Shape‐memory effect in hyperbranched poly(ethyleneimine)‐modified epoxy thermosets

A series of shape‐memory epoxy thermosets were synthesized by crosslinking diglycidyl ether of bisphenol A with mixtures of commercially available hyperbranched poly(ethyleneimine) and polyetheramine. Thermal, mechanical and shape‐memory properties were studied and the effect on them of the content and structure of the hyperbranched polymer was discussed. Measurements showed that the glass transition temperature can be tailored from 60 °C to 117 °C depending on the hyperbranched polymer content, and all formulations showed an appropriate glassy/rubbery storage modulus ratio. Shape‐memory programming was carried out at TgE′ given the excellent mechanical properties of the materials, with maximum stress and failure strain up to 15 MPa and 60%, respectively. The resulting shape‐memory behavior was excellent, with maximum shape recovery and shape fixity of 98% as well as a fast shape‐recovery rate of 22%/min. The results show that hyperbranched poly(ethyleneimine) as a crosslinking agent can be used to enhance mechanical and shape‐memory properties with different effects depending on the crosslinking density. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2015 , 53, 924–933     

Biodegradable thermoset shape‐memory polymer developed from poly(β‐amino ester) networks

The purpose of this study was to develop a degradable thermoset shape‐memory polymer from poly(β‐amino ester) (PBAE) networks. PBAE was chosen to be the crosslinker as it is biodegradable and has been projected as a potential material for biomedical applications. The low glass transition temperature of PBAE was increased to a biomedically relevant range using methyl methacrylate and methyl acrylate as the linear chain builders. The thermo‐mechanical properties of the networks were tailored such that they exhibited onset of glass transition temperature in between the room temperature (22 °C) and the body temperature (37 °C). Free‐strain recovery tests under heating and isothermal conditions were performed to quantify shape‐memory behavior. Testing showed that sampled programmed at 10 °C initiated deformation recovery at a lower temperature and a faster rate as compared to programming at 60 °C. Higher thermal conductivity of water enabled the samples to recover faster in water than in air. Samples with higher PBAE crosslinking densities exhibited higher normalized mass loss under regular and accelerated conditions. The amount of water absorption in the networks also increased with the crosslinker concentration independent of the testing conditions. © 2012 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2012     

Poly(methacrylic acid)‐grafted clay–thermoplastic elastomer composites with water‐induced shape‐memory effects

Composites with excellent water‐induced shape‐memory effects (SMEs) were successfully synthesized by first using clay as the SME‐activating phase and thermoplastic polyurethane (TPU) as the matrix. Naturally abundant clay was grafted with poly(methacrylic acid) (PMAA) to improve particle interactions, which allowed for the formation of strong percolation networks in the composites, determined by swelling tests and dynamic mechanical analysis in combination with theoretical modeling. This led to significant improvements of the polymer modulus and high water absorptions, causing reversible modulus changes of up to 30 times from the wet to the dry condition. The results from cyclic wetting‐drying‐stretching tests showed the TPU–clay composite containing 10.4 vol % PMAA‐grafted clay exhibited the best SMEs among the composites investigated, with the shape fixity and shape recovery ratios being 82% and 91%, respectively. Besides SMEs, these new polymer–clay composites were also pH‐sensitive and mechanically adaptive upon exposure to water. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013 , 51, 1513–1522     

Synthesis of a new multiarm star polymer based on hyperbranched poly(styrene) core and poly(ε‐caprolactone) arms and its use as reactive modifier of epoxy thermosets

A well‐defined multiarm star copolymer poly(styrene)‐b‐poly(ε‐caprolactone) (PSOH‐b‐PCL) with an average number of PCL arms per molecule of 60 has been prepared. 4‐Chloromethyl styrene (4‐CMS) was polymerized by means of atom transfer radical polymerization (ATRP) to obtain a hyperbranched poly(styrene) with chlorines as terminal groups. Subsequently, chlorines were substituted by reaction with diisopropanolamine (DIPA) to give the hydroxyl‐ended derivative. Finally, the hydroxyl‐ended hyperbranched poly(styrene) has been used as a macroinitiator core to polymerize ε‐caprolactone by means of cationic ring‐opening polymerization so as to obtain the star copolymer. In a second step, PSOH‐b‐PCL was used as reactive modifier of diglycidylether of bisphenol A formulations cured by 1‐methyl imidazole (1‐MI) obtaining nanostructured thermosets. The curing process was studied by dynamic scanning calorimetry and Fourier transform infrared spectroscopy (FTIR). By rheometry, the effect of this new polymer topology on the complex viscosity (η*) of the reactive mixture and on the gelation process was also analyzed. The thermomechanical characteristics of the modified materials were determined. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis of backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s through proton‐transfer polymerization

Stimuli‐responsive hyperbranched polymers have attracted great attention in recent years because of their wide applications in biomedicine. Through proton‐transfer polymerization of triethanolamine and 1,2,7,8‐diepoxyoctane with the help of potassium hydride, a series of novel backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s were prepared successfully in one‐pot. The degrees of branching of the resulting polymers were at 0.40–0.49. Turbidity measurements revealed that hyperbranched poly(amine‐ether)s exhibited thermo and pH dual‐responsive properties in water. Importantly, these responsivities could be readily adjusted by changing the polymer composition as well as the polymer concentration in aqueous solution. Moreover, in vitro evaluation demonstrated that hyperbranched poly(amine‐ether)s showed low cytotoxicity and efficient cell internalization against NIH 3T3 cell lines. These results suggest that these backbone thermo and pH dual‐responsive hyperbranched poly(amine‐ether)s are promising materials for biomedicine. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Shape‐memory polymer networks from oligo(ϵ‐caprolactone)dimethacrylates

Polymer networks showing a thermally induced shape‐memory effect were prepared through the crosslinking of oligo(?‐caprolactone)dimethacrylates under photocuring with or without an initiator. The influence of the molecular weight of the oligo(?‐caprolactone)dimethacrylates and the initiator concentration on the macroscopic properties of the polymer networks was investigated. The isothermal and nonisothermal crystallization behavior of the polymer networks was evaluated as a basic principle of the functionalization process. Shape‐memory properties such as the strain fixity and strain recovery rate were quantified with cyclic thermomechanical tensile experiments for different maximum elongations. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 1369–1381, 2005     

Network structure and thermomechanical properties of hybrid DGEBA networks cured with 1‐methylimidazole and hyperbranched poly(ethyleneimine)s

The use of commercially available hyperbranched poly(ethyleneimine)s (Lupasol?, BASF) as polymeric modifiers in diglycidyl ether of bisphenol A thermosetting formulations using 1‐methylimidazole (MI) as anionic initiator has been studied. Poly(ethyleneimine)s can get incorporated into the network structure by condensation of amine and epoxy groups. The excess, over‐stoichiometric epoxy groups can undergo anionic homopolymerization initiated by MI. The thermal, dynamomechanical, and mechanical properties of the resulting materials have been determined using DSC, thermomechanical analysis (TMA), dynamomechanical analysis (DMA), and mechanical testing. The effect of the different amine modifiers on the MI networks, determined by their structure, is complex. Low initiator content and high molecular weight modifiers create significant mobility restrictions, which have a strong effect on the glass transition temperature and the apparent crosslinking density of the cured materials. © 2012 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2012     

Optimization of the shape memory effect in shape memory polymers

In this article, we show that given a thermoresponsive shape memory polymer, it is possible to alter a number of its properties, such as the recovery temperature, shape fixity ratio, maximum recovery stress, and final recovery stress (and even a right combination of some of them, e.g., the maximum recovery stress and final recovery stress), simply by means of selecting the programming temperature to achieve optimized performance. Some concerns for the implementation in real engineering practice are also discussed. Although the focus is on the case of a fixed maximum strain in programming, alternative programming approaches can be investigated in a similar way for optimized performance as well. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Preparation of modified multi‐walled carbon nanotubes as a reinforcement for epoxy shape‐memory polymer composites

Effectively improving the mechanical properties and thermal resistance of epoxy shape‐memory polymers (ESMPs) without affecting their shape‐memory performance is necessary to expand these polymers in practical applications. In this article, modified multi‐walled carbon nanotubes (MWCNTs) were prepared and used as efficient reinforcement for enhancing the comprehensive properties of ESMPs. Increases of nearly 289% to 444% for impact strength and 112% to 184% for tensile force were obtained by adding only 0.1 to 1 wt% epoxy‐modified MWCNTs. The addition of unmodified and carboxyl‐modified MWCNTs was also investigated but showed less impact on the mechanical properties of the ESMPs than epoxy‐modified MWCNTs. Thermogravimetry analysis (TGA) and dynamic mechanical analyses (DMA) showed that less than 1 wt% modified MWCNTs can enhance the heat resistance of ESMPs greatly. Although the shape recovery time for composite materials increased upon adding the MWCNTs, the entire recovery time was still less than 1 minute, and the shape recovery rate was relatively high, nearly 100%.     

Multiarm star poly(glycidol)‐block‐poly(ε‐caprolactone) of different arm lengths and their use as modifiers of diglycidylether of bisphenol a thermosets

Well‐defined multiarm star copolymers, hyperbranched poly(glycidol)‐b‐poly(ε‐caprolactone), with an average of 100–110 arms per molecule and a molecular weight of arms of 3000 g/mol (PGOH‐b‐PCL₃₀) and 1000 g/mol (PGOH‐b‐PCL₁₀) were synthesized by cationic ring‐opening polymerization of ε‐caprolactone from a poly(glycidol) core and used to modify diglycidylether of bisphenol A formulations. The curing process, studied by dynamic scanning calorimetry, was only slightly retarded when PGOH‐b‐PCL_x were added to the formulation. By rheometry, the effect of this new topology and the arm length on the complex viscosity (η*) and gelation of the reactive mixture was analyzed in detail. The addition of these new reactive modifiers decreases the global shrinkage and increases the conversion at gelation. In addition, the modified thermosets have an improved reworkability. The homogeneity of pure DGEBA and modified thermosets was proved by dynamic thermomechanical analysis and electronic microscopy (FESEM). Addition of star‐like structures led to a more toughened fracture of the thermoset in comparison to pure DGEBA. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Organic‐montmorillonite modified shape memory epoxy composite

A series of organic‐montmorillonite (OMMT) modified shape memory epoxy (SMEP) composites were prepared for the purpose of application on space deployable structures. Tensile test, dynamic mechanical analysis (DMA), X‐ray diffraction (XRD), scanning electron microscope (SEM), and fold‐deploy shape memory test methods were used to characterize the mechanical, structure, and shape memory properties of these materials. The results showed addition of OMMT could improve the composites' toughness, tensile strength, transition temperature, and shape recovery speed, while shape recovery ratio was unaffected. Composite with 3wt%. OMMT had the optimum combination property. It could fully recover its original shape in about 2 min at 185°C under the maximum bending angle of 180°. Its elongation at break and tensile strength were increased by 835 and 17.4%, respectively, compared to that of neat SMEP. The transition temperature also slightly increased. Copyright © 2010 John Wiley & Sons, Ltd.     

Synthesis of imidazole‐terminated hyperbranched polymers with POSS‐branching points and their pH responsive and coordination properties

An imidazole‐terminated hyperbranched polymer with octafunctional POSS branching units denoted as POSS‐HYPAM‐Im was prepared by the polymerization of excess amounts of tris(2‐aminoethyl)amine with the first‐generation methyl ester‐terminated POSS‐core poly(amidoamine)‐typed dendrimer, reacting with methyl acrylate, and ester‐amide exchange reaction with 3‐aminopropylimidazole. The imidazole‐terminated hyperbranched poly(amidoamine) denoted as HYPAM‐Im was also synthesized with 1‐(3‐aminopropyl)imidazole from a methyl ester‐terminated hyperbranched poly(amidoamine) by the ester‐amide exchange reaction. The transmittance of the POSS‐HYPAM‐Im solution drastically decreased when the solution pH was greater than 8.2. On the other hand, the transmittance of the HYPAM‐Im solution gradually decreased when the solution pH at 8.5 and was greater than 9. Spectrophotometric titrations of the hyperbranched polymer aqueous solutions with Cu²⁺ ions indicated the variation of the coordination modes of POSS‐HYPAM‐Im from the Cu²⁺–N₄ complex to the Cu²⁺–N₂O₂ complex and the existence of the only one complexation mode of Cu²⁺–N₄ between Cu²⁺ ion and HYPAM‐Im with increasing the concentrations. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2695–2701     

Synthesis and characterization of new poly(ethyleneimine)‐g‐poly(methyl methacrylate) star‐block copolymers with hyperbranched cationic core

Hyperbranched polyethyleneimine (hb‐PEI) is used as polymeric scaffold to synthesize new PEI‐g‐polymethylmethacrylate (PEI‐g‐PMMA) block copolymers, consisting of a hyperbranched, partially quarternized cationic core, and PMMA‐arms. The arms are grafted to the PEI scaffold by means of the “grafting to” method. Ammonium groups, covalently bond to the hyperbranched core, provide good adhesion to negatively charged surfaces, even in case of low‐surface charges. The PMMA strands provide compatibility of the macromolecules to PMMA matrices, hence generating potential dispersants, and compatibilizers for PMMA. A peculiar association behavior in organic solution is observed as supported by dynamic light scattering and DOSY measurements. First evidences of the applicability of the macromolecules as dispersants to prepare PMMA‐nanocomposites are given. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 3700–3715     

Thermo‐/moisture‐responsive shape‐memory effect of poly(2‐ethyl‐2‐oxazoline) networks

In this work, poly(2‐ethyl‐2‐oxazoline) (PEtOx) is crosslinked to realize a moisture‐ and thermo‐responsive shape‐memory polymer. The obtained PEtOx networks exhibit excellent shape‐memory properties with storable strains of up to 650% and recovery values of 100% over at least 10 shape‐memory cycles. The trigger temperature (T_trig) of 68 °C of a PEtOx network at a relative humidity (RH) of 0% decreases with increasing moisture and equals room temperature at an RH of 40%. Thus, programmed PEtOx networks trigger sensitively on a certain temperature/moisture combination and, further, can be programmed as well as triggered at room temperature exclusively by varying humidity. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019 , 57, 1053–1061     

Reduction‐cleavable hyperbranched polymers with limited intramolecular cyclization via click chemistry

In this contribution, we present new reduction‐cleavable hyperbranched disulfide bonds‐containing poly(ester triazole)s with limited intramolecular cyclization, which can be synthesized by the Cu(I)‐catalyzed azide–alkyne cycloaddition (CuAAC) of A₂ monomer of dipropargyl 3,3′‐dithiobispropionate and B₃ monomer of tris(hydroxymethyl)ethane tri(4‐azidobutanoate). The hyperbranched poly(ester triazole)s possess numerous terminal groups and weight‐average molecular weight up to 20,400 g mol^?1 with a polydispersity index in the range 1.57–2.17. The CuAAC introduces rigid triazole units into the backbones of hyperbranched poly(ester triazole)s and reduces intramolecular cyclization, which is proved by topological analysis and ¹H NMR spectroscopy. The disulfide bonds on backbones endow the reduction‐cleavable feature to the hyperbranched poly(ester triazole)s at the presence of dithiothreitol. It gives a novel and convenient methodology for the synthesis of reduction‐responsive functional polymer with controlled topologies, and the reduction‐cleavable hyperbranched poly(ester triazole)s with limited intramolecular cyclization are expected to possess potential in the application of stimuli‐responsive anticancer drug nanocarriers. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2374–2380     

Synthesis of pH‐ and thermoresponsive poly(2‐n‐propyl‐2‐oxazoline) based copolymers

Polymers that possess lower critical solution temperature behavior such as poly(2‐alkyl‐2‐oxazoline)s (PAOx) are interesting for their application as stimulus‐responsive materials, for example in the biomedical field. In this work, we discuss the scalable and controlled synthesis of a library of pH‐ and temperature‐sensitive 2‐n‐propyl‐2‐oxazoline P(nPropOx) based copolymers containing amine and carboxylic acid functionalized side chains by cationic ring opening polymerization and postpolymerization functionalization strategies. Using turbidimetry, we found that the cloud point temperature (CP) is strongly dependent on both the polymer concentration and the polymer charge (as a function of pH). Furthermore, we observed that the CP decreased with increasing salt concentration, whereas the CP increased linearly with increasing amount of carboxylic acid groups. Finally, turbidimetry studies in PBS‐buffer indicate that CPs of these polymers are close to body temperature at biologically relevant polymer concentrations, which demonstrates the potential of P(nPropOx) as stimulus‐responsive polymeric systems in, for example, drug delivery applications. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 1573–1582     

Synthesis and characterization of photocrosslinked poly(ε‐caprolactone)s showing shape‐memory properties

Poly(ε‐caprolactone) (PCL) with a pendent coumarin group was prepared by solution polycondensation from 7‐(3,5‐dicarboxyphenyl) carbonylmethoxycoumarin dichloride and α, ω‐dihydroxy terminated poly(ε‐caprolactone) with molecular weights of 1250, 3000, and 10,000 g/mol. These photosensitive polymers underwent a rapid reversible photocrosslinking upon exposure to irradiation with alternating wavelengths (>280/254 nm) without a photoinitiator. The thermal and mechanical properties of the photocrosslinked films were examined by means of differential scanning calorimetry and stress–strain measurements. The crosslinked films exhibited elastic properties above the melting temperature of the PCL segment along with significant decrease in the ultimate tensile strength and Young's modulus. Shape‐memory properties such as strain fixity ratio (R_f) and strain recovery ratio (R_r) were determined by means of a cyclic thermomechanical tensile experiments under varying maximum strains (ε_m = 100, 300, and 500%). The crosslinked ICM/PCL‐3000 and ‐10,000 films exhibited the excellent shape‐memory properties in which both R_f and R_r values were 88–100% for tensile strain of 100–500%; after the deformation, the films recovered their permanent shapes instantaneously. In vitro degradation was performed in a phosphate buffer saline (pH 7.2) at 37 °C with or without the presence of Pseudomonas cepacia lipase. The presence of the pendent coumarin group and the crosslinking of the polymers pronouncedly decreased the degradation rate. The crosslinked biodegradable PCL showing a good shape‐memory property is promising as a new material for biomedical applications. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 2422–2433, 2009     

Shape memory polybenzoxazines based on a siloxane‐containing diphenol

A siloxane‐containing diphenol is synthesized from 1,1,3,3‐tetramethyldisiloxane and o‐allylphenol, followed by the Mannich condensation with aniline, methylamine, and formaldehyde yielding two siloxane‐containing benzoxazines. The onset polymerization temperature of aniline‐based benzoxazine is higher than that of the methylamine counterpart. The dynamic mechanical properties of the polybenzoxazines depend on the structure of the starting primary amines. Both polybenzoxazines exhibit one‐way dual‐shape memory behavior in response to changes in temperature, and they show excellent shape fixity ratios in bending, tension, and tensile stress–strain tests, high shape recovery ratios in bending and tension tests, but relatively low shape recovery ratios in tensile stress–strain test. The network chain segments including the alkylsiloxane units serve as a thermal control switch based on the glass transition temperatures (39 and 53 °C) for the polybenzoxazines. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 1255–1266     

Synthesis of well‐defined 7‐arm and 21‐arm poly(N‐isopropylacrylamide) star polymers with β‐cyclodextrin cores via click chemistry and their thermal phase transition behavior in aqueous solution

The syntheses of well‐defined 7‐arm and 21‐arm poly(N‐isopropylacrylamide) (PNIPAM) star polymers possessing β‐cyclodextrin (β‐CD) cores were achieved via the combination of atom transfer radical polymerization (ATRP) and click reactions. Heptakis(6‐deoxy‐6‐azido)‐β‐cyclodextrin and heptakis[2,3,6‐tri‐O‐(2‐azidopropionyl)]‐β‐cyclodextrin, β‐CD‐(N₃)₇ and β‐CD‐(N₃)₂₁, precursors were prepared and thoroughly characterized by nuclear magnetic resonance and matrix‐assisted laser desorption/ionization time‐of‐flight mass spectrometry. A series of alkynyl terminally functionalized PNIPAM (alkyne‐PNIPAM) linear precursors with varying degrees of polymerization (DP) were synthesized via atom transfer radical polymerization (ATRP) of N‐isopropylacrylamide using propargyl 2‐chloropropionate as the initiator. The subsequent click reactions of alkyne‐PNIPAM with β‐CD‐(N₃)₇ and β‐CD‐(N₃)₂₁ led to the facile preparation of well‐defined 7‐arm and 21‐arm star polymers, namely β‐CD‐(PNIPAM)₇ and β‐CD‐(PNIPAM)₂₁. The thermal phase transition behavior of 7‐arm and 21‐arm star polymers with varying molecular weights were examined by temperature‐dependent turbidity and micro‐differential scanning calorimetry, and the results were compared to those of linear PNIPAM precursors. The anchoring of PNIPAM chain terminal to β‐CD cores and high local chain density for star polymers contributed to their considerably lower critical phase separation temperatures (T_c) and enthalpy changes during phase transition as compared with that of linear precursors. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 404–419, 2009     

Core‐shell nanoparticles with hyperbranched poly(arylene‐oxindole) interiors

Core‐shell type star polymers composed of poly(tert‐butyl acrylate) (poly(t‐BuA)) arms and 100% hyperbranched poly(arylene‐oxindole) interiors were synthesized via the “core‐first” method. Atom transfer radical polymerization of t‐BuA initiated by 2‐bromopropionyl terminal groups of the hyperbranched core was applied for the synthesis of the stars. The resultant star structures were characterized by gel permeation chromatography with triple detection. Polymers of molar masses M_n up to 1.68 × 10⁵ g/mol were obtained. The obtained star polymers compared with the linear counterparts of the same molar mass have a much more compact structure in solution. The intrinsic viscosities of the stars are also significantly lower than their linear counterparts. Light scattering experiments were performed to provide information about the size of these macromolecules in solution. Preliminary characterization of the thermal properties of these novel materials is also reported. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1120–1135, 2009