Al和Sn离子掺杂对La1.2Ca1.8Mn2O7输运性质的影响

研究了Al和Sn离子掺杂对层状钙钛矿结构锰氧化物La1.2Ca1.8Mn2O7输运性质的影响.发现Al,Sn掺杂后样品电阻率增加,并且半导体导电区域电阻值与可变程跃迁导电模型符合得较好;同时掺杂样品金属-绝缘转变温度逐步降低,最大磁电阻值比未掺杂样品增大.     

过渡金属离子掺杂对La1.2Ca1.8Mn2O7输运性质的影响

研究了过渡金属元素掺杂对层状钙钛矿结构锰氧化物La1.2Ca1.8Mn2O7体系输运性质的影响.实验结果表明不同过渡金属离子掺杂均导致体系的金属-绝缘转变温度降低,电阻率与最大磁电阻值(Cr除外)增加.当掺杂量较高时,磁性Cr、Fe、Co、Ni离子对体系性质的影响与其磁性相互作用密切相关.     

La1.4-xNd0.6SrxCuO4中的一维电子结构

1995年,Ｔｒａｎｑｕａｄａ等通过中子散射实验首先在Ｌａ16-ｘＮｄ04ＳｒｘＣｕＯ4中观察到一维自旋-电荷密度的调制,即所谓条纹相.当ｘ=1/8,电荷条纹的周期恰好是4ａ(ａ是四方ＣｕＯ2平面的晶格常数),而自旋的调制周期是8ａ.具体说,可运动的电荷载流子被限制在很窄的一维条纹内,在电荷条纹之间是自旋反铁磁排列的绝缘区;在跨越电荷条纹时,自旋序的位相翻转.早在1989年,Ｚａａｎｅｎ等就曾预言:在掺杂过渡金属氧化物中可能存在条纹相.不过,根据平均场理论作出的上述预言所导致的直接结果是:条纹相是整体绝缘的.这与掺杂铜氧化物中的实际情…     

La4/3(Sr1-xBax)5/3Mn2O7的电输运性质研究

本文主要介绍用溶胶-凝胶法制备的Ba离子掺杂的双层钙钛矿锰基氧化物La4/3(Sr1-xBax)5/3Mn2O7(00.4范围内,低温电阻值随烧结温度增加而减小.出现这种反常行为的结果可能是由于随着Sr逐步被Ba离子取代而引起的失配效应造成结构相分离所致.     

La2/3Ca1/3MnO3体系La位上Y掺杂及其对输运性质的影响

零场下(La1-xYx)2/3Ca1/3MnO3(0相似文献   

超导铁磁体RuSr2Gd1.4Ce0.6Cu2O10-δ的输运性质和磁共振研究

本文对RuSr2Gd1.4Ce0.6Cu2O10-δ样品的微结构、输运性质及磁共振性质进行了实验研究。研究表明RuSr2Gd1.4Ce0.6Cu2O10-δ样品的晶格参数自280K至30K缓慢下降。长时间流动氧气退火可提高零电阻转变温度（Tc(0)），但不影响超导起始转变温度（Tc(onset)）。正常态电阻在110K和180K附近有一微小波动，可能是由于RuO2面载流子与Ru磁矩之间交换作用引起的自旋散射降低所至。电子顺磁共振测量显示有两个只收峰，其中一个对应Gd离子的电子顺磁共振（EPR），另外一个在铁磁转变温度以下出现，它对应Ru离子的铁磁共振（FMR）。本文对磁共振谱的线宽、强度和g因子随温度的变化进行了探讨。     

La0.7Sr0.3MnO3外延膜缺陷性质的慢正电子束研究

用单能慢正电子束,测量了不同氧分压下生长的La0.7Sr0.3MnO3外延膜的S参数与入射正电子能量E的关系.结果发现La0.7Sr0.3MnO3外延膜中S参数与氧分压是非单调变化的;这与沉积氧分压的两种作用相关联的.在氧分压较高的LSMO薄膜中, 空位浓度的增加主要是由沉积原子(离子)与氧原子碰撞几率增大,使其缺乏足够的动能去填补空位引起的;在低氧分压的LSMO薄膜中, 空位浓度的增大则主要是提供成膜所需要的氧原子缺乏,从而导致氧空位及其相关缺陷增加.     

热处理温度对La4/3Sr5/3Mn2O7的结构及电输运性质的影响

用溶胶-凝胶法并经过不同温度(TA)处理而制备出La4/3Sr5/3Mn2O7多晶样品.零场下阻温关系测量表明,较低TA处理的样品有较高的绝缘体-金属转变温度Tp,而对较高TA处理的样品,其Tp在表面和体内有较大差别,表面上有较高的Tp值,且电阻率较低,但在体内Tp低且电阻率高.结合结构分析,我们认为,较高温度处理有利于Sr3Ti2O7相的形成,但太高温度(如高于1450℃)处理的样品,虽然以Sr3Ti2O7相为主,但其表面易形成(La,Sr)MnO3相.     

基于La_(1.4)Ca_(1.6)Mn_2O_7结构、电输运及磁性研究(英文)

我们制备了名义成分是La1.4 Ca1.6 Mn2 O7的多晶样品,并且研究了它的结构、磁性和电性.利用Rietveld方法对X射线衍射数据进行精修的结果表明,该La1.4 Ca1.6 Mn2 O7是由钙钛矿锰氧化物La0.66 Ca0.34 MnO3和氧化钙CaO组成的复相混合物.其中,La0.66 Ca0.34 MnO3占相成分的大部分,而CaO占小部分.我们对比了该名义组分样品La1.4 Ca1.6 Mn2 O7和La0.7 Ca0.3 MnO3的铁磁居里转变温度和绝缘体-金属转变温度,结果表明该La1.4 Ca1.6 Mn2 O7的磁输运性质是由其中的钙钛矿相成分决定的.所有的这些结果表明,名义组分样品La1.4 Ca1.6 Mn2 O7实际上并没有形成所谓的Sr3Ti2O7型的双层结构,而实际形成的是以钙钛矿结构作为主相的复相混合物.     

钙钛矿Mn基氧化物的电子顺磁共振行为的实验研究

借助电子顺磁共振技术,对Mn³⁺/Mn⁴⁺=2∶1和1∶1的两个典型体系 在居里温度T_C以上温区的顺磁行为进行了实验研究.实验表明,存在一特征温度 T_min,通过该温度将T_C以上的磁行为分成两个明显可区分的温区： 在T_min以上,共振谱由一对称的单线构成,Lande 因子g值与温度无关且接近 自由电子的值(～20023),线宽随温度呈线性变化等;而在T_{min关键词： 稀土锰氧化物 电子顺磁共振 交换变窄 自旋-自旋相互作用 自旋-晶格相互作用}     

双层钙钛矿锰氧化物La1.4(Ca1-xSrx)1.6Mn2O7的制备工艺对材料结构和性能的影响

本文主要介绍了双层类钙钛矿锰氧化物La1.4Ca1.6Mn2O7及其掺杂样品不同的制备工艺，分析了它们的XRD和R－T图像，讨论了制备方法对材料结构以及电磁性能的影响。     

Pressure-Induced Crossover From Two- to Three-Dimensional Magnetic Correlations in La 1.4 Sr 1.6 Mn 2 O 7 Manganite

Magnetic pressure-temperature phase diagram of La 1.4 Sr 1.6 Mn 2 O 7 layered manganese oxide has been studied by neutron diffraction. Three phases have been found in this compound at ambient pressure: high-temperature phase with quasi two-dimensional correlations of the magnetic moments on Mn sites and two low-temperature phases with long-range order - antiferromagnetic and ferromagnetic. Under hydrostatic pressure the antiferromagnetic phase is favoured with respect to the two-dimensional and long-range ferromagnetic phases. The magnetic phase with two-dimensional correlations is thus suppressed by the antiferromagnetic phase with long-range order. We discuss this result in terms of the pressure-induced electron transfer and compare our conclusions with predictions given by theoretical calculations.     

Magnetotransport properties of a layered La1.6Ca1.4Mn2O7 polycrystal

Magnetotransport properties of a two-layered La_1.6Ca_1.4Mn₂O₇ polycrystal have been examined as a function of temperature and applied field. It was found that the magnetic transition temperature (T_c) is about 70 K higher than the insulator–metal transition temperature (T_p). Two peaks were observed on both the temperature dependence of the imaginary part of the ac magnetic susceptibility χ^′′(T ) and that of the magnetoresistance MR(T). One is slightly below T_p∼107 K and the other is near T_c∼170 K. Below 70 K, the MR ratio increases with decreasing temperature. Around and above T_p but below T_c, the magnetization shows some indication of saturation, whereas the MR ratio shows no indication of saturation. The magnetotransport properties can be explained by considering the anisotropy exchange interactions along the a–b plane and the c direction, and the low-temperature MR can be attributed to the effects of the nearly fully spin-polarized carriers’ tunneling through the insulating (La,Ca)₂O₂ layers between the adjacent MnO₂ bilayers. Received: 18 September 2000 / Accepted: 20 February 2001 / Published online: 26 April 2001     

（La0．6Nd0．4）0．7Sr0．3MnO3薄膜的厚度依赖的结构与输运性

厚度为6～100 nm的(La0.6Nd0.4)0.7,Sr0.3MnO3(LNSMO)薄膜是由脉冲激光沉积生长在SrTiO3[STO(001)]衬底上.X-射线衍射(XRD)线扫描、ω-摇摆曲线和倒空间衍射显示,随着膜厚(t)的变化,薄膜的结构经历了由完全应变到部分弛豫的变化.电阻测量显示存在两个不同的厚度依赖的金属-绝缘体转变温度(Tp),对于应变的薄膜(t≤17 nm),Tp敏感地依赖于双轴应变和膜厚;而对较厚的薄膜(t≥35nm),Tp对于膜厚是较小敏感的.这个厚度依 赖的输运性的变化可被解释为菱形LNSMO的角度畸变诱导的应变和弛豫.我们的结果表明金属-绝缘体转变温度和相分离都受薄膜的应变态控制.     

Co替代La2／3Ca1／3Mn0．9Co0．1O3输运特性和双峰效应的研究

系统研究了Mn位替代的La2/3Ca2/3Mn0.9Co0.1O3的电输运特性和磁诱导行为,这里替代Co离子的多价态对应有多重的自旋态变化.发现了存在于Co替代La2/3Ca1/3Mn0.9Co0.1O3电输运行为上的双峰效应,具体表现为除了居里温度Tc附近电阻-温度曲线的金属-绝缘(M-I)转变行为(TMIH约为182K)以外,在低温区域电输运行为出现二次性的类M-I转变现象(TMIL乱约为124K).通过对外加磁场下输运特性的研究表明,随外加磁场的增加,电阻-温度曲线整体呈现降低行为,即表现为负的磁电阻效应;同时,高温区峰值温度TMIH向高温区移动,这与传统CMR锰氧化物M-I转变特性完全一致;而低温峰值温度了TMIL则几乎不变,即TMIL表现出某种磁场无关的特征.结合样品磁特性测量结果,我们发现,除了场冷(FC)和零场冷(ZFC)曲线的分叉现象可能证明Co替代诱导Mn位的磁无序而导致体系出现不均匀的铁磁/反铁磁(FM/AFM)团簇外,在低温峰值温度TMIL乱附近没有观察到磁性异常变化.对照对Cu和Cr等相关体系的类似研究,证明这种低温二次M-I转变可能与Co替代导致体系的氧缺陷有关.     

(La1-xSmx)0.185Sr0.15CuO4的输运性质的研究

通过对系列（La1-xSmx)0.185Sr0.15CuO4（x=0,0.05,0.10,0.15)的多晶样品在4.2K-300K的电阻率和液氮温区内的热电势的测量,发现（La1-xSmx)0.185Sr0.15CuO4的电阻率在高温区呈现出线性关系,其斜率也随着x的增大而增大,在x=0.10时达到最大,而在Tc到100K的温区,随着Sm含量的增加,则呈现出由金属行为到类半导体行为的转变,同时超导温度Tc也随着降低,液氮温区内的温差热电势反映了随着Sm含量的增加,体系的载流子浓度也随之降低。     

La4/3Ca5/3Mn2O7的结构、电输运及磁性质研究

采用溶胶-凝胶法,在不同温度烧结制备了名义组分为La4/3Ca5/3Mn2O7的多晶样品.X射线结构分析以及电、磁输运性质的测量表明:La4/3Ca5/3Mn2O7形成的是La2/3Ca1/3MnO3和CaO的混合物.