯乙炔)

聚对苯乙炔（ＰＰＶ）及其衍生物具有独特的光电性能，经强氧化剂掺杂后是一类重要的导电材料［１］，而且具有良好的非线性光学（ＮＬＯ）性质［２］，也是目前为止性能最好的电致发光材料［３］，因而ＰＰＶ及其衍生物的合成成为电致发光领域研究的热点之一。目前国内外...     

聚(2,5-二烷氧基对苯乙炔)的合成新方法

二烷氧基苯;化学脱氢反应;聚(2;5-二烷氧基对苯乙炔)的合成新方法     

含磺酸钠基的杂萘联苯聚芳醚砜酮的合成与表征

对4,4'-二氯二苯砜进行磺化改性制得磺化二氯二苯砜,不同比例的4,4'-二氯二苯砜和磺化二氯二苯砜与含二氮杂萘酮结构的类双酚单体(DHPZ)及4,4'-二氟二苯酮共聚合制得不同磺化度的磺化聚醚砜酮.对磺化单体及聚合物进行了IR和¹HNMR表征,并研究了聚合物的溶解性和成膜性能.     

聚甲基丙烯酸甲酯-丙烯酸酰胺嵌段共聚物的合成与表征

引发剂;苯胺;聚甲基丙烯酸甲酯-丙烯酸酰胺嵌段共聚物的合成与表征     

聚环氧氯丙烷的合成与表征

环氧丙烷-三氯化铁、环氧氯丙烷-二乙基氯化铝和铝卟啉-环氧氯丙烷体系是合成分子量为10~4数量级晶态和10~5数量级非晶态聚环氧氯丙烷的比较理想的体系。利用合成产物的分级试样确定了非晶态聚环氧氯丙烷的Mark-Houwink方程。     

聚对苯基苯酚取代磷腈的合成与表征

环状三聚六氯化磷腈在α-氯代萘中开环聚合得到聚氯化磷腈.后者与对苯基苯酚钠反应合成了标题聚合物.测定了该聚合物的IR、~1H NMR谱.GPC估计其数均分子量为6×10~4.扭辫分析表明,该聚合物的玻璃化转变温度与粘流温度分别为0℃和130℃,硫化温度为210℃.     

Synthesis and Characterization of Folate‐decorated Cobalt Ferrite Nanoparticles Coated with Poly(Ethylene Glycol) for Biomedical Applications

A stable and biocompatible targeting complex CFNs@PEG‐FA is developed. The initially synthesized cobalt ferrite nanoparticles (CFNs) were treated with poly(ethylene glycol) (PEG) in order to improve biocompatibility of the CFNs. Citric acid (CA) was used as the coupling agent, which made PEG to bond with the CFNs. CFNs@PEG were conjugated with folic acid (FA) to synthesize CFNs@PEG‐FA, which was capable of targeting the FA receptor positive (FAR+) cancer cells. Synthesized nanoparticles were physically and chemically analyzed using EDX, FT‐IR, XRD, TGA, FESEM, TEM, DLS, and VSM. The biocompatibility of CFNs@PEG‐FA was assessed in vitro on HSF 1184 (human skin fibroblast cells) and HeLa (human cervical cancer cell, FAR+) using MTT assay and AO/EB staining florescence method. High level of CFNs@PEG‐FA binding to HeLa was confirmed through quantitative and qualitative in vitro targeting studies. Results show that CFNs@PEG‐FA can be a potential biomaterial for use in biomedical trials, especially magnetic hyperthermia. The findings through this in vitro study are to be compared in future with those of in vivo studies.     

Synthesis and Enzymatic Degradation of Nylon 66 Copolymers with Poly(Ethyleneglycol)s

Abstract

Nylon 66 (N66) copolymers were prepared by melt polycondensation of adipic acid and hexamethylenediamine with 5–80 mol% poly(ethylene glycol) (PEG), where the molecular weight (MW) of PEG was 200–1000. The reduced specific viscosity of the copolymers was increased by the copolymerization. The crystallinity and melting temperature (T _m) of N66 components decreased with increasing PEG content, but T _m depression of copolymers at the same mole content decreased with increasing MW of PEG, suggesting that the copolymer structures are not of the random type but of the block type at the higher MW of PEG. The water absorption increased with increasing PEG content, and its increase was much higher at the higher MW of PEG. The enzymatic degradation was estimated by the weight loss of copolymer films in the buffer solution with and without a lipase at 37°C. The weight loss was enhanced appreciably by the presence of a lipase, and increased abruptly at higher PEG content, which was correlated to water absorption and the concentration of ester linkages. The enzymatic degradation of these N66 copolymers was much higher than that of previously reported PET copolymers with PEG. The abrupt increase of weight loss by alkali hydrolysis was fairly comparable to that of water absorption.     

新型聚原酸酯共聚物的合成及性能研究

以二聚甘油为原料,经过酯交换及氨基脱保护反应合成了一种两端含氨基的环状原酸酯新单体。该单体与辛二酸/十二烷二酸活性酯缩聚得到两种新的疏水性聚原酸酯共聚物POEAd-1和POEAd-2,其数均分子量分别由凝胶渗透色谱(GPC)测得为1.24×104及1.81×104,分散度(PDI)分别为1.59及1.93。热失重分析法证实POEAd-1和POEAd-2具有较高的热稳定性能,其起始降解温度分别可达198.5℃及202.5℃。溶血试验和MTT细胞毒性试验表明,POEAd-1和POEAd-2均具有良好生物相容性,作为一种潜在的生物医用材料,在药物缓控释领域将具有广阔的应用前景。     

Synthesis and Characterization of Poly(ether-block-amide) Membranes

Poly(ether-block-amide) membranes were made via casting a solution on a nonsolvent (water) surface. In this research, effects of different parameters such as ratio of solvent mixture (n-butanol/isopropanol), temperature, composition of coagulation bath (water) and polymer concentration, on quality of the thin film membranes were studied. The mechanism of membrane formation involves solution spreading, solvent–nonsolvent exchange, and partial evaporation of the solvent steps. Solvent- nonsolvent exchange is the main step in membrane formation and determines membrane morphology. However, at higher temperature of polymeric solution greater portion of solvent evaporates. The results showed that type of demixing process (mutual affinity between solvent and nonsolvent) has important role in film formation. Also, addition of solvent to the nonsolvent bath is effective on membrane morphology. The film quality enhances with increasing isopropanol ratio in the solvent mixture. This behavior can be related to increasing of solution surface tension, reduction of interfacial tension between solution and nonsolvent and delayed solvent-nonsolvent demixing. Uniform films were made at a temperature rang of 60–80 °C and a polymer concentration of 4–7 wt%. Morphology of the membranes was investigated with scanning electron micrograph (SEM). Pervaporation of ethyl butyrate/water mixtures was studied using these membranes and high separation performance was achieved. For ethyl butyrate/water mixtures, It was observed that both permeation flux and separation factor increase with increasing ethyl butyrate content in the feed. Increasing temperature in limited range studied resulted in decreasing separation factor and increasing permeation flux.     

聚四氢呋喃三元醇的合成及表征

合成了一种新的三元引发剂[C₂H₅C(CH₂OCH₂CH₂CO+ClO₄^-)₃],并用于制备聚四氢呋喃三元醇.用¹HNMR,FTIR和GPC法对聚合物的结构进行了表征.结果表明,产物中环状齐聚物的含量极低.对聚合物水解产物的分子量及分子量分布测定结果表明,产物为预期的三元醇,聚合反应过程中链转移可以忽略,聚合物的分子量可控.     

聚(乙烯基四唑-co-丙烯酸)的合成与表征

以聚丙烯腈为原料,首先通过部分腈基的[3+2]合环反应转化为聚(乙烯基四唑-co-丙烯腈)[Poly(VT-co-AN)],再通过碱性水解反应将剩余的腈基转化为羧基,合成出聚(乙烯基四唑-co-丙烯酸)[Poly(VT-co-AA)]。 采用傅里叶红外变换光谱仪(FT-IR)、核磁共振碳谱仪(¹³C NMR)、酸碱滴定等方法对Poly(VT-co-AN)和[Poly(VT-co-AA)的结构进行了表征,结果表明,Poly(VT-co-AN)的分子链中含有腈基、四唑基团和部分羧基,四唑基团的含量为68.6%,与酸碱滴定法测定的四唑基团的含量相近,[Poly(VT-co-AA)中含有四唑基团和羧基,不含有腈基,酸值高于Poly(VT-co-AN),四唑基团的含量为67.6%,与叠氮化钠与聚丙烯腈的摩尔比相近。 热失重分析结果显示[Poly(VT-co-AA)的热分解速率加快,在270~285 ℃的温度区间内分解完全。